DE19905799A1 - Material for softening rigid polyurethane bandages, e.g. along edges and cutting lines, comprises the reaction product of a polyurethane prepolymer with a mono- or bi-functional organic hydroxy compound - Google Patents

Material for softening rigid polyurethane bandages, e.g. along edges and cutting lines, comprises the reaction product of a polyurethane prepolymer with a mono- or bi-functional organic hydroxy compound

Info

Publication number
DE19905799A1
DE19905799A1 DE1999105799 DE19905799A DE19905799A1 DE 19905799 A1 DE19905799 A1 DE 19905799A1 DE 1999105799 DE1999105799 DE 1999105799 DE 19905799 A DE19905799 A DE 19905799A DE 19905799 A1 DE19905799 A1 DE 19905799A1
Authority
DE
Germany
Prior art keywords
reaction
polyurethane
reaction material
polyurethane prepolymer
bandages
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE1999105799
Other languages
German (de)
Inventor
Michael Weigold
Kurt Seeger
Frank Kura
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lohmann GmbH and Co KG
Original Assignee
Lohmann GmbH and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lohmann GmbH and Co KG filed Critical Lohmann GmbH and Co KG
Priority to DE1999105799 priority Critical patent/DE19905799A1/en
Publication of DE19905799A1 publication Critical patent/DE19905799A1/en
Withdrawn legal-status Critical Current

Abstract

A reaction material for preventing the complete hardening of polyurethane (PU) prepolymer-impregnated binding material for the production of partly softened rigid bandages consists of or contains a reaction product of PU prepolymers derived from polyisocyanates and polyols with mono- or bi-functional compounds with organic hydroxyl groups (I). An Independent claim is also included for a method for preventing the complete hardening of PU prepolymer-impregnated binding material as above by reacting the PU prepolymer with (I) so that 10-100% of the free isocyanate groups undergo reaction and then swelling the intermediate obtained with a 1-6C aliphatic alcohol, preferably ethanol, to form an alcohol gel with a solid content of 25-80%.

Description

Polyurethansteifverbände werden aus textilen Bindenmateria­ lien, die mit Polyurethanprepolymer imprägniert sind, her­ gestellt, indem die Binden entweder direkt zirkulär um den zu fixierenden Teil des Körpers unter Ausbildung eines Steifverbandes gewickelt werden, wobei dessen Aushärtung unter Einwirkung der normalen Luftfeuchtigkeit bei ver­ gleichsweise längerer Einwirkungsdauer erfolgt, oder aber das Bindenmaterial vor dem Wickeln erst kurz in Wasser ge­ taucht wird, wodurch die Aushärtung innerhalb weniger Minu­ ten erreicht wird.Rigid polyurethane bandages are made from textile bandage material lien, which are impregnated with polyurethane prepolymer provided by the bandages either directly circularly around the part of the body to be fixed, forming a Rigid bandage are wound, its curing under the influence of normal humidity at ver equally long exposure takes place, or else the bandage material briefly in water before wrapping is immersed, resulting in curing within a few minutes ten is reached.

Im ersten Fall kann die Aushärtung beschleunigt werden, in­ dem der fertig angelegte Verband mit Wasser oder wasserhal­ tigen Substanzen, wie z. B. Cremes, benetzt wird.In the first case, curing can be accelerated in which the finished dressing with water or water term substances, such as. B. creams is wetted.

Ein Nachteil solcher Kunststoffsteifverbände besteht darin, daß an ihren Enden scharfe Kanten entstehen, die infolge der Bewegung des damit umgebenen Körperteils zu Aufschür­ fungen führen können, andererseits auch eine völlige Immo­ bilisierung zur Folge zu haben, die bei längerem Tragen des Steifverbandes zur Muskelatrophie führen und die Thrombose­ gefahr erhöhen.A disadvantage of such plastic cast bandages is that that sharp edges arise at their ends, which result from the movement of the part of the body surrounding it to open can also lead to complete immo to result in bilization, which occurs when the Cast bandage lead to muscle atrophy and thrombosis increase risk.

Alternative Verbände unter der Bezeichnung "Softcasts", wie sie beispielsweise in den US-Patenten 4,968,542 bzw. 5,007,418 beschrieben sind, bleiben in der Gänze halbhart bzw. gummielastisch. Infolgedessen fehlt solchen Verbänden die erforderliche Ruhigstellung beispielsweise in einem Frakturbereich, weshalb sie speziell für aktive Sportler gedacht sind, die bei nicht zu schweren Verletzungen, wie beispielsweise Sehnenzerrungen oder Muskelrissen, für einen schnellen Heilungsprozeß keine völlige Immobilisierung ei­ nes Körperteils erfordern. Alternative associations under the name "Softcasts", such as for example in U.S. Patents 4,968,542 and 5,007,418, remain semi-hard as a whole or rubbery. As a result, such associations are missing the required immobilization, for example, in one Fracture area, which is why it is specifically for active athletes are thought of in the case of not too serious injuries, such as for example, tendon strain or muscle tears, for one rapid healing process no complete immobilization part of the body.  

Aus der Praxis ist es bekannt, daß routinierte Anwender, wie beispielsweise Sportärzte, derartige "Softcasts" mit anderen Kunststoffsteifverbänden kombinieren, um dadurch im Bereich einer Fraktur formsteife Verbände zu erhalten. Die­ ses Verfahren hat jedoch den Nachteil, daß es einerseits nicht so routinierte Anwender, wie Arzthelferinnen, Kran­ kenpfleger etc. überfordert, und andererseits eine in allen Größen und Farben vermehrte, fallweise doppelte Lagerhal­ tung verursacht.It is known in practice that experienced users, such as sports doctors, with such "softcasts" combine other plastic cast bandages to To maintain a fracture in the area of a fracture. The However, this method has the disadvantage that it is one hand not as experienced users as medical assistants, crane kenpfleger etc. overwhelmed, and on the other hand one in all Sizes and colors increased, sometimes double warehouse tung caused.

Ausgehend vom vorgenannten Stand der Technik liegt der Er­ findung die Aufgabe zugrunde, ein Reaktionsmaterial und ein Verfahren zum Verhindern einer vollständigen Aushärtung von mit Polyurethanprepolymer imprägniertem Bindenmaterial an­ zugeben, das sich unter Vermeidung der vorgenannten Schwie­ rigkeiten und technischen Grenzen zur Herstellung von Po­ lyurethanprepolymersteifverbänden mit partiell oder topisch verminderter Steifheit eignet, indem es die Aushärtung we­ nigstens teilweise verhindert, dabei die Oberflächenkleb­ rigkeit des Prepolymers unterdrückt und eine problemlose Handhabung sowie Anwendung gewährleistet.Based on the aforementioned prior art, the Er the task is based on a reaction material and a Process to prevent complete curing of binding material impregnated with polyurethane prepolymer admit that avoiding the aforementioned Schwie abilities and technical limits for the production of buttocks polyurethane prepolymer stiffness with partial or topical reduced stiffness is suitable by the hardening we at least partially prevented, the surface adhesive suppressed prepolymer and a problem-free Handling and application guaranteed.

Zur Lösung der Aufgabe wird mit der Erfindung ein Reak­ tionsmaterial der im Oberbegriff von Anspruch 1 genannten Art zur Herstellung von partiell erweichten Steifverbänden vorgeschlagen, welches dadurch gekennzeichnet ist, daß es ein Umsetzungsprodukt von Polyurethanprepolymeren aus Poly­ isocyanaten und Polyolen mit mono- oder bifunktionellen or­ ganischen hydroxylgruppenhaltigen Verbindungen ist, oder ein solches Umsetzungsprodukt enthält.To solve the problem, the invention provides a reak tion material mentioned in the preamble of claim 1 Type for the production of partially softened cast bandages proposed, which is characterized in that it a reaction product of polyurethane prepolymers made of poly isocyanates and polyols with mono- or bifunctional or ganic compounds containing hydroxyl groups, or contains such a reaction product.

Mit Vorteil kann das Reaktionsmaterial bei einem mit Polyu­ rethanprepolymer getränktem Bindenmaterial so zur Reaktion gebracht werden, daß 10 bis 100% der freien Isocyanatgrup­ pen reagieren und die so entstandenen Produkte mit Alkoho­ len zu Alkoholgelen gequollen werden, die eine mittel- bis hochviskose Konsistenz aufweisen.With a Polyu binding material impregnated with rethane prepolymer for reaction brought that 10 to 100% of the free isocyanate group pen react and the resulting products with alcohol  len swollen to alcohol gels, which are a medium to have a highly viscous consistency.

Diese Alkoholgele lassen sich problemlos in die Polyure­ thansteifverbände einarbeiten und verhindern dort eine vollständige oder teilweise Aushärtung.These alcohol gels can be easily mixed into the polyure Work in as stiff bandages and prevent one there complete or partial curing.

Weitere vorteilhafte Ausbildungen des Reaktionsmaterials sind entsprechend den Unteransprüchen vorgesehen. Dieses ist beispielsweise dadurch gekennzeichnet, daß die Poly­ urethanprepolymere einen Restgehalt an freiem Isocyanat zwischen 5 und 25% enthalten.Further advantageous designs of the reaction material are provided according to the subclaims. This is characterized, for example, in that the poly urethane prepolymers a residual content of free isocyanate contain between 5 and 25%.

Das Reaktionsmaterial nach der Erfindung ist auch dadurch gekennzeichnet, daß es das Produkt einer zweistufigen Um­ setzung der Polyurethanprepolymere ist, mit deren erster Stufe 10 bis 100% der freien Isocyanatgruppen mit minde­ stens einer hydrosylgruppenhaltigen Verbindung zur Reaktion gebracht worden sind, wobei in einer zweiten Stufe die restlichen Isocyanatgruppen durch Ethanolzugabe im Über­ schuß unter Bildung von Alkoholgelen mit einem Feststoffge­ halt von 25 bis 80% zur Reaktion gebracht werden.The reaction material according to the invention is also thereby characterized that it is the product of a two-stage order setting of the polyurethane prepolymers, with their first Level 10 to 100% of the free isocyanate groups with at least least a hydrosyl group-containing compound for the reaction have been brought, the second stage remaining isocyanate groups by adding ethanol in excess shot to form alcohol gels with a solid gel hold from 25 to 80% to be reacted.

Das Reaktionsmaterial nach der Erfindung ist weiterhin da­ durch gekennzeichnet, daß es sich bei den in der ersten Stufe eingesetzten hydroxylgruppenhaltigen Verbindungen um monofunktionelle organische hydrosylgruppenhaltige Verbin­ dungen mit 2 bis 6 Kohlenstoffatomen handelt.The reaction material according to the invention is still there characterized in that it is in the first Step used hydroxyl group-containing compounds monofunctional organic compound containing hydrosyl groups with 2 to 6 carbon atoms.

Weiterhin sieht die Erfindung vor, daß es sich bei den in der ersten Stufe eingesetzten hydrosylgruppenhaltigen Ver­ bindungen um Polyethylenglykole mit einem Molekulargewicht bis 2000 Dalton handeln kann.Furthermore, the invention provides that the in the first stage used hydrosyl group-containing Ver bonds around polyethylene glycols with a molecular weight can trade up to 2000 daltons.

Ein Verfahren zum Verhindern einer vollständigen Aushärtung von mit Polyurethanprepolymer getränktem Bindenmaterial zur Herstellung von partiell erweichten Steifverbänden ist nach der Erfindung dadurch gekennzeichnet, daß die Polyurethan­ prepolymere mit mono- oder bifunktionellen, organischen hy­ droxylgruppenhaltigen Verbindungen derart zur Reaktion ge­ bracht werden, daß 10 bis 100% der freien Isocyanatgruppen reagieren und die so entstandenen Zwischenprodukte unter Bildung von Gelen mit 25 bis 80% Feststoff mit Alkoholen zu Alkoholgelen geguollen werden.A method to prevent complete curing of binding material impregnated with polyurethane prepolymer for Manufacture of partially softened casts is after  the invention, characterized in that the polyurethane prepolymers with mono- or bifunctional, organic hy droxyl group-containing compounds for the reaction be brought up that 10 to 100% of the free isocyanate groups react and the resulting intermediates below Formation of gels with 25 to 80% solids with alcohols be poured into alcohol gels.

Eine Ausbildung des Verfahrens nach der Erfindung sieht vor, daß das mit Polyurethanprepolymer getränkte Bindenma­ terial nach Ausbildung eines Verbandes und vor dessen Aus­ härtung durch wenigstens stellenweises Eintragen von orga­ nischen hydrosylgruppenhaltigen Verbindungen partiell an der Aushärtung gehindert wird.An embodiment of the method according to the invention provides proposes that the Bindenma material after the formation of an association and before it leaves hardening by at least partially entering orga African hydrosyl group-containing compounds curing is prevented.

Eine weitere Ausgestaltung des Verfahrens nach der Erfin­ dung ist dadurch gekennzeichnet, daß ein mit Polyurethan­ prepolymer getränktes Bindenmaterial nach Herstellung eines Verbandes und vor dessen Erhärtung entlang einer vorgesehe­ nen weichzumachenden Schnittlinie oder im Bereich von weichzumachenden Verbandsrändern mit hydroxylgruppenhalti­ gem weichmachendem Reaktionsmaterial versetzt wird.Another embodiment of the process according to the Erfin manure is characterized in that one with polyurethane prepolymer impregnated bandage material after production of a Association and before its hardening along a provided a line to be softened or in the range of soft bandages with hydroxyl groups is added according to the softening reaction material.

Eine weitere Ausgestaltung des Verfahrens nach der Erfin­ dung sieht vor, daß zur Herstellung von Verbänden mit ver­ minderter Härte das in einer Packung mit Polyurethanprepo­ lymer getränkt vorliegende ungehärtete Bindenmaterial mit hydroxylgruppenhaltigem Reaktionsmaterial versetzt und nach Verkneten zu einer innigen Mischung als Verbandsmaterial verwendet wird. Um dies zu erleichtern, kann in einer anderen Variante des Verfahrens mit der Erfindung vorgesehen sein, daß dem in einer originalen Primärpackung vorliegenden Bindenmaterial in dieser Packung eine Reaktionsmaterial enthaltende Do­ siervorrichtung beigepackt wird. Damit kann der Anwender, Arzt oder Arzthelfer, nach eigenem Ermessen einen Verband mit verminderter Steifheit herstellen. Another embodiment of the process according to the Erfin dung provides that for the production of associations with ver reduced hardness in a pack with polyurethane prepo lymer soaked present unhardened bandage material added reaction material containing hydroxyl groups and after Knead into an intimate mixture as a dressing material is used. To facilitate this, another variant of the Method with the invention be provided that in an original primary packaging present bandage material Do contains reaction material in this pack siervorrichtung is included. This allows the user Doctor or medical assistant, at your own discretion an association with reduced stiffness.  

Zu diesem Zweck sieht das Verfahren nach der Erfindung wei­ ter vor, daß die hinzudosierbare Menge an Reaktionsmaterial zu einem in der Primärpackung vorliegenden Bindenmaterial nach Maßgabe der vorgesehenen Minderung der Steifheit eines damit herstellbaren Verbandes bevorzugt nach der Erfahrung exakt vorherbestimmt wird.For this purpose, the method according to the invention looks white ter that the metered amount of reaction material to a bandage material in the primary packaging according to the intended reduction in the stiffness of a Association that can be produced with this is preferred based on experience is predetermined exactly.

Schließlich ist mit der Erfindung eine Verwendung des Reak­ tionsmaterials und/oder des Verfahrens zur Herstellung von Polyurethansteifverbänden mit insgesamt bzw. partiell oder topisch verminderbarer Steifheit vorgesehen.Finally with the invention is a use of the reak tion material and / or the method for producing Rigid polyurethane bandages with total or partial or topically reduced stiffness provided.

Die Erfindung wird nachfolgend mit einigen Anwendungsbei­ spielen für partiell erweichte Steifverbände im einzelnen weiter erläutert, wobei die Erfindung jedoch nicht auf die­ se Beispiele beschränkt sein soll:
The invention is explained in more detail below with some examples of applications for partially softened casts, but the invention is not intended to be limited to the following examples:

  • - Scharfkantige Ränder eines Verbandes können zu Verletzun­ gen der Haut führen, insbesondere dann, wenn das den Ver­ band aufnehmende Glied ab und zu bewegt wird. Durch er­ findungsgemäße Erweichung der Verbandsränder kann der Verband dem Druck bei Bewegungen ausweichen und damit Verletzungen vermeiden.- Sharp edges of a bandage can be injured lead to the skin, especially if the Ver band receiving member is moved from time to time. Through it softening of the bandage edges according to the invention can Dressing to avoid the pressure with movements and thus Avoid injuries.
  • - Klassische Kunststoffsteifverbände müssen zum Abnehmen mit einer Gipssäge entlang einer Grenzlinie aufgeschnit­ ten werden. Durch Verrutschen der Säge oder falsche Hand­ habung kann es sehr leicht zu Verletzungen der beim lan­ gen Verbandtragen besonders empfindlich gewordenen Haut kommen.
    Eine nach der Erfindung weich gemachte Schnittlinie ent­ lang des Verbandes ermöglicht die Entfernung mit einer Schere. Dabei entfällt auch das lästige Geräusch der Gipssäge, das bei vielen Patienten Angst hervorruft.     - Classic plastic cast bandages must be cut open along a border line with a plaster saw. If the saw slips or is handled incorrectly, injuries to the skin that has become particularly sensitive when wearing long bandages can easily occur.
    A cut line ent softened according to the invention along the bandage enables removal with scissors. This also eliminates the annoying sound of the plaster saw, which causes fear in many patients.
  • - Bei den meisten Frakturen muß nur der Frakturbereich ruhiggestellt werden. Eine partielle Erweichung der übri­ gen Verbandsbereiche nach der Erfindung führt zu mehr Be­ wegungsfreiheit, wodurch mit Vorteil eine verbesserte Muskelatrophieprophylaxe bzw. Throniboseprophylaxe er­ reicht wird.- With most fractures, only the fracture area has to be be immobilized. A partial softening of the rest gene association areas according to the invention leads to more loading freedom of movement, which is an advantage Muscle atrophy prophylaxis or thronibose prophylaxis is enough.
  • - Durch partielle Erweichung nach der Erfindung besteht die Möglichkeit, abnehmbare Orthesen und Verbände mit und oh­ ne Gelenke zu fertigen.- By partial softening according to the invention Possibility of removable orthoses and bandages with and oh to manufacture ne joints.

Durch Einbringen einer vorgegebenen dünnen Menge an Reak­ tionsmaterial in eine Bindenpackung vor deren Applikation, wobei das Reaktionsmaterial mit dem Bindenmaterial durch Verkneten innig vermischt wird, lassen sich Steifverbände mit vorgebbarer Verminderung der Steifheit herstellen. Nachfolgend wird die Herstellung und Anwendung des erfin­ dungsgemäßen Reaktionsmaterials anhand der nachfolgenden Beispiele näher erläutert.By introducing a predetermined thin amount of reak in a sanitary napkin pack before application, wherein the reaction material with the binding material through Kneading is intimately mixed, casting bandages Manufacture with a predeterminable reduction in stiffness. The following is the production and application of the inventions reaction material according to the invention based on the following Examples explained in more detail.

BEISPIELEXAMPLE 1.1 Herstellung des Reaktionsmaterials1.1 Preparation of the reaction material

200 ml Polyurethanprepolymer aus der Kunststoffsteifver­ bandfertigung werden in einem thermostatisierten 1000 ml- Reaktionsgefäß mit Planschliff und Deckel mit Schutzgasan­ schluß, Rührer, Rückflußkühler und Tropftrichter vorgelegt und auf 60°C erwärmt. Die hydroxylgruppenhaltige organi­ sche Verbindung (ROH) wird so zudosiert, daß die Reaktions­ temperatur nicht über 85°C ansteigt. Nach Ende der Zudo­ sierung und erneuter Einstellung eines Temperaturgleichge­ wichts wird mit der der jeweiligen Rezeptur entsprechenden Menge eines aliphatischen C1-C6-Alkohols, vorzugsweise Ethanol, verdünnt. Die Lösung wird ohne vorherige Abkühlung in Vorratsbehälter abgefüllt.
200 ml of polyurethane prepolymer from the Kunststoffsteifver band production are placed in a thermostated 1000 ml reaction vessel with surface grinding and cover with a protective gas connection, stirrer, reflux condenser and dropping funnel and heated to 60 ° C. The hydroxyl group-containing organic compound (ROH) is metered in so that the reaction temperature does not rise above 85.degree. After the end of the metering and re-adjustment of a temperature equilibrium, the amount of an aliphatic C 1 -C 6 alcohol, preferably ethanol, corresponding to the respective formulation is diluted. The solution is filled into storage containers without cooling.

1.2 Herstellung erfindungsgemäßer Verbände1.2 Production of dressings according to the invention

In einer ersten Anwendung werden frisch gewickelte Kunst­ stoffsteifverbände in einem 5 cm breiten Bereich zirkulär mit dem Reaktionsmaterial aus Beispiel 1 bis 6 behandelt, indem das Material aus einer PE-Flasche mit Tropfaufsatz in den Verband eingedrückt wird. Auf die gleiche Weise wird auf der ganzen Länge des Verbandes ein 1 cm breiter Strei­ fen behandelt.In a first application, freshly wrapped art Circular stiffening in a 5 cm wide area treated with the reaction material from Examples 1 to 6, by inserting the material from a PE bottle with a drip cap the bandage is pushed in. In the same way a 1 cm wide streak along the entire length of the dressing fen treated.

In einer zweiten Anwendung wird mittels einer Spritze 40 ml des Reaktionsmaterials gemäß Beispiel 1 bis 6 in die Origi­ nalpackung einer Kunststoffsteifverbandbinde dosiert und in der Verpackung in die Binde eingeknetet. Sofort nach dem Öffnen der Verpackung wird die Binde trocken appliziert. In a second application, 40 ml of the reaction material according to Examples 1 to 6 in the Origi nal pack of a plastic bandage bandage dosed and in of the packaging kneaded into the bandage. Immediately after When the packaging is opened, the bandage is applied dry.  

1.3 Beurteilung des Ergebnisses1.3 Assessment of the result

Die Beurteilung der Steifverbände erfolgte nach 1 h, 24 h sowie 1 Woche.The casts were assessed after 1 h, 24 h as well as 1 week.

Die Bewertung entsprach den Noten 1 = sehr gut bis 6 = man­ gelhaft.The rating was 1 = very good to 6 = one geligen.

Der Lagenverbund war in allen Fällen gut, ebenso verschwand bei allen Versuchen nach spätestens 30 min die Oberflächen­ klebrigkeit.
The layer bond was good in all cases, and the surface stickiness disappeared in all tests after 30 minutes at the latest.

Claims (12)

1. Reaktionsmaterial zum Verhindern einer vollständigen Aushärtung von mit Polyurethanprepolymer getränktem Binden­ material zur Herstellung von partiell erweichten Steifver­ bänden, dadurch gekennzeichnet, daß es ein Umsetzungspro­ dukt von Polyurethanprepolymeren aus Polyisocyanaten und Polyolen mit mono- oder bifunktionellen organischen hy­ droxylgruppenhaltigen Verbindungen ist, oder ein solches Umsetzungsprodukt enthält.1. Reaction material to prevent complete hardening of binding material impregnated with polyurethane prepolymer for the production of partially softened stiffening tapes, characterized in that it is a reaction product of polyurethane prepolymers made of polyisocyanates and polyols with mono- or bifunctional organic compounds containing hydroxyl groups, or such Contains implementation product. 2. Reaktionsmaterial nach Anspruch 1, dadurch gekenn­ zeichnet, daß die Polyurethanprepolymere einen Restgehalt an freiem Isocyanat zwischen 5 und 25% enthalten.2. Reaction material according to claim 1, characterized records that the polyurethane prepolymers have a residual content contain between 5 and 25% of free isocyanate. 3. Reaktionsmaterial nach Anspruch 1 oder 2, dadurch ge­ kennzeichnet, daß es das Produkt einer zweistufigen Umset­ zung der Polyurethanprepolymere ist, in deren erster Stufe 10 bis 100% der freien Isocyanatgruppen mit mindestens ei­ ner hydroxylgruppenhaltigen Verbindung zur Reaktion ge­ bracht wurden, wobei in einer zweiten Stufe die restlichen Isocyanatgruppen durch Ethanolzugabe im Überschuß unter Bildung von Alkoholgelen mit einem Feststoffgehalt von 25 bis 80% umgesetzt wurden.3. Reaction material according to claim 1 or 2, characterized ge indicates that it is the product of a two-stage implementation tion of the polyurethane prepolymers is in its first stage 10 to 100% of the free isocyanate groups with at least egg ner hydroxyl group-containing compound for reaction were brought, with the remaining in a second stage Isocyanate groups by adding ethanol in excess Formation of alcohol gels with a solids content of 25 up to 80% were implemented. 4. Reaktionsmaterial nach einem oder mehreren der Ansprü­ che 1 bis 3, dadurch gekennzeichnet, daß es sich bei den in der ersten Stufe eingesetzten hydroxylgruppenhaltigen Ver­ bindungen um monofunktionelle organische hydroxylgruppen­ haltige Verbindungen mit 2 bis 6 Kohlenstoffatomen handelt.4. Reaction material according to one or more of the claims che 1 to 3, characterized in that it is in the the first stage used hydroxyl-containing Ver bonds around monofunctional organic hydroxyl groups containing compounds with 2 to 6 carbon atoms. 5. Reaktionsmaterial nach einem oder mehreren der Ansprü­ che 1 bis 4, dadurch gekennzeichnet, daß es sich bei den in der ersten Stufe eingesetzten hydroxylgruppenhaltigen Ver­ bindungen um Polyethylenglykole mit einem Molekulargewicht bis 2000 Dalton handelt. 5. Reaction material according to one or more of the claims che 1 to 4, characterized in that it is in the the first stage used hydroxyl-containing Ver bonds around polyethylene glycols with a molecular weight up to 2000 daltons.   6. Verfahren zum Verhindern einer vollständigen Aushär­ tung von mit Polyurethanprepolymer getränktem Bindenmateri­ al zur Herstellung von partiell erweichten Steifverbänden, dadurch gekennzeichnet, daß die Polyurethanprepolymere mit mono- oder bifunktionellen organischen hydroxylgruppenhal­ tigen Verbindungen derart zur Reaktion gebracht werden, daß 10 bis 100% der freien Isocyanatgruppen reagieren und die so entstandenen Zwischenprodukte unter Bildung von Gelen mit 25 bis 80% Feststoff mit aliphatischem C1-C6- Alkohol, vorzugsweise Ethanol, zu Alkoholgelen gequollen werden.6. A method for preventing complete curing of impregnated with polyurethane prepolymer binding material for the production of partially softened casts, characterized in that the polyurethane prepolymers are reacted with mono- or bifunctional organic hydroxyl group-containing compounds in such a way that 10 to 100% of the free Isocyanate groups react and the intermediate products thus formed are swollen to form alcohol gels with aliphatic C 1 -C 6 alcohol, preferably ethanol, to form gels containing 25 to 80% solids. 7. Verfahren nach Anspruch 6, dadurch gekennzeichnet, daß das mit Polyurethanprepolymer getränkte Bindenmatarial nach Ausbildung eines Verbandes und vor dessen Aushärtung durch wenigstens stellenweises Eintragen von organischen hy­ droxylgruppenhaltigen Verbindungen partiell an der Aushär­ tung gehindert wird.7. The method according to claim 6, characterized in that the pad material soaked with polyurethane prepolymer Formation of an association and before it hardens at least partial entry of organic hy Compounds containing droxyl groups partially on the cure is prevented. 8. Verfahren nach Anspruch 6 oder 7, dadurch gekannzeich­ net, daß ein mit Polyurethanprepolymer getränktes Bindenma­ terial nach Herstellung eines Verbandes und vor dessen Er­ härtung entlang einer vorgesehenen weichzumachenden Schnittlinie oder im-Bereich von weichzumachenden Verbands­ rändern mit hydroxylgruppenhaltigem weichmachendem Reak­ tionsmaterial gemäß den Ansprüchen 1 bis 5 versetzt wird.8. The method according to claim 6 or 7, characterized net that a Bindenma impregnated with polyurethane prepolymer material after the creation of a dressing and before it curing along an intended to be softened Cutting line or in the area of dressing to be softened edges with hydroxyl-containing softening reak tion material according to claims 1 to 5 is added. 9. Verfahren nach Anspruch 6, dadurch gekennzeichnet, daß zur Herstellung von Verbänden mit verminderter Härte das in einer Packung mit Polyurethanprepolymer getränkt vorliegen­ de ungehärtete Bindenmaterial mit hydroxylgruppenhaltigem Reaktionsmaterial gemäß den Ansprüchen 1 bis 5 versetzt und nach Verkneten zu einer innigen Mischung als Verbandsmate­ rial verwendet wird. 9. The method according to claim 6, characterized in that for the production of bandages with reduced hardness the in a package soaked with polyurethane prepolymer de uncured bandage material containing hydroxyl groups Reaction material according to claims 1 to 5 and after kneading to an intimate mixture as a dressing material rial is used.   10. Verfahren nach einem oder mehreren der Ansprüche 6 bis 9, dadurch gekennzeichnet, daß dem in einer originalen Pri­ märverpackung vorliegenden Bindenmaterial in dieser Packung eine Reaktionsmaterial gemäß Ansprüchen 1 bis 5 enthaltende Dosiervorrichtung beigepackt wird.10. The method according to one or more of claims 6 to 9, characterized in that the in an original Pri This packaging contains the sanitary material in this pack containing a reaction material according to claims 1 to 5 Dosing device is included. 11. Verfahren nach einem oder mehreren der Ansprüche 6 bis 10, dadurch gekennzeichnet, daß die hinzudosierbare Menge an Reaktionsmaterial nach Maßgabe der vorgesehenen Minde­ rung der Steifheit eines damit herstellbaren Verbandes be­ vorzugt nach der Erfahrung exakt vorherbestimmt wird.11. The method according to one or more of claims 6 to 10, characterized in that the amount to be added of reaction material in accordance with the intended Minde stiffness of a bandage that can be produced with it preferably based on experience. 12. Verwendung des Reaktionsmaterials und/oder Verfahren nach den vorhergehenden Ansprüchen zur Herstellung von Po­ lyurethansteifverbänden mit insgesamt bzw. partiell oder topisch verminderbarer Steifheit.12. Use of the reaction material and / or method according to the preceding claims for the production of Po stiff bandages with total or partial or topically reduced stiffness.
DE1999105799 1999-02-12 1999-02-12 Material for softening rigid polyurethane bandages, e.g. along edges and cutting lines, comprises the reaction product of a polyurethane prepolymer with a mono- or bi-functional organic hydroxy compound Withdrawn DE19905799A1 (en)