DE3424293A1 - DIMENSIONS, ESPECIALLY FOR ROOF COVERINGS - Google Patents

DIMENSIONS, ESPECIALLY FOR ROOF COVERINGS

Info

Publication number
DE3424293A1
DE3424293A1 DE19843424293 DE3424293A DE3424293A1 DE 3424293 A1 DE3424293 A1 DE 3424293A1 DE 19843424293 DE19843424293 DE 19843424293 DE 3424293 A DE3424293 A DE 3424293A DE 3424293 A1 DE3424293 A1 DE 3424293A1
Authority
DE
Germany
Prior art keywords
weight
parts
combinations
acetone
mixture
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19843424293
Other languages
German (de)
Inventor
Josef Prag/Praha Mittenhuber
Milan Brünn/Brno Popelka
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TEPLOTECHNA OP
Original Assignee
TEPLOTECHNA OP
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from CS514383A external-priority patent/CS247753B1/en
Priority claimed from CS43184A external-priority patent/CS251616B1/en
Priority claimed from CS84430A external-priority patent/CS251615B1/en
Priority claimed from CS84432A external-priority patent/CS251617B1/en
Application filed by TEPLOTECHNA OP filed Critical TEPLOTECHNA OP
Publication of DE3424293A1 publication Critical patent/DE3424293A1/en
Withdrawn legal-status Critical Current

Description

MASSE, INSBESONDERE FÜR DACHBELÄGEDIMENSIONS, IN PARTICULAR FOR ROOF COVERINGS

Die Erfindung betrifft eine Masse, insbesondere für Dachbeläge, die namentlich als Werkstoff zum Bedecken von Dachüberzügen, wie Dachpappe, zum Ankleben von Wasserabdichtungsfolien aus Kautschuk oder Kunststoffmaterialien bzw. auch als Dichtungs- und Fugenmasse anwendbar ist. Die Masse kann eventuell auch als ein 'trittfester Dachbelag dienen.The invention relates to a mass, in particular for roof coverings, namely as a material for covering of roof coverings, such as roofing felt, for gluing waterproofing foils made of rubber or plastic materials or can also be used as a sealant and joint compound. The mass can possibly also be used as a 'non-slip' Serve roof covering.

Gegenwärtig verwendet man als Dachbeläge am häufigsten Werkstoffe auf der Basis von Asphalt, dessen Preis ständig steigt und welcher immer mehr zu einem Mangelmaterial wird, davon abgesehen, daß er in manchen Fällen wegen seiner Eigenschaften den Anforderungen an Beständigkeit und Lebensdauer eines infolge veränderlicher Wetterbedingungen periodisch außerordentlich beanspruchten Dachbelags nicht gerecht wird. Darüberhinaus stellt die Verarbeitung und Vorbereitung des Asphalts für diesen Zweck beträchtliche Ansprüche an Energie.Currently, the most common roofing materials used are asphalt-based materials, the price of which is constant increases and which becomes more and more a shortage of material, apart from the fact that in some cases it is because of its properties meet the requirements for resistance and service life as a result of changing weather conditions periodically extraordinarily stressed roof covering does not do justice. In addition, the processing and preparing the asphalt for this purpose requires considerable energy.

Für trittfeste Dachbeläge werden meistenteils Kunststoffmaterialien verwendet. Bei der Verarbeitung von Kunststoffen zu vorgefertigten Bahnen für Bodenbeläge oder Folien für äußere Wasserabdichtungen kommt es innerhalb kürzerer oder längerer Zeit zu einer erheblichen Kontraktion dieser Materialien, was deren Benutzung zu einer ganzen Reihe von Verwendungszwecken, insbesondere zum Herstellen von Dachbelägen und Wasserabdichtungen, praktisch ausschließt.Plastic materials are mostly used for stable roof coverings used. When processing plastics into prefabricated sheets for floor coverings or foils for external waterproofing, there is a considerable contraction of these within a shorter or longer period of time Materials, which means that they can be used for a wide variety of purposes, particularly for the manufacture of roof coverings and waterproofing, practically excludes.

Auf dem Gebiet des Anklebens vor allem von Wasserabdichtungsbelägen, beispielsweise aus Kautschuk- und Kunststoffolien, herrscht auch ein Mangel an preiswerten Werkstoffen mit entsprechenden physikochemischen Eigenschaften, die wäh-In the field of gluing, especially of waterproofing coverings, For example, from rubber and plastic films, there is also a lack of inexpensive materials corresponding physicochemical properties that

rend der gesamten Lebensdauer des wasserabdichtenden Belags aufrechterhalten werden sollen. Problematisch ist auch die Vielseitigkeit der Klebstoffe für verschiedenartige Substrate wie Beton, Dachbahnen aus Asphalt, Blech, Kunststoffe auf PVC-Basis, Glas oder dergleichen.rend should be maintained for the entire service life of the waterproofing covering. Problematic is also the versatility of the adhesives for various substrates such as concrete, asphalt roofing membranes, Sheet metal, PVC-based plastics, glass or the like.

Die vorliegende Erfindung soll die obenerwähnten Nachteile des Standes der Technik eliminieren und ihr liegt die Aufgabe zugrunde, eine Masse, insbesondere für Dachbeläge, zur Verfügung zu stellen, die erfindungsgemäß dadurch gekennzeichnet ist, daß sie aus einem Grundgemisch besteht, enthaltend 13 bis 50 Gew.-% eines ketonischen und/oder aromatischen Lösungsmittels, z.B. Aceton, Toluol bzw. deren Kombinationen, 10 bis 75 Gew.-% Abfallpech der Dimethylterephthalathersteilung, 3 bis 15 Gew.-% Weichmacher, z.B. Dibutylphthalat, Dioctyladipat oder a.! phatische Leichtöle,und 8 bis 25 Gew.-% Mischpolymerisat, z.B. Vinylchlorid/Vinylacetat.The present invention is intended to eliminate the above-mentioned disadvantages of the prior art and its object is to provide a compound, in particular for roof coverings, which is characterized according to the invention in that it consists of a basic mixture containing 13 to 50 wt. -% of a ketonic and / or aromatic solvent, for example acetone, toluene or combinations thereof, 10 to 75% by weight of waste pitch of the dimethyl terephthalate division, 3 to 15% by weight of plasticizers, for example dibutyl phthalate, dioctyl adipate or a. ! phatic light oils, and 8 to 25% by weight copolymer, for example vinyl chloride / vinyl acetate.

Vorzugsweise enthält das Grundgemisch ferner 0,5 bis 16 Gew.-% eines Stabilisators, z.B. Aluminiumpulver oder Zinkoxid. Diese aus dem Grundgemisch hergestellte Masse ist insbesondere für Dachbeläge einsetzbar.Preferably, the base mix also contains 0.5 to 16% by weight of a stabilizer such as aluminum powder or Zinc oxide. This mass produced from the basic mixture can be used in particular for roof coverings.

Die zum Ankleben von insbesondere wasserabdichtenden Bahnen und Folien bestimmte Masse besteht vorzugsweise neben dem Grundgemisch aus einem sekundären Gemisch, das 0,6 bis 6,5 Gewichtsteile Abfallpech der Dimethylterephthalatherstellung, 7,2 bis 18 Gewichtsteile eines ketonischen und/oder aromatischen Lösungsmittels, z.B. Aceton, Keton bzw. deren Kombinationen, 0,1 bis 0,7 Gewichtsteile Weichmacher, z.B. Dibutylphthalat, Dioctyladipat oder aliphatische Leichtöle, 0,05 bis 1 Gewichtsteile Mischpolymerisat, z.B. Vinylchlorid/Vinylacetat, The compound intended for gluing, in particular, waterproofing sheets and foils, is preferably made in addition to the basic mixture of a secondary mixture, the 0.6 to 6.5 parts by weight of waste pitch from dimethyl terephthalate production, 7.2 to 18 parts by weight of a ketonic and / or aromatic solvent, e.g. acetone, Ketone or combinations thereof, 0.1 to 0.7 parts by weight plasticizers, e.g. dibutyl phthalate, dioctyl adipate or aliphatic light oils, 0.05 to 1 part by weight of copolymer, e.g. vinyl chloride / vinyl acetate,

0,05 bis 0,6 Gewichtsteile Butadien-Styrol-Kautschuk und 0,03 bis 0,4 Gewichtsteile synthetisches oder Naturharz, z.B. Kumaron-Inden-Harz, bezogen auf 3 bis 10 Gewichtsteile des Grundgemisches, enthält.0.05 to 0.6 parts by weight of butadiene-styrene rubber and 0.03 to 0.4 parts by weight synthetic or natural resin, e.g., coumarone-indene resin, based on 3 to 10 parts by weight of the basic mixture contains.

Zum Steigern der Relaxationsfähigkeit ist es vorteilhaft, daß die Masse außer dem Grundgemisch noch 1 bis 25 Gewichtsteile eines Relaxationsmittels, z.B. Butylester der Acrylsäure oder Äthylenylstyrolacrylat, bezogen auf 100 Gewichtsteile des sekundären Gemisches, enthält.To increase the ability to relax, it is advantageous that the mass, in addition to the basic mixture, also contain 1 to 25 parts by weight a relaxation agent, e.g. butyl ester of acrylic acid or ethylenyl styrene acrylate per 100 parts by weight of the secondary mixture.

Soll die Masse für trittfeste Dachbeläge verwendet werden, ist es vorteilhaft, daß sie noch 0,3 bis 5,5 Gewichtsteile eines Regeneriermittels, z.B. Polystyrol, Terpolymerisat von Acrylnitril/Butadien/Styrol bzw. deren Kombinationen, und 1,5 bis 8 Gewichtsteile eines ketonischen und/oder aromatischen Lösungsmittels, z.B. Aceton, Toluol bzw. deren Kombinationen, bezogen auf 1 bis 8 Gewichtsteile des Grundgemisches, enthält. If the compound is to be used for stable roof coverings, it is advantageous that it contains 0.3 to 5.5 parts by weight of a regenerant, e.g. polystyrene, terpolymer of acrylonitrile / butadiene / styrene or their combinations, and 1.5 to 8 parts by weight of a ketonic and / or aromatic solvents, e.g. acetone, toluene or their combinations, based on 1 to 8 parts by weight of the basic mixture.

Zum Erzielen einer Farbabstimmung mit den anderen Bauelementen kann die Masse ferner 0,05 bis 0,3 Gewichtsteile eines Farbpigments, z.B. Eisen/III/-oxid, Zinkoxid, Titandioxid und Chromsesquioxid, bezogen auf 1 bis 8 Gewichtsteile des Grundgemisches, enthalten.To achieve a color match with the other components the mass can also contain 0.05 to 0.3 parts by weight of a color pigment, e.g. iron / III / oxide, zinc oxide, Titanium dioxide and chromium sesquioxide based on 1 to 8 parts by weight of the basic mixture.

Die erfindungsgemäße Masse kann in einer ganzen Reihe von Gebieten die Produkte aus Asphalt vollständig ersetzen und übertrifft sie sogar in manchen Eigenschaften. Gegenüber den Asphaltprodukten sind insbesondere die niedrigeren Anschaffungskosten zu beachten, da die Basis der Masse aus sekundären, bisher weiter unverarbeiteten Rohstoffen besteht. Ein weiterer Vorteil der erfindungsgemäßen Masse liegt darin, daß sie nicht einmal innerhalb einer verhältnismäßig sehr langen Zeitspanne zur Kontraktion neigt, was diese Masse neben anderen EigenschaftenThe composition according to the invention can completely replace asphalt products in a number of areas and even surpasses them in some properties. Compared to the asphalt products, in particular the lower ones Acquisition costs must be taken into account, as the base of the mass consists of secondary, previously unprocessed Raw materials. Another advantage of the composition of the invention is that they are not even within tends to contract over a relatively long period of time, which this mass, among other properties, has

gerade zum Ausführen von Dachbelägen und von Wasserabdichtungsarbeiten im allgemeinen vorbestimmt.especially for carrying out roof coverings and waterproofing work generally predetermined.

Ein weiterer Vorteil der erfindungsgemäßen Masse besteht darin, daß sie photochemisch beständig ist, so daß sie wegen ihrer Indifferenz gegen Sonneneinstrahlung auch für äußere Wasserabdichtungen verwendet werden kann. Die Masse weist überdies eine dauerhafte Elastizität auf, so daß die aus ihr hergestellten Beläge keine Tendenz zur Bruch- und Rißbildung zeigen. Die erfindungsgemäße Masse weist darüberhinaus eine Auffrischungsfähigkeit auf, selbst wenn sie mehrere Jahre der Wärme ausgesetzt ist. Diese Fähigkeit kann durch gewisse Maßnahmen noch gesteigert werden. Sie besitzt ferner ein hohes Haftvermögen gegenüber verschiedenartigen Substraten, einschließlich Beton, Kunststoffen, Glas, Holz, Zinkblech, Stahl, Aluminium, Buntmetallen, Ziegelware und auch synthetischem Kautschuk. Die Masse kann durch Aufspachteln, Gießen oder auch maschinell aufgetragen werden. Sie ist eventuell auch als Fugenmasse anwendbar.There is another advantage of the composition according to the invention in that it is photochemically stable, so that because of its indifference to solar radiation, too can be used for external waterproofing. The mass also has a permanent elasticity, see above that the coverings made from it show no tendency to break and crack. The inventive In addition, the mass has a refreshability even after being exposed to heat for several years is. This ability can be increased by taking certain measures. She also has a high Adhesion to various substrates including concrete, plastics, glass, wood, zinc sheet, Steel, aluminum, non-ferrous metals, brick goods and synthetic rubber. The mass can be applied by spatula, Pouring or applied by machine. It can also be used as a grout.

Beispiel 1example 1

Durch Vermischen von 660 kg Aceton, 16 00 kg Abfallpech der Dimethylterephthalatherstellung, 34 0 kg Dibutylphthalat, 4 25 kg Mischpolymerisat und 50 kg Aluminiumpulver wurde ein Dachdeckungsstoff vorbereitet.By mixing 660 kg of acetone, 1600 kg of waste pitch the production of dimethyl terephthalate, 34 0 kg of dibutyl phthalate, A roofing material was prepared for 25 kg of mixed polymer and 50 kg of aluminum powder.

Dieser Stoff wies die nachfolgenden physikochemischen Parameter auf:This substance had the following physicochemical parameters:

spezifisches Gewicht 1,1 bis 1,2 kg/1specific weight 1.1 to 1.2 kg / 1

Brüchigkeit nach Reifung bis 5 - 100CFragility after ripening up to 5 - 10 0 C

Wärmebeständigkeit nach Reifung:Heat resistance after maturation:

permanent bis 800Cpermanent up to 80 0 C

kurzzeitig bis 900C Schrumpfung von auf 700C erhitztem Film - innerhalb 7 Tage 1 %Briefly up to 90 ° C shrinkage of film heated to 70 ° C - within 7 days 1%

Frostbeständigkeit in einer Lösung (bestimmt die Aufspachtelbarkeit) bis -250C Flammpunkt nach Reifung -15O0CFrost resistance in a solution (determines whether it can be troweled on) down to -25 0 C flash point after maturation -15O 0 C

Beispiel 2Example 2

Dem Stoff gemäß Beispiel 1 wurde 20% Dibutylphthalat zugegeben.20% dibutyl phthalate was added to the fabric according to Example 1.

Dieser Stoff wurde insbesondere zum Aufkleben von wasserabdichtenden Belägen aus Kautschuk- und Kunststoffolien im Winter bestimmt.This fabric was especially designed for gluing waterproofing Coverings made of rubber and plastic films are determined in winter.

Beispiel 3Example 3

In einem Homogenisator wurde ein Klebstoff vorbereitet aus 2000 Gewichtsteilen Toluol,An adhesive was prepared from in a homogenizer 2000 parts by weight of toluene,

1300 Gewichtsteilen Abfallpech der Dimethylterephthalatherstellung, 40 Gewichtsteilen Dibutylphthalat, 80 Gewichtsteilen Vinylchlorid/Vinylacetat-Mischpoly-1300 parts by weight of waste pitch from dimethyl terephthalate production, 40 parts by weight of dibutyl phthalate, 80 parts by weight of vinyl chloride / vinyl acetate mixed poly-

merisatmerisat

30 Gewichtsteilen Butadien-Styrol-Kautschuk und 20 Gewichtsteilen synthetischem Kumaron-Inden-Harz.30 parts by weight of butadiene-styrene rubber and 20 parts by weight of synthetic coumarone-indene resin.

Der Kleber wies die nachfolgenden physikochemischen Parameter auf:The adhesive had the following physicochemical parameters:

spezifisches Gewicht 1,1 kg/1specific weight 1.1 kg / 1

Wärmebeständigkeit: permanent bis 700C kurzzeitig bis 900CHeat resistance: permanent up to 70 ° C. briefly up to 90 ° C.

Reifepunkt nach Entflammung -1500CMaturity point after ignition -150 0 C

FolienabschälfestigkeitFilm peel strength

innerhalb 2 Tage 0,6 Nx/cmwithin 2 days 0.6 Nx / cm

innerhalb 6 Wochen 30 Nx/cmwithin 6 weeks 30 Nx / cm

Beispiel 4Example 4

In einem Homogenisator wurde ein Klebstoff von nachfolgender Zusammensetzung vollkommen homogenisiert: 20Q0 Gewichtsteile ToluolAn adhesive with the following composition was completely homogenized in a homogenizer: 20Q0 parts by weight of toluene

1300 Gewichtsteile Abfallpech der Dimethylterephthalatherstellung 1300 parts by weight of waste pitch from dimethyl terephthalate production

40 Gewichtsteile Dibutylphthalat 80 Gewichtsteile Vinylchlorid/Vinylacetat-Mischpoly-40 parts by weight of dibutyl phthalate 80 parts by weight of vinyl chloride / vinyl acetate mixed poly-

merisatmerisat

30 Gewichtsteile Butadien-Styrol-Kautschuk 20 Gewichtsteile synthetischem Kumaron-Inden-Harz und 600 Gewichtsteile Butylester der Acrylsäure.30 parts by weight of butadiene-styrene rubber, 20 parts by weight of synthetic coumarone-indene resin and 600 parts by weight of the butyl ester of acrylic acid.

Der Klebstoff wurde in der Praxis zum Ankleben von wasserabdichtenden Bändern geprüft. Dabei wies er außerordentliche Elastizität ohne Abbauspuren und Oberflächenrisse auf.The glue was used in practice for gluing waterproofing Ribbons checked. It showed extraordinary elasticity without signs of degradation and surface cracks on.

Beispiel 5Example 5

Eine Masse für trittfeste Beläge wurde aus den nachfolgenden Ingredienzien vorbereitet:A compound for non-slip coverings was prepared from the following ingredients:

25 Gewichtsteile Abfallpech der Dimethylterephthalatherstellung 25 parts by weight of waste pitch from dimethyl terephthalate production

6 Gewichtsteile Dibutylphthalat 5 Gewichtsteile Vinylchlorid/Vinylacetat-Mischpoly-6 parts by weight of dibutyl phthalate 5 parts by weight of vinyl chloride / vinyl acetate mixed poly-

merisatmerisat

75 Gewichtsteile Toluol
9 Gewichtsteile Aceton und
25 Gewichtsteile Polystyrol.75 parts by weight of toluene
9 parts by weight of acetone and
25 parts by weight of polystyrene.

Beispiel 6Example 6

Eine Masse für trittfeste Beläge bestand aus 15 Gewichtsteilen Abfallpech der Dimethylterephthalatherstellung
3,5 Gewichtsteilen Dibutylphthalat 3 Gewichtsteilen Vinylchlorid/Vinylacetat-Mischpoly- .A compound for hard-wearing coverings consisted of 15 parts by weight of waste pitch from dimethyl terephthalate production
3.5 parts by weight of dibutyl phthalate 3 parts by weight of vinyl chloride / vinyl acetate mixed poly.

merisat
25 Gewichtsteilen Toluolmerisat
25 parts by weight of toluene

7 Gewichtsteilen Aceton und
3,5 Gewichtsteilen Acrylnitril-Butadien-Styrol.7 parts by weight of acetone and
3.5 parts by weight of acrylonitrile-butadiene-styrene.

Die Massen der Beispiele 5 und 6 wurden langzeitig "auf Substraten im Freien geprüft, wobei photochemische Stabilität und Elastizität des Belags sogar nach mehreren Jahren festgestellt worden ist.The compositions of Examples 5 and 6 were long-term "on" Substrates tested outdoors, with photochemical stability and elasticity of the covering even after several years has been established.

Claims (6)

ν. FÖNER ϊ~ »- β f - Nf G H ■ A " U ; S FINCK PATENTANWÄLTE EUROPEAN PATENT ATTORNEYS MARIAHILFPLATZ 2 & 3, MÜNCHEN 9O POSTADRESSE: POSTFACH 95 O1 6O, D-8OOO MÖNCHEN 95 '"ί Λ 9 Λ 2 TEPLOTECHNA 2. Juli 1984 oborovy podnik DEAA-32028.5 MASSE, INSBESONDERE FÜR DACHBELÄGE Patentansprücheν. FÖNER ϊ ~ »- β f - Nf GH ■ A" U; S FINCK PATENTANWÄLTE EUROPEAN PATENT ATTORNEYS MARIAHILFPLATZ 2 & 3, MUNICH 9O POSTAL ADDRESS: PO Box 95 O1 6O, D-8OOO MÖNCHEN 95 '"ί 9 Λ 2 2 July 1984 oborovy podnik DEAA-32028.5 DIMENSIONS, IN PARTICULAR FOR ROOFING claims 1. Masse, insbesondere für Dachbeläge, dadurch gekennzeichnet , daß sie aus einem Grundgemisch besteht, enthaltend 13 bis 50 Gew.-% eines ketonischen und/oder aromatischen Lösungsmittels, z.B. Aceton, Toluol bzw. deren Kombinationen, 10 bis 75 Gew.-% Abfallpech aus der Dimethylterephthalatherstellung, 3 bis 15 Gew.-% Weichmacher, z.B. Dibutylphthalat, Dioctyladipat oder aliphatische Leichtöle und 8 bis 25 Gew.-% Mischpolymerisat, z.B. Vinylchlorid/Vinylacetat.1. Mass, especially for roof coverings, characterized in that it consists of a basic mixture consists, containing 13 to 50 wt .-% of a ketonic and / or aromatic solvents, e.g. acetone, toluene or their combinations, 10 to 75% by weight of waste pitch from dimethyl terephthalate production, 3 to 15% by weight of plasticizers, e.g. dibutyl phthalate, dioctyl adipate or aliphatic light oils and 8 to 25% by weight Mixed polymer, e.g. vinyl chloride / vinyl acetate. 2. Masse nach Anspruch 1, dadurch gekennzeichnet, daß das Grundgemisch zusätzlich 0,5 bis 16 Gew.-% eines Stabilisators, z.B. Aluminiumpulver oder Zinkoxid, enthält.2. Mass according to claim 1, characterized in that that the basic mixture additionally contains 0.5 to 16% by weight of a stabilizer, e.g. aluminum powder or zinc oxide, contains. 3. Masse nach einem der Ansprüche 1 und 2, dadurch gekennzeichnet , daß sie neben dem Grundgemisch ein sekundäres Gemisch enthält mit folgender Zusammensetzung: 3. Composition according to one of claims 1 and 2, characterized in that it is in addition to the basic mixture contains a secondary mixture with the following composition: 0,6 bis 6,5 Gewichtsteile Abfallpech der Dimethyltere-0.6 to 6.5 parts by weight of waste pitch of the dimethyl tere- phthalatherstellung,phthalate production, 7,2 bis 18 Gewichtsteile eines ketonischen und/oder aromatischen Lösungsmittels, z.B. Aceton, Keton bzw,7.2 to 18 parts by weight of a ketonic and / or aromatic solvent, e.g. acetone, ketone or deren Kombinationen, 0,1 bis 0,7 Gewichtsteile Weichmacher, z.B. Dibutyl-their combinations, 0.1 to 0.7 parts by weight plasticizers, e.g. dibutyl phthalat, Dioctyladipat oder aliphatische Leichtöle, 0,05 bis 1 Gewichtsteile Mischpolymerisat, z.B. Vinyl-phthalate, dioctyl adipate or aliphatic light oils, 0.05 to 1 part by weight copolymer, e.g. vinyl chlorid/Vinylacetat, 0,05 bis 0,6 Gewichtsteile Butadien-Styrol-Kautschuk und 0,03 bis 0,4 Gewichtsteile synthetisches oder Naturharz,chloride / vinyl acetate, 0.05 to 0.6 parts by weight butadiene-styrene rubber and 0.03 to 0.4 parts by weight synthetic or natural resin, z.B. Kumaron- Inden-Harz, bezogen auf 3 bis 10 Gewichtsteile des Grundgemisches.e.g., coumarone-indene resin based on 3 to 10 parts by weight of the base mix. 4. Masse nach Anspruch 3, dadurch gekennzeichnet, daß sie zusätzlich 1 bis 25 Gewichtsteile eines Relaxationsmittels, z.B. Butylester der Acrylsäure oder Äthylenylstyrolacrylat , bezogen auf 100 Gewichtsteile des sekundären Gemisches , enthält.4. Mass according to claim 3, characterized in that that they additionally 1 to 25 parts by weight of a relaxation agent, for example butyl ester of acrylic acid or Ethylenyl styrene acrylate, based on 100 parts by weight of the secondary mixture contains. 5. Masse nach einem der Ansprüche 1 und 2, dadurch gekennzeichnet , daß sie ferner 0,3 bis 5,5 Gewichtsteile eines Regeneriermittels, z.B. Polystyrol, Terpolymerisate von Acrylnitril/Butadien/Styrol bzw. deren Kombinationen und 1,5 bis 8 Gewichtsteile eines ketonischen und/oder aromatischen Lösungsmittels, z.B. Aceton, Toluol bzw. deren Kombinationen, bezogen auf 1 bis 8 Gewichtsteile des Grundgemisches, enthält.5. Composition according to one of claims 1 and 2, characterized in that it is also 0.3 to 5.5 Parts by weight of a regenerant, e.g. polystyrene, terpolymers of acrylonitrile / butadiene / styrene or their Combinations and 1.5 to 8 parts by weight of a ketonic and / or aromatic solvent, e.g. acetone, toluene or their combinations, based on 1 to 8 parts by weight of the basic mixture. 6. Masse nach Anspruch 5, dadurch gekennzeichnet, daß sie ferner 0,05 bis 0,3 Gewichtsteile eines Farbpigments, z.B. Eisen/III/-oxid, Zinkoxid, Titandioxid und Chromsesquioxid , bezogen auf 1 bis 8 Gewichtsteile des Grundgemisches , » enthält.6. Composition according to claim 5, characterized in that that they also contain 0.05 to 0.3 parts by weight of a colored pigment, e.g. iron / III / oxide, zinc oxide, titanium dioxide and chromium sesquioxide, based on 1 to 8 parts by weight of the base mixture.
DE19843424293 1983-07-07 1984-07-02 DIMENSIONS, ESPECIALLY FOR ROOF COVERINGS Withdrawn DE3424293A1 (en)