DE19936481A1 - Preparation of easily processed soft polyurethane foams, useful as noise damping materials, with good noise damping properties and high loss factor - Google Patents

Preparation of easily processed soft polyurethane foams, useful as noise damping materials, with good noise damping properties and high loss factor

Info

Publication number
DE19936481A1
DE19936481A1 DE1999136481 DE19936481A DE19936481A1 DE 19936481 A1 DE19936481 A1 DE 19936481A1 DE 1999136481 DE1999136481 DE 1999136481 DE 19936481 A DE19936481 A DE 19936481A DE 19936481 A1 DE19936481 A1 DE 19936481A1
Authority
DE
Grant status
Application
Patent type
Prior art keywords
optionally
characterized
based
wt
oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE1999136481
Other languages
German (de)
Inventor
Bernd Zaschke
Peter Falke
Inge Rotermund
Kirsten Schmaler
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BASF SE
Original Assignee
BASF SE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

Easily processed soft PUR foams of good noise damping properties and high loss factor can be prepared from special polyurethane mixtures. Easily processed PUR foams of good noise damping properties and high loss factor can be prepared from special polyetherol mixtures, i.e. by: (a) reaction of organic and/or modified organic polyisocyanates; with (b) a polyetherol mixture; and optionally with (c) other compounds having a hydrogen atom reactive to isocyanates in the presence of water and/or other propellant, catalysts, and optionally adjuvants and additives. The polyether mixture (b) comprises: (1) at least 2-8-functional polyetherols based on ethylene oxide and propylene oxide and optionally butylene oxide, of OH number 20-80 mg KOH/g and more than 50% primary OH groups; and (2) at least one castor oil polyetherol based on ethylene oxide and optionally propylene oxide and/or butylene oxide of OH number 50-160 mg KOH/g. An Independent claim is included for a polyurethane foam material having noise damping properties prepared as above.

Description

Die Erfindung betrifft ein Verfahren zur Herstellung von Polyurethanweichschaumstoffen mit schalldämpfenden Eigen schaften durch Umsetzung von organischen und/oder modifizierten organischen Polyisocyanaten (a) mit einem Polyetherolgemisch (b) und gegebenenfalls weiteren gegenüber Isocyanaten reaktive Wasserstoffatome aufweisenden Verbindungen (c) in Gegenwart von Wasser und/oder anderen Treibmitteln (d), Katalysatoren (e) und gegebenenfalls weiteren Hilfs- und Zusatzstoffen (f), wobei ein spezielles Polyetherolgemisch eingesetzt wird. The invention relates to a process for the preparation of flexible polyurethane foams having sound-deadening self-unions by reacting organic and / or modified organic polyisocyanates (a) with a polyetherol mixture (b) and optionally other isocyanate-reactive hydrogen atoms containing compounds (c) in the presence of water and / or other blowing agents (d), catalysts (s) and optionally further auxiliaries and additives (f), whereby a special polyetherol is used.

Die Herstellung von Polyurethanen (PUR) durch Umsetzung von organischen Polyisocyanaten mit Verbindungen mit mindestens zwei reaktiven Wasserstoffatomen, beispielsweise Polyoxyalkylen polyaminen und/oder vorzugsweise organischen Polyhydroxyl verbindungen, insbesondere Polyetherolen mit Molekulargewichten von z. The preparation of polyurethanes (PUR) by reacting organic polyisocyanates with compounds having at least two reactive hydrogen atoms, such as polyoxyalkylene polyamines and / or preferably organic polyhydroxyl compounds, in particular polyether polyols with molecular weights of z. B. 300 bis 6000, und gegebenenfalls Kettenverlängerungs- und/oder Vernetzungsmitteln mit Molekulargewichten bis ca. 400 in Gegenwart von Katalysatoren, Treibmitteln, Flammschutzmitteln, Hilfsmitteln und/oder Zusatzstoffen ist bekannt und wurde viel fach beschrieben. , 300 to 6000, and possibly chain extenders and / or crosslinking agents having molecular weights up to about 400 in the presence of catalysts, blowing agents, flame retardants, auxiliaries and / or additives is known and has been described a lot of times. Eine zusammenfassende Übersicht über die Her stellung von PUR wird z. A summary overview of the position of Her PUR z. B. im Kunststoffhandbuch, Band VII, Poly urethane, Carl-Hanser-Verlag, München, 1. Auflage 1966, heraus gegeben von Dr. As in the plastics, Volume VII, poly urethane Carl Hanser Verlag, Munich, 1st edition 1966, given out by Dr. R. Vieweg und Dr. R. Vieweg and Dr. A. Höchtlen, sowie 2. Auflage 1983 und 3. Auflage 1993, herausgegeben von Dr. A. Hoechtlen and 2nd edition 1983 and 3rd edition 1993, edited by Dr. G. Oertel, gegeben. G. Oertel given.

Das Hauptanwendungsgebiet für kalthärtende Weichschaumstoffe sind Polsterelemente für die Möbelindustrie und Sitzelemente für die Autoindustrie. The main area of ​​application for cold-curing foams are padding elements for the furniture industry, seat elements for the automotive industry. Daneben finden zahlreiche PUR-Weichschäume für schalldämpfende Zwecke, wie z. In addition, find numerous polyurethane flexible foams for sound deadening purposes such. B. beim Automobilteppich Anwendung. As the automotive carpet application.

Das offenporige Schaumgerüst bietet günstige Voraussetzungen für eine Luftschallabsorption. The open-cell foam structure provides favorable conditions for absorption of airborne sound. Das Dämpfungsverhalten der Weich schaumstoffe, das z. The damping behavior of the soft foams, the z. B. durch den sogenannten Verlustfaktor η beschrieben werden kann, wird in zahlreichen Schriften als eine Größe zur Optimierung des Schalldämpfungsmaßes angesehen. B. can be described η by the so-called loss factor, is considered to be a size to optimize the sound absorption values ​​in numerous writings. Der Verlustfaktor η The loss factor η

η = W v /2πW r η = W v / 2πW r

bringt zum Ausdruck, welcher Schallanteil während einer Schwingungsperiode irreversibel in Wärme umgewandelt wird. expresses the proportion which sound is converted irreversibly into heat during an oscillation period. Hohe Verlustfaktoren bewirken demzufolge eine höhere Schall dämpfung. therefore high loss factors cause attenuation higher sound.

In DE-A-27 51 774 wird ein schalldämmendes Verbundsystem auf Basis einer Kombination von Hartschaum- und Weichschaumpolyolen beschrieben, das hohe Anteile an Schwerstoffen enthält, was sich ungünstig auf das Flächengewicht des Werkstückes auswirkt. In DE-A-27 51 774 a sound absorbing composite system will be described on the basis of a combination of rigid foam and Weichschaumpolyolen containing high amounts of heavy materials, which is unfavorable to the basis weight of the workpiece.

In DE-A-37 10 731 wird ein Weichschaumstoff mit schallisolierenden und entdröhnenden Eigenschaften vorgestellt. In DE-A-37 10 731 a flexible foam will be presented with sound-insulating and entdröhnenden properties. Die auf dieser Basis bei relativ hohen Rohdichten gefertigten Wandverkleidungselemente mit Teppichauflage können Ricinusöl als einen Bestandteil ent halten. The manufactured on this basis at relatively high densities wall cladding elements with carpet can keep castor oil as an ingredient ent. Die als besonderer Vorzug erzielten adhäsiven Ober flächeneigenschaften erfordern ein Verschäumen in einem Kenn zahlbereich von < 80. The surface properties achieved as a particular advantage adhesive upper require foaming in a characteristic speed range of <80th

DE-A-33 16 652 beschreibt einen Schaumstoff mit geräuschmindernden Eigenschaften. DE-A-33 16 652 describes a foam with a noise-reducing properties. Hier werden deutliche Anteile an Ricinusöl ver wandt, insbesondere in Kombination mit einem nicht näher spezifi zierten Polyetheralkohol auf Ethylenoxidbasis. Here significant fractions of castor oil are ver Wundt, particularly in combination with an unspecified specifi ed polyether based on ethylene oxide. Die OH-Zahl der A-Komponente liegt dabei im Bereich von 150 bis 250 mg KOH/g. The OH number of component A is in the range of 150 to 250 mg KOH / g. Trotz eines Zusatzes von FCKW werden Rohdichten von größer als 120 kg/m 3 erreicht. In spite of an addition of CFC densities are reached 3 m of greater than 120 kg /. Zudem muß das Schaumstück auf dem dünnwandigen Trägermaterial aufgeklebt werden. In addition, the foam piece must be glued to the thin substrate. Diese Einschränkungen lassen unter gegenwärtigen Bedingungen keine ökonomische und mit den Forderungen des Umweltschutzes vertretbare Fertigung von Akustik schäumen zu. These restrictions can under current conditions foam to any economic and reasonable with the requirements of environmental protection manufacture of acoustics.

In EP-A-433878 werden Teppichschäume mit viskoelastischen Eigen schaften aufgezeigt. In EP-A-433878 carpet foams are shown with viscoelastic intrinsic properties. Diese bestehen aus einer speziellen Kombi nation von hydrophilen und hydrophoben Polyolen. These consist of a specific combination nation of hydrophilic and hydrophobic polyols. Diese Systeme verfügen über ein gutes Schallabsorptionsverhalten, entmischen sich jedoch nach kurzer Zeit während der Lagerung, wenn nicht permanent gerührt wird. These systems have a good sound absorption behavior, but segregate after a short time during storage, if not permanently stirred. DE-A-39 42 330 beschreibt ebenfalls spezielle Polyolmischungen zur Herstellung derartiger visko elastischer Schaumstoffe. DE-A-39 42 330 also describes special polyol mixtures for the production of such visco elastic foams.

In EP-A-331941 werden Akustikschäume mit einem Verlustfaktor von < 0,5 beansprucht. In EP-A-331941 acoustic foams are claimed with a loss factor of <0.5. Diese Schaumstoffe werden durch eine Kombination von speziellen hydrophilen und hydrophoben Poly etherolen hergestellt. These foams are prepared etherolen by a combination of specific hydrophilic and hydrophobic poly.

DE-A-41 29 666 verwendet miteinander unverträgliche Polyole, die sich langsam entmischen. DE-A-41 29 666 uses each other incompatible polyols which segregate slowly. Durch hohe Anteile an ethylenoxid reichen Polyolen und Einhaltung von Kennzahlen < 80 läßt sich eine adhäsive Teppichoberfläche erzielen. Through high levels of ethylene oxide rich polyols and compliance ratios <80 is an adhesive carpet surface can be achieved. Schalldämpfende Eigen schaften lassen sich nach DE-A-400 10 444 durch eine Kombination von Polyester- und Polyetheralkoholen erreichen. Sound absorbing properties inherent can be achieved by a combination of polyester and polyether alcohols in accordance with DE-A-400 10 444. Auch diese Systeme neigen sehr stark zur Entmischung. These systems have a strong tendency to separate.

Die im Stand der Technik aufgeführten Erfindungen gestatten durchaus die Herstellung von Weichschaumstoffen mit schall absorbierenden Eigenschaften, wobei es bei dieser Stoffklasse noch ein beachtliches Verbesserungspotential im Hinblick auf die Eigenschaften und die Verarbeitbarkeit gibt. The inventions listed in the prior art allow quite the production of flexible foams with sound-absorbing properties, there is still considerable potential for improvement in terms of the properties and processability in this class.

Der Erfindung lag die Aufgabe zugrunde, schallabsorbierende, leicht zu verarbeitende weiche PUR-Schaumstoffe mit einem Verlustfaktor < 0,2 zu erzeugen. The invention had the object to produce sound-absorbing, easy to work with soft polyurethane foams with a loss factor <0.2.

Die Aufgabe wurde dadurch gelöst, daß zur Herstellung der PUR- Weichschaumstoffe ein Polyetherolgemisch (b), bestehend aus The object is achieved in that for the production of polyurethane foams, a polyetherol mixture (b) consisting of

  • 1. mindestens einem zwei- bis achtfunktionellen Polyetherol auf der Basis von Ethylenoxid und Propylenoxid und gegebenenfalls Butylenoxid mit einer OH-Zahl von 20 bis 80 mg KOH/g und einem Anteil an primären OH-Gruppen größer als 50% und 1. at least one two- to eight-functional polyetherol based on ethylene oxide and propylene oxide and, optionally, butylene oxide with an OH number of 20 to 80 mg KOH / g and a proportion of primary OH groups greater than 50% and
  • 2. mindestens einem Ricinusölpolyetherol auf der Basis Ethylen oxid und gegebenenfalls Propylenoxid und/oder Butylenoxid mit einer OH-Zahl von 50 bis 160 mg KOH/g 2. at least one Ricinusölpolyetherol based on ethylene oxide and optionally propylene oxide and / or butylene oxide with an OH number of 50 to 160 mg KOH / g

eingesetzt wird. is used.

Gegenstand der Erfindung ist somit ein Verfahren zur Her stellung von PUR-Weichschaumstoffen mit schalldämpfenden Eigen schaften durch Umsetzung von organischen und/oder rriodifizierten organischen Polyisocyanaten (a) mit einem Polyetherolgemisch (b) und gegebenenfalls weiteren gegenüber Isocyanaten reaktive Wasserstoffatome aufweisenden Verbindungen (c) in Gegenwart von Wasser und/oder anderen Treibmitteln (d), Katalysatoren (e) und gegebenenfalls weiteren Hilfs- und Zusatzstoffen (f), das dadurch gekennzeichnet ist, daß das Polyetherolgemisch (b) besteht aus The invention thus relates to a process for the preparation position of PUR foams having sound-deadening self-unions by reacting organic and / or rriodifizierten organic polyisocyanates (a) with a polyetherol mixture (b) and optionally other isocyanate-reactive hydrogen atoms containing compounds (c) in the presence of water and / or other blowing agents (d), catalysts (s) and optionally further auxiliaries and additives (f), which is characterized in that the polyetherol mixture (b) consists of

  • 1. mindestens einem zwei- bis achtfunktionellen Polyetherol auf der Basis von Ethylenoxid und Propylenoxid und gegebenenfalls Butylenoxid mit einer OH-Zahl von 20 bis 80 mg KOH/g und einem Anteil an primären OH-Gruppen größer als 50% und 1. at least one two- to eight-functional polyetherol based on ethylene oxide and propylene oxide and, optionally, butylene oxide with an OH number of 20 to 80 mg KOH / g and a proportion of primary OH groups greater than 50% and
  • 2. mindestens einem Ricinusölpolyetherol auf der Basis Ethylen oxid und gegebenenfalls Propylenoxid und/oder Butylenoxid mit einer OH-Zahl von 50 bis 160 mg KOH/g. 2 on the basis of at least one oxide Ricinusölpolyetherol ethylene and optionally propylene oxide and / or butylene oxide with an OH number of 50 to 160 mg KOH / g.

Gegenstände der Erfindung sind weiterhin die nach diesem Ver fahren hergestellten PUR-Weichschaumstoffe mit schalldämpfenden Eigenschaften sowie deren Verwendung als Dämpfungsmaterial. Objects of the invention are further the drive produced by this Ver PUR foams having sound-deadening properties, and their use as a damping material.

Wir fanden bei unseren Untersuchungen überraschenderweise, daß durch Einsatz des erfindungsgemäßen speziellen Polyetherol gemisches es möglich ist, weiche gut schalldämpfende PUR-Schaum stoffe herzustellen, die leicht zu verarbeiten sind und einen hohen Verlustfaktor von < 0,2, vorzugsweise 0,3 bis 0,45 auf weisen. We found in our investigations, surprisingly, that it is possible through the use of special Polyetherol inventive mixture used to manufacture soft good sound-absorbing polyurethane foam materials that are easy to process and a high loss factor of <0.2, preferably 0.3 to 0 exhibit 45th

Zu den erfindungsgemäß im Polyolgemisch eingesetzten Komponenten ist folgendes auszuführen: To the present invention used in the polyol component can run:
Der Bestandteil (b1) besteht aus mindestens einem zwei- bis achtfunktionellen Polyetherol auf der Basis von Ethylenoxid und Propylenoxid und gegebenenfalls Butylenoxid mit einer OH-Zahl von 20 bis 80 mg KOH/g und einem Anteil an primären OH-Gruppen größer als 50%, vorzugsweise größer als 70%. The component (b1) comprises at least one two- to eight-functional polyetherol based on ethylene oxide and propylene oxide and, optionally, butylene oxide with an OH number of 20 to 80 mg KOH / g and a proportion of primary OH groups greater than 50%, preferably greater than 70%.

Beispielsweise kommen hierfür in Betracht Polyetherole basierend auf Glycerin oder Trimethylolpropan als Starter. For example, come into consideration for this polyetherols based on glycerol or trimethylolpropane as a starter. Sie weisen in der Regel eine Blockstruktur auf. They have a block structure in general. Vorzugsweise werden Polyether ole mit einem Ethylenoxidendcap eingesetzt, besonders bevorzugt werden Polyetherole auf Basis von Glycerin oder Trimethylolpropan mit einem Polypropylenoxidblock und einem Ethylenoxidendcap. Preferably polyether oils are used with a Ethylenoxidendcap are particularly preferred polyether polyols based on glycerol or trimethylolpropane with a polypropylene oxide and a Ethylenoxidendcap.

Die Komponente b1) kommt vorzugsweise in Anteilen von 20 bis 70 Gew.-%, vorzugsweise von 30 bis 60 Gew.-%, jeweils bezogen auf das Gesamtgewicht der Komponente b), zum Einsatz. Component b1) is preferably used in proportions of 20 to 70 wt .-%, preferably from 30 to 60 wt .-%, each based on the total weight of component b), are used.

Der Bestandteil (b2) besteht aus mindestens einem Ricinusölpoly etherol auf der Basis Ethylenoxid und gegebenenfalls Propylenoxid und/oder Butylenoxid mit einer OH-Zahl von 50 bis 160 mg KOH/g, vorzugsweise von 80 bis 160 mg KOH/g. The component (b2) comprises at least one Ricinusölpoly etherol based on ethylene oxide and optionally propylene oxide and / or butylene oxide with an OH number of 50 to 160 mg KOH / g, preferably from 80 to 160 mg KOH / g.

Das Ricinusölpolyetherol wird durch übliche Addition von Ethylen oxid und gegebenenfalls Propylenoxid und/oder Butylenoxid an Ricinusöl hergestellt. The Ricinusölpolyetherol oxide is by conventional addition of ethylene and optionally propylene oxide and / or butylene oxide prepared with castor oil. Besonders bevorzugt wird ein Additions produkt von Ethylenoxid an Ricinusöl. an addition is especially preferred product of ethylene oxide with castor oil.

Die Komponente b2) kommt vorzugsweise in Anteilen von 1 bis 70 Gew.-%, besonders bevorzugt von 10 bis 40 Gew.-%, bezogen auf das Gesamtgewicht der Komponente b), zum Einsatz. Component b2) is preferably used in proportions of from 1 to 70 wt .-%, particularly preferably from 10 to 40 wt .-%, based on the total weight of component b), are used.

Dem Polyetherolgemisch (b) kann gegebenenfalls reines Ricinusöl (b3) zugegeben werden. The polyetherol (b) pure castor oil (b3) may be optionally added.

Falls reines Ricinusöl zum Einsatz kommt, so wird es vorzugs weise in Anteilen von 0,5 bis 10 Gew.-%, besonders bevorzugt von 0,5 bis 6 Gew.-%, jeweils bezogen auf das Gesamtgewicht der Komponente b), verwendet. If pure castor oil is used, it is preferential, in proportions of 0.5 to 10 wt .-%, particularly preferably from 0.5 to 6 wt .-%, each based on the total weight of component b), is used.

Dem Polyetherolgemisch (b) kann weiterhin gegebenenfalls der Be standteil (b4), bestehend aus einem oder mehreren Polyetherolen auf der Basis von Propylenoxid und gegebenenfalls Ethylenoxid mit einem Anteil an primären OH-Gruppen von weniger als 20%, zugegeben werden. The polyetherol mixture (b) may further optionally the Be stand part (b4) consisting of one or more polyether polyols based on propylene oxide and optionally ethylene oxide with a proportion of primary OH groups of less than 20%, are added.

Beispielsweise kommen hierfür in Betracht Polyetherole basierend auf Wasser, Propylenglykol oder Ethylenglykol als Starter. For example, come into consideration for this polyetherols based on water, propylene glycol or ethylene glycol as the starter. Sie weisen üblicherweise eine Blockstruktur auf. They usually have a block structure. Vorzugsweise werden Polyetherole mit einer Propylenoxidkette eingesetzt. Preferably, polyether polyols are used having a propylene oxide chain. In einer besonders bevorzugten Verfahrensvariante wird als b4) ein Poly propylenglykol eingesetzt. In a particularly preferred process variant, a poly propylene glycol is used as b4).

Falls eine Komponente b4) zum Einsatz kommt, so wird sie vorzugs weise in Anteilen von 0,5 bis 7 Gew.-%, vorzugsweise von 0,5 bis 5 Gew.-%, jeweils bezogen auf das Gesamtgewicht der Komponente b), verwendet. If a component b4) is used, it is preferential, in levels of from 0.5 to 7 wt .-%, preferably from 0.5 to 5 wt .-%, each based on the total weight of component b), is used ,

Die genannten Polyetherole werden nach bekannten Verfahren, wie sie beispielsweise weiter unten beschrieben sind, hergestellt. The polyetherols above are prepared by known methods as are described for example below.

Die erfindungsgemäßen PUR-Weichschaumstoffe mit schalldämpfenden Eigenschaften werden durch Umsetzung von organischen und/oder modifizierten organischen Polyisocyanaten (a) mit dem oben be schriebenen Polyetherolgemisch (b) und gegebenenfalls weiteren gegenüber Isocyanaten reaktive Wasserstoffatome aufweisenden Ver bindungen (c) in Gegenwart von Wasser und/oder anderen Treib mitteln (d), Katalysatoren (e) und gegebenenfalls weiteren Hilfs- und Zusatzstoffen (f) hergestellt. The inventive polyurethane foams having sound-deadening properties by reacting organic and / or modified organic polyisocyanates (a) with the above-be signed polyetherol mixture (b) and optionally further Ver isocyanate-reactive hydrogen atoms having bonds (C) in the presence of water and / or other blowing agents (d), catalysts (s) and optionally further auxiliaries and additives (f) was prepared.

Zu den verwendbaren weiteren Ausgangskomponenten ist im einzelnen folgendes auszuführen: Among the usable further starting components is to be performed in particular:
Als organische und/oder modifizierte organische Polyisocyanate (a) kommen die an sich bekannten aliphatischen, cycloali phatischen, araliphatischen und vorzugsweise aromatischen mehrwertigen Isocyanate in Frage. Suitable organic and / or modified organic polyisocyanates (a) are the conventional aliphatic, cycloali phatic, araliphatic and preferably aromatic polyfunctional isocyanates are also suitable.

Im einzelnen seien beispielhaft genannt: Alkylendiisocyanate mit 4 bis 12 Kohlenstoffatomen im Alkylenrest, wie 1,12-Dodecandi isocyanat, 2-Ethyl-tetramethylendiisocyanat-1,4, 2-Methylpenta methylendiisocyanat-1,5, Tetramethylendiisocyanat-1,4 und vor zugsweise Hexamethylendiisocyanat-1,6, cycloaliphatische Diiso cyanate, wie Cyclohexan-1,3- und -1,4-diisocyanat sowie beliebige Gemische dieser Isomeren, 1-Isocyanato-3,3,5-trimethyl-5-iso cyanatomethylcyclohexan (IPDI), 2,4- und 2,6-Hexahydrotoluylen diisocyanat sowie die entsprechenden Isomerengemische, 4,4'-, 2,2'- und 2,4'-Dicyclohexylmethandiisocyanat sowie die ent sprechenden Isomerengemische, und vorzugsweise aromatische Di- und Polyisocyanate, wie z. 2-methyl pentamethylene alkylene diisocyanates having from 4 to 12 carbon atoms in the alkylene radical, such as 1,12-dodecanedioic isocyanate, 2-ethyl-tetramethylenediisocyanate-1,4, diisocyanate-1,5, tetramethylene diisocyanate-1,4 and most preferably: The following may be exemplified hexamethylene 1,6-diisocyanate, cycloaliphatic diiso cyanates such as cyclohexane-1,3- and -1,4-diisocyanate and any mixtures of these isomers, 1-isocyanato-3,3,5-trimethyl-5-iso cyanatomethylcyclohexan (IPDI), 2,4- and 2,6-hexahydrotoluene diisocyanate and the corresponding isomer mixtures, 4,4'-, 2,2'- and 2,4'-dicyclohexylmethane diisocyanate and the ent speaking isomer mixtures, and preferably aromatic diisocyanates and polyisocyanates such , B. 2,4- und 2,6-Toluylendiisocyanat und die entsprechenden Isomerengemische, 4,4'-, 2,4'- und 2,2'-Diphenylmethandiisocyanat und die entsprechenden Isomeren gemische, Mischungen aus 4,4'- und 2,2'-Diphenylmethandiiso cyanaten, Polyphenylpolymethylenpolyisocyanate, Mischungen aus 4,4'-, 2,4'- und 2,2'-Diphenylmethandiisocyanaten und Poly phenylpolymethylenpolyisocyanaten (Roh-MDI) und Mischungen aus Roh-MDI und Toluylendiisocyanaten. B. 2,4- and 2,6-diisocyanate and the corresponding isomer mixtures, 4,4'-, 2,4'- and 2,2'-diphenylmethane diisocyanate and the corresponding isomeric mixtures, mixtures of 4,4'- and 2 , 2'-diphenylmethane cyanates, polyphenyl polymethylene polyisocyanates, mixtures of diphenylmethane 4,4'-, 2,4'- and 2,2'-diphenylmethane diisocyanates, and poly phenylpolymethylenpolyisocyanaten (crude MDI) and mixtures of crude MDI and tolylene diisocyanates. Die organischen Di- und Poly isocyanate können einzeln oder in Form ihrer Mischungen ein gesetzt werden. The organic di- and poly isocyanates can be a set individually or in the form of their mixtures. Besonders bevorzugt werden Gemische aus Poly phenylpolymethylenpolyisocyanat mit MDI, wobei vorzugsweise der Anteil an 2,4'-MDI < 30 Gew.-% beträgt. Particularly preferred are mixtures of poly phenylpolymethylenpolyisocyanat with MDI, preferably wherein the proportion of 2,4'-MDI <30 wt .-% by weight.

Häufig werden auch sogenannte modifizierte mehrwertige Iso cyanate, dh Produkte, die durch chemische Umsetzung organischer Di- und/oder Polyisocyanate erhalten werden, verwendet. Frequently, modified polyfunctional iso cyanate are, ie products which are obtained by chemical reaction of organic di- and / or polyisocyanates. Beispiel haft genannt seien Ester-, Harnstoff-, Biuret-, Allophanat-, Carbodiimid-, Isocyanurat-, Uretdion- und/oder Urethangruppen enthaltende Di- und/oder Polyisocyanate. Specific examples are ester, urea, biuret, allophanate, carbodiimide, isocyanurate, uretdione and / or urethane-containing di- and / or polyisocyanates. Im einzelnen kommen bei spielsweise in Betracht: modifiziertes 4,4'-Diphenylmethandiiso cyanat, modifizierte 4,4'- und 2,4'-Diphenylmethandiisocyanat mischungen, modifiziertes Roh-MDI oder 2,4- bzw. 2,6-Toluylen diisocyanat, Urethangruppen enthaltende organische, vorzugsweise aromatische Polyisocyanate mit NCO-Gehalten von 43 bis 15 Gew.-%, vorzugsweise von 31 bis 21 Gew.-%, bezogen auf das Gesamtgewicht, beispielsweise Umsetzungsprodukte mit niedermolekularen Diolen, Triolen, Dialkylenglykolen, Trialkylenglykolen oder Polyoxy alkylenglykolen mit Molekulargewichten bis 6000, insbesondere mit Molekulargewichten bis 1500, wobei diese als Di- bzw. Poly oxyalkylenglykole einzeln oder als Gemische eingesetzt werden können. In particular are used in play are: modified 4,4'-diphenylmethane diisocyanate, modified diphenylmethane 4,4'- and 2,4'-diphenylmethane diisocyanate mixtures diisocyanate modified raw MDI or tolylene 2,4- or 2,6-, urethane-containing organic, preferably, aromatic polyisocyanates having NCO contents of from 43 to 15 wt .-%, preferably from 31 to 21 wt .-%, based on the total weight, for example, reaction products with low molecular weight diols, triols, dialkylene glycols, trialkylene or polyoxy alkylene glycols with molecular weights up to 6000, in particular having molecular weights up to 1500, said oxyalkylene individually as di- and poly-, or may be used as mixtures. Beispielsweise genannt seien: Diethylen-, Dipropylen glykol, Polyoxyethylen-, Polyoxypropylen- und Polyoxypropylen polyoxyethenglykole, -triole und/oder -tetrole. Named as examples are: diethylene glycol, dipropylene glycol, polyoxyethylene, polyoxypropylene and polyoxypropylene polyoxyethenglykole, triols and / or tetrols. Geeignet sind auch NCO-Gruppen enthaltende Prepolymere mit NCO-Gehalten von 25 bis 3,5 Gew.-%, vorzugsweise von 21 bis 14 Gew.-%, bezogen auf das Gesamtgewicht, hergestellt aus den nachfolgend beschriebenen Polyester- und/oder vorzugsweise Polyetherpolyolen und 4,4'-Di phenylmethandiisocyanat, Mischungen aus 2,4'- und 4,4'-Diphenyl methandiisocyanat, 2,4- und/oder 2,6-Toluylendiisocyanaten oder Roh-MDI. Also suitable are NCO-containing prepolymers having NCO contents of from 25 to 3.5 wt .-%, preferably from 21 to 14 wt .-%, based on the total weight made of the below-described polyester and / or preferably polyether polyols and 4,4'-di- phenylmethane, diisocyanate, mixtures of 2,4'- and 4,4'-diphenyl diisocyanate, 2,4- and / or 2,6-tolylene diisocyanates or crude MDI. Bewährt haben sich ferner flüssige, Carbodiimidgruppen und/oder Isocyanuratringe enthaltende Polyisocyanate mit NCO- Gehalten von 43 bis 15, vorzugsweise 31 bis 21, Gew.-%, be zogen auf das Gesamtgewicht, z. further have proven containing polyisocyanates having NCO contents 43-15 liquid, carbodiimide groups and / or isocyanurate rings, preferably 31 to 21 wt .-%, be subjected to the total weight, eg. B. auf Basis von 4,4'-, 2,4'- und/oder 2,2'-Diphenylmethandiisocyanat und/oder 2,4- und/oder 2,6-Toluylendiisocyanat. Example based on 4,4'-, 2,4'- and / or 2,2'-diphenylmethane diisocyanate and / or 2,4- and / or 2,6-diisocyanate.

Die modifizierten Polyisocyanate können miteinander oder mit unmodifizierten organischen Polyisocyanaten, wie z. The modified polyisocyanates can, together or with unmodified organic polyisocyanates such. B. 2,4'-, 4,4'-Diphenylmethandiisocyanat, Roh-MDI, 2,4- und/oder 2,6-Toluylendiisocyanat, gemischt werden. B. 2,4 ', 4,4'-diphenylmethane diisocyanate, crude MDI, 2,4- and / or 2,6-tolylene diisocyanate, are mixed.

Besonders bewährt haben sich als organische Polyisocyanate und kommen daher vorzugsweise zur Anwendung: Mischungen aus Toluylen diisocyanaten und Roh-MDI oder Mischungen aus modifizierten Urethangruppen enthaltenden organischen Polyisocyanaten mit einem NCO-Gehalt von 33,6 bis 15 Gew.-%, insbesondere solche auf Basis von Toluylendiisocyanaten, 4,4'-Diphenylmethandiiso cyanat, Diphenylmethandiisocyanat-Isomerengemischen oder Roh-MDI und insbesondere Roh-MDI mit einem Diphenylmethandiisocyanat- Isomerengehalt von 30 bis 80 Gew.-%. have proved particularly suitable as organic polyisocyanates and are therefore preferably used: tolylene diisocyanates, mixtures of and crude MDI or mixtures of modified organic polyisocyanates containing urethane groups and having an NCO content of 33.6 to 15 wt .-%, particularly those based on of toluene diisocyanates, 4,4'-diphenylmethane diisocyanate, diphenylmethane diisocyanate isomer mixtures or crude MDI, in particular crude MDI having a diphenylmethane diisocyanate isomer content of from 30 to 80 wt .-%.

Neben dem oben beschriebenen erfindungsgemäßen Polyetherolgemisch (b) werden gegebenenfalls weitere gegenüber Isocyanaten reaktive Wasserstoffatome aufweisende Verbindungen (c) eingesetzt. In addition to the above-described inventive polyetherol mixture (b) further isocyanate-reactive hydrogen atoms containing compounds (c) are optionally used.

Hierfür werden vorrangig Verbindungen mit mindestens zwei reak tiven Wasserstoffatomen verwendet. For this, compounds having at least two reac tive hydrogen atoms are used first. Dabei werden zweckmäßigerweise solche mit einer Funktionalität von 2 bis 8, vorzugsweise 2 bis 3, und einem Molekulargewicht von 300 bis 8000, vorzugsweise von 300 bis 6000 und insbesondere 1000 bis 5000, verwendet. In this case are expediently those having a functionality of 2 to 8, preferably 2 to 3 and a molecular weight of 300 to 8000, preferably from 300 to 6000, in particular 1000 to 5000, is used.

Erfindungsgemäß bevorzugt eingesetzt werden Polyole, insbesondere Polyetherpolyole. According to the invention preference is given to polyols, in particular polyether polyols. Daneben können beispielsweise auch Polyether polyamine und/oder weitere Polyole, ausgewählt aus der Gruppe der Polyesterpolyole, Polythioetherpolyole, Polyesteramide, hydroxyl gruppenhaltigen Polyacetale und hydroxylgruppenhaltigen ali phatischen Polycarbonate oder Mischungen aus mindestens zwei der genannten Polyole verwendet werden. In addition, polyethers can, for example, polyamines and / or more polyols selected from the group of polyester polyols, polythioether polyols, polyesteramides, hydroxyl group-containing polyacetals and hydroxyl-ali phatic polycarbonates or mixtures are used of at least two of said polyols. Die Hydroxylzahl der Polyhydroxylverbindungen beträgt dabei in aller Regel 20 bis 80 und vorzugsweise 28 bis 56. The hydroxyl number of the polyhydroxyl compounds is generally from 20 to 80 and preferably 28 to 56th

Die in den Komponenten (b) und (c) verwendeten Polyetherpolyole werden nach bekannten Verfahren, beispielsweise durch anionische Polymerisation mit Alkalihydroxiden, wie z. The polyether polyols in the components (b) and (c) used according to known methods, for example by anionic polymerization with alkali hydroxides such. B. Natrium- oder Kaliumhydroxid, oder Alkalialkoholaten, wie z. Sodium or potassium hydroxide, or alkali metal alkoxides such. B. Natriummethylat, Natrium- oder Kaliumethylat oder Kaliumisopropylat als Kata lysatoren und unter Zusatz mindestens eines Startermoleküls, das 2 bis 8, vorzugsweise 2 bis 3, reaktive Wasserstoffatome gebunden enthält, oder durch kationische Polymerisation mit Lewissäuren, wie Antimonpentachlorid, Borfluorid-Etherat ua, oder Bleich erde, (als Katalysatoren aus einem oder mehreren Alkylenoxiden mit 2 bis 4 Kohlenstoffatomen im Alkylenrest hergestellt. Für spezielle Einsatzzwecke können auch monofunktionelle Starter in den Polyetheraufbau eingebunden werden. Sodium methylate, sodium or potassium ethoxide or potassium isopropoxide catalysts as Kata and with addition of at least one initiator molecule containing 2 to 8, preferably 2 to 3 reactive hydrogen atoms, or by cationic polymerization with Lewis acids such as antimony pentachloride, boron fluoride etherate, etc., or bleaching earth, (as catalysts prepared in the alkylene group of one or more alkylene oxides having 2 to 4 carbon atoms. For special applications, monofunctional initiators can be incorporated into the polyether.

Geeignete Alkylenoxide sind beispielsweise Tetrahydrofuran, 1,3-Propylenoxid, 1,2- bzw. 2,3-Butylenoxid, Styroloxid und vorzugsweise Ethylenoxid und 1,2-Propylenoxid. Suitable alkylene oxides are, for example, tetrahydrofuran, 1,3-propylene oxide, 1,2- or 2,3-butylene oxide, styrene oxide and preferably ethylene oxide and 1,2-propylene oxide. Die Alkylenoxide können einzeln, alternierend nacheinander oder als Mischungen verwendet werden. The alkylene oxides may be used individually, alternately in succession or as mixtures.

Als Startermoleküle kommen beispielsweise in Betracht: Wasser, organische Dicarbonsäuren, wie Bernsteinsäure, Adipinsäure, Phthalsäure und Terephthalsäure, aliphatische und aromatische, gegebenenfalls N-mono-, N,N- und N,N'-dialkylsubstituierte Diamine mit 1 bis 4 Kohlenstoffatomen im Alkylrest, wie gegebenenfalls mono- und dialkylsubstituiertes Ethylendiamin, Diethylentriamin, Triethylentetramin, 1,3-Propylendiamin, 1,3- bzw. 1,4-Butylendiamin, 1,2-, 1,3-, 1,4-, 1,5- und 1,6-Hexa methylendiamin, Phenylendiamin, 2,3-, 2,4- und 2,6-Toluylendiamin und 4,4', 2,4'- und 2,2'-Diaminodiphenylmethan. Possible starter molecules are, for example: water, organic dicarboxylic acids such as succinic acid, adipic acid, phthalic acid and terephthalic acid, aliphatic and aromatic, optionally N-mono-, N, N- and N, N'-dialkyl-substituted diamines having 1 to 4 carbon atoms in the alkyl radical such as unsubstituted or mono- and dialkyl-substituted ethylenediamine, diethylenetriamine, triethylenetetramine, 1,3-propylenediamine, 1,3- or 1,4-butylenediamine, 1,2-, 1,3-, 1,4-, 1,5- and 1,6-hexa methylenediamine, phenylenediamine, 2,3-, 2,4- and 2,6-toluenediamine and 4,4 ', 2,4'- and 2,2'-diaminodiphenylmethane. Als Starter moleküle kommen ferner in Betracht: Alkanolamine, wie z. molecules as a starter may be used are: alkanolamines such. B. Ethanolamin, N-Methyl- und N-Ethylethanolamin, Dialkanolamine, wie z. Ethanolamine, N-methyl- and N-ethylethanolamine, dialkanolamines such. B. Diethanolamin, N-Methyl- und N-Ethyldiethanolamin, und Trialkanolamine, wie z. As diethanolamine, N-methyl- and N-ethyldiethanolamine, and trialkanolamines such. B. Triethanolamin, und Ammoniak. As triethanolamine, and ammonia. Vorzugs weise verwendet werden mehrwertige, insbesondere zwei- und/oder dreiwertige Alkohole, wie Ethandiol, Propandiol-1,2 und -2,3, Diethylenglykol, Dipropylenglykol, Butandiol-1,4, Hexandiol-1,6, Glycerin, Trimethylolpropan, Pentaerythrit. Preference, polyhydric be used, in particular dihydric and / or trihydric alcohols such as ethanediol, propanediol-1,2 and -2,3, diethylene glycol, dipropylene glycol, 1,4-butanediol, 1,6-hexanediol, glycerol, trimethylolpropane, pentaerythritol , Insbesondere geeignet für den vorgeschlagenen Anwendungsfall sind Polyetherole auf Basis von Propylen- und/oder Ethylenoxid, gegebenenfalls auch Butylenoxid, die unter Verwendung von Ricinusöl als Starter hergestellt werden. Particularly suitable for the proposed application are polyetherols based on propylene and / or ethylene oxide, optionally also butylene, which are prepared using castor oil as a starter.

Als Polyetherpolyole eignen sich ferner polymermodifizierte Polyetherpolyole, vorzugsweise Pfropfpolyetherpolyole, ins besondere solche auf Styrol- und/oder Acrylnitrilbasis, die durch in situ Polymerisation von Acrylnitril, Styrol oder vorzugsweise Mischungen aus Styrol und Acrylnitril, z. As polyether polyols are polymer-modified polyether polyols, preferably graft polyether polyols, in particular those based on styrene and / or acrylonitrile, which are prepared by in situ polymerization of acrylonitrile, styrene or preferably mixtures of styrene and acrylonitrile, eg. B. im Gewichtsverhältnis 90 : 10 bis 10 : 90, vorzugsweise 70 : 30 bis 30 : 70, zweckmäßigerweise in den vorgenannten Polyetherpolyolen analog den Angaben der deutschen Patentschriften 11 11 394, 12 22 669 (US 3304273, 3383351, 3523093), 11 52 536 (GB 1040452) und 11 52 537 (GB 987618) hergestellt werden, sowie Polyetherpolyol dispersionen, die als disperse Phase, üblicherweise in einer Menge von 1 bis 50 Gew.-%, vorzugsweise 2 bis 25 Gew.-%, ent halten: z. B. in the weight ratio 90: 10 to 10: 90, preferably 70: 30 to 30: 70, advantageously in the abovementioned polyether polyols analogous to the specifications of German Patents 11 11 394, 12 22 669 (US 3,304,273, 3,383,351, 3,523,093), 11 52 536 (GB 1040452) and 11 52 537 (GB 987 618) are prepared, and polyether polyol dispersions which comprise as the disperse phase, usually in an amount of 1 to 50 wt .-%, preferably 2 to 25 wt .-%, keep ent: z. B. Polyharnstoffe, Polyhydrazide, tert.-Aminogruppen gebunden enthaltende Polyurethane und/oder Melamin und die z. B. polyureas, polyhydrazides, polyurethanes containing bound tert-amino and / or melamine and z. B. beschrieben werden in EP-B-011752 (US 4304708), US-A-4374209 und DE-A-32 31 497. As described in EP-B-011,752 (US 4,304,708), US-A-4,374,209 and DE-A-32 31 497th

Die Polyetherpolyole können einzeln oder in Form von Mischungen verwendet werden. The polyether polyols can be used singly or in the form of mixtures.

Geeignete Polyesterpolyole können beispielsweise aus organischen Dicarbonsäuren mit 2 bis 12 Kohlenstoffatomen, vorzugsweise ali phatischen Dicarbonsäuren mit 4 bis 6 Kohlenstoffatomen, mehr wertigen Alkoholen, vorzugsweise Diolen, mit 2 bis 12 Kohlen stoffatomen, vorzugsweise 2 bis 6 Kohlenstoffatomen, nach üblichen Verfahren hergestellt werden. Suitable polyester polyols can be prepared from 2 to 6 carbon atoms by conventional methods, for example, from organic dicarboxylic acids having 2 to 12 carbon atoms, preferably ali phatic dicarboxylic acids containing 4 to 6 carbon atoms, polyhydric alcohols, preferably diols, atoms of 2 to 12 carbons, preferably. Üblicherweise werden die organischen Polycarbonsäuren und/oder -derivate und mehrwertigen Alkohole, vorteilhafterweise im Molverhältnis von 1 : 1 bis 1,8, vorzugsweise von 1 : 1,05 bis 1,2, katalysatorfrei oder vorzugs weise in Gegenwart von Veresterungskatalysatoren, zweckmäßiger weise in einer Atmosphäre aus Inertgas, wie z. Usually, the organic polycarboxylic acids and / or derivatives and polyhydric alcohols, advantageously in a molar ratio of 1: 1 to 1.8, preferably from 1: 1.05 to 1.2, a catalyst or preference, in the presence of esterification catalysts, expediently in an atmosphere of inert gas such. B. Stickstoff, Kohlenmonoxid, Helium, Argon ua, in der Schmelze bei Tempera turen von 150 bis 250°C, vorzugsweise 180 bis 220°C, gegebenen falls unter vermindertem Druck bis zu der gewünschten Säurezahl, die vorteilhafterweise kleiner als 10, vorzugsweise kleiner als 2 ist, polykondensiert. For example, nitrogen, carbon monoxide, helium, argon, etc., in the melt at tempera tures from 150 to 250 ° C, preferably 180 to 220 ° C, where appropriate under reduced pressure until the desired acid number which is advantageously less than 10, preferably less 2 is polycondensed.

Die Polyurethanschaumstoffe können ohne oder unter Mitverwendung von Kettenverlängerungs- und/oder Vernetzungsmitteln hergestellt werden, wobei diese in der Regel aber nicht erforderlich sind. The polyurethane foams can be produced with or without concomitant use of chain extenders and / or crosslinking agents, which are not usually required. Als Kettenverlängerungs- und/oder Vernetzungsmittel verwendet werden Diole und/oder Triole mit Molekulargewichten kleiner als 400, vorzugsweise 60 bis 300. In Betracht kommen beispielsweise aliphatische, cycloaliphatische und/oder araliphatische Diole mit 2 bis 14, vorzugsweise 4 bis 10 Kohlenstoffatomen, wie z. As chain extenders and / or crosslinkers used are diols and / or triols having molecular weights of less than 400, preferably 60 to 300. Examples are aliphatic, cycloaliphatic and / or araliphatic diols having 2 to 14, preferably 4 to 10 carbon atoms are, for , B. Ethylenglykol, Propandiol-1,3, Decandiol-1,10, o-, m-, p-Di hydroxycyclohexan, Diethylenglykol, Dipropylenglykol und vorzugs weise Butandiol-1,4, Hexandiol-1,6 und Bis-(2-hydroxyethyl)- hydrochinon, Triole, wie 1,2,4- und 1,3,5-Trihydroxycyclohexan, Triethanolamin, Diethanolamin, Glycerin und Trimethylolpropan und niedermolekulare hydroxylgruppenhaltige Polyalkylenoxide auf Basis Ethylen- und/oder 1,2-Propylenoxid und den vorgenannten Diolen und/oder Triolen als Startermoleküle. For example, ethylene glycol, propanediol-1,3, decanediol-1,10, o-, m-, p-di hydroxycyclohexane, diethylene glycol, dipropylene glycol and preference as butanediol-1,4, hexanediol-1,6 and bis- (2- hydroxyethyl) - hydroquinone, triols such as 1,2,4- and 1,3,5-trihydroxycyclohexane, triethanolamine, diethanolamine, glycerol and trimethylolpropane and low molecular weight hydroxyl-containing polyalkylene oxides based on ethylene oxide and / or 1,2-propylene oxide and the abovementioned diols and / or triols as starter molecules.

Sofern zur Herstellung der Polyurethanschaumstoffe Ketten verlängerungsmittel, Vernetzungsmittel oder Mischungen davon Anwendung finden, kommen diese zweckmäßigerweise in einer Menge bis zu 5 Gew.-%, bezogen auf das Gewicht der Polyolverbindungen, zum Einsatz. The following is provided for the preparation of the polyurethane foams chain extenders, crosslinking agents or mixtures thereof are employed, they are advantageously used in an amount up to 5 wt .-%, based on the weight of the polyol compounds.

Als Treibmittel (d) können die aus der Polyurethanchemie all gemein bekannten Fluorchlorkohlenwasserstoffe (FCKW) sowie hoch- und/oder perfluorierte Kohlenwasserstoffe verwendet werden. As blowing agent (d) may be selected from polyurethane chemistry, all public known chlorofluorocarbons (CFCs) as well as high and / or perfluorinated hydrocarbons are used. Der Einsatz dieser Stoffe wird jedoch aus ökologischen Gründen stark eingeschränkt bzw. ganz eingestellt. The use of these substances is greatly restricted for environmental reasons or completely stopped. Neben den HFCKW und HFKW bieten sich insbesondere aliphatische und/oder cycloaliphatische Kohlenwasserstoffe, insbesondere Pentan und Cyclopentan, oder Acetale, wie z. In addition to HCFCs and HFCs in particular, aliphatic and / or cycloaliphatic hydrocarbons, in particular pentane and cyclopentane, or acetals such. B. Methylal, als Alternativtreibmittel an. B. methylal as alternative blowing agents. Diese physikalischen Treibmittel werden üblicherweise der Polyol komponente des Systems zugesetzt. These physical blowing agents are typically added to the polyol component of the system. Sie können jedoch auch in der Isocyanatkomponete oder als Kombination sowohl der Polyol komponente als auch der Isocyanatkomponente zugesetzt werden. However, they can also be added to the isocyanate component or as a combination of both the polyol component and the isocyanate component. Möglich ist auch ihre Verwendung zusammen mit hoch- und/oder perfluorierten Kohlenwasserstoffen in Form einer Emulsion der Polyolkomponente. They can also be used together with highly and / or perfluorinated hydrocarbons in form of an emulsion of the polyol component. Als Emulgatoren, sofern sie Anwendung finden, werden üblicherweise oligomere Acrylate eingesetzt, die als Seitengruppen Polyoxyalkylen- und Fluoralkanreste gebunden enthalten und einen Fluorgehalt von ungefähr 5 bis 30 Gew.-% aufweisen. As emulsifiers, if they are used, oligomeric acrylates are commonly used which contain bound as side groups polyoxyalkylene and fluoroalkane radicals, and have a fluorine content of approximately 5 to 30 wt .-%. Derartige Produkte sind aus der Kunststoffchemie hinreichend bekannt, z. Such products are well known from polymer chemistry, z. B. aus EP-A-351614. Example from EP-A-351,614th

Die eingesetzte Menge des Treibmittels bzw. der Treibmittel mischung liegt dabei bei 1 bis 25 Gew.-%, vorzugsweise 1 bis 15 Gew.-%, jeweils bezogen auf das Gesamtgewicht der Komponenten (b) bis (f). The amount of blowing agent or blowing agent mixture used is from 1 to 25 wt .-%, preferably 1 to 15 wt .-%, each based on the total weight of components (b) to (f).

Weiterhin ist es möglich und insbesondere im Weichschaum üblich, als Treibmittel der Polyolkomponente Wasser in einer Menge von 0,5 bis 15 Gew.-%, vorzugsweise 1 bis 5 Gew.-%, bezogen auf das Gesamtgewicht der Komponenten (b) bis (f) zuzusetzen. It is also possible, particularly in the flexible foam common to (as a blowing agent to the polyol component water in an amount of 0.5 to 15 wt .-%, preferably 1 to 5 wt .-%, based on the total weight of components (b) f ) add. Der Wasserzusatz kann in Kombination mit dem Einsatz der anderen beschriebenen Treibmittel erfolgen. The addition of water can be done in combination with the use of the other blowing agents described.

Als Katalysatoren (e) zur Herstellung von Polyurethanschaum stoffen werden insbesondere Verbindungen verwendet, die die Reaktion der reaktiven Wasserstoffatome, insbesondere hydroxyl gruppenenthaltender Verbindungen der Komponenten (b) und (c), mit den organischen, gegebenenfalls modifizierten Polyisocyanaten (a) stark beschleunigen. As catalysts (e) for the preparation of polyurethane foam materials are used especially compounds which inhibit the reaction of the reactive hydrogen atoms, particularly hydroxyl group-containing compounds of the components (b) and (c) with the organic, modified or unmodified polyisocyanates (a) is greatly accelerated. In Betracht kommen organische Metall verbindungen, vorzugsweise organische Zinnverbindungen, wie Zinn-(II)-salze von organischen Carbonsäuren, z. Organic metal are compounds, preferably organic tin compounds such as tin (II) salts of organic carboxylic acids, eg. B. Zinn-(II)- acetat, Zinn-(II)-octoat, Zinn-(II)-ethylhexoat und Zinn-(II)- laurat, und die Dialkylzinn-(IV)-salze von organischen Carbon säuren, z. As tin (II) - acetate, tin (II) octoate, tin ethylhexoate (II) and tin (II) - laurate, and the dialkyltin (IV) salts of organic carboxylic acids, eg. B. Dibutylzinndiacetat, Dibutylzinndilaurat, Dibutyl zinnmaleat und Dioctylzinndiacetat. As dibutyl tin dilaurate, dibutyl tin maleate and dioctyl. Die organischen Metaliver bindungen werden allein oder vorzugsweise in Kombination mit stark basischen Aminen eingesetzt. The organic Metaliver compounds are used alone or preferably in combination with strongly basic amines. Genannt seien beispielsweise Amidine, wie 2,3-Dimethyl-3,4,5,6-tetrahydropyrimidin, tertiäre Amine, wie Triethylamin, Tributylamin, Dimethylbenzylamin, N-Methyl-, N-Ethyl-, N-Cyclohexylmorpholin, N,N,N',N'-Tetra methylethylendiamn, N,N,N',N'-Tetramethylbutandiamin, N,N,N',N'- Tetramethyl-hexandiamin-1,6, Pentamethyldiethylentriamin, Tetra methyldiaminoethylether, Bis-(dimethylaminopropyl)-harnstoff, Dimethylpiperazin, 1,2-Dimethylimidazol, 1-Aza-bicyclo-(3,3,0)- octan und vorzugsweise 1,4-Diazabicyclo-(2,2,2)-octan, und Amino alkanolverbindungen, wie Triethanolamin, Triisopropanolamin, N-Methyl- und N-Ethyldiethanolamin und Dimethylethanolamin. Examples which may be mentioned are amidines such as 2,3-dimethyl-3,4,5,6-tetrahydropyrimidine, tertiary amines such as triethylamine, tributylamine, dimethylbenzylamine, N-methyl-, N-ethyl-, N-cyclohexylmorpholine, N, N, 'methylethylendiamn, N'-tetra, N, N, N', N, N'-tetramethylbutanediamine, N, N, N ', N'-tetramethyl-1,6-hexanediamine, pentamethyldiethylenetriamine, tetra methyldiaminoethylether, bis (dimethylaminopropyl) - urea, dimethylpiperazine, 1,2-dimethylimidazole, 1-aza-bicyclo- (3,3,0) - octane and preferably 1,4-diazabicyclo (2,2,2) -octane, and amino alcanol, such as triethanolamine, triisopropanolamine, N-methyl- and N-ethyldiethanolamine and dimethylethanolamine. Als Katalysatoren kommen ferner in Betracht: Tris-(dialkylamino alkyl)-s-hexahydrotriazine, insbesondere Tris-(N,N-dimethylamino propyl)-s-hexahydrotriazin, Tetraalkylammoniumhydroxide, wie Tetramethylammoniumhydroxid, Alkalihydroxid, wie Natriumhydroxid, und Alkalialkoholate, wie Natriummethylat und Kaliumisopropylat, sowie Alkalisalze von langkettigen Fettsäuren mit 10 bis 20 C-Atomen und gegebenenfalls seitenständigen OH-Gruppen. Other suitable catalysts are: tris (dialkylamino alkyl) -s-hexahydrotriazines, in particular tris (N, N-dimethylamino propyl) -s-hexahydrotriazine, tetraalkylammonium hydroxides such as tetramethylammonium hydroxide, alkali metal hydroxide such as sodium hydroxide and alkali metal alcoholates such as sodium methylate and potassium isopropoxide, and alkali metal salts of long chain fatty acids having 10 to 20 carbon atoms and possibly lateral OH groups. Vorzugsweise verwendet werden 0,001 bis 5 Gew.-%, insbesondere 0,05 bis 2 Gew.-% Katalysator bzw. Katalysatorkombination, bezogen auf das Gesamtgewicht der Komponenten (b) bis (f). Preferably used are 0.001 to 5 wt .-%, particularly 0.05 to 2 wt .-% of catalyst or catalyst combination, based on the total weight of components (b) to (f).

Der Reaktionsmischung zur Herstellung der erfindungsgemäßen schallabsorbierenden Polyurethanschaumstoffe können gegebenen falls noch weitere Hilfsmittel und/oder Zusatzstoffe (f) ein verleibt werden. The reaction mixture for preparing the sound-absorbing polyurethane foams of the invention may where appropriate further auxiliaries and / or additives (f) are a verleibt. Genannt seien beispielsweise oberflächenaktive Substanzen, Schaumstabilisatoren, Zellregler, Füllstoffe, Farb stoffe, Pigmente, Flammschutzmittel, Hydrolyseschutzmittel, fungistatische und bakteriostatisch wirkende Substanzen. Examples include surface-active substances, foam stabilizers, cell regulators, fillers, materials color, pigments, flame retardants, hydrolysis, fungistatic and bacteriostatic substances.

Geeignete Flammschutzmittel sind beispielsweise Trikresyl phosphat, Tris-(2-chlorethyl)phosphat, Tris-(2-chlorpropyl)- phosphat, Tetrakis-(2-chlorethyl)-ethylendiphosphat, Dimethyl methanphosphonat, Diethanolaminomethylphosphonsäurediethylester sowie handelsübliche halogenhaltige Flammschutzpolyole. Suitable flame retardants are, for example Trikresyl phosphate, tris (2-chloroethyl) phosphate, tris (2-chloropropyl) - phosphate, ethylene diphosphate tetrakis (2-chloroethyl), dimethyl methane phosphonate, diethanolaminomethylphosphonate and commercially available halogen-containing Flammschutzpolyole. Außer den bereits genannten halogensubstituierten Phosphaten können auch anorganische oder organische Flammschutzmittel, wie roter Phosphor, Aliumiumoxidhydrat, Antimontrioxid, Arsenoxid, Ammoniumpolyphosphat und Calciumsulfat, Blähgraphit oder Cyanur säurederivate, wie z. Apart from the abovementioned halogen-substituted phosphates, inorganic or organic flame retardants such as red phosphorus, Aliumiumoxidhydrat, antimony trioxide, arsenic oxide, ammonium polyphosphate and calcium sulfate, expandable graphite or cyanuric acid derivatives can such. B. Melamin, oder Mischungen aus mindestens zwei Flammschutzmitteln, wie z. For example, melamine, or mixtures of at least two flame retardants such. B. Ammoniumpolyphosphaten und Melamin sowie gegebenenfalls Maisstärke oder Ammoniumpoly phosphat, Melamin und Blähgraphit und/oder gegebenenfalls aromatische Polyester zum Flammfestmachen der Polyisocyanat polyadditionsprodukte verwendet werden. As ammonium polyphosphates and melamine and also, if appropriate, corn starch, or ammonium poly phosphate, melamine and expandable graphite and / or optionally be used aromatic polyesters to flameproof the polyisocyanate polyaddition products. Besonders wirksam erweisen sich dabei Zusätze an Melamin. Particularly effective prove Additions of melamine. Im allgemeinen hat es sich als zweckmäßig erwiesen, 5 bis 50 Gew.-Teile, vorzugsweise 5 bis 25 Gew.-Teile, der genannten Flammschutzmittel für jeweils 100 Gew.-Teile der Komponenten (b) bis (f) zu verwenden. In general, it has proved advantageous, 5 to 50 parts by weight, preferably to use 5 to 25 parts by weight, of the flame retardants mentioned per 100 parts by weight of components (b) to (f).

Als oberflächenaktive Substanzen kommen z. As surface-active substances, for coming. B. Verbindungen in Betracht, welche zur Unterstützung der Homogenisierung der Aus gangsstoffe dienen und gegebenenfalls auch geeignet sind, die Zellstruktur der Kunststoffe zu regulieren. As compounds which which serve to support homogenization of the transition from materials and are optionally also suitable for regulating the cell structure of the plastics. Genannt seien bei spielsweise Emulgatoren, wie die Natriumsalze der Ricinusöl sulfate oder Fettsäuren sowie Salze von Fettsäuren mit Aminen, z. such as the sodium salts of castor oil sulfates or fatty acids and salts of fatty acids with amines, for., may be mentioned at play, emulsifiers B. ölsaures Diethylamin, stearinsaures Diethanolamin, ricinol saures Diethanolamin, Salze von Sulfonsäuren, z. B. diethylamine oleate, diethanolamine stearate, ricinoleic acid diethanolamine, salts of sulfonic acids, such. B. Alkali- oder Ammoniumsalze von Dodecylbenzol- oder Dinaphthylmethandisulfon säure und Ricinolsäure; As alkali metal or ammonium salts of dodecylbenzene- or Dinaphthylmethandisulfon acid and ricinoleic acid; Schaumstabilisatoren, wie Siloxan oxalkylenmischpolymerisate und andere Organopoylsiloxane, oxethylierte Alkylphenole, oxethylierte Fettalkohole, Paraffin öle, Ricinusöl- bzw. Ricinolsäureester, Türkischrotöl und Erd nußöl, und Zellregler, wie Paraffine, Fettalkohole und Dimethyl polysiloxane. Foam stabilizers such as siloxane oxalkylenmischpolymerisate and other organopolysiloxanes, ethoxylated alkylphenols, ethoxylated fatty alcohols, paraffin oils, castor oil or ricinoleic esters, Turkey and ground nut oil, and cell regulators such as paraffins, fatty alcohols and dimethyl polysiloxane. Die oberflächenaktiven Substanzen werden üblicher weise in Mengen von 0,01 bis 5 Gew.-Teilen, bezogen auf 100 Gew.- Teile der Komponenten (b) bis (f), angewandt. The surfactants are typically used in amounts of 0.01 to 5 parts by weight, based on 100 parts by weight of components (b) to (f) applied.

Als Füllstoffe, insbesondere verstärkend wirkende Füll stoffe, sind die an sich bekannten, üblichen organischen und anorganischen Füllstoffe, Verstärkungsmittel, Beschwerungsmittel, Mittel zur Verbesserung des Abriebverhaltens in Anstrichfarben, Beschichtungsmittel usw. zu verstehen. As fillers, in particular reinforcing fillers fabrics, the known conventional organic and inorganic fillers, reinforcing agents, weighting agents, agents for improving the abrasion behavior in paints, coating agents, etc., are to be understood. Im einzelnen seien bei spielhaft genannt: anorganische Füllstoffe, wie silikatische Mineralien, beispielsweise Schichtsilikate, wie Antigorit, Serpentin, Hornblenden, Ampibole, Chrisotil und Talkum, Metall oxide, wie Kaolin, Aluminiumoxide, Titanoxide und Eisenoxide, Metallsalze, wie Kreide, Schwerspat und anorganische Pigmente, wie Cadmiumsulfid und Zinksulfid, sowie Glas ua Vorzugsweise verwendet werden Kaolin (China Clay), Aluminiumsilikat und Copräzipitate aus Bariumsulfat und Aluminiumsilikat sowie natür liche und synthetische faserförmige Mineralien, wie Wollastonit, Metall- und insbesondere Glasfasern verschiedener Länge, die gegebenenfalls geschlichtet sein können. The following may be mentioned in play are: inorganic fillers such as siliceous minerals, for example phyllosilicates, such as antigorite, serpentine, hornblende, amphiboles, chrysotile, and talc, oxides of metal, such as kaolin, aluminum oxides, titanium oxides and iron oxides, metal salts such as chalk, barite and inorganic pigments such as cadmium sulfide and zinc sulfide, and glass, etc. Preferably, kaolin (china clay), aluminum silicate and coprecipitates of barium sulfate and aluminum silicate and natuer Liche and synthetic fibrous minerals such as wollastonite, metal fibers and in particular glass fibers of various lengths which settled may optionally be , Als organische Füll stoffe kommen beispielsweise in Betracht: Kohle, Kollophonium, Cyclopentadienylharze und Pfropfpolymerisate sowie Cellulose fasern, Polyamid-, Polyacrylnitril-, Polyurethan-, Polyester fasern auf der Grundlage von aromatischen und/oder aliphatischen Dicarbonsäureestern und insbesondere Kohlenstoffasern. Suitable organic filling materials are for example: carbon, rosin, cyclopentadienyl resins and graft polymers and also cellulose fibers, polyamide, polyacrylonitrile, polyurethane, polyester fibers based on aromatic and / or aliphatic dicarboxylic esters and in particular carbon fibers. Die anorganischen und organischen Füllstoffe können einzeln oder als Gemische verwendet werden und werden der Reaktionsmischung vor teilhafterweise in Mengen von 0,5 bis 50 Gew.-%, vorzugsweise 1 bis 40 Gew.-%, bezogen auf das Gesamtgewicht der Komponenten (b) bis (f), einverleibt, wobei jedoch der Gehalt an Matten, Vliesen und Geweben aus natürlichen und synthetischen Fasern Werte bis 80 erreichen kann. The inorganic and organic fillers can be used individually or as mixtures, and the reaction mixture prior to part way enough, in amounts of from 0.5 to 50 wt .-%, preferably 1 to 40 wt .-%, based on the total weight of components (b) to (f) incorporated into, but can reach the content of mats, nonwovens and woven fabrics of natural and synthetic fibers values ​​to 80 wt.

Nähere Angaben über die oben genannten anderen üblichen Hilfs- und Zusatzstoffe sind der Fachliteratur, beispielsweise der Monographie von JH Saunders und KC Frisch "High Polymers" Band XVI, Polyurethanes, Teil 1 und 2, Verlag Interscience Publishers 1962 bzw. 1964, oder dem oben zitierten Kunststoff handbuch, Polyurethane, Band VII, Hanser-Verlag München, Wien, 1. bis 3. Auflage, zu entnehmen. Further details regarding the abovementioned other customary auxiliaries and additives in the technical literature, for example the monograph by JH Saunders and KC Frisch, "High Polymers", Volume XVI, Polyurethanes, Parts 1 and 2, Verlag Interscience Publishers 1962 and 1964, or the above- cited Kunststoff Handbuch, Polyurethane, Volume VII, Hanser-Verlag Munich, Vienna, 1st to 3rd edition be seen.

Zur Herstellung der erfindungsgemäßen schalldämpfenden PUR- Schäume werden die organischen und/oder modifizierten organischen Polyisocyanate (a), das Polyetherolgemisch (b) und gegebenen falls weiteren gegenüber Isocyanaten reaktive Wasserstoffatome aufweisenden Verbindungen (c) in solchen Mengen zur Umsetzung gebracht, daß das Äquivalenzverhältnis von NCO-Gruppen der Polyisocyanate (a) zur Summe der reaktiven Wasserstoffatome der Komponenten (b) und ggf. (c) 0,70 bis 1,25 : 1, vorzugsweise 0,90 bis 1,15 : 1, beträgt. For preparing the sound absorbing polyurethane foams of this invention are the organic and / or modified organic polyisocyanates (a), the polyetherol mixture (b) and, if appropriate further isocyanate-reactive hydrogen atoms containing compounds (c) in such amounts reacted so that the equivalent ratio of NCO groups of the polyisocyanates (a) to the sum of the reactive hydrogen atoms of components (b) and optionally (c) from 0.70 to 1.25: 1, preferably from 0.90 to 1.15: 1, is.

PUR-Schaumstoffe nach dem erfindungsgemäßen Verfahren werden vor teilhafterweise nach dem one-shot-Verfahren, beispielsweise mit Hilfe der Hochdruck- oder Niederdruck-Technik in offenen oder geschlossenen Formwerkzeugen, beispielsweise metallischen Form werkzeugen hergestellt. PUR foams by the novel process are prepared before geous enough, by the one-shot process, for example with the aid of high-pressure or low-pressure technique, in open or closed molds, for example metallic mold tools. Üblich ist auch das kontinuierliche Auftragen des Reaktionsgemisches auf geeigneten Bandstraßen zur Erzeugung von Schaumblöcken. It is also common continuous application of the reaction mixture to suitable conveyor belts for producing slabstock foams.

Als besonders vorteilhaft hat es sich erwiesen, nach dem Zwei komponentenverfahren zu arbeiten und die Aufbaukomponenten (b) bis (f) zu einer sogenannten Polyolkomponente, oft auch als Komponente A bezeichnet, zu vereinigen und als Isocyanat komponente, oft auch als Komponente B bezeichnet, die organischen und/oder modifizierten organischen Polyisocyanate (a), besonders bevorzugt ein NCO-Prepolymer oder Mischungen aus diesem Pre polymeren und weiteren Polyisocyanaten, und gegebenenfalls Treibmittel (d) zu verwenden. Particularly advantageous has proven to employ the two-component process and to combine the formative components (b) to (f) to form a polyol, often referred to as component A, and component as isocyanate, often referred to as component B, to use the organic and / or modified organic polyisocyanates (a), particularly preferably an NCO prepolymer or a mixture of this pre polymeric and other polyisocyanates, and optionally the blowing agent (d).

Die Ausgangskomponenten werden bei einer Temperatur von 15 bis 90°C, vorzugsweise von 20 bis 60°C und insbesondere von 20 bis 35°C, gemischt und in das offene oder gegebenenfalls unter er höhtem Druck in das geschlossene Formwerkzeug eingebracht oder bei einer kontinuierlichen Arbeitsstation auf ein Band, das die Reaktionsmasse aufnimmt, aufgetragen. The starting components are mixed at a temperature of 15 to 90 ° C, preferably from 20 to 60 ° C and especially from 20 to 35 ° C and introduced into the open or optionally with he elevated pressure in the closed mold or in a continuous workstation on a belt which receives the reaction mass, is applied. Die Vermischung kann mechanisch mittels eines Rührers, mittels einer Rührschnecke oder durch eine Hochdruckvermischung in einer Düse durchgeführt werden. The mixing can be carried out mechanically by means of a stirrer, by means of a paddle screw or by a high pressure mixing in a nozzle. Die Formwerkzeugtemperatur beträgt zweckmäßigerweise 20 bis 110°C, vorzugsweise 30 bis 60°C und insbesondere 35 bis 55°C. The mold temperature is advantageously from 20 to 110 ° C, preferably 30 to 60 ° C and in particular 35 to 55 ° C.

Die nach dem erfindungsgemäßen Verfahren hergestellten PUR- Schaumstoffe (Akustikschäume) weisen eine Dichte von 10 bis 800 kg/m 3 , vorzugsweise von 60 bis 100 kg/m 3 auf. The (acoustic foams) produced by the process of this invention polyurethane foams have a density of 10 to 800 kg / m 3, preferably from 60 to 100 kg / m 3. Besonders eignen sie sich als Material für Schalldämmzwecke. They are particularly suitable as a material for Schalldämmzwecke.

Die vorliegende Erfindung soll anhand der angeführten Beispiele erläutert werden, ohne jedoch hierdurch eine entsprechende Ein grenzung vorzunehmen. The present invention will be illustrated by the examples, without however thereby make a corresponding A limitation.

Beispiele Examples

Eine Polyolzusammensetzung - siehe Tabelle 1 - wurde mit einem Prepolymeren auf Basis von Diphenylmethandiisocyanat(MDI)- Derivaten und einem Polyetherol auf Basis Ethylenoxid und Propylenoxid mit einem NCO-Gehalt von 28,9 Gew.-% bei der jeweils angegebenen Kennzahl (KZ) verschäumt. A polyol composition - see Table 1 - was measured with a prepolymer based on diphenylmethane diisocyanate (MDI) - foamed derivatives and a polyetherol based on ethylene oxide and propylene oxide having an NCO content of 28.9 wt .-% at the respectively specified code (KZ) ,

Tabelle 1 Table 1

Zusammensetzung der Akustikschäume Composition of the acoustic foams

Lupranol® 2040 OH-Zahl 28 mg KOH/g, Polyetheralkohol auf Basis von Propylen- und Ethylenoxid (BASF), Lupranol® 2040 OH number 28 mg KOH / g, the polyether alcohol based on propylene oxide and ethylene oxide (BASF),
Lupranol® 2043 OH-Zahl 29 mg KOH/g, Polyetheralkohol auf Basis von Propylen- und Ethylenoxid (BASF), Lupranol® 2043 OH number 29 mg KOH / g, the polyether alcohol based on propylene oxide and ethylene oxide (BASF),
Lupranol® 2042 OH-Zahl 27 mg KOH/g, Polyetheralkohol auf Basis von Propylen- und Ethylenoxid (BASF), Lupranol® 2042 OH number 27 mg KOH / g, the polyether alcohol based on propylene oxide and ethylene oxide (BASF),
Lupranol® 2047 OH-Zahl 42 mg KOH/g, Polyetheralkohol auf Basis von Propylen- und Ethylenoxid (81 Gew.-%) (BASF), Lupranol® 2047 OH number 42 mg KOH / g, the polyether alcohol based on propylene oxide and ethylene oxide (81 wt .-%) (BASF),
Lupranol® 1200 OH-Zahl 250 mg KOH/g, Polyetheralkohol auf Basis von Propylenoxid (BASF), Lupranol® 1200 OH number 250 mg KOH / g, the polyether alcohol based on propylene oxide (BASF),
Lupranol® 4100 OH-Zahl 25 mg KOH/g, Graftpolyetheralkohol (BASF), Lupranol® 4100 OH number 25 mg KOH / g, Graftpolyetheralkohol (BASF),
Lupragen® N 201 Aminkatalysator (BASF), Lupragen® N 201 amine catalyst (BASF),
Lupragen® N 206 Aminkatalysator (BASF), Lupragen® N 206 amine catalyst (BASF),
B 8680, B 8631 Sililkonstabilisator (Goldschmidt), B 8680, B 8631 Sililkonstabilisator (Goldschmidt)
SH 209 Sililkonstabilisatoren (OSi), SH 209 Sililkonstabilisatoren (OSi)
Polyol A Versuchsprodukt - OH-Zahl 150 mg KOH/g, Poly etheralkohol auf Basis von Ricinusöl-Ethylenoxid (BASF), Polyol A trial product - OH number 150 mg KOH / g, poly ether alcohol based on castor oil-ethylene oxide (BASF),
Polyol B Versuchsprodukt - OH-Zahl 110 mg KOH/g, Poly etheralkohol auf Basis von Ricinusöl-Ethylenoxid (BASF), Polyol B Test product - OH number 110 mg KOH / g, poly ether alcohol based on castor oil-ethylene oxide (BASF),
Polyol C Versuchsprodukt - OH-Zahl 87 mg KOH/g, Poly etheralkohol auf Basis von Ricinusöl-Ethylenoxid (BASF), Polyol C Trial product - OH number 87 mg KOH / g, poly ether alcohol based on castor oil-ethylene oxide (BASF),
Polyol D Versuchsprodukt - OH-Zahl 145 mg KOH/g, Poly etheralkohol auf Basis von Ricinusöl und Propylen- und Ethylenoxid (BASF). Polyol D experimental product - OH number 145 mg KOH / g, poly ether alcohol based on castor oil and propylene and ethylene oxide (BASF).

Die erhaltenen Kennwerte der Akustikschäume sind in Tabelle 2 zusammengefaßt. The characteristic values ​​obtained acoustic foams are summarized in Table 2 below.

Tabelle 2 table 2

Kennwerte der Akustikschäume Characteristics of the acoustic foams

Die Akustikschäume auf Basis der Ricinusölderivate bzw. deren Kombination mit Ricinusöl weisen eine sehr gute Schaumstruktur und ein gutes Fließverhalten auf. The acoustic foams based on castor oil or their combination with castor oil have a very good foam structure and good flow behavior. Durch die Verwendung nach wachsender Rohstoffe kann zudem die Umwelt nachhaltig geschont werden. Through the use of renewable resources, the environment can also be permanently protected.

Claims (14)

  1. 1. Verfahren zur Herstellung von Polyurethanweichschaum stoffen mit schalldämpfenden Eigenschaften durch Umsetzung von organischen und/oder modifizierten organischen Poly isocyanaten (a) mit einem Polyetherolgemisch (b) und gegebenenfalls weiteren gegenüber Isocyanaten reaktive Wasserstoffatome aufweisenden Verbindungen (c) in Gegenwart von Wasser und/oder anderen Treibmitteln (d), Katalysatoren (e) und gegebenenfalls weiteren Hilfs- und Zusatzstoffen (f), dadurch gekennzeichnet , daß das Polyetherolgemisch (b) besteht aus 1. A method for producing polyurethane soft foam materials having sound-deadening properties by reacting organic and / or modified organic poly isocyanates (a) with a polyetherol mixture (b) and optionally other isocyanate-reactive hydrogen atoms containing compounds (c) in the presence of water and / or other blowing agents (d), catalysts (s) and optionally further auxiliaries and additives (f), characterized in that the polyetherol mixture (b) consists of
    • 1. mindestens einem zwei- bis achtfunktionellen Polyetherol auf der Basis von Ethylenoxid und Propylenoxid und gegebenenfalls Butylenoxid mit einer OH-Zahl von 20 bis 80 mg KOH/g und einem Anteil an primären OH-Gruppen größer als 50% und 1. at least one two- to eight-functional polyetherol based on ethylene oxide and propylene oxide and, optionally, butylene oxide with an OH number of 20 to 80 mg KOH / g and a proportion of primary OH groups greater than 50% and
    • 2. mindestens einem Ricinusölpolyetherol auf der Basis Ethylenoxid und gegebenenfalls Propylenoxid und/oder Butylenoxid mit einer OH-Zahl von 50 bis 160 mg KOH/g. 2. at least one Ricinusölpolyetherol based on ethylene oxide and optionally propylene oxide and / or butylene oxide with an OH number of 50 to 160 mg KOH / g.
  2. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß b) reines Ricinusöl b3) enthält. 2. The method according to claim 1, characterized in that b) of pure castor oil b3) contains.
  3. 3. Verfahren nach einem der Ansprüche 1 bis 2, dadurch gekenn zeichnet, daß b) mindestens ein weiteres Polyetherol b4) auf der Basis von Propylenoxid und gegebenenfalls Ethylenoxid mit einem Anteil an primären OH-Gruppen von weniger als 20% ent hält. 3. A method according to any one of claims 1 to 2, characterized in that holding b) at least one further polyetherol b4) on the basis of propylene oxide and optionally ethylene oxide with a proportion of primary OH groups of less than 20% ent.
  4. 4. Verfahren nach einem der Ansprüche 1 bis 3, dadurch gekenn zeichnet, daß b1) einen Anteil an primären OH-Gruppen größer als 70% aufweist. 4. The method according to any one of claims 1 to 3, characterized in that b1) has a proportion of primary OH groups greater than 70%.
  5. 5. Verfahren nach einem der Ansprüche 1 bis 4, dadurch gekenn zeichnet, daß b2) eine OH-Zahl von 80 bis 160 mg KOH/g auf weist. 5. A method according to any one of claims 1 to 4, characterized in that b2) has an OH number of 80 to 160 mg KOH / g.
  6. 6. Verfahren nach einem der Ansprüche 1 bis 5, dadurch gekenn zeichnet, daß b2) durch Addition von Ethylenoxid an Ricinusöl hergestellt wird. 6. A method according to any one of claims 1 to 5, characterized in that b2) is prepared by addition of ethylene oxide onto castor oil.
  7. 7. Verfahren nach einem der Ansprüche 1 bis 6, dadurch gekenn zeichnet, daß b2) in Anteilen von 1 bis 70 Gew.-%, vorzugs weise von 10 bis 40 Gew.-%, bezogen auf das Gesamtgewicht der Komponente b), eingesetzt wird. 7. A method according to any one of claims 1 to 6, characterized in that b2), used in proportions of from 1 to 70 wt .-%, preferably from 10 to 40 wt .-%, based on the total weight of component b) becomes.
  8. 8. Verfahren nach einem der Ansprüche 1 bis 7, dadurch gekenn zeichnet, daß b1) in Anteilen von 20 bis 70 Gew.-%, vorzugs weise von 30 bis 60 Gew.-%, jeweils bezogen auf das Gesamt gewicht der Komponente b), eingesetzt wird. 8. A method according to any one of claims 1 to 7, characterized in that b1) in proportions of 20 to 70 wt .-%, preferably from 30 to 60 wt .-%, each based on the total weight of component b) is used.
  9. 9. Verfahren nach einem der Ansprüche 1 bis 8, dadurch gekenn zeichnet, daß b3) in Anteilen von 0,5 bis 10 Gew.-%, vorzugs weise von 0,5 bis 6 Gew.-%, jeweils bezogen auf das Gesamt gewicht der Komponente b), eingesetzt wird. 9. A method according to any one of claims 1 to 8, characterized in that b3) in weight proportions of from 0.5 to 10 wt .-%, preferably from 0.5 to 6 wt .-%, each based on the total of component b), is used.
  10. 10. Verfahren nach einem der Ansprüche 1 bis 9, dadurch gekenn zeichnet, daß b4) in Anteilen von 0,5 bis 7 Gew.-%, vorzugs weise von 0,5 bis 5 Gew.-%, jeweils bezogen auf das Gesamt gewicht der Komponente b), eingesetzt wird. 10. A method according to any one of claims 1 to 9, characterized in that b4) in proportions of from 0.5 to 7 wt .-%, preferably from 0.5 to 5 wt .-%, each based on the total weight of component b), is used.
  11. 11. Verfahren nach einem der Ansprüche 1 bis 10, dadurch gekenn zeichnet, daß als organische und/oder modifizierte organische Polyisocyanate Toluylendiisocyanat, Gemische aus Diphenyl methandiisocyanat-Isomeren, Gemische aus Diphenylmethandiiso cyanat und Polyphenylpolymethylpolyisocyanat oder Toluylen diisocyanat mit Diphenylmethandiisocyanat und/oder Poly phenylpolymethylpolyisocyanat eingesetzt werden. 11. A method according to any one of claims 1 to 10, characterized in that the organic and / or modified organic polyisocyanates tolylene diisocyanate, diphenyl diisocyanate, mixtures of diisocyanate isomers, mixtures of diphenylmethane diisocyanate and Polyphenylpolymethylpolyisocyanat or toluene with diphenylmethane diisocyanate and / or poly phenylpolymethylpolyisocyanat used become.
  12. 12. Polyurethanweichschaumstoffe mit schalldämpfenden Eigen schaften, herstellbar durch Umsetzung von organischen und/oder modifizierten organischen Polyisocyanaten (a) mit einem Polyetherolgemisch (b) und gegebenenfalls weiteren gegenüber Isocyanaten reaktive Wasserstoffatome aufweisenden Verbindungen (c) in Gegenwart von Wasser und/oder anderen Treibmitteln (d), Katalysatoren (e) und gegebenenfalls weiteren Hilfs- und Zusatzstoffen (f), dadurch gekenn zeichnet, daß das Polyetherolgemisch (b) besteht aus 12, flexible polyurethane foams having sound-deadening self-properties which can be produced by reacting organic and / or modified organic polyisocyanates (a) with a polyetherol mixture (b) and optionally other isocyanate-reactive hydrogen atoms containing compounds (c) in the presence of water and / or other blowing agents ( d), catalysts (s) and optionally further auxiliaries and additives (f), characterized characterized marked in that the polyetherol mixture (b) consists of
    • 1. mindestens einem zwei- bis achtfunktionellen Polyetherol auf der Basis von Ethylenoxid und Propylenoxid und gegebenenfalls Butylenoxid mit einer OH-Zahl von 20 bis 80 mg KOH/g und einem Anteil an primären OH-Gruppen größer als 50% und 1. at least one two- to eight-functional polyetherol based on ethylene oxide and propylene oxide and, optionally, butylene oxide with an OH number of 20 to 80 mg KOH / g and a proportion of primary OH groups greater than 50% and
    • 2. mindestens einem Ricinusölpolyetherol auf der Basis Ethylenoxid und gegebenenfalls Propylenoxid und/oder Butylenoxid mit einer OH-Zahl von 50 bis 160 mg KOH/g. 2. at least one Ricinusölpolyetherol based on ethylene oxide and optionally propylene oxide and / or butylene oxide with an OH number of 50 to 160 mg KOH / g.
  13. 13. Polyurethanweichschaumstoffe mit schalldämpfenden Eigen schaften gemäß Anspruch 12, dadurch gekennzeichnet, daß sie einen Verlustfaktor von 0,20 bis 0,50 aufweisen. 13, flexible polyurethane foams having sound-deadening self-properties according to claim 12, characterized in that they have a loss factor of from 0.20 to 0.50.
  14. 14. Verwendung der Polyurethanweichschaumstoffe mit schall dämpfenden Eigenschaften gemäß einem der Ansprüche 12 oder 13 als Dämpfungsmaterial. 14. Use of the flexible polyurethane foams having sound-absorbing properties according to any one of claims 12 or 13 as a damping material.
DE1999136481 1999-08-03 1999-08-03 Preparation of easily processed soft polyurethane foams, useful as noise damping materials, with good noise damping properties and high loss factor Withdrawn DE19936481A1 (en)