DE1150044B - Verfahren zur Herstellung von beschichteten, unter Flammeneinwirkung nichttropfenden, flammfesten Geweben aus Polyamiden oder linearen Polyestern - Google Patents
Verfahren zur Herstellung von beschichteten, unter Flammeneinwirkung nichttropfenden, flammfesten Geweben aus Polyamiden oder linearen PolyesternInfo
- Publication number
- DE1150044B DE1150044B DEF23165A DEF0023165A DE1150044B DE 1150044 B DE1150044 B DE 1150044B DE F23165 A DEF23165 A DE F23165A DE F0023165 A DEF0023165 A DE F0023165A DE 1150044 B DE1150044 B DE 1150044B
- Authority
- DE
- Germany
- Prior art keywords
- flame
- coated
- polyamides
- production
- fabrics made
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Vollsynthetische Gewebe aus Polyamiden, z. B. auf Basis von ε-Caprolactam oder Adipinsäure und
Hexamethylendiamin, oder Polyestern auf Basis von Terephthalsäure und Glykolen besitzen auf Grund
ihrer Vorzüge ein besonderes Interesse. Für die Herstellung beschichteter Gewebe (Kunstleder) ist es jedoch
nachteilig, daß diese Materialien eine leichte Entflammbarkeit aufweisen und daß ein Schmelzen
und Abtropfen der vollsynthetischen Trägersubstanz stattfindet. Dadurch wird die Gefahr einer Ausbreitung
eines Brandes erheblich vergrößert.
Es wurde nun überraschenderweise gefunden, daß man beschichtete, unter Flammeneinwirkung nicht
tropfende, flammfeste Gewebe aus Polyamiden oder linearen Polyestern herstellen kann, wenn man die Gewebe
mit Streichmassen beschichtet, die Plastisole, Antimontrioxyd in Mengen von etwa 8 bis 19% sowie
außerdem Sulfide oder Oxyde zweiwertiger Metalle und bzw. oder Mischungen von Sulfiden zweiwertiger
Metalle mit Salzen zweiwertiger Metalle, vorzugsweise in Mengen bis zu ewa 11%, enthalten.
Als Plastisole kommen Kunststoffe, vor allem Polyvinylchlorid, in Frage, die mit Weichmachern
plastifiziert sind. Als Weichmacher seien beispielsweise Trikresylphosphat, Triphenylphosphat, Dioctylphthalat
u. ä. genannt.
Neben Polyvinylchlorid haben sich vor allen Dingen als filmbildende Stoffe Polychloropren sowie
Umsetzungsprodukte des Polyäthylens mit Chlor und Schwefeldioxyd bewährt.
Die Streichmassen sollen, sofern sie auf Polyvinylchlorid aufgebaut sind, auf 60 Teile Polyvinylchlorid
etwa 40 bis 48 Teile Weichmacher enthalten. Der Zusatz von Antimontrioxyd verhindert schon in verhältnismäßig
geringer Menge das Abtropfen des geschmolzenen Materials. Ein ausreichender Flammschutz
bei gleichzeitiger Verhinderung des Abtropfens wird jedoch nur erzielt, wenn man den Streichmassen
Mengen von mehr als 8% Antimontrioxyd sowie außerdem Verbindungen zweiwertiger Metalle, z. B.
Metallsulfiden, wie Zinksulfid, oder Metalloxyden, wie Zinkoxyd oder Bleioxyd, oder Mischungen von
Sulfiden mit Metallsalzen, z.B. Lithopon, zusetzt. Ein Zusatz von etwa 8 bis 19% Antimontrioxyd und vorzugsweise
bis zu etwa 11% der vorstehend genannten Verbindungen zweiwertiger Metalle oder Mischungen
aus Verbindungen zweiwertiger Metalle, bezogen auf die Menge der Weichmacher enthaltenden Polyvinylchloridpaste,
hat sich als besonders wirksam erwiesen. Die Höhe des Zusatzes wird durch die Anforderungen
an die Streichbarkeit der Paste begrenzt. Der Flammfestausrüstungseffekt kann durch Ver-Verfahren
zur Herstellung
von beschichteten, unter Flammeneinwirkung nichttropfenden, flammfesten Geweben
aus Polyamiden oder linearen Polyestern
Anmelder:
Farbwerke Hoechst Aktiengesellschaft
vormals Meister Lucius & Brüning,
Frankfurt/M., Brüningstr. 45
Dr. Eduard Hilscher, Kelkheim-Münster,
ist als Erfinder genannt worden
ist als Erfinder genannt worden
wendung nichtbrennbarer Weichmacher noch verbessert werden.
Da die Haftfestigkeit von Weichmacher enthaltendem Polyvinylchlorid auf den in Betracht kommenden
vollsynthetischen Faserstoffen gering ist, ist es zweckmäßig, den Grundanstrich der Polyvinylchloridpaste
unter Zusatz von geeigneten Haftvermittlern auszuführen. Hierfür eignet sich beispielsweise eine Kombination
von hydroxylgruppenhaltigen Polyestern mit Polyisocyanat. Man kann dabei auch so verfahren,
daß der Polyester aus einer Lösung im organischen Lösungsmittel auf das Gewebe aufgebracht
und die Polyisocyanatkomponente in die Polyvinylchloridpaste eingearbeitet wird.
Art und Menge der aufzubringenden Beschichtungsmasse hängen naturgemäß von dem Gewicht des
rohen vollsynthetischen Gewebes ab. So ist es vorteilhaft, ein Gewebe, dessen Gewicht etwa 280 g/qm
beträgt, mit einer zweiseitigen Beschichtung zu versehen, um den notwendigen Effekt zu erzielen. Bei
sehr leichten Geweben kann man mit verhältnismäßig kleinen Auflagen arbeiten, und unter Umständen genügt
in solchen Fällen eine einseitige Beschichtung. Sofern es der Anwendungszweck des Gewebes erfordert,
können selbstverständlich Farbpigmente mit eingearbeitet werden.
Die gemäß dem Verfahren der vorliegenden Erfindung ausgerüsteten Gewebe bieten besonderes Interesse
für militärische Artikel, wie Wagenplanen, Zeltplanen und Zeltböden sowie Abdeckstoffe. Auch für
Ausrüstungsgegenstände, wie Taschen, Wasser-
309 600/235
behälter und ähnliches können sie verwendet werden. Selbstverständlich können die ausgerüsteten Gewebe
auch für andere Zwecke eingesetzt werden, beispielsweise für Sonnenschutzvorhänge, Theatervorhänge
und ähnliches.
Es ist zwar bereits bekannt, daß man schwer entflammbare Kunststoffilme erhält, wenn man nichtbrennbare Plastifizierungsmittel, z.B. Trikresylphosphat,
Triphenylphosphat u. ä., in die Kunststoffpasten einarbeitet. Es ist ferner bekannt, Antimontrioxyd
Flammschutzappreturen zuzusetzen, die zum Tränken von Textilmaterial verwendet werden. Aus der schweizerischen
Patentschrift 210 205 ist es auch bereits bekannt, filmbildende thermoplastische Stoffe, verteilt in
einem nichtlösenden Plastifizierungsmittel, zum Streichen und Beschichten von Textilmaterial zu verwenden.
Hieraus konnte jedoch das Verfahren der vorliegenden Erfindung, die Erzielung eines ausreichenden
Flammschutzes bei gleichzeitiger Verhinderung des Abtropfens von beschichteten Geweben aus Polyamiden
oder linearen Polyestern, nicht entnommen werden.
Ein Polyamidgewebe von einem Gewicht von etwa 200 g/m2 wird mit einer weichmacherhaltigen, nichtpigmentierten
Polyvinylchloridpaste (60:40), der 10 bis 14 %> Haftvermittler zugesetzt sind, dünn bestrichen.
Nach der Vorgelierung bei 120° C werden dann drei Striche einer nach folgender Rezeptur hergestellten
Polyvinylchloridpaste aufgebracht:
600 Teile Polyvinylchlorid,
480 Teile Dioctylphthalat,
108 Teile Antimontrioxyd,
84 Teile Lithopone,
2 Teile Farbstoff.
480 Teile Dioctylphthalat,
108 Teile Antimontrioxyd,
84 Teile Lithopone,
2 Teile Farbstoff.
Nach jedem Strich wird bei 120° C vorgeliert. Dann wird die Rückseite des Gewebes in gleicher
Weise beschichtet und schließlich 5 Minuten bei 170° C durchgeliert. Das Gewebe hat eine Auflage
von 380 g/m2. Das so hergestellte Kunstleder zeigt bei längerer Berührung mit einer Gasflamme kein
Abtropfen des Trägermaterials und brennt nach Entfernung der Flamme nicht weiter.
Ein etwa 70 g/m2 wiegendes Polyamidgewebe wird in der im Beispiel 1 beschriebenen Weise mit einer
Haftschicht versehen und mit folgender Paste einseitig zweimal bestrichen:
600 Teile Polyvinylchlorid,
440 Teile Dioctylphthalat,
140 Teile Antimontrioxyd,
440 Teile Dioctylphthalat,
140 Teile Antimontrioxyd,
80 Teile Zinksulfid,
3 Teile Farbstoff.
3 Teile Farbstoff.
Nach jedem Strich wird 10 Minuten bei 170° C
ίο geliert. Das beschichtete Gewebe besitzt ein Gewicht
von 180 g/m2. Es ist nicht brennbar und tropft nicht.
Ein Polyestergewebe (Gewicht 180 g/m2) wird in
der im Beispiel 1 angegebenen Weise mit einer Haftschicht versehen und beidseitig mit je vier Strichen
unter Verwendung der nachstehenden Polyvinylchloridpaste beschichtet und wie üblich geliert:
600 Teile Polyvinylchlorid,
480 Teile Trikresylphosphat,
480 Teile Trikresylphosphat,
93 Teile Antimontrioxyd,
97 Teile Zinkoxyd,
1 Teil Farbstoff.
97 Teile Zinkoxyd,
1 Teil Farbstoff.
Das beschichtete Gewebe zeigt keine Entflammbarkeit und keine Schmelztropfenbildung.
Wird das Trikresylphosphat durch Dioctylphthalat ersetzt und etwa die gleiche Auflage erzielt, so zeigt
das Gewebe eine verringerte Flammfestigkeit, aber ebenfalls kein Abtropfen.
Claims (1)
- Patentanspruch:Verfahren zur Herstellung von beschichteten, unter Flammeneinwirkungnicht tropfenden, flammfesten Geweben aus Polyamiden oder linearen Polyestern, dadurch gekennzeichnet, daß man die Gewebe mit Streichmassen beschichtet, die Piastisole, Antimontrioxyd in Mengen von etwa 8 bis 19% sowie außerdem Sulfide oder Oxyde zweiwertiger Metalle und bzw. oder Mischungen von Sulfiden zweiwertiger Metalle mit Salzen zweiwertiger Metalle, vorzugsweise in Mengen bis zu etwa 11%, enthalten.In Betracht gezogene Druckschriften:
schweizerische Patentschrift Nr. 210 205;
Schaeffer, Chemikalienkunde für den Textilveredler, 1951, S. 89.