CN203019723U - High-barrier composite hose - Google Patents
High-barrier composite hose Download PDFInfo
- Publication number
- CN203019723U CN203019723U CN 201320003267 CN201320003267U CN203019723U CN 203019723 U CN203019723 U CN 203019723U CN 201320003267 CN201320003267 CN 201320003267 CN 201320003267 U CN201320003267 U CN 201320003267U CN 203019723 U CN203019723 U CN 203019723U
- Authority
- CN
- China
- Prior art keywords
- layer
- barrier
- hose
- tack coat
- composite soft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The utility model relates to a high-barrier composite hose. The composite hose comprises a hose body, wherein the hose wall of the hose body is provided with a barrier layer which is a PVA (Polyvinyl Acetate) coating, preferably, the hose wall of the hose body is also provided with a printing layer, an outer bonding layer, an inner bonding layer and a heat sealing layer, the printing layer, the outer bonding layer, the barrier layer, the inner bonding layer and the heat sealing layer are orderly glue-jointed from the outside to the inside, the hose wall of the hose body is further provided with an ink layer, the ink layer is located between the printing layer and the outer bonding layer and is respectively glue-jointed with the printing layer and the outer bonding layer, or the ink layer is located outside of the printing layer and glue-jointed with the printing layer, the high-barrier composite hose further comprises a hose shoulder which is mounted on the hose body, and the high-barrier composite hose further comprises a cap which is arranged on a hose port of the hose shoulder in a covering manner. The high-barrier composite hose provided by the utility model is high in barrier property, comprehensively improved in barrier performance, convenient to process, low in production cost and suitable for large-scale promotion and application.
Description
Technical field
The utility model relates to the tubing field, and particularly composite soft tube material field, specifically refer to a kind of high-barrier composite soft tube.
Background technology
Along with the development of material science, the large molecule of plastics has been widely used in the various aspects of social production.In the tubing field, plastic tube is with its high barrier to steam and air, and the safety and sanitation avirulence is being brought into play extremely important effect at packaging fields such as modern cosmetics, food, medicines especially.
Domestic existing explained hereafter plastic tube, the most of use of barrier layer be EVOH.When common EVOH co-extrusion PE film is produced, need large-scale multi-layer co-extruded line, working condition requires high, and EVOH itself is expensive.
The utility model content
The purpose of this utility model is to have overcome above-mentioned shortcoming of the prior art, and a kind of high-barrier composite soft tube is provided, and the barrier of this high-barrier composite soft tube is high, and barrier obtains General Promotion, and easy to process, and production cost is low, is suitable for large-scale promotion application.
In order to realize above-mentioned purpose, high-barrier composite soft tube of the present utility model is characterized in, comprises hose body, and the tube wall of described hose body has barrier layer, and described barrier layer is the PVA coat.
Preferably, the tube wall of described hose body also comprises printed layers, outer tack coat, interior tack coat and hot sealing layer, and described printed layers, described outer tack coat, described barrier layer, described interior tack coat and described hot sealing layer are fitted from outside to inside successively.
More preferably, described printed layers and described hot sealing layer are thermoplastic polyethylene's thin layer, and described interior tack coat and described outer tack coat are transparent resin of binding property layer.
Preferably, the tube wall of described hose body also comprises ink lay, described ink lay is fitted with described printed layers and described outer tack coat between described printed layers and described outer tack coat and respectively, and perhaps described ink lay is positioned at outside described printed layers and with described printed layers and fits.
Preferably, described high-barrier composite soft tube also comprises the pipe shoulder, and described pipe shoulder is installed on described hose body.
More preferably, the wall of described pipe shoulder also has described barrier layer.Therefore, described pipe shoulder is also high-barrier, is for example high-barrier polyethylene pipe shoulder.
More preferably, described high-barrier composite soft tube also comprises cap, and described cap lid is located on the mouth of pipe of described pipe shoulder.
The beneficial effects of the utility model are: high-barrier composite soft tube of the present utility model comprises hose body, the tube wall of described hose body has barrier layer, described barrier layer is the PVA coat, due to the barrier layer that adopts novel PVA coat film as plastic tube, resistance oxygen effect is higher than EVOH, and the wet effect of resistance has had very large improvement especially, comprehensively improved the barrier of plastic tube, and PVA coat film production cost is low, the range of work is wide, be applied to plastic tube production, can produce more high barrier, the product of more packaging characters.
Description of drawings
Fig. 1 is the cross section part schematic diagram of high-barrier composite soft tube of the present utility model.
The specific embodiment
In order more clearly to understand technology contents of the present utility model, describe in detail especially exemplified by following examples.
See also shown in Figure 1ly, this high-barrier composite soft tube comprises hose body, and the tube wall of described hose body has barrier layer 3, and described barrier layer 3 is PVA coats.
In order to improve the performance of hose body, see also shown in Figure 1, in specific embodiment of the utility model, the tube wall of described hose body also comprises printed layers 1, outer tack coat 2, interior tack coat 4 and hot sealing layer 5, and described printed layers 1, described outer tack coat 2, described barrier layer 3, described interior tack coat 4 and described hot sealing layer 5 are fitted from outside to inside successively.
Described printed layers 1 and described hot sealing layer 5 are thermoplastic polyethylene's thin layer, and described interior tack coat 4 and described outer tack coat 2 are transparent resin of binding property layer.
The tube wall of described hose body can also comprise the ink lay (not shown), described ink lay is fitted with described printed layers 1 and described outer tack coat 2 between described printed layers 1 and described outer tack coat 2 and respectively, and perhaps described ink lay is positioned at outside described printed layers 1 and with described printed layers 1 and fits.
Described high-barrier composite soft tube also comprises pipe shoulder (not shown), and described pipe shoulder is installed on described hose body.
The wall of described pipe shoulder also has described barrier layer 3.Therefore, described pipe shoulder is also high-barrier, is for example high-barrier polyethylene pipe shoulder.
Described high-barrier composite soft tube also comprises the cap (not shown), and described cap lid is located on the mouth of pipe of described pipe shoulder.
The manufacture method of above-mentioned high-barrier composite soft tube comprises the following steps:
(1) extrude for the first time compound: printed layers 1, outer tack coat 2 and barrier layer 3 are extruded Compound Machining rolling film are transported to the second composite part;
(2) extrude for the second time compound: will be transported to the volume film of the second composite part and interior tack coat 4 and hot sealing layer 5 and extrude Compound Machining;
(3) cut: to carrying out deburring through the volume film of extruding for the second time after compound, and cut into the required width of tubulation;
(4) tubulation: the section that will roll up film both sides is repaired, and utilizes external force will roll up film and is wrapped on shaping axle, and under the welding of high-frequency energy, volume film both sides are bonded together, and complete the welding of pipe shaft;
(5) casting is takeed on: pipe shaft is enclosed within on suitable injection machine plug, after plastics rotate plasticizing by extruder screw, clamp-ons supporting pipe shoulder mould, and cooling, complete the welding of pipe shoulder and pipe shaft.
Concrete processing conditions is as follows:
(1) extrude for the first time compound raw material:
Polyethylene film, PE particle/EAA particle, PVA coated film
Extrude for the first time compound processing conditions:
The tack coat processing temperature | Main blowing tension force | Secondary blowing tension force | Winding tension |
315℃~325℃ | 200~220N | 120~150N | 240~260N |
Main blowing is printed layers, and secondary blowing is the PVA coat film.
(2) extrude for the second time compound raw material:
Polyethylene film, PE particle/EAA particle is extruded compound semi-finished product for the first time
Extrude for the second time compound processing conditions
The tack coat processing temperature | Main blowing tension force | The second secondary blowing tension force | Winding tension |
315℃~325℃ | 200~220N | 80~100N | 240~260N |
Main blowing is for to extrude compound semi-finished product for the first time, and the second secondary blowing is hot sealing layer.
(3) processing conditions of tubulation
Injection temperature | Injection pressure | Cooling water temperature | Cooling water pressure | The plastic cement temperature | High-frequency energy |
200~250℃ | 20~60bar | 10~20℃ | 3~7bar | 200~300℃ | 50(is outer)/65(is interior) |
The welding fastness of pipe shaft pipe shoulder:
Interventions Requested and result:
Material: the outer tack coat 2/ barrier layer 3(PVA coat of printed layers 1/)/interior tack coat 4/ hot sealing layer 5
1, compound
2, cut
Interventions Requested | Test stone | The method instrument | Assay |
Outward appearance | Do not allow bad order | The 30cm range estimation | Qualified |
The single mode width | 129±1mm | PET tape (precision 0.2mm) | 129.0~129.4mm |
The end face flatness | ≤1mm | Range estimation | Smooth |
3, trombone slide
4, casting shoulder
Interventions Requested | Test stone | The method instrument | Assay |
Outward appearance | Do not allow bad order | The 30cm range estimation | Qualified |
Pipe shoulder thickness | 1.3±0.2mm | Slide measure (0.02mm) | 1.22~1.34mm |
Pipe shoulder cornerite | ≥2.0 | The KMK chi | 2.0~2.2mm |
Pipe shoulder peel strength | The rectangular hand of 15mm tears, non-cracking | ? | Qualified |
Fall | 2.0m/3 inferior | ? | Qualified |
5, barrier information
(1) PVA coat film barrier
Material | PE#PVA80um |
Thoroughly wet data | 1.42g/m 2.day.0.1Mpa(37.8℃,90%) |
The oxygen flow data | 0.38cm3/m 2.day.0.1Mpa(23℃,0%) |
Ambient temperature and humidity | 22℃(60%) |
(2) EVOH co-extrusion film barrier
Material | EVOH co-extrusion film 70u(EVOH15um) |
Thoroughly wet data | 3.38~3.7g/m 2.day.0.1Mpa(37.8℃,90%) |
The oxygen flow data | 0.3~0.5cm 3/m 2.day.0.1Mpa(23℃,0%) |
Ambient temperature and humidity | 22℃(60%) |
Domestic existing explained hereafter plastic tube, the most of use of barrier layer be EVOH, and this novel PVA(polyvinyl alcohol, polyvinyl alcohol) coat has the wet resistance of better resistance oxygen effect, and is and more convenient on the mode of production.When common EVOH co-extrusion PE film is produced, need outsourcing processing, need simultaneously large-scale multi-layer co-extruded line, working condition requires high, and this Novel PVA only needs to apply one deck PVA coating on former film PE, and is easy to process, produce drop into little.After the PE film applies the PVA coating, improved better after tested the wet effect of resistance oxygen resistance of plastic tube, and barriering effect is all higher than generic EVOH co-extrusion PE film.From the comparison of getting on of the price of bi-material, EVOH itself is expensive, its complex manufacturing, production cost are higher, and there is very large cost advantage in the application of this Novel PVA coat film, use the PVA coat film as barrier layer, not only better barriering effect can be reached, more cost can be effectively reduced.
Therefore, major advantage of the present invention is:
1, the barrier layer of Plastics in China composite soft tube generally uses EVOH co-extrusion film as barrier layer, and the Novel PVA coat film is gathered around than EVOH co-extrusion film and had higher barrier.
2, the general large-scale Multi-layer co-extrusion film-blowing equipment of barrier material EVOH co-extrusion film need of production of plastic composite hose, equipment requirement and difficulty of processing are higher, and the PVA coat film only need can reach requirement by coating one deck PVA on original base material, greatly reduces difficulty of processing.
3, there is larger cost advantage in the PVA coat film on the price of raw material own than EVOH co-extrusion film.
To sum up, the barrier of high-barrier composite soft tube of the present utility model is high, and barrier obtains General Promotion, and easy to process, and production cost is low, is suitable for large-scale promotion application.
In this specification, the utility model is described with reference to its specific embodiment.But, still can make various modifications and conversion obviously and not deviate from spirit and scope of the present utility model.Therefore, specification and accompanying drawing are regarded in an illustrative, rather than a restrictive.
Claims (7)
1. a high-barrier composite soft tube, is characterized in that, comprises hose body, and the tube wall of described hose body has barrier layer, and described barrier layer is the PVA coat.
2. high-barrier composite soft tube according to claim 1, it is characterized in that, the tube wall of described hose body also comprises printed layers, outer tack coat, interior tack coat and hot sealing layer, and described printed layers, described outer tack coat, described barrier layer, described interior tack coat and described hot sealing layer are fitted from outside to inside successively.
3. high-barrier composite soft tube according to claim 2, is characterized in that, described printed layers and described hot sealing layer are thermoplastic polyethylene's thin layer, and described interior tack coat and described outer tack coat are transparent resin of binding property layer.
4. high-barrier composite soft tube according to claim 1, it is characterized in that, the tube wall of described hose body also comprises ink lay, described ink lay is fitted with described printed layers and described outer tack coat between described printed layers and described outer tack coat and respectively, and perhaps described ink lay is positioned at outside described printed layers and with described printed layers and fits.
5. high-barrier composite soft tube according to claim 1, is characterized in that, described high-barrier composite soft tube also comprises the pipe shoulder, and described pipe shoulder is installed on described hose body.
6. high-barrier composite soft tube according to claim 5, is characterized in that, the wall of described pipe shoulder also has described barrier layer.
7. high-barrier composite soft tube according to claim 5, is characterized in that, described high-barrier composite soft tube also comprises cap, and described cap lid is located on the mouth of pipe of described pipe shoulder.