CN1736859A - Super active carbon preparation method - Google Patents
Super active carbon preparation method Download PDFInfo
- Publication number
- CN1736859A CN1736859A CN200510010965.XA CN200510010965A CN1736859A CN 1736859 A CN1736859 A CN 1736859A CN 200510010965 A CN200510010965 A CN 200510010965A CN 1736859 A CN1736859 A CN 1736859A
- Authority
- CN
- China
- Prior art keywords
- temperature
- active carbon
- shell
- microwave
- gac
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a preparation method for super active carbon. Wherein, carbonizing and breaking up the raw material of coco shell or walnut shell to predetermined particle size and mix evenly with solid potassium hydroxide; activating the mixture in microwave oven with nitrogen protection during the process to obtain activation material; clearing the material with muriatic acid and then distilled water for many times to neutrality and obtain the said product. The product with this method has strong adsorption property, high specific surface area and high adsorption value to iodine and methylene blue. The method is simple and convenient to control.
Description
One, technical field
The super-activated carbon preparation method belongs to chemical production technical field.
Two, background technology
Gac is a kind of the have highly developed pore texture and carbon material adsorbing material of good absorption property, has been widely used in a plurality of fields such as environmental protection, chemical industry, food-processing, metallurgy, medicine are refining, military chemistry protection.Along with the development of environment and energy science and technology, Application of Brand Active Carbon is constantly widened, as is used for the field such as electrode, Sweet natural gas and hydrogen storage, support of the catalyst, gas delivery of electric double layer capacitance.But the loading capacity of common gac can not satisfy above needs, therefore is badly in need of the novel absorbent charcoal material that research and development have high-adsorption-capacity or super absorption property.
The raw material of preparation super-activated carbon is generally coal, refinery coke, shell etc.Because to contain trial of strength high for the impurity ash content in the coal, cause the ash of active carbon content height, the specific surface area that make low; Be though that the gac quality product that makes of raw material is better with the refinery coke, its production cost height, valuable product.
At present, the preparation method of super-activated carbon mainly is divided into two classes: i.e. physical activation method and chemical activation method.Physical activation method is at first removed the carbonaceous material charing volatilizable composition wherein, generates the using pyrolysis thing of rich carbon, feeds the activated gas activation then, by the new hole of perforate, reaming and creation, forms flourishing microvoid structure.General its carbonization temperature is 400～600 ℃, 800～1000 ℃ of activation temperatures.Chemical activation method generally is that the adding chemical reagent carries out a step charing to starting material and activation obtains super-activated carbon, needs by changing medium temperature realization charing and reactivation process.No matter be physical activation method or chemical activation method, its technology all exists soak time long, cost height, problems such as complex process.
The disclosed active carbon with high specific surface area preparation method of F, M, Ograd and A, N, Wenerbeng by research centre, U.S. A Moke oil company, be with potassium hydroxide and refinery coke by 2～4: 1 mixes, be warmed up to 850 ℃ and react and obtain gac after 400～500 ℃ of following preroasting, the gac specific surface area of gained is up to 3000m
2/ g.It by the disclosed patent No. of Shanxi Inst. of Coal Chemistry, Chinese Academy of Sciences a kind of high-specific surface area activity of 00315662.4, be that potassium hydroxide is mixed by 5: 1 with refinery coke, kept 1 hour at 400 ℃, continue to be heated to 800 ℃ and keep obtaining in 1.5～2 hours active carbon with high specific surface area.By the disclosed patent No. of Shanxi Inst. of Coal Chemistry, Chinese Academy of Sciences 97123209.1 active carbon with high specific surface area preparation method, be to be raw material with the coal, be with potassium hydroxide and coal by 1～5: 1 mixes, kept 1 hour at 400 ℃, continue to be heated to 800 ℃ and keep obtaining in 1 hour active carbon with high specific surface area.
The shortcoming of above method is to be raw material with coal or refinery coke, and the wasting of resources is big; And its whole process is finished in a reaction vessel, needs in the production to finish charing and reactivation process by changing medium temperature, and the difficult control of processing condition is unfavorable for the industrialization continuous production; Simultaneously, its heating is to adopt traditional method, and the reaction process time is long, the manufacturing cost height.
By the disclosed patent No. of Institutes Of Technology Of Taiyuan 03111949.2 active carbon with high specific surface area preparation method, be that activation at high temperature obtains corn cob is flooded oven dry in the solution of potassium hydroxide and Potassium peroxide after, its shortcoming is that dipping back raw material needs oven dry, the technical process complexity, the production process time is long, and steeping process causes the potassium hydroxide utilization ratio low.
The applicant is in 931146937.2 the patent in the patent No., the method of a kind of " microwave irradiation make powder gac " is disclosed, this method is to flood more than 12 hours wood chip in phosphoric acid or liquor zinci chloridi, obtain gac with microwave radiation after 5～15 minutes again, 600～900 ℃ of microwave radiation temperature.Its shortcoming is that the process time is long, and phosphoric acid and zinc chloride utilization ratio are low, and the charcoal absorption performance that makes is not high, and methylene blue adsorption value has only 195mg/g, belongs to common gac.
The applicant is the method that discloses a kind of " microwave radiation tobacco rod solid waste is made gac " in 02113270.4 the patent in the patent No., this method is to flood in 50% liquor zinci chloridi after the tobacco rod solid waste is crushed to 1～15mm, the mass ratio of raw material and solution is 1: 3.5～5, dipping time is 8～10 hours, dipping back raw material radioactivation in microwave obtains gac, and the gac methylene blue adsorption value is 255mg/g.Its technology also exists the process time long, the shortcoming of charcoal absorption poor performance.
Compare with above method, advantage of the present invention is to be the feedstock production super-activated carbon with agricultural solid waste such as coconut husk and nut-shells, has overcome the high shortcoming of raw materials cost; Replace known liquid impregnation method with the solid phase mixing method, it is long to have overcome preparation process time, the shortcoming that the activator utilization ratio is low; Among the known active carbon with high specific surface area preparation method one step carbonization-activation is divided into charing carries out, do not need to change temperature of reaction, processing condition to be easy to control and suitable industrialization continuous production in the reactivation process with two steps of activation.Adopt microwave heating to replace the traditional heating method, utilize microwave heating speed fast, can make the process for preparing active carbon time short to the characteristics of material inside heating, condition be easy to control.The activated carbon-iodine adsorptive value that makes reaches 2378mg/g, and methylene blue adsorption value reaches 750mg/g, and specific surface area reaches 2863m
2/ g is considerably beyond common gac.
Three, summary of the invention
The object of the present invention is to provide a kind of super-activated carbon preparation method.With charing after coconut husk and the nut-shell fragmentation and be crushed to certain particle size; mix back activation in microwave oven with the KOH solid and obtain gac; lead to nitrogen protection on bed of material surface in the reactivation process; the gac chlorohydric acid pickling; carry out repeatedly rinsing with distilled water again, dry to neutral back and obtain active carbon finished products.The activated carbon-iodine adsorptive value that obtains reaches 2378mg/g, and methylene blue adsorption value reaches 750mg/g, and specific surface area reaches 2863m
2/ g.
The present invention finishes according to the following steps,
1, raw material coconut husk or nut-shell being crushed to 2～5mm, and placing microwave oven, is 700W at microwave power, and charing 10min obtains coconut husk or nut-shell carbonized material under the condition that carbonization temperature is 600 ℃;
2, carbonized material is crushed to 40～300 μ m, with hydrogen KOH solid be to mix in 1: 3～1: 7 by carbonized material/potassium hydroxide mass ratio;
3, compound places microwave oven, and in the logical nitrogen protection in bed of material surface, radiation heating 10～30min carries out priming reaction under the microwave power of 200～2000W, and temperature of reaction is 650～750 ℃, gets activated material;
4, activation back material is 3% salt acid elution 1～5 time with concentration expressed in percentage by weight, uses the distilled water rinsing to pH value to 5.0～7.0 then;
5, material places baking oven drying under 100 ℃～120 ℃ temperature to obtain active carbon finished products in 2～5 hours after the rinsing.
Its activating mechanism is that KOH and decolorizing carbon generation selective reaction generate K
2CO
3Mode consumed carbon, meanwhile in charcoal, produced a large amount of micropores, formed flourishing pore texture, its chemical equation is:
The present invention has the following advantages: (1) utilizes agriculture and forestry organic waste material coconut husk and nut-shell to make super-activated carbon, the carbonized material physical strength height that coconut husk or nut-shell obtain after charing, the internal structure densification, ash content is few, have high bulk density, in addition, contain sylvite in its ash content, when activation, can play the effect of catalyzer, help activation; (2) coconut husk and nut-shell belong to agriculture and forestry organic waste material, also are a kind of renewable resourcess simultaneously, are the feedstock production super-activated carbon with coconut husk and nut-shell, have both helped waste ' s reclamation and environment protection, also can reduce the gac manufacturing cost; (3) replace known solution dipping method with the solid phase mixing activation method, shortened the used time of process for preparing active carbon greatly, can improve the KOH utilization ratio simultaneously, reduce production costs; (4) the step carbonization-activation of one among the known active carbon with high specific surface area preparation method is divided into charing and carries out, do not need to change temperature of reaction, processing condition to be easy to control and suitable industrialization continuous production in the reactivation process with two steps of activation; (5) utilize microwave can be directly to the heating of material inside, homogeneous heating, advantage such as speed is fast makes the process for preparing active carbon time spent few, energy expenditure is low, gac yield height; (6) since microwave can be directly to the heating of material inside, can make that gac is inner to produce a large amount of active sites, be that heating source prepares gac and can effectively promote gac pore-creating with it, reduce activation temperature, improve quality of activated carbon; (7) feed nitrogen protection on bed of material surface in the reactivation process, can prevent the influence of the existence of block, both can improve charcoal absorption performance and specific surface area, also can improve the gac yield reactivation process.
Four, description of drawings: Fig. 1 is technical process of the present invention.
Five, specific embodiment
Embodiment 1
Coconut husk and nut-shell are crushed to 2～3mm, at microwave power 700W, charing 10min obtains the coconut husk carbonized material under the carbonization temperature 600C, with the carbonized material that makes be crushed to behind the 71 μ m be 1: 3 thorough mixing with the KOH solid by carbonized material/potassium hydroxide mass ratio after, place microwave oven, at microwave power 700W, activation temperature activates 25min down for 700 ℃, lead to nitrogen on bed of material surface in the reactivation process, with weight percent concentration be behind 3% the chlorohydric acid pickling 3 times with the distilled water rinsing to pH value to 6.0, under 120 ℃ temperature, obtained the finished product gac in dry 2 hours.
Its test conditions and detected result such as table one:
Table one: microwave heating potassium hydroxide activation method prepares super-activated carbon test conditions and index
| Test conditions | Detected result | ||||||
| Microwave power (W) | Activation temperature (℃) | Carbon alkali mass ratio | Soak time (min) | Iodine sorption value (mg/g) | Methylene blue adsorption value (mg/g) | Specific surface area (m 2/g) | The rate of recovery (%) |
| 700 | 700 | 1∶3 | 25 | 2378 | 750 | 2863 | 24.3 |
Embodiment 2
Coconut husk is crushed to 3-5mm, at microwave power 700W, charing 10min obtains the coconut husk carbonized material under the carbonization temperature 600C, the carbonized material that makes is crushed to 120 μ m and the KOH solid is that 1: 6 thorough mixing is placed in the microwave oven by carbonized material/potassium hydroxide mass ratio, at microwave power 1400W, activation temperature activates 15min down for 750 ℃, lead to nitrogen on bed of material surface in the reactivation process, weight percent concentration be behind 3% the chlorohydric acid pickling 5 times with the distilled water rinsing to pH value to 5.5, under 120 ℃ temperature, obtained the finished product gac in dry 3 hours.
Its test conditions and detected result such as table two:
Table two: microwave heating potassium hydroxide activation method prepares super-activated carbon test conditions and index
| Test conditions | Detected result | ||||||
| Microwave power (W) | Activation temperature (℃) | Carbon alkali mass ratio | Soak time (min) | Iodine sorption value (mg/g) | Methylene blue adsorption value (mg/g) | Specific surface area (m 2/g) | The rate of recovery (%) |
| 1400 | 750 | 1∶6 | 15 | 2265 | 720 | 2645 | 27.5 |
Execute example 3
Nut-shell is crushed to 2～3mm, at microwave power 700W, 600 ℃ of following charing 10min of carbonization temperature obtain the nut-shell carbonized material, the carbonized material of system is crushed to 50 μ m and the KOH solid is that 1: 4 thorough mixing is placed in the microwave oven by charcoal/alkali mass ratio, at microwave power 490W, activation temperature activates 30min down for 650 ℃ and obtains gac, lead to nitrogen on bed of material surface in the reactivation process, the gac weight percent concentration be behind 3% the chlorohydric acid pickling 4 times with the distilled water rinsing to pH value to 6.5, under 120 ℃ temperature, obtained the finished product gac in dry 5 hours.
Its test conditions and detected result such as table three:
Table three: microwave heating potassium hydroxide activation method prepares super-activated carbon test conditions and index
| Test conditions | Detected result | ||||||
| Microwave power (W) | Activation temperature (℃) | Carbon alkali mass ratio | Soak time (min) | Iodine sorption value (mg/g) | Methylene blue adsorption value (mg/g) | Specific surface area (m 2/g) | The rate of recovery (%) |
| 490 | 650 | 1∶4 | 40 | 2186 | 660 | 2427 | 30.6 |
From embodiment as can be seen, it is strong that the super-activated carbon that makes with microwave heating potassium hydroxide activation method has an absorption property, the characteristics that specific surface area is high.Its iodine sorption value, methylene blue adsorption value and specific surface area are considerably beyond common gac, and its yield is up to 30.6%.
Claims (1)
1. the preparation method of a super-activated carbon, it is characterized in that: the present invention finishes according to the following steps,
1), raw material coconut husk or nut-shell are crushed to 2～5mm, and placing microwave oven, is 700W at microwave power, and charing 10min obtains coconut husk or nut-shell carbonized material under the condition that carbonization temperature is 600 ℃;
2), carbonized material is crushed to 40～300 μ m, with hydrogen KOH solid be to mix in 1: 3～1: 7 by carbonized material/potassium hydroxide mass ratio;
3), compound places microwave oven, and in the logical nitrogen protection in bed of material surface, radiation heating 10～30min carries out priming reaction under the microwave power of 200～2000W, temperature of reaction is 650～750 ℃, activated material;
4), the activated material concentration expressed in percentage by weight is 3% salt acid elution 1～5 time, uses the distilled water rinsing to pH value to 5.0～7.0 then;
5), material places baking oven drying under 100 ℃～120 ℃ temperature to obtain active carbon finished products in 2～5 hours after the rinsing.