CN1702254A - 铁矿渣混凝土空心隔墙条板 - Google Patents

铁矿渣混凝土空心隔墙条板 Download PDF

Info

Publication number
CN1702254A
CN1702254A CN 200510010863 CN200510010863A CN1702254A CN 1702254 A CN1702254 A CN 1702254A CN 200510010863 CN200510010863 CN 200510010863 CN 200510010863 A CN200510010863 A CN 200510010863A CN 1702254 A CN1702254 A CN 1702254A
Authority
CN
China
Prior art keywords
slag
iron
concrete hollow
hollow partition
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200510010863
Other languages
English (en)
Inventor
张小强
Original Assignee
张小强
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 张小强 filed Critical 张小强
Priority to CN 200510010863 priority Critical patent/CN1702254A/zh
Publication of CN1702254A publication Critical patent/CN1702254A/zh
Pending legal-status Critical Current

Abstract

铁矿渣混凝土空心隔墙条板,其特征是将铁矿渣作为主要原料制作工业灰渣混凝土空心隔墙条板。它由下列成分组成,水泥、铁矿渣、粉煤灰、膨胀珍珠岩与陶粒、聚炳烯纤维;它的具体配方为;(重量百分比),水泥15~40%、铁矿渣20~60%、粉煤灰9.9~20%、膨胀珍珠岩与陶粒15~20%、聚炳烯纤维0.02~0.04%。用本发明制作的轻质墙板强度高,比重符合轻质墙板要求,密实度高、收缩值低、有效的防止了轻质墙板的板缝开裂现象。

Description

铁矿渣混凝土空心隔墙条板
技术领域
本发明属建筑材料轻质墙板材料组分技术领域。
背景技术
现有的工业灰渣制成的混凝土空心隔墙条板,主要以煤渣、粉煤灰、陶粒、膨胀珍珠岩、水泥为原料,制成空心隔墙条板,这种轻质墙板主要用于框架结构房屋中的非承重墙,替代传统的红砖,是墙体改革的一大突破,用空心隔墙条板代替非承重墙能极大地节约土地资源,具有广泛的应用前景。但现有的工业灰渣制成的混凝土空心隔墙条板主要原料采用的是煤渣、粉煤灰,因其特有的性质,如细粉太多,收缩值大使得隔墙条板结构显得疏松,强度不高,板缝易开裂,严重影响隔墙板的质量,也使得这一产品难以广泛推广应用。
发明内容
:本发明的目的正是为了克服上述现有技术存在的不足之处而提供一种颗粒比粉煤灰粗,强度比粉煤灰高,在工业灰渣混凝土中起粗骨料的作用,达到提高强度、增加密实度、降低收缩值、减少板缝开裂现象的铁矿渣混凝土空心隔墙条板。
本发明的目的是通过如下技术方案来实现的。
将铁矿渣作为主要原料制作工业灰渣混凝土空心隔墙条板。
本发明按下列成份组成,水泥、铁矿渣、粉煤灰、膨胀珍珠岩与陶粒、聚炳烯纤维。
具体配方为:水泥15~40%、铁矿渣20~60%、粉煤灰9.9~20%、膨胀珍珠岩与陶粒15~20%、聚炳烯纤维0.02~0.04%。
铁矿渣是钢铁厂冶炼钢铁产生的废渣,由于铁矿渣的比重较大,一直难以进入轻质墙板材料领域,大量的铁矿渣除少数用作水泥掺合料外,基本都废弃掉了。本发明将工业灰渣用作混凝土空心隔墙条板的主要原料,充分利用其颗粒粗形成的混凝土结构密实,制成的隔墙条板强度高,收缩值低,加之整个配方从比重上进行了控制,在综合性能上有所考虑,是一种具有替代性作用的工业灰渣混凝土空心隔墙条板材料。
具体实施方式
实施例1,取水泥20kg铁矿渣55kg、粉煤灰9.9710kg。膨胀珍珠岩与陶粒的混合物(比例任意)15kg,聚炳烯纤维0.03kg,配以水混合后,采用专用的长线台座式螺旋挤压机制作成需要长度的混凝土空心隔墙板。
实施例2,取水泥15kg铁矿渣60kg粉煤灰9.96kg。膨胀珍珠岩与陶粒的混合物(比例任意)15kg,聚炳烯纤维0.04kg,配以水混合后,采用专用的长线台座式螺旋挤压机制作成需要长度的混凝土空心隔墙板。
实施例3,取水泥40kg铁矿渣20kg粉煤灰20kg。膨胀珍珠岩与陶粒的混合物(比例任意)19.98kg,聚炳烯纤维0.02kg,配以水混合后,采用专用的长线台座式螺旋挤压机制作成需要长度的混凝土空心隔墙板。

Claims (3)

1.铁矿渣混凝土空心隔墙条板,其特征是将铁矿渣作为主要原料制作工业灰渣混凝土空心隔墙条板。
2.根据权利要求1所述的铁矿渣混凝土空心隔墙条板它由下列成份组成,水泥、铁矿渣、粉煤灰、膨胀珍珠岩与陶粒、聚炳烯纤维。
3.根据权利要求1所述的铁矿渣混凝土空心隔墙条板,其特征是具体配方为(重量百分比):水泥15~40%、铁矿渣20~60%、粉煤灰9.9~20%、膨胀珍珠岩与陶粒15~20%、聚炳烯纤维0.02~0.04%。
CN 200510010863 2005-06-21 2005-06-21 铁矿渣混凝土空心隔墙条板 Pending CN1702254A (zh)