CN204991482U - Subassembly of resistance and electric capacity polyphone - Google Patents

Subassembly of resistance and electric capacity polyphone Download PDF

Info

Publication number
CN204991482U
CN204991482U CN201520607109.1U CN201520607109U CN204991482U CN 204991482 U CN204991482 U CN 204991482U CN 201520607109 U CN201520607109 U CN 201520607109U CN 204991482 U CN204991482 U CN 204991482U
Authority
CN
China
Prior art keywords
layer
resistance
dielectric
dielectric layer
assembly
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201520607109.1U
Other languages
Chinese (zh)
Inventor
苟引刚
王久
高桂丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen Penang Electronics Co.,Ltd.
Original Assignee
SHENZHEN BENCENT ELECTRONICS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHENZHEN BENCENT ELECTRONICS CO Ltd filed Critical SHENZHEN BENCENT ELECTRONICS CO Ltd
Priority to CN201520607109.1U priority Critical patent/CN204991482U/en
Application granted granted Critical
Publication of CN204991482U publication Critical patent/CN204991482U/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The utility model discloses a subassembly of resistance and electric capacity polyphone, the embodiment of the utility model provides a subassembly of resistance capacitance polyphone includes a stromatolithic capacitor electrode layer, a dielectric layer and resistance layer in proper order, and the application circuit who has solved present resistance capacitance polyphone through this laminated structure is difficult to miniaturized problem to and solved carry on paster when production loosely organized, the fabric swatch area is big, system level packaging technology is difficult to realize, integrated circuit is difficult to miniaturized problem. And the simply easy realization of the method of this subassembly of preparation in this embodiment, improved mounting efficiency.

Description

The assembly of a kind of resistance and electric capacity series winding
Technical field
The application relates to electronic component technology field, is specifically related to the assembly of a kind of resistance capacitance series winding.
Background technology
At present, in the implementation procedure of protective circuit, generally need to use the resistance capacitance element with series winding relation, discrete resistors, capacitances in series are used, such as, just need to have resistance and the electric capacity of cascaded structure relation as the Bobsmith circuit structure realizing matched impedance in RJ45 protection; This circuit structure also comprises and forms a protective element of closed-loop path with resistance, electric capacity series winding respectively, the traditional implementation of this circuit is by discrete resistance, electric capacity and protective device gradation laminating on a printed-wiring board, it is long that technique realizes the time, taking PCB surface amasss more, not easily realizes miniaturization.
Utility model content
The embodiment of the present application provides the assembly of a kind of resistance and electric capacity series winding, and the efficiency that the application circuit solving existing resistance capacitance series winding carries out when paster is produced is low, because loosely organized, fabric swatch area is large, is unfavorable for the problem that product trend toward miniaturization develops.
First aspect, the embodiment of the present application provides the assembly of a kind of resistance and electric capacity series winding, comprising:
First capacitance electrode layer of lamination, the first dielectric layer and resistive layer successively.
In conjunction with first aspect, in the implementation that the first is possible, described first dielectric layer comprises N number of dielectric layering of contraposition lamination, pressing, described N be greater than 0 integer.
In conjunction with first aspect and the first the possible implementation based on first aspect, in the implementation that the second is possible, this assembly also comprises:
Be stacked on the second capacitance electrode layer between described first dielectric layer and described resistive layer.
Based on the implementation that the second of first aspect is possible, in the implementation that the third is possible, described resistive layer comprises:
First resistance slurry printed layers of lamination and resistance electrode layer from the bottom to top.
Based on the third possible implementation of first aspect, in the 4th kind of possible implementation, this assembly also comprises:
Be stacked on second dielectric layer on described second capacitance electrode layer surface;
Described second dielectric layer offers through hole;
Described resistive layer comprises:
For filling described through hole, and be printed in the described first resistance slurry printed layers on the described second capacitance electrode layer surface in described through hole;
Be stacked on the described resistance electrode layer on described first resistance slurry printed layers surface.
Based on the 4th kind of possible implementation of first aspect, in five kinds of possible implementations, described through hole is polygon or manhole or fan-shaped pylone or ellipse hole.
Based on the 5th kind of possible implementation of first aspect, in the 6th kind of possible implementation, described through hole is symmetric polygonal through hole.
Based on the 6th kind of possible implementation of first aspect, in the 7th kind of possible implementation, described symmetric polygonal through hole is square through-hole, and the length of side of described square through-hole is the arbitrary value in 0.5mm ~ 2mm.
Based on the 7th kind of possible implementation of first aspect, in the 8th kind of possible implementation, the degree of depth of described square through-hole is the arbitrary value in 0.2 ~ 0.6mm.
Based on the 5th kind of possible implementation of first aspect, in the 9th kind of possible implementation, each dielectric in described first dielectric layer is layered as the first ceramic dielectric matrix for making capacitor, and described second dielectric layer is the second ceramic dielectric matrix.
Based on the 9th kind of possible implementation of first aspect, in the tenth kind of possible implementation, described first ceramic dielectric matrix is oxide or the titanate of the second major element, described titanate comprises barium titanate dielectric matrix, calcium titanate dielectric base body or magnesium titanate dielectric base body, and the oxide of described second major element comprises alundum (Al2O3) dielectric base body.
Based on the tenth kind of possible implementation of first aspect, in the 11 kind of possible implementation, described first capacitance electrode layer, described second capacitance electrode layer, described resistance electrode layer comprise alloy formed by palladium, platinum, gold, silver, copper or nickel or above-mentioned at least two kinds of metals.
Based on the 11 kind of possible implementation of first aspect, in the 12 kind of possible implementation, described first resistance slurry printed layers is ruthenium system resistance slurry.
Based on the 12 kind of possible implementation of first aspect, in the 13 kind of possible implementation, the plasma resistance resistivity of described first resistance slurry printed layers is 700 ~ 1400 Ω cm.
Based on the 13 kind of possible implementation of first aspect, in the 14 kind of possible implementation, the thickness of described assembly is between 1mm-3mm, and the length of described assembly is not more than 2.5mm, is not less than 1mm; The width of described assembly is not more than 2.5mm, is not less than 1mm.
Second aspect, the embodiment of the present application provides a kind of method making the assembly of resistance and electric capacity series winding, comprising:
The first dielectric layer is made by slurry casting technique;
By described first dielectric layer of sintering curing technique solidification;
Printed resistor slurry is in the upper surface of described first dielectric layer;
Burn described first dielectric layer and described resistance slurry altogether by sintering curing technique and form resistive layer to solidify described resistance slurry, described resistive layer is solidified and is connected to described first dielectric layer;
An electrode layer is printed respectively in the lower surface of described first dielectric layer and the upper surface of described resistive layer;
By electrode layer and described resistive layer described in sintering curing technique solidification connection one, and solidification connects electrode layer and described first dielectric layer described in another.
In conjunction with second aspect, in the implementation that the first is possible, describedly make the first dielectric layer by slurry casting technique, comprising:
By the powder of grinding technics preparation for making the first dielectric layer;
Described powder is made slurry;
By slurry casting technique, described slurry is laminated;
Described thin slice is carried out section and form N number of dielectric layering; Described N be greater than 0 integer;
By laminated process, lamination is carried out in described N number of dielectric layering, form described first dielectric layer of predetermined thickness.
In conjunction with the first possible implementation of second aspect, in the implementation that the second is possible, described by the powder of grinding technics preparation for making the first dielectric layer, comprising:
By grinding technics preparation for making oxide or the titanate of the second major element of the first dielectric layer, described titanate comprises barium titanate dielectric matrix, calcium titanate dielectric base body or magnesium titanate dielectric base body, and the oxide of described second major element comprises alundum (Al2O3) dielectric base body.
In conjunction with the first possible implementation of second aspect or second aspect or the possible implementation of the second, in the implementation that the third is possible, describedly burn described first dielectric layer and described resistance slurry altogether by sintering curing technique and form resistive layer to solidify described resistance slurry, described resistive layer is solidified and is connected to described first dielectric layer, comprising:
Under arbitrary temperature conditions of burning altogether in 900 DEG C ~ 1300 DEG C scopes, burn described first dielectric layer and described resistance slurry altogether by sintering curing technique and form resistive layer to solidify described resistance slurry, described resistive layer is solidified and is connected to described first dielectric layer.
In conjunction with the third possible implementation of second aspect, in the 4th kind of possible implementation, under described arbitrary temperature conditions of burning altogether in 900 DEG C ~ 1300 DEG C scopes, burn described first dielectric layer and described resistance slurry altogether by sintering curing technique and form resistive layer to solidify described resistance slurry, described resistive layer is solidified and is connected to described first dielectric layer, comprising:
Arbitrary in 950 DEG C ~ 1100 DEG C burns under temperature conditions altogether, burns described first dielectric layer altogether and described resistance slurry forms resistive layer to solidify described resistance slurry by sintering curing technique, described resistive layer is solidified and is connected to described first dielectric layer.
In conjunction with the third possible implementation of second aspect, in the 5th kind of possible implementation, described printed resistor slurry, in the upper surface of described first electrode layer, comprising:
Make the resistance slurry that plasma resistance resistivity is 700 ~ 1400 Ω cm;
Print described resistance slurry in the upper surface of described first electrode layer.
In conjunction with the 5th kind of possible implementation of second aspect, in the 6th kind of possible implementation, described method also comprises:
Cutting forms M the described assembly of preliminary dimension, described M be greater than zero integer;
Described assembly is tested and packed.
The third aspect, the embodiment of the present application provides a kind of method making the assembly of resistance and electric capacity series winding, comprising:
The first dielectric layer is made by slurry casting technique;
By described first dielectric layer of sintering curing technique solidification;
One first dielectric layer electrode is printed respectively at the upper and lower faces of described first dielectric layer;
Described first dielectric layer and described first dielectric layer electrode is connected by the solidification of sintering curing technique;
Printed resistor slurry is in the surface of arbitrary described first dielectric layer electrode;
Solidify described resistance slurry by sintering curing technique and form resistive layer, connect described resistive layer and described first dielectric layer electrode to solidify;
Print a resistive layer electrode in the surface of described resistive layer;
Described resistive layer and described resistive layer electrode is connected by the solidification of sintering curing technique.
In conjunction with the third aspect, in the implementation that the first is possible, describedly make the first dielectric layer by slurry casting technique, comprising:
By the powder of grinding technics preparation for making the first dielectric layer;
Described powder is made slurry;
By slurry casting technique, described slurry is laminated;
Described thin slice is carried out section and form N number of dielectric layering; Described N be greater than 0 integer;
By laminated process, lamination is carried out in described N number of dielectric layering, form described first dielectric layer of predetermined thickness.
In conjunction with the first possible implementation of the third aspect, in the implementation that the second is possible, described by the powder of grinding technics preparation for making the first dielectric layer, comprising:
By grinding technics preparation for making oxide or the titanate of the second major element of the first dielectric layer, described titanate comprises barium titanate dielectric matrix, calcium titanate dielectric base body or magnesium titanate dielectric base body, and the oxide of described second major element comprises alundum (Al2O3) dielectric base body.
In conjunction with the implementation that the second of the third aspect is possible, in the implementation that the third is possible, described printed resistor slurry, in the surface of arbitrary described first dielectric layer electrode, comprising:
Make the resistance slurry that plasma resistance resistivity is 700 ~ 1400 Ω cm;
Print described resistance slurry in the surface of arbitrary described first dielectric layer electrode.
In conjunction with the third possible implementation of the third aspect, in the 4th kind of possible implementation, described by after sintering curing technique solidification described first dielectric layer of connection and described first dielectric layer electrode, and, printed resistor slurry is before the surface of arbitrary described first dielectric layer electrode, and described method also comprises:
By the surface of laminated process lamination second dielectric layer in arbitrary described first dielectric layer electrode, form described second dielectric layer of predetermined thickness;
Described second dielectric layer offers the surface that at least one through hole extends to described first dielectric layer electrode;
Resistance slurry described in the surface printing of the described first dielectric layer electrode in described through hole, realizes printed resistor slurry in the surface of arbitrary described first dielectric layer electrode.
In conjunction with the 4th kind of possible implementation of the third aspect, the 5th kind of possible implementation, described by described first dielectric layer of sintering curing technique solidification, comprising:
Under arbitrary sintering temperature condition in 1300 DEG C ~ 1400 DEG C scopes, by described first dielectric layer of sintering curing technique solidification.
In conjunction with the third possible implementation of the third aspect, in the 6th kind of possible implementation, describedly solidify described resistance slurry by sintering process and form resistive layer, connect described resistive layer and described first dielectric layer electrode to solidify, comprising:
Under arbitrary sintering temperature condition in 800 DEG C ~ 950 DEG C scopes, solidify described resistance slurry by sintering process and form resistive layer, connect described resistive layer and described first dielectric layer electrode to solidify.
In conjunction with the 6th kind of possible implementation of the third aspect, in the 7th kind of possible implementation, described method also comprises:
Cutting forms M the described assembly of preliminary dimension, described M be greater than zero integer;
Described assembly is tested and packed.
The assembly of resistance capacitance that the utility model embodiment provides series winding comprises the first capacitance electrode layer of lamination successively, the first dielectric layer and resistive layer, by this laminated construction solve existing discrete resistors, electric capacity series winding application circuit carry out paster produce time efficiency low, because loosely organized, fabric swatch area is large, be unfavorable for the problem that product trend toward miniaturization develops.And the method making this assembly in the present embodiment is simple and easy to realize, and improves load efficiency.
Accompanying drawing explanation
In order to be illustrated more clearly in the embodiment of the present application or technical scheme of the prior art, be briefly described to the accompanying drawing used required in embodiment or description of the prior art below, apparently, accompanying drawing in the following describes is only some embodiments of the application, for those of ordinary skill in the art, under the prerequisite not paying creative work, other accompanying drawing can also be obtained according to these accompanying drawings.
The equivalent circuit diagram of the modular construction that Fig. 1 a provides for the embodiment of the present application;
The modular construction schematic diagram of a kind of resistance that Fig. 1 b provides for the embodiment of the present application and electric capacity series winding;
The modular construction schematic diagram of the another kind of resistance that Fig. 2 provides for the embodiment of the present application and electric capacity series winding;
The modular construction schematic diagram of the another kind of resistance that Fig. 3 provides for the embodiment of the present application and electric capacity series winding;
A kind of assembly method flow chart making resistance and electric capacity series winding that Fig. 4 a provides for the embodiment of the present application;
The another kind that Fig. 4 b provides for the embodiment of the present application makes the assembly method flow chart of resistance and electric capacity series winding;
The another kind that Fig. 4 c provides for the embodiment of the present application makes the assembly method flow chart of resistance and electric capacity series winding;
The another kind that Fig. 4 d provides for the embodiment of the present application makes the assembly method flow chart of resistance and electric capacity series winding;
The another kind that Fig. 4 e provides for the embodiment of the present application makes the assembly method flow chart of resistance and electric capacity series winding;
A kind of method flow diagram making the assembly of resistance and electric capacity series winding that Fig. 5 a provides for the present embodiment;
The manufacture method flow chart of the printed resistor layer that Fig. 5 b provides for the embodiment of the present application;
Fig. 5 c provide for the embodiment of the present application another make the method flow diagram of the assembly of resistance and electric capacity series winding;
Fig. 5 d provide for the embodiment of the present application another make the method flow diagram of the assembly of resistance and electric capacity series winding.
Embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present application, be clearly and completely described the technical scheme in the embodiment of the present application, obviously, described embodiment is only some embodiments of the present application, instead of whole embodiments.Below by specific embodiment, be described in detail respectively.
The present embodiment provides the assembly of a kind of resistance and electric capacity series winding, comprising:
First capacitance electrode layer of lamination, the first dielectric layer and resistive layer successively.
As the optional execution mode of one, the first dielectric layer comprises N number of dielectric layering of contraposition lamination, pressing, N be greater than 0 integer.
As the optional execution mode of one, between two the often adjacent dielectric layerings in all N number of dielectric layerings, be connected with inner electrode layer.
As the optional execution mode of one, this assembly also comprises:
Be stacked on the second capacitance electrode layer between the first dielectric layer and resistive layer.
As the optional execution mode of one, resistive layer comprises:
First resistance slurry printed layers of lamination and resistance electrode layer from the bottom to top.
Preferably, as the optional execution mode of one, this assembly also comprises:
Be stacked on second dielectric layer on the second capacitance electrode layer surface;
Second dielectric layer offers through hole;
Resistive layer comprises:
For filling vias, and be printed in the first resistance slurry printed layers on the second capacitance electrode layer surface in through hole;
Be stacked on the resistance electrode layer on the first resistance slurry printed layers surface.
As the optional execution mode of one, each dielectric in the first dielectric layer is layered as the first ceramic dielectric matrix for making capacitor, and the second dielectric layer is the second ceramic dielectric matrix.
Preferably, as the optional execution mode of one, described first ceramic dielectric matrix is oxide or the titanate of the second major element, described titanate comprises barium titanate dielectric matrix, calcium titanate dielectric base body or magnesium titanate dielectric base body, and the oxide of described second major element comprises alundum (Al2O3) dielectric base body.Each dielectric layering can be same or different dielectric base body, the restriction not by the present embodiment during specific implementation.
Preferably, as the optional execution mode of one, the first capacitance electrode layer, the second capacitance electrode layer, resistance electrode layer comprise alloy formed by palladium, platinum, gold, silver, copper or nickel or above-mentioned at least two kinds of metals.
Preferably, as the optional execution mode of one, the first resistance slurry printed layers is ruthenium system resistance slurry.
Preferably, through hole is polygon or manhole.
Preferably, through hole is triangle, quadrangle or regular polygon or symmetric polygonal through hole or manhole or ellipse hole or semi-circular through hole or fan-shaped pylone.
Preferably, through hole is square through-hole.
Preferably, the length of side of square through-hole is the arbitrary value in 0.5mm ~ 2mm.
Preferably, the length of side of square through-hole is the arbitrary value in 0.3mm ~ 5mm.
Preferably, the length of side of square through-hole is the arbitrary value in 0.6mm ~ 1.5mm.
Preferably, the length of side of square through-hole is the arbitrary value in 0.7mm ~ 1mm.
Preferably, the length of side of square through-hole is the arbitrary value in 0.8mm ~ 1mm.
Preferably, the length of side of square through-hole is 0.9mm.
Preferably, the length of side of square through-hole is 1.2mm.
Preferably, the length of side of square through-hole is 1.8mm.
Preferably, the length of side of square through-hole is 2.8mm.
Preferably, the length of side of square through-hole is 1.8mm.
Preferably, the length of side of square through-hole is 1.7mm.
Preferably, the length of side of square through-hole is 1.6mm.
Preferably, the degree of depth of square through-hole is the arbitrary value in 0.2 ~ 0.6mm.
Preferably, the degree of depth of square through-hole is the arbitrary value in 0.2 ~ 0.5mm.
Preferably, the degree of depth of square through-hole is the arbitrary value in 0.3 ~ 0.5mm.
Preferably, the degree of depth of square through-hole is the arbitrary value in 0.4 ~ 0.6mm.
Preferably, the degree of depth of square through-hole is the arbitrary value in 0.3 ~ 0.4mm.
Preferably, the degree of depth of square through-hole is the arbitrary value in 0.35 ~ 0.55mm.
Preferably, the degree of depth of square through-hole is 0.45mm.
Preferably, the plasma resistance resistivity of the first resistance slurry printed layers is 700 ~ 1400 Ω cm.
Preferably, the plasma resistance resistivity of the first resistance slurry printed layers is 740 ~ 1300 Ω cm.
Preferably, the plasma resistance resistivity of the first resistance slurry printed layers is 750 ~ 1000 Ω cm.
Preferably, the plasma resistance resistivity of the first resistance slurry printed layers is 750 ~ 820 Ω cm.
Preferably, the plasma resistance resistivity of the first resistance slurry printed layers is 730 ~ 780 Ω cm.
Preferably, the plasma resistance resistivity of the first resistance slurry printed layers is 700 Ω cm.
Preferably, the plasma resistance resistivity of the first resistance slurry printed layers is 805 Ω cm.
Preferably, the plasma resistance resistivity of the first resistance slurry printed layers is 721 Ω cm.
Preferably, the plasma resistance resistivity of the first resistance slurry printed layers is 1200 Ω cm.
Preferably, the plasma resistance resistivity of the first resistance slurry printed layers is 1000 Ω cm.
Preferably, the plasma resistance resistivity of the first resistance slurry printed layers is 900 Ω cm.
Preferably, the plasma resistance resistivity of the first resistance slurry printed layers is 850 Ω cm.
As the optional execution mode of one, the thickness of assembly is between 1mm-3mm, and the length of assembly is not more than 2.5mm, is not less than 1mm; The width of assembly is not more than 2.5mm, is not less than 1mm.
As the optional execution mode of one, the thickness of assembly is between 1mm-2mm, and the length of assembly is not more than 2mm, is not less than 1mm; The width of assembly is not more than 2mm, is not less than 1mm.
As the optional execution mode of one, the thickness of assembly is between 1.5mm-2.5mm, and the length of assembly is not more than 1.8mm, is not less than 1.1mm; The width of assembly is not more than 2.3mm, is not less than 1.5mm.
As the optional execution mode of one, the thickness of assembly is between 1.5mm-2mm, and the length of assembly is not more than 2.2mm, is not less than 1.4mm; The width of assembly is not more than 2.1mm, is not less than 1.4mm.
As the optional execution mode of one, the thickness of assembly is 1.8mm, and the length of assembly is 1.5mm; The width of assembly is 2mm.
As the optional execution mode of one, the thickness of assembly is 1.9mm, and the length of assembly is 1.6mm; The width of assembly is 1.8mm.
The object that realizes of the modular construction in the present embodiment is the laminated construction making a kind of resistance and electric capacity series winding, refer to Fig. 1 a, the equivalent circuit diagram of the modular construction that Fig. 1 a provides for the embodiment of the present application, as shown in Figure 1a, the equivalent electric circuit of the modular construction that the present embodiment provides is that resistance R and electric capacity C contact, and is described the modular construction that the present embodiment provides below in conjunction with accompanying drawing.Refer to Fig. 1 b, the modular construction schematic diagram of a kind of resistance that Fig. 1 b provides for the embodiment of the present application and electric capacity series winding.As shown in Figure 1 b, the assembly of the resistance that the present embodiment provides and electric capacity series winding comprises the first capacitance electrode layer 100, first dielectric layer 120 and resistive layer 140 of lamination successively, and wherein resistive layer 140 comprises the first resistance slurry printed layers 141 and the resistance electrode layer 142 of lamination from the bottom to top.The assembly of the resistance capacitance series winding that the embodiment of the present application provides comprises the first capacitance electrode layer 100, first dielectric layer 120 and resistive layer 140 of lamination successively, the efficiency of application circuit when carrying out paster and producing being solved existing resistance capacitance series winding by this laminated construction is low, because loosely organized, fabric swatch area is large, not easily realize the problem of miniaturization.And the method making this assembly in the present embodiment is simple and easy to realize, and improves load efficiency.
As the optional execution mode of one, the first dielectric layer comprises N number of dielectric layering of contraposition lamination, pressing, N be greater than 0 integer.In the present embodiment, the number of the dielectric layer that the first dielectric layer comprises can be set, to mate with the capacitance preset, be achieved the laminated construction of multiple electric capacity by this structure.
Preferably, as the optional execution mode of one, refer to Fig. 2, the modular construction schematic diagram of the another kind of resistance that Fig. 2 provides for the embodiment of the present application and electric capacity series winding.Final RC series component finished product thickness is between 1mm-3mm, and resistance whole comprehensive electrode, is convenient to the welded encapsulation being similar to chip product; Length component is not more than 2.5mm, is not less than 1mm; Assembly is wide is not more than 2.5mm, is not less than 1mm.
As shown in Figure 2, this assembly that the present embodiment provides also comprises:
Be stacked on the second capacitance electrode layer 210 between the first dielectric layer 120 and resistive layer 140, to realize the stability annexation that electric capacity and resistance carry out contacting.
As the optional execution mode of one, refer to Fig. 3, the modular construction schematic diagram of the another kind of resistance that Fig. 3 provides for the embodiment of the present application and electric capacity series winding, as shown in Figure 3, this assembly in present embodiment also comprises the second dielectric layer 310 being stacked on the second capacitance electrode layer 210 surface; Wherein, the second dielectric layer offers through hole 311.And in the present embodiment, resistive layer 140 comprises the first resistance slurry printed layers 141 and resistance electrode layer 142, wherein, the first resistance slurry printed layers 141 for filling vias 311, and is printed in the surface of the second capacitance electrode layer 210 in through hole 311; And resistance electrode layer 142 is stacked on the surface of the first resistance slurry printed layers 141.By the area of the spatial limitation resistive layer of through hole and space in present embodiment, the resistance of predetermined resistance can be realized.
As the optional execution mode of one, the first dielectric layer is the first ceramic dielectric matrix for making capacitor, and the second dielectric layer is the second ceramic dielectric matrix.
Preferably, as the optional execution mode of one, described first ceramic dielectric matrix is oxide or the titanate of the second major element, described titanate comprises barium titanate dielectric matrix, calcium titanate dielectric base body or magnesium titanate dielectric base body, and the oxide of described second major element comprises alundum (Al2O3) dielectric base body.
Preferably, as the optional execution mode of one, the first capacitance electrode layer, the second capacitance electrode layer, resistance electrode layer comprise alloy formed by palladium, platinum, gold, silver, copper or nickel or above-mentioned at least two kinds of metals.
Preferably, as the optional execution mode of one, the first resistance slurry printed layers is ruthenium system resistance slurry.
On the other hand, the present embodiment provides a kind of method making the assembly of resistance and electric capacity series winding, comprising:
The first dielectric layer is made by slurry casting technique;
The first dielectric layer is solidified by sintering curing technique;
Printed resistor slurry is in the upper surface of the first dielectric layer;
Burn the first dielectric layer and resistance slurry altogether by sintering curing technique and form resistive layer to solidify resistance slurry, resistive layer is solidified and is connected to the first dielectric layer;
An electrode layer is printed respectively in the lower surface of the first dielectric layer and the upper surface of resistive layer;
By sintering curing technique solidification connection one electrode layer and resistive layer, and solidification connects another electrode layer and the first dielectric layer.
As the optional execution mode of one, make the first dielectric layer by slurry casting technique, comprising:
By the powder of grinding technics preparation for making the first dielectric layer;
Powder is made slurry;
By slurry casting technique, slurry is laminated;
Thin slice is carried out section and form N number of dielectric layering; N be greater than 0 integer;
By laminated process, lamination is carried out in N number of dielectric layering, form the first dielectric layer of predetermined thickness.
As the optional execution mode of one, by the powder of grinding technics preparation for making the first dielectric layer, comprising:
By grinding technics preparation for making oxide or the titanate of the second major element of the first dielectric layer, described titanate comprises barium titanate dielectric matrix, calcium titanate dielectric base body or magnesium titanate dielectric base body, and the oxide of described second major element comprises alundum (Al2O3) dielectric base body.
As the optional execution mode of one, burn the first dielectric layer and resistance slurry altogether by sintering curing technique and form resistive layer to solidify resistance slurry, resistive layer is solidified and is connected to the first dielectric layer, comprising:
Arbitrary in 900 DEG C ~ 1300 DEG C scopes burns under temperature conditions altogether, burns the first dielectric layer altogether and resistance slurry forms resistive layer solidify resistance slurry by sintering curing technique, makes resistive layer solidification be connected to the first dielectric layer.
As the optional execution mode of one, burn the first dielectric layer and resistance slurry altogether by sintering curing technique and form resistive layer to solidify resistance slurry, resistive layer is solidified and is connected to the first dielectric layer, comprising:
Arbitrary in 950 DEG C ~ 1100 DEG C burns under temperature conditions altogether, burns the first dielectric layer altogether and resistance slurry forms resistive layer solidify resistance slurry by sintering curing technique, makes resistive layer solidification be connected to the first dielectric layer.
Preferably, arbitrary in 980 DEG C ~ 1050 DEG C burns under temperature conditions altogether, burns the first dielectric layer altogether and resistance slurry forms resistive layer solidify resistance slurry by sintering curing technique, makes resistive layer solidification be connected to the first dielectric layer.
Preferably, arbitrary in 1000 DEG C ~ 1050 DEG C burns under temperature conditions altogether, burns the first dielectric layer altogether and resistance slurry forms resistive layer solidify resistance slurry by sintering curing technique, makes resistive layer solidification be connected to the first dielectric layer.
Preferably, arbitrary in 980 DEG C ~ 1000 DEG C burns under temperature conditions altogether, burns the first dielectric layer altogether and resistance slurry forms resistive layer solidify resistance slurry by sintering curing technique, makes resistive layer solidification be connected to the first dielectric layer.
Preferably, arbitrary in 1050 DEG C ~ 1100 DEG C burns under temperature conditions altogether, burns the first dielectric layer altogether and resistance slurry forms resistive layer solidify resistance slurry by sintering curing technique, makes resistive layer solidification be connected to the first dielectric layer.
Preferably, arbitrary in 1100 DEG C ~ 1300 DEG C burns under temperature conditions altogether, burns the first dielectric layer altogether and resistance slurry forms resistive layer solidify resistance slurry by sintering curing technique, makes resistive layer solidification be connected to the first dielectric layer.
As the optional execution mode of one, printed resistor slurry, in the upper surface of the first electrode layer, comprising:
Make the resistance slurry that plasma resistance resistivity is 700 ~ 1400 Ω cm;
Printed resistor slurry is in the upper surface of the first electrode layer.
As the optional execution mode of one, method also comprises:
Cutting forms M assembly of preliminary dimension, M be greater than zero integer;
Assembly is tested and packs.
Refer to Fig. 4 a, a kind of assembly method flow chart making resistance and electric capacity series winding that Fig. 4 a provides for the embodiment of the present application.As shown in fig. 4 a, the method for the assembly of the making resistance that the present embodiment provides and electric capacity series winding, comprising:
810, the first dielectric layer is made by slurry casting technique;
820, the first dielectric layer is solidified by sintering curing technique;
830, printed resistor slurry is in the upper surface of the first dielectric layer;
840, burn the first dielectric layer and resistance slurry altogether by sintering curing technique and form resistive layer to solidify resistance slurry, resistive layer is solidified and is connected to the first dielectric layer;
850, an electrode layer is printed respectively in the lower surface of the first dielectric layer and the upper surface of resistive layer;
860, by sintering curing technique solidification connection one electrode layer and resistive layer, and solidification connects another electrode layer and the first dielectric layer.
As the optional execution mode of one, refer to Fig. 4 b, the another kind that Fig. 4 b provides for the embodiment of the present application makes the assembly method flow chart of resistance and electric capacity series winding, as shown in Figure 4 b, makes the first dielectric layer, comprising by slurry casting technique:
811, by the powder of grinding technics preparation for making the first dielectric layer;
812, powder is made slurry;
813, by slurry casting technique, slurry is laminated;
814, thin slice is carried out section and form N number of dielectric layering; N be greater than 0 integer;
815, by laminated process, lamination is carried out in N number of dielectric layering, form the first dielectric layer of predetermined thickness.
As the optional execution mode of one, by the powder of grinding technics preparation for making the first dielectric layer, comprising:
By grinding technics preparation for making oxide or the titanate of the second major element of the first dielectric layer, described titanate comprises barium titanate dielectric matrix, calcium titanate dielectric base body or magnesium titanate dielectric base body, and the oxide of described second major element comprises alundum (Al2O3) dielectric base body.
As the optional execution mode of one, burn the first dielectric layer and resistance slurry altogether by sintering curing technique and form resistive layer to solidify resistance slurry, resistive layer is solidified and is connected to the first dielectric layer, comprising:
Arbitrary in 900 DEG C ~ 1300 DEG C scopes burns under temperature conditions altogether, burns the first dielectric layer altogether and resistance slurry forms resistive layer solidify resistance slurry by sintering curing technique, makes resistive layer solidification be connected to the first dielectric layer.
As the optional execution mode of one, burn the first dielectric layer and resistance slurry altogether by sintering curing technique and form resistive layer to solidify resistance slurry, resistive layer is solidified and is connected to the first dielectric layer, comprising:
Arbitrary in 950 DEG C ~ 1100 DEG C burns under temperature conditions altogether, burns the first dielectric layer altogether and resistance slurry forms resistive layer solidify resistance slurry by sintering curing technique, makes resistive layer solidification be connected to the first dielectric layer.
As the optional execution mode of one, printed resistor slurry, in the upper surface of the first electrode layer, comprising:
Make the resistance slurry that plasma resistance resistivity is 700 ~ 1400 Ω cm;
Printed resistor slurry is in the upper surface of the first electrode layer.
As the optional execution mode of one, method also comprises:
Cutting forms M assembly of preliminary dimension, M be greater than zero integer;
Assembly is tested and packs.
On the other hand, the present embodiment also provides a kind of method making the assembly of resistance and electric capacity series winding, comprising:
The first dielectric layer is made by slurry casting technique;
The first dielectric layer is solidified by sintering curing technique;
One first dielectric layer electrode is printed respectively at the upper and lower faces of the first dielectric layer;
By sintering curing technique solidification connection first dielectric layer and the first dielectric layer electrode;
Printed resistor slurry is in the surface of arbitrary first dielectric layer electrode;
Resistive layer is formed, to solidify contact resistance layer and the first dielectric layer electrode by sintering curing technique solidification resistance slurry;
Print a resistive layer electrode in the surface of resistive layer;
By sintering curing technique solidification contact resistance layer and resistive layer electrode.
As the optional execution mode of one, make the first dielectric layer by slurry casting technique, comprising:
By the powder of grinding technics preparation for making the first dielectric layer;
Powder is made slurry;
By slurry casting technique, slurry is laminated;
Thin slice is carried out section and form N number of dielectric layering; N be greater than 0 integer;
By laminated process, lamination is carried out in N number of dielectric layering, form the first dielectric layer of predetermined thickness.
As the optional execution mode of one, by the powder of grinding technics preparation for making the first dielectric layer, comprising:
By grinding technics preparation for making oxide or the titanate of the second major element of the first dielectric layer, described titanate comprises barium titanate dielectric matrix, calcium titanate dielectric base body or magnesium titanate dielectric base body, and the oxide of described second major element comprises alundum (Al2O3) dielectric base body.
As the optional execution mode of one, printed resistor slurry, in the surface of arbitrary first dielectric layer electrode, comprising:
Make the resistance slurry that plasma resistance resistivity is 700 ~ 1400 Ω cm;
Printed resistor slurry is in the surface of arbitrary first dielectric layer electrode.
As the optional execution mode of one, after sintering curing technique solidification connection first dielectric layer and the first dielectric layer electrode, and printed resistor slurry is before the surface of arbitrary first dielectric layer electrode, and method also comprises:
By the surface of laminated process lamination second dielectric layer in arbitrary first dielectric layer electrode, form the second dielectric layer of predetermined thickness;
Second dielectric layer offers the surface that at least one through hole extends to the first dielectric layer electrode;
The surface printing resistance slurry of the first dielectric layer electrode in through hole, realizes printed resistor slurry in the surface of arbitrary first dielectric layer electrode.
As the optional execution mode of one, solidify the first dielectric layer by sintering curing technique, comprising:
Under arbitrary sintering temperature condition in 1300 DEG C ~ 1400 DEG C scopes, solidify the first dielectric layer by sintering curing technique.
In other embodiments, can under the sintering temperature condition of 1300 DEG C or 1310 DEG C or 1320 DEG C or 1330 DEG C or 1340 DEG C or 1350 DEG C or 1360 DEG C or 1370 DEG C or 1380 DEG C or 1390 DEG C or 1400 DEG C, solidify the first dielectric layer by sintering curing technique, the condition of concrete sintering temperature realizes not by the restriction of the present embodiment.
As the optional execution mode of one, form resistive layer by sintering process solidification resistance slurry, to solidify contact resistance layer and the first dielectric layer electrode, comprising:
Under arbitrary sintering temperature condition in 800 DEG C ~ 950 DEG C scopes, form resistive layer, to solidify contact resistance layer and the first dielectric layer electrode by sintering process solidification resistance slurry.
In other embodiments, can under the sintering temperature condition of 800 DEG C or 810 DEG C or 850 DEG C or 825 DEG C or 860 DEG C or 880 DEG C or 900 DEG C or 910 DEG C or 920 DEG C or 940 DEG C or 830 DEG C or 845 DEG C, resistive layer is formed by sintering process solidification resistance slurry, to solidify contact resistance layer and the first dielectric layer electrode, the condition of concrete sintering temperature realizes not by the restriction of the present embodiment.
As the optional execution mode of one, method also comprises:
Cutting forms M assembly of preliminary dimension, M be greater than zero integer;
Assembly is tested and packs.Refer to Fig. 4 c, the another kind that Fig. 4 c provides for the embodiment of the present application makes the assembly method flow chart of resistance and electric capacity series winding.As illustrated in fig. 4 c, the method for the assembly of the making resistance that the present embodiment provides and electric capacity series winding, comprising:
910, the first dielectric layer is made by slurry casting technique;
920, the first dielectric layer is solidified by sintering curing technique;
930, one first dielectric layer electrode is printed respectively at the upper and lower faces of the first dielectric layer;
940, by sintering curing technique solidification connection first dielectric layer and the first dielectric layer electrode;
950, printed resistor slurry is in the surface of arbitrary first dielectric layer electrode;
960, resistive layer is formed, to solidify contact resistance layer and the first dielectric layer electrode by sintering curing technique solidification resistance slurry;
970, a resistive layer electrode is printed in the surface of resistive layer;
980, by sintering curing technique solidification contact resistance layer and resistive layer electrode.
As the optional execution mode of one, refer to Fig. 4 d, the another kind that Fig. 4 d provides for the embodiment of the present application makes the assembly method flow chart of resistance and electric capacity series winding.As shown in figure 4d, make the first dielectric layer by slurry casting technique, comprising:
911, by the powder of grinding technics preparation for making the first dielectric layer;
912, powder is made slurry;
913, by slurry casting technique, slurry is laminated;
914, thin slice is carried out section and form N number of dielectric layering; N be greater than 0 integer;
915, by laminated process, lamination is carried out in N number of dielectric layering, form the first dielectric layer of predetermined thickness.
As the optional execution mode of one, by the powder of grinding technics preparation for making the first dielectric layer, comprising:
By grinding technics preparation for making oxide or the titanate of the second major element of the first dielectric layer, described titanate comprises barium titanate dielectric matrix, calcium titanate dielectric base body or magnesium titanate dielectric base body, and the oxide of described second major element comprises alundum (Al2O3) dielectric base body.
As the optional execution mode of one, printed resistor slurry, in the surface of arbitrary first dielectric layer electrode, comprising:
Make the resistance slurry that plasma resistance resistivity is 700 ~ 1400 Ω cm;
Printed resistor slurry is in the surface of arbitrary first dielectric layer electrode.
As the optional execution mode of one, refer to Fig. 4 e, the another kind that Fig. 4 e provides for the embodiment of the present application makes the assembly method flow chart of resistance and electric capacity series winding.As shown in fig 4e, in the present embodiment, after sintering curing technique solidification connection first dielectric layer and the first dielectric layer electrode, and printed resistor slurry is before the surface of arbitrary first dielectric layer electrode, and method also comprises:
941, by the surface of laminated process lamination second dielectric layer in arbitrary first dielectric layer electrode, the second dielectric layer of predetermined thickness is formed;
942, the second dielectric layer offers the surface that at least one through hole extends to the first dielectric layer electrode;
Then step 950 replaces to step 943, namely as follows:
The surface printing resistance slurry of the first dielectric layer electrode 943, in through hole, realizes printed resistor slurry in the surface of arbitrary first dielectric layer electrode.
As the optional execution mode of one, solidify the first dielectric layer by sintering curing technique, comprising:
Under arbitrary sintering temperature condition in 1300 DEG C ~ 1400 DEG C scopes, solidify the first dielectric layer by sintering curing technique.
As the optional execution mode of one, form resistive layer by sintering process solidification resistance slurry, to solidify contact resistance layer and the first dielectric layer electrode, comprising:
Under arbitrary sintering temperature condition in 800 DEG C ~ 950 DEG C scopes, form resistive layer, to solidify contact resistance layer and the first dielectric layer electrode by sintering process solidification resistance slurry.
As the optional execution mode of one, method also comprises:
Cutting forms M assembly of preliminary dimension, M be greater than zero integer;
On the other hand, the present embodiment also provides a kind of method making the assembly of resistance and electric capacity series winding, comprising:
Make N number of first dielectric layer; N be greater than 0 integer;
Contraposition is stacked and pressed together all first dielectric layers;
Sintered by all first dielectric layers of high-sintering process to pressing;
At the upper surface printed resistor layer of the first dielectric layer of most top layer; And,
The first capacitance electrode layer is printed at the lower surface of the first dielectric layer of the bottom.
As the optional execution mode of one, at the upper surface printed resistor layer of the first dielectric layer of most top layer, comprising:
Make resistance slurry;
Coating resistance slurry is at the upper surface of the first dielectric layer of most top layer;
By high-sintering process, resistance slurry is sintered, form the first resistance slurry printed layers;
The upper surface of printing electric conducting material to the first resistance slurry printed layers, forms resistance electrode layer.
As the optional execution mode of one, after being sintered by all first dielectric layers of high-sintering process to pressing, and before the upper surface printed resistor layer of the first dielectric layer of most top layer, the method also comprises:
Print the second capacitance electrode layer in the upper surface of the first dielectric layer of most top layer;
Then at the upper surface printed resistor layer of the first dielectric layer of most top layer, comprising:
At the upper surface printed resistor layer of the second capacitance electrode layer.
As the optional execution mode of one, make N number of first dielectric layer, comprising:
Make dielectric slurry;
On coating dielectric slurry to N number of first carrier, N be greater than 0 integer.
As the optional execution mode of one, at printing second capacitance electrode layer after the upper surface of the first dielectric layer of most top layer, and before the upper surface printed resistor layer of the second capacitance electrode layer, the method also comprises:
Lamination second dielectric layer is in the upper surface of the second capacitance electrode layer;
Through hole is offered at the middle part of the second dielectric layer;
At the upper surface printed resistor layer of the second capacitance electrode layer, comprising:
Make resistance slurry;
The surface of the second capacitance electrode layer of resistance slurry in through hole is filled in coating;
By high-sintering process, resistance slurry is sintered, form the first resistance slurry printed layers;
The upper surface of printing electric conducting material to the first resistance slurry printed layers, forms resistance electrode layer.
As the optional execution mode of one, after being sintered by all first dielectric layers of high-sintering process to pressing, and before the upper surface printed resistor layer of the first dielectric layer of most top layer, the method also comprises:
According to pre-set dimension, longitudinal segmentation is carried out to the first dielectric layer of pressing, be made into several and meet pre-set dimension, and the pressing module of N number of first dielectric layer.
As the optional execution mode of one, after the lower surface of the first dielectric layer of the bottom prints the first capacitance electrode layer, the method also comprises
Cut according to package dimension.
Preferably, as the optional execution mode of one, the first dielectric layer is the first ceramic dielectric matrix for making capacitor, and the second dielectric layer is the second ceramic dielectric matrix.
Preferably, as the optional execution mode of one, first ceramic dielectric matrix is oxide or the titanate of the second major element, described titanate comprises barium titanate dielectric matrix, calcium titanate dielectric base body or magnesium titanate dielectric base body, and the oxide of described second major element comprises alundum (Al2O3) dielectric base body.
Preferably, as the optional execution mode of one, the first capacitance electrode layer, inner electrode layer, the second capacitance electrode layer, resistance electrode layer comprise alloy formed by palladium, platinum, gold, silver, copper or nickel or above-mentioned at least two kinds of metals.
Preferably, as the optional execution mode of one, the first resistance slurry printed layers is ruthenium system resistance slurry.
Below in conjunction with accompanying drawing, the assembly making method that the present embodiment provides is described.Refer to Fig. 5 a, a kind of method flow diagram making the assembly of resistance and electric capacity series winding that Fig. 5 a provides for the present embodiment.As shown in Figure 5 a, a kind of method making the assembly of resistance and electric capacity series winding that the present embodiment provides, comprises the steps:
410, N number of first dielectric layer is made; Wherein, N be greater than 0 integer;
420, the upper surface coating inner electrode layer of N-1 the first dielectric layer;
430, contraposition is stacked and pressed together all first dielectric layers; Wherein, inner electrode layer is connected with between adjacent first dielectric layer;
440, sintered by all first dielectric layers of high-sintering process to pressing;
450, at the upper surface printed resistor layer of the first dielectric layer of most top layer; And,
460, the first capacitance electrode layer is printed at the lower surface of the first dielectric layer of the bottom.
As the optional execution mode of one, the preferred implementation of the step 450 that the present embodiment provides is as follows, refers to Fig. 5 b particularly, the manufacture method flow chart of the printed resistor layer that Fig. 5 b provides for the embodiment of the present application.As shown in Figure 5 b, at the upper surface printed resistor layer of the first dielectric layer of most top layer, 451 to step 454 is comprised the steps:
451, resistance slurry is made;
452, the upper surface of resistance slurry at the first dielectric layer of most top layer is applied;
453, by high-sintering process, resistance slurry is sintered, form the first resistance slurry printed layers;
454, print the upper surface of electric conducting material to the first resistance slurry printed layers, form resistance electrode layer.
Preferably, as the optional execution mode of one, after the step 440 shown in Fig. 5 a, and before step 450, present embodiment also provides a kind of preferred construction manufacturing method.Refer to Fig. 5 c particularly, Fig. 5 c provide for the embodiment of the present application another make the method flow diagram of the assembly of resistance and electric capacity series winding.As shown in Figure 5 c, the assembly making method that present embodiment provides comprises the steps:
410, N number of first dielectric layer is made; Wherein, N be greater than 0 integer;
420, the upper surface coating inner electrode layer of N-1 the first dielectric layer;
430, contraposition is stacked and pressed together all first dielectric layers; Wherein, inner electrode layer is connected with between adjacent first dielectric layer;
440, sintered by all first dielectric layers of high-sintering process to pressing;
441, the second capacitance electrode layer is printed in the upper surface of the first dielectric layer of most top layer;
450, at the upper surface printed resistor layer of the second capacitance electrode layer; And,
460, the first capacitance electrode layer is printed at the lower surface of the first dielectric layer of the bottom.
In the present embodiment, the manufacture method shown in Fig. 5 a is increased after step 441, need change the step 450 shown in Fig. 5 a, namely at the upper surface printed resistor layer of the first dielectric layer of most top layer, comprising:
450, at the upper surface printed resistor layer of the second capacitance electrode layer.
As the optional execution mode of one, make N number of first dielectric layer, comprise the following steps:
411, dielectric slurry is made;
412, apply on dielectric slurry to N number of first carrier, N be greater than 0 integer.
As the optional execution mode of one, preferably, refer to Fig. 5 d, Fig. 5 d provide for the embodiment of the present application another make the method flow diagram of the assembly of resistance and electric capacity series winding.As fig 5d, after the step 441 shown in Fig. 5 c, and before step 450, also comprise the steps to realize a kind of preferred modular construction manufacture method.Particularly, at printing second capacitance electrode layer after the upper surface of the first dielectric layer of most top layer, and before the upper surface printed resistor layer of the second capacitance electrode layer, the method also comprises:
442, lamination second dielectric layer is in the upper surface of the second capacitance electrode layer;
443, through hole is offered at the middle part of the second dielectric layer; And the step 450 shown in Fig. 5 c adopts preferred mode to realize in the present embodiment, namely as fig 5d, at the upper surface printed resistor layer of the second capacitance electrode layer, comprise the following steps:
444, resistance slurry is made;
445, the surface of the second capacitance electrode layer of resistance slurry in through hole is filled in coating;
446, by high-sintering process, resistance slurry is sintered, form the first resistance slurry printed layers;
447, print the upper surface of electric conducting material to the first resistance slurry printed layers, form resistance electrode layer.
As the optional execution mode of one, after being sintered by all first dielectric layers of high-sintering process to pressing, and before the upper surface printed resistor layer of the first dielectric layer of most top layer, the method also comprises:
According to pre-set dimension, longitudinal segmentation is carried out to the first dielectric layer of pressing, be made into several and meet pre-set dimension, and the pressing module of N number of first dielectric layer.
As the optional execution mode of one, after the lower surface of the first dielectric layer of the bottom prints the first capacitance electrode layer, the method also comprises
Cut according to package dimension.
Preferably, as the optional execution mode of one, the first dielectric layer is the first ceramic dielectric matrix for making capacitor, and the second dielectric layer is the second ceramic dielectric matrix.
Preferably, as the optional execution mode of one, first ceramic dielectric matrix is oxide or the titanate of the second major element, described titanate comprises barium titanate dielectric matrix, calcium titanate dielectric base body or magnesium titanate dielectric base body, and the oxide of described second major element comprises alundum (Al2O3) dielectric base body.
Preferably, as the optional execution mode of one, the first capacitance electrode layer, inner electrode layer, the second capacitance electrode layer, resistance electrode layer comprise alloy formed by palladium, platinum, gold, silver, copper or nickel or above-mentioned at least two kinds of metals.
Preferably, as the optional execution mode of one, the first resistance slurry printed layers is ruthenium system resistance slurry.
In several embodiments that the application provides; should be understood that; more than describe; be only the embodiment of the application; but the protection range of the application is not limited thereto; anyly be familiar with those skilled in the art in the technical scope that the application discloses, amendment or the replacement of various equivalence can be expected easily, these amendments or replace all should be encompassed in the application protection range within.

Claims (14)

1. an assembly for resistance and electric capacity series winding, is characterized in that, comprising:
First capacitance electrode layer of lamination, the first dielectric layer and resistive layer successively.
2. assembly as claimed in claim 1, it is characterized in that, described first dielectric layer comprises N number of dielectric layering of contraposition lamination, pressing, described N be greater than 0 integer.
3. assembly as claimed in claim 1 or 2, is characterized in that, also comprise:
Be stacked on the second capacitance electrode layer between described first dielectric layer and described resistive layer.
4. assembly as claimed in claim 3, it is characterized in that, described resistive layer comprises:
First resistance slurry printed layers of lamination and resistance electrode layer from the bottom to top.
5. assembly as claimed in claim 4, is characterized in that, also comprise:
Be stacked on second dielectric layer on described second capacitance electrode layer surface;
Described second dielectric layer offers through hole;
Described resistive layer comprises:
For filling described through hole, and be printed in the described first resistance slurry printed layers on the described second capacitance electrode layer surface in described through hole;
Be stacked on the described resistance electrode layer on described first resistance slurry printed layers surface.
6. assembly as claimed in claim 5, is characterized in that, described through hole is polygon or manhole or fan-shaped pylone or ellipse hole.
7. assembly as claimed in claim 6, it is characterized in that, described through hole is symmetric polygonal through hole.
8. assembly as claimed in claim 7, it is characterized in that, described symmetric polygonal through hole is square through-hole, and the length of side of described square through-hole is the arbitrary value in 0.5mm ~ 2mm.
9. assembly as claimed in claim 8, it is characterized in that, the degree of depth of described square through-hole is the arbitrary value in 0.2 ~ 0.6mm.
10. assembly as claimed in claim 6, it is characterized in that, each dielectric in described first dielectric layer is layered as the first ceramic dielectric matrix for making capacitor, and described second dielectric layer is the second ceramic dielectric matrix.
11. assemblies as claimed in claim 10, it is characterized in that, described first ceramic dielectric matrix is oxide or the titanate of the second major element, described titanate comprises barium titanate dielectric matrix, calcium titanate dielectric base body or magnesium titanate dielectric base body, and the oxide of described second major element comprises alundum (Al2O3) dielectric base body.
12. assemblies as claimed in claim 4, is characterized in that, described first resistance slurry printed layers is ruthenium system resistance slurry.
13. assemblies as claimed in claim 12, is characterized in that, the plasma resistance resistivity of described first resistance slurry printed layers is 700 ~ 1400 Ω cm.
14. assemblies as claimed in claim 13, it is characterized in that, the thickness of described assembly is between 1mm-3mm, and the length of described assembly is not more than 2.5mm, is not less than 1mm; The width of described assembly is not more than 2.5mm, is not less than 1mm.
CN201520607109.1U 2015-08-12 2015-08-12 Subassembly of resistance and electric capacity polyphone Active CN204991482U (en)