CN1813654A - 氧化锆全瓷牙科修复材料及其制备方法 - Google Patents
氧化锆全瓷牙科修复材料及其制备方法 Download PDFInfo
- Publication number
- CN1813654A CN1813654A CNA200510134251XA CN200510134251A CN1813654A CN 1813654 A CN1813654 A CN 1813654A CN A200510134251X A CNA200510134251X A CN A200510134251XA CN 200510134251 A CN200510134251 A CN 200510134251A CN 1813654 A CN1813654 A CN 1813654A
- Authority
- CN
- China
- Prior art keywords
- zirconium oxide
- repair material
- full
- dental repair
- porcelain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
序号 | 平均粒径μm | 氧化钇稳定的四方相氧化锆 | 助熔剂 | 粘结剂 | ||||||||||
氧化钇% | 氧化锆% | 硼铝硅系玻璃% | SiO2 | Al2O3 | B2O3 | K2O | Na2O | 羟基磷灰石% | β-硅灰石% | 聚乙烯醇% | 羧甲基纤维素% | 聚丙烯% | ||
1 | 0.3 | 3.00 | 40+51 | 2 | 79 | 3 | 11 | 5 | 2 | 4 | 3 | |||
2 | 0.2 | 4.15 | 40+48 | 4 | 80 | 2 | 12 | 5 | 1 | 4 | 4 | |||
3 | 0.4 | 5.15 | 40+46 | 5 | 5 | 2 | 2 | |||||||
4 | 0.4 | 5.15 | 40+52 | 5 | 79 | 2 | 13 | 5.5 | 0.5 | 3 | ||||
5 | 0.3 | 3.00 | 40+47 | 10 | 1 | 1 | 1 | |||||||
6 | 0.2 | 4.15 | 40+49 | 8 | 1 | 2 | ||||||||
7 | 0.4 | 4.15 | 40+50 | 2 | 80 | 3 | 11 | 5 | 1 | 2 | 2 | 2 | 2 |
序号 | 混合造粒 | 冷等静压成型 | 排塑 | 烧结 | |||||||||
球磨时间min | 真空度Pa | 温度℃ | 颗径μm | 成型压力MPa | 保压时间min | 升温速度℃/h | 升温温度℃ | 保温时间h | 升温速度℃/h | 升温度温度℃ | 保温时间h | 降温速度℃/h | |
1 | 15 | 2 | -40 | 0.5 | 200 | 5 | 40 | 600 | 3 | 50 | 1250 | 3 | 200 |
2 | 20 | 5 | -45 | 0.8 | 160 | 10 | 50 | 700 | 2 | 100 | 1350 | 2 | 175 |
3 | 30 | 10 | -50 | 1 | 100 | 20 | 80 | 800 | 1 | 150 | 1400 | 1 | 150 |
4 | 25 | 8 | -46 | 0.5 | 150 | 10 | 70 | 800 | 1 | 150 | 1400 | 2 | 200 |
5 | 15 | 9 | -48 | 0.7 | 170 | 10 | 80 | 700 | 2 | 100 | 1300 | 1 | 170 |
6 | 20 | 7 | -40 | 0.8 | 120 | 20 | 40 | 750 | 2 | 120 | 1250 | 1.5 | 180 |
7 | 30 | 6 | -50 | 0.6 | 150 | 10 | 50 | 650 | 1 | 80 | 1400 | 1.5 | 160 |
序号 | 抗折强度MPa | 断裂韧性MPa·m0.5 | 弹性模量MPa | 维氏硬度MPa |
1 | 1120 | 13.1 | 134 | 1324 |
2 | 1184 | 14.4 | 145 | 1380 |
3 | 1323 | 13.5 | 137 | 1354 |
4 | 1003 | 11.7 | 130 | 1250 |
5 | 1143 | 12.1 | 131 | 1276 |
6 | 1200 | 15.0 | 150 | 1400 |
7 | 1178 | 13.4 | 141 | 1380 |
8 | 340-360 | 2.7-3.5 | - | - |
9 | 600 | 13 | 140 | 1050~1200 |
Claims (5)