The macromolecule composite self-adhering water-proof coiled material
Technical field
The utility model relates to a kind of waterproof roll, a kind of macromolecule composite self-adhering water-proof coiled material of more specifically saying so with self-adhesion performance.
Background technology
As everyone knows, polymer membranes is a kind of waterproofing materials of function admirable, generally is used for roofing, the waterproof of basement, the protection against the tide of industry and civilian construction, the water-tight corrosion-proof of structure such as freezer, swimming pool, subway, tunnel, drinking water pool, sewage reservoir.It is the lamination composite water-proof structure and the job practices thereof of bottom with the double-sided self-adhesive waterproof coiled materials that Chinese patent 03122800.3 discloses a kind of, be sheet type coiled material straticulate structure, with double-sided self-adhesive waterproof coiled materials as the bottom waterproofing course, one sticking face and base adhesive of double-sided self-adhesive waterproof coiled materials, another bonding plane connects one to two layer of common waterproof roll, forms the lamination composite of water-proof coiled material.But matcoveredn above the above-mentioned lamination composite water-proof structure.Construction sequence is as follows: a, base treatment; B, brushing base treatment agent; C, negative and positive angle, inlet for stom water, gutter, board and tube, wall pipe easy to leak place connection detail are handled, after evenly the brushing base treatment agent was treated its drying, the double-sided self-adhesive extra play was done in the part; D, double-sided self-adhesive waterproof coiled materials paving; E, waterproof roll overlap joint; F, on self-adhesive layer the common waterproof roll of paving, compress compacting with pressure roller; G, waterproof roll are received head; H, do topping.There is following defective in the compound construction method of this waterproof roll: (1) is after a sticking face and base adhesive, when another bonding plane connects common waterproof roll, all has viscosity owing to double-sided self-adhesive waterproof coiled materials is two-sided, the construction technical requirement height of this moment, the position that the artificial construction makes common coiled material be superimposed upon on the double-sided self-adhesive waterproof coiled materials easily produces dimensional errors.Double-sided self-adhesive coiled material and common waterproof roll will be superimposed when (2) constructing at the scene, this work progress troublesome poeration is wasted time and energy.Even problems such as bonding is not firm can appear between coiled material.
The utility model content
The utility model technical issues that need to address, promptly the purpose of this utility model is for a kind of macromolecule composite self-adhering water-proof coiled material is provided.This macromolecule composite self-adhering water-proof coiled material the time can not produce dimensional errors in construction, and can omit double-sided self-adhesive coiled material and common waterproof roll this working procedure that is superimposed, and is time saving and energy saving.
Technical problem of the present utility model can solve by taking following measure: the macromolecule composite self-adhering water-proof coiled material, its design feature is, comprise macromolecule coiled material layer and rubber asphalt self-adhesive layer, macromolecule coiled material layer and rubber asphalt self-adhesive layer are one-body molded, the rubber asphalt self-adhesive layer is compounded in macromolecule coiled material layer bottom surface, and the bottom surface of rubber asphalt self-adhesive layer is provided with one deck separation layer; The rubber asphalt self-adhesive layer has adhibit quality.
The utility model technical solution problem, can also take following measure:
Described macromolecule coiled material layer is provided with overlap edge, macromolecule composite self-adhering coiled material can be connected into random length or width by described overlap edge, and described overlap edge does not have the rubber asphalt self-adhesive layer.
Preceding described separation layer is for being coated with the silicon separation layer.
Preceding described macromolecule coiled material layer is made of polythene PE membrane material or PE single face composite membrane.
Preceding described macromolecule coiled material layer is made of polyvinylchloride membrane material or PE single face composite membrane.
Preceding described macromolecule coiled material layer is made of ethylene-vinyl acetate modified bitumen intermingling material.
Preceding described macromolecule coiled material layer is made of the TPO waterproof roll.
Macromolecule composite self-adhering coiled material fabric width can be 1m, 1.5m or 2.0m.
The utlity model has following outstanding effect:
1, the utility model is because one-body molded with macromolecule coiled material layer and rubber asphalt self-adhesive layer, when construction, can disposablely be laid in the basic unit, the operation that is equivalent to twice lay waterproof roll is economized slightly once, on the one hand can be time saving and energy saving, improve efficiency of construction, accelerate construction progress, can avoid producing the position dimension deviation on the other hand, improve construction quality and construction effect.
2, because being combined with each other, rubber asphalt self-adhesive layer of the present utility model and macromolecular material form a kind of product, therefore, make rubber asphalt self-adhesive layer and polymer material layer form one, bonding firmly, the water resistance of product can be effectively improved, the self-healing performance after product is hindered by hard thing chromium can also be improved.
3, the utility model macromolecular compounded waterproof material fabric width can be 1.0m, 1.5m, 2.0m, reduces seam than fabric width 1.0m tack coiled material, saves cost, increases the waterproof assurance coefficient; The utility model can be in basal plane moisture 18% following self-adhesion construction; Also can be in self-adhesion construction more than the environment temperature-8 ℃.Enlarged the range of application of tack waterproof roll.
Description of drawings
Fig. 1 is the schematic diagram of the utility model specific embodiment 1.
Fig. 2 is the schematic diagram of the utility model specific embodiment 2.
When Fig. 3 is the utility model specific embodiment 2, the sectional drawing at overlap edge position.
The specific embodiment
Below in conjunction with specific embodiment the utility model is specifically described.
Specific embodiment 1:
In Fig. 1, the macromolecule composite self-adhering water-proof coiled material, form by polymer material layer 1 and rubber asphalt self-adhesive layer 2, described polymer material layer 1 is made of polyethylene (PE) membrane material (or PE single face composite membrane), before described rubber asphalt self-adhesive layer (2) be heavily to hand over 90# pitch to be formed by type SBS rubber and other two kinds of synthetic high polymer elastic bodys and base oil, antioxidant, stabilizing agent and high-quality.Described rubber asphalt self-adhesive layer 2 is compounded on polymer material layer 1 bottom surface, and described rubber asphalt self-adhesive layer 2 has viscosity; Described rubber asphalt self-adhesive layer 2 can be compounded in the overlap edge position, and the bottom surface of rubber asphalt self-adhesive layer 2 is compounded with one deck and is coated with silicon separation layer 3.
The utility model can be taked following method construction: during construction, can earlier the macromolecule composite self-adhering water-proof coiled material be led to open overlaying, paste the location again.Slowly extract out from the bottom surface of macromolecule composite self-adhering water-proof coiled material then and be coated with the silicon barrier paper.Catch up with gas that the macromolecule composite self-adhering water-proof coiled material is compressed compacting in construction basic unit with rubber roll then.In overlapping the slot place when operation of carrying out between coiled material, throw off scrap (bridge) earlier and be coated with the silicon barrier paper, and then compress compacting with air bells removing roll and get final product.Do not have the kind of two-sided self-adhesion at macromolecule composite self-adhering water-proof coiled material overlap edge, adopt hot blast welding job practices.
The utlity model has following performance:
Index name | Measured value | Standard No. |
Hot strength (Mpa) | 10.0 | GB/T17643-1998 |
Elongation at break (%) | 200 | GB18173 |
Low-temperature bending, ℃ | -20 flawlesses | GB18173 |
Permeability resistance, 0.3Mpa, 30mm | Waterproof | GB18173 |
Adhesive property (N/mm) | 2.5 | JC863-2000 |
The moisture 18% o'clock caking property (N/mm) of moist basal plane | 2.0 | JC863-2000 |
Annotate: this table is only applicable to P type PVC composite self-adhering water-proof coiled material; Other macromolecule composite self-adhering water-proof coiled materials 1-4 item index should be by its macromolecule coiled material layer performance indications requirement.
Specific embodiment 2:
In Fig. 2, macromolecule composite self-adhering water-proof coiled material, its fabric width are 1m, 1.5m, 2.0m.Be made of polymer material layer 1 and rubber asphalt self-adhesive layer 2, described polymer material layer 1 is made of polyvinyl chloride (PVC) membrane material, ethylene-vinyl acetate modified bitumen intermingling material, TPO waterproof roll.Before described rubber asphalt self-adhesive layer (2) be heavily to hand over 90# pitch to be formed by type SBS rubber and other two kinds of synthetic high polymer elastic bodys and base oil, antioxidant, stabilizing agent and high-quality.Described rubber asphalt self-adhesive layer 2 is compounded on polymer material layer 1 bottom surface; Preceding described macromolecule coiled material layer 1 is provided with the overlap edge position, the not compound described rubber asphalt self-adhesive layer 2 in described overlap edge position, and the bottom surface of rubber asphalt self-adhesive layer 2 is compounded with one deck and is coated with silicon separation layer 3.When can making construction, the not compound described rubber asphalt self-adhesive layer 2 in overlap edge position two blocks of coiled materials are connected with welding.