CN215051013U

CN215051013U - Double-faced satin fabric with silk luster

Info

Publication number: CN215051013U
Application number: CN202121173486.0U
Authority: CN
Inventors: 仝晓婷; 陈红霞; 肖俐
Original assignee: Jiangsu Goldsun Textile Science and Technology Co Ltd
Current assignee: Jiangsu Goldsun Textile Science and Technology Co Ltd
Priority date: 2021-05-28
Filing date: 2021-05-28
Publication date: 2021-12-07
Anticipated expiration: 2031-05-28

Abstract

The utility model discloses a two-sided satin surface fabric with silk texture gloss. The fabric is formed by interweaving warp yarns and weft yarns according to a double-faced satin weave; on the front surface of the fabric, in a weave cycle, a first warp and a weft are interwoven every eight weft at intervals, the warp floats on the weft when not interwoven, the warp sinks under the weft when interwoven, a second warp and the weft are interwoven every eight weft at intervals, the weft floats on the warp when not interwoven, the weft sinks under the warp when interwoven, the interweaving rule of odd warps is the same as that of the first warp, and the interweaving rule of even warps is the same as that of the second warp; adjacent interlacing points of odd numbered warp yarns are separated by 4 picks and adjacent interlacing points of even numbered warp yarns are separated by 4 picks. The fabric has excellent skin-friendly performance, cool and silky touch feeling, soft and bright gloss as silk, and high strength, and meets the production and use requirements.

Description

Double-faced satin fabric with silk luster

Technical Field

The utility model belongs to the technical field of domestic fabrics, concretely relates to two-sided satin surface fabric with silk texture gloss.

Background

The acetate fiber has biodegradable performance, and the acetate fiber is paid attention again by fabric developers along with the increasing requirement on environmental protection. The acetate fiber has good skin-friendly performance and is easy to manage, especially the acetate filament fiber has excellent appearance style and hand feeling of the mulberry silk, but the acetate fiber has low strength, and the application of the acetate fiber is limited to a certain extent. In patent application CN112030309A, "a acetate fiber fabric and its production process" selects bright acetate fiber filaments as warp yarns, and S-twisted and Z-twisted filaments obtained by twisting acetate fiber filaments and cationic filaments in a plying manner as weft yarns, and then obtains a garment fabric with high strength, soft and comfortable hand feeling, and strong woolen feeling by satin weaving. Patent application CN106012214A 'Jacquard acetate filament home textile fabric and production method thereof' provides a jacquard acetate filament home textile fabric, wherein warp yarns of the fabric adopt polyester filaments, weft yarns adopt acetate filaments, the weave is large jacquard weave fabric, the finished product width is 160cm, and the fabric is used as summer quilt fabric. As the width of the finished home textile fabric is 250cm, the width requirement of gray fabric is higher, uneven warp tension is more easily generated in wide width weaving processing than in narrow width, and the problem of broken ends is more easily caused due to low warp strength. The polyester filament yarn also has the appearance of silk-like fabric, but the moisture regain of the polyester is low, and the skin-friendly performance of the fabric is poor. Because the home textile bedding fabric is in direct contact with the skin, the skin-friendly comfort of the fabric is an important consideration factor for consumers to purchase, and the fabric can present a high-grade appearance on the basis of comfort and is also an appeal for the consumers.

SUMMERY OF THE UTILITY MODEL

To the technical problem, the utility model provides a two-sided satin surface fabric that contains acetic acid filament, this surface fabric have excellent close skin performance, the nice and cool silky touch, gloss is as gentle bright as silk, powerful height satisfies production and operation requirement.

In order to achieve the above purpose, the utility model adopts the following technical means:

a double-faced satin fabric with silk luster is formed by interweaving warp yarns and weft yarns according to a double-faced satin weave;

on the front surface of the fabric, in a weave cycle, a first warp and a weft are interwoven every eight weft at intervals, the warp floats on the weft when not interwoven, the warp sinks under the weft when interwoven, a second warp and the weft are interwoven every eight weft at intervals, the weft floats on the warp when not interwoven, the weft sinks under the warp when interwoven, the interweaving rule of odd warps is the same as that of the first warp, and the interweaving rule of even warps is the same as that of the second warp; adjacent interlacing points of odd numbered warp yarns are separated by 4 picks and adjacent interlacing points of even numbered warp yarns are separated by 4 picks.

Further, the warp yarns are 70D-90D of core-spun twisted yarns of acetate filaments and nylon filaments, wherein the nylon filaments are core filaments of the core-spun twisted yarns.

Furthermore, the cross-sectional area of the nylon filament is 15% -25% of that of the core-spun twisted yarn.

Further, the weft yarn is one of a modal yarn, a tencel yarn or a viscose filament yarn.

Further, the warp density of the fabric is 280-350 pieces/inch.

The utility model discloses following beneficial effect can be realized:

1. because acetate fiber's brute force is low, is unfavorable for the high warp density of wide breadth to be weavingd, the utility model discloses an adopt the compound silk of acetic acid-polyamide fibre, promote the yarn brute force on the one hand and do benefit to the high warp density wide breadth to be weavingd, embody the outward appearance of acetate filament on the fabric surface on the one hand.

2. The double-faced warp-faced satin weave is adopted, so that the front and back faces of the fabric are in the warp-faced satin weave appearance, namely, the warp yarns are reflected in the fabric appearance, and the fabric is endowed with silky luster and silky smooth and soft touch through high-warp-density weaving.

3. The weft of the fabric is made of regenerated cellulose fibers, so that the fabric has good moisture absorption performance, and the comfort of the fabric is improved.

Drawings

Fig. 1 is the tissue structure diagram of the fabric of the present invention, wherein: the machine direction yarns are warp yarns, the cross direction yarns are weft yarns, ■ indicates warp points, i.e., warp yarns over weft yarns, □ indicates weft points, i.e., weft yarns over warp yarns, successive warp points constitute warp floats, and successive weft points constitute weft floats.

Detailed Description

The technical solution of the present invention will be further explained with reference to the accompanying drawings and specific embodiments.

As shown in fig. 1, the utility model provides a double-faced satin fabric, the front and the back of which are satin weave. The method for analyzing the interweaving rule of the fabric from the front side comprises the following steps: in a weave cycle, warp 1 is interwoven with weft, A is a weft structure point, namely an interweaving point, the other eight warp structure points are warp float long lines, and the warp is interwoven once every eight weft; warp 2 is interwoven with weft, B is a warp structure point, namely an interweaving point, the other eight weft structure points are weft float long lines, and the warp is interwoven once every eight wefts; the interweaving points of two adjacent warp yarns of the

warp yarns

1, 3, 5, 7, 9, 11, 13, 15 and 17 are separated by 4 weft yarns; the interweaving points of two adjacent warp yarns of the

warp yarns

2, 4, 6, 8, 10, 12, 14, 16 and 18 are separated by 4 weft yarns; the odd number of warps constitute the fabric front side and the even number of warps constitute the fabric back side, so that both the front side and the back side of the fabric present a warp satin weave style.

The warp yarn of the fabric is 70D-90D of acetic acid filament/nylon filament core-spun twisted yarn, wherein the nylon filament is core yarn of the core-spun twisted yarn, and the cross-sectional area of the nylon filament is 15% -25% of that of the core-spun twisted yarn. The nylon filament has higher strength, small initial modulus of fiber and soft fiber, improves the strength of the composite yarn and does not reduce the softness of the fabric. After the warp is twisted, the problem that the double-faced satin weave of the long floating long thread is easy to hook is solved.

The weft yarns of the fabric are one of Modal yarns, tencel yarns and viscose filament yarns, so that the fabric has good dimensional stability, absorbs moisture and is breathable, and the fabric is endowed with better comfort performance.

In order to embody the silky luster texture of the fabric, the fabric is woven in a high-warp density mode, and the warp density is 280-350 pieces/inch, so that the double-faced satin weave tissue woven in the high-warp density mode is silky and smooth in touch.

Example 1

The fabric warp is 70D of acetic acid filament/nylon filament core-spun twisted yarn, wherein the nylon filament is core yarn of the composite yarn, and the cross-sectional area of the nylon filament is 15% of that of the core-spun twisted yarn.

The weft of the fabric is 100-inch Modal yarns.

The fabric is woven by a high warp density, the warp density is 350 pieces/inch, and the fabric is woven on an air jet loom.

Example 2

The fabric warp is 90D of acetate filament/nylon filament core-spun twisted yarn, wherein the nylon filament is core yarn of the composite yarn, and the cross-sectional area of the nylon filament is 25% of that of the core-spun twisted yarn.

The weft yarn of the fabric is 60-inch tencel yarn.

The fabric is woven by a high warp density, the warp density is 280 pieces/inch, and the fabric is woven on an air jet loom.

Example 3

The fabric warp is 80D of acetate filament/nylon filament core-spun twisted yarn, wherein the nylon filament is core yarn of the composite yarn, and the cross-sectional area of the nylon filament is 20% of that of the core-spun twisted yarn.

The fabric weft yarns are viscose filament yarns 75D.

The fabric is woven by a high warp density, the warp density is 320 threads/inch, and the fabric is woven on an air jet loom.

Claims

1. A two-sided satin surface fabric with silk gloss which characterized in that: the fabric is formed by interweaving warp yarns and weft yarns according to a double-faced satin weave;

2. The double-sided satin fabric according to claim 1, characterized in that: the warp yarns are 70D-90D of core-spun twisted yarns of acetate filaments and nylon filaments, wherein the nylon filaments are core filaments of the core-spun twisted yarns.

3. The double-sided satin fabric according to claim 2, characterized in that: the cross-sectional area of the nylon filament is 15% -25% of that of the core-spun twisted yarn.

4. The double-sided satin fabric according to claim 1, characterized in that: the weft yarn is one of a modal yarn, a tencel yarn or a viscose filament yarn.

5. The double-sided satin fabric according to claim 1, characterized in that: the warp density of the fabric is 280-350 pieces/inch.