The application is the division of Chinese patent application number No. 018186793
Background technology
Numerous as the working method number of making reduced iron or alloy iron, wherein, has inner rotation reductive agent and carbon at rotary kiln, heat reductive Weir formula rotary kiln (ウ エ Le Star キ Le Application) processing method now, perhaps in formula reduction furnace at the bottom of the rotary kiln, carry out formula processing method at the bottom of the rotary kiln of sintering and reducing.Wherein, as the high working method of productivity, the operation shown in TOHKEMY 2000-54034 communique by formula processing method enforcement at the bottom of the rotary kiln.The formula processing method is a kind of below furnace roof that the fixed refractory materials is made and sidewall at the bottom of the rotary kiln, the furnace bottom that the notched discoid refractory materials of central part is made turns round with certain speed in orbit, thereby the formed body that makes for example pelletizing class material powder on the furnace bottom of packing into moves the working method of sintering and reducing stove based on the reduction pattern (below be called rotary kiln) towards heating region, reduced zone, discharge portion, is used for the reduction of oxidized metal.The furnace bottom diameter of rotary kiln is 10~50 meters, and the furnace bottom width is 2~6 meters.
As raw material, use the oxidized metal of dust ore or oxidized metal powder etc. and as the carbon of reductive agent.In the manufacturing of reduced iron, the iron ore of the particulate of use pelletizing supply source (ベ レ ッ ト Off イ one De) etc. etc.Although reductive agent uses carbon, wish to use that the temperature that generates up to reduction reaction is about 1100 ℃, the also higher carbon of nonvolatile carbon component (fixed carbon) ratio.Such carbon source is powdery coke or smokeless carbon preferably.
The powder of the metal oxide-containing of raw material is after reductive agent mixes at the carbon with this oxidized metal desired number of reduction, is a granulated into and is green pellets, and stratiform supply at the bottom of the rotary kiln.The comprehensive spreading of green pellets is on the furnace bottom of rotary kiln.In rotary kiln, under the furnace roof and sidewall that refractory materials is made, the furnace bottom of central notched circle revolution, the each several part in the stove of the pelletizing on the furnace bottom moves, and is heated rapidly.During 5 minutes to 20 minutes, sintering under the high temperature about 1300 ℃ by the carbon in the pelletizing, makes the oxidized metal reduction, generates metal.In rotary kiln,, has pelletizing difficult advantage of bursting apart in stove because green pellets is statically placed on the furnace bottom.As a result, the problem of attaching powder shape raw material on the fire resistive material product of no rotary kiln, and, have the high advantage of yield rate that is called pelletizing.In addition, owing to can use output height, coal measures reductive agent or powder raw material that cost is low, in recent years, the example of enforcement constantly increases.
In addition, to reduce and remove in the processing of impurity at the scales of skin that peel off that will produce from Magnetite (processed) end that blast furnace, converter, electric furnace produce or rolling process or metal fragment also be effective to processing method at the bottom of the rotary kiln, also processing is used as powder treatment, also is a kind of effective working method of metals resources recirculation.When powder reduction, can remove dezincify, lead, basic metal, haloid element and other impurity and also be the advantage of processing method at the bottom of the rotary kiln, this also is the especially effectively reason of working method such as the powder that already produces of relative recirculation system iron.
The operation of processing method roughly is summarized as follows at the bottom of the rotary kiln.At first, be mixed with in will metal oxide as the dust ore of raw material or powder, metal fragment this oxide compound reduction must quantity carbon be reductive agent after, granulation.Have severally as prilling process, for example,, make water accounts 8~15 spheric green pellets weight %, 5~20mm with the tablets press of pan-type pelletizer etc.This green pellets stratiform at the bottom of the rotary kiln is supplied with, with plane spreading on furnace bottom.Spreading is heated in stove rapidly at the green pellets on the furnace bottom, through 5~30 minutes, and sintering under the high temperature about 1300 ℃.At this moment,, make the oxidized metal reduction, generate metal by being mixed in the carbon in the green pellets as reductive agent.Fixed carbon amount in the reductive agent is the amount by obtaining with the oxygen amount of reductive metal compound roughly.Degree of metalization after the reduction is different according to the reductive metal, for iron, nickel, manganese, more than 90%, even difficult reductive chromium is also more than 40%.
Aforesaid with the oxidized metal in the formula reduction furnace at the bottom of the rotary kiln particularly the powder that produces of refining of metal or processing industry, prick bits or metal fragment etc. and reduce, to obtain the reducing metal, be a kind of effective working method.When using the secondary resultant of metal industry such as powder as raw material, be a kind of effective means of resource recirculation.
But,, particularly, in the secondary resultant of above-mentioned metal industry, be mixed with the impurity of organism in machinery oil, the water, chlorine agent, resin-oatmeal etc. even also exist impurity such as chlorine in the dust ore that uses as one of raw material.For example, in the sedimentary metal fragment, sneaked into the machinery oil of 1~5 weight % in the bundle bits accumulator tank that in the rolling process of steel, produces.In addition, sneak into the chlorine of 0.1~0.3 weight % in the blast furnace powder.
In addition, be used for rotary kiln at the bottom of formula reduction furnace reductive electric furnace powder packets contain chlorine or oil, but also comprise other materials of dioxin.These impurity are in the stove internal combustion or the evaporation of rotary kiln, and the material of discharging outside stove is more.At this moment, organism can burn, and emits carbonic acid gas or water vapour.But when incomplete combustion, the benzene etc. that also exists cigarette ash, carbon, not combustion is included in the situation in the combustion gases.In addition, chlorine dose has the degree that forms separately to salt such as the gas of chlorine or hydrogen chloride gas or formation sodium-chlor, zinc chloride, any one all be height ratio with combustion gases one in the same way stove discharge outward.These organism or chlorine react in combustion gases, although a small amount of, also generate Dioxins.Particularly, carbon monoxide concentration in incomplete combustion and the combustion gases taking place when high, reacts or from the building-up reactions of gas phase, increased the growing amount of dioxin by chlorine and benzene class in stove.
, in equipment formation and operational method in the past, do not have sufficient knowledge, may not necessarily suppress the operation that dioxin produces.In operation in the past, main purpose is the heat supply that only carries out to reduction reaction, and, in exhaust-gas disposal, the main body of Kao Lving was to prevent on the path that powder handles attached to combustion gases or on the method for waste heat recovery, practical situation are fully not reflect the method for subduing dioxin on equipment design originally.In investigation after this, find, in rotary kiln, when the temperature of combustion in the stove is high, though compare with other burning working method, the growing amount of dioxin is few, and is little to the burden of environment, but be not have dioxin in combustion gases, according to occasion, its concentration is at 1~5ng-TEQ/Nm
3
That is to say in the reduction furnace operation headed by the reduction furnace of formula at the bottom of the rotary kiln that carries out with existing method, also do not have to find to suppress the operational method that dioxin produces effectively.
As above-mentioned, at rotary kiln or Weir now in the reduction furnace of formula rotary kiln etc.,, produce carbonic acid gas and contain the pyritous combustion gas of a large amount of water vapour by carbon and the heavy oil that acts as a fuel or the burning of natural-gas as reductive agent.This combustion gas is that raw material per ton gives off 2000~3000Nm
3Include the powder that produces in the stove in this emission gases, by exhaust air passageways, after in discharged-gas processing device, cooling off with methods such as waterings, control of dust, and to airborne release.Processing method is along with the reduction reaction of oxidized metal at the bottom of the above-mentioned rotary kiln, and therefore the volatilizable impurity such as dezincify, lead, chlorine that remove are the more working methods of a kind of powder generation.
Operation meeting at the bottom of rotary kiln so in the metallic reducing stove of formula reduction furnace or rotary kiln etc. produces a large amount of combustion gas that contains the volume powder, the sensible heat that this emission gases is possessed is about 30% of input all energy, in order to become the high operation of thermo-efficiency, important task is the recovery to the used heat of combustion gas.
But, when the waste heat recovery of carrying out the pyritous combustion gas, exist powder securely attached to the heating surface of waste heat boiler or heat exchanger, and the problem of corroding these surperficial metals.As a result, for example, shown in TOHKEMY 2000-169906 communique,, also adopt the temperature of suitably controlling boiler or heat exchanger, with the method that prevents that powder from adhering to even in this method in the past in the treatment process of the emission gases in the rotary kiln.This method is a kind of means of effective processing emission gases, but because of the composition of powder, and powder can be attached to the inner face of heat exchanger, and in the time in 2 weeks to 1 month, existing can sealing emission gases path problems.Particularly, powder is when hanging down melting point, the strong adhesion of powder, and problem is more serious.
Powder by generations such as rotary kilns not only contains the raw materials such as ferric oxide that disperse, more than contain anionic species such as basic metal, zinc, lead, other volatile metals and chlorine.Be in powder part about 600~1100 ℃ in the temperature of emission gases exit passageway, the composition of these powder exists because of steam, and it begins into liquid and separate out along with the decline of temperature of exhaust gas.This liquid be the emulsion that powder composition that solid disperses forms high viscosity.This emulsion is because can be attached on the emission gases path, and blocking problem easily takes place the part that narrows down in the path.That is to say, when heat exchanger being set, narrow down, easily stop up at this partial discharge gas path in order to reclaim used heat.The corrodibility of the liquid of an alkali metal salt is strong, also has the problem of metallic corrosion at this emulsion attachment portion.
Although it is a kind of technology that prevents that effectively powder from adhering to that above-mentioned spy opens the disclosed method of 2000-169906 communique, particularly, under an alkali metal salt and zn cpds situation how, can not prevent attachment phenomenon fully.In conventional art so, can not give sufficient attention to the powder composition in the emission gases, can not solve the recovery of heat heat exchanger blocking problem of emission gases fully.
Summary of the invention
Therefore, in order to solve the above problems, when seeking the generation of a kind of inhibition Dioxins from the combustion gases that the metallic reducing fire grate of rotary kiln or rotary kiln etc. goes out, reclaim the technology of the sensible heat that this emission gases possesses effectively.
The operational method of formula reduction furnace at the bottom of the rotary kiln of the present invention, it is characterized in that, at least carry out the pre-heated heat exchanger of preheating is carried out in heat exchange to air discharged-gas processing device having, in the combustion gas refrigerative operational method with formula reduction furnace at the bottom of the rotary kiln, the total mole number B of total mole number A, sodium and the potassium of zinc that is contained in the powder of combustion gas and lead and the total mole number C of chlorine and fluorine satisfy the relation of (C-B)/A<0.36.
The operational method of formula reduction furnace is characterized in that at the bottom of the described rotary kiln, and in the powder of described combustion gas, the ratio that contains of the compound of sodium that is contained or potassium and chlorine or fluorine is lower than 35 weight %.
The operational method of formula reduction furnace at the bottom of the described rotary kiln, it is characterized in that, temperature of exhaust gas in the emission gases exit passageway ingress of described reduction furnace is higher than 800 ℃, is lower than 550 ℃ in the preheating of air of described discharged-gas processing device with the temperature of the emission gases at heat exchanger entrance place.
The operational method of formula reduction furnace is characterized in that at the bottom of the described rotary kiln, and the temperature of described emission gases was cooled to be lower than 550 ℃ from being higher than 800 ℃ in 5 seconds.
The operational method of formula reduction furnace at the bottom of the rotary kiln of the present invention, in formula reduction furnace at the bottom of the rotary kiln of the discharged-gas processing device that has band preheating of air formula heat exchanger at least, with the raw material sintering and reducing after the powder shaping of metal oxide-containing and carbon, carry out heat exchange and come the cooling combustion emission gases, it is characterized in that, zinc in the described raw material and plumbous total mole number A ', the total mole number B ' of sodium and potassium, and the relation of setting up (0.8C '-0.7B ')/A '<0.36 between the total mole number C ' of chlorine and fluorine, and, temperature of exhaust gas at the emission gases exit passageway place of described reduction furnace is higher than 800 ℃, is higher than 550 ℃ in the temperature of the emission gases at described preheating of air formula heat exchanger entrance place.
The invention solves above-mentioned problem, its main points are as follows.
(1) operational method of formula reduction furnace at the bottom of a kind of rotary kiln, it is characterized in that, make the combustion gases that produce in the stove of formula reduction furnace at the bottom of the rotary kiln, in the emission gases exit passageway of this reduction furnace and among near at least one side the emission gases exit passageway, in greater than 0.9 second time, temperature is reached be higher than 800 ℃, and become Reynolds number for greater than 30000 turbulent state, afterwards, has waste heat boiler, any was cooled to be lower than 300 ℃ from being higher than 800 ℃ with these combustion gases separately or in the discharged-gas processing device of combination mutually sprinkler system and air heat exchanger in 6 seconds, behind the control of dust, discharge.
(2) operational method of formula reduction furnace at the bottom of a kind of rotary kiln, it is characterized in that, make the combustion gases that produce in the stove of formula reduction furnace at the bottom of the rotary kiln, in this reduction furnace emission gases exit passageway and among near at least one side the emission gases exit passageway, the carbon monoxide concentration volumetric ratio is for being lower than 200ppm, in greater than 0.9 second time, temperature is reached be higher than 800 ℃, and become Reynolds number for greater than 30000 turbulent state, afterwards, has waste heat boiler, any was cooled to be lower than 300 ℃ from being higher than 800 ℃ with these combustion gases separately or in the discharged-gas processing device of combination mutually sprinkler system and air heat exchanger in 6 seconds.
(3) operational method of formula reduction furnace at the bottom of a kind of rotary kiln, it is characterized in that, make the combustion gases that produce in the stove of formula reduction furnace at the bottom of the rotary kiln, in this reduction furnace emission gases exit passageway and among near at least one side the emission gases exit passageway, in 0.9 second time, temperature is reached be higher than 800 ℃, the carbon monoxide concentration volumetric ratio is for being lower than 200ppm, and become Reynolds number (レ イ ノ Le ズ) for greater than 30000 turbulent state, afterwards, cool off these combustion gases fast.
(4) operational method of formula reduction furnace at the bottom of a kind of rotary kiln, it is characterized in that, make the combustion gases that produce in the stove of formula reduction furnace at the bottom of the rotary kiln, in this reduction furnace emission gases exit passageway and among near at least one side the emission gases exit passageway, in greater than 0.6 second time, temperature is reached be higher than 800 ℃, the carbon monoxide concentration volumetric ratio is for being lower than 60ppm, and become Reynolds number for greater than 50000 turbulent state, afterwards, has waste heat boiler, any was cooled to be lower than 300 ℃ from being higher than 800 ℃ with these combustion gases separately or in the discharged-gas processing device of combination mutually sprinkler system and air heat exchanger in 6 seconds.
According to the operational method of formula reduction furnace at the bottom of the arbitrary described rotary kiln in (1)~(4), it is characterized in that (5) combustion gases that produce in the described stove are higher than 1200 ℃ in the temperature of furnace interior, and the mole ratio of the relative carbonic acid gas of carbon monoxide is greater than 0.1.
According to the operational method of formula reduction furnace at the bottom of the arbitrary described rotary kiln in (1)~(5), it is characterized in that (6) combustion gases that produce in the described stove were cooled to be lower than 300 ℃ from being higher than 800 ℃ in 6 seconds.
(7) according to the operational method of formula reduction furnace at the bottom of (6) described rotary kiln, it is characterized in that, the cooling of the combustion gases that produce in the described stove is that any carries out separately or in the discharged-gas processing device of combination mutually having waste heat boiler, sprinkler system and air heat exchanger.
(8) according to the operational method of formula reduction furnace at the bottom of the arbitrary described rotary kiln in (1)~(7), it is characterized in that the total mole number B of total mole number A, sodium and the potassium of zinc that contains in the powder of the combustion gases that produce in the described stove and lead and the total mole number C of chlorine and fluorine satisfy the relation of (C-B)/A<0.36.
According to the operational method of formula reduction furnace at the bottom of the arbitrary described rotary kiln in (1)~(8), it is characterized in that (9) in the powder of the combustion gases that produce in the described stove, the ratio that contains of the compound of sodium that is contained or potassium and chlorine or fluorine is lower than 35 weight %.
According to the operational method of formula reduction furnace at the bottom of (8) or (9) described rotary kiln, it is characterized in that (10) temperature of the gas that produces in the described stove was cooled to be lower than 550 ℃ from being higher than 800 ℃ in 5 seconds.
(11) operational method of formula reduction furnace at the bottom of a kind of rotary kiln, it is characterized in that, in the discharged-gas processing device that has the pre-heated heat exchanger that can carry out preheating and heat exchange at least to air, with the combustion gas cooling of formula reduction furnace at the bottom of the rotary kiln, the total mole number B of total mole number A, sodium and the potassium of zinc that is contained in the powder of combustion gas and lead and the total mole number C of chlorine and fluorine satisfy the relation of (C-B)/A<0.36.
According to the operational method of formula reduction furnace at the bottom of (11) described rotary kiln, it is characterized in that (12) in the powder of described combustion gas, the ratio that contains of the compound of sodium that is contained or potassium and chlorine or fluorine is lower than 35 weight %.
(13) according to the operational method of formula reduction furnace at the bottom of (11) or (12) described rotary kiln, it is characterized in that, temperature of exhaust gas in the emission gases exit passageway ingress of described reduction furnace is higher than 800 ℃, is lower than 550 ℃ in the preheating of air of described discharged-gas processing device with the temperature of the emission gases at heat exchanger entrance place.
According to the operational method of formula reduction furnace at the bottom of the arbitrary described rotary kiln in (11)~(13), it is characterized in that (14) temperature of described emission gases was cooled to be lower than 550 ℃ from being higher than 800 ℃ in 5 seconds.
(15) operational method of formula reduction furnace at the bottom of a kind of rotary kiln, in formula reduction furnace at the bottom of the rotary kiln of the discharged-gas processing device that has band preheating of air formula heat exchanger at least, with the raw material sintering and reducing after the powder shaping of metal oxide-containing and carbon, the cooling combustion emission gases, it is characterized in that, zinc in the described raw material and plumbous total mole number A ', the total mole number B ' of sodium and potassium, and the relation of setting up (0.8C '-0.7B ')/A '<0.36 between the total mole number C ' of chlorine and fluorine, and, temperature of exhaust gas in the emission gases exit passageway ingress of described reduction furnace is higher than 800 ℃, is higher than 550 ℃ in the temperature of the emission gases at described preheating of air formula heat exchanger entrance place.
(16) according to the operational method of formula reduction furnace at the bottom of the arbitrary described rotary kiln in (1)~(15), it is characterized in that, the combustion gases that produce in the described refrigerative stove are further by the sack cleaner in the discharged-gas processing device, control of dust under 170~250 ℃ temperature.
(17) formula reduction furnace equipment at the bottom of a kind of rotary kiln, it is characterized in that, be provided with: reduction furnace with oxidized metal of rotary type furnace bottom, and discharged-gas processing device, this discharged-gas processing device is made of refrigerating unit and particle collector, this refrigerating unit is by waste heat boiler, sprinkler system and preheating of air combine separately or mutually with heat exchanger, simultaneously, between this reduction furnace and this discharged-gas processing device, be connected by passage, this passage length converted as if the time of passing through of the combustion gases that produce in the stove with this reduction furnace, then be length, and internal diameter and internal gas flow velocity is long-pending greater than 7.2m greater than 0.9 second
2/ second.
(18) formula reduction furnace equipment at the bottom of a kind of rotary kiln, it is characterized in that, be provided with: reduction furnace with oxidized metal of rotary type furnace bottom, and discharged-gas processing device, this discharged-gas processing device is made of refrigerating unit and particle collector, this refrigerating unit is by waste heat boiler, sprinkler system and preheating of air combine separately or mutually with heat exchanger, simultaneously, between this reduction furnace and this discharged-gas processing device, be connected by passage, this passage length converted as if the time of passing through of the combustion gases that produce in the stove with this reduction furnace, then be length, and internal diameter and internal gas flow velocity is long-pending greater than 12m greater than 0.6 second
2/ second.
(19) according to formula reduction furnace equipment at the bottom of (17) or (18) described rotary kiln, it is characterized in that, in the refrigerating unit in the described discharged-gas processing device, as with combustion gases from being higher than 800 ℃ of internal volumes that are cooled to be lower than 300 ℃ of parts 6 times less than the combustion gas flow of per second.
(20) formula reduction furnace equipment at the bottom of a kind of rotary kiln, it is characterized in that, be provided with: reduction furnace with oxidized metal of rotary type furnace bottom, and discharged-gas processing device, this discharged-gas processing device is made of refrigerating unit and particle collector, this refrigerating unit is by waste heat boiler, sprinkler system and preheating of air combine separately or mutually with heat exchanger, simultaneously, also have the vibration of strike and give device, the mechanism of at least one in gas blowing device and the sootblower, in order to removing with the powder on the heat exchanger attached to the described preheating of air of this discharged-gas processing device.
The embodiment of invention
According to reduction furnace explanation the present invention as formula at the bottom of the rotary kiln shown in Figure 1 of reduction furnace one form.Working method shown in Figure 1 mainly is made of formula reduction furnace 1, waste heat boiler 3, sprinkler system 4, heat exchanger (air preheater) 5 and precipitron 7 at the bottom of the rotary kiln.The view that the rotary kiln structure is shown is Fig. 2 and Fig. 3.Fig. 2 is the sectional drawing that rotary kiln is shown.Fig. 3 illustrates the stretch-out view of the round furnace bottom of the central gap in the stove at turning direction.
The structure of rotary kiln 1 below furnace roof 10 that the fixed refractory materials is made and furnace wall 11, exists on wheel 13 and moves and rotating furnace bottom 12 shown in the sectional drawing of Fig. 2.On furnace wall 11, be provided with burner 14, from burner 14, blow fuel, produce the pyritous combustion gases by flame 15.Sprinkle the green pellets 16 that constitutes by oxidied metal powder and carbon dust on furnace bottom 12 upper berths.As rotary kiln 1 in Fig. 3 of the stretch-out view of circumferential direction, the job content to the heating of green pellets 16 and reduction etc. has been described.
The green pellets of raw material is to mix by the powder with the carbonaceous reducing agent of dust ore or converter gas powder, the secondary resultant of pricking system iron such as bits and powdery coke etc.The green pellets of this raw material passes through raw material supplying portion 17 spreadings on furnace bottom 12.Be generally 1~3 layer thickness.Along with furnace bottom 12 moves and turns round, green pellets 16 is introduced in the heating region 18.The furnace roof portion of heating region 18 links to each other with emission gases exit passageway 2.At this, the concentration of carbon monoxide and hydrogen is higher in the green pellets 16 of heating, and enters pyritous reduced zone 19.At this, green pellets 16 interior oxidation metals and carbon reaction are with the reducing metal.Afterwards, reductive green pellets 16 is discharged in stove by the discharge screw machine 21 of reducting pellet discharge portion 20.Combustion gases promptly flow to more cryogenic heating region 18 from pyritous reduced zone 19 towards the direction opposite with pelletizing, therefore, discharge outside stove from emission gases exit passageway 2.In addition, although not necessarily,, the occasion of using dividing plate 22 is arranged also in order to carry out effectively cutting apart of zone.
Combustion gases in the stove are fuel and the air that are configured in from reduced zone 19 to heating region the burner 14 on 18 the furnace wall side, and the carbon monoxide that produces from green pellets is the gas at center, are the gas of mixed firing.These combustion gases flow to heating region 18 from reduced zone 19.Afterwards, discharge outside the stove of rotary kiln 1 from the emission gases exit passageway 2 of the furnace roof portion of heating region 18.
At first, in reduced zone 19,, sufficient reducing environment must be arranged for the reduction of green pellets.Oxidized metal as the reduction object in processing method at the bottom of the rotary kiln is iron, nickel, chromium, lead, zinc, manganese etc.According to the reductibility of these metals, the temperature of reduced zone 19 is more than 1200 ℃ the time, and the molar ratio of the relative carbonic acid gas of carbon monoxide must be more than 0.1.Under this condition, but the reduction of acceleration green pellets 16.
As under the temperature more than 1200 ℃, the organism and the chlorine that are mixed in the green pellets 16 also are decomposed into carbon monoxide, carbonic acid gas, water vapour, hydrogen, hydrogenchloride, can suppress the growing amount of dioxin better.
Then, the combustion gases in the stove flow in the heating region 18.At this, do not carry out the reduction of green pellets 16, up to being heated to till the pelletizing temperature arrives about 1100 ℃.Burning gas temperature at this is 1100~1200 ℃ in the part near reduced zone 19, and is 800~1100 ℃ in the part near emission gases exit passageway 2.In addition, emission gases exit passageway 2 and temperature waste heat boiler 3 connection portions are more than 800 ℃.Owing to do not reduce in heating region 18, reduction degree also can be lower in the environment of combustion gases.
Therefore, in part remaining oxygen is arranged at least, can make carbon monoxide concentration also become lower state near emission gases exit passageway 2.
In the present invention, the part that is connected with waste heat boiler 3 near the part of emission gases exit passageway 2 and emission gases exit passageway 2 of the heating region 18 in the stove of reduction furnace is called near the emission gases exit passageway.
As near the exhaust air passageways 2 and the composition of the combustion gases in exhaust air passageways 2, emission gases exit passageway 2 with waste heat boiler 3 connection portions, by making oxygen concn more than 0.5 volume %, carbon monoxide concentration can be remained on volumetric ratio below 200ppm.Although also comprise in the stove of rotary kiln 1,, wish in emission gases exit passageway 2 from the viewpoint of the component of control combustion gases with the part of the condition considerable part of this description.In addition, in Fig. 1 example, emission gases exit passageway 2 is to link to each other with the waste heat boiler 3 that can carry out recovery of heat, but so long as cooling gas fast can link to each other with the gas quench system or the heat reclamation device of other modes.And from the flue management and the safety problem of combustion gases and the viewpoint consideration of subduing dioxin all the more, preferably carbon monoxide concentration is below the 600ppm under volumetric ratio.In addition, except these conditions, consider that from the viewpoint of gas good mixing the state as emission gases flows when becoming the turbulent state of well dispersing, can reduce dioxin.The method for generation of turbulent flow is with aftermentioned.
After this, combustion gases, are cooled to below 300 ℃ with heat exchanger 5 by waste heat boiler 3, sprinkler system 4 and preheating of air.Cooling off the needed time was preferably in below 6 seconds.The refrigerative combustion gases are through control of dust prepass 6, by precipitron 7 dedustings, by vacuum fan 8 exhausting, from chimney 9 to airborne release.Precipitron 7 uses sack cleaner.That is, among near at least one side of combustion gases in the emission gases exit passageway and the emission gases exit passageway with rotary kiln, after perfect combustion more than 800 ℃, cool off fast and control of dust, can suppress the generation of Dioxins, simultaneously, can prevent adhering to of powder.
The inventor is according to the job behavior of rotary kiln, and the operating condition of the generation of the dioxin that suppresses combustion gases is investigated.For this reason, carry out several experiments, under aforesaid condition, draw the conclusion that to carry out the processing of combustion gases.Below, explain this experiment content.
The inventor distinguishes, in order to suppress the generation of dioxin, in the processing of the combustion gases of heating region below 18 of rotary kiln, controlled temperature and gaseous constituent are important.How unburnt state can take place in dioxin under 300~600 ℃ envrionment temperature.That is to say, the organic molecule of the several complexity in the unburnt gas and chlorine reaction, the temperature that forms dioxin is 300~600 ℃.Therefore, in this temperature province, in order there not to be complicated organic molecule such as benzene, in reduced zone 19, the combustion gases that will contain many carbon monoxide are in the part from heating region 18 to emission gases exit passageway 2 promptly in exhaust air passageways 2 and near the exhaust air passageways, perfect combustion under the high temperature more than 800 ℃.
As will at high temperature implementing perfect combustion, oxygen can mix well with combustion gases under remaining state.For this reason, the inventor finds that the turbulent state that combustion gases are fully dispersed is a kind of gas blended effective means, therefore, works out use and is generated as the combustion gases condition of the turbulent state of purpose to prevent dioxin.Fig. 4 illustrates this experimental result.Fig. 4 is under the turbulent state for illustrating under proper condition, burning gas temperature more than 800 ℃, carbon monoxide concentration is the hold-time under the following state of 200ppm and the relation of the Dioxins concentration in the emission gases under volumetric ratio.As shown in Figure 4, with burning gas temperature be more than 800 ℃, carbon monoxide concentration under volumetric ratio for the corresponding time of dioxin restraining condition below the 200ppm as being more than 0.9 second, Dioxins concentration can be at 0.1ng-TEQ/Nm
3Below, better.That is to say that turbulent flow is when fully dispersing, suitable combustion gases state is as continuing 0.9 second, and the organic molecule that then is judged to be aforesaid complexity does not exist, and satisfies the condition that dioxin generates that suppresses.
In order to make mixing of combustion gases produce suitable turbulent flow, can make as the Reynolds number of the index of estimating hydromechanical flow state bigger.Usually, surpass for 2300 the moment at Reynolds number, flowing becomes turbulent flow., in the present invention, because the turbulent flow of fully dispersing of the state that becomes the combustion gases good mixing must be arranged, and then bigger Reynolds number must be arranged.In the inventor's experiment, Reynolds number then is judged to be the uniform state that forms the combustion gases that conform with this purpose as in the flow state more than 30000.Therefore, condition of the present invention is, the temperature of combustion gases is more than 800 ℃, and carbon monoxide concentration is more than 30000 for Reynolds number in the part under the following state of 200ppm under volumetric ratio.
In order further to reduce dioxin, require lower carbon monoxide concentration and the Reynolds number of Geng Gao.The result of inventor's investigation, the dioxin concentration in the emission gases is at 0.06ng-TEQ/Nm
3Under the following better state, wish that carbon monoxide concentration is below the 60ppm under volumetric ratio, and Reynolds number is more than 50000.Under this state, owing to become very good mixing state, even the time of this state continuance is 0.6 second effect of also can fully volatilizing.As keep this condition, can obtain dioxin concentration in the emission gases at 0.02~0.06ng-TEQ/Nm
3Very good achievement.
In addition, Reynolds number is a non-dimensional number, for by gas viscosity long-pending divided by gas density, gas flow rate and representative length.Reynolds number is the index of expression flow state, surpasses at 2300 o'clock, and Reynolds number is high more, and mobile turbulent flow phenomenon is just obvious more.The representative length of the calculating of Reynolds number is in the present invention used the width of furnace bottom 12 or the diameter of emission gases exit passageway 2.Carry out in the condition of the present invention, burning gas temperature is 800~1200 ℃, and the density of combustion gases is 0.25~0.4kg/m
3About, and viscosity is 4 * 10
-5~6 * 10
-5Kg/ms.Therefore, amassing as the flow velocity of the width of the diameter of emission gases exit passageway 2 or furnace bottom 12 and combustion gases at 7.2m
2More than/second, then Reynolds number is more than 30000.And, as amassing of the flow velocity of the width of the diameter of emission gases exit passageway 2 or furnace bottom 12 and combustion gases at 12m
2More than/second, then Reynolds number is more than 50000.In order to obtain above-mentioned needed Reynolds number, it is a kind of effective means that the diameter of consideration furnace bottom width, exit passageway comes the method for pilot-gas flow velocity.
After realizing such state, much less can not increase carbon monoxide concentration once more.
Then, it is important combustion gases being cooled fast to 300 ℃ from 800 ℃.Purpose is to have shortened the time of the temperature province of the dioxin resynthesis under 300~600 ℃ of temperature.For this reason, the inventor has resolved and has cooled off the required time.In experimental result shown in Figure 5, cooling time, dioxin concentration will be at 0.1ng-TEQ/Nm when surpassing 6 seconds
3More than.That is to say, from 800 ℃ of times that are cooled to 300 ℃ be very important below 6 seconds.Therefore, discharged-gas processing device from 800 ℃ of internal volumes that are cooled to 300 ℃ of parts become per second combustion gas flow be necessary below 6 times.
So long as can keep above-mentioned speed of cooling, the method for cooling of combustion gases can be arbitrarily.In Fig. 1 example, used waste heat boiler, sprinkler system and preheating of air combination with heat exchanger (heat exchanger of combustion gases and air).This method is a kind of temperature controlled optimal method of carrying out waste heat recovery to greatest extent and correctly carrying out combustion gases.Yet, only make up sprinkler system and air preheater wanting also can to omit waste heat boiler under the situations such as simplified apparatus.At this moment, the waste heat recovery amount is roughly 1/2nd of the described equipment of Fig. 1.In addition, in the time need not carrying out waste heat recovery fully, only just combustion gases can be cooled to below 300 ℃ with sprinkler system.
Like this, cool off effectively, prevented well on the refrigerating unit and even recovery of heat (heat exchange) device of powder attached to discharged-gas processing device, as following describe in detail, zinc that contains in the powder of the combustion gases that produce in the stove and plumbous total mole number A, the total mole number B of sodium and potassium, and the relation of satisfied (the C-B)/A of the total mole number C of chlorine and fluorine<0.36, just can prevent to be attached to the heat exchange on refrigerating unit or recovery of heat (exchange) device well, cooling efficiency reduces or is attached to the narrow of exhaust air passageways due to the passage because of powder, hinder the mobile phenomenon.In addition, the basic metal (sodium or potassium) that contains in the powder of generation gas in the stove is lower than 35 weight % with the ratio that contains of the compound of haloid element (chlorine or fluorine), then can suppress well adhering to of powder.In addition, preferably, the temperature of generation gas from being cooled to more than 800 ℃ below 550 ℃, just can suppress powder and adhere on discharged-gas processing device in 5 seconds in the stove, can effectively suppress the reduction of cooling efficiency.
As above-mentioned, produce in order to suppress Dioxins, in discharged-gas processing device, cool off emission gases apace, but carry out the aspect of heat exchange, the thermo-efficiency of recovery of heat from improve operation and consider it also is extremely important this moment.
But, just as discussed previously, owing to because of being included in a large amount of powder in this pyritous emission gases attached to the variety of problems that generates on heat reclamation device in the discharged-gas processing device of heat storage boiler, preheating of air formula heat exchanger etc. or the refrigerating unit, can not become a kind of efficient device, be not only heat recovery efficiency, the cooling efficiency self that is used to suppress the emission gases of Dioxins also can be affected.For this reason, the contriver further studies these aspects.
In combustion gas, disperse composition, basic metal and haloid element zinc or metal such as lead such, after evaporable material and the reduction at high temperature, evaporation of raw materials such as unreduced ferric oxide enters as the powder composition.In these compositions, the basic metal halogen as sodium-chlor or Potassium monofluoride and zinc chloride or lead chloride, the melting point of himself remain on 700~900 ℃., the inventor finds that when the ratio of basic metal halogen and zinc chloride or lead chloride was high in the powder in the emission gases, these became branch to merge, and melting point is reduced to 550~600 ℃.And find, the powder under this condition mostly can attached to the emission gases path promptly in stove below the exhaust air passageways, through discharged-gas processing device on the emission gases path that atmosphere is dispersed.
The result who resolves attached to the powder mass on the emission gases path is shown, muriate and muriate are for a long time, these compositions in the powder can be adhered under the temperature more than 450~600 ℃, and particularly when the ratio of zinc and the plumbous relative zinc of halogenide and plumbous oxide compound is high, this tack grow.In addition, powder is attached to the survey showed that in heat exchange etc. during to 550 ℃ of common operative temperatures, zinc in the powder and plumbous halogenide such as relative zinc and plumbous oxide compound with halid summation with the mole conversion below 18%, then tackiness a little less than, can peel off easily.But, also be under this condition, the basic metal halogen is 35% o'clock that the part by weight of the compound of basic metal (sodium or potassium) and haloid element (chlorine or fluorine) surpasses all weight of powder, showing has also increased tackiness slightly.For this reason, proportionally to be lower than 35 weight % containing of the compound of basic metal that contains in the powder and haloid element.
Thus, in the present invention, the ratio of each element in the control powder is so that the zinc in the powder is below 22% under molar ratio with plumbous relative zinc of halogenide and plumbous oxide compound.This control is with the molar ratio of the zinc in the powder, lead, sodium, potassium, chlorine and fluorine, (mole number of the mole number+fluorine of chlorine)-(mole number of the mole number+potassium of sodium), just will with below 18% of sum total of the responseless haloid element mole number of basic metal mole number that is zinc and plumbous mole number.In addition, because zinc and lead are the divalent positively charged ion, to the ion valence mumber revisal of the anionic haloid element of 1 valency.Use ((mole number of the mole number+fluorine of chlorine)-(mole number of the mole number+potassium of sodium))/(mole number of the mole number+lead of zinc) (index 1) as the index when the operation.In the operation of reality, become the condition of index 1<0.36.That is, zinc that comprises in the powder and plumbous total mole number are that the total mole number of A, sodium and potassium is the total mole number of B, chlorine and fluorine when being C, (C-B)/and A<0.36.
In order correctly to manage the composition of powder, need carry out the composition management of raw material.In processing method at the bottom of the rotary kiln, zinc and plumbous from raw material to the emission gases rate of transform more than 90%, the alkali-metal rate of transform is about 70%, the rate of transform of haloid element is about 80%.Consider these rates of transform, determine zinc, lead, the basic metal in the raw material, the ratio of haloid element.When it is represented with formula, become (0.8 (mole number of the mole number+fluorine of chlorine)-0.7 (mole number of the mole number+potassium of sodium))/(0.9~1.0 (mole number of the mole number+lead of zinc)), be shown (0.8 (mole number of the mole number+fluorine of chlorine)-0.7 (mole number of the mole number+potassium of sodium))/(mole number of the mole number+lead of zinc) (index 2) with the simple type sublist, it is carried out operation as the level of control that raw material cooperates.In the operation of reality, condition is an index 2<0.36.That is, zinc that comprises in the raw material and plumbous total mole number are that the total mole number of A ', sodium and potassium is the total mole number of B ', chlorine and fluorine when being C ', become (0.8C '-0.7B ')/A '<0.36.
The emission gases that is included in the powder of adjusting under this condition imports the emission gases treatment facility from emission gases exit passageway 2.In the temperature of exhaust gas of this part more than 800 ℃.Below 800 ℃ the time, exist muriate or fluorochemical and after entering emission gases exit passageway 2, separate out at once, near the inlet of emission gases exit passageway 2, blocking problem takes place, and, consider that from the viewpoint that aforesaid inhibition Dioxins generates temperature will be more than 800 ℃.
After this, emission gases imports waste heat boiler 3 and carries out recovery of heat, below the emission gases quick cooling to 550 ℃.As in the temperature of exhaust gas of waste heat boiler 3 outlet more than 550 ℃ the time, further cool off with watering water cooler 4, make temperature of exhaust gas below 550 ℃.To watering water cooler 4, carry out the cooling of emission gases from waste heat boiler 3 fast.It is important becoming the time of melting body with shortening muriate and fluorochemical.Inventor's discovery, as adopt powder shown in the present, by being in 5 seconds below 550 ℃, at quick cooling end serious powder attachment phenomenon can not take place.Therefore, all also be effective even employing watering formula air-turbocooler etc. carry out cooling process.
Emission gases is further carried out heat exchange and recovery of heat with air in heat exchanger 5, be cooled to below 300 ℃ preferably about 200 ℃.In addition, consider, be preferably in 6 seconds to the cooling below 300 ℃ from 800 ℃ and carry out from the viewpoint of the resynthesis of aforesaid inhibition Dioxins.The temperature of heat exchanger 5 inlet parts also is an important job factor.That is to say that in the powder constituent of the scope of the invention, when the temperature of exhaust gas of heat exchanger was too high, sodium-chlor that does not finally solidify or zinc chloride etc. adopted liquid state, attached to the heat exchanger metallic surface, produced the problem of obstruction or metallic corrosion.In order to prevent making dirty of the heating surface of powder due to adhering to, reclaim used heat effectively, and, adhere in order to prevent powder, be preferably in and in the heat exchanger 5 powder be set and remove device.Have multiplely although powder is removed device, the general employing blows the grey formula of blowing of high pressure gas or steam or the beating type powder is removed device.The pattern of heat exchanger also is the important important document that prevents that powder from adhering to.Adhering to strong heat exchanger for powder adopts blowing air in a kind of pipe, the outer logical emission gases of pipe and will manage the powder of outside and remove the heat exchanger of pattern by blowing ash, and parallel plate is set mostly, also can adopt air and emission gases alternately to flow, scrape the heat exchanger of attaching powder pattern with scraper plate.
At this moment, the air by the heat exchange heating uses with hot blast as the combustion air of rotary kiln 1 or the prior drying of pelletizing.
So heat exchange and refrigerative combustion gas are removed powder through ensuing precipitron prepass 6 in precipitron 7.
Precipitron 7 can be the precipitron that can not synthesize the bag-type dusting type of dioxin in machine once more.Have a plurality of cloth that the fibrous septum is tiny as sack cleaner and make the pouch filter cloth, the gas that contains powder is by this filter cloth, to remove the device of powder.The operating temperature of sack cleaner can be more than 150 ℃.Reason is, below 150 ℃, becomes acid dew point, and equipment corrodes easily.Because the heat-resisting problem of filter cloth is wished in the temperature below 250 ℃.In processing method at the bottom of the rotary kiln, when the reduction-oxidation metal, oxide compound such as zinc, lead, basic metal or muriate are discharged from combustion gases.These materials become the superfine micropowder, with control of dust fully such as cyclone.And the reaction of dioxin resynthesis simultaneously, can take place because the control of dust ability is not enough in the electrostatic precipitation machine in machine, therefore, be not suitable for this working method, and the precipitron of sack cleaner formula is best.
But, too high during with watering cooling combusting gas sensible heat part how because of the water vapor concentration in the combustion gases, wetting phenomena can take place in sack cleaner, therefore wish use wet type precipitron.Particularly, when the moisture in the combustion gases surpassed 30 weight %, fly-ash separator latch up phenomenon or corrosion can take place in sack cleaner wetting serious thus.In order to make the moisture in the combustion gases be no more than 30 weight %, the moisture addition in the time of need making watering is every 1Nm
3Combustion gases are below 400kg.When carrying out the watering of above amount, use the wet type precipitron of washer in the mound, Fen etc.
At last, the combustion gas of removing behind the powder is dispersed to atmosphere from chimney 9 by the power of vacuum fan 8.
As above-mentioned, in the method for the invention, the operation of the reduction furnace by processing method at the bottom of the rotary kiln, even with the secondary resultant of metal industry as raw material, carry out when the reduction of metal, also can make the generation of dioxin be suppressed to minimum, when can implement to be difficult to the operation of contaminate environment, can suppress powder attached to the phenomenon on the discharged-gas processing device, can carry out heat exchange and cooling effectively, can realize the operation that thermo-efficiency is high.
Embodiment
(embodiment 1~embodiment 3 and comparative example 1)
In the reduction furnace of processing method at the bottom of the rotary kiln shown in Figure 1, the powdery coke is mixed in powdered iron ore, electric furnace powder and the little powdered expanded skin, making the green pellets of 10~20mm, and in reduction furnace to its reduction.The center of the furnace bottom of rotary kiln directly is 17m, and the furnace bottom width is 4m, has the ability of the reduced iron of per hour making 15 tons.The length of the reduced zone 19 of this rotary kiln is 35m, and the length of heating region 18 is 18m.Adopt this equipment to carry out the result of operation by shown in the table 1.And in embodiment 1,2 and comparative example, the generating capacity of combustion gases is 27000~30000Nm
3/ hour, and in embodiment 3, generating capacity is 17000Nm
3/ hour.
In embodiment 1, the reduced zone temperature of rotary kiln 1 is 1270 ℃, and the molar ratio of the carbon monoxide of carbonic acid gas is 0.55 relatively.Green pellets is reduction in 8 minutes in reduced zone 19.These combustion gases flow in heating region 18, at this, and slowly cooling, in the 7m of emission gases exit passageway 2 span, the temperature of combustion gases is 1030 ℃, carbon monoxide concentration is 88ppm under volumetric ratio, and oxygen concn is 1.1 volume %.In the inside of emission gases exit passageway 2, burning gas temperature is 980 ℃, and the carbon monoxide concentration volumetric ratio is 69ppm, and oxygen concn is 1.3 volume %.
The combustion gases flow velocity be 5.5m/ second in the stove in 5m part of emission gases exit passageway 2, and, in emission gases exit passageway 2 inside that 6m grows, be 6.1m/ second.The width of the furnace bottom 12 in stove internal heating zone is 4m, and the long-pending of furnace bottom width and combustion gases flow velocity is 22m
2/ second, Reynolds number is 100000.In addition, the diameter of emission gases exit passageway 2 is 2.4m, and the long-pending of channel diameter and combustion gases flow velocity is 14.6m
2/ second, Reynolds number is 70000.Therefore, the time under the condition of temperature that satisfies combustion gases of the present invention and composition is 0.9 second in the inside in stove internal heating zone 18, and is 1.0 seconds in the inside of emission gases exit passageway 2, adds up to 1.9 seconds.
In addition, combustion gases between 5, were cooled to 210 ℃ from 980 ℃ from waste heat boiler 3 to air preheater in 5.7 seconds.Afterwards, combustion gas is dispersed to atmosphere by sack cleaner formula precipitron 7 controls of dust.Dioxin concentration in the combustion gas is 0.05ng-TEQ/Nm at this moment
3, become the little state of environmental pollution.
In embodiment 2, be the better contents processing of condition.The temperature of the combustion gases of emission gases exit passageway 2 is 1105 ℃, and carbon monoxide concentration also is 45ppm under volumetric ratio.The Reynolds number of emission gases exit passageway 2 is 72000.This burning gas temperature is 0.8 second in the time more than 800 ℃, is in the condition of the present invention.In addition, from 800 ℃ of times that are cooled to 300 ℃ be 4.7 seconds.As a result, the dioxin in the combustion gases is 0.02ng-TEQ/Nm
3, very good.
In embodiment 3, be the operation result under the slightly little condition of Reynolds number.In this operation, be the reduction rate that reduces pelletizing, the little condition of flow that makes combustion gases.In stove, the carbon monoxide concentration of combustion gases is more than the 300ppm under volumetric ratio, and at the inlet of emission gases exit passageway 2, the combustion gases that become 130ppm are handled.In this operation, the Reynolds number of emission gases exit passageway 2 is 42000.This burning gas temperature is 910 ℃, is 1.4 seconds in the time more than 800 ℃, is in the condition of the present invention.In addition, from 800 ℃ of times that are cooled to 300 ℃ be 4.9 seconds.As a result, the dioxin in the combustion gases becomes high slightly 0.101ng-TEQ/Nm
3, but be in the good range.In addition, in the operation of these embodiment, the reduction ratio of pelletizing also is about 85%, better.
In addition, will as with the green pellets of the same raw material of embodiment reductive but do not observe in the comparative example of operating condition of the present invention in above-mentioned rotary kiln 1, the concentration of dioxin in combustion gases is higher.In comparative example, although the temperature of reduced zone is identical with embodiment 1 with the combustion gases composition, the temperature of heating region is different with the combustion gases composition.As condition, just Reynolds number is 60000, and is higher., at heating region, burning gas temperature is minimum to be 760 ℃, and, hypoxgia in environment gas, oxygen concn is roughly under the 0 volume %, and carbon monoxide concentration is 800ppm under volumetric ratio.Even carbon monoxide concentration also is 500ppm in the inside of emission gases exit passageway 2.
As a result, the concentration of the dioxin in the combustion gases in the chimney 9 is 0.52ng-TEQ/Nm
3, higher.That is to say, in comparative example,, can not reduce the generation of dioxin owing to can not suitably control the temperature and the composition of combustion gases.
(embodiment 4~embodiment 6 and comparative example 2)
The emission gases treatment facility of the reduction furnace that Fig. 1 carries out at the bottom of for the embodiment 4~embodiment 6 of operational method of the present invention and comparative example 2 employed rotary kilns.This reduction furnace per hour reduces 18 tons the green pellets as raw material, and 1100 ℃ emission gases per hour produces 45000Nm
3Table 2 illustrates the operating condition and the result thereof of embodiment and comparative example.
Embodiment 4 is for to be source of iron and to use the powdery coke to carry out the example of operation as reductive agent with iron ore and converter powder.The impurity of this raw material is less, and the index 2 of material composition is 0.18, is in the scope of the present invention.As a result, the index 1 of powder composition also is 0.17, and the ratio of basic metal halogen also is 20 weight %, and is lower.For the emission gases treatment condition, discharging
Table 1
| | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 |
Reduced zone | Temperature | 1270℃ | 1300℃ | 1280℃ | 1270℃ |
CO/CO
2Than (mol ratio)
| 0.55 | 0.41 | 0.45 | 0.55 |
Near the emission gases exit passageway portion | Temperature | Be higher than 980 ℃ | 1150℃ | 910℃ | 780℃ |
CO concentration (volume %) | 69~88ppm | 45ppm | 135ppm | 500ppm |
Reynolds number | Greater than 70000 | 72000 | 42000 | 60000 |
Hold-time | 1.9 second | 0.8 second | 1.5 second | - |
Cooling time afterwards (800 → 300 ℃) | Be lower than 5.7 seconds | Be lower than 4.7 seconds | 4.9 second | - |
The pelletizing reduction ratio | 85% | 84% | 87% | 83% |
Dioxin concentration: ng-TEQ/Nm in the emission gases
3 | 0.05 | 0.02 | 0.101 | 0.52 |
The temperature of exhaust gas of the inlet of
pneumatic outlet passage 2 is 970 ℃, and is higher, and
heat exchanger 5 temperature ins are 480 ℃, and are lower, thereby powder really can be attached in the emission gases treatment system.
Among the embodiment 6, the composition of raw material or powder within the scope of the invention, although be method of the present invention, the temperature of exhaust gas of emission gases treatment system is not the result who carries out under good condition.In addition, raw material uses the raw material identical with embodiment 5.Index 1 is identical with embodiment 5 with index 2.But the temperature of exhaust gas of emission gases exit passageway 2 inlets is 760 ℃, and is lower, and the temperature of exhaust gas that enters the mouth at heat exchanger 5 is 570 ℃, and is higher.As a result, in the emission gases treatment system problem that slight powder adheres to can take place.In the maintenance department of operation after 3 months, confirming has dirt settling at the inlet of emission gases exit passageway 2.And, at the inlet of heat exchanger 5, can stop up at leisure, must cleaning after 2 months.
Comparative example 2 illustrates the raw material adjustment that conventional art carries out and the operation result of temperature of exhaust gas and powder management.In comparative example 1, because many raw materials such as use chlorine, the index 2 of material composition is 0.48.As a result, the index 1 of powder is 0.51.And the ratio of basic metal halogen also is 30 weight %, and is higher.As a result,, dirt settling is arranged, after 1 month, clean at the inlet of emission gases exit passageway 2 although the temperature condition of emission gases is good.In addition, it is very fast that the inlet of heat exchanger 5 stops up, will interruption operation after 2 weeks.So, except condition of the present invention, can not be for a long time, stably work continuously.
In addition, the application of the invention is carried out for a long time, operation stably sustainably, in addition, owing to can carry out heat exchange well, can carry out the reduction of the high oxidized metal of energy efficiency, can reduce the expense that metal is made significantly.
Utilizability on the industry
According to the present invention, in the operation of the sintering and reducing stove of formula reduction furnace at the bottom of the rotary kiln etc. that the dioxin that produces in the combustion gas is compared with the past, can be suppressed at 1/2~1/10 significantly.And, can suppress the obstruction in the emission gases path of the discharged-gas processing device of powder due to adhering to, can retrieve used heat effectively from the pyritous emission gases, can improve the thermo-efficiency of sintering and reducing stove.Thus, the by product that is produced by metal industries such as powder, metal fragment, oxide skins can be reduced effectively, simultaneously, can under high productivity, carry out this operation, can reduce the manufacturing expense of reducing metal.
Table 2