CN1243904A - 盲孔承重空心砖及其制造方法 - Google Patents

盲孔承重空心砖及其制造方法 Download PDF

Info

Publication number
CN1243904A
CN1243904A CN 99113162 CN99113162A CN1243904A CN 1243904 A CN1243904 A CN 1243904A CN 99113162 CN99113162 CN 99113162 CN 99113162 A CN99113162 A CN 99113162A CN 1243904 A CN1243904 A CN 1243904A
Authority
CN
China
Prior art keywords
clay
brick
blind hole
coal
roast
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 99113162
Other languages
English (en)
Inventor
包国臣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 99113162 priority Critical patent/CN1243904A/zh
Publication of CN1243904A publication Critical patent/CN1243904A/zh
Pending legal-status Critical Current

Abstract

一种盲孔承重空心砖及其制造方法,砖的承重面上有盲孔,盲孔底部是锥形,盲孔带有一定稍度。制砖材料主要包括粘土、煤矸石和工业废渣。按比例把粘土、煤矸石和工业废渣混合拌匀后,加入到轮碾合料机中造粒,然后再用手动压力机或全自动压砖机模压成坯,再经过烧结成为本产品。这种砖是实心砖理想的替代产品,符合国家产业政策,符合环保和节能政策,是国家鼓励发展的新型建材产品,具有显著的经济效益和社会效益。

Description

盲孔承重空心砖及其制造方法
本发明涉及一种建筑用砌体材料,主要是盲孔承重空心砖及其制造方法。
目前建筑用砌体材料,大多为粘土烧制的实心红砖,这种砖浪费大量的土地资源。近几年开始出现利用粉煤灰、工业废渣和粘合剂生产出带有通孔的砖体,但在使用中都不十分理想。
本发明的目的就是提供一种盲孔承重空心砖,并提供其制造方法。
本发明的目的是通过以下措施来实现:
在砖体(1)的承重面上分布有盲孔(2),盲孔带有稍度,盲孔底部呈锥形,盲孔形状包括圆形和方形,圆形盲孔直径为10-30毫米。孔洞面积占承重总面积的15-30%。行与行之间的孔呈错落有序分布。砖体表面有凹槽(3)。
本发明的方法如下:
配方
粘土35-60%,煤干石15-30%、工业废渣25-40%。
制坯
将粘土干燥,然后粉碎过4目筛;将煤干石粉碎过8目筛,将工业废渣粉碎过8目筛,然后将上述料按配比混合拌匀,再把混合好的料加入到轮碾合料机中(或采用S116、S114碾砂机),同时加水,使料含水量在8-12%,经混合碾压5-10分钟,把粉状料碾压成直径小于5毫米的颗粒,然后出料。把出料在潮湿的库房内放置48-72小时阴干,阴干好的料加入到压砖机的模腔内,采取一轻二重的三次加压程序,再用锤头提出坯体,将坯体在干燥室中干燥。
培烧
干燥后的坯体,湿度应小于5%,将坯体装入窑内培烧,培烧温度在900±40℃。培烧时间,如用普通轮窑,培烧周期60-72小时;如用70米以上的隧道窑,培烧周期36-42小时。
在配方中提到的粘土包括红粘土、黄粘土、沙壤土、江河淤泥、陶土;煤干石包括石煤、煤泥、炉渣;工业废渣包括各种金属矿和非金属矿尾砂。
附图说明:
图1是本发明的带有盲孔的正面示意图,其中(1)砖体,(2)盲孔。
图2是图1的立体示意图,其中(3)凹槽。
图3是图1中A-A剖视图,表示盲孔的位置和形状。
本发明具有如下优点:
1、节约土地资源。
2、废物利用,有利环保。
3、砌筑时不浪费沙浆,使孔洞不进灰浆,使砌体牢固,封闭保温。
下面对本发明做进一步说明:
这种砖在承重面上设置有盲孔,即六面体砖,承重的大面,一面无孔而另一面有孔洞,但孔洞不透到另一面。盲孔的形状可以是圆孔,也可以是方孔,孔本身有一定的稍度,孔的底部是锥形。盲孔的分布,横向都在一条线上,竖向孔和孔应错开位置。当孔是圆形时,孔径是10-30毫米,当孔是方形时,可以是正方形,也可以长方形,还可是两种形状兼而有之。例如在标准普通砖面上设置有直径是20毫米的孔17个,即分为三行,上下行各为6个孔,中间行5个孔。总之,孔洞面积应占承重面的面积的比例为15-30%。
这种砖的生产关键是制坯,制坯的关键是压坯,本发明在压坯过程中,将配方中的混合料进行造粒。如按比例将粘土、煤干石、粉煤灰混合好,然后加入到轮碾合料机中(也可使用S116或S114碾砂机),同时加水,使料的含水量在8-12%,经过混合碾压,排出料粉中空气,使料的密实度增加,经过5-10分钟的碾压,形成直径小于5毫米的假颗粒,如有饼状的料,可用松砂机在出料时击碎。出料的颗粒是否合格,可用手试,即用手握料成团,一松手即散开,说明料的湿度合适。经过造粒的料经36-48小时的阴干,使水分均化,粘结性提高,再把料加入压机模腔中,三次加压后,将坯体提出模腔,入干燥室干燥,使水份在5%以下。然后进炉培烧,最后成为成品。压制坯体时的压强按成品厚度计算,在厚度为50毫米时,压强不低于220公斤/cm2,厚度增加时,所需压强递增。成型设备采用手动压力机或全自动压砖机,产品收缩率0-2%。
这种砖的烧结温度范围是900±40℃,成品烧结气氛为氧化气氧,烧成压力采用预热段负压作业,高温段零压至微正压作业,每块砖的烧成需热量范围在550-650卡/块。
这种砖的材料主要是利用部分粘土和其它工业废渣,粘土可利用荒坡、弃地(不必要占用耕地),工业废渣(铁矿尾砂、珍珠岩矿尾矿、金矿尾砂、钼矿、锰矿、江河淤沙、电厂煤灰、各种煤干石、石煤等),只要符合制砖条件,都可利用。但碳酸盐类矿渣、硫酸盐类矿渣及有放射性元素的矿物不能用。
这种砖是实心粘土砖的理想替代产品,符合国家产业政策,符合环保和节能政策,经济效益和社会效益十分显著,是国家鼓励发展的新型建筑产品。
实施例:
配方(按百分比)
1、粘土60、煤干石15、工业废渣25。
2、粘土35、煤干石30、工业废渣40。
3、粘土47.5、煤干石22、工业废渣22.5。

Claims (4)

1、一种盲孔承重空心砖,其特征是在砖体(1)的承重面上分布有盲孔(2),盲孔带有稍度,盲孔底部呈锥形;盲孔形状包括圆形和方形,圆形盲孔直径为10-30毫米;孔洞面积占承重面总面积的15-30%;行与行之间的孔呈错落有序分布。
2、根据权利要求1所说的空心砖,其特征是砖体表面有凹槽(3)。
3、盲孔承重空心砖的制造方法,其特征是
配方:
粘土35-60%、煤干石15-30%、工业废渣25-40%;
制坯
将粘土干燥,然后粉碎过4目筛;将煤干石粉碎过8目筛;将工业废渣粉碎过8目筛;然后将上述料按配比混合拌匀,再把混合好的料加入到轮碾合料机中,或采用S116、S114碾砂机,同时加水,使料含水量在8-12%,经混合碾压5-10分钟,把粉状料碾压成直径小于5毫米的颗粒,然后出料,把出料在潮湿的库房内放置48-72小时阴干,阴干好的料加入到压砖机的模腔内,采取一轻二重三次加压程序,再用锤头提出坯体,将坯体在干燥室中干燥;
培烧
干燥后的坯体,湿度应小于5%,将坯体装入窑内培烧,培烧温度在900±40℃,培烧时间如用普通轮窑,周期为60-72小时;如用70米以上的隧道窑,周期为36-42小时。
4、根据权利要求3所说的方法,其特征是粘土包括红粘土、黄粘土、沙壤土、江河淤泥、陶土;煤干石包括石煤、煤泥、炉渣;工业废渣包括各种金属矿和非金属矿尾砂。
CN 99113162 1999-08-12 1999-08-12 盲孔承重空心砖及其制造方法 Pending CN1243904A (zh)