DE10019816A1 - A process for coating a yarn as well as textile fabric produced thereby - Google Patents

A process for coating a yarn as well as textile fabric produced thereby

Info

Publication number
DE10019816A1
DE10019816A1 DE2000119816 DE10019816A DE10019816A1 DE 10019816 A1 DE10019816 A1 DE 10019816A1 DE 2000119816 DE2000119816 DE 2000119816 DE 10019816 A DE10019816 A DE 10019816A DE 10019816 A1 DE10019816 A1 DE 10019816A1
Authority
DE
Grant status
Application
Patent type
Prior art keywords
yarn
characterized
surface
coating
gas phase
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE2000119816
Other languages
German (de)
Inventor
Dietmar Wirtz
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ASTEN AG EUPEN
Original Assignee
ASTEN AG EUPEN
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

A method for coating a yarn, wherein said yarn is exposed to a gaseous phase from whence monomers settle on the surface of the yarn in a polymerized state. In order to provide a yarn with a microstructured and especially dirt repellant surface, the yarn is a flock yarn or a chenille yarn. A yarn produced in such a way is especially suitable for use as a skin in paper machines.

Description

Die Erfindung betrifft ein Verfahren zur Beschichtung eines Garns, bei dem dieses einer Gasphase ausgesetzt wird, aus der heraus sich Monomere an der Oberfläche des Garn anlagern und dabei polymerisieren. The invention relates to a process for coating a yarn, in which this gas phase is exposed from the out monomers deposit on the surface of the yarn and thereby polymerize.

Derartige Beschichtungsverfahren sind beispielsweise für Garne in Form von Monofila menten allgemein bekannt. Such coating methods are generally known, for example, for yarns in the form of Monofila elements. Die dabei aus der Gasphase heraus angelagerten Monomere bilden auf der Oberfläche eines derart behandelten Monofilaments eine polymerisierte Dünnschicht, die mit dem Material des Monofilaments eine sehr innige und damit haltbare Verbindung eingeht. The thereby deposited from the gas phase monomers form on the surface of the thus treated monofilament a polymerized thin film, which undergoes a very intimate and durable bond with the material of the monofilament. Häufig wird die Dünnschichtanlagerung im Wege einer sogenannten Plasmapoly merisation durchgeführt, bei der es sich um ein Vakuumbeschichtungsverfahren handelt. Frequently, the Dünnschichtanlagerung by way of a so-called Plasmapoly polymerization is carried out, in which there is a vacuum deposition process. Dieses Verfahren ist aufgrund der niedrigen Prozeßtemperatur zum Beschichten von Kunst stoffen besonders gut geeignet. This process is due to the low process temperature for coating art particularly suitable materials. Die abgeschiedenen Polymerschichten lassen sich durch eine gezielte Prozeßführung in weiten Bereichen verändern und auf verschiedenste Anforderungen einstellen. The deposited polymer layers can be changed by a targeted process control within a wide range and adjust to different requirements. Hierdurch lassen sich Oberflächen und deren Eigenschaften konstruieren, die sich mit anderen Verfahren kaum realisieren lassen. In this way, let surfaces and construct their properties, which can hardly be realized by other methods. Ein Vorteil der Plasmapolymerisation ist auch darin zu sehen, daß der gesamte Prozeß in einer abgeschlossenen Vakuumkammer stattfindet und daher nur sehr geringe Mengen meist ungiftiger Prozeßgase zum Einsatz kommen und hieraus resultiert ein relativ hohes Maß an Umweltverträglichkeit, die auch in guten Recyc lingeigenschaften besteht, da die nur, im dicken Schichten das Materialverhalten beim Recycling kaum beeinflussen. An advantage of the plasma can also be seen that the entire process takes place in an enclosed vacuum chamber and, therefore, only very small amounts usually non-toxic process gases are used and this results in a relatively high degree of environmental compatibility, which is traveling characteristics even in good Recyc as the only in thick layers hardly influence the material behavior during recycling.

Bei der Plasmapolymerisation wird ein Gas (Plasma) erzeugt, das durch äußere Anregung mit Hilfe elektromagnetischer Strahlung freie Elektronen, Ionen und Neutralteilchen enthält. In the plasma polymerization, a gas (plasma) is generated by means of electromagnetic radiation contains by external excitation of free electrons, ions and neutral particles. Wenn dieses Gas unter stark verringertem Druck steht, können nur die geladenen Teilchen, dh im wesentlichen die sehr leichten Elektronen, Energie aufnehmen. When this gas is under a greatly reduced pressure, can only the charged particles, ie essentially absorb the very light electrons energy. Durch Einbringung spezieller Monomere in ein solches Niederdruckplasma werden auf die Moleküle aufgrund des Zusammenstoßes mit den Elektronen Energien übertragen. By incorporation of specific monomers in such a low-pressure plasma are transmitted with the electron energies on the molecules due to the collision. Obwohl das Plasma selbst nahezu Raumtemperatur besitzt, entspricht die Energie der Monomere einer extrem hohen Temperatur, so daß sie dazu in der Lage sind, chemische Bindungen an der Oberfläche des zu beschichtenden Materials aufzubrechen und Reaktionen in Gang zu setzen, die normalerweise erst bei hohen Temperaturen ablaufen können. Although the plasma itself has nearly room temperature, the energy of the monomers an extremely high temperature, so that they are capable of forming chemical bonds break up on the surface of the material to be coated and to set reactions in motion, and are generally only at high temperatures corresponding to can run. Auf diese Weise können die gewünschten Hochtemperatureffekte erreicht werden, ohne daß es zu einer thermischen Belastung des Beschichtungsgutes kommt. In this way, the desired high temperature effects can be achieved without resulting in a thermal loading of the coating material. Da nach erfolgter Plasmapolymerisation im wesentlichen nur noch die Eigenschaften der neu abgeschiedenen Polymere Auswirkungen zeigen, lassen sich die Oberflächeneigenschaften derart behandelter Monofilamente gezielt beeinflussen. Because after the plasma essentially only the properties of the newly deposited polymers exhibit effects, the surface properties such treated monofilaments can specifically influence. Je nach Art der eingesetzten Monomere und der gewählten Prozeßparameter läßt sich beispielsweise eine hydrophobe oder hydrophile Monofilamentoberfläche erzeugen. Depending on the type of monomers used and the selected process parameter is a hydrophobic or hydrophilic monofilament can be produced, for example. Es lassen sich somit schmutzabweisende Eigenschaften erzeugen oder die Anziehungskräfte zwischen einer Oberfläche und einem damit in Kontakt befindlichen Substrat gezielt steuern. thus, it is possible to produce soil-repellent properties or control the attractive forces between a surface and a substrate in contact therewith specifically. Ein anderer mittels der Plasmabeschichtung erzeugter Effekt besteht beispielsweise in der Verbesserung der Farbechtheit des behandelten Another means of the plasma coating is generated effect, for example, in the improvement of the color fastness of the treated

Bekannt ist die Plasmabeschichtung von Garnen bisher nur bei Monofilamenten, mit denen sich zwar textile Flächengebilde für verschiedenste Anwendungsfälle herstellen lassen. the plasma coating of yarns is known so far only in monofilaments, which indeed can be produced fabrics for various applications. Dennoch sind für bestimmte Verwendungszwecke textiler Flächengebilde auch andere Arten von Garnen wünschenswert oder unverzichtbar, so daß die Aufgabe der Erfindung darin besteht, ein Verfahren vorzuschlagen, mit dem sich andere Garne als solche in Monofila mentform in ihren Oberflächeneigenschaften beeinflussen lassen. However, other types of yarns are desirable or essential for certain uses of textile sheet materials, so that the object of the invention is to propose a method which can be other yarns as such, in form Monofila ment affect their surface properties.

Ausgehend von einem Verfahren der eingangs beschriebenen Art wird diese Aufgabe erfindungsgemäß dadurch gelöst, daß das Garn ein Flockgarn oder Chenillegarn ist. Starting from a method of the type described at the outset, this object is achieved in that the yarn is a flocked yarn or chenille yarn.

Überraschenderweise hat sich herausgestellt, daß auch diese Garne, die aus mindestens einem in Längsrichtung verlaufenden Seelenfaden und einer Vielzahl von senkrecht hierzu ausgerichteten Kurzfasern bestehen, erfolgreich und wirkungsvoll mit einer Beschichtung aus einer Gasfaser heraus versehen lassen. Surprisingly, it has been found that these yarns can also be composed of at least one running in the longitudinal direction of core yarn and a plurality of perpendicular thereto aligned short fibers successfully and efficiently provided with a coating of a gas fiber out. Diese Erkenntnis ist keineswegs selbstverständlich, da bei Flockgarn aufgrund der klebetechnischen Verbindung zwischen den orthogonalen Kurz fasern (Flock) und der Seele negative Auswirkungen auf die Integrität des Garns zu befürch ten waren. This finding is not self-evident, since flock yarn due to technical adhesive connection between the orthogonal short fibers (flock) and the soul negative impact on the integrity of the yarn th to befürch were. Derartige Beeinträchtigungen treten bei dem erfindungsgemäßen Verfahren jedoch nicht auf, so daß sich das mit Hilfe dieses Verfahrens hergestellte Garn zum einem durch spezielle physikalisch-geometrische Eigenschaften in Form einer Oberfläche mit einer Mikro struktur als auch durch besondere Oberflächeneigenschaften auszeichnet, die durch die Poly merdünnschicht erzeugt werden. However, such drawbacks do not occur in the inventive method, so that the yarn produced by this process is characterized, on the one by special physical and geometrical properties in the form of a surface having a micro-structure as well as by special surface properties merdünnschicht by the poly generated become.

Das erfindungsgemäße Verfahren erlaubt somit die Herstellung eines Garns, das zum Beispiel die Selbstreinigungseigenschaften der Blätter der Lotus-Pflanze nachahmt, wobei der soge nannte "Lotus-Effekt" darin besteht, daß eine Oberfläche zum einen eine mikrostrukturierte Gestalt besitzt und daher keine hinreichend großen Anhaftstellen für Schmutzpartikel bietet. The inventive method thus allows the production of a yarn which mimics the self-cleaning properties of the leaves of the lotus plant, for example, the so-called "Lotus effect" consists in that a surface on the one hand has a micro-structured form, and therefore, no sufficiently large attachment sites provides for dirt particles. Dieser Teil des Lotus-Effekts wird bei dem Garn gemäß dem erfindungsgemäßen Verfahren von den orthogonalen Kurzfasern verwirklicht, die dem Garn eine "Bürstenstruktur" verleihen, wobei - insbesondere im verwobenen Zustand eines solchen Garns - die mögliche Kontaktfläche für Schmutzpartikel lediglich von den Stirnseiten der Kurzfasern (Borsten) gebildet wird, so daß die Kontaktfläche denkbar gering ist. This part of the lotus effect is realized in the yarn according to the method of the orthogonal short fibers, which give the yarn a "brush structure", where - particularly in the woven state of such a yarn - the possible contact surface for dirt particles only from the ends of the short fibers (bristles) is formed so that the contact surface is conceivable low.

Der zweite Teil des Lotus-Effekts beruht auf der Aktivierung der Oberflächenenergie der mikrostrukturierten Oberfläche, die bei dem erfindungsgemäßen Verfahren durch die Beschichtung aus der Gasphase ermöglicht wird. The second part of the lotus effect based on the activation of the surface energy of the microstructured surface is in the inventive method possible through the coating from the gas phase. Diese erhöhte Oberflächenenergie, die aufgrund der erfindungsgemäßen Beschichtung die gesamte Oberfläche des Garns betrifft, bewirkt eine erhebliche Steigerung des beispielsweise abstoßenden Effekts auf Schmutz partikel. This increased surface energy, which relates to the entire surface of the yarn due to the coating of the invention causes a substantial increase in, for example, repellent effect on dirt particles. Schmutzpartikel können allenfalls an den kleinen stirnseitigen Kontaktflächen der Kurzfasern anhaften und werden beispielsweise von Wassertropfen, die aufgrund der abweisenden Eigenschaften des Garn nicht bis auf den Seelenfaden vordringen können, regelrecht überrollt, dabei mitgenommen und somit von der Oberfläche entfernt. Dirt particles can adhere at most at the small end-face contact surfaces of the short fibers and, for example, of water drops, which can be up to the core thread to penetrate due to the repellent properties of the yarn not literally overwhelmed entrained thereby and thus removed from the surface.

Garne, die nach dem erfindungsgemäßen Verfahren hergestellt sind, zeichnen sich daher durch äußerst vorteilhafte schmutzabweisende Eigenschaften aus, wie sie sich aufgrund der fehlenden mikrostrukturierten Flächenkomponenten bei plasmabeschichteten Monofilamenten nach dem Stand der Technik nicht entfernt erzielen lassen. Yarns made by the inventive process, therefore, are characterized by extremely beneficial soil-repellent properties, as they can not be due to the lack microstructured surface components in plasma-coated monofilaments according to the prior art achieve away.

Um den erfindungsgemäßen Beschichtungsvorgang auch bei Trägergarnen aus temperatur empfindlichen Werkstoffen durchführen zu können, wird vorgeschlagen, daß die Gasphase ein Vakuum-Plasma ist. In order to perform the coating process according to the invention even with support yarns of temperature-sensitive materials, it is proposed that the gas phase is a vacuum plasma.

Zur Erzielung einer besonders schmutzabweisenden Eigenschaft wird vorgeschlagen, daß als Monomere die Stoffe Fluorkarbone verwendet werden. To achieve a particularly stain-proofing property is proposed that can be used as monomers substances fluorocarbons.

Die Erfindung umfaßt des weiteren ein Flockgarn oder Chenillegarn oder ein ähnliches Garn mit radial ausgerichteten Kurzfasern, das dadurch gekennzeichnet ist, daß seine Oberfläche mit einer aus einer Gasphase heraus aufgebrachten polymerisierten Dünnschicht aus einem Monomer versehen ist. The invention further comprises a flocked yarn chenille yarn or yarn or similar with radially oriented short fibers, which is characterized in that its surface is provided with a coating applied from a gas phase thin film of a polymerized monomer.

Die besonders schmutzabweisenden Eigenschaften eines derartigen Garns werden dadurch erzielt, daß beide Komponenten des in der Natur vorkommenden "Lotus-Effekts" nach gebildet werden, und zwar sowohl die mikrostrukturierte Oberfläche durch die radial ver laufenden Kurzfasern als auch die durch die Dünnschicht erreichte Oberflächenaktivierung. The especially soil-repellent properties of such a yarn are achieved in that both components of the naturally occurring "lotus effect", after formed, both the microstructured surface by the radially ver running short fibers and the surface activation achieved by the thin film.

Alternativ schlägt die Erfindung ein Flockgarn oder Chenillegarn vor, das dadurch gekenn zeichnet ist, daß die Oberfläche eines Garn, aus dem die ungefähr radial zu der Längsachse des Trägergarns verlaufenden Kurzfasern gebildet werden, vor seiner Verbindung mit dem Trägergarn mit einer aus einer Gasphase heraus aufgebrachten polymerisierten Dünnschicht versehen ist. Alternatively, the invention proposes a flocked yarn or chenille yarn, which is characterized labeled in characterized in that the surface of a yarn, from which the approximately radial to the longitudinal axis of the Trägergarns short fibers are formed, before its connection to the support yarn with a coating applied from a gas phase polymerized thin film is provided.

Hierbei kann entweder vor der Verbindung von Trägergarn und Kurzfasern eine separate Plasmabeschichtung des Trägergarns durchgeführt werden, oder aber es wird auf diesen Schritt verzichtet, wodurch sich die schmutzabweisenden Eigenschaften des erhaltenen Flockgarn oder Chenillegarns je nach Anwendungsfall kaum ändern, da die Schmutzpartikel den Bereich des Trägergarns aufgrund der abstoßenden Wirkung der radialen Kurzfasern ohnehin kaum erreichen können. Here, a separate plasma coating of Trägergarns can be carried out either before the connection of support yarn and short fibers, or will be omitted this step, whereby the dirt-repellent properties of the obtained flocked yarn or chenille yarn hardly change depending on the application, since the dirt particles to the region of the Trägergarns due to the repulsive effect of the radial short fibers can achieve in any case hardly.

Vorteilhafterweise handelt es sich bei der Gasphase um ein Vakuumplasma, in das wiederum vorzugsweise Monomere in Form von Fluorkarbonen eingebracht werden. Advantageously, it is in the gaseous phase to a vacuum plasma, are introduced into the turn, preferably in the form of monomers fluorocarbons.

Gegenstand der Erfindung ist außerdem ein textiles Flächengebilde, das einen wesentlichen Anteil eines Flockgarns oder Chenillegarns, wie es zuvor beschrieben wurde, enthält. The invention is also a textile fabric containing a substantial proportion of a flocked yarn chenille yarn or as previously described.

Eine besonders vorteilhafte Anwendung eines derartigen textilen Flächengebildes besteht darin, daß es als Papiermaschinenbespannung, beispielsweise als Trockensieb einer Papier maschine, verwendet wird. A particularly advantageous application of such a fabric is that it is used as paper machine clothing, such as a drying wire of a paper machine. Hier sind die hervorragenden schmutzabweisenden Eigenschaften eines derartigen Flächengebildes, beispielsweise in Form eines Gewebes, besonders er wünscht, da die Verschmutzungsproblematik, insbesondere mit dem stetig ansteigenden Altpapieranteil bei der Papierherstellung, zunehmende Bedeutung bekommt. Here are the excellent soil-repellent properties of such a sheet, for example in the form of a fabric, particularly he wishes, since the pollution problem, particularly with the ever-increasing percentage of recycled paper in papermaking, gets increasingly important.

Die Erfindung wird nachfolgend anhand eines Ausführungsbeispiels des erfindungsgemäßen Verfahrens näher erläutert: The invention is explained in more detail below using an exemplary embodiment of the inventive method:
Ein handelsübliches Flockgarn, das aus einem Polyesterseelenfaden und im elektrostatischen Verfahren darauf aufgebrachten Polyester-Kurzfasern (Flock) besteht, wird in einem kontinuierlichen Prozeß einer Vakuum-Plasmapolymerisationsanlage zugeführt, in deren Vakuumkammer ein Druck von ca. 1-100 Pa und einer Temperatur von ca. 20°C herrscht. A commercial flocked yarn consisting of a polyester core yarn and in the electrostatic method applied thereto polyester short fibers (flock) is supplied in a continuous process a vacuum Plasmapolymerisationsanlage, in the vacuum chamber a pressure of about 1-100 Pa and a temperature of ca . 20 ° C prevails. Das Plasma wird z. The plasma z. B. durch Mikrowellenstrahlung eines Magnetrons bei einer Frequenz z. For example, by microwave radiation at a frequency of a magnetron z. B. von 2,45 GHz erzeugt. produced as of 2.45 GHz. Alternativ ist auch eine Plasmaerzeugung mittels einer Gleichspannungsquelle (Gleichstromentladung) oder einer Wechselspannungsquelle (z. B. 50 Hz oder 13,56 MHz) möglich. Alternatively, a plasma generating means of a DC voltage source (DC discharge) or an alternating voltage source (eg., 50 Hz or 13.56 MHz) is possible. Dem Plasma wird ein Fluorkarbon z. The plasma is a fluorocarbon such. B. C 4 F g oder CF 4 als Monomer zugeführt, das sich sowohl an den Oberflächen der Kurzfasern als auch der Seelenfaser in Form einer polymerisierten Dünnschicht ablagert. B. C 4 F g or CF 4 is supplied as a monomer, which is deposited on both the surfaces of the short fibers and the core fiber in the form of a polymerized thin film.

Claims (10)

  1. 1. Verfahren zur Beschichtung eines Garns, bei dem dieses einer Gasphase ausgesetzt wird, aus der heraus sich Monomere an der Oberfläche des Garns anlagern und dabei polymerisieren, dadurch gekennzeichnet , daß das Garn ein Flockgarn oder Chenillegarn ist. 1. A process for coating a yarn, in which this gas phase is subjected to attach monomers from which on the surface of the yarn and thereby polymerize, characterized in that the yarn is a flocked yarn or chenille yarn.
  2. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß die Gasphase ein Vakuum- Plasma ist. 2. The method according to claim 1, characterized in that the gas phase is a vacuum plasma.
  3. 3. Verfahren nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß als Monomere Fluorkarbone verwendet werden. 3. The method of claim 1 or 2, characterized in that there are used as monomers fluorocarbons.
  4. 4. Flockgarn oder Chenillegarn oder ein ähnliches Garn mit radial ausgerichteten Kurzfasern, dadurch gekennzeichnet, daß seine Oberfläche mit einer aus einer Gasphase heraus aufgebrachten polymerisierten Dünnschicht aus einem Monomer versehen ist. 4. The flocked yarn chenille yarn or yarn or similar with radially oriented short fibers, characterized in that its surface is provided with a coating applied from a gas phase thin film of a polymerized monomer.
  5. 5. Garn, dadurch gekennzeichnet, daß die Oberfläche eines Garns, aus dem ungefähr radial zu der Längsachse eines Trägergarns verlaufende Kurzfasern gebildet werden, vor seiner Verbindung mit dem Trägergarn mit einer aus einer Gasphase heraus aufgebrachten polymerisierten Dünnschicht versehen ist. 5. Yarn, characterized in that the surface of a yarn formed from the approximately radial to the longitudinal axis of a Trägergarns short fibers, is provided with a coating applied from a gas phase polymerized thin film prior to its connection to the support yarn.
  6. 6. Garn nach Anspruch 4 oder 5, dadurch gekennzeichnet, daß die Gasphase ein Vakuumplasma ist. 6. A yarn according to claim 4 or 5, characterized in that the gas phase is a vacuum plasma.
  7. 7. Garn nach einem der Ansprüche 4 bis 6, dadurch gekennzeichnet, daß die Monomere Fluorkarbone sind. 7. A yarn according to any one of claims 4 to 6, characterized in that the monomers are fluorocarbons.
  8. 8. Textiles Flächengebilde, dadurch gekennzeichnet, daß es einen wesentlichen Anteil eines Garns nach einem der Ansprüche 4 bis 7 enthält. 8. A textile fabric, characterized in that it contains a substantial proportion of a yarn according to any one of claims 4 to 7th
  9. 9. Papiermaschinenbespannung, dadurch gekennzeichnet, daß sie aus einem textilen Flächengebilde nach Anspruch 8 besteht. 9. The paper machine clothing, characterized in that it consists of a textile fabric of claim 8.
  10. 10. Trockensieb, dadurch gekennzeichnet, daß es aus einem textilen Flächengebilde nach Anspruch 8 besteht. 10. dryer fabric, characterized in that it consists of a textile fabric of claim 8.
DE2000119816 2000-04-20 2000-04-20 A process for coating a yarn as well as textile fabric produced thereby Withdrawn DE10019816A1 (en)