CN1559967A - 一种水泥基轻质防火保温砂浆 - Google Patents

一种水泥基轻质防火保温砂浆 Download PDF

Info

Publication number
CN1559967A
CN1559967A CNA200410016573XA CN200410016573A CN1559967A CN 1559967 A CN1559967 A CN 1559967A CN A200410016573X A CNA200410016573X A CN A200410016573XA CN 200410016573 A CN200410016573 A CN 200410016573A CN 1559967 A CN1559967 A CN 1559967A
Authority
CN
China
Prior art keywords
thermal insulating
cement
mortar
insulating layers
insulating mortar
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA200410016573XA
Other languages
English (en)
Inventor
孙振平
蒋正武
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongji University
Original Assignee
Tongji University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongji University filed Critical Tongji University
Priority to CNA200410016573XA priority Critical patent/CN1559967A/zh
Publication of CN1559967A publication Critical patent/CN1559967A/zh
Pending legal-status Critical Current

Abstract

本发明属建筑材料技术领域,具体涉及一种水泥基轻质防火保温砂浆。由普通硅酸盐水泥、粉煤灰、膨胀珍珠岩、纤维素、十二烷基苯磺酸钠组成,使用本发明能高效地对建筑物墙面和顶面做保温层施工,从而大幅度改善建筑物保温隔热性,减少北方冬季供暖和南方夏季降温能耗,本发明密度轻、耐高温、不燃、抗火性好,使用安全。本发明适用于钢筋混凝土、混凝土、粘土砖、金属等墙、屋面的保温层施工,也适合浴室、地下室和冷库等的保温层施工。

Description

一种水泥基轻质防火保温砂浆
技术领域
本发明属建筑材料技术领域,具体涉及一种水泥基轻质防火保温砂浆。
背景技术
人口爆炸、资源匮乏和环境恶化是当前人们面临的主要问题,这将导致全球气候显著变暖。
我国过去由于综合国力较弱,建筑物的设计和施工一直奉行“因陋简就,满足实用性”的原则,所以现有旧建筑物多以实心粘土砖、混凝土为围护材料(墙面和顶面),原因是它们既可以承重,又充当了围护材料。然而这些传统围护材料保温隔热性很差。北方地区冬季寒冷,必须采用供暖设施取暖;南方地区则夏季异常炎热,目前空调几乎普及。不论北方还是南方地区,由于建筑物保温隔热性能不佳,导致室内外热量交换大,冬季室内温度较低,而夏季室内温度较高,室内居住的人感到非常不舒适,而采用供暖或空调降温措施后,也因为保温措施不当而浪费了大量能源。近年来,随着人民生活水平的提高和综合国力的增强,建设保温隔热性好、通风情况佳、舒适、节能、降耗的绿色生态的建筑已经被列入议事日程。为此,研制和生产符合时代要求的保温隔热材料,进一步提高建筑物保温隔热性,降低北方供暖和南方空调能耗,就显得十分迫切了。
现有的保温材料,如聚苯乙烯泡沫塑料等尽管重量轻、保温效果好,但防火性不好,易燃,影响使用者的安全,另外其对施工配套材料要求十分高;加气砌块等材料只能在建筑施工时使用,不能用作对旧建筑物的改造材料。国内住宅的建设从过去的因陋简就,到现在的更加注重舒适性、节能、节约能源和生态性,一场新的建设革命和对老建筑的功能性改造正在悄然兴起,而在这场改造过程中需求大量的防水材料(如坡屋顶材料、防水砂浆和防水涂料等)和保温隔热材料。对已建大楼,在内墙表面和外墙表面施涂一定厚度的保温砂浆,然后再进行抹面和表面装饰处理,无疑是最为方便有效和节省成本的做法。
发明内容
本发明的目的在于提供一种能有效对建筑物进行保温隔热处理的水泥基轻质防火保温砂浆。
本发明提出的水泥基轻质防火保温砂浆,由普通硅酸盐水泥、粉煤灰、膨胀珍珠岩、纤维素、十二烷基苯磺酸钠组成,各组份的重量比为:
普通硅酸盐水泥      100粉煤灰              2-30膨胀珍珠岩          32-80纤维素              0-0.007十二烷基苯磺酸钠    0.0003-0.002各组份较佳的重量比为:普通硅酸盐水泥      100粉煤灰              4-28膨胀珍珠岩          50-70纤维素              0.0025-0.006十二烷基苯磺酸钠    0.0005-0.0015本发明的制备方法是:按前述各重量比例称量各组份,先将水泥、粉煤灰、纤维素和十二烷基苯磺酸钠通过物理机械混合均匀,再将该混合物与膨胀珍珠岩通过物理机械混合均匀,即得到本产品。
本发明中,普通硅酸盐水泥作为无机胶凝材料,能与水发生水化反应,产生凝胶状物质,将膨胀珍珠岩胶结在一起,产生强度,同时水泥水化产物凝固后还能与墙面、屋面等基底材料产生化学和物理作用,使保温砂浆层与墙面或屋面粘结牢固。粉煤灰含有SiO2和Al2O3等活性物质,可以与水泥水化产物Ca(OH)3发生二次水化反应,产生一定量胶凝物质,提高砂浆强度和与基底材料的粘结能力。膨胀珍珠岩是经高温煅烧后体积膨胀20-30倍后的产物,主要成分SiO2和Al2O3,结构类似玉髓结构,含有结构水。由于内部含有大量孔隙,膨胀珍珠岩的松散堆积密度只有120kg/m3左右,其导热系数非常低,只有0.04-0.06Kcal/m.h.℃,可耐受800℃高温,不会燃烧。纤维素作为保水增稠组份,其作用在于能在水泥浆体中溶胀,产生桥连作用,并通过分子吸附作用将水泥颗粒、粉煤灰颗粒和膨胀珍珠岩颗粒连接在一起,避免水泥颗粒沉降和膨胀珍珠岩颗粒上浮,保证砂浆拌合后的均匀性;由于该砂浆中质量较轻的膨胀珍珠岩的体积占90%以上,粘聚性很差,而纤维素的存在大大增加了砂浆加水拌合后的粘聚性和施工性;纤维素的作用还在于防止浆体中水分被基底材料吸收或过度蒸发,从而起到良好的自养护作用。十二烷基苯磺酸钠的作用在于可以使砂浆在加水搅拌过程中引入一定量的气泡,增加粘聚性和施工性,并且砂浆导热系数能进一步降低。因为砂浆中浆体体积较少,施工性差,在水泥浆体中引入一定量气泡相当于增加了浆体的体积,再者,含有大量不连通气泡的浆体硬化后,其导热系数大大降低。
本发明采用防火性极好的膨胀珍珠岩颗粒,并附以多种胶凝材料和外加剂,为一种轻质、防火和保温隔热性十分优良的保温砂浆,其供应形式为袋包装干粉。使用时,只要在现场按照比例加水搅拌均匀后即可进行施工,加水量为保温砂浆重量的100-150%。经检验,本发明松散容重低于350kg/m3,导热系数低于0.09W/m.K,抗压强度大于0.3MPa,粘结抗拉强度大于0.2MPa,产品不燃,而且由于多孔、导热系数极低,对阻隔热量传递、防止火势蔓延非常有效。经过实际工程应用后认为加水拌合后粘聚性好,易施工,采用本发明对墙面处理过的房屋夏季室内气温比未处理过的房屋低2-3℃,空调能耗节约15%左右,且每年的空调运行时间可比原来缩短20天左右,本发明技术值得大力推广。
本发明对金属无锈蚀作用,广泛适用于钢筋混凝土、混凝土、粘土砖、金属等墙、屋面的保温层施工,也适合于浴室、地下室和冷库等的保温层施工。
具体实施方式
实施例1,水泥基轻质防火保温砂浆按普通硅酸盐水泥59.52%(质量百分比,下同),粉煤灰8.33%,膨胀珍珠岩32.14662%,纤维素0.00298%,十二烷基苯磺酸钠0.0004%配制而成。所配制产品的松散堆积密度为335kg/m3,当加入占干粉材料110%的水进行搅拌后,产品即可施工,硬化绝干后表观密度420kg/m3,28d抗压强度为0.5MPa,粘结抗拉强度为0.35MPa,导热系数为0.082W/m.K。
实施例2,水泥基轻质防火保温砂浆按普通硅酸盐水泥57.80%,粉煤灰9.25%,膨胀珍珠岩32.94607%,纤维素0.00347%,十二烷基苯磺酸钠0.00046%配制而成。所配制产品的松散堆积密度为323kg/m3,当加入占干粉材料115%的水进行搅拌后,产品即可施工,硬化绝干后表观密度414kg/m3,28d抗压强度为0.4MPa,粘结抗拉强度为0.30MPa,导热系数为0.075W/m.K。
实施例3,水泥基轻质防火保温砂浆按普通硅酸盐水泥54.62%,粉煤灰15.25%,膨胀珍珠岩30.12593%,纤维素0.00327%,十二烷基苯磺酸钠0.0008%配制而成。所配制产品的松散堆积密度为342kg/m3,当加入占干粉材料125%的水进行搅拌后,产品即可施工,硬化绝干后表观密度404kg/m3,28d抗压强度为0.45MPa,粘结抗拉强度为0.32MPa,导热系数为0.080W/m.K。

Claims (3)

1.一种水泥基轻质防火保温砂浆,其特征在于由普通硅酸盐水泥、粉煤灰、膨胀珍珠岩、纤维素和十二烷基苯磺酸钠组成,各组份的重量比为:普通硅酸盐水           100粉煤灰                 2-30膨胀珍珠岩             32-80纤维素                 0-0.007十二烷基苯磺酸钠       0.0003-0.002。
2.根据权利要求1所述的水泥基轻质防火保温砂浆,其特征在于各组份的重量比为:普通硅酸盐水泥         100粉煤灰                 4-28膨胀珍珠岩             50-70纤维素                 0.0025-0.006十二烷基苯磺酸钠       0.0005-0.0015。
3.一种如权利要求1所述的水泥基轻质防火保温砂浆的使用方法,其特征在于加入该材料重量100-150%的水,搅拌均匀。
CNA200410016573XA 2004-02-26 2004-02-26 一种水泥基轻质防火保温砂浆 Pending CN1559967A (zh)