CN209384512U - A kind of fibre cement compound sandwich multi-ribbed plate - Google Patents
A kind of fibre cement compound sandwich multi-ribbed plate Download PDFInfo
- Publication number
- CN209384512U CN209384512U CN201822209685.7U CN201822209685U CN209384512U CN 209384512 U CN209384512 U CN 209384512U CN 201822209685 U CN201822209685 U CN 201822209685U CN 209384512 U CN209384512 U CN 209384512U
- Authority
- CN
- China
- Prior art keywords
- fibre cement
- convex rib
- core layer
- muscle
- lightweight core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of fibre cement compound sandwich multi-ribbed plate, belongs to the technical field of concrete prefabricated component component.The component is the lamellar composite battenboard being made of lightweight core layer and the fibre cement surface layer being symmetricly set at left and right sides of lightweight core layer；The convex rib I and convex rib II that several intersect in length and breadth are provided on the inner surface of two layers of the fibre cement surface layer in left and right, vertical muscle is coated in the inside of convex rib I, transverse bar is coated in the inside of convex rib II, ipsilateral vertical muscle and transverse bar intersection are connected to form reinforced mesh, and several rows are overlapped between two reinforced mesh through lightweight core layer through muscle；The left and right sides surface of lightweight core layer be provided with the matched horizontal groove of convex rib I and with the matched vertical groove of convex rib II.The utility model solves the technical issues of being not easy cloth muscle, substantially increases element mechanics performance, and the scope of application of expandable member simplifies manufacture craft, reduces production cost.
Description
Technical field
The utility model relates to the technical fields of concrete prefabricated component component, are especially a kind of compound folder of fibre cement
Core multi-ribbed plate.
Background technique
Traditional composite laminboard is broadly divided into two major classes: one kind is ordinary reinforced concrete composite laminboard, another kind of
It is thin-walled surface layer composite laminboard.
The characteristics of ordinary reinforced concrete composite laminboard is: surface thickness is larger, is built-in with bar frame, intensity, just
The mechanical properties such as degree, anti-bending strength and shear resistance are good, are suitable for carrying biggish occasion --- for example often as Side fascia
It uses；But its maximum shortcoming is exactly --- quality weight, workable occasion are very limited.
Come to be situated between in detail come another traditional composite laminboard --- the thin-walled surface layer composite laminboard that continues below.Traditional thin-walled
The structure of surface layer composite laminboard are as follows: both sides be with a thickness of 2~15cm thin wall cement panel (such as fibre cement panel or
Fiber calcium silicate board with microporous), it is intermediate be light core plate (light core plate can according to the demand of heat preservation or the different function such as sound insulation or fire prevention into
Row selection, there are commonly foam styrofoam, foamed polyurethane plate, foam glass board, foamed ceramic panel, rock wool board, glass fiber cottons
The light weight boards such as plate).The manufacture craft of conventional thin wall layer composite laminboard are as follows: by fibre cement panel (or fiber silico-calcium
Plate) with light core plate by organic agent molding bonded, obtained battenboard is commonly referred to as composite laminboard after fibre cement.
From the above in technique as can be seen that the characteristics of thin-walled surface layer composite laminboard, is: surface layer is thin, light weight, and can benefit
Use have the characteristics that keep the temperature insulate against sound or fire prevention functional material as light core plate, and then make thin-walled surface layer composite laminboard at
For a kind of multifunction board with lightweight, heat preservation or sound insulation or fire prevention.But it also exist in use it is following
Shortcoming: (1) it since surface thickness relatively thin (with a thickness of 2~15cm), is not easy to arrange that reinforcing bar (commonly uses reinforcing bar in component inside
Diameter is 1~φ of φ 8 etc.), it causes the mechanics index of physics such as intensity, the rigidity of composite laminboard very low, is suitable only for as not having
There is the specific function plate of bearing requirements to use, narrow scope of application.(2) due to being by organic glue sticking between surface layer and sandwich layer
Molding, is on the one hand that organic gel is at high cost, has pollution to environment；Another aspect complex manufacturing technology needs first opposite respectively
Plate and middle layer plate are processed, are then bonded twice again；In addition, the globality after bonding is poor.Therefore, from Specific construction
The actual needs of side is set out, prefer to design and produce out a kind of lightweight that can have higher building reason mechanical property, heat preservation or
Sound insulation or fireproof multifunction board, can take into account ordinary reinforced concrete composite laminboard in conventional composite battenboard and
The NEW TYPE OF COMPOSITE sandwich multi-ribbed plate of both thin-walled surface layer composite laminboards advantage, this NEW TYPE OF COMPOSITE sandwich multi-ribbed plate are a kind of energy
Enough smoothly realization inside cloth muscle, the thin-walled surface layer that mechanical property is good, applied widely, manufacture craft is simple, production cost is low are multiple
Co-clip core plate.
Summary of the invention
The purpose of this utility model is exactly directed to above-mentioned existing deficiencies in the technology and provides a kind of fiber water
Mud compound sandwich multi-ribbed plate.The utility model solves the technology that conventional thin wall layer composite laminboard component inside is not easy cloth muscle
Problem is substantially increased using fibre cement composite laminboard as intensity, the rigidity, bending resistance of the thin-walled surface layer composite laminboard of representative
The mechanical properties such as performance and shear resistance, expand the scope of application of component, while also simplifying manufacture craft, reducing production
Cost, the globality for improving component increase a kind of with higher building reason mechanical property for concrete prefabricated component component family
Lightweight, heat preservation or sound insulation or fireproof multifunction board.
The purpose of this utility model can be realized by following technique measures:
The fibre cement compound sandwich multi-ribbed plate of the utility model is by lightweight core layer and to be symmetricly set on a lightweight core layer left side
The lamellar composite battenboard that the fibre cement surface layer of right two sides is constituted；It is all provided on the inner surface of two layers of the fibre cement surface layer in left and right
Being equipped with convex rib I that several intersect in length and breadth and convex rib II, (convex rib I can sufficiently wrap up vertical muscle, convex
Transverse bar can sufficiently be wrapped up by playing shape rib II, further provide installation foundation for the arrangement of bar frame, smoothly solve biography
The technical issues of being not easy cloth muscle in system thin-walled surface layer composite laminboard component), it is coated with vertical muscle in the inside of convex rib I,
It is coated with transverse bar in the inside of convex rib II, ipsilateral vertical muscle and transverse bar intersection are connected to form reinforced mesh, in two steel
Several rows are overlapped between muscle mesh sheet, and through the muscle that runs through of lightweight core layer, (two reinforced mesh are by forming steel after overlapping through muscle
Muscle rack substantially increases intensity, rigidity, anti-bending strength and the shear resistance of fibre cement composite laminboard)；In lightweight core layer
Left and right sides surface be provided with the matched horizontal groove of convex rib I and matched vertical recessed with convex rib II
Slot (for horizontal groove for embedding convex rib I, vertical groove is for embedding convex rib II).
Lightweight core layer described in the utility model is foam styrofoam, foamed polyurethane plate, foam glass board, foamed ceramics
Any one of plate, rock wool board, glass fiber cotton plate are (since lightweight core layer has the characteristics that keep the temperature or insulate against sound or prevent fires using such
Functional material core plate, so fibre cement compound sandwich multi-ribbed plate component just have many advantages, such as heat preservation or sound insulation or fire prevention).
The usual thickness range with a thickness of 2~15cm(thin-walled surface layer of fibre cement surface layer described in the utility model).
The fibre cement compound sandwich multi-ribbed plate of the utility model is by lightweight core layer and to be symmetricly set on a lightweight core layer left side
The lamellar composite battenboard that the fibre cement surface layer of right two sides is constituted；It is all provided on the inner surface of two layers of the fibre cement surface layer in left and right
Being equipped with several convex ribs I, (convex rib I can sufficiently wrap up vertical muscle, further provide for the arrangement of bar frame
Installation foundation, smoothly solves the technical issues of being not easy cloth muscle in conventional thin wall layer compound sandwich board member), in convex
The equal level in the inside of rib I is coated with vertical muscle, and several are overlapped between the vertical muscle of the height such as left and right sides through lightweight core layer
Through muscle (between the vertical muscle of the height such as left and right sides two by through muscle overlap joint after improve fibre cement composite laminboard
Intensity, rigidity, anti-bending strength and shear resistance)；It is provided with and convex rib I on the left and right sides surface of lightweight core layer
Matched horizontal groove (horizontal groove is for embedding convex rib I).
Lightweight core layer described in the utility model is foam styrofoam, foamed polyurethane plate, foam glass board, foamed ceramics
Any one of plate, rock wool board, glass fiber cotton plate are (since lightweight core layer has the characteristics that keep the temperature or insulate against sound or prevent fires using such
Functional material core plate, so fibre cement compound sandwich multi-ribbed plate component just have many advantages, such as heat preservation or sound insulation or fire prevention).
The usual thickness range with a thickness of 2~15cm(thin-walled surface layer of fibre cement surface layer described in the utility model).
The design principle of the utility model is as follows:
The utility model smoothly solves traditional thin-walled by the convex rib to gather in fibre cement surface layer inner surface
The technical issues of being not easy cloth muscle in surface layer compound sandwich board member, substantially increases using fibre cement composite laminboard as representative
The mechanical properties such as intensity, rigidity, anti-bending strength and the shear resistance of thin-walled surface layer composite laminboard.The fiber water of the utility model
Mud compound sandwich multi-ribbed plate selects accordingly according to the different load demand such as load-bearing wall panel or lining or internal partition
The use that structure, i.e. the utility model can satisfy a variety of use occasions such as load-bearing wall panel or lining or internal partition is wanted
It asks, it is applied widely.Meanwhile the surface material in the utility model and between lightweight core layer be pressed by once-cast
Type, compared with traditional organic gel technique for sticking, the globality for simplifying manufacture craft, reducing production cost, improving component,
Decrease the pollution to environment.In addition, the material of lightweight core layer can use function according to heat preservation or sound insulation or fire prevention etc.
Different demands select (such as foam styrofoam, foamed polyurethane plate, foam glass board, foamed ceramic panel, rock wool board, glass
Fiber cotton plate etc.), and then fibre cement compound sandwich multi-ribbed plate is made to have many advantages, such as lightweight, heat preservation or sound insulation or fire prevention as one kind
Multifunction board.
More specifically, according to the difference of the use occasion of fibre cement composite laminboard and stress size, the utility model
The convex rib I and convex rib II intersected in length and breadth, the utility model can be set in fibre cement surface layer inner surface
Convex rib I can be only set in fibre cement surface layer inner surface, such convex rib I can sufficiently wrap up vertical muscle, horizontal
It also can sufficiently be wrapped up by convex rib II when muscle needs to arrange, provide installation for the arrangement of reinforcing bar and subsequent bar frame
Basis smoothly solves the technical issues of being not easy cloth muscle in conventional thin wall layer compound sandwich board member.Due in fibre cement
Reinforcing bar can be smoothly arranged in composite laminboard, then bar frame is formed after muscle by overlap joint, substantially increase fiber water
Intensity, rigidity, anti-bending strength and the shear resistance of mud composite laminboard.
The advantageous effects of the utility model are as follows:
The utility model solves the technical issues of conventional thin wall layer composite laminboard component inside is not easy cloth muscle, significantly
It improves using fibre cement composite laminboard as the intensity of the thin-walled surface layer composite laminboard of representative, rigidity, anti-bending strength and resists
The mechanical properties such as ability are cut, the scope of application of component is expanded, while also simplifying manufacture craft, reduces production cost, mentions
The high globality of component, for concrete prefabricated component component family increase it is a kind of with higher building manage mechanical property lightweight,
Heat preservation or sound insulation or fireproof multifunction board.
Detailed description of the invention
Fig. 1 is the structural front view of the utility model embodiment one.
Fig. 2 is the partial enlarged view in Fig. 1 at A.
Fig. 3 is the left view of Fig. 1.
Fig. 4 is the top view of Fig. 1.
Fig. 5 is the structural front view of the utility model embodiment two.
Fig. 6 is the partial enlarged view in Fig. 5 at B.
Fig. 7 is the left view of Fig. 5.
Fig. 8 is the top view of Fig. 5.
Serial number in figure: 1, fibre cement surface layer, 1-1, convex rib I, 1-2, convex rib II, 2, lightweight core layer,
2-1, horizontal groove, 2-2, vertical groove, 3, vertical muscle, 4, transverse bar, 5, run through muscle.
Specific embodiment
The utility model is further described below with reference to attached drawing and two embodiments:
Embodiment one
As shown in Figure 1 to 4, the fibre cement compound sandwich multi-ribbed plate for implementing one is by lightweight core layer 2 and to be symmetrical arranged
The lamellar composite battenboard that fibre cement surface layer 1 in 2 left and right sides of lightweight core layer is constituted；In two layers of the fibre cement surface layer in left and right
The II 1-2(convex rib of I 1-1 of convex rib and convex rib that several intersect in length and breadth is provided on 1 inner surface
I 1-1 can sufficiently wrap up vertical muscle 3, and II 1-2 of convex rib can sufficiently wrap up transverse bar 4, be further the arrangement of bar frame
Installation foundation is provided, smoothly solves the technical issues of being not easy cloth muscle in conventional thin wall layer compound sandwich board member), convex
The inside for playing I 1-1 of shape rib is coated with vertical muscle 3, is coated with transverse bar 4, ipsilateral vertical muscle 3 in the inside of II 1-2 of convex rib
It is connected to form reinforced mesh with the intersection of transverse bar 4, several rows running through through lightweight core layer 2 is overlapped between two reinforced mesh
Two reinforced mesh of muscle 5(substantially increase fibre cement composite laminboard by forming bar frame after overlapping through muscle 5
Intensity, rigidity, anti-bending strength and shear resistance)；It is provided with and convex rib I on the left and right sides surface of lightweight core layer 2
The matched horizontal groove 2-1 of 1-1 and with the matched vertical groove 2-2(horizontal groove 2-1 of II 1-2 of convex rib for embedding
Convex rib I 1-1, vertical groove 2-2 are for embedding II 1-2 of convex rib).
Implement one described in lightweight core layer 2 be foam styrofoam, foamed polyurethane plate, foam glass board, foamed ceramic panel,
Any one of rock wool board, glass fiber cotton plate (due to lightweight core layer 2 using it is such have the characteristics that keep the temperature insulate against sound or prevent fires
Functional material core plate, so fibre cement compound sandwich multi-ribbed plate component just has many advantages, such as heat preservation or sound insulation or fire prevention).
The usual thickness range with a thickness of 2~15cm(thin-walled surface layer of fibre cement surface layer 1 described in embodiment one).
In conclusion the fibre cement compound sandwich multi-ribbed plate of embodiment one is a kind of two way ribbed slab and in two way ribbed slab
Interior equal cloth muscle, and have the bar frame that big rigidity is formed after the overlap joint of muscle 5, substantially increase fibre cement composite laminboard
Intensity, rigidity, anti-bending strength and shear resistance can satisfy the force request of load-bearing wall panel, so such structure is suitable as
Load-bearing wall panel uses.
The specific manufacturing process of embodiment one is as follows:
Firstly, it is necessary to according to the material of the use occasion of component and functional requirement selection lightweight core layer 2, such as can be from bubble
Foam styrofoam, foam glass board, foamed ceramic panel, rock wool board, is selected in glass fiber cotton plate foamed polyurethane plate；And root
The lightweight core layer 2 of correspondingly-sized is ordered according to the template specification to prefabricated components；Then, it opens up in lightweight core layer 2 and convex
The matched horizontal groove 2-1 of I 1-1 of rib and with the matched vertical groove 2-2 of II 1-2 of convex rib；Next, being arranged
The vertical muscle 3 of level and transverse bar 4 are welded into corresponding steel according to the positional relationship of horizontal groove 2-1 and vertical groove 2-2 by reinforcing bar
Muscle mesh sheet, and reinforced mesh is embedded in horizontal groove 2-1 and vertical groove 2-2；Then, along the thickness side of lightweight core layer 2
Run through muscle 5 to interspersed, and the both ends that will pass through muscle 5 overlap on two reinforced mesh；Lightweight core layer 2 after cloth muscle is placed on
The middle position of the cuboid shaping mold cavity of corresponding molding die, then to the two sides of lightweight core layer 2 and the clip cavity of shaping mold cavity
Interior casting fiber concrete slurry forms fibre cement surface layer 1 through solidification and just after maintenance；Finally, certain strong wait conserve
Fibre cement compound sandwich multi-ribbed plate component is detached from shaping mold cavity after degree.
Embodiment two
As shown in Fig. 5~Fig. 8, the fibre cement compound sandwich multi-ribbed plate of embodiment two is to set by lightweight core layer 2 and symmetrically
Set the lamellar composite battenboard that the fibre cement surface layer 1 in 2 left and right sides of lightweight core layer is constituted；In two layers of the fibre cement face in left and right
Vertical muscle 3 can sufficiently be wrapped up by being provided with I 1-1 of several I 1-1(convex ribs of convex rib on the inner surface of layer 1, into
One step provides installation foundation for the arrangement of bar frame, smoothly solves and is not easy in conventional thin wall layer compound sandwich board member
The technical issues of cloth muscle), vertical muscle 3, the vertical muscle 3 of the height such as left and right sides are coated in the equal level in inside of I 1-1 of convex rib
Between be overlapped with several through lightweight core layer 2 between the vertical muscle 3 of height such as two at left and right sides of muscle 5(by running through
Muscle 5 improves intensity, rigidity, anti-bending strength and the shear resistance of fibre cement composite laminboard after overlapping)；In lightweight core layer 2
Left and right sides surface be provided with the matched horizontal groove 2-1(horizontal groove 2-1 of I 1-1 of convex rib for embed it is convex
Play I 1-1 of shape rib).
Lightweight core layer 2 described in embodiment two is foam styrofoam, foamed polyurethane plate, foam glass board, foamed ceramics
Any one of plate, rock wool board, glass fiber cotton plate are (since lightweight core layer 2 has heat preservation or the spies such as sound insulation or fire prevention using such
The functional material core plate of point, so fibre cement compound sandwich multi-ribbed plate component just has many advantages, such as heat preservation or sound insulation or fire prevention).
The usual thickness range with a thickness of 2~15cm(thin-walled surface layer of fibre cement surface layer 1 described in embodiment two).
In conclusion the fibre cement compound sandwich multi-ribbed plate of embodiment two is a kind of unidirectional floor and in unidirectional floor
Interior cloth muscle, and there is certain intensity, rigidity, flexing resistance by overlapping through muscle 5 between the vertical muscle 3 of the height such as left and right sides
Energy and shear resistance, can satisfy the force request of lining, so such structure is suitable as lining use.
The specific manufacturing process of embodiment two is as follows:
Firstly, it is necessary to according to the material of the use occasion of component and functional requirement selection lightweight core layer 2, such as can be from bubble
Foam styrofoam, foam glass board, foamed ceramic panel, rock wool board, is selected in glass fiber cotton plate foamed polyurethane plate；And root
The lightweight core layer 2 of correspondingly-sized is ordered according to the template specification to prefabricated components；Then, it opens up in lightweight core layer 2 and convex
The matched horizontal groove 2-1 of I 1-1 of rib；Next, being arranged reinforcing bar, i.e., interts along the thickness direction of lightweight core layer 2 and run through
Muscle 5, the both ends overlap joint that will pass through muscle 5 are embedded in horizontal groove 2-1 and are waited on two vertical muscle 3 of height；After cloth muscle
Lightweight core layer 2 is placed on the middle position of the cuboid shaping mold cavity of corresponding molding die, then to the two sides of lightweight core layer 2 with
It is poured fiber concrete slurry in the clip cavity of shaping mold cavity, forms fibre cement surface layer 1 through solidification and just after maintenance；Finally,
Fibre cement compound sandwich multi-ribbed plate component is detached from shaping mold cavity after conserving some strength.
The component of the utility model is applied widely, in addition to it is above-mentioned can be used as load-bearing wall panel or lining use other than,
The internal partition for being also used as specific function uses.When the utility model component as internal partition in use, to component itself
Rigidity requirement it is lower, internal reinforcing bar, production can also be saved when selecting the overall structure of embodiment one or embodiment two
Technique is simpler, cost is lower.
Claims (6)
1. a kind of fibre cement compound sandwich multi-ribbed plate, it is characterised in that: it is by lightweight core layer (2) and to be symmetricly set on lightweight
The lamellar composite battenboard that fibre cement surface layer (1) at left and right sides of sandwich layer (2) is constituted；In two layers of the fibre cement surface layer in left and right
(1) the convex rib I (1-1) and convex rib II (1-2) that several intersect in length and breadth are provided on inner surface, convex
The inside for playing shape rib I (1-1) is coated with vertical muscle (3), is coated with transverse bar (4) in the inside of convex rib II (1-2), ipsilateral
Vertical muscle (3) and transverse bar (4) intersection be connected to form reinforced mesh, several rows are overlapped between two reinforced mesh through lightweight
Sandwich layer (2) runs through muscle (5)；It is provided on the left and right sides surface of lightweight core layer (2) and is matched with convex rib I (1-1)
Horizontal groove (2-1) and with convex rib II (1-2) matched vertical groove (2-2).
2. fibre cement compound sandwich multi-ribbed plate according to claim 1, it is characterised in that: the lightweight core layer (2) is
Any one of foam styrofoam, foamed polyurethane plate, foam glass board, foamed ceramic panel, rock wool board, glass fiber cotton plate.
3. fibre cement compound sandwich multi-ribbed plate according to claim 1, it is characterised in that: the fibre cement surface layer
(1) with a thickness of 2~15cm.
4. a kind of fibre cement compound sandwich multi-ribbed plate, it is characterised in that: it is by lightweight core layer (2) and to be symmetricly set on lightweight
The lamellar composite battenboard that fibre cement surface layer (1) at left and right sides of sandwich layer (2) is constituted；In two layers of the fibre cement surface layer in left and right
(1) it is provided with several convex ribs I (1-1) on inner surface, is worn in the equal level in inside of convex rib I (1-1)
Equipped with vertical muscle (3), several are overlapped between the vertical muscle (3) of the height such as left and right sides through lightweight core layer (2) through muscle
(5)；It is provided with and convex rib I (1-1) matched horizontal groove (2-1) on the left and right sides surface of lightweight core layer (2).
5. fibre cement compound sandwich multi-ribbed plate according to claim 4, it is characterised in that: the lightweight core layer (2) is
Any one of foam styrofoam, foamed polyurethane plate, foam glass board, foamed ceramic panel, rock wool board, glass fiber cotton plate.
6. fibre cement compound sandwich multi-ribbed plate according to claim 4, it is characterised in that: the fibre cement surface layer
(1) with a thickness of 2~15cm.