CN1923742A - Novel construction materials and process method thereof - Google Patents

Novel construction materials and process method thereof Download PDF

Info

Publication number
CN1923742A
CN1923742A CN 200510047115 CN200510047115A CN1923742A CN 1923742 A CN1923742 A CN 1923742A CN 200510047115 CN200510047115 CN 200510047115 CN 200510047115 A CN200510047115 A CN 200510047115A CN 1923742 A CN1923742 A CN 1923742A
Authority
CN
China
Prior art keywords
loess
stirrer
water
weight
wetting agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200510047115
Other languages
Chinese (zh)
Inventor
宋哲
Original Assignee
宋哲
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 宋哲 filed Critical 宋哲
Priority to CN 200510047115 priority Critical patent/CN1923742A/en
Publication of CN1923742A publication Critical patent/CN1923742A/en
Pending legal-status Critical Current

Abstract

The invention discloses a new-typed building material, which is composed of at least one combined powder-shaped solid material of 40-60% loess, medical stone, jade and sericite, wherein the wetting agent, purified water and soluble emulsion paint can be added in the material, which produces large amount of radioactive far infrared ray and anion to improve kinds of harmful material and gas.

Description

A kind of New Building Materials and working method thereof
Technical field
The present invention relates to a kind of novel material of construction and working method thereof.
Background technology
At present, known building coating can only be to having built decoration, having beautified the effect of wall.The toxin that can produce the cement of building, objectionable impurities such as the formaldehyde behind the decoration and gas are like water off a duck's back.Along with the wall in people and the long-time house of living of animal with on every side because of ultraviolet ray, the infiltration and the humidity of flue dust peculiar smell cause bacterial reproduction, go rotten and infested, the ornament of chemosynthesis and carpet have in a large amount of bacterial reproduction air and fill the air objectionable impuritiess such as peculiar smell and fibrous magnesium silicate.Eczema is caught a cold in recent years, headache, and dermatitis etc. can produce detrimentally affect to human body.Up to the present use perfume compound and chemical to come deodorizing and equilibrium moisture usually.This can't fundamentally thoroughly solve an above difficult problem.
Summary of the invention
The purpose of this invention is to provide a kind of novel material of construction, it can overcome existing shortcoming in the prior art, radiates the far infrared rays of 6~20 mu m ranges in a large number and produces negative ion, play antibacterial, protection against the tide, sterilization, the effect of heavy metal is received in deodorizing, can improve people's living environment.
The object of the present invention is achieved like this: it is that wherein loess accounts for the 40-60% of gross weight by at least a pulverulent solids material that combines in loess and medical stone, jade and the sericite.
The working method of above-mentioned material of construction comprises the steps:
A, get the loess of ground surface below 1 meter, be heated to 750~1500 ℃, kept 15-30 minute, reduce to room temperature then, heat repeatedly, lower the temperature three times;
B, get loess 40-60%, other solid material 40-60% by weight, mix mutually, be crushed to more than 200 orders, be stirred to evenly, make pulverous material of construction in the stirrer high speed.
The using method of this material of construction is identical with cement, tempers can be used in earth material and be used for adhesives between the brick and tile.
Can also be added with wetting agent, pure water and water-soluble emulsion paint in the above-mentioned pulverulent solids material of construction, make wallcovering.Weight hundred ratios of each component are as follows in the wallcovering: pulverulent solids material: wetting agent: pure water: water-soluble emulsion paint=16: 4: 20: 60.
The working method of above-mentioned wallcovering comprises the steps:
A, get the loess of ground surface below 1 meter, be heated to 750~1500 ℃, kept 15-30 minute, be cooled to room temperature then, heat repeatedly, lower the temperature three times;
B, get loess 40-60%, other solid material 40-60% by weight and mix, material is crushed to more than 200 orders, fully stirs in stirrer, makes and adds material A;
C, get A material 16% by weight, add wetting agent 4%, pure water 20%, water-soluble emulsion paint 60% and mixes mutually, insert the interior high-speed stirring of stirrer, it is mixed.
The operating weight of solid material medical stone, jade and sericite can be arranged in pairs or groups arbitrarily in the material of construction of the present invention.
Wetting agent among the present invention uses any water-soluble wetting agent all passable.
The main component of loess has quartz, calcite and mica, and quartz accounts for mineral total amount 40~50% loess and has the characteristic of emitting far infrared ray.So the deodorizing that can purify water, stimulate circulation, alleviating pain, fatigue recovery helps for sleep.The Nicotine of removing the smoking generation has extraordinary effect.
The main chemical compositions of medical stone is inorganic silico-aluminate.Comprising SiO2, Al2O3, Fe2O3, FeO, MgO, CaO, K2O, Na2O, TiO2, P2O5, MnO etc., also contain the required whole major elements of animal, as: trace element and rare earth elements such as K, Na, Ca, Mg, Cu, Mo, about 58 kinds more than.Medical stone has performances such as adsorptivity, solvability, modulability, biological activity and mineralising.But objectionable impurities in the dedusting deodorizing absorbed air, the Nicotine of removing the smoking generation has extraordinary effect.
Sericite belongs to mica mineral, it is a kind of sheet particulate white mica, structure is dioctahedron, promptly constitutes tetrahedral top oxygen (active oxygen) by two-layer tortoise oxygen tetrahedron and layer of aluminum oxygen octahedra and is positioned at two-layer six veil central authorities with additional negatively charged ion (OH), constitutes active crystal water group.(001) cleavage is complete, can be split into sheet as thin as a wafer, and radius-thickness ratio is big.The sericite crystal-chemical formula is: K 0.5-1(Al, Fe, Mg) 2(SiAl) 4O 10(OH) 2NH 2O, its Chemical Composition: SiO 243.13~49.04%, Al 2O 327.93~37.44%, K 2O+Na 2O9~11%, H 2O 4.13~6.12%.Sericite has satin luster, and radius-thickness ratio>80 are white in color.Light gray-white, proportion 2.6-2.7, hardness 2-3, full of elasticity, flexible.High temperature resistant (more than the 600C), chemicals-resistant corrodibility is strong, and ultraviolet ray is had splendid shielding effect.Radioresistance 5 * 1014 thermal neutrons/cm2 is to illumination.
Jade contains the trace element of multiple human body needs, as zinc, iron, copper, manganese, magnesium, selenium, cobalt, chromium, titanium, calcium, potassium, sodium etc., the a large amount of red places far away of beautiful radiation ripples line form linear light ripple is used for oncotherapy, reduce to cough and breathe heavily, sharp lung nourishes heart, tranquillizing by calming the heart replenishes insufficient element of human body and trace element.The classical Huangdi's Internal Classics of the medical science of Ancient Times in China, Tang Materia Medica, " legendary god of farming's book on Chinese herbal medicine ", " book on Chinese herbal medicine receive order " but in all claim jade can pacify soul, dredge blood vessels, aligning lung, bright order, flexibilizing tendon and strengthening bone.
The present invention utilizes loess, jade, medical stone, combinations of materials such as sericite can radiate the far infrared rays and the negative ion of 6~20 mu m ranges in a large number, and are antibacterial, protection against the tide, sterilization, deodorizing receives the characteristic of heavy metal to solve the toxin that cement produces, the peculiar smell in the house, mouldy, Nicotine, humidity, formaldehyde etc. improve the human residential environment.
Material of construction of the present invention can radiate human body beneficial's far infrared rays and negative ion, improves various objectionable impuritiess and obnoxious flavour that building and finishing bring.The present invention can nip off a large amount of harmful electronic wave, in and objectionable impurities lipid peroxide in the human body, ph value has no to injure at 8~9.5 pairs of human bodies, loess, beautiful, medical stone, physical property adjustable air humidity such as sericite purify air, remove peculiar smell, smoke, delaying human body caducity stimulates circulation.
Embodiment
The present invention will be further described in detail below in conjunction with specific embodiment.
Embodiment one
A, at first get the loess 36kg on following 1 meter of the face of land, go into the process furnace baking, be warming up to 1500 ℃, keep reducing to room temperature after 15 minutes; Heat up repeatedly, lower the temperature three times.
B, will toast in the later loess and add medical stone 14.4kg, beautiful 14.4kg, sericite 7.2kg, and wear into 200 orders with raymond mill, and be stirred to evenly in the stirrer high speed, be that A expects.
C, in the A that makes material, add water-based system with no foam wetting agents (the novel wetting agent of the German TegoChemieService of TegoWet500 company) 18kg, pure water 90kg, stirred 30~60 minutes with 3000~4000rpm at the high-speed vacuum stirrer, stir moistening even, add water-soluble emulsion paint 270kg then, got final product in 60~90 minutes with the stirring of 1000~1500rpm rotating speed with stirrer.
Can whitewash floor and wall in order to the painting object that last method is made.
Embodiment two
A, at first get the loess 100kg on following 1 meter of the face of land, go into the process furnace baking, be warming up to 1000 ℃, keep reducing to room temperature after 20 minutes; Heat up repeatedly, lower the temperature three times.
B, will toast in the later loess and add medical stone 80kg, and wear into 320 orders with raymond mill, and be stirred to evenly in the stirrer high speed, be that A expects.
C, in A material, add wetting agent Supreme Being Si Balong 6900 series (Disparlon-6900: trade(brand)name) 44.8kg and pure water 224kg, insert the high-speed vacuum stirrer with 3000-4000rpm stir stirred in 30~60 minutes moistening evenly; Add water based emulsion polymkeric substance 672kg, got final product in 60~90 minutes with the stirring of 1000~1500rpm rotating speed with stirrer.Can whitewash floor and wall in order to the painting object that last method is made.
Embodiment three
A, at first get the loess 60kg on following 1 meter of the face of land, go into the process furnace baking, be warming up to 750 ℃, keep reducing to room temperature after 30 minutes; Heat up repeatedly, lower the temperature three times.
B, will toast in the later loess and add medical stone 40kg, wear into 320 orders, and be stirred to evenly in the stirrer high speed and get final product with raymond mill, with the material of construction of this method making can be used as ground or brick, watt the caking agent use.
Embodiment four
A, at first get the loess 32kg on following 1 meter of the face of land, go into the process furnace baking, be warming up to 1500 ℃, keep reducing to room temperature after 15 minutes; Heat up repeatedly, lower the temperature three times.
B, adding medical stone 24kg, beautiful 24kg wear into 320 orders with raymond mill, and are stirred to evenly in the stirrer high speed.
C, interpolation wetting agent Supreme Being Si Balong 6900 series (Disparlon-6900: trade(brand)name) 20kg and pure water 100kg, inserting the high-speed vacuum stirrer stirred moistening even in 30~60 minutes with the 3000-4000rpm stirring, add dope for inner wall of architecture 300kg, utilize stirrer 1000-1500rpm to stir and got final product in 60~90 minutes.Make material of construction in order to last method and can be used as the metope painting object.

Claims (4)

1, a kind of New Building Materials is characterized in that it is that wherein loess accounts for the 40-60% of gross weight by at least a pulverulent solids material that combines in loess and medical stone, jade and the sericite.
2, according to the said material of construction of claim 1, it is characterized in that it also is added with wetting agent, pure water and water-soluble emulsion paint, its weight percent is as follows: pulverulent solids material: wetting agent: pure water: water-soluble emulsion paint=16: 4: 20: 60.
3,, it is characterized in that it comprises the steps: as the working method of the said material of construction of claim 1
A, get the loess of ground surface below 1 meter, be heated to 750~1500 ℃, kept 15-30 minute, reduce to room temperature then, heat repeatedly, lower the temperature three times;
B, get loess 40-60%, other solid material 60-40% by weight, mix mutually, be crushed to more than 200 orders, be stirred to evenly in the stirrer high speed and get final product.
4,, it is characterized in that it comprises the steps: as the working method of the said material of construction of claim 2
A, get the loess of ground surface below 1 meter, be heated to 750~1500 ℃, kept 15-30 minute, reduce to room temperature then, heat repeatedly, lower the temperature three times;
B, get loess 40-60%, other solid material 60-40% by weight and mix, be crushed to more than 200 orders, in stirrer, fully stir, make and add material A;
C, get A material 16% by weight, add wetting agent 4%, pure water 20%, water-soluble emulsion paint 60% and mixes mutually, insert the interior high-speed stirring of stirrer, it is mixed.
CN 200510047115 2005-08-31 2005-08-31 Novel construction materials and process method thereof Pending CN1923742A (en)