CN1629405B - Method for repairing crack on asphalt road pavement - Google Patents

Method for repairing crack on asphalt road pavement Download PDF

Info

Publication number
CN1629405B
CN1629405B CN 200410101036 CN200410101036A CN1629405B CN 1629405 B CN1629405 B CN 1629405B CN 200410101036 CN200410101036 CN 200410101036 CN 200410101036 A CN200410101036 A CN 200410101036A CN 1629405 B CN1629405 B CN 1629405B
Authority
CN
China
Prior art keywords
asphalt
zhejiang
cracks
green
crack
Prior art date
Application number
CN 200410101036
Other languages
Chinese (zh)
Other versions
CN1629405A (en
Inventor
江其超
Original Assignee
深圳市魁道道路用材技术开发有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to CN200410051953 priority Critical
Priority to CN200410051953.7 priority
Application filed by 深圳市魁道道路用材技术开发有限公司 filed Critical 深圳市魁道道路用材技术开发有限公司
Priority to CN 200410101036 priority patent/CN1629405B/en
Publication of CN1629405A publication Critical patent/CN1629405A/en
Application granted granted Critical
Publication of CN1629405B publication Critical patent/CN1629405B/en

Abstract

A method for repairing crack on asphalt road pavement, relates to a processing method of the cracks of asphalt road. The repair method includes the following steps: a. cleaning the crack surface, and clearing away the dust attached on the slit surface, and so on; b. cracks are carried out a reperfussion and a filling-up handling with the asphalt glue, or carried out a pasting handling by inserting a sealing strip with the major components of asphalt on the crack surface; c. using an asphalt recovery agent with the main ingredients of the asphalt and the coal tar to brush around the asphalt glue and the sealing strip. The invention can form an effective sealing layer around the cracks to prevent the water damage.

Description

沥青道路路面裂缝的修补方法 Asphalt road pavement crack repair method

技术领域 FIELD

[0001] 本发明涉及浙青道路路面裂缝的处理方法。 [0001] The present invention relates to a method of processing green Zhejiang road surface cracks. 背景技术 Background technique

[0002] 浙青道路在浙青铺装完成开放交通一段时间后,因各种原因浙青路面会出现裂缝。 [0002] After the completion of paving roads Zhejiang green open traffic for some time in Zhejiang Green, for various reasons, Zhejiang green pavement cracks will appear. 如果不及时处理出现的这些裂缝,在外因包括雨水、车辆等因素的作用下,会加速对浙青路面的破坏,缩短浙青路面的使用寿命。 If left untreated these cracks appear in external factors, including rain, vehicles and other role, will accelerate the destruction of the green pavement Zhejiang, Zhejiang Green shorten the life of the road.

[0003] 现有技术虽然对裂缝的处理方法有多种,如对缝里进行注灌浙青胶、或在缝面涂布浙青胶、或在缝面直接粘贴封缝带(压缝带),但是在用上述方法处理后,浙青胶或封缝带的周围仍然处在大量的微裂缝、松散,还会引起水破坏。 [0003] While the prior art has a plurality of crack processing method, such as injection-filling the crevices Zhejiang green gum, surface coating or slot Zhejiang green gum, or directly pasted seam Sealing tape surface (seam belt press ), but after treatment with the method described above, or around Zhejiang green gum sealing strip is still in a large number of micro-cracks, loose, it can also cause water damage.

发明内容 SUMMARY

[0004] 本发明的目的在于提供一种减少水破坏的浙青路面裂缝修补方法。 [0004] The object of the present invention to provide a green Zhejiang pavement crack repair method of reducing water damage.

[0005] 本发明的目的可以这样实现,设计一种浙青道路路面裂缝的修补方法,包括以下步骤: [0005] The object of the present invention can be achieved, to devise a method for repairing Zhejiang Green Road pavement crack, comprising the steps of:

[0006] a、清洁裂缝面,将缝面附着的灰尘等脏物清除干净; [0006] a, cleaning the fracture face, the slit of the dust and the like attached to the surface cleaned;

[0007] b、裂缝用浙青胶进行灌注、填满处理或用主要成分为浙青的封缝带在裂缝面上进行粘贴处理; [0007] b, cracks were perfused with Zhejiang green glue, filled or processing of the paste processing Zhejiang cyan sealers in the fracture surface of the belt with a main component;

[0008] C、用主要成分为浙青和煤焦油的浙青修复剂涂刷浙青胶或封缝带的周围。 [0008] C, with the main component of green rubber squeegee or around Zhejiang Sealing tape is green and coal tar Zhejiang Zhejiang green repair agent.

[0009] 本发明可以在已修补裂缝的周围形成有效的密封层,防止水破坏。 [0009] The present invention can form an effective seal around the layer cracks patched, to prevent water damage.

附图说明 BRIEF DESCRIPTION

[0010] 图1是本发明的剖面示意图。 [0010] FIG. 1 is a schematic cross-sectional view of the present invention. 具体实施方式 Detailed ways

[0011] 以下结合实施例对本发明作进一步的描述。 [0011] The following embodiments in conjunction with the present invention will be further described.

[0012] 一种浙青道路路面裂缝的修补方法,包括以下步骤: [0012] A method for repairing cracks in road pavement Zhejiang Green, comprising the steps of:

[0013] a、清洁裂缝面,将缝面附着的灰尘等脏物清除干净,包括缝面上松散的沙、石子等脏杂物; [0013] a, cleaning the fracture face, the slit of the dust and the like attached to the surface clean, the surface comprising a loose seam sand, gravel, dirt and other debris;

[0014] b、裂缝用浙青胶进行灌注、填满处理或用主要成分为浙青的封缝带在裂缝面上进行粘贴处理; [0014] b, cracks were perfused with Zhejiang green glue, filled or processing of the paste processing Zhejiang cyan sealers in the fracture surface of the belt with a main component;

[0015] C、用主要成分为浙青和煤焦油的浙青复原剂涂刷浙青胶或封缝带的周围,在已修补的裂缝周围形成有效的密封层。 [0015] C, with the main component of green rubber squeegee or around Zhejiang Sealing tape is Zhejiang Zhejiang cyan and green recovery agents are coal tar, formed an effective seal layer around cracks patched.

[0016] 本发明所采用的材料都可在市面上购买到。 Materials used [0016] The present invention can be purchased in the market. 这些材料的主要成分基本上以浙青为主,商品的名称因厂家而各异,如浙青封缝带、浙青压缝带、浙青修复剂、浙青修复王、浙青修复油等等。 The main components of these materials substantially mainly of Zhejiang green, the product name and by different manufacturers, such as Green Tape Sealants Zhejiang, Zhejiang seamed belt press green, cyan Zhejiang restoratives, Wang Zhe green repair, repair Zhejiang green oil Wait. 采用本发明方法修补后的路面如图1所示,浙青路面1上的裂缝粘贴着封缝带2,在其上覆盖一层复原剂涂刷层3。 Using the method of the present invention a road surface shown in FIG. 1 repairing cracks on the road surface 1 is pasted Zhejiang Green Sealing tape 2 covered restoration brushing agent layer 3 thereon.

[0017] 所述浙青复原剂涂刷层3的厚度为0. 2〜40毫米。 [0017] The thickness of the green restoration Zhejiang brushing agent layer 3 is 0. 2~40 mm. 该浙青复原剂涂刷层可将裂缝四周的微裂缝、松散全部封闭形成有效的防水层。 The restoration agent Zhejiang green overcoat layer may be micro-cracks around the crack, loose all closed to form an effective water barrier. 较佳涂刷层3的厚度为2〜30毫米。 The thickness of overcoat layer 3 is preferably 2~30 mm.

[0018] 所述封缝带的头尾部相接时,两端设有斜切口。 When the first tail [0018] Sealing of the contact strip, with both ends of the oblique incision. 对称的斜切口可以增加封缝带连接处的接触面积,使连接处更加牢固。 Symmetrical oblique incision can increase the contact area with a sealing seam at the connection, at the connection more solid.

[0019] 所述裂缝大于20毫米时,先使用砂石将裂缝填实直至缝深距路面1. 2〜1. 8倍缝宽处。 When [0019] the fracture more than 20 mm, the first use of sand until fracture tamped seam depth from road 1. 2~1. 8 times the slit width. 也可以采用浙青融化与砂石混同先将裂缝填实。 It may also be used to melt and Zhejiang green sand infill confused first crack.

[0020] 本发明还包括步骤d、将直径为1〜4毫米的细沙铺洒在浙青复原剂涂刷层上。 [0020] The present invention further comprises the step of d, 1 ~ 4 mm, a diameter of sand is spread over the green restoration Zhejiang brushing agent layer. 细沙可以充实涂刷层并增大摩擦力。 You can enrich brushing sand layer and increase the friction. 路面可以在施工后10个小时左右通车运行。 Road traffic can run at about 10 hours after construction.

Claims (5)

  1. 一种沥青道路路面裂缝的修补方法,包括以下步骤:a、清洁裂缝面,将缝面附着的灰尘等脏物清除干净;b、裂缝用沥青胶进行灌注、填满处理或用主要成分为沥青的封缝带在裂缝面上进行粘贴处理;其特征在于:c、用主要成分为沥青和煤焦油的沥青复原剂涂刷沥青胶或封缝带的周围。 A method for repairing cracks in the asphalt road surface, comprising the steps of: a, cleaning the fracture face, the slit of the dust and the like attached to the surface cleaned; B, cracks were perfused with asphalt mastic, to fill a main component or treated with asphalt sealing strip of the fracture surface of the paste process; wherein: c, surrounding asphalt or asphalt rubber squeegee recovery agent sealing tape with a main component of asphalt and coal tar.
  2. 2.根据权利要求1所述的修补方法,其特征在于:所述浙青复原剂形成的涂刷层的厚度为0. 2〜40毫米。 2. The repair method according to claim 1, wherein: the thickness of the overcoat layer formed Zhejiang Green restoring agent 0. 2~40 mm.
  3. 3.根据权利要求1所述的修补方法,其特征在于:所述封缝带的头尾部相接时,两端设有斜切口。 The repair method according to claim 1, wherein: the first tail when in contact with the sealing seam ends with oblique incision.
  4. 4.根据权利要求1所述的修补方法,其特征在于:所述裂缝大于20毫米时,先使用砂石将裂缝填实直至缝深距路面1. 2〜1. 8倍缝宽处。 The repair method according to claim 1, wherein: said crack more than 20 mm, the sand will be used to crack tamped until the slit depth from the road surface 8 1. 2~1 times the slit width.
  5. 5.根据权利要求1所述的修补方法,其特征在于:还包括步骤d、将直径为1〜4毫米的细沙铺洒在浙青复原剂涂刷层上。 The repair method according to claim 1, characterized in that: further comprising the step of d, 1 ~ 4 mm, a diameter of sand is spread over the green restoration Zhejiang brushing agent layer.
CN 200410101036 2004-10-22 2004-11-24 Method for repairing crack on asphalt road pavement CN1629405B (en)