CN201649501U - Polyphenyl composite decorative board - Google Patents

Polyphenyl composite decorative board Download PDF

Info

Publication number
CN201649501U
CN201649501U CN2010201302415U CN201020130241U CN201649501U CN 201649501 U CN201649501 U CN 201649501U CN 2010201302415 U CN2010201302415 U CN 2010201302415U CN 201020130241 U CN201020130241 U CN 201020130241U CN 201649501 U CN201649501 U CN 201649501U
Authority
CN
China
Prior art keywords
polyphenyl
cracking resistance
slurry
decorative
decorative board
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CN2010201302415U
Other languages
Chinese (zh)
Inventor
王琰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sichuan Familia New Building Materials Co., Ltd
Original Assignee
王琰
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 王琰 filed Critical 王琰
Priority to CN2010201302415U priority Critical patent/CN201649501U/en
Application granted granted Critical
Publication of CN201649501U publication Critical patent/CN201649501U/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

The utility model provides a polyphenyl composite decorative board, which is of a layered structure and consists of a polyphenyl board, anti-crack mortar, high-strength alkali-resistant mesh fabrics and a decorative slurry layer. The utility model effectively overcomes the defect that the conventional product is too heavy, which does not meet the national requirement; in terms of the fabrication technique, the utility model binds the polyphenyl board and the decorative slurry layer together, the decorative slurry layer is thin, consequently, the weight of the decorative board is reduced, and when in use, the decorative board cannot easily come off due to light weight. According to need, a pigment can be added in the slurry, a beautify pattern can be made, the simulation degree is extremely high, and the heat-preserving layer of the conventional product is dispensed with.

Description

A kind of polyphenyl composite decorative board
Technical field
The utility model relates to a kind of building and ornament materials, specifically is a kind of polyphenyl composite decorative board.
Background technology
Past have plenty of employing daub on exterior wall, yet the stain resistance of coating is poor to the decoration of exterior wall site operation normally.Therefore the decoration to exterior wall all adopts decoration panel marble, granite mostly, but pertinent regulations according to national decoration of exterior wall standard, weight to decoration of exterior wall must not be too heavy, because too heavy words can come off easily, cause damage, yet a large amount of in the market granite, marble and decoration panels that use are as decorative exterior wall, yet granite, marble exist cladding cost too high, easily come off, be not incubated, if adopt this mode one to increase the cost of product, two cause the weight of decorative panel excessive easily, do not meet national standard.
The utility model content
The technical problems to be solved in the utility model is to overcome above-mentioned shortcoming a kind of polyphenyl composite decorative board and its manufacture craft are provided, it is that polyphenyl plate and pulp layer are solidified as one, removed insulation layer from,, avoided the bonding situation that the super scope of weight occurs to take place so the very thin body of decorative layer is light; Solve the big problem of weight in the prior art.
The present invention is achieved in that a kind of polyphenyl composite decorative board of structure, be layer structure, it is characterized in that: comprise polyphenyl plate, scraped one deck cracking resistance mortar at the polyphenyl plate upper surface, on the cracking resistance mortar, be equipped with high-strength alkaline-resisting grid cloth then, and on high-strength alkaline-resisting grid cloth, scraped anticracking grout again, be covered with on the anticracking grout of scraping outside and comprise the decoration pulp layer that forms by portland cement, quartz sand, iron oxide pigment and cement additire mixing preparation; On the another side of polyphenyl plate, also scrape one deck cracking resistance mortar, on this cracking resistance mortar, also be equipped with high-strength alkaline-resisting grid cloth, on this high-strength alkaline-resisting grid cloth, scraped one deck anticracking grout again.
According to polyphenyl plate composite decorating board described in the utility model, it is characterized in that: anticracking grout thickness is no more than 1.5 millimeters.
Advantage of the present utility model is: present technique has adopted polyphenyl plate to can be used for the insulation layer of construction wall, roof heat insulation, composite insulating board, and be the extraordinary heat-barrier material of a kind of effect, be applicable to the characteristic of various ornament materials, on manufacture craft, the present invention is solidified as one with polyphenyl plate and decoration pulp layer, with decorate pulp layer make the very thin weight that alleviates decorative panel on the whole, also just reached the purpose of the light difficult drop-off of body during use.Can add pigment as required in slurry, can make the grain pattern that becomes exquisite appearance, fidelity is high, and has removed the insulation layer of prior art from.
Description of drawings
Fig. 1 is the polyphenyl composite decorative board structural representation
Wherein, 1, polyphenyl plate; 2, cracking resistance mortar, 3, high-strength alkaline-resisting grid cloth, 4, decorate pulp layer.
The specific embodiment
The present invention implements according to following proposal:
The invention provides a kind of polyphenyl composite decorative board, be layer structure, comprise polyphenyl plate 1, polyphenyl plate 1 has played insulation, heat insulation useful effect here, scraped one deck cracking resistance mortar 2 at the polyphenyl plate upper surface, on cracking resistance mortar 2, be equipped with high-strength alkaline-resisting grid cloth 3 then, and on high-strength alkaline-resisting grid cloth 3, scraped anticracking grout 2 again, be covered with on the anticracking grout of scraping outside 2 and comprise the decoration pulp layer 4 that forms by portland cement, quartz sand, iron oxide pigment and cement additire mixing preparation; On the another side of polyphenyl plate 1, also scrape one deck cracking resistance mortar 2, on this cracking resistance mortar 2, also be equipped with high-strength alkaline-resisting grid cloth 3, on this high-strength alkaline-resisting grid cloth 3, scraped one deck anticracking grout 2 again.Described anticracking grout thickness is no more than 1.5 millimeters.
A kind of manufacture craft of polyphenyl composite decorative board: it is characterized in that step is as follows:
1., prepare: require the required mould that meets thickness, size specification requirement of producing according to the building operations occasion, prepare polyphenyl plate according to the size and the specification requirement of mould, and polyphenyl plate is fit in the mould; Mould is the same like a box, but the thickness of the aspect ratio polyphenyl plate of mould more greatly;
2., decorate the preparation of slurry: described decoration slurry is made of portland cement, quartz sand, iron oxide pigment and cement additire mixing, according to the 100Kg portland cement: 200~400Kg quartz sand: 0.5~2Kg cement additire mixes, optimal proportion is, 100Kg portland cement: 300Kg quartz sand: the 1.2Kg cement additire mixes, the effect of iron oxide pigment is to get look and forms pattern, therefore it can add component according to actual needs, makes behind the slurry standby;
3., preparation: scrape the cracking resistance mortar that one deck plays bonding effect on the first polyphenyl plate in mould, its requirement is that the thickness of cracking resistance mortar does not exceed 1.5 millimeters, and then on the cracking resistance mortar, be equipped with the high-strength alkaline-resisting grid cloth of one deck, and then on this grid cloth, scrape the cracking resistance mortar that a layer thickness does not exceed 1.5 millimeters then again;
4., inject slurry: completing steps is in time put into the soft mode of a band porous after 3. in mould, by the decoration slurry that 2. implantation step on the cracking resistance mortar of the hole on the soft mode prepares, Ci Shi decoration slurry has added pigment according to demand so; Take off the decoration slurry strickling that soft mode will just inject then, form thin and even; (soft mode itself is provided with a lot of holes, and its effect is to be injected into formation slurry heap on the cracking resistance mortar by the hole on it decorating slurry, the slurry heap is wipeed off afterwards again, forms pattern);
5., secondary pouring: 4. lay one deck decoration pulp layer again in the back at once at completing steps, in the decoration slurry, also be added with pigment according to demand, and then integral body strickling (just wipeing off along the edge of mould is whole), uniform compacted zone is just decorated pulp layer to form thin;
6., vibration and shaping: carry out vibration processing on the platform that is positioned over vibration that completing steps will make after 5., requirement is that upper surface is carried out vibration processing, make slurry fill up the groove of mould substantially, discharge the air in the slurry simultaneously, make to have between anticracking grout, the slurry well and merge;
7., completing steps carries out the demoulding, maintenance operation after 6., its requirement is that highest hardness is arrived in maintenance;
8., maintenance after the highest hardness to its surface finish;
9., wait to polish and spraying waterproofing agent of organosilicon on the slurry of drying after finishing;
10., scrape rough: scraped its thickness of layer of even at the soffit of polyphenyl plate and do not exceeded 1.5 millimeters cracking resistance mortars, secondly on the cracking resistance mortar, be covered with high-strength alkaline-resisting grid cloth, on the high-strength alkaline-resisting grid cloth of laying, scrape a layer thickness again and do not exceed 1.5 millimeters cracking resistance mortars.
The composition of pulp layer also comprises stone: described slurry mainly is that the dosage of other material is as follows: quartz sand 200~400Kg, water reducing agent 800~1400g, reinforcing agent 4000~10000g, water 30~40Kg are by mixing by cement 100Kg meter.

Claims (2)

1. polyphenyl composite decorative board, be layer structure, it is characterized in that: comprise polyphenyl plate (1), scraped one deck cracking resistance mortar (2) at the polyphenyl plate upper surface, on cracking resistance mortar (2), be equipped with high-strength alkaline-resisting grid cloth (3) then, and on high-strength alkaline-resisting grid cloth (3), scraped anticracking grout (2) again, be covered with on the anticracking grout of scraping outside (2) and decorate pulp layer (4); On the another side of polyphenyl plate (1), also scrape one deck cracking resistance mortar (2), on this cracking resistance mortar (2), also be equipped with high-strength alkaline-resisting grid cloth (3), on this high-strength alkaline-resisting grid cloth (3), scraped one deck anticracking grout (2) again.
2. polyphenyl plate composite decorating board according to claim 1 is characterized in that: anticracking grout (2) thickness is no more than 1.5 millimeters.
CN2010201302415U 2010-03-12 2010-03-12 Polyphenyl composite decorative board Expired - Lifetime CN201649501U (en)