CN1489651A - 防紫外光用轧光织物 - Google Patents

防紫外光用轧光织物 Download PDF

Info

Publication number
CN1489651A
CN1489651A CNA028041844A CN02804184A CN1489651A CN 1489651 A CN1489651 A CN 1489651A CN A028041844 A CNA028041844 A CN A028041844A CN 02804184 A CN02804184 A CN 02804184A CN 1489651 A CN1489651 A CN 1489651A
Authority
CN
China
Prior art keywords
fabric
clothes
calendering
upf
nylon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA028041844A
Other languages
English (en)
Inventor
M・伍兹
M·伍兹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Invista Technologies Sarl
Original Assignee
EI Du Pont de Nemours and Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by EI Du Pont de Nemours and Co filed Critical EI Du Pont de Nemours and Co
Publication of CN1489651A publication Critical patent/CN1489651A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种服装，它包含至少一个由单层厚度含合成聚合物长丝织物组成的区域，其中该织物至少一个表面经过了轧光处理且该织物具有至少30的按照AATCC试验方法183－1999测定的紫外线保护系数。本发明还提供一种层合织物，它包含提供防紫外光的上述织物的层，以及第二织物或薄膜的层如对紫外辐射敏感的材料。本发明还提供制备防紫外光织物的方法，包括下列步骤：由一种或多种复丝纱成形一种织物；以及轧光该织物；随后按照AATCC试验方法183－1998测定轧光后织物的紫外线保护系数(UPF)。

Description

防紫外光用轧光织物
本发明涉及一种改进织物的紫外(UV)线遮挡性能的方法以及包含按该方法生产的改良织物的服装和其他制品。
公众对过分暴露于太阳紫外线辐照的危险的认识导致对具有高太阳紫外线保护系数(如下文定义的UPF)的纺织织物的需求。此种高UPF应以低成本实现，且不损害舒适、耐久、美学等品质或其他纺织织物的品质。
在服装领域，低于15的UPF被认为是“低保护”，UPF介于15～30，认为是“中等保护”，而UPF大于30，算作“高保护”。澳大利亚辐射实验室对具有等于或大于40的UPF的织物颁发特殊认证。
具有高UPF值的织物也用于保护非生物免受阳光和其他UV辐照的需要。特别是，此种织物可成形为一种外层，用以保护某种紫外敏感织物和具有有用性能的薄膜。
美国专利6,037,280(Edwards等人)，转让给KoalaKonnection，公开一种紫外(UV)线遮挡纺织品，它包括一种织物、紫外遮挡颗粒和用于将颗粒固定在织物上的粘结剂。该文献公开，该紫外遮挡纺织品不过是用某种紫外遮挡剂与粘结剂组合起来涂布织物获得紫外遮挡能力的。测定了某些织物与颗粒组合的紫外线保护系数。此类组合显示相当于织物组合对照例的2～3倍的UPF改进。
美国专利5,503,917描述一种具有较高UV保护系数的机织织物。此种提高是通过织物的砂洗，随后进行空气喷射洗涤的加工步骤达到的。
本发明人惊奇地发现，包含部分合成聚合物长丝的织物当织物经过轧光(轧光(chintzing))处理时，其UPF将大大提高。轧光是一种已知技术，用于改进某种织物的防风能力，减少纤维从纤维隔热层透过织物泄漏，或者改变某种织物的外观。然而，迄今为止轧光从未被用于改进紫外光保护系数。
本发明的目的是提供一种表现出高紫外线保护系数的服装。
本发明另一个目的是提供一种层合结构，其中具有高UPF的织物保护层被层合到第二薄膜或织物的层上。
在第一方面，本发明提供一种包含至少一个由单层厚度织物组成的区域的服装，其中该织物包含合成聚合物长丝，该织物的至少一个表面经过了轧光处理，且该织物具有至少30的按下文定义的紫外线保护系数(UPF)。
优选的是，该服装选自衬衫、女衬衫、裤子(长或短的)、泳装或帽子。优选的是，该服装是儿童服装物品。优选的是，该服装基本或本质上由单层厚度织物组成，例如，单层厚度衬衫。此种服装当穿在身上且同一身体区域不再有任何其他服装、织物或防晒保护覆盖物时能提供满意的防太阳紫外线辐照保护。在某些实施方案中，织物被仅在一面轧光，而这一面可以是服装贴身的一面。
术语“单层厚度”是指纺织长丝的单层机织、非织造布或针织物。优选的是，该织物的重量小于150g/m2，更优选50～100g/m2。这样的织物是比较轻薄的织物，适合炎热气候。优选的是，该织物具有至少0.085标准立方米(3标准立方英尺)每分钟，更优选至少0.14标准立方米(5标准立方英尺)每分钟在125Pa静压下，按下文测定的空气渗透率。较高的空气渗透率给织物提供透气性和凉爽。
该织物包含合成长丝且优选它基本上由合成长丝组成。优选的是，合成长丝是热塑性的，更优选它们是熔融纺长丝，最优选它们选自聚酰胺长丝、聚酯长丝及其混合物。优选的聚酰胺是尼龙6、尼龙66、尼龙46、尼龙7、尼龙10、尼龙11、尼龙610、尼龙612、尼龙12和它们的混合物和共聚酰胺；优选的聚酯包括聚对苯二甲酸乙二醇酯(PET)、聚对苯二甲酸1，3-丙二醇酯(PTT)和聚对苯二甲酸1，4-丁二醇(tetrabutylene)酯。更优选的聚酰胺包括尼龙6、尼龙66，而更优选的聚酯包括PET和PTT。
优选的是，合成长丝包含紫外吸收剂材料，更优选它们包含二氧化钛颗粒。优选的二氧化钛颗粒的粒度还使其具有消光剂的作用(优选介于0.3～1μm)，且优选它们以0.1～4wt％，更优选0.5～3wt％的重量浓度存在。替代或附加地，该聚合物可包括其他用于紫外光吸收的添加剂，如：CYASORB(注册商标)UV-3346、-1164、-3638、-5411；和TINUVIN(注册商标)234，其含量介于约0.1～0.3wt％。
本发明服装中的织物至少一面是轧光的。织物的轧光是通过在织物的至少一个表面加热和加压完成的。轧光的表面根据该表面特有的塑性形变很容易识别出来。轧光温度优选维持在140℃～195℃。轧光压力优选是50吨/平方英寸(6.5×106N/m2)(±10％)且轧光优选以12～18m/min的速度实施。
轧光优选采用一对夹辊实施。夹辊的第一辊具有硬质、光滑的加热表面，例如加热的不锈钢。第二辊不加热通常覆盖有尼龙/羊毛或任选地包纸。此种类型轧光设备可由Kusters纺织机械公司(I-85，Zima Park Drive，P.O.Box 6128，Spartanburg，S.C.29304，USA)购得。
正如下面的实例更详细地说明的那样，本发明人发现，轧光直接导致UPF值非常大和令人惊奇的提高。UPF因轧光而提高了十倍以上，轧光后织物可表现出500或更高，或甚至1000或更高的UPF。
按照本发明服装中的织物具有至少30，更优选至少40，进一步优选至少100，最优选至少500的紫外线保护系数，按AATCC试验方法183-1999的规定。本发明人发现，此种UPF值借助轧光可轻易地达到。
在第二方面，本发明提供一种多层织物，它具有至少30的按AATCC试验方法183-1999的规定的紫外线保护系数，它包含：含合成聚合物长丝的第一织物构成的第一层，其中第一织物的至少一面经过了轧光处理；以及第二织物或薄膜构成的第二层，其中第二织物或薄膜层合到第一织物上。
第二织物或薄膜可以是一种当不存在该轧光层时表现出低UPF的织物或薄膜，例如，单独第二织物或薄膜可表现出小于20或者小于10的UPF，因此就要求第一织物保证该层合物具有足以提供有效太阳紫外线保护作用的高UPF。优选的是，层合物本身具有至少80，更优选至少150的UPF。
优选的是，层合物具有50～250g/m2，更优选50～150g/m2的织物重量。
在另一种优选的实施方案中，第二织物或薄膜包含对紫外线辐照敏感的材料。此种材料在暴露于刚好海平面的太阳紫外线达500小时或更长，更典型地100小时或更长之后将表现出变色或不可接受的机械性能。此种紫外敏感织物的例子包括某些聚酯和聚酯衍生物如共聚醚酯共聚物。其他此类材料包括某些聚氨酯、聚氯乙烯和PTFE衍生物。该材料还包括紫外敏感染料或增塑剂。该轧光第一织物高得出奇的UPF使它们能够给其下面的紫外敏感层提供有效防紫外降解保护。
本发明这方面的第一织物的优选特性符合上面关于本发明第一方面每一种优选实施方案的服装织物的规定。然而，可以想象，在这些实施方案中的第一织物可能特别轻薄，例如，50g/m2或更低。
第一织物优选通过熔融粘合、水力缠结(水刺)、粘合剂粘合、针刺或其他传统方法粘合到第二织物上。
在第三方面，本发明还提供一种制备紫外光保护织物的方法，包括下列步骤：由一种或多种复丝纱成形一种织物；以及轧光该织物；随后按照AATCC试验方法183-1998测定轧光后织物的紫外线保护系数(UPF)。
优选的是，本发明方法还包括轧光步骤前测定织物的UPF的步骤。这样便可以就轧光对UPF的效果做出评估和优化。
优选的是，轧光条件的选择应保证在轧光步骤中UPF提高到至少1.5倍，更优选至少3倍，最优选提高到10倍或更高。在某些优选的实施方案中，轧光前的UPF低于40，而轧光后的UPF大于40。在另一种优选的实施方案中，轧光前的UPF大于30，更优选大于50，而轧光后的UPF是轧光前UPF的3倍以上，更优选10倍以上。
优选的是，轧光步骤前的织物具有低于规定阈值的UPF，且其中所选择的轧光条件可保证轧光后织物的UPF提高到大于规定的阈值。优选的阈值包括30、40、100和1000的UPF值，具体视织物的预期用途而定。
本发明这方面的轧光织物的优选特性正如上面有关本发明第一方面每一种优选实施方案的服装织物所规定的。用于本发明这方面的的轧光方法和条件已在上面做了描述。
在第四方面，本发明还提供一种制造层合材料的方法，包括下列步骤：按本发明方法制备紫外光保护织物，随后将紫外光保护织物层合到第二织物或薄膜上。优选的是，层合材料以及第二织物或薄膜的特性符合上面涉及本发明第二方面所描述的。
在第五方面，本发明提供一种制造服装的方法，包括下列步骤：按本发明方法制备紫外光保护织物，随后将织物制成服装，其中该服装的至少一个区域由单层厚度的织物构成。优选的是，服装的特性符合前面涉及本发明第一方面所描述的。
下面将通过实例进一步描述本发明的具体实施方案和程序。
织物UPF值的测定
织物UPF值是按照AATCC试验方法183-1999，题为“按红斑(Erythemally)加权的紫外线穿透织物的透射或遮挡”(全套方法可以在线定购：www.aatcc.org/testmthds)确定的。该标准试验方法确定紫外波长范围内纺织织物遮挡或透射紫外辐射的大小，其中考虑太阳紫外线光谱能量分布和不同紫外波长对皮肤的伤害程度(红斑加权)做了适当加权处理。
扼要地，紫外辐射经样品的透射是在分光光度计或分光辐射计按已知的波长间隔测定的。紫外线保护系数(UPF)是根据检测器在没有样品情况下(检测到)的加权紫外射线辐照度与检测器在有样品时的加权紫外射线辐照度之比计算出来的。加权系数的选择反映在该波长间隔内紫外辐射所引起的皮肤潜在伤害(红斑)，并在试验方法中做了描述。检测器在没有样品时检测的加权紫外射线辐照度等于，测定各个波长间隔的光谱辐照度乘上该间隔对应的红斑权重，乘上适当太阳辐射光谱的权重函数，乘上波长间隔，最后求总和。当存在样品时，在检测器处的加权紫外辐照度等于，从样品测定各个波长间隔的光谱辐照度，乘上波长间隔，然后求和。该方法还能计算出对UVA和UyB射线的遮挡百分率。
织物空气渗透率的测定
织物空气渗透率以标准立方英尺每分钟(SCFM)为单位，采用试验方法BS EN ISO 9237在125Pa静压下测定。1SCFM等于0.028标准立方米每分钟。
实例1(对比例)
为比较的目的，研究了添加剂对未轧光机织织物测定的UPF的影响。
扼要地，机织成一种经纬纱如表1规定的织物。在每种情况下，试验纱线一律用作纬纱，将它与标准经纱交叉织造。织物经煮炼之后进行干燥，但不再进行其他处理。织物样品W7775被染成浅绿色，但其他样品一律不染色。织物不进行轧光。测定的UPF和空气渗透率数值载于表1。
可以看出，全有光(基本上不含二氧化钛)织物0，W7775和W7306的UFP值仅有3.9～5。这对于有效防太阳紫外线保护来说太低了。有趣的是，浅绿色染料在W7775中，或者荧光增白剂在W7306中的加入对UPF的影响相对地很小。
消光(1.0和1.5％二氧化钛，仅在纬纱中)织物P和Q的UPF值介于7.3～7.8。这对于防太阳紫外线有效保护来说仍然过低。
消光(1.5％二氧化钛，仅在经纱中)织物02的UPF是36.55。这虽然提供较高程度防太阳紫外线保护，但主要归功于经纱的较高纱线重量、长丝支数和织造密度所导致的织物的高二氧化钛含量。
全消光织物(1.5％二氧化钛，经纬纱兼有)样品Q2的UPF值为84.4。这显示了二氧化钛的紫外吸收作用。
然而，可以看出，未轧光织物所达到的最高UPF值低于100。更高的UPF值对于某些用途可能是可心的。另外，在某些场合，可心的是降低织物中诸如二氧化钛之类紫外吸收材料的含量，因为高消光剂含量的存在将彻底改变服装的外观。
实例2(对比例)
为比较的目的，研究了各种不同纱线长丝的支数和织造密度对多种未轧光织物的UPF测定值的影响。结果载于表2。
可以看出，增加纱线的长丝支数和增加织造密度各自都趋于增加UPF值，正如所料。然而，这两种效应都比较小，比在长丝中加入二氧化钛的效应或者轧光的效果都小得多。还应注意，重磅织物和织造得紧密的织物在最需要防太阳紫外线保护的热天不大可能被接受。
实例3
下面，研究了轧光对某些织物的UPF测定值的影响。
轧光加工采用由Kusters纺织机械公司(I-85，Zima ParkDrive，P.O.Box 6128，Spartanburg，S.C.29304，USA)制造的一对夹辊进行。夹辊的第一辊是带加热的不锈钢；第二辊不加热，但覆盖有尼龙/羊毛。轧光温度为约165℃。轧光压力为约50吨/平方英寸(6.5×106N/m2)(±10％)，轧光是在约16m/min速度的条件下进行的。
表3中给出的最后6个结果是关于成对织物的。每对织物除了轧光处理之外其他均相同。物品W6948与W6956之间的比较显示，UPF改进了12倍。物品W6946与W6938之间的比较显示UPF改进了24倍。轧光前后的织物K11478的比较显示，此种效应也延伸至针织物的轧光。
从各对织物得出以下结论，轧光对改进UPF非常显著，而且此种效果在机织和针织织物上都反映出来。不成对的织物W7494表明即便是相当轻薄的织物，经过轧光之后都能达到格外高的UPF。
上面的实施例仅为举例说明的目的给出。许多其他落在所附权利要求范围内的实施方案对于内行读者是显而易见的。
                                          表1
    样品 经纱 纬纱 织物组织      空气渗透率(立方英尺/分钟)     UPF
    O 90f102 Nylon 66有光 78f20 Nylon 66有光 经密：57.5/cm纬密：30.6/cm织物重量：____     17.3     3.9
    P 90f102 Nylon 66有光 78f20 Nylon 66消光(1％TiO2) 经密：56/cm纬密：30/cm织物重量：____     13.8     7.8
    Q 90f102 Nylon 66有光 78f20 Nylon 66消光(1.5％TiO2) 经密：58/cm纬密：30/cm织物重量：____     16.1     7.3
    O2 90f102 Nylon 66消光(1.5％TiO2) 78f20 Nylon 66有光 经密：55/cm纬密：35/cm织物重量：87.2g/m2     11.3     36.55
    Q2 90f102 Nylon 66消光(1.5％TiO2) 78f20 Nylon 66 消光(1.5％TiO2) 经密：55/cm纬密：35/cm织物重量：88.4g/m2     10.7     84.4
    W7775 50f15有光尼龙加浅绿染料 50f15有光尼龙加浅绿染料 经密：62.5/cm纬密：45/cm织物重量：97.3g/m2     -     5
    W7306 50f15有光尼龙加荧光增白剂 50f15有光尼龙加荧光增白剂 经密：61/cm纬密：47/cm织物重量：62g/m2     -     4.6
所有织物均未轧光
                                        表2
    样品   经纱 纬纱 织物组织      空气渗透率(立方英尺/分钟)     UPF
    Q2  90f102 Nylon 66消光(1.5％TiO2) 78f20 Nylon 66消光(1.5％TiO2) 经密：55/cm纬密：35/cm织物重量：88.4g/m2     10.7     84.4
    T6342  90f102 Nylon 66消光(1.5％TiO2) 78f51 Nylon 66消光(1％TiO2) 经密：55/cm纬密：35/cm/织物重量：87.5g/m2     6.83     109
    PET  90f102 Nylon 66消光(1.5％TiO2) 78f68 PET消光(1.5％TiO2) 经密：55/cm纬密：35/cm织物重量：94g/m2     4.91     138
    C1  90f102 Nylon 66有光 78f51 Nylon 66消光(1％TiO2) 经密：48/cm纬密：32/cm织物重量：78.8g/m2     18.4     10.1
    C2  90f102 Nylon 66有光 78f51 Nylon 66消光(1％TiO2) 经密：48/cm纬密：35/cm织物重量：84g/m2     10.9     14.2
    C3  90f102 Nylon 66有光 78f51 Nylon 66消光(1％TiO2) 经密：48/cm纬密：37/cm织物重量：83.6g/m2     13.0     14.5
    C4  90f102 Nylon 66有光 78f51 Nylon 66消光(1％TiO2) 经密：48/cm纬密：38/cm织物重量：86.9g/m2     10.2     15.9
所有织物均未轧光
                                        表3
    样品 经纱 纬纱 针织组织     UPF
    W7494轧光 78f51全消光Nylon(1.5％Tio2)) 78f51全消光Nylon 经密：55/cm纬密：49/cm织物重量：84.4g/m2     7724
    W6948轧光 78f51全消光 Nylon 100f51全消光AJT Nylon 经密：60/cm纬密：35/cm织物重量：90g/m2     1654
    W6956未轧光 78f51全消光 Nylon 100f51全消光AJT Nylon 经密：61/cm纬密：35/cm织物重量：92g/m2     135
    W6946轧光 78f51全消光 Nylon 135f114全消光AJT Nylon 经密：60/cm纬密：31/cm织物重量：98g/m2     5582
    W6938未轧光 78f51全消光AJT Nylon 135f114全消光AJT Nylon 经密：60纬密：31织物重量：100g/m2     234
    K11478轧光 110f92 Nylon 66消光(1.5％TiO2)与氨纶 28号针单面针织物     9241
    K11478未轧光 110f92 Nylon 66消光(1.5％TiO2)与氨纶 28号针单面针织物     459

Claims (29)

1.一种服装，它包含至少一个由单层厚度含合成聚合物长丝织物组成的区域，其中该织物至少一个表面经过了轧光处理且该织物具有至少30的按照AATCC试验方法183-1999测定的紫外线保护系数。
2.权利要求1的服装，其中该服装选自衬衫、裤子(长或短的)、泳装或帽子。
3.权利要求1或2的服装，其中该服装基本或本质上由单层厚度的该织物构成。
4.以上任何一项权利要求的服装，其中该织物具有小于150g/m2，优选介于50～100g/m2的重量。
5.以上任何一项权利要求的服装，其中该织物具有至少0.085标准立方米(3标准立方英尺)每分钟，优选至少0.14标准立方米(5标准立方英尺)每分钟的空气渗透率，按照试验方法BSEN ISO 9237在125Pa静压下测定。
6.以上任何一项权利要求的服装，其中该织物包含选自聚酰胺长丝、聚酯长丝及其混合物的合成长丝。
7.权利要求6的服装，其中该合成长丝选自尼龙6、尼龙66、尼龙46、尼龙7、尼龙10、尼龙11、尼龙610、尼龙612、尼龙12及其混合物和共聚酰胺。
8.权利要求6的服装，其中该合成长丝选自聚对苯二甲酸乙二醇酯(PET)、聚对苯二甲酸1，3-丙二醇酯(PTT)和聚对苯二甲酸1，4-丁二醇酯。
9.以上任何一项权利要求的服装，其中至少一部分合成长丝包含除了合成聚合物以外的紫外吸收剂添加剂。
10.权利要求9的服装，其中紫外吸收剂添加剂包含二氧化钛颗粒，其重量浓度介于0.1～4wt％，优选1～3wt％。
11.以上任何一项权利要求的服装，其中该织物仅在一面进行轧光处理。
12.以上任何一项权利要求的服装，其中该织物的UPF至少是40。
13.以上任何一项权利要求的服装，其中该织物的UPF至少是100。
14.以上任何一项权利要求的服装，其中该织物的UPF至少是500。
15.以上任何一项权利要求的服装，其中该织物的UPF至少是1000。
16.以上任何一项权利要求的服装，其中该织物未经染色。
17.一种多层织物，它具有按照AATCC试验方法183-1999测定的至少30的紫外线保护系数，所述多层织物包含：含合成聚合物长丝的第一织物的第一层，其中第一织物至少一个表面经过轧光处理；以及第二织物或薄膜的层，其中第二织物或薄膜层合到第一织物上。
18.权利要求17的多层织物，其中第二织物或薄膜单独的UPF至少是10。
19.权利要求17或18的多层织物，其中第二织物或薄膜包含对紫外辐射敏感的材料。
20.权利要求19的多层织物，其中对紫外辐射敏感的材料包含聚酯或聚酯衍生物。
21.权利要求17～20中任何一项的多层织物，其中第一织物采用选自熔融粘合、水力缠结、粘合剂粘合、针刺或其组合的方法粘合到第二织物上。
22.一种制备紫外光保护织物的方法，包括下列步骤：
由一种或多种复丝纱成形一种织物；以及
轧光该织物；随后
按照AATCC试验方法183-1998测定轧光后织物的紫外线保护系数(UPF)。
23.权利要求22的方法，还包括在轧光步骤前测定织物的UPF的步骤。
24.权利要求23的方法，其中轧光条件的选择应保证在所述轧光步骤中UPF增加到至少1.5倍。
25.权利要求22、23或24的方法，其中轧光步骤前织物的UPF低于规定的阈值，且其中轧光条件的选择应保证轧光后织物的UPF增加到大于规定阈值的数值。
26.一种制造多层织物的方法，包括下列步骤：
按照权利要求22～25中任何一项的方法制备紫外光保护织物，随后
将该紫外光保护织物层合到第二织物或薄膜上。
27.权利要求26的方法，它适合用来制造权利要求17～21中任何一项的多层织物。
28.一种制造服装的方法，包括下列步骤：
按照权利要求22～25中任何一项的方法制备紫外光保护织物，随后
将该织物制成服装，其中服装的至少一个区域由单层厚度织物组成。
29.权利要求28的方法，其中服装是权利要求1～16中任何一项的服装。
CNA028041844A 2001-01-26 2002-01-24 防紫外光用轧光织物 Pending CN1489651A (zh)