DE102015107173A1 - ABSORPTION OF SOFTMAKERS BY ZEOLITHE - Google Patents

ABSORPTION OF SOFTMAKERS BY ZEOLITHE Download PDF

Info

Publication number
DE102015107173A1
DE102015107173A1 DE102015107173.8A DE102015107173A DE102015107173A1 DE 102015107173 A1 DE102015107173 A1 DE 102015107173A1 DE 102015107173 A DE102015107173 A DE 102015107173A DE 102015107173 A1 DE102015107173 A1 DE 102015107173A1
Authority
DE
Germany
Prior art keywords
composition
decorative layer
molecular sieve
carrier molding
plasticizer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE102015107173.8A
Other languages
German (de)
Other versions
DE102015107173B4 (en
Inventor
Wolfgang Fischer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lisa Draexlmaier GmbH
Original Assignee
Lisa Draexlmaier GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lisa Draexlmaier GmbH filed Critical Lisa Draexlmaier GmbH
Priority to DE102015107173.8A priority Critical patent/DE102015107173B4/en
Priority to CN201610302746.7A priority patent/CN106113865A/en
Publication of DE102015107173A1 publication Critical patent/DE102015107173A1/en
Application granted granted Critical
Publication of DE102015107173B4 publication Critical patent/DE102015107173B4/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

Die vorliegende Erfindung betrifft eine Zusammensetzung (1) zur Aufnahme von Weichmachungsmitteln aus einer weichmacherhaltigen Dekorschicht (2) und/oder einem weichmacherhaltigem thermoplastischen Trägerformteil (3), wobei die Zusammensetzung (1) zumindest ein Beschichtungsmittel (4) und ein Molekularsieb (5) umfasst und zwischen der Dekorschicht (2) und dem Trägerformteil (3) angeordnet ist, und wobei das Molekularsieb (5) zur adsorptiven Aufnahme von Weichmachungsmitteln geeignet ist und aus einem zeolithischen Material oder einem Kohlenstoffmolekularsieb (carbon molecular sieve, CMS) besteht, sowie ein Kunststoffbauteil mit beschichtetem Trägerformteil, und die Verwendung der Zusammensetzung.The present invention relates to a composition (1) for receiving softening agents from a plasticized decorative layer (2) and / or a plasticized thermoplastic carrier molding (3), wherein the composition (1) comprises at least one coating agent (4) and a molecular sieve (5) and between the decorative layer (2) and the carrier molding (3), and wherein the molecular sieve (5) is suitable for adsorptive incorporation of softening agents and consists of a zeolitic material or a carbon molecular sieve (CMS), and a plastic component with coated carrier molding, and the use of the composition.

Description

Die vorliegende Erfindung betrifft eine Zusammensetzung zur Aufnahme von Weichmachungsmitteln aus einer weichmacherhaltigen Dekorschicht und/oder einem weichmacherhaltigem thermoplastischen Trägerformteil, sowie ein Kunststoffbauteil mit beschichtetem Trägerformteil, und die Verwendung der Zusammensetzung. The present invention relates to a composition for receiving softening agents from a plasticized decorative layer and / or a plasticized thermoplastic carrier molding, and a plastic component with coated carrier molding, and the use of the composition.

Technisches Gebiet Technical area

Seit langem werden PVC-Materialien (Polyvinylchlorid) im Innenraum von Automobilen verarbeitet, z. B. als Kaschierfolie oder Kunstleder. Oftmals handelt es sich auch um Interieurteile, die ihre entsprechenden optischen, haptischen und funktionalen Eigenschaften durch Verkleben von Spritzgussbauteilen mit unterschiedlichen Oberflächendekoren erhalten. Insbesondere werden Kunststoffteile als Spritzgussformkörper oder Trägerformteil für den Automobilinnenraum, beispielsweise Instrumententafeln, Türverkleidung oder Mittelkonsolen, eingesetzt. Diese können sowohl mit einem Dekor beschichtet als auch mit einem weiteren Kunststoffteil verklebt sein oder lackiert werden. For a long time PVC materials (polyvinyl chloride) are processed in the interior of automobiles, eg. B. as laminating film or artificial leather. Often they are also interior parts, which receive their corresponding optical, haptic and functional properties by gluing injection molded components with different surface decorations. In particular, plastic parts are used as injection molding or carrier molding for the automotive interior, such as instrument panels, door trim or center consoles. These can be both coated with a decor as well as glued or painted with another plastic part.

Stand der Technik State of the art

PVC-Materialien sind aus dem Stand der Technik hinlänglich bekannt und können insbesondere vorteilhaft zur dekorativen Ausgestaltung von Fahrzeuginnenräumen eingesetzt werden. PVC-Schaummaterialien und PVC-Folien können kostengünstig hergestellt werden, wobei einfache und energiesparende Streichverfahren eingesetzt werden können, die im Stand der Technik ebenfalls bekannt sind. PVC materials are well known from the prior art and can be used particularly advantageous for the decorative design of vehicle interiors. PVC foam materials and PVC films can be inexpensively manufactured using simple and energy-saving coating techniques also known in the art.

Trägerformteile des Stands der Technik, die mit PVC-Folie oder Kunstleder oder anderen Dekormaterialien kaschiert werden sollen, werden im Stand der Technik vor der Weiterverarbeitung, also dem Aufbringen der Dekorschicht, häufig mechanisch behandelt, um einerseits während des Einsatzes des kaschierten Formteils eine Ablösung zu vermeiden und andererseits möglichst umgehend nach dem Aufbringen der Kaschierung eine Weiterverarbeitung des kaschierten Formteils zu ermöglichen. Carrier moldings of the prior art, which are to be laminated with PVC film or synthetic leather or other decorative materials, are often mechanically treated in the prior art prior to further processing, so the application of the decorative layer, on the one hand during the use of the laminated molding a detachment avoid and on the other hand as soon as possible after application of the lamination to allow further processing of the laminated molding.

Aus der EP 0 307 546 B1 ist das Aufbringen eines lösungsmittelfreien Dispersionshaftvermittlers aus Ethylen-Vinylazetat-Kopolymeren oder Polyurethan auf Kunststofffolien auf der Basis von Hart-PVC oder Halbhart-PVC bekannt, wobei die so vorbereiteten Kunststofffolien auf unterschiedlichste Werkstoffe wie Spanlatten, Hartfaserplatten, Bleche usw. aufgebracht werden. From the EP 0 307 546 B1 the application of a solvent-free dispersion bonding agent of ethylene-vinyl acetate copolymers or polyurethane on plastic films based on rigid PVC or semi-rigid PVC is known, the thus prepared plastic films are applied to a variety of materials such as chipboard, hardboard, sheets, etc.

Der Zusatz von Weichmachern verleiht dem von Natur aus harten Werkstoff PVC und seinen Derivaten plastische Eigenschaften, wie Nachgiebigkeit und Weichheit. Als Weichmacher werden vor allem Phthalsäureester, Adipinsäureester und Phosphorsäureester eingesetzt. Die Weichmacher lagern sich bei der thermoplastischen Verarbeitung zwischen die Molekülketten des PVC ein und lockern dadurch das Gefüge. Diese Einlagerung ist eine physikalische Aufdehnung der Struktur, so daß trotz der geringen Flüchtigkeit eine Migration und Gasabgabe erfolgt. Dadurch kommt es je nach Anwendungszweck zu einer sorbierten Oberflächenschicht oder auch zur Wanderung des Weichmachers in angrenzende Materialien, insbesondere Klebeschichten, oder auch durch den Luftraum in benachbarte Substanzen. The addition of plasticizers gives the inherently hard material PVC and its derivatives plastic properties, such as flexibility and softness. The plasticizers used are above all phthalic acid esters, adipic acid esters and phosphoric acid esters. The plasticizers are incorporated in the thermoplastic processing between the molecular chains of the PVC and thereby loosen the structure. This incorporation is a physical expansion of the structure, so that migration and gas release takes place despite the low volatility. Depending on the purpose of use, this results in a sorbed surface layer or even in migration of the plasticizer into adjacent materials, in particular adhesive layers, or even through the air space into adjacent substances.

GB 851 753 offenbart Mischungen, die Harz-Homopolymere oder -Copolymere von Vinylchlorid und Ester von Isophthalsäure und/oder Terephthalsäure umfassen. Diese Mischungen zeigen ein verringertes "Verderben", ein Phänomen, bei dem der Weichermacher eines Vinylchlorid-Harzes aus dem Harz in eine Oberfläche wandert, wodurch dessen Härte, Glätte und Glanz verringert werden. GB 851 753 discloses mixtures comprising resin homopolymers or copolymers of vinyl chloride and esters of isophthalic acid and / or terephthalic acid. These blends exhibit reduced "spoilage", a phenomenon in which the plasticizer of a vinyl chloride resin migrates from the resin into a surface, thereby reducing its hardness, smoothness and gloss.

Die JP 10251469 offenbart Polyvinylchlorid-Harzzusammensetzungen für die Herstellung von Folien für Nahrungsmittelverpackungen, welche Adipat-Weichmacher umfassen. The JP 10251469 discloses polyvinyl chloride resin compositions for the manufacture of food packaging films comprising adipate plasticizers.

Ein Nachteil der Verfahren und Formkörper des Standes der Technik liegt darin, daß durch die geringe Verträglichkeit von Weichmachern und PVC die Permanenz der Weichmacher verringert wird, d. h. daß diese relativ schnell aus dem PVC-Halbzeug, -Fertigzeug oder -Bauteil austreten, wodurch eine starke Funktions- und Wertminderung des entsprechenden Teils entsteht. Dies führt insbesondere zu Problemen bei der Verklebung von Materialien mit hohen Weichmachergehalten wie beispielsweise den in der Automobilindustrie häufig verwendeten weichen PVC-Folien, da es zur Wanderung der Weichmacherverbindungen aus dem Substrat in die Klebeschicht kommt, was die Beständigkeit der Klebeverbindung deutlich vermindert und zur unerwünschten Ablösung des Dekors führen kann. A disadvantage of the prior art processes and moldings is that the low compatibility of plasticizers and PVC reduces the permanence of the plasticizers, i. H. that these emerge relatively quickly from the PVC semi-finished, finished product or component, whereby a strong function and depreciation of the corresponding part arises. This leads in particular to problems in the bonding of materials with high plasticizer contents such as the soft PVC films commonly used in the automotive industry, since it comes to migration of the plasticizer compounds from the substrate in the adhesive layer, which significantly reduces the resistance of the adhesive bond and the undesirable Replacement of the decor can result.

Beschreibung der Erfindung Description of the invention

Die Aufgabe der vorliegenden Erfindung besteht somit darin, Mittel und Bauteile bereitzustellen, mit denen die nachteiligen Wirkungen der Weichmachermigration in PVC enthaltenden Bauteilen derart vermindert oder unterdrückt werden, daß ein mit einer Kaschierung, einem Dekor oder Beschichtung versehenes Bauteil keine Beeinträchtigungen infolge der Weichmachermigration aufweist. The object of the present invention is therefore to provide means and components with which the adverse effects of plasticizer migration in PVC-containing components are reduced or suppressed such that a provided with a lamination, a decor or coating component has no adverse effects due to the plasticizer migration.

Diese Aufgabe wird erfindungsgemäß durch eine Zusammensetzung zur Aufnahme von Weichmachungsmitteln aus einer weichmacherhaltigen Dekorschicht und/oder einem weichmacherhaltigem thermoplastischen Trägerformteil mit den Merkmalen gemäß Anspruch 1, sowie einem Kunststoffbauteil, insbesondere Innenverkleidungsbauteil für Innenräume von Kraftfahrzeugen, mit einem thermoplastischen Trägerformteil und einer weichmacherhaltigen Dekorschicht gemäß Anspruch 7, und der Verwendung des Zusammensetzung gemäß Anspruch 8 gelöst. This object is achieved by a composition for receiving softeners from a plasticized decorative layer and / or a plasticized thermoplastic carrier molding with the features of claim 1, and a plastic component, in particular interior trim component for interiors of motor vehicles, with a thermoplastic carrier molding and a plasticized decorative layer according to claim 7, and the use of the composition according to claim 8 dissolved.

Das erfindungsgemäße Zusammensetzung enthält zumindest ein Beschichtungsmittel und ein Molekularsieb und ist zwischen der Dekorschicht und dem Trägerformteil angeordnet, wobei das Molekularsieb zur adsorptiven Aufnahme von Weichmachungsmitteln geeignet ist und aus einem zeolithischen Material oder einem Kohlenstoffmolekularsieb (carbon molecular sieve, CMS) besteht. The composition according to the invention contains at least one coating agent and one molecular sieve and is arranged between the decorative layer and the carrier molding, wherein the molecular sieve is suitable for the adsorptive absorption of softening agents and consists of a zeolitic material or a carbon molecular sieve (CMS).

Nach der Erfindung wird die Weichmachermigration aus einer weichmacherhaltigen Dekorschicht und/oder einem weichmacherhaltigem thermoplastischen Trägerformteil mittels dem in der Zusammensetzung enthaltenen Molekularsieb abgefangen und somit eine Beeinträchtigung der Verklebung von Trägerformteil und Dekorschicht unterbunden. In bestimmten Ausführungsformen kann die Dekorschicht z.B. aus Leder, Kunstleder, Folien, Textil, etc. gebildet sein und/oder eine Abstandsschicht (Haptikschicht), z.B. aus Abstandsgewirke, Vliese, Gelpolster, Schaumstoffen beinhalten. Das Dekor kann mehrschichtig und/oder beschichtet sein und Weichmachungsmittel und PVC oder Derivate enthalten. Die zwischen der Dekorschicht und dem Trägerformteil angeordnete Zusammensetzung übernimmt bezüglich der migrierenden Weichmachermoleküle die Funktion einer Sperrschicht. According to the invention, the plasticizer migration from a plasticizer-containing decorative layer and / or a plasticized thermoplastic carrier molded part is intercepted by means of the molecular sieve contained in the composition and thus prevents impairment of the bonding of carrier molding and decorative layer. In certain embodiments, the decorative layer may be e.g. be made of leather, synthetic leather, films, textile, etc. and / or a spacer layer (haptic layer), e.g. from spacer, fleeces, gel pads, foams include. The decor may be multi-layered and / or coated and contain softening agents and PVC or derivatives. The composition arranged between the decorative layer and the carrier molded part assumes the function of a barrier layer with respect to the migrating plasticizer molecules.

Bevorzugt umfasst das Beschichtungsmittel in der Zusammensetzung einen Klebstoff, der ein Dispersionsklebstoff oder ein Schmelzklebstoff mit jeweils einer Polyolkomponente und einer Härterkomponente ist, und der in einem Anteil von 90 bis 99,999 Gew.-% und das Molekularsieb in einem Anteil von 0,001 bis 10 Gew.-% in der Zusammensetzung enthalten sind. Die Kaschierung von Trägern mit PVC-haltigen Dekorschichten erfolgt vorteilhaft unter Verwendung von Dispersionsklebstoff, der beidseits auf die zu verbindenden Seiten der zwei Schichten aufgetragen wird. In der genannten Massenverteilung wird einerseits eine maximale Weichmacheraufnahme gewährleistet, andererseits ist das Molekularsieb in hinreichend geringer Menge enthalten, ohne die mechanischen Eigenschaften des Klebstoffes zu beeinträchtigen. Darüber hinaus kann das Molekularsieb in diesen Mengen die Eigenschaft eines Füllstoffes annehmen, jedoch ist dies im Sinne der Erfindung nicht erforderlich. Preferably, the coating composition in the composition comprises an adhesive which is a dispersion adhesive or a hot melt adhesive having in each case a polyol component and a hardener component and which is present in an amount of from 90 to 99.999% by weight and the molecular sieve in an amount of from 0.001 to 10% by weight. -% are included in the composition. The lamination of substrates with PVC-containing decorative layers is advantageously carried out using dispersion adhesive, which is applied on both sides of the sides to be joined of the two layers. On the one hand, maximum plasticizer absorption is ensured in the stated mass distribution; on the other hand, the molecular sieve is contained in a sufficiently small amount without impairing the mechanical properties of the adhesive. In addition, the molecular sieve in these amounts may assume the property of a filler, but this is not required in the context of the invention.

Bevorzugt weisen die Partikel des zeolithischen Materials eine Größe im Bereich von 0,1 bis 20 µm auf und das zeolithische Material einen Porenöffnungsdurchmesser im Bereich von 0,5 bis 10,0 nm. Als Molekularsieb wurden experimentell beispielsweise Zeolith Na-A (SYLOSIV A4®, Porengröße 0,4 nm), Zeolith ZSM-5 (Silicalite, Porengröße 0,5 nm) oder Zeolith A4 (Zeopor® K80, Klinoptilolith, Porengröße 0,4 nm) verwendet, allerdings sollte die Porengröße der feinen Poren eines Weichmacher adsorbierenden Molekularsiebs innerhalb eines Bereiches von 0,35 nm bis 10,0 nm gesteuert sein, je nach Molekülgröße des verwendeten Weichmachers. Preferably, the particles of the zeolitic material have a size in the range of 0.1 to 20 microns and the zeolitic material has a pore opening diameter in the range of 0.5 to 10.0 nm. As a molecular sieve, for example, zeolite Na-A (SYLOSIV A4 ® , pore size 0.4 nm), zeolite ZSM-5 (silicalite, pore size 0.5 nm) or zeolite A4 (Zeopor ® K80, clinoptilolite, pore size 0.4 nm) used, but should have the pore size of the fine pores of a molecular sieve adsorbent plasticizer be controlled within a range of 0.35 nm to 10.0 nm, depending on the molecular size of the plasticizer used.

Bevorzugt enthält die weichmacherhaltige Dekorschicht und/oder das weichmacherhaltige thermoplastische Trägerformteil zumindest ein Polymer, ausgewählt aus der Gruppe bestehend aus Polyvinylchlorid, Polyvinylidenchlorid, Polyvinylbutyrat, Polycarbonat, Polyalkyl(meth)acrylat und Copolymeren oder Derivaten davon. In einer weiter bevorzugten Ausführungsform ist mindestens ein Polymer, das beispielsweise in einem geschäumten Formteil oder Dekorschicht enthalten ist, ausgewählt aus der Gruppe Polyvinylchlorid, Polyvinylidenchlorid, Polyvinylbutyrat, Polyalkylmethacrylat und Copolymeren davon. In einer besonders bevorzugten Ausführungsform ist mindestens ein Polymer ein Polyvinylchlorid (Homo- oder Copolymer). In einer weiteren besonders bevorzugten Ausführungsform kann das Polymer ein Copolymer von Vinylchlorid mit einem oder mehreren Monomeren ausgewählt aus der Gruppe bestehend aus Vinylidenchlorid, Vinylacetat, Vinylpropionat, Vinylbutyrat, Vinylbenzoat, Methylacrylat, Ethylacrylat oder Butylacrylat sein. Preferably, the plasticizer-containing decorative layer and / or the plasticizer-containing thermoplastic carrier molding contains at least one polymer selected from the group consisting of polyvinyl chloride, polyvinylidene chloride, polyvinyl butyrate, polycarbonate, polyalkyl (meth) acrylate and copolymers or derivatives thereof. In a further preferred embodiment, at least one polymer which is contained, for example, in a foamed molding or decorative layer, is selected from the group consisting of polyvinyl chloride, polyvinylidene chloride, polyvinyl butyrate, polyalkyl methacrylate and copolymers thereof. In a particularly preferred embodiment, at least one polymer is a polyvinyl chloride (homo- or copolymer). In a further particularly preferred embodiment, the polymer may be a copolymer of vinyl chloride with one or more monomers selected from the group consisting of vinylidene chloride, vinyl acetate, vinyl propionate, vinyl butyrate, vinyl benzoate, methyl acrylate, ethyl acrylate or butyl acrylate.

Alternativ kann das thermoplastische Trägerformteil, sofern es keine Weichmacher enthält, zumindest einen Kunststoff aufweisen, der ausgewählt ist aus der Gruppe bestehend aus Acrylnitril-Butadien-Styrol (ABS), Styrol-Acrylnitril (SAN), Polystyrol (PS), Polycarbonat (PC), Polyethylen(PE), Polypropylen (PP), Polyamide (PA), oder Mischungen daraus. Alternatively, the thermoplastic carrier molding, if it contains no plasticizers, at least one plastic selected from the group consisting of acrylonitrile-butadiene-styrene (ABS), styrene-acrylonitrile (SAN), polystyrene (PS), polycarbonate (PC) , Polyethylene (PE), polypropylene (PP), polyamides (PA), or mixtures thereof.

Bevorzugt weisen die weichmacherhaltige Dekorschicht und/oder das weichmacherhaltige thermoplastische Trägerformteil zumindest ein Weichmachungsmittel, ausgewählt aus der Gruppe der Phthalsäureester, Adipate, Citrate, Trimellitate oder Cyclohexandicarboxylate, auf. Insbesondere handelt es sich bei den Weichmachern um Ester der ortho-Phthalsäure, der Isophthalsäure, der Terephthalsäure, der Cyclohexandicarbonsäure, der Trimellitsäure, der Zitronensäure, der Benzoesäure, der Isononansäure, der 2-Ethylhexansäure, der Octansäure, der 3,5,5-Trimethylhexansäure und/oder um Ester des Butanol, Pentanol, Octanol, 2-Ethylhexanol, Isononanol, Decanol, Dodecanol, Tridecanol, Glycerin und/oder Isosorbid sowie deren Derivate und Mischungen. Zu den üblichen Weichmachern gehören beispielsweise (ortho)-Phthalsäureester wie Di-2-ethylhexylphthalat (DEHP), Diisono-nylphthalat (DINP) und Diisodecylphthalat (DIDP). Ortho-Phthalsäureester geraten jedoch wegen ihrer toxikologischen Eigenschaften zunehmend in Bedrängnis. Als alternative Weichmacher sind in daher neuerer Zeit Cyclohexandicarbonsäureester beschrieben worden, wie beispielsweise Diisononylcyclohexancarbonsäureester (DINCH). Preferably, the plasticizer-containing decorative layer and / or the plasticized thermoplastic carrier molding at least one plasticizer selected from the group of phthalic acid esters, adipates, citrates, trimellitates or cyclohexanedicarboxylates on. In particular, the plasticizers are esters of ortho-phthalic acid, isophthalic acid, terephthalic acid, cyclohexanedicarboxylic acid, trimellitic acid, citric acid, benzoic acid, isononanoic acid, 2-ethylhexanoic acid, octanoic acid, 3,5,5- Trimethylhexanoic acid and / or esters of Butanol, pentanol, octanol, 2-ethylhexanol, isononanol, decanol, dodecanol, tridecanol, glycerol and / or isosorbide and their derivatives and mixtures. The usual plasticizers include, for example, (ortho) -phthalic acid esters such as di-2-ethylhexyl phthalate (DEHP), diisononyl phthalate (DINP) and diisodecyl phthalate (DIDP). However, ortho-phthalic acid esters are increasingly in difficulty because of their toxicological properties. Cyclohexanedicarboxylic acid esters, for example diisononylcyclohexanecarboxylic acid esters (DINCH), have therefore recently been described as alternative plasticizers.

Es ist bekannt, dass mit zunehmender Kettenlänge der Ester die Unverträglichkeit des Weichmachers mit dem PVC ansteigt. Dies kann zur Konsequenz haben, daß PVC-Zusammensetzungen wie z.B. PVC-Plastisole atypische (z.B. ungewöhnlich hohe) und nicht vorhersehbare Viskositätsverläufe (z.B. in Abhängigkeit von der Schergeschwindigkeit) zeigen, die die Verarbeitung der PVC-Plastisole erschweren. Bei der Herstellung von Folien zeigt sich oftmals, daß diese zunehmend intransparent erscheinen und/oder eine Verfärbung der Folie eintritt, die in den meisten Anwendungen unerwünscht ist. Auch hierbei kann die Zusammensetzung der Erfindung vorteilhaft eingesetzt werden. It is known that with increasing chain length of the ester, the incompatibility of the plasticizer with the PVC increases. This may result in PVC compositions such as e.g. PVC plastisols exhibit atypical (e.g., unusually high) and unpredictable viscosity trajectories (e.g., as a function of shear rate) which make the processing of PVC plastisols difficult. In the production of films, it often appears that they appear increasingly non-transparent and / or discoloration of the film occurs, which is undesirable in most applications. Again, the composition of the invention can be used advantageously.

Das erfindungsgemäße Kunststoffbauteil, insbesondere ein Innenverkleidungsbauteil für Innenräume von Kraftfahrzeugen, mit einem thermoplastischen Trägerformteil und einer weichmacherhaltigen Dekorschicht, weist zwischen dem Trägerformteil und der Dekorschicht eine Zusammensetzung auf, die zumindest ein Beschichtungsmittel und ein Molekularsieb umfasst und zwischen der Dekorschicht und dem thermoplastischen Trägerformteil angeordnet ist. Dabei ist das Molekularsieb zur adsorptiven Aufnahme von Weichmachungsmitteln geeignet und besteht aus einem zeolithischen Material oder einem Kohlenstoffmolekularsieb (carbon molecular sieve, CMS). Das Beschichtungsmittel ist zum Beschichten und/oder Verkleben der Dekorschicht ausgebildet. In bestimmten Ausführungsformen kann die Dekorschicht z.B. aus Leder, Kunstleder, Folien, Textil, etc. gebildet sein und/oder eine Abstandsschicht (Haptikschicht), z.B. aus Abstandsgewirke, Vliese, Gelpolster, Schaumstoffen beinhalten. Das Dekor kann mehrschichtig und/oder beschichtet sein und Weichmachungsmittel und PVC oder Derivate enthalten. Die zwischen der Dekorschicht und dem Trägerformteil angeordnete Zusammensetzung übernimmt bezüglich der migrierenden Weichmachermoleküle die Funktion einer Sperrschicht. The plastic component according to the invention, in particular an interior trim component for interior of motor vehicles, with a thermoplastic carrier molding and a plasticized decorative layer, between the carrier molding and the decorative layer has a composition comprising at least one coating agent and a molecular sieve and is disposed between the decorative layer and the thermoplastic carrier molding , The molecular sieve is suitable for the adsorptive absorption of softening agents and consists of a zeolitic material or a carbon molecular sieve (CMS). The coating agent is designed for coating and / or gluing the decorative layer. In certain embodiments, the decorative layer may be e.g. be made of leather, synthetic leather, films, textile, etc. and / or a spacer layer (haptic layer), e.g. from spacer, fleeces, gel pads, foams include. The decor may be multi-layered and / or coated and contain softening agents and PVC or derivatives. The composition arranged between the decorative layer and the carrier molded part assumes the function of a barrier layer with respect to the migrating plasticizer molecules.

Kurze Figurenbeschreibung Short description of the figures

Nachfolgend werden einzelne Ausführungsformen der Erfindung anhand der Zeichnung näher beschrieben. Hereinafter, individual embodiments of the invention will be described in more detail with reference to the drawing.

Darin zeigt 1 eine schematische Darstellung einer zwischen einer Dekorschicht (2) und einem Trägerformteil (3) angeordneten Zusammensetzung (1) zur Aufnahme von Weichmachungsmitteln aus der weichmacherhaltigen Dekorschicht (2) und/oder dem weichmacherhaltigem thermoplastischen Trägerformteil (3). Die Zusammensetzung (1) besteht aus einem Klebstoff (4) und einem Molekularsieb (5), insbesondere einem geeigneten zeolithischen Material. It shows 1 a schematic representation of a between a decorative layer ( 2 ) and a carrier molding ( 3 ) arranged composition ( 1 ) for receiving softening agents from the plasticized decorative layer ( 2 ) and / or the plasticized thermoplastic carrier molding ( 3 ). The composition ( 1 ) consists of an adhesive ( 4 ) and a molecular sieve ( 5 ), in particular a suitable zeolitic material.

Ein Interieur-Trägerformteil (3), das mit weichmacherhaltiger PVC-Folie (3) oder Kunstleder oder anderen Dekormaterialien kaschiert werden soll, wird gemäß der Erfindung vor der Weiterverarbeitung mit der Zusammensetzung (1) beschichtet, um die Weichmachermigration mittels dem in der Zusammensetzung (1) enthaltenen Molekularsieb (5) abgefangen und somit eine Beeinträchtigung der Verklebung von Trägerformteil (3) und Dekorschicht unterbunden wird. An interior carrier molding ( 3 ), which contains plasticized PVC film ( 3 ) or artificial leather or other decorative materials is, according to the invention prior to further processing with the composition ( 1 ) to facilitate plasticizer migration by means of the 1 ) contained molecular sieve ( 5 ) intercepted and thus a deterioration of the bonding of carrier molding ( 3 ) and decorative layer is prevented.

Alternativ oder zusätzlich kann das in der Zusammensetzung (1) enthaltene Molekularsieb (5) zur Aufnahme von Weichmachungsmitteln aus einem weichmacherhaltigen thermoplastischen Trägerformteil (3) vorgesehen sein. Alternatively or additionally, in the composition ( 1 ) contained molecular sieve ( 5 ) for receiving softening agents from a plasticized thermoplastic carrier molding ( 3 ) be provided.

Denkbar ist auch eine Einarbeitung des geeigneten zeolithischen Materials (5) in das Trägerformteil (3) oder in ausgewählte Bereiche der Dekorschicht (2), die z.B. aus Leder, Kunstleder, Folien, Textil, etc. gebildet sein und/oder eine Abstandsschicht (Haptikschicht), z.B. aus Abstandsgewirke, Vliese, Gelpolster, Schaumstoffen beinhalten kann. Die Dekorschicht (2) kann mehrschichtig und/oder beschichtet sein und Weichmachungsmittel und PVC oder Derivate enthalten. Also conceivable is incorporation of the suitable zeolitic material ( 5 ) in the carrier molding ( 3 ) or selected areas of the decorative layer ( 2 ), which may be formed, for example, of leather, artificial leather, films, textiles, etc., and / or may include a spacer layer (haptic layer), for example of spacer knits, nonwovens, gel pads, foams. The decorative layer ( 2 ) may be multilayered and / or coated and contain softening agents and PVC or derivatives.

Die erfindungsgemäße Verwendung einer Zusammensetzung (1) zur Aufnahme von Weichmachungsmitteln aus einer weichmacherhaltigen Dekorschicht (2) und/oder einem weichmacherhaltigem thermoplastischen Trägerformteil (3) beinhaltet als Kunststoffbauteil ein beschichtetes, kaschiertes oder verklebtes Auto-, Flugzeug- oder Schiffzubehörteil oder ein Teil eines Auto-, Flugzeug- oder Schiffzubehörteils, bevorzugt ein beschichtetes, kaschiertes oder verklebtes Interieurbauteil. The use according to the invention of a composition ( 1 ) for receiving softening agents from a plasticizer-containing decorative layer ( 2 ) and / or a plasticized thermoplastic carrier molding ( 3 ) includes as plastic component a coated, laminated or glued car, aircraft or marine accessory or part of a car, aircraft or marine accessory, preferably a coated, laminated or glued interior component.

Die positive Wirkung des Molekularsiebs (5) im Klebstoff (4) der Zusammensetzung (1) wird für den Betrachter dadurch erkennbar, daß beispielsweise nach Verkleben eines PVC-haltigen Lederdekors (2) oder einer PVC-Folie (2) auf einem Formkörper (3) keine Ablösungserscheinungen infolge der Weichmachermigration unter dem Lederdekor (2) oder der Folie (3) sichtbar werden. Mit Hilfe des Molekularsiebs (5) im Klebstoff (4) wird die Fertigung von kaschierten Bauteilen deutlich erleichtert und ihre Qualität verbessert. The positive effect of the molecular sieve ( 5 ) in the adhesive ( 4 ) of the composition ( 1 ) becomes apparent to the viewer that, for example, after bonding a PVC-containing leather decor ( 2 ) or a PVC film ( 2 ) on a shaped body ( 3 ) no separation phenomena as a result of plasticizer migration under the leather decor ( 2 ) or the film ( 3 ) become visible. With the help of the molecular sieve ( 5 ) in the adhesive ( 4 ) becomes the manufacturing Of laminated components significantly easier and improves their quality.

Die zwischen der Dekorschicht (2) und dem Trägerformteil (3) angeordnete Zusammensetzung (1) übernimmt in einer bevorzugten Ausführungsform bezüglich der migrierenden Weichmachermoleküle die Funktion einer Sperrschicht. The between the decorative layer ( 2 ) and the carrier molding ( 3 ) composition ( 1 ) takes over in a preferred embodiment with respect to the migrating plasticizer molecules, the function of a barrier layer.

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

  • EP 0307546 B1 [0005] EP 0307546 B1 [0005]
  • GB 851753 [0007] GB 851753 [0007]
  • JP 10251469 [0008] JP 10251469 [0008]

Claims (8)

Zusammensetzung (1) zur Aufnahme von Weichmachungsmitteln aus einer weichmacherhaltigen Dekorschicht (2) und/oder einem weichmacherhaltigem thermoplastischen Trägerformteil (3), wobei die Zusammensetzung (1) zumindest ein Beschichtungsmittel (4) und ein Molekularsieb (5) umfasst und zwischen der Dekorschicht (2) und dem Trägerformteil (3) angeordnet ist, und wobei das Molekularsieb (5) zur adsorptiven Aufnahme von Weichmachungsmitteln geeignet ist und aus einem zeolithischen Material oder einem Kohlenstoffmolekularsieb (carbon molecular sieve, CMS) besteht. Composition ( 1 ) for receiving softening agents from a plasticizer-containing decorative layer ( 2 ) and / or a plasticized thermoplastic carrier molding ( 3 ), the composition ( 1 ) at least one coating agent ( 4 ) and a molecular sieve ( 5 ) and between the decorative layer ( 2 ) and the carrier molding ( 3 ) and wherein the molecular sieve ( 5 ) is suitable for the adsorptive uptake of plasticizers and consists of a zeolitic material or a carbon molecular sieve (CMS). Zusammensetzung (1) nach Anspruch 1, wobei das Beschichtungsmittel (4) einen Klebstoff umfasst, der ein Dispersionsklebstoff oder ein Schmelzklebstoff mit jeweils einer Polyolkomponente und einer Härterkomponente ist und der in einem Anteil von 90 bis 99,999 Gew.-% und das Molekularsieb in einem Anteil von 0,001 bis 10 Gew.-% in der Zusammensetzung (1) enthalten ist. Composition ( 1 ) according to claim 1, wherein the coating agent ( 4 ) comprises an adhesive which is a dispersion adhesive or a hotmelt adhesive having in each case a polyol component and a hardener component and which is present in an amount of from 90 to 99.999% by weight and the molecular sieve in an amount of from 0.001 to 10% by weight in the composition ( 1 ) is included. Zusammensetzung (1) nach Anspruch 1 oder 2, wobei die Partikel des zeolithischen Materials eine Größe im Bereich von 0,1 bis 20 µm aufweisen und das zeolithische Material einen Porenöffnungsdurchmesser im Bereich von 0,5 bis 10,0 nm aufweist. Composition ( 1 ) according to claim 1 or 2, wherein the particles of the zeolitic material have a size in the range of 0.1 to 20 microns and the zeolitic material has a pore opening diameter in the range of 0.5 to 10.0 nm. Zusammenseztung (1) nach einem der Ansprüche 1 bis 3, wobei die weichmacherhaltige Dekorschicht (2) und/oder das weichmacherhaltige thermoplastische Trägerformteil (3) zumindest ein Polymer, ausgewählt aus der Gruppe bestehend aus Polyvinylchlorid, Polyvinylidenchlorid, Polyvinylbutyrat, Polycarbonat, Polyalkyl(meth)acrylat und Copolymeren oder Derivaten davon, aufweist. Association ( 1 ) according to one of claims 1 to 3, wherein the plasticizer-containing decorative layer ( 2 ) and / or the plasticizer-containing thermoplastic carrier molding ( 3 ) at least one polymer selected from the group consisting of polyvinyl chloride, polyvinylidene chloride, polyvinyl butyrate, polycarbonate, polyalkyl (meth) acrylate and copolymers or derivatives thereof. Zusammensetzung (1) nach einem der Ansprüche 1 bis 3, wobei das thermoplastische Trägerformteil (3) zumindest einen Kunststoff aufweist, der ausgewählt ist aus der Gruppe bestehend aus Acrylnitril-Butadien-Styrol (ABS), Styrol-Acrylnitril (SAN), Polystyrol (PS), Polycarbonat (PC), Polyethylen(PE), Polypropylen (PP), Polyamide (PA), oder Mischungen daraus. Composition ( 1 ) according to one of claims 1 to 3, wherein the thermoplastic carrier molding ( 3 ) comprises at least one plastic selected from the group consisting of acrylonitrile-butadiene-styrene (ABS), styrene-acrylonitrile (SAN), polystyrene (PS), polycarbonate (PC), polyethylene (PE), polypropylene (PP), Polyamides (PA), or mixtures thereof. Zusammensetzung (1) nach einem der Ansprüche 1 bis 4, wobei die weichmacherhaltige Dekorschicht (2) und/oder das weichmacherhaltigem thermoplastischen Trägerformteil (3) zumindest ein Weichmachungsmittel, ausgewählt aus der Gruppe der Phthalsäureester, Adipate, Citrate, Trimellitate oder Cyclohexandicarboxylate, aufweist. Composition ( 1 ) according to one of claims 1 to 4, wherein the plasticizer-containing decorative layer ( 2 ) and / or the plasticized thermoplastic carrier molding ( 3 ) has at least one softening agent selected from the group of phthalic acid esters, adipates, citrates, trimellitates or cyclohexanedicarboxylates. Kunststoffbauteil, insbesondere Innenverkleidungsbauteil für Innenräume von Kraftfahrzeugen, mit einem thermoplastischen Trägerformteil (3) und einer weichmacherhaltigen Dekorschicht (2), wobei zwischen dem Trägerformteil (3) und der Dekorschicht (2) eine Zusammensetzung (1) vorgesehen ist, die zumindest ein Beschichtungsmittel (4) und ein Molekularsieb (5) umfasst und zwischen der Dekorschicht (2) und dem thermoplastischen Trägerformteil (3) angeordnet ist, wobei das Molekularsieb (5) zur adsorptiven Aufnahme von Weichmachungsmitteln geeignet ist und aus einem zeolithischen Material oder einem Kohlenstoffmolekularsieb (carbon molecular sieve, CMS) besteht, und wobei das Beschichtungsmittel (4) zum Beschichten und/oder Verkleben der Dekorschicht (2) ausgebildet ist. Plastic component, in particular interior trim component for interior spaces of motor vehicles, with a thermoplastic carrier molding ( 3 ) and a plasticized decorative layer ( 2 ), wherein between the carrier molding ( 3 ) and the decorative layer ( 2 ) a composition ( 1 ) is provided, the at least one coating agent ( 4 ) and a molecular sieve ( 5 ) and between the decorative layer ( 2 ) and the thermoplastic carrier molding ( 3 ), wherein the molecular sieve ( 5 ) is suitable for the adsorptive absorption of softening agents and consists of a zeolitic material or a carbon molecular sieve (CMS), and wherein the coating agent ( 4 ) for coating and / or bonding the decorative layer ( 2 ) is trained. Verwendung einer Zusammensetzung (1) zur Aufnahme von Weichmachungsmitteln aus einer weichmacherhaltigen Dekorschicht (2) und/oder einem weichmacherhaltigem thermoplastischen Trägerformteil (3) gemäß einem der Ansprüche 1 bis 6 zur Herstellung eines Kunststoffbauteils nach Anspruch 7, wobei das Kunststoffbauteil ein beschichtetes, kaschiertes oder verklebtes Auto-, Flugzeug- oder Schiffzubehörteil oder ein Teil eines Auto-, Flugzeug- oder Schiffzubehörteils, bevorzugt ein beschichtetes, kaschiertes oder verklebtes Interieurbauteil ist. Use of a composition ( 1 ) for receiving softening agents from a plasticizer-containing decorative layer ( 2 ) and / or a plasticized thermoplastic carrier molding ( 3 ) according to any one of claims 1 to 6 for the production of a plastic component according to claim 7, wherein the plastic component is a coated, laminated or glued car, aircraft or marine accessory or part of a car, aircraft or marine accessory, preferably a coated, laminated or glued interior component is.
DE102015107173.8A 2015-05-07 2015-05-07 Plastic component with a thermoplastic carrier molding and the use of a composition for absorbing plasticizers Active DE102015107173B4 (en)