DE102006058244A1 - Veneered panel, method for producing a veneered panel and use of broke papers in this method - Google Patents

Veneered panel, method for producing a veneered panel and use of broke papers in this method Download PDF

Info

Publication number
DE102006058244A1
DE102006058244A1 DE200610058244 DE102006058244A DE102006058244A1 DE 102006058244 A1 DE102006058244 A1 DE 102006058244A1 DE 200610058244 DE200610058244 DE 200610058244 DE 102006058244 A DE102006058244 A DE 102006058244A DE 102006058244 A1 DE102006058244 A1 DE 102006058244A1
Authority
DE
Germany
Prior art keywords
veneer
veneered
resin
carrier plate
paper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE200610058244
Other languages
German (de)
Inventor
Johann Lienbacher
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kaindl Flooring GmbH
Original Assignee
Kaindl Flooring GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kaindl Flooring GmbH filed Critical Kaindl Flooring GmbH
Priority to DE200610058244 priority Critical patent/DE102006058244A1/en
Priority to PCT/EP2007/010824 priority patent/WO2008071393A2/en
Publication of DE102006058244A1 publication Critical patent/DE102006058244A1/en
Withdrawn legal-status Critical Current

Abstract

Eine furnierte Platte (10) umfasst eine Trägerplatte (12), welche an wenigstens einer ihrer Oberflächen (12a, 12b) mit einem Furnier (14, 24) verklebt ist. Erfindungsgemäß ist die Verklebung mittels eines mit Harz (18, 28) getränkten Papiers (16, 26) gebildet. Ferner erfindungsgemäß sind auch das Verfahren zur Herstellung einer solchen furnierten Platte (10), sowie die Möglichkeit der Verwendung von Ausschusspapieren, insbesondere aus der Herstellung von Laminatfußbodenpaneelen oder/und Dekorplatten.A veneered panel (10) comprises a support plate (12) bonded to a veneer (14, 24) on at least one of its surfaces (12a, 12b). According to the invention, the bonding is formed by means of a paper (16, 26) impregnated with resin (18, 28). Furthermore, according to the invention, the method for producing such a veneered panel (10), as well as the possibility of using scrap paper, in particular from the production of laminate floor panels and / or decorative panels.

Description

Die Erfindung betrifft eine furnierte Platte umfassend eine Trägerplatte, welche an wenigstens einer ihrer Oberflächen mit einem Furnier verklebt ist.The The invention relates to a veneered panel comprising a support plate, which glued to at least one of their surfaces with a veneer is.

Derartige furnierte Platten sind aus dem Stand der Technik seit langem bekannt. Dabei wird das Furnier mit der Trägerplatte unter Verwendung von Harnstoff- oder Polyvinylacrylat-Leimen mittels Verpressen verklebt. Bei industriellen Verfahren wird in der Regel Harnstoff-Leim in Verbindung mit Härtern eingesetzt, um kürzere Presszeiten zu erreichen. Für die Beleimung der Oberfläche der Trägerplatte wird eine Leimmischanlage sowie eine Leimauftragsanlage benötigt. Der beim Verpressen von Furnier und Trägerplatte eingesetzte Druck beträgt üblicherweise zwischen etwa 6 kg/cm2 und etwa 10 kg/cm2, und die beim Verpressen eingesetzte Temperatur beträgt je nach Leimmischung zwischen etwa 90°C und etwa 130°C.Such veneered panels have long been known in the art. The veneer is glued to the carrier plate using urea or polyvinyl acrylate glues by means of compression. In industrial processes, urea glue is usually used in conjunction with hardeners to achieve shorter pressing times. For the gluing of the surface of the carrier plate a glue mixing plant and a glue application system is required. The pressure used in the pressing of veneer and carrier plate is usually between about 6 kg / cm 2 and about 10 kg / cm 2 , and the temperature used in the pressing is between about 90 ° C and about 130 ° C depending on the glue mixture.

Ausgehend von diesem Stand der Technik ist es Aufgabe der vorliegenden Erfindung, furnierte Platten mit einem alternativen, neuartigen Schichtaufbau, sowie ein alternatives, neuartiges Verfahren zur Herstellung von furnierten Platten bereitzustellen.outgoing from this prior art, it is an object of the present invention Veneered panels with an alternative, novel layer structure, as well as an alternative, novel process for the production of to provide veneered panels.

Diese Aufgabe wird gemäß einem ersten Gesichtspunkt der Erfindung durch eine furnierte Platte der eingangs genannten Art gelöst, bei welcher die Verklebung mittels eines mit Harz getränkten Papiers gebildet ist. Wurde bislang ausschließlich Leim zum Verkleben von Trägerplatte und Furnier eingesetzt, so findet hierfür erfindungsgemäß erstmals Harz Verwendung, und dies auch nicht in der reinen Form, sondern in Form eines mit Harz getränkten Papiers. Hierfür gibt es im Stand der Technik kein Vorbild.These Task is done according to a First aspect of the invention by a veneered panel of the beginning solved kind, in which the bonding by means of a resin-impregnated paper is formed. Was previously only glue for bonding of support plate and veneer used, it is according to the invention for the first time Resin use, and not in the pure form, but in the form of a resin impregnated Paper. Therefor There is no model in the art.

Der Hauptvorteil des neuartigen Schichtaufbaus der erfindungsgemäßen furnierte Platte, insbesondere der Verwendung eines mit Harz getränkten Papiers zur Verklebung von Furnier und Trägerplatte, ist darin zu sehen, dass die Herstellung von furnierten Platten nicht mehr nur auf speziell für deren Herstellung unter Verwendung von Leim ausgestatteten Anlagen erfolgen kann, sondern auch auf Kurztaktpressen, HPL-Pressen (HPL – high pressure laminate) oder CPL-Pressen (continuous pressure laminate), wie sie üblicherweise bei der Herstellung von Laminatfußbodenpaneelen, Dekorplatten, beispielsweise im Möbelbau, oder dergleichen plattenförmigen Materialien eingesetzt werden. Der erfindungsgemäße Schichtaufbau ermöglicht es somit den Herstellern derartiger plattenförmiger Materialien, ihre Produktpalette erweitern und somit ihre Fertigungsanlagen effektiver auslasten zu können, ohne hierfür hohe Investitionskosten aufwenden zu müssen. Insbesondere müssen weder Leimmisch- noch Leimauftragsanlagen angeschafft werden. Mit dem bisherigen Schichtaufbau unter Verwendung von Leim zum Verkleben von Trägerplatte und Furnier war der Einsatz von Kurztaktpressen, HPL-Pressen oder CPL-Pressen nicht möglich, da der Leim aufgrund der Tatsache, dass bei diesen Pressentypen höhere Drücke zum Einsatz kommen als bei herkömmlichen Furnierpressen, durch das Furnier durchschlug, was zu Fleckenbildung führte. Als weiterer Vorteil des erfindungsgemäßen Schichtaufbaus ist anzuführen, dass die Rüst- und Reinigungszeiten bei Leimanlagen entfallen.Of the Main advantage of the novel layer structure of the veneered invention Plate, in particular the use of a resin-impregnated paper for gluing veneer and carrier plate, can be seen in it that the production of veneered panels is no longer limited to special for their Manufacture using equipment equipped with glue done but also on short cycle presses, HPL presses (HPL - high pressure laminates) or CPL (continuous pressure laminate) presses, as commonly used in the art the production of laminate floor panels, Decorative panels, for example in furniture, or the like plate-shaped materials be used. The layer structure according to the invention makes it possible thus the manufacturers of such plate-shaped materials, their product range expand and thus utilize their production facilities more effectively to be able to without this to spend high investment costs. In particular, neither must Leimisch- still glue application systems are purchased. With the previous layer structure using glue for bonding from support plate and veneer was the use of short-cycle presses, HPL presses or CPL pressing not possible because of the glue due to the fact that with these press types higher pressures are used as in conventional Veneer presses through which veneer penetrated, causing staining led. Another advantage of the layer structure according to the invention is that the setup and cleaning times for glue systems omitted.

Als besonders geeignet hat sich der Einsatz von Harnstoff-Harz oder/und Melamin-Harz oder/und Harnstoff-Melamin-Harz erwiesen, wie es auch zum Tränken von Dekorpapieren bei der Herstellung von Laminatfußbodenpaneelen oder/und Dekorplatten eingesetzt wird.When The use of urea resin or / and has been particularly suitable Melamine resin or / and urea-melamine resin proved as well for watering of decor papers in the manufacture of laminate flooring panels and / or decorative panels is used.

Ferner kann das Papier vor dem Tränken mit Harz ein Flächengewicht von zwischen etwa 13 g/m2 und etwa 150 g/m2 aufweisen. Darüber hinaus kann die zum Tränken des Papiers verwendete Harzmenge zwischen dem etwa 1,0-Fachen und dem etwa 3,0-Fachen von dessen Flächengewicht betragen.Further, the paper may have a basis weight of between about 13 g / m 2 and about 150 g / m 2 before impregnation with resin. In addition, the amount of resin used to impregnate the paper can range from about 1.0 times to about 3.0 times its basis weight.

Auch dies entspricht den bei der Herstellung von Laminatfußbodenpaneelen oder/und Dekorplatten üblicherweise verwendeten Parametern.Also this is the same as in the production of laminate flooring panels and / or decorative panels usually used parameters.

In Weiterbildung der Erfindung kann das Furnier eine Dicke von zwischen etwa 0,2 mm und etwa 2,5 mm, vorzugsweise von zwischen etwa 0,5 mm und etwa 0,7 mm, aufweisen. Der erfindungsgemäße Schichtaufbau eignet sich somit für alle weltweit üblichen Furnierdicken. Ebenso eignet sich der erfindungsgemäße Schichtaufbau für alle weltweit üblichen Furnierarten.In Further development of the invention, the veneer can have a thickness of between about 0.2 mm and about 2.5 mm, preferably between about 0.5 mm and about 0.7 mm. The layer structure according to the invention is suitable thus for all worldwide Veneer thickness. Likewise, the layer structure according to the invention is suitable for all worldwide standard Veneers.

Als Furnier kann sowohl ein einstückiges Furnier als auch ein aus Furnierstreifen durch Stumpfverleimung zusammengesetztes Furnier eingesetzt werden. Lediglich aus Furnierstreifen mittels Leimfaden zusammengesetzte Furniere eignen sich nicht, da der Leimfaden bei den eingesetzten, im Vergleich zur herkömmlichen Furnierherstellung erheblich höheren Drücken durch das Furnier durchschlägt und zu Fleckenbildung führen würde.When Veneer can be both a one-piece Veneer as well as a veneer strip by butt gluing composite veneer are used. Only from veneer strips using glued thread composite veneers are not suitable because the glue thread used in the, compared to the conventional one Veneer production significantly higher To press pierces through the veneer and lead to staining would.

Die erfindungsgemäße Art der Verklebung von Furnier- und Trägerplatte kann selbstverständlich auf einer einzigen oder alternativ auch auf beiden Oberflächen der Trägerplatte eingesetzt werden. Alternativ zur beidseitigen Aufbringung von Furnier kann ferner vorgesehen sein, dass die Trägerplatte auf ihrer einen Oberfläche mit Furnier und auf ihrer anderen Oberfläche mit einem Gegenzugpapier, beispielsweise mit einem Natron-Kraftpapier oder einem Dekorpapier, verklebt ist.The inventive type of Bonding of veneer and carrier plate of course on a single or alternatively on both surfaces of the support plate be used. Alternatively to two-sided application of veneer can also be provided that the carrier plate on its one surface with Veneer and on its other surface with a countertransport paper, for example, with a soda-kraft paper or decorative paper, is glued.

Wie dies an sich bekannt ist, kann die Trägerplatte aus Span- oder Fasermaterial gebildet sein, insbesondere kann sie eine Spanplatte oder/und eine LDF-Platte oder/und eine MDF-Platte oder/und eine HDF-Platte oder/und eine OSB-Platte oder/und eine Span-Tischlerplatte (auch "Span-Stabsperrholz" genannt) sein.As this is known per se, the carrier plate made of chip or fiber material In particular, it may be a chipboard and / or a LDF board and / or MDF board and / or HDF board and / or an OSB board and / or a chipboard board (also called chipboard plywood).

Nach einem weiteren Gesichtpunkt betrifft die vorliegende Erfindung ein Verfahren zur Herstellung einer erfindungsgemäßen furnierten Platte, umfassend die Schritte Bereitstellen einer Trägerplatte, Bereitstellen eines Furniers, Bereitstellen einer für die Verklebung des Furniers mit der Trägerplatte bestimmten Schicht und Verkleben der Trägerplatte mit dem Furnier mittels der Schicht unter Verwendung einer Presseneinrichtung, wobei der Schritt des Aufbringens der die Verklebung des Furniers mit der Trägerplatte bestimmten Schicht erfindungsgemäß das Anordnen eines mit Harz getränkten Papiers zwischen Trägerplatte und Furnier umfasst.To In another aspect, the present invention relates to A method for producing a veneered panel according to the invention, comprising the steps of providing a carrier plate, providing a veneer, Provide a for the gluing of the veneer with the carrier plate certain layer and bonding the carrier plate with the veneer by means of the layer using a press device, wherein the step of applying the gluing of the veneer with the carrier plate certain layer according to the invention arranging a resin impregnated Paper between support plate and veneer covers.

Wie vorstehend bereits erwähnt eignet sich für die Durchführung dieses Verfahrens besonders eine Kurztaktpresse oder/und eine HPL-Presse oder/und eine CPL-Presse. Ferner kann die Pressentemperatur beispielsweise zwischen etwa 150°C und etwa 185°C betragen oder/und kann der Pressendruck zwischen etwa 20 kg/cm2 und etwa 80 kg/cm2 betragen. Dabei können die Pressentemperatur und der Pressendruck in Abhängigkeit von der Holzart des Furniers, der Stärke des Furniers und gewünschtenfalls weiterer Parameter gewählt werden. Als Pressenzeit kann vorzugsweise eine Zeit zwischen etwa 20 Sekunden und etwa 60 Sekunden gewählt werden. Als Pressbleche werde üblicherweise glatte seidenmatte Pressbleche verwendet. Nach Wunsch oder/und Bedarf können die Pressbleche aber auch eine andere Oberflächenstruktur aufweisen.As already mentioned above, a short-cycle press or / and an HPL press or / and a CPL press are particularly suitable for carrying out this method. Further, the press temperature may be, for example, between about 150 ° C and about 185 ° C or / and the press pressure may be between about 20 kg / cm 2 and about 80 kg / cm 2 . In this case, the press temperature and the press pressure depending on the wood type of the veneer, the thickness of the veneer and, if desired, further parameters can be selected. The pressing time may preferably be a time between about 20 seconds and about 60 seconds. As press plates usually smooth satin-mat pressed sheets are used. However, if desired or / and required, the press plates may also have a different surface structure.

Hinsichtlich der Harze, Papiere, Furniere und Trägerplatten, die bei dem erfindungsgemäßen Verfahren zum Einsatz kommen können, sei auf die vorstehenden Ausführungen zu den Abwandlungsmöglichkeiten der erfindungsgemäßen furnierten Platte verwiesen.Regarding the resins, papers, veneers and support plates used in the process according to the invention can be used be to the above statements to the possibilities of modification of veneered according to the invention Plate directed.

Wird die Trägerplatte beidseitig mit Furnier verklebt, oder auf ihrer einen Oberfläche mit Furnier und auf ihrer anderen Oberfläche mit einem Gegenzugpapier verklebt, so kann der hierfür erforderliche Schichtaufbau in einem einzigen Pressschritt verklebt werden. In diesem Pressschritt kann ferner ein Overlaypapier zur Versiegelung der Fumieroberfläche mit verpresst werden.Becomes the carrier plate glued on both sides with veneer, or on its one surface with Veneer and on its other surface with a pull-back paper glued, so can this required layer structure glued in a single pressing step become. In this pressing step may also be an overlay paper for sealing the fumigation surface be pressed with.

Vorstehend wurde bereits ausgeführt, dass die mit Harz getränkten Papiere, welche in der erfindungsgemäßen furnierten Platte und bei dem erfindungs gemäßen Verfahren zu deren Herstellung eingesetzt werden, jenen Papieren entsprechen, die bei der Herstellung von Laminatfußbodenpaneelen oder/und Dekorplatten als Dekorpapiere verwendet werden. Nun kommt es bei der Herstellung von Laminatfußbodenpaneelen oder Dekorplatten gelegentlich vor, dass diese Dekorpapiere, beispielsweise aufgrund eines nicht vorherzusehenden Maschinenstillstands, zu lange gelagert werden, sodass das Harz zu stark trocknet bzw. auskondensiert. Die Folge ist, dass diese Dekorpapiere zur Herstellung von Laminatfußbodenpaneelen oder Dekorplatten nicht mehr verwendet werden können, da in diesem Fall die Gefahr einer Fleckenbildung oder Offenporigkeit an der Sichtfläche des Laminatfußbodenpaneels oder/und der Dekorplatte bestehen würde. Zu lange gelagerte Dekorpapiere müssen daher ausgesondert und als Sondermüll entsorgt werden, was mit entsprechenden Kosten verbunden ist. Weitere Gründe dafür, dass ein Dekorpapier als Ausschusspapier ausgesondert werden muss, können ein zu hoher Harzauftrag, ein zu geringer Harzauftrag oder eine falsche Rezeptur der Harzmischung sein. Ferner kommt es vor, dass Restmengen von Dekorpapieren mit einem nicht mehr für den Vertrieb geeigneten, weil unmodern gewordenen Dekor als Ausschuss behandelt werden müssen.above has already been executed that with resin soaked Papers which in the veneer plate according to the invention and in the inventive method used for their manufacture correspond to those papers, in the manufacture of laminate flooring panels and / or decorative panels be used as decor papers. Now it comes in the production of laminate floor panels or Decorative panels occasionally suggest that these decorative papers, for example due to an unforeseen machine downtime, too long be stored so that the resin dries too much or condenses out. The result is that these decorative papers for the production of laminate flooring panels or decorative panels can no longer be used, since in this case the Danger of staining or open porosity on the visible surface of the Laminatfußbodenpaneels and / or the decorative panel would exist. Too long stored decor papers have to Therefore, be discarded and disposed of as hazardous waste, what with corresponding costs. Other reasons for choosing a decorative paper as Waste paper must be rejected, can be too high resin order, Too little resin application or a wrong formulation of the resin mixture be. It also happens that residual amounts of decorative papers with no longer for one the distribution suitable, because unfashionable decor as committee must be treated.

Es hat sich jedoch gezeigt, dass sich solche Ausschusspapiere ohne Weiteres noch für die erfindungsgemäße Verklebung von Trägerplatte und Furnier eignen. Daher betrifft die vorliegende Erfindung nach einem weiteren Gesichtpunkt auch die Verwendung von Ausschusspapieren, welche beispielsweise aus der Herstellung von Laminatfußbodenpaneelen stammen, bei der Herstellung einer erfindungsgemäßen furnierten Platte, insbesondere unter Einsatz des erfindungsgemäßen Herstellungverfahrens.It However, it has been shown that such broke papers without More for the bond according to the invention from support plate and veneer are suitable. Therefore, the present invention relates to Another aspect is the use of scrap paper, which, for example, from the production of laminate flooring panels in the production of a veneered panel according to the invention, in particular using the production process of the invention.

Auch wenn die mit Harz getränkten Papiere üblicherweise an ihren Ober- und Unterseiten einen unterschiedlichen Harzauftrag haben, spielt es erfindungsgemäß keine Rolle, ob das mit Harz getränkte Papier gewendet oder ungewendet auf die Trägerplatte aufgebracht wird. Ferner können nicht nur Ausschuss-Dekorpapiere, sondern auch Ausschuss-Overlaypapiere verwendet werden.Even if the papers impregnated with resin usually have a different resin application on their upper and lower sides, it does not matter according to the invention whether the resin-impregnated paper turned or unswept applied to the carrier plate. Further, not only scrap decorative papers but also reject overlay papers can be used.

Nachzutragen ist noch, dass mit dem erfindungsgemäßen Herstellungsverfahren auch Kleinmengen ab einem Stück furnierte Platte problemlos hergestellt werden können.Begrudge is still that with the manufacturing method of the invention also Small quantities from one piece Veneered plate can be easily manufactured.

Nachzutragen ist ferner, dass aufgrund der höheren eingesetzten Pressendrücke das Furnier stärker verdichtet wird als nach dem herkömmlichen Furnierverfahren. Aus dieser höheren Verdichtung resultiert eine verglichen mit dem herkömmlichen Herstellungsverfahren größere Glattheit der Oberfläche der furnierten Platte nach deren Entnahme aus der Presseneinrichtung und somit ein verringerter Schleifaufwand im Zuge der weiteren Verarbeitung.Begrudge is further that because of the higher used pressing pressures the veneer is more compacted is considered after the conventional Veneer procedures. Out of this higher Compaction results compared to the conventional one Manufacturing process greater smoothness the surface the veneered plate after its removal from the press device and thus a reduced grinding effort in the course of further processing.

Schließlich kann im Bedarfsfall auf die Sichtfläche des Furniers noch eine dessen Abnutzung mindernde Schutzschicht aufgebracht werden. Hierfür eignet sich jede aus dem Stand der Technik zu diesem Zweck bekannte Ausführungsvariante.Finally, can if necessary, on the visible surface of the veneer still one of its wear-reducing protective layer be applied. Therefor Any known from the prior art for this purpose Embodiment.

Die Erfindung wird im Folgenden anhand der beigefügten Zeichnung an einem Ausführungsbeispiel näher erläutert werden. Es stellt dar:The Invention will be explained in more detail below with reference to the accompanying drawings of an embodiment. It shows:

1 ein grobschematisches Ablaufdiagramm zur Erläuterung des Verfahrens zur Herstellung der erfindungsgemäßen furnierten Platte. 1 a rough schematic flow diagram for explaining the method for producing the veneered panel according to the invention.

In 1 ist eine erfindungsgemäße furnierte Platte ganz allgemein mit 10 bezeichnet. Sie umfasst eine Trägerplatte 12, die auf ihren beiden Oberflächen 12a und 12b jeweils mit einem Furnier 14 bzw. 24 belegt ist. Die Verklebung des Furniers 14, das in dem dargestellten Ausführungsbeispiel von einem einstückigen Furnierfixmaß gebildet ist, wird mittels eines Papiers 16 bewerkstelligt, welches mit einem in der Zeichnung gepunktet angedeuteten Harz 18 getränkt ist.In 1 is a veneered panel according to the invention in general with 10 designated. It comprises a carrier plate 12 on both surfaces 12a and 12b each with a veneer 14 respectively. 24 is occupied. Gluing the veneer 14 , which is formed in the illustrated embodiment of a one-piece veneer fixed dimension, is by means of a paper 16 accomplished, which with a dotted in the drawing indicated resin 18 is soaked.

In analoger Weise wird zur Verklebung des Furniers 24 ein mit Harz 28 getränktes Papier 26 eingesetzt. Im Unterschied zum Furnier 14 ist das Furnier 24 jedoch ein aus stumpfverleimten Furnierstreifen 24a, 24b zusammengesetztes Furnierfixmaß, wobei die Stumpfverleimung in 1 durch den Strich 30 angedeutet ist.In an analogous way, the gluing of the veneer 24 one with resin 28 soaked paper 26 used. Unlike the veneer 14 is the veneer 24 but one of blunt veneer strips 24a . 24b composite veneer fixation, wherein the butt bonding in 1 by the stroke 30 is indicated.

Obgleich dies vorstehend nicht ausdrücklich erwähnt worden ist, versteht es sich von selbst, dass die beiden Papiere 16, 26 nicht identisch ausgebildet zu sein brauchen, insbesondere nicht das gleiche Flächengewicht aufzuweisen brauchen. Ferner können die Harze 18, 28 unterschiedlich zusammengesetzt sein. Vorzugsweise kommen erfindungsgemäß Harnstoff-Harze oder Melamin-Harze oder Harnstoff-Melamin-Harzgemische zum Einsatz. Schließlich können sich auch die Furniere 14, 24 voneinander unterscheiden, und zwar sowohl hinsichtlich der Holzart als auch hinsichtlich ihrer Dicke D als auch hinsichtlich ihrer Herstellung als Schälfurnier oder Messerfurnier. Hinsichtlich der Holzart können alle bekannten Furniere eingesetzt werden.Although not explicitly mentioned above, it goes without saying that the two papers 16 . 26 not need to be identical, in particular need not have the same basis weight. Furthermore, the resins 18 . 28 be composed differently. Preferably according to the invention urea resins or melamine resins or urea-melamine resin mixtures are used. Finally, the veneers can also be 14 . 24 differ from each other, both in terms of the type of wood and in terms of their thickness D and in terms of their production as a peeled veneer or sliced veneer. With regard to the type of wood, all known veneers can be used.

In 1 ist ferner das Verfahren zur Herstellung der erfindungsgemäßen furnierten Platte grobschematsich dargestellt. Bei diesem Herstellungsverfahren wird in einem Schritt a zunächst eine Trägerplatte 12 bereitgestellt, in einem Schritt b ein mit der Trägerplatte 12 zu verklebendes Furnier 14 und in einem Schritt c eine für die Verklebung des Furniers 14 mit der Trägerplatte 12 bestimmte Schicht, die erfindungsgemäß von einem mit Harz 18 getränkten Papier 16 gebildet ist. Anschließend wird zunächst das harzgetränkte Papier 16 von Hand oder automatisch auf die Oberfläche 12a der Trägerplatte 12 aufgelegt und das Furnier 14 auf das harzgetränkte Papier 16 aufgelegt, wiederum entweder von Hand oder automatisch.In 1 Furthermore, the method for producing the veneered panel according to the invention is roughly illustrated. In this production method, in a step a, first a carrier plate 12 provided, in a step b a with the carrier plate 12 glued veneer 14 and in a step c one for the bonding of the veneer 14 with the carrier plate 12 certain layer according to the invention of one with resin 18 soaked paper 16 is formed. Subsequently, the resin-impregnated paper is first 16 by hand or automatically on the surface 12a the carrier plate 12 hung up and the veneer 14 on the resin-impregnated paper 16 in turn, either manually or automatically.

Sofern die Trägerplatte 12 auch an ihrer anderen Oberfläche 12b mit einem Furnier versehen werden soll, werden die entsprechenden Schritte auch für das Furner 24 und das harzgetränkte Papier 26 durchgeführt.If the carrier plate 12 also on its other surface 12b should be provided with a veneer, the corresponding steps are also for the Furner 24 and the resin-soaked paper 26 carried out.

Der so erhaltene Schichtaufbau wird dann in einem Schritt d in eine Presseinrichtung 40 eingebracht, die beispielsweise eine Kurztaktpresse, eine CPL-Presse oder eine HPL-Presse sein kann. In dieser Presseinrichtung wird der Schichtaufbau unter dem Einfluss von erhöhter Temperatur und erhöhtem Druck zu der erfindungsgemäßen furnierten Platte 10 verpresst.The layer structure thus obtained is then in a step d in a pressing device 40 introduced, which may be, for example, a short-cycle press, a CPL press or an HPL press. In this pressing device, the layer structure under the influence of elevated temperature and elevated pressure to the veneered panel according to the invention 10 pressed.

Beispiele:Examples:

Beispiel 1: Eichenfurnier Dicke des Furniers: etwa 0,55 mm Flächengewicht des ungetränkten Papiers: etwa 80 g/m2 Flächengewicht des harzgetränkten Papiers: etwa 200 g/m2 verwendetes Harz: Harnstoff-Melamin-Harz Pressentemperatur: etwa 175°C Pressendruck: etwa 40 kg/cm2 Pressenzeit: etwa 45 Sekunden Beispiel 2: Buchenfurnier Dicke des Furniers: etwa 0,60 mm Flächengewicht des ungetränkten Papiers: etwa 80 g/m2 Flächengewicht des harzgetränkten Papiers: etwa 200 g/m2 verwendetes Harz: Harnstoff-Melamin-Harz Pressentemperatur: etwa 175°C Pressendruck: etwa 40 kg/cm2 Pressenzeit: etwa 45 Sekunden Beispiel 3: Ahornfurnier Dicke des Furniers: etwa 0,60 mm Flächengewicht des ungetränkten Papiers: etwa 80 g/m2 Flächengewicht des harzgetränkten Papiers: etwa 200 g/m2 verwendetes Harz: Harnstoff-Melamin-Harz Pressentemperatur: etwa 175°C Pressendruck: etwa 45 kg/cm2 Pressenzeit: etwa 45 Sekunden Beispiel 4: Kirschbaumfurnier Dicke des Furniers: etwa 0,50 mm Flächengewicht des ungetränkten Papiers: etwa 80 g/m2 Flächengewicht des harzgetränkten Papiers: etwa 200 g/m2 verwendetes Harz: Harnstoff-Melamin-Harz Pressentemperatur: etwa 175°C Pressendruck: etwa 35 kg/cm2 Pressenzeit: etwa 45 Sekunden Example 1: Oak veneer Thickness of the veneer: about 0.55 mm Basis weight of the unimpregnated paper: about 80 g / m 2 Basis weight of the resin-impregnated paper: about 200 g / m 2 used resin: Urea-melamine resin Press temperature: about 175 ° C Press pressure: about 40 kg / cm 2 Press time: about 45 seconds Example 2: beech veneer Thickness of the veneer: about 0.60 mm Basis weight of the unimpregnated paper: about 80 g / m 2 Basis weight of the resin-impregnated paper: about 200 g / m 2 used resin: Urea-melamine resin Press temperature: about 175 ° C Press pressure: about 40 kg / cm 2 Press time: about 45 seconds Example 3: Maple veneer Thickness of the veneer: about 0.60 mm Basis weight of the unimpregnated paper: about 80 g / m 2 Basis weight of the resin-impregnated paper: about 200 g / m 2 used resin: Urea-melamine resin Press temperature: about 175 ° C Press pressure: about 45 kg / cm 2 Press time: about 45 seconds Example 4: cherry tree veneer Thickness of the veneer: about 0.50 mm Basis weight of the unimpregnated paper: about 80 g / m 2 Basis weight of the resin-impregnated paper: about 200 g / m 2 used resin: Urea-melamine resin Press temperature: about 175 ° C Press pressure: about 35 kg / cm 2 Press time: about 45 seconds

Claims (16)

Furnierte Platte (10) umfassend eine Trägerplatte (12), welche an wenigstens einer ihrer Oberflächen (12a, 12b) mit einem Furnier (14, 24) verklebt ist, dadurch gekennzeichnet, dass die Verklebung mittels eines mit Harz (18, 28) getränkten Papiers (16, 26) gebildet ist.Veneered plate ( 10 ) comprising a support plate ( 12 ), which on at least one of their surfaces ( 12a . 12b ) with a veneer ( 14 . 24 ), characterized in that the bonding by means of a resin ( 18 . 28 ) soaked paper ( 16 . 26 ) is formed. Furnierte Platte nach Anspruch 1, dadurch gekennzeichnet, dass das Harz (18, 28) ein Harnstoff-Harz oder/und ein Melamin-Harz oder/und ein Harnstoff-Melamin-Harz ist.Veneered board according to claim 1, characterized in that the resin ( 18 . 28 ) is a urea resin and / or a melamine resin and / or a urea-melamine resin. Furnierte Platte nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass das Papier (16, 26) vor dem Tränken mit Harz (18, 28) ein Flächengewicht von zwischen etwa 13 g/m2 und etwa 150 g/m2 aufweist.Veneered panel according to claim 1 or 2, characterized in that the paper ( 16 . 26 ) before soaking with resin ( 18 . 28 ) has a basis weight of between about 13 g / m 2 and about 150 g / m 2 . Furnierte Platte nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, dass die zum Tränken des Papiers verwendete Harzmenge zwischen dem etwa 1,0-Fachen und dem etwa 3,0-Fachen von dessen Flächengewicht beträgt.Veneered plate according to one of claims 1 to 3, characterized in that used for impregnating the paper Amount of resin between about 1.0 times and about 3.0 times its basis weight is. Furnierte Platte nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass das Furnier (14, 24) eine Dicke (D) von zwischen etwa 0,2 mm und etwa 2,5 mm, vorzugsweise von zwischen etwa 0,5 mm und etwa 0,7 mm, aufweist.Veneered panel according to one of claims 1 to 4, characterized in that the veneer ( 14 . 24 ) has a thickness (D) of between about 0.2 mm and about 2.5 mm, preferably between about 0.5 mm and about 0.7 mm. Furnierte Platte nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, dass das Furnier ein einstückiges Furnier (14) oder ein aus Furnierstreifen (24a, 24b) durch Stumpfverleimung (30) zusammengesetztes Furnier (24) ist.Veneered panel according to one of claims 1 to 5, characterized in that the veneer is a one-piece veneer ( 14 ) or a veneer strip ( 24a . 24b ) by butt bonding ( 30 ) composite veneer ( 24 ). Furnierte Platte nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, dass die Trägerplatte (12) beidseitig (12a, 12b) mit Furnier (14, 24) verklebt ist.Veneered plate according to one of claims 1 to 6, characterized in that the carrier plate ( 12 ) on both sides ( 12a . 12b ) with veneer ( 14 . 24 ) is glued. Furnierte Platte nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, dass die Trägerplatte (12) auf ihrer einen Oberfläche mit Furnier und auf ihrer anderen Oberfläche mit einem Gegenzugpapier, beispielsweise mit einem Natron-Kraftpapier oder einem Dekorpapier, verklebt ist.Veneered plate according to one of claims 1 to 6, characterized in that the carrier plate ( 12 ) is glued on its one surface with veneer and on its other surface with a Gegenzugpapier, for example, with a soda kraft paper or decorative paper, glued. Furnierte Platte nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, dass die Trägerplatte (12) aus Span- oder Fasermaterial gebildet ist, insbesondere eine Spanplatte oder/und eine LDF-Platte oder/und eine MDF-Platte oder/und eine HDF-Platte oder/und eine OSB-Platte oder/und eine Span-Tischlerplatte ist.Veneered plate according to one of claims 1 to 8, characterized in that the carrier plate ( 12 ) is formed of chip or fiber material, in particular a chipboard and / or an LDF board and / or an MDF board and / or an HDF board and / or an OSB board and / or a chipboard. Verfahren zur Herstellung einer furnierten Platte (10) nach einem der Ansprüche 1 bis 9, umfassend die Schritte: a) Bereitstellen einer Trägerplatte (12), b) Bereitstellen eines Furniers (14, 24), c) Bereitstellen einer für die Verklebung des Furniers (14, 24) mit der Trägerplatte (12) bestimmten Schicht (16, 26), d) Verkleben der Trägerplatte (12) mit dem Furnier (14, 24) mittels der Schicht (16, 26) unter Verwendung einer Presseneinrichtung (40), dadurch gekennzeichnet, dass der Schritt c) des Bereitstellens der für die Verklebung des Furniers (14, 24) mit der Trägerplatte (12) bestimmten Schicht das Anordnen eines mit Harz (18, 28) getränkten Papiers (16, 26) zwischen Trägerplatte (12) und Furnier (14, 24) umfasst.Method for producing a veneered panel ( 10 ) according to one of claims 1 to 9, comprising the steps: a) providing a carrier plate ( 12 ), b) providing a veneer ( 14 . 24 ), c) providing one for the bonding of the veneer ( 14 . 24 ) with the carrier plate ( 12 ) specific layer ( 16 . 26 ), d) bonding the carrier plate ( 12 ) with the veneer ( 14 . 24 ) by means of the layer ( 16 . 26 ) using a press device ( 40 ), characterized in that the step c) of providing the for the bonding of the veneer ( 14 . 24 ) with the carrier plate ( 12 ) certain layer arranging one with resin ( 18 . 28 ) soaked paper ( 16 . 26 ) between carrier plate ( 12 ) and veneer ( 14 . 24 ). Verfahren nach Anspruch 10, dadurch gekennzeichnet, dass die Presseneinrichtung (40) eine Kurztaktpresse oder/und eine CPL-Presse oder/und eine HPL-Presse ist.Method according to claim 10, characterized in that the press device ( 40 ) is a short-cycle press and / or a CPL press and / or an HPL press. Verfahren nach Anspruch 10 oder 11, dadurch gekennzeichnet dass die Pressentemperatur zwischen etwa 150°C und etwa 185°C beträgt.A method according to claim 10 or 11, characterized the press temperature is between about 150 ° C and about 185 ° C. Verfahren nach einem der Ansprüche 10 bis 12, dadurch gekennzeichnet dass der Pressendruck zwischen etwa 20 kg/cm2 und etwa 80 kg/cm2 beträgt.Method according to one of claims 10 to 12, characterized in that the pressing pressure between about 20 kg / cm 2 and about 80 kg / cm 2 . Verfahren nach einem der Ansprüche 10 bis 13, dadurch gekennzeichnet dass die Presszeit zwischen etwa 20 Sekunden und etwa 60 Sekunden beträgt.Method according to one of claims 10 to 13, characterized that the pressing time is between about 20 seconds and about 60 seconds is. Verfahren nach einem der Ansprüche 10 bis 14, dadurch gekennzeichnet, dass dann, wenn die Trägerplatte (12) beidseitig (12a, 12b) mit Furnier (14, 24) zu verkleben ist oder die Trägerplatte (12) auf ihrer einen Oberfläche mit Furnier und auf ihrer anderen Oberfläche mit einem Gegenzugpapier, beispielsweise mit einem Natron-Kraftpapier, zu verkleben ist, die Verklebung in einem einzigen Pressschritt erfolgt.Method according to one of claims 10 to 14, characterized in that when the carrier plate ( 12 ) on both sides ( 12a . 12b ) with veneer ( 14 . 24 ) or the carrier plate ( 12 ) is to be glued on one surface with veneer and on its other surface with a Gegenzugpapier, for example with a soda kraft paper, the bonding takes place in a single pressing step. Verwendung von Ausschusspapieren, welche beispielsweise aus der Herstellung von Laminatfußbodenpaneelen oder/und Dekorplatten stammen, bei der Herstellung einer furnierten Platte (10) nach einem der Ansprüche 1 bis 9, insbesondere unter Einsatz des Verfahrens nach einem der Ansprüche 10 bis 15.Use of broke papers, which originate for example from the production of laminate floor panels and / or decorative panels, in the manufacture of a veneered panel ( 10 ) according to one of claims 1 to 9, in particular using the method according to one of claims 10 to 15.
DE200610058244 2006-12-11 2006-12-11 Veneered panel, method for producing a veneered panel and use of broke papers in this method Withdrawn DE102006058244A1 (en)