CN1583640A - 灌浆式防火玻璃及其内含的透明防火凝胶 - Google Patents
灌浆式防火玻璃及其内含的透明防火凝胶 Download PDFInfo
- Publication number
- CN1583640A CN1583640A CN 200410027474 CN200410027474A CN1583640A CN 1583640 A CN1583640 A CN 1583640A CN 200410027474 CN200410027474 CN 200410027474 CN 200410027474 A CN200410027474 A CN 200410027474A CN 1583640 A CN1583640 A CN 1583640A
- Authority
- CN
- China
- Prior art keywords
- fire prevention
- gel
- resistant glass
- water
- flame resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种灌浆式防火玻璃的透明防火凝胶,该防火透明凝胶的组成成分中包括胶凝剂、交联剂、引发剂、阻燃填充剂、水以及pH值调节剂,所述防火透明凝胶的pH值为1~5。发明所述配方制成的透明防火凝胶中不含有高价金属铝离子,由pH值调节剂调节pH值,因此耐老化和杂质少。依据上述配方制作的防火玻璃,包括由上、下基板(1)、(2)和开口边框(3)制成中空的玻璃盒(4);液态的透明防火凝胶材料(5)注入所述空腔(41)中。由于该凝胶已经完全保证了透明防火凝胶与玻璃盒粘结的牢固度,所以可以完全不使用偶联剂,因此具有气泡少的特点。
Description
技术领域 本发明涉及建筑物防护,特别涉及制作建筑物防火空间封闭用防火玻璃及其内含的透明防火凝胶。
背景技术 目前制作灌浆式防火玻璃的透明防火凝胶基本采用ZL95102099.4《防火玻璃》所公开的配方,这个配方中含有硫酸铝钾这种高价金属离子成分。由于硫酸铝钾比较难溶解,价格也较高,所以,采用上述配方制成的防火玻璃产品成本较高,同时该类产品还存在长期使用环境下易老化以及所含杂质多等缺陷。另外,采用现有技术制作防火玻璃必须使用偶联剂,以便将透明防火凝胶与玻璃盒进行有效的粘结,使玻璃盒中的透明防火凝胶不下坠,玻璃不变形。但是,偶联剂的使用也带来一些副作用,就是容易产生气泡,影响防火玻璃的质量。
发明内容 本发明在上述发明专利的基础上,主要对上述配方中的交联剂、阻燃填充剂的成分进行改进,提出采用不含高价金属铝离子的新配方,并且采用PH值调节剂进行调节PH值,并且在制作防火玻璃的过程中不使用偶联剂,解决上述现有技术中的不足之处。
本发明的技术方案如下:一种灌浆式防火玻璃的透明防火凝胶,该防火透明凝胶的组成成分中包括胶凝剂、交联剂、引发剂、阻燃填充剂、水以及PH值调节剂。由于硫酸铝钾在透明防火凝胶中所起到的阻燃作用可以用其他物质代替,而硫酸铝钾会产生比较大的副作用,所以,本配方在现有技术的配方中取消含有高价金属离子的硫酸铝钾,采用PH值调节剂调节整个透明防火凝胶的PH值,保证交联反应正常进行,同时避免了因含高价金属铝离子而产生的易老化和杂质多的缺陷。
一种依据上述配方制作的防火玻璃,包括由上、下基板和开口边框制成中空的玻璃盒;液态的透明防火凝胶材料由开口边框上的开口注入所述空腔中,经交联反应后,该透明防火凝胶材料胶凝且与所述上、下基板和开口边框粘结成一体,再用封口条密封上述开口。由于采用本发明所述配方已经完全保证了透明防火凝胶与玻璃盒粘结的牢固度,所以在制作产品的过程中可以完全不使用偶联剂,因此可以避免因使用偶联剂而产生的气泡;又由于采用本发明所述配方制成的透明防火凝胶中不含有高价金属铝离子,所以,成品防火玻璃耐老化、杂质少。
采用本发明提供配方所生产的产品,在防火阻燃方面与现有技术的产品相比具有相同或更优的效果,同时具有透光性优良、气泡少、使用寿命长以及生产成本低的特点。
附图说明
图1是本发明所述产品的立体示意图。
具体实施方式 结合附图进一步阐述本发明的各种实施方式。
一种灌浆式防火玻璃的透明防火凝胶,该防火透明凝胶的组成成分中包括胶凝剂、交联剂、引发剂、阻燃填充剂、水以及PH值调节剂。其中所述胶凝剂为丙烯酰胺;引发剂为过硫酸盐、亚硫酸氢盐氧化还原体系;交联剂为亚甲基双丙烯酰胺或甲醛中的任一种;阻燃填充剂为氯化物、硫酸盐、水溶性磷酸盐、水溶性硅酸盐或有机多羟基化合物中的任一种;或者为氯化物、硫酸盐、水溶性磷酸盐、水溶性硅酸盐,有机多羟基化合物中的全部或部分混合的混合物。所述氯化物为氯化铵、氯化钠、氯化钾、氯化钙、氯化镁中的任一种,或者为氯化铵、氯化钠、氯化钾、氯化钙、氯化镁中全部或部分混合的混合物;所述硫酸盐为硫酸钾、硫酸钠、硫酸锌、硫酸铵或硫酸镁中的任一种,或者为硫酸钾、硫酸钠、硫酸锌、硫酸铵和硫酸镁中全部或部分混合的混合物;所述水溶性磷酸盐为磷酸钾、磷酸钠、磷酸铵或多聚磷酸铵中的任一种,或者为磷酸钾、磷酸钠、磷酸铵和多聚磷酸铵全部或部分混合的混合物;所述水溶性硅酸盐为硅酸钾、硅酸钠中的任一种,或者为硅酸钾、硅酸钠混合物;有机多羟基化合物为丙二醇或甘油等。所述PH值调节剂为硫酸、磷酸或盐酸的任一种或者为硫酸、磷酸和盐酸全部或部分混合物的混合物。本配方在现有技术的配方中取消含有高价金属铝离子的硫酸铝钾,采用PH值调节剂调节整个透明防火凝胶的PH值,保证交联反应正常进行,同时避免了因含高价金属铝离子而产生的易老化和杂质多的缺陷。
在上述配方中,防火透明凝胶中各成分按重量计算的组成比例具体选择为:胶凝剂4~10%;交联剂0.01~5%,其中选择亚甲基双丙烯酰胺为0.01~0.2%,优选方案是0.02~0.1%,选择甲醛为0.5~5%,优选方案是1~3%;引发剂0.001~0.2%,优选方案是0.01~0.1%;PH值调节剂主要根据PH值的调节需求而定,一般范围是0.005~10%;阻燃填充剂选择氯化物是4~24%,选择水溶性磷酸盐是0~20%,优选方案是5~15%,选择水溶性硅酸盐是0~20%,优选方案是5~15%,硫酸盐是0~20%,优选方案是5~15%,有机多羟基化合物如甘油是0~20%,优选方案是5~15%;水根据上述各成分选定的比例不同而不同,一般在50~91%范围内。
为了比较好的进行交联反应,该防火透明凝胶的PH值应该选择为1~5,优选方案是2~3。
由图1可知,一种依据上述配方制作的防火玻璃,包括由上、下基板1、2和开口边框3制成中空的玻璃盒4;液态的透明防火凝胶材料5由开口边框3上的开口31注入所述空腔41中,经交联反应后,该透明防火凝胶材料5胶凝且与所述上、下基板1、2和开口边框3粘结成一体,再用封口条32密封上述开口31。由于采用本发明所述配方已经完全保证了透明防火凝胶5与玻璃盒4粘结的牢固度,所以在制作产品的过程中可以完全不使用偶联剂,因此可以避免因使用偶联剂而产生的气泡;又由于采用本发明所述配方制成的透明防火凝胶5中不含有高价金属铝离子,所以,成品防火玻璃耐老化、杂质少。
Claims (10)
1.一种灌浆式防火玻璃的透明防火凝胶,其特征在于:该防火透明凝胶的组成成分中包括胶凝剂、交联剂、引发剂、阻燃填充剂、水以及PH值调节剂。
2.根据权利要求1所述灌浆式防火玻璃的透明防火凝胶,其特征在于:所述胶凝剂为丙烯酰胺;引发剂为过硫酸盐和亚硫酸氢盐的混合物。
3.根据权利要求1所述灌浆式防火玻璃的透明防火凝胶,其特征在于:所述交联剂为亚甲基双丙烯酰胺或甲醛的任一种。
4.根据权利要求1所述灌浆式防火玻璃的透明防火凝胶,其特征在于:所述阻燃填充剂为氯化物、硫酸盐、水溶性磷酸盐、水溶性硅酸盐或有机多羟基化合物中的任一种;或者为氯化物、硫酸盐、水溶性磷酸盐、水溶性硅酸盐和有机多羟基化合物中的全部或部分混合的混合物。
5.根据权利要求4所述灌浆式防火玻璃的透明防火凝胶,其特征在于:所述氯化物为氯化铵、氯化钠、氯化钾、氯化钙、氯化镁中全部或部分混合的混合物;所述硫酸盐为硫酸钾、硫酸钠、硫酸锌、硫酸铵或硫酸镁中的任一种,或者为硫酸钾、硫酸钠、硫酸锌、硫酸铵和硫酸镁中全部或部分混合的混合物;所述水溶性磷酸盐为磷酸钾、磷酸钠、磷酸铵或多聚磷酸铵中的任一种,或者为磷酸钾、磷酸钠、磷酸铵和多聚磷酸铵全部或部分混合的混合物;所述水溶性硅酸盐为硅酸钾、硅酸钠中的任一种,或者为硅酸钾、硅酸钠混合物;有机多羟基化合物为丙二醇或甘油。
6.根据权利要求1所述灌浆式防火玻璃的透明防火凝胶,其特征在于:所述PH值调节剂为硫酸、磷酸或盐酸的任一种。
7.根据权利要求1所述灌浆式防火玻璃的透明防火凝胶,其特征在于:所述PH值调节剂为硫酸、磷酸和盐酸全部或部分的混合物。
8.根据权利要求1所述灌浆式防火玻璃的透明防火凝胶,其特征在于:所述防火透明凝胶中各成分按重量的组成比例为:胶凝剂4~10%;交联剂0.01~5%;引发剂0.001~0.2%;PH值调节剂0.005~10%;阻燃填充剂4~44%;水50~91%。
9.根据权利要求1所述灌浆式防火玻璃的透明防火凝胶,其特征在于:所述防火透明凝胶的PH值为1~5。
10.一种依据权利要求1所述配方制作的防火玻璃,其特征在于:包括由上、下基板(1)、(2)和开口边框(3)制成中空的玻璃盒(4);液态的透明防火凝胶材料(5)由开口边框(3)上的开口(31)注入所述空腔(41)中,经交联反应后,该透明防火凝胶材料(5)胶凝且与所述上、下基板(1)、(2)和开口边框(3)粘结成一体,然后用封口条(32)密封上述开口(31)得到成品。