CN1597742A - Preparation method of water soluble undenatured natural collagen - Google Patents
Preparation method of water soluble undenatured natural collagen Download PDFInfo
- Publication number
- CN1597742A CN1597742A CN 200410040487 CN200410040487A CN1597742A CN 1597742 A CN1597742 A CN 1597742A CN 200410040487 CN200410040487 CN 200410040487 CN 200410040487 A CN200410040487 A CN 200410040487A CN 1597742 A CN1597742 A CN 1597742A
- Authority
- CN
- China
- Prior art keywords
- sex change
- acid
- natural collagen
- water
- soluble
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A water-soluble unmodified natural collagen is prepared from the skin of beef or pork through water washing, removing beef or pork, adding defatting agent, defatting, water washing, removing hair, outting to obtain hypoderm layer, immersing in NaCl solution, cutting to become small blocks, regulating pH=2-4, adding proteinase, stirring for 1-3 days, centrifugal separation to obtain supernatant, adding NaCl, salting, dissolving the deposit in alcohol solution, adding acylating agent, reacting, centrifugal separation to obtain deposit, washing with diluted acid and depositing three times, and freeze drying.
Description
One, technical field
The present invention relates to a kind of preparation method of water-soluble not sex change natural collagen.The preparation field that belongs to bio-medical material.
Two, background technology
Collagen protein or title collagen are a kind of fibrous protein, are one of important animal proteinums.Collagen is present in all kinds of animal bodies widely, from vertebrates to fish, skin, tendon, cartilage, various internal organs, vessel wall and the esophagus etc. of animal such as batrachians, birds and mammals all have collagen.Collagen has occupied 30% of total amount in the interior all proteins of vertebrates body, is main structural protein, and skin contains collagen more than 50%.
Sex change natural collagen (being biological active collagen) is not a kind of biomacromolecule, molecular weight be 300,000.Natural structure when its structure still keeps in animal body, i.e. the triple helix structure of collagen, this natural collagen protein is counted as the integral part of organism and is not considered to foreign matter.Natural collagen help cell survival and growth, can promote that thrombocyte condenses, function such as low antigenicity and excellent biological compatibility, be used widely aspect burn, wound, cornea disease, beauty treatment, orthopedic, the hard tissue repair.Chi H.Lee, Anuj Singla andYugyung Lee, Biochemical applications of collagen, International Journal of Pharmaceutics, 2001,221:1-22. because the sex change natural collagen does not also have good performance of keeping humidity and promotes the epidermal growth breeding, thus skin elasticity, minimizing wrinkle strengthened effectively, so also be used for the cosmetics of super quality.Chvapil，M.andEckmayer，Z.，Role?of?proteins?in?cosmetics，International?Journal?of?Cosmetic?Science，1985，7：41-49。
The method of obtaining main employing of sex change natural collagen does not have at present: (1) acid system, and promptly use organic acid such as acetate, citric acid, dilute hydrochloric acid etc. to extract natural collagen; (2) acid-enzyme hydrolysis method with acid and proteolytic enzyme acting in conjunction, under acidic conditions, extracts natural collagen from animal tissues.Miller，E.J.and?Rhodes，R.K.，Preparation?andcharacterization?of?the?different?types?of?collagen，Methods?Enzymol.，1982，82：33-64。Because the sex change natural collagen is not a solubility in acid collagen, can only could stable existence under acidic conditions so extract the collagen that obtains through above method.If the pH value of this collagen solution is brought up to 6-8, then collagen will be precipitated out.If the solids after this collagen solution lyophilize, so this solids also can only be dissolved in the acidic solution, and can not be dissolved in the neutral water.So this not sex change natural collagen that obtains usually is can not be soluble in water.And many occasions of using at collagen, then need under neutrallty condition, use, require collagen to have water-soluble or the sex change natural collagen can stable existence and precipitation do not occur under the neutrallty condition of pH6-8 yet, also do not change its natural structure, have good biological activity equally.When being used as hemostatic material, medical dressing as collagen, directly contact with tissue, the physiological condition of general human body is exactly in neutrality, pH is 7.2-7.4, when collagen is used for makeup, generally also requires the scope collagen energy stable existence of pH, and sex change does not take place at 6-8.
Three, summary of the invention
The objective of the invention is to provide a kind of preparation method of water-soluble not sex change natural collagen, be characterized in acid collagen made not that the sex change natural collagen can be directly water-soluble, with the solution state stable existence at the deficiencies in the prior art.
Purpose of the present invention is realized that by following technical measures wherein said raw material umber is parts by weight except that specified otherwise.
The preparation method of water-soluble not sex change natural collagen:
1. the not extraction of sex change natural collagen of solubility in acid
Get 100 parts of fresh ox-hide, pigskin or salted ox-hide, the pigskins of slaughtering, wash fleshing with water after, add grease-removing agent 2-3 part and handled 3-5 hour, co-processing 2 times, take out hair after, split, obtain skin corium (one deck skin promptly), soaked one day with 10% salt solution, washing cooling back chopping is with 10 parts of the onal pieces of chopping, with acid for adjusting pH to 2-4, add proteinase-10 .1-1 part, in temperature 4-6 ℃ stir process 1-3 days, obtain not sex change natural collagen solution of solubility in acid.
2. the solubility in acid purifying of sex change natural collagen not
Above-mentioned solubility in acid collagen liquid is separated with the 14000-16000rpm supercentrifuge, remove filter residue, add 3-5M NaCl in the supernatant liquor and saltout, the gained precipitation with the dissolving of 0.5-1M acetate, obtains concentration and is not sex change natural collagen solution of 1% solubility in acid after centrifugation.
3. the preparation of water-soluble not sex change natural collagen solution
With 200 parts of the solubility in acid collagen solutions of above-mentioned purifying, add acylating agent 1-10 part, reaction is 3-8 hour under room temperature.Measure the acylation reaction degree, the acidylate rate is 92-95%, obtains the thick product of water-soluble not sex change natural collagen.
4. the purifying of water-soluble not sex change natural collagen
With the thick product centrifugation of above-mentioned water-soluble not sex change natural collagen, collecting precipitation is used 0.01-0.1M dilute acid soln washing precipitation 3 times again, and the precipitation that obtains makes water-soluble not sex change natural collagen after lyophilize.
Grease-removing agent is any in ethylene glycol ethyl ether, aliphatic acid polyethenoxy ether or the alkylphenol polyoxyethylene.
Enzyme is any in stomach en-, 537 aspartic proteases, the fungi prozyme.
Acylating agent is any in pimelic acid acid anhydride, MALEIC ANHYDRIDE, the Tetra hydro Phthalic anhydride.
The denaturation temperature that records collagen solution with difference formula scanning calorimeter is 36-38 ℃, sees for details shown in Figure 1.The molecular weight that the SDS-PAGE electrophoretic method records collagen is respectively α chain 100,000, β chain 200,000, γ chain 300,000, sees for details shown in Figure 2.Dissolve in neutral solution or the water, water-soluble back becomes stable transparent viscous solution.This water-soluble not sex change natural collagen can be used for cosmetics and biomedical sector.
Four, description of drawings
Fig. 1 is the DSC thermal denaturation temperature test pattern of water-soluble natural collagen.
Fig. 2 is the SDS-PAGE electrophoretic separation figure of water-soluble natural collagen.
Five, embodiment
Below by embodiment the present invention is specifically described; be necessary to be pointed out that at this present embodiment only is used for the present invention is further specified; can not be interpreted as limiting the scope of the invention, the person skilled in the art in this field can make some nonessential improvement and adjustment according to the content of the invention described above.
Embodiment 1: get the fresh ox-hide 100kg after slaughtering, fleshing machine is removed the unnecessary meat tissue of flesh noodles, the washing back adds ethylene glycol ethyl ether 3kg, handled 3 hours, washing back dehairing machine takes out most of hair, and split takes off a layer skin corium, soaked 1 day with 10% salt solution, be cut into fine grained chippings after the washing, get onal piece 10kg, with acid for adjusting pH to 2-4, add stomach en-0.5kg, 4-6 ℃ following stir process 1-3 days, separate with the 14000rpm high speed centrifugation and to remove filter residue, add 3M NaCl in the supernatant liquor and saltout, the precipitation that centrifugation obtains is dissolved with 1M acetate, and collagen solution concentration is 1%.Get collagen solution 200g, add pimelic acid acid anhydride 3g, reaction is 3 hours under room temperature, and recording the acidylate rate is 92%, centrifugation, and precipitation 0.05M diluted acid water washing 3 times, lyophilize obtains water-soluble not sex change natural collagen.
Embodiment 2: get salted pigskin 100kg, after the fleshing machine fleshing was handled, the washing degreasing added fatty alcohol-polyoxyethylene ether 3kg, handles co-processing 2 times 5 hours.Washing back dehairing machine takes out most of hair, and split takes off a layer skin corium, soaked 1 day with 10% salt solution, be cut into fine grained chippings after the washing, get onal piece 10kg, add the lemon acid for adjusting pH to 2-4, add 537 enzyme 1kg, in temperature 4-6 ℃ stir process 1-3 days, separate with the 15000rpm high speed centrifugation and to remove filter residue, add 5M NaCl in the supernatant liquor and saltout, the precipitation that centrifugation obtains is dissolved with 0.5M acetate, and collagen solution concentration is 1%.Get collagen solution 200g, add MALEIC ANHYDRIDE 5g, reaction is 5 hours under room temperature, and recording the acidylate rate is 95%, centrifugation, and precipitation obtains water-soluble not sex change natural collagen with 3 postlyophilizations of 0.0gM diluted acid water washing.
Embodiment 3: get salted ox-hide 100kg; fleshing machine is removed the unnecessary meat tissue of flesh noodles; the washing back adds alkylphenol polyoxyethylene 2kg degreasing; handled 3 hours; washing back dehairing machine takes out most of hair; split; take off a layer skin corium, soaked 1 day, be cut into fine grained chippings after the washing with 10% salt solution; get onal piece 10kg; add the lemon acid for adjusting pH to 2-4, add fungi prozyme 0.2kg, in temperature 4-6 ℃ stir process 1-3 days; separate except that filter residue with the 16000rpm high speed centrifugation; add 5M NaCl in the supernatant liquor and saltout, the precipitation that centrifugation obtains is with the dissolving of 1M acetate, obtains concentration and be 1% solubility in acid collagen solution; get this collagen solution 200g; add Tetra hydro Phthalic anhydride 8g, reaction is 8 hours under room temperature, and recording the acidylate rate is 93%; centrifugation, precipitation obtains water-soluble not sex change natural collagen with 3 postlyophilizations of 0.1M diluted acid water washing.
Claims (4)
1. the preparation method of water-soluble not sex change natural collagen is characterized in that:
(1) the not extraction of sex change natural collagen of solubility in acid
Choose fresh ox-hide, pigskin or salted ox-hide, pigskin, 100 weight parts are behind the washing fleshing, add grease-removing agent 2-3 weight part and handle 3-5 hour co-processing 1-2 time, pull out a mao back split, obtain skin corium, soaked 1 day with 10% salt solution, washing cooling back chopping, get onal piece 10 weight parts of chopping, to 2-4, add proteinase-10 .1-1 weight part with acid for adjusting pH, in temperature 4-6 ℃ stir process 1-3 days, obtain not sex change natural collagen solution of solubility in acid.
(2) the solubility in acid purifying of sex change natural collagen not
Above-mentioned solubility in acid collagen liquid is separated with the 14000-16000rpm supercentrifuge, remove filter residue, add 3-5M NaCl in the supernatant liquid and saltout, the gained precipitation with the dissolving of 0.5-1M acetate, obtains concentration and is not sex change natural collagen solution of 1% solubility in acid after centrifugation.
(3) preparation of water-soluble not sex change natural collagen
With solubility in acid natural gum stoste 200 weight parts of above-mentioned purifying, add acylating agent 1-10 weight part, reaction is 3-8 hour under the room temperature, measures the acylation reaction degree, and the acidylate rate is 92-95%, obtains the thick product of water-soluble not sex change natural collagen.
(4) purifying of water-soluble not sex change natural collagen
With the thick product centrifugation of above-mentioned water-soluble not sex change natural collagen, collecting precipitation precipitates 3 times with the water washing of 0.01-0.1M diluted acid again, and the precipitation that obtains makes water-soluble not sex change natural collagen after lyophilize.
2. as the preparation method of water-soluble not sex change natural collagen as described in claims 1, it is characterized in that grease-removing agent is any in ethylene glycol ethyl ether, aliphatic acid polyethenoxy ether, the alkylphenol polyoxyethylene.
3. as the preparation method of water-soluble not sex change natural collagen as described in claims 1, it is characterized in that proteolytic enzyme is any in stomach en-, 537 aspartic proteases, the fungi prozyme.
4. as the preparation method of water-soluble not sex change natural collagen as described in claims 1, it is characterized in that acylating agent is any in pimelic acid acid anhydride, MALEIC ANHYDRIDE, the Tetra hydro Phthalic anhydride.