CN1647858A - 利用低温等离子体还原负载金属催化剂的方法 - Google Patents

利用低温等离子体还原负载金属催化剂的方法 Download PDF

Info

Publication number
CN1647858A
CN1647858A CN 200410093820 CN200410093820A CN1647858A CN 1647858 A CN1647858 A CN 1647858A CN 200410093820 CN200410093820 CN 200410093820 CN 200410093820 A CN200410093820 A CN 200410093820A CN 1647858 A CN1647858 A CN 1647858A
Authority
CN
China
Prior art keywords
metal
plasma
catalyst
method
no3
Prior art date
Application number
CN 200410093820
Other languages
English (en)
Inventor
刘昌俊
邹吉军
张月萍
Original Assignee
天津大学
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 天津大学 filed Critical 天津大学
Priority to CN 200410093820 priority Critical patent/CN1647858A/zh
Publication of CN1647858A publication Critical patent/CN1647858A/zh

Abstract

本发明涉及一种利用低温等离子体还原负载金属催化剂的方法。具体步骤如为1)金属盐的活性组分,溶于去离子水或蒸馏水中,金属组分的质量含量为0.01%~20%,将溶液注入催化剂载体中,室温下静置8~24小时,然后在40~ 110℃干燥2~10小时;2)将步骤1)中的催化剂放在等离子体装置的两个电极之间,在放电管中的压力为50Pa~0.1MPa,通入惰性气体或空气或氧气作为等离子体放电气体,在电极上加100~20000V的直流或交流电压,处理5~200分钟。低温等离子体含有大量的电子,具有极强的还原性能,可以很容易地将金属离子还原为单质金属;其气体的温度接近室温,避免了高温下的不良热效应。过程简单,所需还原时间短;不使用化学还原剂,对环境友好。

Description

利用低温等离子体还原负载金属催化剂的方法

技术领域

本发明属于一种制备负载型催化剂的方法,特别涉及一种利用低温等离子体还原负载金属催化剂的方法。

背景技术

负载型金属催化剂是化学工业中常用的催化剂,通过负载,一般采用浸渍,可以使昂贵的金属活性组分均匀的分散到载体表面,从而节约金属的用量,提高催化剂的活性。多数情况下,具有催化作用的是单质金属,因此,担载到催化剂载体上的金属盐在使用前需要还原为金属单质。通常使用的是利用氢气在高温下还原,但是该方法往往引起金属颗粒的团聚,结果使金属的分散不均匀,分散度降低,活性低下。另外,高温可能对载体本身的性能产生负面影响,比如,破坏载体自身结构,产生强的金属-载体作用,这些结果都可能对催化剂性能产生负面影响。为了获得高分散的还原态金属催化剂,以下方法被提出来:(1)液相还原。首先将金属盐溶液与催化剂体混合,然后加入化学还原剂,如NaBH4、肼、甲醛和柠檬酸等,使金属还原并吸附在载体上,最后分离干燥。该方法使金属的分散性得到一定改善,缺点在于,使用的还原剂对环境危害巨大,尤其是效果最好的Kaffer法使用的肼是剧毒物质。(2)光还原沉积法。该方法与液相还原类似,在醇或醛溶液中加入载体和欲担载的金属盐,采用紫外光照射使金属还原到载体上。获得的催化剂分散性较高,但是,该方法需要长时间的强光照射,而且金属很难完全负载到载体上,目前还不适于大规模的应用。(3)溶胶(sol-gel)法。在惰性气体氛围下将金属制成溶胶,然后吸附到载体上,或者将金属溶胶加入到催化剂载体的前驱体中。溶胶法得到的催化剂金属分散性好,但制备过程繁琐,条件苛刻。(4)气相沉积法。利用高温或等离子体溅射将金属原子沉积到载体上,一般需要采用挥发性金属盐为原料,并在接近真空条件下进行,还不适于工业应用。(5)其他方法如微生物还原法,有机溶胶法,离子交换-还原法等。

一种好的催化剂还原方法不仅要能保持金属的高分散性,而且不能增加对环境的污染,还应该过程简单、易于操作。

发明内容

本发明公开一种利用低温等离子体还原负载型催化剂的方法。目的在于,在不使用氢气、肼等化学还原剂的情况下,利用低温等离子体的电子效应在常温下将负载型金属催化剂还原,并保持金属的高分散性。

本发明的具体步骤如下:1)金属盐的活性组分,溶于去离子水或蒸馏水中,金属组分的质量含量为0.01%~20%,将溶液注入催化剂载体中,室温下静置8~24小时,然后在40~110℃干燥2~10小时;2)将步骤1)中的催化剂放在等离子体装置的两个电极之间,在放电管中的压力为50Pa~0.1MPa,通入惰性气体或空气或氧气作为等离子体放电气体,在电极上加100~20000V的直流或交流电压,处理5~200分钟。

当后续的反应体系要求焙烧催化剂时,本发明还包括步骤3)焙烧:即将步骤2)等离子体还原的催化剂在惰性气体氛围下焙烧1~10小时,温度为150~600℃。

本发明的低温等离子体是辉光放电、介质阻挡放电或电晕放电。

对于难溶的金属盐如PdCl2等,可在溶液中加入盐酸助其溶解,然后将溶液蒸发接近干燥除去盐酸,再加入蒸馏水或去离子水。

本发明的等离子体放电气体是优选Ar、N2、O2、He、以及空气,放电气压优选为50Pa~0.1Mpa。

对于多组分金属催化剂,可在步骤1中一次浸渍多种金属,或按步骤1)、2)、3)重复进行。

本发明的金属盐的活性组分为现有的使用的金属盐的活性组分都可以,其中包括H2PtCl6、PdCl2、Ni(NO3)2、Au(NO3)2、Cu(NO3)2、Ag(NO3)2、Fe(NO3)3、Co(NO3)2、Zn(NO3)2、K2CrO3或钼酸铵的一种或几种。

本发明的负载金属的载体为现有的使用的负载金属的载体都可以;其中包括分子筛、钙钛矿、活性炭、氧化硅、Al2O3、La2O3、TiO2或ZrO2。

本发明所公布的等离子体还原方法能迅速有效地将负载在催化剂载体上的金属还原。催化剂处理前具有金属盐的颜色,而经过等离子体还原后,均变为灰黑色,显示金属盐转变为金属单质。如图1所示的X光电子能谱(XPS),分析发现经过等离子体还原后,催化剂表面的金属均为还原态;如图2和图3所示的高分辨透射电镜(TEM),等离子体还原的催化剂具有较好的分散性。

低温等离子体含有大量的电子,具有极强的还原性能,可以很容易地将金属离子还原为单质金属;其气体的温度接近室温,避免了高温下的不良热效应。过程简单,所需还原时间短;不使用化学还原剂,对环境友好。

附图说明

图1:0.5%Pt/TiO2催化剂经等离子体还原后的XPS谱图;图2:0.5%Pt/TiO2经等离子体还原后的TEM照片;图3:0.5%Pt/TiO2经氢气300℃还原后的TEM照片。

具体实施方式

实施例1:以TiO2为载体,浸渍H2PtCl6溶液,金属Pt的含量为0.5%;静置24小时,100℃干燥4小时;催化剂用电晕放电等离子体还原,催化剂置于放电管的两个板电极之间,密闭,将系统抽空,充入Ar做放电气体,维持200Pa的压力,在电极上施加1000V的直流电压,还原时间为30分钟。

实施例2:与实施例1基本相同,但La2O3为载体,浸渍Ni(NO3)2溶液,金属Ni的含量为7.0%;N2做放电气体,压力为50Pa,电压为500V直流,还原时间为45分钟;再浸渍Fe(NO3)3溶液,第二金属Fe的含量为3.0%,重复前面的处理步骤。

实施例3:与实施例1基本相同,但活性炭为载体,将PdCl2溶解在盐酸溶液中,然后蒸发溶液到接近干燥,再添加去离子水形成溶液,然后浸渍,金属Pd的含量为20.0%;He做放电气体,压力为1000Pa,电压为5000V直流,还原时间120分钟。

实施例4:与实施例1基本相同,但钙钛矿SrTiO3为载体,浸渍H2PtCl6溶液,金属Pt的含量为0.01%,将系统抽空,充入O2做放电气体,维持10Pa的压力,电压为100V直流,还原时间为5分钟。处理后的催化剂在N2氛围下焙烧6小时,焙烧温度为600℃。

实施例5:以HZSM-5分子筛为载体,浸渍Co(NO3)2溶液,金属Co的含量为2%;静置24小时,110℃干燥8小时;催化剂用介质阻挡放电等离子体还原,催化剂置填充于两个电极之间,通入Ar做放电气体,维持常压0.1MPa的压力,在电极上施加8000V的交流电压,还原时间为150分钟。

实施例6:与实施例5基本相同,但氧化硅为载体,浸渍Fe(NO3)3溶液,金属Fe的含量为3.0%,He做放电气体,电压为20000V,还原时间200分钟。再浸渍Cu(NO3)2溶液,第二金属Cu,含量为0.5%,重复前面的处理步骤。

实施例7:与实施例5基本相同,但Al2O3为载体,浸渍Ag(NO3)2溶液,金属Ag的含量为9.0%,空气做放电气体,电压为12000V,  还原时间40分钟。

实施例8:以ZrO2为载体,浸渍钼酸铵溶液和K2CrO3溶液,金属Mo、Cr的含量分别为5.0%、0.2%;静置24小时,110℃干燥10小时;催化剂用电晕放电等离子体还原,催化剂置于板电极上,通入Ar做放电气体,维持常压0.1MPa的压力,在电极上施加16000V的交流电压,还原时间为80分钟。

实施例9:与实施例8基本相同,但TiO2为载体,浸渍Au(NO3)2溶液,金属Au的含量为0.3%,放电气体为空气,电压为3000V,还原时间30分钟。

实施例10:与实施例8基本相同,但NaZSM-5为载体,浸渍Zn(NO3)2溶液,金属Zn的含量为2%,放电气体为空气,电压为5000V,还原时间20分钟,然后在Ar氛围下焙烧2小时,焙烧温度为300℃。

Claims (8)

1.一种利用低温等离子体还原负载金属催化剂的方法,步骤如下:1)将金属盐的活性组分,溶于去离子水或蒸馏水中,金属组分的质量含量为0.01%~20%,将溶液注入催化剂载体中,室温下静置8~24小时,然后在40~110℃干燥2~10小时;2)将步骤1)中的催化剂放在等离子体装置的两个电极之间,在放电管中的压力为50Pa~0.1MPa,通入惰性气体或空气或氧气作为等离子体放电气体,在电极上加100~20000V的直流或交流电压,处理5~200分钟。
2.如权利要求1所述的一种利用低温等离子体还原负载金属催化剂的方法,其特征是所述的方法还包括步骤3)焙烧:将步骤2)等离子体还原的催化剂在惰性气体氛围下焙烧1~10小时,温度为150~600℃。
3.如权利要求1或2所述的一种利用低温等离子体还原负载金属催化剂的方法,其特征是所述的低温等离子体是辉光放电、介质阻挡放电或电晕放电。
4.如权利要求1或2所述的一种利用低温等离子体还原负载金属催化剂的方法,其特征是所述的金属盐先用盐酸助溶,然后将溶液蒸发干燥除去盐酸,再加入蒸馏水或去离子水。
5.如权利要求1或2所述的一种利用低温等离子体还原负载金属催化剂的方法,其特征是所述的等离子体放电气体是Ar、N2、O2、He、以及空气,放电气压为50Pa~0.1Mpa。
6.如权利要求1或2所述的一种利用低温等离子体还原负载金属催化剂的方法,其特征是所述的金属盐的活性组分为多组分金属时,在步骤1中一次浸渍多种金属或按步骤1)、2)、3)重复进行。
7.如权利要求1或2所述的一种利用低温等离子体还原负载金属催化剂的方法,其特征是所述的金属盐的活性组分为H2PtCl6、PdCl2、Ni(NO3)2、Au(NO3)2、Cu(NO3)2、Ag(NO3)2、Fe(NO3)3、Co(NO3)2、Zn(NO3)2、K2CrO3或钼酸铵的一种或几种。
8.如权利要求1或2所述的一种利用低温等离子体还原负载金属催化剂的方法,其特征是所述的负载金属的载体是分子筛、钙钛矿、活性炭、氧化硅、Al2O3、La2O3、TiO2或ZrO2。
CN 200410093820 2004-12-01 2004-12-01 利用低温等离子体还原负载金属催化剂的方法 CN1647858A (zh)