CN207177165U - A kind of high abrasion Dali stone ceramic tile - Google Patents

A kind of high abrasion Dali stone ceramic tile Download PDF

Info

Publication number
CN207177165U
CN207177165U CN201720721926.9U CN201720721926U CN207177165U CN 207177165 U CN207177165 U CN 207177165U CN 201720721926 U CN201720721926 U CN 201720721926U CN 207177165 U CN207177165 U CN 207177165U
Authority
CN
China
Prior art keywords
layer
ceramic tile
corundum
nanometer
high abrasion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201720721926.9U
Other languages
Chinese (zh)
Inventor
管蒙蒙
杨奎彬
易仕伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Seagull champion Limited
Original Assignee
Champion Building Materials (anhui) Co Ltd
Xinyi Ceramic (penglai) Co Ltd
XINYI CERAMIC (CHINA) CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Champion Building Materials (anhui) Co Ltd, Xinyi Ceramic (penglai) Co Ltd, XINYI CERAMIC (CHINA) CO Ltd filed Critical Champion Building Materials (anhui) Co Ltd
Priority to CN201720721926.9U priority Critical patent/CN207177165U/en
Application granted granted Critical
Publication of CN207177165U publication Critical patent/CN207177165U/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The utility model belongs to architectural pottery technical field, more particularly to a kind of high abrasion Dali stone ceramic tile.Include green body layer, glaze layer, decorative layer and wearing layer successively from down to up, nanometer α corundum is contained in the wearing layer, the particle diameter of the nanometer α corundum is 10 40nm.The utility model adds nanometer α corundum by the superficial layer in ceramic tile, forms transparent wear-resistant coating, can greatly improve the anti-wear performance grade of ceramic tile glaze paint, anti-wear performance grade is by standard detection up to IV levels.

Description

A kind of high abrasion Dali stone ceramic tile
Technical field
Architectural pottery technical field is the utility model is related to, more particularly to a kind of high abrasion Dali stone ceramic tile.
Background technology
Dali stone ceramic tile can reach forcing for natural marble due to its texture, color, texture, feel and visual effect True effect, decorative effect are also significantly better than lithotome, since the birth and popularization of especially throwing glaze and ink-jet technology entirely, extensively Obtain the favor of consumer.But the glaze paint of existing Dali stone ceramic tile exist one it is fatal the shortcomings that, i.e., wearability is poor, uses Because the reasons such as abrasion, the bright surface of script are easy to cut occur, influence glossiness and surface effect in journey.Therefore, such as The wearability what improves Dali stone ceramic tile is the great difficult problem that ceramic industry faces.
Utility model content
In view of the shortcomings of the prior art, the utility model provides a kind of high abrasion Dali stone ceramic tile.
Technical solutions of the utility model are as follows:
A kind of high abrasion Dali stone ceramic tile, include green body layer, glaze layer, decorative layer and wearing layer successively from down to up, it is described Contain nanometer α-corundum in wearing layer.
The particle diameter of the nanometer α-corundum is 10-40nm.
Nanometer α-the corundum is added to wearing layer by spraying mode.
Nanometer α-the corundum to form wearing layer by glazing operation or work standard to operate again by being added in protection glaze.
Compared with prior art, beneficial effect is the utility model:The utility model is added by the superficial layer in ceramic tile Plus nano α-corundum, transparent wear-resistant coating is formed, the anti-wear performance grade of ceramic tile glaze paint, anti-wear performance grade can be greatly improved By standard detection up to IV levels.
Brief description of the drawings
The utility model is further illustrated with reference to the accompanying drawings and examples.
Fig. 1 is the structural representation of the utility model specific embodiment 1.
Fig. 2 is the structural representation of the utility model specific embodiment 2.
Fig. 3 is the partial enlargement structural representation of wearing layer in Fig. 2.
Wherein:1st, green body layer;2nd, glaze layer;3rd, decorative layer;4th, wearing layer;401st, nanometer α-corundum;402nd, glaze is protected.
Embodiment
The utility model is described in further detail below in conjunction with the accompanying drawings.
Embodiment 1:
As shown in figure 1, a kind of high abrasion Dali stone ceramic tile, include successively from down to up green body layer 1, glaze layer 2, decorative layer 3, Wearing layer 4;Its Making programme is, in the surface glazing layer 2 of green body layer 1, then to print decorative layer 3 on the surface of glaze layer 2, then spray and receive Rice α-corundum forms wearing layer 4;The particle diameter of described nanometer α-corundum is 10 ~ 40nm;Nanometer α-the corundum passes through the side of spraying Formula is added to glaze paint top layer, forms high abrasion clear coat in ceramic tile surface after kiln sinters, it can greatly improve ceramic tile The anti-wear performance grade of glaze paint, anti-wear performance grade is by standard detection up to IV levels.
Embodiment 2:
As shown in Figures 2 and 3, a kind of high abrasion Dali stone ceramic tile, green body layer 1, glaze layer 2, dress are included successively from down to up Adorn layer 3, wearing layer 4;Its Making programme is, in the surface glazing layer 2 of green body layer 1, then to print decorative layer 3 on the surface of glaze layer 2, then Apply the protection glaze 402 containing nanometer α-corundum 401 and form wearing layer 4;The particle diameter of described nanometer α-corundum 401 is about 10 ~ 40nm;Nanometer α-the corundum 401 is operated by being added in protection glaze 402 by operation or work standard, in porcelain after kiln sinters Brick surface forms high abrasion clear coat, and it can greatly improve the anti-wear performance grade of ceramic tile glaze paint, and anti-wear performance grade is pressed Standard detection is up to IV levels.
Above-mentioned drawings and Examples are merely to illustrate the utility model, and any art those of ordinary skill is to it The appropriate change or modification done, or use other flower pattern instead and make this technical change, it all should be regarded as not departing from this practicality newly Type patent category.

Claims (4)

  1. A kind of 1. high abrasion Dali stone ceramic tile, it is characterised in that:Include green body layer successively from down to up(1), glaze layer(2), decoration Layer(3)And wearing layer(4), the wearing layer(4)In contain nanometer α-corundum.
  2. 2. high abrasion Dali according to claim 1 stone ceramic tile, it is characterised in that:The particle diameter of the nanometer α-corundum is 10-40nm。
  3. 3. high abrasion Dali according to claim 1 or 2 stone ceramic tile, it is characterised in that:Nanometer α-the corundum passes through spray The mode of applying is added to glaze paint top layer and forms wearing layer(4).
  4. 4. high abrasion Dali according to claim 1 or 2 stone ceramic tile, it is characterised in that:Nanometer α-the corundum is by adding It is added in protection glaze to form wearing layer by glazing operation or work standard to operate again(4).
CN201720721926.9U 2017-06-21 2017-06-21 A kind of high abrasion Dali stone ceramic tile Active CN207177165U (en)