CN1804084A - 稀土镓合金及其制造方法 - Google Patents

稀土镓合金及其制造方法 Download PDF

Info

Publication number
CN1804084A
CN1804084A CN 200510003404 CN200510003404A CN1804084A CN 1804084 A CN1804084 A CN 1804084A CN 200510003404 CN200510003404 CN 200510003404 CN 200510003404 A CN200510003404 A CN 200510003404A CN 1804084 A CN1804084 A CN 1804084A
Authority
CN
China
Prior art keywords
rare earth
gallium
alloy
metal
vacuum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200510003404
Other languages
English (en)
Inventor
龚斌
蔡志双
杨善平
王昌明
章立志
刘善文
邓聚金
陈明华
姚南红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ganzhou Qiandong Industrial (group) Co Ltd
Original Assignee
Ganzhou Qiandong Industrial (group) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ganzhou Qiandong Industrial (group) Co Ltd filed Critical Ganzhou Qiandong Industrial (group) Co Ltd
Priority to CN 200510003404 priority Critical patent/CN1804084A/zh
Publication of CN1804084A publication Critical patent/CN1804084A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种稀土镓合金及其制造方法，稀土镓合金中金属镓的重量百分比为5％－90％，其中，稀土金属为选自金属镝、金属钕、金属镨中的至少一种。按上述配比将稀土金属与金属镓混合后，在氩气介质保护下，经真空加热炉熔炼，即制取出稀土镓合金。按上述方法制得的稀土镓合金，成分均匀无偏析现象，添加适当比例的本合金至钕铁硼材料中，能提高内禀矫顽力1000奥斯特，同时可降低不可逆损失和提高工作温度。

Description

稀土镓合金及其制造方法
所属技术领域
本发明涉及稀土合金技术领域，尤其是稀土镓合金及其制造方法。
背景技术
部分稀土金属和金属镓加入到钕铁硼材料中，可以进一步提高材料性能。由于稀土金属和金属镓的熔点相差很大，如金属镝的熔点高达1412℃，而金属镓的熔点低至29.78℃，其合金工艺十分困难，目前只能将单一稀土金属和金属镓分别加入钕铁硼材料中，增加了生产工序。
发明内容
本发明的目的在于提供一种稀土镓合金及其制造方法。
本发明解决其技术问题所采用的技术方案是：金属镓占合金的重量百分比5％-90％，其中，稀土金属为选自金属镝、金属钕、金属镨中的至少一种。按上述配比将稀土金属与金属镓混合后，在氩气介质保护下，经真空加热炉熔炼，即制取出稀土镓合金。真空加热炉为真空中频炉、真空电弧炉、真空电阻炉中的一种。
本发明的有益效果是：按上述方法制得的稀土镓合金，成分均匀无偏析现象，添加适当比例的本合金至钕铁硼材料中，能提高内禀矫顽力1000奥斯特，同时可降低不可逆损失和提高工作温度。
具体实施方式
实施例1：稀土金属是从金属镝、金属钕、金属镨中至少选取出其中的一种，按稀土金属52％，金属镓48％的重量百分比混合后，加入到25kg-50kg的真空中频感应熔炼炉中，按表1的五个步骤即制得稀土镓合金。
表1：
  步骤   真空度  电流(A)  电压(V)   功率(KW)  时间(min)   活动
  1   ≤10Pa  0  0   0   抽真空
  2   ≤10Pa  120  280   33.6  5   加热
  3   -0.07MPa  110  380   50  20   充氩气升温
  4   -0.07MPa  120  280   33.6  2   保温
  5   -0.07MPa  0  0   0   浇铸
实施例2：稀土金属是从金属镝、金属钕、金属镨中至少选取出其中的一种，按稀土金属53.7％，金属镓46.3％的重量百分比混合后，加入到25kg-50kg的真空中频感应熔炼炉中，按表1的五个步骤即制得稀土镓合金。
实施例3：稀土金属是从金属镝、金属钕、金属镨中至少选取出其中的一种，按稀土金属40％，金属镓60％的重量百分比混合后，加入到25kg-50kg的真空中频感应熔炼炉中，按表1的五个步骤即制得稀土镓合金。

Claims (3)

1、种稀土镓合金，其特征在于：金属镓占合金的重量百分比为5％-90％，其中，稀土金属为选自金属镝、金属钕、金属镨中的至少一种。
2、一种稀土镓合金的制造方法，其特征在于：将稀土金属与金属镓按金属镓占合金重量百分比5％-90％的对应比混合后，在氩气介质保护下，经真空加热炉熔炼，即制取出稀土镓合金。
3、根据权利要求2所述的稀土镓合金的制造方法，其特征为：真空加热炉为真空中频炉、真空电弧炉、真空电阻炉中的一种。
CN 200510003404 2005-12-28 2005-12-28 稀土镓合金及其制造方法 Pending CN1804084A (zh)