CN1821178A - Method for preparing middle ladle dry vabrative material - Google Patents
Method for preparing middle ladle dry vabrative material Download PDFInfo
- Publication number
- CN1821178A CN1821178A CNA2006100185037A CN200610018503A CN1821178A CN 1821178 A CN1821178 A CN 1821178A CN A2006100185037 A CNA2006100185037 A CN A2006100185037A CN 200610018503 A CN200610018503 A CN 200610018503A CN 1821178 A CN1821178 A CN 1821178A
- Authority
- CN
- China
- Prior art keywords
- dry
- vibrating material
- tundish
- forsterite
- dry vibrating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to the preparation process of dry vibrating material for middle ladle. The dry vibrating material is prepared with magnesite or forsterite in 85-97 wt% and sodium metasilicate in 3-15 wt%, and through mixing, vibration forming, stoving at 100-400 deg.c and demolding. The magnesite or forsterite is graded with 0.088-2 mm components in 80-90 wt% and 0.088 mm below components in 10-20 wt%. The present invention adopts non-toxic, smell-less and harmless sodium metasilicate as bonder, so that the dry vibrating material may be low temperature smelted during the stoving process to polymerize constantly to raise strength. The dry vibrating material has no carbon increment to the molten steel, high corrosion resistance, easy degradation and environment friendship.
Description
One, technical field
The invention belongs to the unshape refractory technical field.Relate in particular to a kind of preparation method of tundish dry vibratory material.
Two, background technology
That the tundish working lining plays in continuous casting production process is high temperature resistant, the effect of slag corrosion resistance, heat-insulation and heat-preservation, and along with the growth day by day of Clean Steel and steel alloy demand, tundish also becomes in the process for making the final key link to steel secondary refining simultaneously.The tundish working lining changes magnesia, the calcareous unshape refractory of magnesium into by silica heat-insulating plate, form of construction work by build by laying bricks or stones change into manual smear, mechanically spraying, along with quoting of quick replacing mouth of a river technology, developed tundish dry vibratory material.As " continuous casting tundish alkaline dry working lining " (CN01115190.0) technology, be unsetting composition based on magnesia, its component is the percentage composition meter by weight: magnesia 85~95%, boride 0.5~3.0%, thermoplastic material 2~10%, phosphoric acid salt 1~3%, fluorochemical 1~3%; " the calcareous dry-type working lining of a kind of novel tundish magnesium " (CN 02117935.2) technology, with synthetic magnesia-calcium clinker, passivation dolomite sand, passive lime stone sand, calcined dolomite sand, lime kilning stone sand etc. is calcareous raw material, with iron scale, clay, silicon powder etc. is sintering aid, with resin, malt sugar, PVC is wedding agent, make the dry type inner lining material through uniform mixing, at the scene by the construction of tundish mould tire, and with 150~350 ℃ of bakings 1~3 hour, take off the mould tire, working lining; " continuous casting tundish working lining " (CN 02116839.3) technology, magnesia 80~95%, alumina 1~10%, soft clay 1~5%, organic thermoplastic compound 2~15%; " a kind of novel tundish dry working lining " (CN1459345A) and " a kind of continuous casting with tundish dry vibratory material and preparation method thereof " (CN200410061192.3) technology, with magnesia, olivine sand, synthetic magnesia-calcium clinker, passivation dolomite sand, calcining olivine sand is basic raw material, with Tai-Ace S 150, polymerize aluminum chloride, halogen, water glass and carbamate additives for low phosphorus hydrochlorate etc. is wedding agent, with iron scale, clay, silicon powder is sintering aid, makes the dry type inner lining material through uniform mixing.
In the above-mentioned tundish dry vibratory material because can not form a large amount of eutectics under the not moisture and high temperature, though prolong work-ing life.But the carbon after the wedding agent resol charing of this kind dry type material, hydrogen can obviously be given molten steel recarburization, increase hydrogen, volatilize irritating smell during bakings such as resol and phosphoric acid salt, oxymuriate, vitriol from material, also contaminate environment.Therefore, restricting the further popularization of this dry-type vibration material in soft steel, ultra low-carbon steel are smelted.
Three, summary of the invention
The object of the invention provides and a kind ofly has no irritating odor, can not increase hydrogen, good, the preparation method easy, eco-friendly tundish dry vibratory material of disintegrating of erosion-resisting characteristics to molten steel recarburization.
For finishing above-mentioned task, the technical solution adopted in the present invention is: percentage composition mixes 85~97% magnesia or forsterite with 3~15% Starso by weight, adopt fetal membrane vibratory compaction after stirring, 100~400 ℃ of bakings, the demoulding obtains tundish dry vibratory material.
The weight percentage of the grain composition of magnesia or forsterite is: 2~0.088mm is 80~90%,<0.088mm is 10~20%.
It is wedding agent that the present invention adopts Starso because Starso is a kind of nontoxic, tasteless, non-harmful inorganic salt, so but in bake process cold melt, with the temperature continuous polymerization that raises, make construction body generation intensity.Therefore, the tundish dry vibratory material that is obtained does not have irritating smell, can not increase hydrogen to molten steel recarburization, and erosion-resisting characteristics is good, is easy to disintegrate environmental friendliness yet.
Four, embodiment
[embodiment] 1 one kinds of preparation methods that use tundish dry vibratory material at 28 tons of continuous castings
In weight percentage: containing MgO and be 97% magnesite clinker is 90%, Starso 10%.Wherein the weight percentage of the grain composition of magnesite clinker is: 1~0.088mm is 80~85%,<0.088mm is 15~20%.Above-mentioned raw materials is mixed, adopt fetal membrane vibratory compaction after stirring, 110~300 ℃ of bakings, the demoulding obtains the tundish liner.
It surveys index: MgO is 89.4%, SiO
2Be 6.2%; Volume density: 110 ℃ * 24h 2.18g/cm
3Compressive strength: 110 ℃ * 24h3.6MPa, 1500 ℃ * 3h burns back 7.3MPa; The line velocity of variation: 1500 ℃ * 3h burns back-1.2%.This kind material uses on 28 tons of continuous casting tundish, and the life-span can reach more than 26 stoves.
The characteristics that present embodiment has are: 1. easy construction; But 2. quick baking and having no burst, spalling, storing time is short, and odorlessness; 3. erosion-resisting characteristics is good, long service life; 4. do not have carburetting, increase the hydrogen phenomenon, thereby can not pollute molten steel; 5. the performance of disintegrating is good, can realize turning over automatically bag.
Claims (2)
1, a kind of preparation method of tundish dry vibratory material is characterized in that percentage composition by weight mixes 85~97% magnesia or forsterite with 3~15% Starso, and fetal membrane vibratory compaction is adopted in the back that stirs, in 100~400 ℃ of bakings, the demoulding.
2, the preparation method of tundish dry vibratory material according to claim 1 is characterized in that the weight percentage of the grain composition of described magnesia or forsterite is: 2~0.088mm is 80~90%,<0.088mm is 10~20%.