CN215560983U - Five-mingzhi mesh fabric - Google Patents

Abstract

The utility model discloses a five-purpose mesh fabric which comprises a first layer, a second layer, a third layer, a fourth layer and a fifth layer which are connected in a weaving mode and distributed layer by layer. The first and fifth layers are configured as cotton yarn or cotton yarn blends, the second and fourth layers are configured as polyester yarn, and the third layer is configured as an intermediate connector yarn. The second layer and the fourth layer are respectively connected with the intermediate connecting yarns, the first layer completely covers the second layer and is provided with mesh jacquard textures, and the fifth layer completely covers the fourth layer. The mesh fabric is of a five-layer weaving structure which is connected with each other after being woven, so that the hollow feeling and the fluffy feeling of an air layer are achieved. The first layer adopts a mesh jacquard process, thereby forming a mesh jacquard effect and having good aesthetic property. The Wumingzhi mesh fabric formed by the five-layer weaving structure has a clean and stiff surface and good fuzzing and pilling resistance.

Description

Five-mingzhi mesh fabric

Technical Field

The utility model relates to the technical field of cloth, in particular to a Wumingzhi mesh fabric.

Background

The sandwich fabric is used as a fabric for manufacturing leisure and sports coat warm clothes and has excellent warm keeping and air permeability. However, the sandwich fabric has fewer layers, cannot form a hollow feeling and a fluffy feeling, and is poor in touch and hand feeling. Moreover, the sandwich fabric is prone to fluffing and pilling, and the user experience is poor, so that improvement is needed.

SUMMERY OF THE UTILITY MODEL

Aiming at the defects in the prior art, the utility model aims to provide a Wumingzhi mesh fabric.

In order to achieve the purpose, the utility model adopts the technical scheme that: the five-open-control mesh fabric comprises a first layer, a second layer, a third layer, a fourth layer and a fifth layer which are connected in a weaving mode and distributed layer by layer, wherein the first layer and the fifth layer are configured to be cotton yarn or cotton blended yarn, the second layer and the fourth layer are configured to be polyester yarn, and the third layer is configured to be middle connecting yarn;

the second layer and the fourth layer are respectively connected with the intermediate connecting yarns, the first layer completely covers the second layer and is provided with mesh jacquard textures, and the fifth layer completely covers the fourth layer.

In one embodiment, the second layer and the fourth layer are configured as fine denier polyester yarns, and the third layer is bound to the fine denier polyester yarns of the second layer and the fourth layer, respectively.

In one embodiment, the fine denier polyester yarn is polyester DTY semi-dull low stretch yarn, and the fineness of the fiber is 30D-50D.

In one embodiment, the fine denier polyester yarn of the second layer and the fine denier polyester yarn of the fourth layer are respectively tucked with the intermediate connecting yarn.

In one embodiment, the cotton yarn or cotton blended yarn is configured as a 30-50 ring spun yarn.

In one embodiment, the fifth layer is configured as a cotton covered polyester plain weave.

In one embodiment, the intermediate connecting yarn is chemical fiber filament with the yarn count of 50D-100D.

In one embodiment, the gram weight of the Wumingzhi mesh fabric is 280-600g/m 2.

After adopting the structure, compared with the prior art, the utility model has the advantages that: the mesh fabric is of a five-layer weaving structure which is connected with each other after being woven, so that the hollow feeling and the fluffy feeling of an air layer are achieved. The first layer adopts a mesh jacquard process, thereby forming a mesh jacquard effect and having good aesthetic property. The Wumingzhi mesh fabric formed by the five-layer weaving structure has a clean and stiff surface and good fuzzing and pilling resistance.

Drawings

The utility model is further illustrated with reference to the following figures and examples:

fig. 1 is a schematic cross-sectional structure view of a wumingzhi mesh fabric of the present invention.

Fig. 2 is a schematic view of a partial surface structure of the wumingzhi mesh fabric of the present invention.

In the figure: a first layer 10; a second layer 20; a third layer 30; a fourth layer 40; and a fifth layer 50.

Detailed Description

The following description is only a preferred embodiment of the present invention, and does not limit the scope of the present invention.

Example, see fig. 1 and as shown in fig. 2: the utility model provides a weaving method of five-purpose mesh fabric, the five-purpose mesh fabric is woven on both sides by a double-side circular knitting machine, and the fabric can be used for leisure sports coat warm clothing. The five-layer fabric comprises a first layer 10, a second layer 20, a third layer 30, a fourth layer 40 and a fifth layer 50 which are connected in a weaving mode and distributed layer by layer, and the five-layer fabric is formed by double-sided weaving through a circular knitting machine. Wherein the first layer 10 and the fifth layer 50 are configured as cotton yarn or cotton blended yarn, the second layer 20 and the fourth layer 40 are configured as polyester yarn, and the third layer 30 is configured as an intermediate connecting yarn, wherein the second layer 20 and the fourth layer 40 are respectively connected with the intermediate connecting yarn. First layer 10 completely covers second layer 20 and fifth layer 50 completely covers fourth layer 40.

The first layer 10 and the fifth layer 50 of the five-bright-mesh fabric adopt a cotton cover polyester weaving method, so that the upper surface and the lower surface of the five-bright-mesh fabric are completely covered by cotton yarn or cotton blended yarn, the surface of the fabric is smooth and clean, and pilling and fluffing are not easy to happen. Further, the first layer 10 is provided with a mesh jacquard texture to enhance the aesthetic appearance of the fabric and the garment being made. Wherein, the first layer 10 adopts the mesh jacquard design, and the parameters such as the size, the spacing and the like of the meshes can be flexibly adjusted according to the market demand and the customer requirement, so as to achieve different mesh jacquard effects and achieve good satisfaction of users. Optionally, the fifth layer 50 is configured as a cotton covered polyester plain weave to differentiate the surface patterns on both sides of the fabric, to improve the fabric identifiability, and to improve the wearing comfort of the wumingzhi mesh fabric. Alternatively, the cotton yarn or cotton blended yarn is configured as a 30-50-inch ring spun yarn. Specifically, the cotton yarn or cotton blended yarn is spun by 30-count ring spinning, 35-count ring spinning, 40-count ring spinning, 45-count ring spinning, or 50-count ring spinning.

The third layer 30 is used as an intermediate layer, the intermediate connecting yarns are used for connecting the polyester yarns of the second layer 20 and the polyester yarns of the fourth layer 40, the intermediate connecting yarns are chemical fiber filaments to form an air layer, the hollow feeling is strong, the fabric is light and warm, and a strong hollow effect can be achieved.

The Wumingzhi mesh fabric is characterized in that the polyester yarns of the second layer 20 and the polyester yarns of the fourth layer 40 are respectively connected with the middle connecting yarns in the weaving process, and the weaving method can ensure that the polyester yarns on two sides of the middle layer are not easily pulled out to form long hook yarns in the fabric using process, so that the defect of fuzzing and pilling caused by pulling of the polyester yarns is overcome, and the area has good fuzzing and pilling resistance. In addition, the first layer 10 and the fifth layer 50 are both cotton yarn, the first layer 10 adopts a mesh jacquard weaving method, so that the fabric has rich texture effect, and the polyester yarn of the second layer 20 and the polyester yarn of the fourth layer 40 are completely covered in the interlayer by a cotton cover polyester weaving method, so that the polyester yarn is not exposed, and the purposes of reducing fluffing and pilling of the fabric are achieved.

Further, the second layer 20 and the fourth layer 40 are configured as fine denier polyester yarns, and the third layer 30 is respectively bound to the fine denier polyester yarns of the second layer 20 and the fine denier polyester yarns of the fourth layer 40. The middle connecting yarn of the third layer 30 is bound with the fine denier polyester yarn of the second layer 20 by tuck connection so as to tightly connect the two. Optionally, the intermediate connecting yarn is chemical fiber filament with yarn count of 50D-100D. For example, the fiber fineness of the intermediate connecting yarn is selected from 50 denier, 60 denier, 70 denier, 80 denier, 90 denier, 100 denier and the like, and the connecting strength of the intermediate connecting yarn is high.

The other side of the middle connecting yarn is bound by a fourth layer of 40 fine denier polyester yarns in a tuck connection mode, so that the upper layer and the lower layer of the fabric are connected through the middle connecting yarn. Wherein the fine denier polyester yarn is polyester DTY semi-dull low stretch yarn, and the fineness of the fiber is 30D-50D. For example, the fiber fineness of the fine denier polyester yarn is selected from the specifications of 30 denier, 35 denier, 40 denier, 45 denier, 50 denier and the like so as to adapt to different fabric processing effects.

In one embodiment, the grammage of the Wumingzhi mesh fabric is 280-600g/m 2. For example, the unit gram weight of the Wumingzhi mesh fabric is set to 280g/m2, 300g/m2, 320g/m2, 340g/m2, 360g/m2, 380g/m2, 400g/m2, 450g/m2, 500g/m2, 550g/m2 and 600g/m 2.

The five-mingzhi mesh fabric is knitted on two sides by a double-side big circular knitting machine, and the original double-side big circular knitting machine needs to be adjusted to adapt to the processing and knitting of the five-mingzhi mesh fabric. Wherein, the knitting arrangement sequence of the double-sided circular knitting machine is adjusted as follows: and two-stage upper disk knitting needles are respectively configured to be a knitting needle B and a knitting needle C, and the arrangement sequence is BC. The four-level knitting needles of the lower disc are respectively configured to be a knitting needle B, a knitting needle C, a knitting needle D and a knitting needle E, the arrangement sequence is BCBCBCDBCBCE, and the knitting needles B, C, D and E represent high and low positions of different knitting needles. Arranging in a triangular mode; two-stage triangles of the upper disc are No. 1 triangles and No. 2 triangles respectively; the four-stage triangles of the lower wall are triangles No. 1, No. 2, No. 3 and No. 4 respectively. And seventy-two moulds are respectively formed between the upper disc and the lower disc, wherein linear materials corresponding to the five-mingzhi mesh fabric are respectively connected and woven between the two-stage triangles of the upper disc and the four-stage triangles of the lower disc. The upper disc and the lower disc are respectively weaved to form an upper layer structure and a lower layer structure of the five-layer connected five-layer fabric, so that the weaving efficiency is high and the weaving effect is good.

The five-layer fabric is five-layer structure, the upper and lower surfaces of the five-layer fabric are made of cotton cover polyester weaving method, and the intermediate connecting yarn is made of chemical fiber filament to form an air layer. The Wumingzhi mesh fabric has smooth surface, is hollow and fluffy, has good elasticity, and has washing resistance, wearing resistance and good heat retention. The five-purpose fabric is provided with mesh jacquard design on the upper surface, so that the five-purpose fabric has abundant surface texture.

The two-sided big circular knitting machine is connected the dacron part of the inner and outer layer fabrics with the middle connecting yarn through tucking mode respectively in the weaving process, so that the middle dacron yarn of the five-mingming mesh fabric is not easy to be pulled out in the using process to form long hooked yarns, and the defect that the five-mingming mesh fabric is fluffed and pilling is avoided.

The upper disc and the lower disc of the double-sided circular knitting machine respectively form a seventy-two die, and the specific arrangement mode of the seventy-two die is as follows.

The first die adopts terylene chemical fiber filaments: the upper disc is knitted with No. 1 triangle tuck and No. 2 triangle floating thread; the No. 1 triangle of the lower plate is weaved with floating threads, and the No. 2 triangle is weaved with tucking; no. 3, No. 4 triangle knitting float yarn.

And the second die adopts terylene chemical fiber filaments: the No. 1 triangular weaving floating thread and the No. 2 triangular weaving tuck are arranged on the upper disc; tucks are woven by No. 1 triangles on the lower disc, floating threads are woven by No. 2 triangles, and the floating threads are woven by No. 3 triangles and No. 4 triangles.

A third mould, which adopts fine denier polyester yarn; the No. 1 triangle and the No. 2 triangle of the upper plate are knitted into a loop; the triangle of the lower plate No. 1, No. 2, No. 3 and No. 4 are all woven floating threads.

A fourth module, which adopts cotton yarn or blended staple fiber yarn; the No. 1 triangle and the No. 2 triangle of the upper plate are knitted into a loop; the triangle of the lower plate No. 1, No. 2, No. 3 and No. 4 is all a weaving floating line.

A fifth mould, which adopts fine denier polyester yarn; the upper disc is a floating line; no. 1 and No. 2 triangles of the lower disc are knitted into loops and No. 3 triangles, and No. 4 triangles are knitted floating threads.

A sixth module, which adopts cotton yarn or blended staple fiber yarn; the upper disc No. 1 triangle and the upper disc No. 2 triangle are all knitted floating threads; no. 1 and No. 2 triangles of the lower disc are knitted into a loop No. 3, and No. 4 triangles are knitted floating threads.

The above six modules are cycled for 5 times to form the arrangement sequence of the first to thirtieth modules.

And a thirty-first die which adopts terylene chemical fiber filaments: the upper disc is knitted with No. 1 triangle tuck and No. 2 triangle floating thread; no. 1 triangle of lower wall weaves the float, No. 2 triangle weaves tucking, No. 3, No. 4 triangle weaves the float.

And a thirty-second die, which adopts terylene chemical fiber filaments: the No. 1 triangular weaving floating thread and the No. 2 triangular weaving tuck are arranged on the upper disc; tucks are woven by No. 1 triangles on the lower disc, floating threads are woven by No. 2 triangles, and the floating threads are woven by No. 3 triangles and No. 4 triangles.

A thirty-third die, which adopts fine denier polyester yarn; the No. 1 triangle and the No. 2 triangle of the upper plate are knitted into a loop; the triangle of the lower plate No. 1, No. 2, No. 3 and No. 4 is all a weaving floating line.

A thirty-fourth module, cotton yarn or blended staple fiber yarn is adopted; the No. 1 triangle and the No. 2 triangle of the upper plate are knitted into a loop; no. 1, No. 2 and No. 4 triangles of the lower disc are all knitted floating threads, and No. 3 is knitted tuck.

A thirty-fifth mould, which adopts fine denier polyester yarn; the upper disc is a braided floating line; no. 1 and No. 2 triangles of the lower disc are knitted into loops and No. 3 triangles, and No. 4 triangles are knitted floating threads.

A thirty-sixth module, cotton yarn or blended staple fiber yarn is adopted; the upper disc No. 1 triangle and the upper disc No. 2 triangle are all knitted floating threads; no. 1 and No. 2 triangles of the lower disc are knitted into loops, and No. 3 and No. 4 triangles are knitted floating threads.

And repeating the first die to the thirtieth die to the sixteenth die to enable the weaving mode of the part to be correspondingly adjusted by matching with other dies.

Sixty-seventh mold, adopting terylene chemical fiber filament: the upper disc is knitted with No. 1 triangle tuck and No. 2 triangle floating thread; the No. 1 triangle of the lower plate is weaved with floating threads, and the No. 2 triangle is weaved with tucking; no. 3, No. 4 triangle knitting float yarn.

Sixty-eight moulds, which adopt terylene chemical fiber filaments: the No. 1 triangular weaving floating thread and the No. 2 triangular weaving tuck are arranged on the upper disc; tucks are woven by No. 1 triangles on the lower disc, floating threads are woven by No. 2 triangles, and the floating threads are woven by No. 3 triangles and No. 4 triangles.

Sixty-ninth mould, fine denier polyester yarn is adopted; the No. 1 triangle and the No. 2 triangle of the upper plate are knitted into a loop; the triangle of the lower plate No. 1, No. 2, No. 3 and No. 4 is all a weaving floating line.

A seventy model, cotton yarn or blended spun yarn is adopted; the upper plate No. 1 triangle and the upper plate No. 2 triangle are knitted into a loop; no. 1, No. 2 and No. 3 triangles of the lower disc are all knitted floating threads, and No. 4 is knitted tuck.

A seventy-first mould, which adopts fine denier polyester yarn; the upper disc is a floating line; no. 1 and No. 2 triangles of the lower disc are knitted into loops, and No. 3 and No. 4 triangles are knitted floating threads.

A seventy-second module, which adopts cotton yarn or blended spun yarn; the upper disc No. 1 triangle and the upper disc No. 2 triangle are all knitted floating threads; no. 1 and No. 2 triangles of the lower disc are knitted into a loop No. 3, and No. 4 triangles are knitted floating threads.

Optionally, the seventy-two module functions are combined, and the five-mingming mesh fabric is knitted according to the weave structure, the yarn arrangement and the yarn length arrangement shown in the following figure.

The double-sided circular knitting machine is adjusted through the modes to weave five-bright-control mesh fabric, the fabric is processed efficiently, the fabric processing is smooth, and the processing efficiency is good.

Furthermore, the double-sided large circular knitting machine comprises a dial and a needle cylinder matched with the dial, wherein the diameter D of the dial is smaller than the diameter D of the needle cylinder, and D-D is larger than or equal to 6mm and smaller than or equal to 12 mm. The double-sided big circular knitting machine adjusts the fit clearance of the dial and the needle cylinder to adapt to different yarns, so that the Wumingzhi mesh fabric with a hollow effect is knitted. Specifically, the difference between the diameter of the dial and the diameter of the cylinder is set to 6mm, 6.5mm, 7mm, 8mm, 9mm, 10mm, 12mm, or the like.

The first die and the second die are used as starting positions for weaving, the length L of the yarn adopted by the first die and the second die is larger than or equal to 16.0cm and smaller than or equal to 19.0cm, and specifically, the length of the yarn is set to be 16mm, 17mm, 18mm, 19mm and the like. When the first die and the second die are used for weaving yarns, the plain needles behind the tuck are knitted by the yarns to downwards press the coils, and then the edge angles of the plain needles are downwards pressed, wherein the pressing amount is a preset value. Alternatively, the pressing amount of the flat pin angular pressing down is set to 1 mm.

In the knitting step, the first die and the second die are intermediate interlayers, 75D/72F DTY semi-dull polyester filament is adopted, the yarn length range is 18.8CM (50 needles), and meanwhile, flat needles behind tucks need to press coils downwards during knitting, and the edges of the flat needles are pressed downwards by 100 threads to play a role in supporting hollow sense.

In the weaving method, the third mould and the fifth mould adopt a weaving method of cotton covered terylene, the cotton yarn on the front surface is 32-inch compact spinning cotton yarn, the terylene is 30D/12F DTY semi-dull low-elasticity terylene yarn, and the yarn length range is 8.8CM (50 needles). In order to achieve this long knitting, the trajectory and the twist angle of the yarn during the knitting are realized by a corresponding triangular shape. Specifically, the first needle pressing position of the upper disc is improved, so that the coil is prevented from retreating, and the first needle pressing position of the lower disc is improved and is set to be a straight line.

Furthermore, the double-sided rounding machine is also provided with two pressing plates, and the pressing plates assist in ring retreating. The first pressing plate is used for preventing the needle-containing coils from floating upwards along with the back knitting needle track, and the second pressing plate is used for adjusting tension of the yarns discharged from the previous die.

Further, the weaving method of the Wumingzhi mesh fabric further comprises the following steps: scutching and rolling, presetting, dyeing and washing, centering, dyeing cotton, drying in a loose mode, setting, inspecting cloth and rolling. The weaving step can finish the gray cloth prepared by the circular knitting machine to obtain the five-layer structure hollow vertical bar double-color fabric.

The pre-setting step comprises the following steps: and arranging and presetting after the preparation of the grey cloth is finished. In the presetting step, the following presetting parameters are adjusted: setting temperature: 200-210 ℃, machine speed: 10-15M/min, overfeed amount: 25 percent. Specifically, the setting temperature is set to 200 ℃, 202 ℃, 205 ℃, 208 ℃, 210 ℃ and the like. The machine speed can be set to 10M/min, 11M/min, 12M/min, 13M/min, 14M/min, 15M/min, etc. The pre-setting fully eliminates the internal stress of the grey cloth, avoids various folding scratches generated in the dyeing process, and can stabilize the gram weight of the finished product.

The dyeing and washing: after the pre-setting, arranging high-temperature vat dyeing, comprising two processes of dye bath and dyeing. Wherein the dye bath process comprises the following parameters: the bath ratio is 1:5, and the pH value of the dye bath is adjusted to 5-6. The dyeing process comprises the following steps: dyeing is started when the liquid temperature in the high-temperature cylinder is 50-60 ℃; then gradually heating to 130 ℃; preserving the heat for 40-60 min at 130 ℃; then cooling and washing. And reduction cleaning is carried out after washing and dyeing, so that the problem of color fastness is avoided, and the fabric is high in attractiveness.

The method comprises the following steps: and after dyeing and washing are finished, taking the cloth and setting in arrangement. In this step, the medium sizing comprises the following medium sizing parameters, temperature: 162-170 ℃, machine speed: 10-15M/min, width: 160-175 CM, overfeeding: 20 to 25 percent. The method specifically comprises the following steps: temperature: 162 deg.C, 163 deg.C, 164 deg.C, 165 deg.C, 167 deg.C, 168 deg.C, 170 deg.C, etc. Machine speed: 10M/min, 11M/min, 12M/min, 13M/min, 14M/min, 15M/min and the like. Breadth: 160cm, 165cm, 170cm, 175cm, etc. Overfeeding: 20%, 22%, 23%, 24%, 25%, etc.

The cotton dyeing: after neutralization, the cotton is dyed in a cylinder, biological enzyme treatment is carried out through enzyme lotion, and then the fabric is put into the enzyme lotion according to the bath ratio of 1:25 and treated for 60min at the temperature of 50 ℃. In the step of dyeing cotton, the formula of the enzyme lotion comprises the following parameters: 0.5g/L of sodium acetate; acetic acid 0.5 g/L; 2g/L of biological enzyme. Wherein the pH value of the enzyme lotion is adjusted to 5.5 by adopting acetic acid. Further, when the soaped fabric is a dark fabric, the soaping frequency of the fabric is not lower than 2 times, 2g/L of silicone oil and 5g/L of raising agent are added into the enzyme lotion.

Fully soaping the dyed cotton, taking the dyed cotton out of a cylinder for dehydration and drying in a loose manner after the soaping is finished.

Shaping: the setting comprises the following setting parameters: temperature: 125-135 ℃, machine speed: 10-16M/min, width: 160-175 CM, overfeed: 30 to 35 percent. The method specifically comprises the following steps: temperature: 125 deg.C, 128 deg.C, 130 deg.C, 132 deg.C, 135 deg.C, etc. Machine speed: 10M/min, 11M/min, 12M/min, 13M/min, 15M/min, 16M/min, and the like. Breadth: 160cm, 165cm, 170cm, 175cm, etc. Overfeeding: 30%, 32%, 33%, 34%, 35%, etc.

After the series of finishing, the gram weight of the fabric is 340g/m 2. The fabric obtained by the method is subjected to a conventional physical and chemical index test, the test method comprises ISO12945-2, 2000REVS, MARTINDALE TESTER, GB/T4802.22500 REVS and wool abrasive materials, and the test results are shown in the following table.

And (4) test conclusion: the Wumingzhi mesh fabric obtained by the embodiment has good performance, and has the characteristics of softness, heat preservation, clean surface, soft hand feeling, washing resistance, wear resistance and the like.

The present invention is not intended to be limited to the particular embodiments shown and described, but is to be accorded the widest scope consistent with the principles and novel features herein disclosed. Other structures and principles are the same as those of the prior art, and are not described in detail herein.

Claims (8)

1. A Wumingzhi mesh fabric is characterized in that: the fabric comprises a first layer, a second layer, a third layer, a fourth layer and a fifth layer which are connected in a weaving mode and distributed layer by layer, wherein the first layer and the fifth layer are configured to be cotton yarn or cotton blended yarn, the second layer and the fourth layer are configured to be polyester yarn, and the third layer is configured to be middle connecting yarn;

the second layer and the fourth layer are respectively connected with the intermediate connecting yarns, the first layer completely covers the second layer and is provided with mesh jacquard textures, and the fifth layer completely covers the fourth layer.

2. The five-ingredient mesh fabric according to claim 1, wherein: the second layer and the fourth layer are configured into fine denier polyester yarns, and the third layer is respectively bound with the fine denier polyester yarns of the second layer and the fine denier polyester yarns of the fourth layer.

3. The five-ingredient mesh fabric according to claim 2, wherein: the fine denier polyester yarn is polyester DTY semi-dull low stretch yarn, and the fineness of the fiber is 30D-50D.

4. The five-ingredient mesh fabric according to claim 2, wherein: the fine denier polyester yarn of the second layer and the fine denier polyester yarn of the fourth layer are respectively connected with the middle connecting yarn tuck.

5. The five-ingredient mesh fabric according to claim 1, wherein: the cotton yarn or the cotton blended yarn is configured into 30-50-English ring spinning yarns.

6. The five-ingredient mesh fabric according to claim 1, wherein: the fifth layer is configured as a cotton covered polyester plain weave.

7. The five-ingredient mesh fabric according to claim 1, wherein: the middle connecting yarn is chemical fiber filament with yarn count of 50D-100D.

8. The five-ingredient mesh fabric according to claim 1, wherein: the gram weight of the Wumingzhi mesh fabric is 280-600g/m 2.