CN202621906U - 一种铁水罐 - Google Patents

一种铁水罐 Download PDF

Info

Publication number
CN202621906U
CN202621906U CN 201220198592 CN201220198592U CN202621906U CN 202621906 U CN202621906 U CN 202621906U CN 201220198592 CN201220198592 CN 201220198592 CN 201220198592 U CN201220198592 U CN 201220198592U CN 202621906 U CN202621906 U CN 202621906U
Authority
CN
China
Prior art keywords
ladle
tank skin
permanent layer
jar
working lining
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 201220198592
Other languages
English (en)
Inventor
王家邦
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Low Carbon Energy Saving Technology Co Ltd
Original Assignee
Suzhou Low Carbon Energy Saving Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Low Carbon Energy Saving Technology Co Ltd filed Critical Suzhou Low Carbon Energy Saving Technology Co Ltd
Priority to CN 201220198592 priority Critical patent/CN202621906U/zh
Application granted granted Critical
Publication of CN202621906U publication Critical patent/CN202621906U/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本实用新型的目的在于提供一种使用寿命长、节能效果好的铁水罐。本实用新型的铁水罐,由罐底、罐壁构成,罐底由上至下依次为罐底工作层、罐底永久层,罐壁由内至外依次为罐壁工作层、罐壁永久层,关键在于所述罐壁工作层由复合砖砌成或致密浇注料浇筑而成,所述罐壁永久层由轻质浇注料浇筑而成。本实用新型的铁水罐的罐壁永久层为轻质浇注料制成的轻质隔热层,能够明显降低罐体的散热损失,对于防止铁水温降、延缓铁水与罐粘结、提高铁水罐使用寿命起到显著的效果。

Description

ー种铁水罐
技术领域
[0001] 本实用新型属于钢铁冶金技术领域,具体涉及到ー种具有使用寿命长、节能效果好的铁水罐。
背景技术
[0002] 铁水罐是高炉炼铁产品铁水的收集与运送设备,在中小高炉上使用。铁水罐由作为内衬的耐火材料和外壳组成,外壳是主要的承载结构,需要有足够的刚度和強度,一般由钢板焊成;耐火材料主要起隔热作用,材质一般采用高铝质、铝碳质或铝碳化硅质。随着冶金工业设备的不断更新,对铁水罐的各项使用性能,包括扩容、延长寿命、防止温度流失过快等方面提出了更高的要求。由于铁水罐通常所用耐火材料的配置缺乏隔热材料的保护,造成铁水温度降低过快,铁水容易变稠、粘罐,因此保护铁水温度,减 少热损失显得至关重要。
实用新型内容
[0003] 本实用新型的目的在于提供ー种使用寿命长、节能效果好的铁水罐。
[0004] 本实用新型的铁水罐,由罐底、罐壁构成,罐底由上至下依次为罐底工作层、罐底永久层,罐壁由内至外依次为罐壁工作层、罐壁永久层,关键在于所述罐壁工作层由复合砖砌成或致密浇注料浇筑而成,所述罐壁永久层由轻质浇注料浇筑而成。
[0005] 所用的轻质浇注料具有结构轻、保温效果好的特点,将其作为罐壁的永久层,可以减少罐壁的热量损失,提高节能效果。另外,上述罐底、罐壁均由工作层、永久层分层构成,并且不同层的材料不同,施工方便、结构稳固,使用寿命长。
[0006] 具体来说,所述罐底工作层由铝碳砖或铝碳化硅砖砌成,所述罐底永久层由轻质浇注料和高铝砖组成,高铝砖位于轻质浇注料上部。
[0007] 具体来说,所述的轻质浇注料骨料为氧化铝空心球、镁铝空心球、刚玉空心球、轻质高铝颗粒或轻质莫来石颗粒中的ー种或几种的混合物。
[0008] 本实用新型的铁水罐的罐壁永久层为轻质浇注料制成的轻质隔热层,能够明显降低罐体的散热损失,对于防止铁水温降、延缓铁水与罐粘结、提高铁水罐使用寿命起到显著的效果。
附图说明
[0009] 图I是本实用新型的铁水罐的结构示意图。
具体实施方式
[0010] 下面对照附图,通过对实施例的描述,对本实用新型的具体实施方式如所涉及的各构件的形状、构造、各部分之间的相互位置及连接关系、各部分的作用及工作原理等作进一歩的详细说明。[0011] 实施例I :
[0012] 如图I所示,本实施例的铁水罐由罐底、罐壁构成,罐底由上至下依次为罐底工作层11、罐底永久层12,罐底工作层11由铝碳砖砌成,罐底永久层12由刚玉空心球轻质浇注料和一层高铝砖砌成;罐壁由内至外依次为罐壁工作层21、罐壁永久层22,罐壁工作层21由莫来石复合砖砌成,罐壁永久层22由氧化铝空心球浇注料浇筑而成。
[0013] 本实施例的施工过程砌筑顺序为罐底永久层12、罐壁永久层22、罐底工作层11、罐壁工作层21。
[0014] 实施例2 :
[0015] 如图I所示,本实施例的铁水罐由罐底、罐壁构成,罐底由上至下依次为罐底工作层11、罐底永久层12,罐底工作层11由铝碳化硅砖砌成,罐底永久层12由氧化铝空心球轻质浇注料和一层高铝砖砌成;罐壁由内至外依次为罐壁工作层21、罐壁永久层22,罐壁エ作层21由高铝浇注料浇筑而成,罐壁永久层22由刚玉空心球浇注料浇筑而成。
[0016] 本实施例的施工过程砌筑顺序为罐底永久层12、罐壁永久层22、罐底工作层11、罐壁工作层21。
[0017] 实施例3:
[0018] 如图I所示,本实施例的铁水罐由罐底、罐壁构成,罐底由上至下依次为罐底工作层11、罐底永久层12,罐底工作层11由铝碳化硅砖砌成,罐底永久层12由镁铝尖晶石空心球轻质浇注料和一层高铝砖砌成;罐壁由内至外依次为罐壁工作层21、罐壁永久层22,罐壁工作层21由刚玉-莫来石浇注料浇筑而成,罐壁永久层22由镁铝空心球轻质浇注料浇筑而成。
[0019] 本实施例的施工过程砌筑顺序为罐底永久层12、罐壁永久层22、罐底工作层11、罐壁工作层21。
[0020] 实施例4 :
[0021] 如图I所示,本实施例的铁水罐由罐底、罐壁构成,罐底由上至下依次为罐底工作层11、罐底永久层12,罐底工作层11由铝碳砖砌成,罐底永久层12由氧化铝空心球、镁铝空心球和刚玉空心球混合轻质浇注料和一层高铝砖砌成;罐壁由内至外依次为罐壁工作层21、罐壁永久层22,罐壁工作层21由高铝复合砖砌成,罐壁永久层22由氧化铝空心球、镁铝空心球和刚玉空心球混合轻质浇注料浇筑而成。
[0022] 本实施例的施工过程砌筑顺序为罐底永久层12、罐壁永久层22、罐底工作层11、罐壁工作层21。
[0023] 实施例5 :
[0024] 如图I所示,本实施例的铁水罐由罐底、罐壁构成,罐底由上至下依次为罐底工作层11、罐底永久层12,罐底工作层11由铝碳砖砌成,罐底永久层12由氧化铝空心球、镁铝空心球和刚玉空心球混合轻质浇注料和一层高铝砖砌成;罐壁由内至外依次为罐壁工作层21、罐壁永久层22,罐壁工作层21由镁质复合砖砌成,罐壁永久层22由氧化铝空心球、镁铝空心球、刚玉空心球、轻质高铝颗粒和轻质莫来石颗粒混合物为骨料的轻质浇注料浇筑而成。
[0025] 本实施例的施工过程砌筑顺序为罐底永久层12、罐壁永久层22、罐底工作层11、
罐壁工作层21。[0026] 实施例6 :
[0027] 如图I所示,本实施例的铁水罐由罐底、罐壁构成,罐底由上至下依次为罐底工作层11、罐底永久层12,罐底工作层11由铝碳砖砌成,罐底永久层12由氧化铝空心球、镁铝空心球和刚玉空心球混合轻质浇注料和一层高铝砖砌成;罐壁由内至外依次为罐壁工作层21、罐壁永久层22,罐壁工作层21由铝碳浇注料浇筑而成,罐壁永久层22由轻质高铝颗粒为骨料的轻质浇注料浇筑而成。
[0028] 本实施例的施工过程砌筑顺序为罐底永久层12、罐壁永久层22、罐底工作层11、罐壁工作层21。
[0029] 实施例7 :
[0030] 如图I所示,本实施例的铁水罐由罐底、罐壁构成,罐底由上至下依次为罐底工作层11、罐底永久层12,罐底工作层11由铝碳砖砌成,罐底永久层12由氧化铝空心球、镁铝空心球和刚玉空心球混合轻质浇注料和一层高铝砖砌成;罐壁由内至外依次为罐壁工作层21、罐壁永久层22,罐壁工作层21由镁碳浇注料浇筑而成,罐壁永久层22由轻质莫来石颗粒为骨料的轻质浇注料浇筑而成。
[0031] 本实施例的施工过程砌筑顺序为罐底永久层12、罐壁永久层22、罐底工作层11、罐壁工作层21。
[0032] 实施例8 :
[0033] 如图I所示,本实施例的铁水罐由罐底、罐壁构成,罐底由上至下依次为罐底工作层11、罐底永久层12,罐底工作层11由铝碳砖砌成,罐底永久层12由氧化铝空心球、镁铝空心球和刚玉空心球混合轻质浇注料和一层高铝砖砌成;罐壁由内至外依次为罐壁工作层21、罐壁永久层22,罐壁工作层21由碱性复合砖,罐壁永久层22由轻质莫来石颗粒为骨料的轻质浇注料浇筑而成。
[0034] 本实施例的施工过程砌筑顺序为罐底永久层12、罐壁永久层22、罐底工作层11、
罐壁工作层21。

Claims (2)

1. ー种铁水罐,由罐底、罐壁构成,罐底由上至下依次为罐底工作层、罐底永久层,罐壁由内至外依次为罐壁工作层、罐壁永久层,其特征在于,所述罐壁工作层由复合砖砌成或致密浇注料浇筑而成,所述罐壁永久层由轻质浇注料浇筑而成。
2.根据权利I所述的铁水罐,其特征在于所述罐底工作层由铝碳砖或铝碳化硅砖砌成,所述罐底永久层由轻质浇注料和高铝砖组成,高铝砖位于轻质浇注料上部。
CN 201220198592 2012-05-07 2012-05-07 一种铁水罐 Expired - Fee Related CN202621906U (zh)