CN1317332C - 水性沥青绝缘胶 - Google Patents
水性沥青绝缘胶 Download PDFInfo
- Publication number
- CN1317332C CN1317332C CNB2004100845038A CN200410084503A CN1317332C CN 1317332 C CN1317332 C CN 1317332C CN B2004100845038 A CNB2004100845038 A CN B2004100845038A CN 200410084503 A CN200410084503 A CN 200410084503A CN 1317332 C CN1317332 C CN 1317332C
- Authority
- CN
- China
- Prior art keywords
- deionized water
- powder
- insulating cement
- oxygen base
- acid ester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种水性沥青绝缘胶,其特征在于:该绝缘胶的成分和各成分的重量百分比为:去离子水 40~50%;石油沥青 25~33%;石棉粉 10~17%;云母粉 4~8%;双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯 1~4%。本发明主要解决其抗冻性、无毒、无味、施工工艺简单、可在潮湿基面上施工的技术问题,其次是解决提高抗静电性能的技术问题。
Description
技术领域:
本发明是关于绝缘材料,尤其是关于一种用于管道绝缘的水性沥青绝缘胶。
现有技术:
现有的用于输油、气、水等流体的管道,其外表所使用的绝缘材料多为水性环氧树脂绝缘胶,但其在实际使用存在如下问题:
1、双组分的现场施工工艺复杂,对施工基面湿度要求高,当施工基面潮湿时不能施工;而且其粘附性差,增加施工的难度。
2、需使用二甲苯、丁醇等有机溶剂,具有较大毒性和呛人的弃味,不仅对施工人员健康有害,也对施工现场周围环境产生污染。
3、抗冻性差,环境温度在零下20℃左右时就易开裂、限制了使用区域范围。
4、延伸性差,会因管道基材的热胀冷缩而开裂、剥落,失去绝缘保护作用。
5、体积电阻率较小,在4×108Ω.m左右,抗静电性能较低。
发明内容:
本发明的目的在于提供一种水性沥青绝缘胶,主要解决其抗冻性、无毒、无味、施工工艺简单、可在潮湿基面上施工的技术问题,其次是解决提高抗静电性能的技术问题。
本发明解决上述技术问题的技术方案如下:
一种水性沥青绝缘胶,其特征在于:该绝缘胶的成分和各成分的重量百分比为:
去离子水 40~50%; 石油沥青 25~33%;
石棉粉 10~17%; 云母粉 4~8%;
双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯 1~4%。
其特征在于:该云母粉为325目片状结构绝缘云母粉。
另一种水性沥青绝缘胶,其特征在于:该绝缘胶的成分和各成分的重量百分比为:
去离子水 40~50%; 石油沥青 25~33%;
石棉粉 10~17%; 云母粉 4~8%;
双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯 1~4%。
硬脂酰胺丙基-β-羟乙基铵二氢磷酸盐 1~3%。
用于制造上述的水性沥青绝缘胶的制造方法,其特征在于:取2/3的去离子水先与石棉粉、云母粉和双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯在反应釜中搅拌均匀,再将加热至≥170℃的石油沥青徐徐加入搅拌中的浆料,待其充分化分散后,加入温度控制在68~72℃的剩余去离子水继续搅拌5分钟。
用于制造上述另一种水性沥青绝缘胶的制造方法,其特征在于:该硬脂酰胺丙基-β-羟乙基铵二氢磷酸盐与2/3的去离子水、石棉粉、云母粉、双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯一起先在反应釜中搅拌均匀,再将加热至≥170℃的石油沥青徐徐加入搅拌中的浆料,待其充分乳化分散后,加入温度控制在68~72℃的剩余去离子水继续搅拌5分钟。
本发明的优点为:
1、抗冻性能好,在-20℃时不开裂。
2、采用有机螯合型的双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯作为偶联剂,对石油沥青、石棉粉进行改性处理后,使本发明兼有合成树脂或橡胶、和沥青的双重优点,提高了其与基材的粘结性能。而且防水、抗渗透、耐腐蚀、耐老化、富有弹性、高温不流淌、低温柔性好。
3、作为填料的石棉粉经表面改性处理后,使胶层透气性好,对水蒸气渗透性大,使本发明在潮湿的基面上亦能施工,从而缩短了施工期。
4、延伸性好,内应力小。
5、加入硬脂酰胺丙基-β-羟乙基铵二氢磷酸盐,使本发明的体积电阻率达9.3×1011Ω.m,为国标值的93倍,可使管道的使用年限延长。
6、本发明为单组分,简化了施工程序,可提高施工效率。
7、安全无毒、无味、无环境污染。
8、成本低。
具体实施方式:
本发明由去离子水、石油沥青、石棉粉、云母粉、双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯(商品代号GN-36)组成,其中石棉粉作为填料,云母粉作为绝缘材料,双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯作为偶联剂;云母粉采用325目的片状结构绢云母粉。各组成的重量百分比为:
去离子水 40~50%; 石油沥青 25~33%;
石棉粉 10~17%; 云母粉 4~8%;
双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯 1~4%。
为提高本发明的体积电阻率,可加入重量百分比1~3%的硬脂酰胺丙基-β-羟乙基铵二氢磷酸盐。
本发明的制作时,先取2/3的去离子水,与称量的石棉粉、云母粉、双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯在反应釜内搅拌均匀成浆料;再将加热至>170℃的石油沥青徐徐加入反应釜中处于搅拌状态的浆料内,并搅拌至充分乳化分散的状态,这一工序时间愈长改性反性的效果愈佳,一般应不少于30分钟;最后将剩余1/3的去离子水加热至68~72℃左右倒入反应釜中,继续搅拌约5分钟。硬脂酰胺丙基-β-羟乙基铵二氢磷酸盐在上述浆料阶段初始即应加入。
现就本发明几个实施例与达到的性能指标,对本发明作进一步说明。
实施例1:去离子水 50%; 石油沥青 33%;
石棉粉 10%; 云母粉 4%;
双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯 1%;
硬脂酰胺丙基-β-羟乙基铵二氢磷酸盐 2%。
实施例2:去离子水 40%; 石油沥青 30%;
石棉粉 17%; 云母粉 8%;
双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯 2%;
硬脂酰胺丙基-β-羟乙基铵二氢磷酸盐 3%
实施例3:去离子水 49%; 石油沥青 25%;
石棉粉 16%; 云母粉 6%;
双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯 3%;
硬脂酰胺丙基-β-羟乙基铵二氢磷酸盐 1%。
实施例4:去离子水 45%; 石油沥青 28%;
石棉粉 14%; 云母粉 6%;
双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯 4%;
硬脂酰胺丙基-β-羟乙基铵二氢磷酸盐 3%。
经有关部门实测,本发明抗冻性在-20℃20次无开裂,粘结力为0.45Mpa,热、碱、紫外处理后的延伸性分别达4.3、6.0、4.7mm,为标准值的1.5~2倍;特别是在加入重量百分比1~3%的硬脂酰胺丙基-β-羟乙基铵二氢磷酸盐时其体积电阻率特佳为9.3×1011Ω.m,是标准值的93倍,与现技术的4×108Ω.m相比要大了三个数量级。
Claims (5)
1、一种水性沥青绝缘胶,其特征在于:该绝缘胶的成分和各成分的重量百分比为:
去离子水 40~50%;石油沥青 25~33%;
石棉粉 10~17%;云母粉 4~8%;
双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯 1~4%。
2、根据权利要求1所述的水性沥青绝缘胶,其特征在于:该云母粉为325目片状结构绢云母粉。
3、一种水性沥青绝缘胶,其特征在于:该绝缘胶的成分和各成分的重量百分比为:
去离子水 40~50%;石油沥青 25~33%;
石棉粉 10~17%;云母粉 4~8%;
双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯 1~4%;
硬脂酰胺丙基-β-羟乙基铵二氢磷酸盐 1~3%。
4、用于制造权利要求1或2所述的水性沥青绝缘胶的制造方法,其特征在于:取2/3的去离子水先与石棉粉、云母粉和双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯在反应釜中搅拌均匀,再将加热至≥170℃的石油沥青徐徐加入搅拌中的浆料,待其充分乳化分散后,加入温度控制在68~72℃的剩余去离子水继续搅拌5分钟。
5、用于制造权利要求3所述的水性沥青绝缘胶的制造方法,其特征在于:该硬脂酰胺丙基-β-羟乙基铵二氢磷酸盐与2/3的去离子水、石棉粉、云母粉、双(二辛基焦磷酰氧基)羟乙酸酯钛酸酯一起先在反应釜中搅拌均匀,再将加热至≥170℃的石油沥青徐徐加入搅拌中的浆料,待其充分乳化分散后,加入温度控制在68~72℃的剩余去离子水继续搅拌5分钟。