CN214032849U - Nylon-viscose elastic cotton-like fabric - Google Patents

Abstract

The utility model relates to a textile fabric field, concretely relates to glue imitative cotton fabric of bright and beautiful elasticity, interweave by the longitude and latitude yarn and form its characterized in that: the warp yarns and the weft yarns are all core-spun yarns, the warp yarns are viscose-coated nylon yarns, and the weft yarns are nylon-coated spandex yarns. The fabric prepared by the scheme has the moisture absorption property, hand feeling, touch feeling and skin-friendly feeling of cotton fabrics, and meanwhile, the chinlon in the warp and weft yarns also provides a skeleton effect for the fabric, the fabric is free from ironing in the process of wearing, and the cost performance is far lower than that of the cotton fabrics; the fabric can be used for casual trousers and other articles.

Description

Nylon-viscose elastic cotton-like fabric

Technical Field

The utility model relates to a textile fabric field, concretely relates to glue imitative cotton fabric of bright and beautiful elasticity.

Background

Cotton fiber is favored because of its excellent moisture absorption, softness and warmth retention; however, the cotton fiber has poor moisture conductivity and dehumidification, antifouling and mildew resistance, and is easy to deform and lose texture after being washed for many times; and the cost of cotton is high, for example, the market price of 40S long stapled cotton is 3.6-3.8 ten thousand yuan/ton.

The chemical spinning fiber has relatively low cost, various types and different performances, for example, viscose has the advantages of strong hygroscopicity, easy dyeing and bright color, but also has the defects of poor wear resistance, poor elasticity and small strength; the chinlon has the advantages of high strength, good elasticity, wear resistance, small specific gravity, acid and alkali resistance and the like, and also has the defects of small hygroscopicity and poor light resistance; spandex has the advantages of strong elasticity, acid and alkali resistance, sweat resistance and the like, and also has the defect of poor hygroscopicity.

With the further improvement of the consumption level, people pursue the multifunction of clothes, and the wearing experience is greatly reduced due to the fact that the cotton fabric is easy to wrinkle and lose shape after washing.

Disclosure of Invention

The technical problem to be solved by the invention is to provide a cotton-like fabric with appearance, hand feeling and touch feeling aiming at the defects in the prior art, and simultaneously, the color fastness and shape-preserving performance of the fabric are greatly improved.

The viscose nylon elastic cotton-like fabric is formed by interweaving warp yarns and weft yarns, wherein the warp yarns and the weft yarns are core-spun yarns, and the viscose nylon elastic cotton-like fabric is characterized in that the warp yarns are viscose nylon-coated yarns, and the weft yarns are nylon spandex-coated yarns.

Preferably, the warp yarn is a tight-stop spun-bonded bale 20D nylon yarn with 32S/40S/50S/60S, and the twist is 700-800 twist/m.

Preferably, the twist direction of the weft yarn is Z twist.

Preferably, the weft yarn is 100D chinlon-wrapped 40D spandex yarn or 100D chinlon-wrapped 70D spandex yarn or 70D chinlon-wrapped 40D spandex yarn, and the twist is 600-700 twists/m.

The invention has the beneficial effects that:

1. the warp yarns are made of tightly spun viscose wrapped nylon yarns, the viscose is outside, the fabric can be endowed with softer hand feeling, the fabric has good moisture absorption and skin affinity, and the fabric is in direct contact with the skin in the process of wearing, so that better comfort can be endowed. The weft adopts chinlon spandex yarn, and chinlon has good elasticity and wear resistance and can provide better wear resistance for the fabric as the outer layer of the weft.

2. The warp and weft yarns contain the chinlon, so that the fabric can be endowed with better elasticity, the defect that viscose is too soft can be overcome, the skeleton effect of the fabric is achieved, the garment is free from ironing and easy to clean when being taken, and the defect that cotton is easy to wrinkle and difficult to shape after washing is overcome.

3. Compared with cotton fabrics, the cost is greatly reduced, the common cotton leisure fabrics in the market mainly comprise long staple cotton, the price is 3.6-3.8 ten thousand yuan/ton, the fabric is made of chemical fiber materials, the cost is 2.3-2.5 ten thousand yuan/ton, and the cost is reduced by nearly 40%.

Drawings

Fig. 1 is an organizational chart in an embodiment of the present invention.

Detailed Description

As shown in the figure, the nylon-bonded elastic cotton-like fabric is formed by interweaving warp yarns and weft yarns, wherein the warp yarns and the weft yarns are core-spun yarns, the warp yarns are core-spun yarns formed by bonding 11 and wrapping nylon 12, and the weft yarns are core-spun yarns formed by wrapping nylon 21 and spandex 22.

If the fabric is used as leisure pants, the warp yarns adopt 32S tightly-packed 20D nylon yarns wrapped by spun-bonded glue, the twist is 700 twists/meter, the weft yarns adopt 70D nylon-wrapped 40D spandex yarns, and the twist is 600 twists/meter;

or the warp adopts 40S tightly-packed 20D nylon yarn wrapped by spun-bonded glue, the twist is 750 twists/m, the weft adopts 70D 40D spandex yarn wrapped by nylon, and the twist is 600 twists/m.

If the body-building clothes fabric: the warp adopts 50S tightly-packed 20D nylon yarn of spun-bonded rubber bag, the twist is 800 twists/m, or adopts 60S tightly-packed 20D nylon yarn of spun-bonded rubber bag, the twist is 800 twists/m; the weft adopts any one of 70D nylon-wrapped 40D spandex yarn or 100D nylon-wrapped 70D spandex yarn, and the twist is 650 plus 700 twists/meter.

The following plain weave is taken as an example, and the nylon-bonded elastic cotton-like fabric of the utility model is further explained by a specific process, which comprises the following steps:

step S1: the blended yarn is woven, as shown in figure 1, the blended yarn is formed by interweaving warp yarns and weft yarns, wherein the warp yarns and the weft yarns are core-spun yarns, the warp yarns are core-spun yarns formed by binding 11 and nylon 12, and the weft yarns are core-spun yarns formed by binding 21 and 22 nylon.

Step S2: and (4) pretreatment, including long-vehicle refining, preshrinking and blank setting.

Step S3: dyeing by a two-bath method, specifically reactive dyeing viscose and acid dyeing nylon.

Step S4: and (5) drying the fabric processed in the step S3: the drying temperature is 185 ℃, and the vehicle speed is 30 m/min.

Step S5: adding a softening agent and a smoothing agent into the post-setting.

The finished product prepared by the steps has good hygroscopicity, hand feeling, touch feeling and skin-friendly feeling of cotton fabrics, and good elasticity, and is free from ironing in the process of taking ready-made clothes.

It should be noted that the above embodiments are only preferred solutions for clearly explaining the present invention, and the modifications and additions which are not inventive and made by those skilled in the art on the basis of the present invention should fall within the protection scope of the present invention.

Claims (5)

1. The nylon-bonded elastic cotton-like fabric is formed by interweaving warp yarns and weft yarns, wherein the warp yarns and the weft yarns are core-spun yarns, and the nylon-bonded elastic cotton-like fabric is characterized in that: the warp yarns are viscose-coated nylon yarns, and the weft yarns are nylon-coated spandex yarns.

2. The nylon-bonded elastic cotton-like fabric according to claim 1, wherein the viscose of the warp yarns is a spun viscose.

3. The nylon-bonded elastic cotton-like fabric according to claim 1, wherein the warp yarns are 32S or 40S viscose-coated 20D nylon yarns, and the twist is 700-; the weft yarn is 70D chinlon-covered 40D spandex yarn, and the twist is 600 twists/m.

4. The nylon-bonded elastic cotton-like fabric according to claim 1, wherein the warp yarns are 50S or 60S viscose 20D nylon yarns, and the twist is 800 twists/m; the weft yarn is 70D chinlon-wrapped 40D spandex yarn or 100D chinlon-wrapped 70D spandex yarn, and the twist is 650 plus 700 twists/meter.

5. The nylon-bonded elastic cotton-like fabric according to claim 1, wherein the twisting direction of the weft yarns is Z-twist.

Images