CN1245933C - 化妆品 - Google Patents
化妆品 Download PDFInfo
- Publication number
- CN1245933C CN1245933C CNB028031016A CN02803101A CN1245933C CN 1245933 C CN1245933 C CN 1245933C CN B028031016 A CNB028031016 A CN B028031016A CN 02803101 A CN02803101 A CN 02803101A CN 1245933 C CN1245933 C CN 1245933C
- Authority
- CN
- China
- Prior art keywords
- powder
- metal
- oxide
- cosmetics
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供一种含有粉末的化妆品,其具有金属薄膜的闪光特性并且不易于沥出金属离子,从而也不易于引起变色或变性,并且不易于导致金属过敏反应。该化妆品中所含的粉末包括基底材料,并且在该基底材料上以金属薄膜和金属氧化物薄膜的顺序形成薄膜。
Description
技术领域
本发明涉及一种含有表面覆盖有金属薄膜的粉末且具有闪光表观的彩妆用化妆品。
背景技术
将彩妆化妆品涂敷在指甲上、眼睛四周或在嘴唇上,由此可以着色或改变这些机体部位的印象。近年来,流行趋势是希望产生闪光感,并且因此对含金属薄片剂的化妆品的需求在增加。所含的基底材料带有金属涂层的粉末,尤其是所含基底材料为小片状的(例如云母或玻璃薄片)带有金属涂层的颗粒时,将具有闪烁的高金属光泽,并且当作为金属薄片剂(laméagent)掺混在化妆品中时,具有显著效果。日本待公开专利公报(Kokai)号62-108805公开了一种其中混合有含贵金属颜料的化妆品,该颜料通过在云母的表面上利用化学镀方法涂覆上金、铂、钯、银等来获得。日本待公开专利公报(Kokai)号1-208324公开了制备有银物质涂层的无机粉末,通过水解银盐使氧化银和/或氢氧化银沉积在无机粉末(例如云母、滑石、玻璃薄片或铝箔)的表面上,并且随后进行热处理,并且称这种粉末是具有优异彩妆效果的化妆品用颜料。此外,日本待公开专利公报(Kokai)号2001-89324公开了一种化妆品组合物,其中含有表面上具有银、镍、铬、钼等的金属薄膜的玻璃微粒。
然而,这些具有金属薄膜的粉末(颜料)由于最外层表面是金属,因此存在的问题是在混合到化妆品中时,化妆品中的有机组分可能由于金属离子的沥出或催化功能的表现而变色或变性。此外,金属离子可能会引起金属过敏反应,并且虽然贵金属例如铂和金不容易电离,但据报导当使用中人体皮肤与例如化妆品直接接触时,即便是金属的轻微沥出也可能导致金属过敏反应。此外,在基底材料的表面上镀有银的情况中,银以小微粒的形式附着,因此尽管是轻微的,也会在镀层的表面形成起伏。当粉末混合在化妆品中时,这些轻微的表面起伏对化妆品在皮肤或指甲上的感觉或铺展性具有不利影响。
发明内容
本发明的完成着眼于对上述问题的解决。本发明的一个目的是提供一种化妆品,其中含有具有金属薄膜的闪光特性并且不易于金属离子的沥出的粉末,由此该化妆品不易于引起变色或变性,并且在皮肤或指甲上的感觉和铺展性也优良。
为了达到上述目的,按照本发明的一个方面,提供一种含有粉末的化妆品,该粉末含有基底材料,并且在该基底材料上以金属薄膜和金属氧化物薄膜的顺序形成薄膜,
其中所述粉末的金属薄膜具有至少一种选自银、金、铂、钯、镍、铜、铬、钼、锡、镁、铝和哈斯特洛伊耐蚀镍基合金的金属作为其主要组分,
其中所述粉末的所述金属氧化物薄膜具有至少一种选自二氧化硅、氧化铝、氧化锆、氧化锌和氧化铈的金属氧化物作为主要组分,
其中以形成所述金属氧化物薄膜之前的重量计,所述粉末具有含量为0.1-30重量%的附着在其表面上的所述金属氧化物薄膜。
此外,在本发明的一个方面,粉末的基底材料优选含有平均厚度为0.5-8.0μm且平均微粒直径为5-1,000μm的玻璃薄片。
实施本发明的最佳方式
现在详细说明本发明的实施方式。然而,本发明并不限于下列实施方式。
本发明涉及一种其中混合有粉末的化妆品,其中在基底材料上形成的金属薄膜进一步被金属氧化物薄膜所覆盖,由此防止金属离子的沥出,从而防止化妆品的变色/变性和金属过敏反应的出现,同时仍然具有高度闪烁的光泽。
金属薄膜表现出特有的金属光泽,因此含有表面上具有金属薄膜的粉末基底材料的材料可以用作闪光颜料。然而,除非解决上述金属离子的沥出的问题,这种材料无法用作直接涂敷在人体皮肤上的化妆品的原料。因此在该金属薄膜上进一步提供金属氧化物薄膜,由此防止金属离子的沥出,而并不损害该金属薄膜的金属光泽。
只要金属氧化物薄膜比金属薄膜处于粉末的更外层,上述功能就可以得到实现。因此必须按照这种顺序形成金属薄膜和金属氧化物薄膜,但在金属薄膜和金属氧化物薄膜之间可以具有中间层薄膜,和/或在基底材料和金属薄膜中间可以形成基础薄膜,和/或金属薄膜和金属氧化物薄膜可以反复多次构建在彼此的顶部。
此外,如果金属氧化物覆盖在银镀层上,则该金属氧化物薄膜可以弄平镀层上的表面起伏,并且因此提高粉末的表面平滑度。因此,可以防止粉末的粘着或附聚,改善含粉末化妆品在皮肤和指甲上的感觉,改进铺展性。
只要所述基底材料是粉末,对其类型或微粒大小没有具体限制。例如,可以使用市售的已知粉末,例如云母、滑石、高岭土、铝片、硫酸钡、二氧化硅薄片、氧化铝薄片、氧氯化铋等。特别是,优选平均厚度在0.5-8.0μm范围内且平均微粒直径在5-1,000μm范围内的玻璃薄片。玻璃薄片具有作为化妆品原料的理想特性,例如由于表面平滑度高而金属光泽更强,和由于是薄片而使在皮肤上的粘着和铺展性较好。此外,如果玻璃薄片具有上述厚度,则可以确保在混合或捏合化妆品时所需的强度,因此微粒直径应不能过小。此外,如果玻璃薄片具有上述微粒直径,则由于这个原因和表面的平滑度,玻璃薄片能够在化妆品中充分流动,因此将可以很好地粘着和附着于皮肤。在需要将化妆品涂敷在纹理上的情况中,优选微粒直径稍大的化妆品,而在需要覆盖性能的情况中,优选微粒直径稍小的化妆品。按照这个目的,可以一起混合使用具有不同微粒直径的玻璃薄片。如果使用具有上述厚度和微粒直径的玻璃薄片,则可以获得足够的闪光性并且无需在彼此之上涂敷多个化妆品层。
对金属薄膜的类型没有特别限制,但作为其主要成分金属薄膜具有至少一种选自银、金、铂、钯、镍、铜、铬、钼、锡、镁、铝的金属,并优选哈斯特洛伊耐蚀镍基合金。其中,贵金属,即银、金、铂和钯在闪光度上优异,而镍在闪光度和颜色变化上优异。
具有所述金属薄膜的基底材料粉末的实例是,例如,具有一个以银作为其薄膜的主要成分的Metashine PS系列(Nippon SheetGlass Co.,Ltd.制备的Metashine RCFSX-5480PS,RCFSX-5230PS,RCFSX-5150PS,RCFSX-5090PS02,RCFSX-5030PS,REFSX-2040PS,REFSX-2025PS,REFSX-2015PS等),具有一个以金作为其薄膜的主要成分的Metashine GG系列(Nippon Sheet Glass Co.,Ltd.制备的Metashine RCFSX-5150GG等),具有以镍作为其薄膜的主要成分的Metashine NS系列和NB系列(Nippon Sheet Glass Co.,Ltd.制备的Metashine RCFSX-5150NS,RCFSX-5230NS,RCFSX-5150NS,RCFSX-5090NS等),和具有一个以哈斯特洛伊耐蚀镍基合金作为其薄膜的主要成分的Crystal Star系列(Toyo Aluminium K.K.制造的Crystal Star GF2525等)。
所述的金属氧化物薄膜优选是具有至少一种选自二氧化硅、氧化铝、氧化锆、氧化锌和氧化铈的金属氧化物作为其主要成分的薄膜。该金属氧化物薄膜可以是单层薄膜,或者可能是具有多层结构的薄膜。此外,在与上述原料混合并由此使主要成分是两种或多种金属氧化物的复合材料的情况中,金属氧化物的结合形式可以适当选择,其目的在于提高对金属薄膜的粘着或者与化妆品中其它材料的相容性。在厚度不超过数个微米的情况下,任何金属氧化物薄膜都是透明的,并且化学稳定性较高,因此可以抑制金属离子的沥出,而且不损害金属薄膜的金属光泽。
以形成金属氧化物薄膜之前的重量计(该重量包括基底材料和金属薄膜,并且在一些情况中还包括中间薄膜,和/或基础薄膜等),优选金属氧化物薄膜的附着用量为0.1-30重量%。在该附着比例小于0.1重量%的情况中,防止金属离子沥出的功能将受到影响。另一方面,如果附着用量超过30重量%时,金属氧化物薄膜倾向于裂开和剥离。此外,也将使原料用量增加,因此使成本升高。另外注意,通过适当调整金属氧化物薄膜的厚度,通过反射光的干扰可以改变其外观,并且在金属薄膜的金属光泽方面可以导致色彩的细微改变。
对形成金属薄膜的方法和形成金属氧化物薄膜的方法没有特别限制;可以采用一种在粉末上形成薄膜的已知方法,例如在粉末的表面上由金属盐沉积氧化物的方法,溶胶-凝胶法,CVD法,或LPD法。例如,下面是形成二氧化硅薄膜的方法:如日本审定专利申请公报(Kokoku)号46-9555所述,一种将硅酸钠(水玻璃)在碱环境下加入到粉末的浆液中,由此将二氧化硅沉积在粉末的表面(金属盐法)的方法;如日本审定专利申请公报(Kokoku)号48-32415所述,一种将粉末和四烷氧基硅烷的混合物置于碱性溶液或碱溶液中,通过水解四烷氧基硅烷在粉末的表面上沉积二氧化硅薄膜(溶胶-凝胶法)的方法;如日本待公开专利公告(Kokai)号3-066764所述,一种使粉末悬浮在氟硅酸溶液中,并且随后通过加入硼酸或铝或升温使平衡移动,由此在粉末上形成二氧化硅薄膜(LPD法)。也可以采用类似方法形成其它的金属氧化物的薄膜,例如氧化铝、氧化锆、氧化锌或氧化铈。
对化妆品的类型没有特别限制,只要它是含有金属薄片剂的化妆品,即闪光颜料。实例是指甲化妆品例如指甲色料或指甲涂层,眼用化妆品例如眼影、眼线、睫毛油或眉笔、粉底、胭脂、颜彩、唇膏、口红,笔形彩妆化妆品例如眼线笔或唇线笔,沉淀型彩妆化妆品其中金属薄片剂在水或溶剂中是处于沉淀状态并且其在使用时在适当振摇后使用,等等。
所述的粉末在化妆品中的含量必须在0.1-100重量%(此后简写为%)的范围内。颜料的含量一般是由化妆品的配方决定的,但含量没有常规限定。在各种不同制剂中粉末的优选含量如下所述。对于指甲化妆品例如指甲色料,优选0.1-50%,更优选3-40%。当小于0.1%时,粉末作为闪光颜料的功能将受到影响,而大于50%时,化妆品的涂敷性能可能会变差。对于通过将粉末在加压下干燥填充或者通过通过用挥发性溶剂湿法填充粉末及随后干燥来获得的固体粉末化妆品例如胭脂或眼影,优选5-80%,并且更优选10-60%。如果粉末含量在此范围内,粉末的闪光性很容易显现,并且使用时感觉良好。在作为疏松粉末使用的粉状化妆品例如眼影或颜彩的情况中,当使用时化妆品与人体皮肤上存在的油混合,因此粉末含量可以是100%。在油性固体化妆品例如唇膏或油性眼影的情况中,优选1-60%,和更优选3-50%。当小于1%时,闪光性将受到影响,而当大于60%时,高温下的流动性会变差,从模压性能的角度考虑这是所不希望的。在通过用表面活性剂使水相和油相一起乳化获得的乳化彩妆化妆品的情况中,优选1-50%,和更优选3-40%。当小于1%时,闪光性易于变得不充分,而当大于50%时,乳化将变得不稳定。在水基彩妆化妆品例如含水睫毛膏或含水凝胶的情况中,其中水中混合有水溶性树脂、含水树脂乳液或增稠剂等,优选0.1-60%,和更优选1-40%。当小于0.1%时,闪光性易于变不充分,而大于60%时,从使用方面考虑将变得不理想。
本发明的粉末可以适当按照化妆品的目的进行疏水改性。实施疏水改性的方法的实例包括用聚硅氧烷化合物例如甲基氢聚硅氧烷、高粘度聚硅氧烷油或聚硅氧烷树脂处理,用表面活性剂例如阴离子表面活性剂或阳离子表面活性剂处理,用大分子化合物例如尼龙、聚甲基丙烯酸甲酯、聚乙烯、氟化树脂或聚氨基酸处理,用含全氟基团的化合物、卵磷脂、胶原、金属皂、亲脂性蜡或多元醇偏酯或全酯处理,或这些处理的结合形式。
化妆品中常用的其它组分可以根据需要混合在该化妆品中。这些其它组分的实例是无机粉末,有机粉末,颜料,着色剂,油性组分,有机溶剂,树脂,增塑剂,等等。
譬如,无机粉末的实例是滑石、高岭土、绢云母、白云母、金云母、鳞云母、黑云母、锂云母、蛭石、碳酸镁、碳酸钙、硅藻土、硅酸钡、硫酸钡、硅酸锶、钨酸金属盐、二氧化硅、羟基磷灰石、沸石、氮化硼、陶瓷粉等。
有机粉末的实例是尼龙粉、聚乙烯粉、聚苯乙烯粉、苯并胍胺粉、聚四氟乙烯粉、二苯乙烯苯聚合物粉、环氧树脂粉、丙烯酸粉等。
颜料的实例是微晶纤维素、无机白色颜料(例如氧化钛和氧化锌)、无机红色颜料(例如红氧化铁和钛酸铁)、无机褐色颜料(例如γ-氧化铁)、无机黄色颜料(例如黄色氧化铁和黄土)、无机黑色颜料(例如黑色氧化铁和碳黑)、无机紫色颜料(例如锰紫色和钴紫)、无机绿色颜料(例如氧化铬、氢氧化铬和钛酸钴)、无机蓝色颜料(例如群青和铁蓝)、珍珠颜料(例如氧化钛涂层的云母、氧化钛涂层的氯氧化铋、氯氧化铋、氧化钛涂层的滑石)、金属粉末颜料(例如铝粉和铜粉),等等。
着色剂的实例是有机颜料,例如201号红,202号红,204号红,205号红,220号红,226号红,228号红,405号红,203号橙,204号橙,205号橙,401号黄和404号蓝,无机颜料例如锆、钡和铝色淀例如3号红,104号红,106号红,227号红,230号红,401号红,505号红,205号橙,4号黄,5号黄,202号黄,203号黄,3号绿和1号蓝,天然着色剂例如叶绿素和β-胡萝卜素,等等。
油性组分的实例是角鲨烷、液体石蜡、凡士林、微晶蜡、石蜡、地蜡、肉豆蔻酸、棕榈酸、硬脂酸、油酸、异硬脂酸、鲸蜡醇、十六烷醇、油醇、2-乙基己酸鲸蜡酯、棕榈酸2-乙基己酯、2-肉豆蔻酸辛基十二烷基酯、新戊二醇二2-乙基己酸酯、三-2-乙基己酸甘油酯、油酸2-辛基十二烷基酯、肉豆蔻酸异丙酯、甘油基三硬脂酸酯、椰油甘油三酯、橄榄油、鳄梨油、蜂蜡、肉豆蔻酸肉豆蔻酯、多种烃(例如貂油和羊毛脂)、硅油、高级脂肪酸、油和脂肪的酯、高级醇、蜡等。
有机溶剂的实例是丙酮、甲苯、乙酸丁酯和其它乙酸酯,等等;树脂的实例是醇酸树脂、脲醛树脂等;增塑剂的实例是樟脑、乙酰基三丁基柠檬酸酯,等。
此外,紫外线吸收剂、抗氧剂、防腐剂、表面活性剂、湿润剂、香料、水、醇、增稠剂等也可以适当选择并且混合在其中。
对化妆品的配制没有特定限制;实例是熟知的形式例如粉末、饼、笔、棒、软膏、液体、奶液或膏。
现在通过实施例对本发明进行更加详细的说明;然而,只要不偏离本发明的范围,本发明不受下列实施例限定。
实施例1-6
首先,将带有银膜的选自Metashine PS系列玻璃薄片的一种合适的材料用作带有金属薄膜的基底材料,并采用下面的方法在其表面形成二氧化硅薄膜。
将50g的Metashine PS悬浮在0.5升的纯水中,并且同时用水浴保持在75℃的温度下,适当称量出硅酸钠溶液(二氧化硅固体含量37.1%,由Wako Pure Chemical Industries,Ltd.制备)且随后用纯水10倍稀释得到一种溶液,将该溶液加入到上述悬浮液中。同时用3.5重量%的盐酸使该悬浮液的pH维持在9.2-9.4。加入完毕,在75℃下持续搅拌30分钟。此后,用滤纸过滤该悬浮液,回收过滤出的固体,并且在用水洗涤并使pH呈中性之后,在100℃下干燥2小时,由此得到银涂覆的玻璃薄片,即其表面上具有二氧化硅的粉末。二氧化硅表面附着比率在各实施例中相对于Metashine PS计算是在1-20重量%的范围内,并且具体如下表1所示。
制成的多种粉末用下列方法评估。
银沥出试验1(在水作用下沥出)
将5g的上述各种粉末加入到95g的95℃的蒸馏水中,使固体含量是5重量%,搅拌30分钟同时温度保持在95℃下,然后进行1小时沥出试验。试验之后,用0.23μm滤膜过滤,滤液中银的含量是通过ICP光发射光谱仪测定,并且计算出每单位重量固体成分的沥出率。
银沥出试验2(在有机溶剂作用下沥出)
将5g的各种上述粉末在60℃下加入到95g的1∶1(重量比)的乙酸乙酯和乙酸丁酯的混合溶剂中,使固体含量是5重量%,搅拌30分钟同时温度保持在60℃下,并且进行6小时试验。试验之后,沥出率按照上述方法测定。
有机物变色试验
将乙酸丁酯、乙酸乙酯、硝基纤维素和所述粉末混合并搅拌使乙酸丁酯∶乙酸乙酯∶硝基纤维素∶粉末比率为50∶25∶20∶5(重量比),将该样品置于10ml玻璃瓶中且密封该瓶。用200W水银灯照射该瓶24小时,目测观察溶液颜色的变化。结果显示在下表1中。通过这种变色试验,可以检验出当粉末混合到含有机物的化妆品中时是否会变色。
表1
实施例 | 1 | 2 | 3 | 4 | 5 | 6 |
平均厚度(μm)平均粒径(μm)二氧化硅薄膜重量%银沥出率1(ppm)银沥出率2(ppm)有机物的变色 | 5.048012.21.2无 | 5.09032.01.2无 | 5.03031.50.8无 | 1.38033.10.7无 | 1.31563.10.6无 | 0.820153.30.8无 |
对照实施例1-3
对不同类型的没有形成二氧化硅薄膜的Metashine PS进行上述实施例的试验。结果如下表2所述。
表2
对照实施例 | 1 | 2 | 3 |
平均厚度(μm)平均粒径(μm)二氧化硅薄膜重量%银沥出率1(ppm)银沥出率2(ppm)有机物的变色 | 5.09009.23.3轻微的黄色 | 1.3800131.21.9黄色 | 1.3150261.11.4黄色 |
由表1可以看出对于所有其上具有二氧化硅薄膜的粉末,银进入水的沥出率非常低,不超过3.3ppm,并且银进入有机溶剂的沥出率也非常低,不超过1.2ppm。此外,可以看出由于金属离子的沥出受到抑制,因此没有出现有机物的变色作用。
另一方面,从表2可以看出对于没有二氧化硅薄膜的玻璃薄片,由于银薄膜暴露,银进入水中的沥出率非常高,在9-261ppm,并且银进入有机溶剂的沥出率是1.4-3.3ppm,即是采用二氧化硅薄膜情形的数倍。所以可以看出,在将没有二氧化硅薄膜的玻璃薄片混合到化妆品中的情形中,由于金属离子的沥出,诱发金属过敏反应的可能性非常高,并且化妆品将会变色。
如上所述,可以看出在金属薄膜上提供金属氧化物薄膜,可以抑制金属离子的沥出,并且同时可以防止有机物的变色。
实施例7
将50g的平均厚度为1.3μm且平均粒径为80μm的银涂覆的玻璃薄片(Nippon Sheet Glass Go.Ltd.制造的Metashine PS)悬浮在0.5升纯水中,并且用水浴保持在75℃的温度下,通过用纯水10倍稀释硅酸钠溶液(二氧化硅固体含量37.1%,由Wako Pure ChemicalIndustries,Ltd.制备)得到一种溶液,将该溶液加入到上述悬浮液中。这是在用3.5重量%的盐酸使该悬浮液的pH维持在9.2-9.4的同时进行的。加料之后,在75℃下持续搅拌30分钟,由此在银薄膜上形成二氧化硅薄膜。二氧化硅薄膜的附着比率相对于银涂覆的玻璃薄片计算是3重量%,其相当于上述实施例4。随后,将用纯水稀释20倍的1.8g氯化铝六水合物得到的溶液缓慢滴加其中。同时用5重量%氢氧化钠水溶液使pH保持在5.3-5.7。加入后,在75℃下持续搅拌30分钟,由此形成氧化铝薄膜(按氧化铝计算,相当于银涂覆玻璃薄片的2重量%)。此后,用滤纸过滤该悬浮液,收集过滤出的固体,在用水洗涤并使pH呈中性之后,在100℃下干燥2小时,由此得到珠光玻璃薄片,即一种具有包含两层(也就是二氧化硅薄膜和氧化铝薄膜)的金属氧化物薄膜的粉末。
对于这些具有二氧化硅-氧化铝双层涂层薄膜的银涂覆玻璃薄片,银进入水中的沥出率是2.5ppm,而银进入有机溶剂中的沥出率是0.5ppm,因此可以看出这些沥出率比实施例4的低。此外,没有观察到有机物的变色现象。
实施例8
将50g的具有5.0μm平均厚度和90μm平均粒径的镍涂覆玻璃薄片(Nippon Sheet Glass Go.Ltd.制造的Metashine NB)悬浮在0.5升纯水中,并且用水浴保持在75℃的温度下,通过用纯水稀释10倍的2.6g氧氯化锆得到的溶液缓慢滴加到该悬浮液中。同时用1重量%氢氧化钠溶液保持该悬浮液的pH在约3。在75℃下持续搅拌30分钟,随后通过加入上述氢氧化钠溶液使该悬浮液的pH升高至7.2,并且在75℃下持续搅拌30分钟。此后,用滤纸过滤该悬浮液,收集过滤出的固体,在用水洗涤并使pH呈中性之后,在100℃下干燥2小时,由此得到镍涂覆的玻璃薄片,即一种具有氧化锆薄膜(按氧化锆计算,相当于镍涂覆的玻璃薄片的2重量%)的粉末。
对于这些具有氧化锆薄膜的镍涂覆玻璃薄片,银进入水中的沥出率是1.8ppm,并且银进入有机溶剂中的沥出率是0.3ppm。
作为对照,对于没有氧化锆薄膜的镍涂覆的玻璃薄片,进入水中的沥出率是2.5ppm,和进入有机溶剂中的沥出率是0.7ppm。此外,在有机物变色试验中,对于具有氧化锆薄膜的的镍涂覆玻璃薄片,观察不到变色现象。因此可以看出氧化锆薄膜能有效抑制镍离子的沥出。
接着,进行一个使用感觉的研究并且也进行有关其中混合有表面上具有金属氧化物薄膜的金属涂覆的玻璃薄片作为金属薄片类闪光颜料的化妆品的研究。对化妆品的评估由10名评审人员对于评估项目在5个水平上进行感觉评估,数值结果转化为1-5的分数,如下表3所示,随后取平均值。
表3
评估项目分数 | 铺展性 | 均匀附着的感觉 | 光泽 | 总的美容效果 | 感觉 |
12345 | 差较差一般较好好 | 无有些不足一般略有明显存在 | 无相当不足略有有非常好 | 差较差一般良好非常好 | 非常差的感觉,例如有砂砾的感觉略差的感觉一般光滑,良好的感觉非常好的感觉 |
在下列实施例和对照实施例中,以容易理解的方式来记录评估结果,10名评审人员评分的平均值用下列符号表示:
◎:至少4.5,至多5.0
○:至少3.5,但小于4.5
●:至少2.5,但小于3.5
△:至少1.5,但小于2.5
X:至少1.0,但小于1.5
实施例9:指甲油
使用下列组合物和采用下述方法制备一种指甲油。
(1)硝基纤维素 12
(2)改性的醇酸树脂 6
(3)乙酰基三丁基柠檬酸酯 5
(4)乙酸正丁酯 36.4
(5)乙酸乙酯 6
(6)正丁醇 2
(7)甲苯 20
(8)氧化铁颜料 0.5
(9)二氧化钛 0.1
(10)实施例2的玻璃薄片 10
(11)云母 1
(12)有机改性的蒙脱石 1(重量%)
将组分(1)-(7)(除了一部分的组分(4)之外)一起溶解,将组分(12)的凝胶混合物和剩余的组分(4)加入该溶液并且进行混合,进一步加入组分(8)-(11)并混合,随后将该混合物填充到容器内,由此得至0指甲油。
对照实施例4:指甲油
按照实施例9得到一种指甲油,除了将组分(10)——具有二氧化硅薄膜的银涂覆的玻璃薄片用对照实施例1的没有二氧化硅薄膜的银涂覆的玻璃薄片代替。
实施例9和对照实施例4的感觉试验的结果如下表4所示。
表4
评估项目 | 感觉 | 铺展性 | 均匀附着的感觉 | 光泽 | 总的美容效果 |
实施例9对照实施例4 | ◎○ | ○○ | ◎◎ | ◎◎ | ◎◎ |
由表4可以看出,在银涂覆的玻璃薄片上的二氧化硅薄膜能够改善指甲油的感觉,而且对指甲油的使用感觉没有不良影响。由于二氧化硅薄膜抑制了前面所述的银离子的沥出,因此按照本发明的粉末可以抑制金属过敏反应的出现,并且阻止指甲油的变色,而且对指甲油的使用感觉无损害。
实施例10:眼影
使用下列方法制备由下列组合物组成的眼影:
(1)滑石 12.6
(2)绢云母 8.1
(3)云母 25.4
(4)实施例4的玻璃薄片 45.0
(5)226号红 0.4
(6)角鲨烷 3.0
(7)棕榈酸2-乙基己酯 5.0
(8)防腐剂 0.3
(9)香料 0.2(重量%)
用Henschel搅拌器混合组分(1)-(5),将组分(6)-(9)混合在一起并加热熔融得到一种材料,将其喷雾在上述组分(1)-(5)的混合物上,进一步混合,随后微粉化,模制在4×6cm的中等大小的圆盘中,由此得到眼影。
对照实施例5:眼影
按照实施例10得到一种眼影,除了将组分(4)——具有二氧化硅薄膜的银涂层玻璃薄片用对照实施例2的银涂覆玻璃薄片代替。
实施例10和对照实施例5的感觉试验的结果如下表5所示。
评估项目 | 感觉 | 铺展性 | 均匀附着的感觉 | 光泽 | 总的美容效果 |
实施例10对照实施例5 | ◎○ | ◎○ | ◎◎ | ◎◎ | ◎◎ |
由表5可以看出,在银涂覆的玻璃薄片上的二氧化硅薄膜能够改善眼影的感觉,而且对眼影的使用感觉没有不良影响。由于二氧化硅薄膜抑制前面所述的银离子的沥出,因此按照本发明的粉末可以抑制金属过敏反应的出现,并且阻止眼影的变色,而且对眼影的使用感觉无损害。
实施例11:唇膏
利用已知方法制备组成如下的唇膏:
(1)石蜡 12
(2)微晶蜡 6
(3)氢化聚丁烯 20
(4)辛基十二烷醇 10
(5)辛酸/癸酸硅油三酯 适量
(6)202号红 0.1
(7)4号黄 0.2
(8)硫酸钡 1
(9)二氧化钛 1
(10)实施例5的玻璃薄片 12
实施例12:口红
利用已知方法制备组成如下的口红。
(1)糊精棕榈酸酯 3
(2)重液体石蜡 适量
(3)异壬酸异辛酯 10
(4)角鲨烷 5
(5)201号红 0.1
(6)群粉 0.5
(7)硫酸钡 0.1
(8)实施例6的玻璃薄片 10
实施例13:含水睫毛膏
利用已知方法制备组成如下的含水睫毛膏。
(1)聚乙烯醇 10
(2)羧乙烯基聚合物 0.5
(3)1,3-丁二醇 5
(4)三乙醇胺 0.6
(5)乙醇 5
(6)防腐剂 0.2
(7)纯水 适量
(8)实施例3的玻璃薄片 8
实施例11-13的化妆品的感觉试验的结果如下表6所示。
表6
评估项目 | 感觉 | 铺展性 | 均匀附着的感觉 | 光泽 | 总的美容效果 |
实施例11实施例12实施例13 | ◎◎◎ | ◎◎○ | ◎◎◎ | ◎◎◎ | ◎◎◎ |
由表6可以看出,在表面上具有二氧化硅薄膜的银涂覆的玻璃薄片混合到唇膏、口红或含水睫毛膏的情况中,使用感觉没有受到特别的损害。此外,由于抑制了银离子的沥出,不会引起金属过敏反应,并且化妆品不变色。
工业实用性
如上述说明书清楚地说明的那样,由于本发明的化妆品使用了含有依次涂覆了金属薄膜和金属氧化物薄膜的基底物质的粉末,所以可以抑制金属离子的沥出,由此防止金属过敏反应的出现和有机物的变色/变性作用,同时由于金属薄膜的存在仍然可以保持金属光泽。
此外,通过使用玻璃薄片作为基底物质,可以通过常规方法制得粒状不是很明显、闪光度非常高的、具有优异的使用感觉(例如均匀附着的感觉和在皮肤上的铺展性)的化妆品。
Claims (2)
1.一种含有粉末的化妆品,该粉末含有基底材料,并且在该基底材料上以金属薄膜和金属氧化物薄膜的顺序形成薄膜,
其中所述粉末的金属薄膜具有至少一种选自银、金、铂、钯、镍、铜、铬、钼、锡、镁、铝和哈斯特洛伊耐蚀镍基合金的金属作为其主要组分,
其中所述粉末的所述金属氧化物薄膜具有至少一种选自二氧化硅、氧化铝、氧化锆、氧化锌和氧化铈的金属氧化物作为主要组分,
其中以形成所述金属氧化物薄膜之前的重量计,所述粉末具有含量为0.1-30重量%的附着在其表面上的所述金属氧化物薄膜。
2.权利要求1所述的化妆品,其中所述粉末的所述基底材料包括具有0.5-8.0μm的平均厚度和5-1,000μm的平均粒径的玻璃薄片。