CN1442279A - Vacuum injection molding method for composite material - Google Patents
Vacuum injection molding method for composite material Download PDFInfo
- Publication number
- CN1442279A CN1442279A CN 03109816 CN03109816A CN1442279A CN 1442279 A CN1442279 A CN 1442279A CN 03109816 CN03109816 CN 03109816 CN 03109816 A CN03109816 A CN 03109816A CN 1442279 A CN1442279 A CN 1442279A
- Authority
- CN
- China
- Prior art keywords
- resin
- mold
- injection molding
- molding method
- runner
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a vacuum injection molding method of a composite material, belonging to the field of composite materials. The vacuum injection molding method has the advantages of simplified process and high molding efficiency. It is characterized in that: the method comprises the following steps: 1. manufacturing a soft mold with a resin runner on one side, wherein the soft mold is provided with a runner port communicated with the resin runner, and the resin runner and the soft mold are integrally formed; 2. covering one side of the soft mold with the resin runner on a hard mold with a reinforcing material laid on the surface, sealing the soft mold and the hard mold into a whole, forming a mold cavity at the joint of the soft mold and the hard mold, and arranging vacuum ports at two ends of the mold cavity; the die cavity is vacuumized by an external vacuum pump; 3. injecting resin from the runner port, sealing the runner port when the mold cavity is filled with the resin, and sealing the vacuum port after the resin is gelled; finally, the mixture is solidified, demoulded and formed. The process operation is simplified, the soft mold can replace a product mold, and a resin runner designed randomly according to the structural characteristics of the product and the soft mold can be molded at one time, so that the molding efficiency is high, and the cost is low.
Description
Technical field
The present invention relates to a kind of vacuum injection molding method, particularly a kind of vacuum injection molding method of composite material structural member.
Technical background
U.S. Pat 4902215 has been announced a kind of resin transfer molding technology in nineteen ninety, form die cavity around wherein film or vacuum bag being sealed in mould, reinforcing material is gone in the shop in the die cavity, lay resin dispersion medium between reinforcing material and film or the vacuum bag, the medium of employing is generally high permeating medium.Disclosed a kind of composite element forming method of complicated shape in another piece U.S. Pat 5052906, also be to adopt the moulding of vacuum aided injecting method, its concrete operations are will be in mold filling process, keep the flow velocity of resin and the regularity that guarantees product, lay peel ply or high permeating medium successively between the reinforcing material in vacuum bag film and die cavity.
Publication number is CN1278762, and the Chinese patent that calendar year 2001 announces is introduced a kind of large composite core structures that forms with vacuum assisted resin transfer molding, wherein adopts kiss core between fibrous material, with vacuum bag it is sealed on the surface of mould to prepare again.This method is provided with groove or the fillet on one or more main feeder conduits and the core, help that uncured resin is flow to and flow through between the core and core and mould between fibrous material in.
In the above-mentioned disclosed technology, including a slice in its mould is to be formed by pliable and tough vacuum bag film, in order to impel resin in die cavity, to flow fast and to soak into fibre reinforced materials, lay peel ply or release cloth, high permeating medium successively between reinforcing material and vacuum bag film.Also need in addition to seal with vacuum compound, to reach the requirement of vacuum aided to the mould sealing property, the price of above-mentioned fluid sealant, film, vacuum bag, high permeating medium and peel ply or release cloth is all very expensive, and the probability of recycling is very little, cause the cost height, in the actual production process of large-sized structural parts, expend lot of manpower and material resources.
Summary of the invention
The purpose of this invention is to provide a kind of process, simple to operate, low cost of manufacture, novel evacuated injection moulding method that shaping efficiency is high simplified.
For achieving the above object, the present invention has adopted following technical scheme: a kind of composite vacuum injection molding method, it is characterized in that: it comprises the steps:
1) manufacture the soft mode that is provided with resin flow channel in a side, described soft mode is provided with the runner mouth that communicates with resin flow channel, and described resin flow channel and described soft mode are one-body molded;
2) soft mode that a side of step 1) moulding is had a resin flow channel is overlying on the surface and is covered with on the die of reinforcing material, and described soft mode and described die are sealed into one, and its joint forms die cavity, and described die cavity two ends are provided with vacuum port; Described die cavity communicates with the external world by described vacuum port, by the vavuum pump of peripheral hardware described die cavity is evacuated;
3) the runner mouth that is formed by step 1) injects resin, be full of in the described die cavity behind the resin the sealing of runner mouth, behind the described resin gel with its vacuum port sealing;
4) with material cured, the demoulding of step 3) moulding.
Described soft mode is an elastomeric material, and its elastomeric material is selected silastic material for use.
Described reinforcing material adopts a kind of in fiber cloth, carbon fiber or the glass fibre; Described resin adopts the liquid thermosetting resin, and described liquid thermosetting resin is selected unsaturated polyester resin or epoxy resin for use.
Described die is a kind of in fiberglass or the metal material.
Described solidification temperature, hardening time and demould time, its hardening time and temperature are determined according to the requirement of the self performance of used resin material.
The present invention adopts said method, and it has the following advantages:
1. directly on soft mode, offer resin flow channel, replaced the use of special-purpose permeating medium and peel ply, reduced manufacturing cost, simplified technological operation with soft mode.
2. on soft mode, design resin flow channel and moulding simultaneously according to products characteristics, the resin injection rate is accelerated, improved shaping efficiency through vacuumizing.
3. soft mode can use repeatedly repeatedly, and is indeformable, and not can with the die adhesion.
4. remove the placement process of permeating medium and peel ply from, improved the stability of technology.
5. soft mode can compress reinforcing material during owing to moulding, has reduced product internal voids rate, and the density of product is improved.
Description of drawings
Fig. 1 is a molding structure schematic diagram of the present invention
Fig. 2 is a resin flow channel structural representation of the present invention
The specific embodiment
As shown in Figure 1: the silicon rubber that the present invention adopts has better elastic, can be processed into the soft mode 1 of different shape on demand, and silicon rubber itself also has certain rigidity, therefore can protect the shape invariance of product.In moulding, the silicon rubber inboard has resin flow channel, with its resin flow channel and mantle 1 moulding simultaneously; Soft mode 1 inboard after the moulding is overlying on die 6 upsides that the surface is covered with fiber glass reinforcement, with sealing strip 4 sealings, locks with flange around it again; Vacuum port 5 is left in both sides, its vacuum port 5 joins with the peripheral hardware vavuum pump, soft mode 1 forms die cavity 3 with the resin flow channel that die 6 is covering in the face, vavuum pump with peripheral hardware is evacuated die cavity 3, and the negative pressure of vacuum in the die cavity 3 is adsorbed on silicon rubber soft mode 1 on the die 6 tightly, with the fiber glass reinforcement compacting in the die cavity 3, reduced porosity, the content of the fibre reinforced materials in the goods has been improved, make the structure of its goods fine and close more, improved the performance of product.
As shown in Figure 2, peculiar performance of silicon rubber self and the design feature that will make product, in moulding Fig. 1 in the machine silicon rubber soft mode 1, open the runner 9 of certain size on its surface, runner is the groove shape, divide resin sprue 7 and auxilliary runner 8, when resin after runner mouth 2 injects the die cavity 3 of Fig. 1, to at first be full of sprue 7, be full of auxilliary runner 8 and then, soak into reinforcing material gradually, resin is full of rear enclosed runner mouth, product is through curing, stripping forming, and the time of curing and temperature determine according to the characteristic that the resin that is adopted self is had.
Claims (6)
1. composite vacuum injection molding method, it is characterized in that: it may further comprise the steps:
1) manufacture the soft mode that is provided with resin flow channel in a side, described soft mode is provided with the runner mouth that is communicated with resin flow channel, and described resin flow channel and described soft mode are one-body molded;
2) soft mode that a side of step 1) moulding is had a resin flow channel is overlying on the surface and is covered with on the die of reinforcing material, and described soft mode and described die are sealed into one, and its joint forms die cavity, and described die cavity two ends are provided with vacuum port; Described die cavity communicates with the external world by described vacuum port, by the vavuum pump of peripheral hardware described die cavity is evacuated;
3) the runner mouth that is formed by step 1) injects resin, be full of in the described die cavity behind the resin the sealing of runner mouth, behind the described resin gel with its vacuum port sealing;
4) with material cured, the demoulding of step 3) moulding.
2. composite vacuum injection molding method according to claim 1 is characterized in that: described soft mode is an elastomeric material.
3. composite vacuum injection molding method according to claim 2 is characterized in that: described elastomeric material is a silastic material.
4. composite vacuum injection molding method according to claim 1 is characterized in that: described reinforcing material is a kind of in fiber cloth, carbon fiber or the glass fibre, and described resin is the liquid thermosetting resin.
5. composite vacuum injection molding method according to claim 4 is characterized in that: described liquid thermosetting resin is unsaturated polyester resin or epoxy resin.
6. composite vacuum injection molding method according to claim 1 is characterized in that: described die adopts a kind of in fiberglass or the metal material.