CN1209778C - 铜基粉末电触头的制备方法 - Google Patents

铜基粉末电触头的制备方法 Download PDF

Info

Publication number
CN1209778C
CN1209778C CN 03132535 CN03132535A CN1209778C CN 1209778 C CN1209778 C CN 1209778C CN 03132535 CN03132535 CN 03132535 CN 03132535 A CN03132535 A CN 03132535A CN 1209778 C CN1209778 C CN 1209778C
Authority
CN
China
Prior art keywords
deformation
cold
contact
blank
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 03132535
Other languages
English (en)
Other versions
CN1482638A (zh
Inventor
邵文柱
甄良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Harbin Institute of Technology Shenzhen
Original Assignee
Harbin Institute of Technology Shenzhen
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Harbin Institute of Technology Shenzhen filed Critical Harbin Institute of Technology Shenzhen
Priority to CN 03132535 priority Critical patent/CN1209778C/zh
Publication of CN1482638A publication Critical patent/CN1482638A/zh
Application granted granted Critical
Publication of CN1209778C publication Critical patent/CN1209778C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

铜基粉末电触头的制备方法，它涉及一种电工开关用接触元件的制备方法。现有电触头的复压过程不能保证残余孔隙率达到所要求的水平，这一点对铜基电触头尤为明显。本发明致密化过程为多次深度压力变形过程：首先是热挤压，将大坯件挤成板材或棒材，温度为700～750℃，挤压比为20～30；然后通过板材轧制或丝材拉拔进行多道次的冷变形强化，冷变形强化总变形量为70～90%；最终通过冲压或冷镦变形制成触头件。本发明的方法提高了开关电器的可靠性和持久性，它使触头元件的工作寿命得到提高，同时使其它一些使用性能得到改善，通过本发明的致密化过程，可以保证电触头高效密实至理论密度，获得高质量触头。

Description

铜基粉末电触头的制备方法
技术领域：本发明涉及一种电工开关用接触元件的制备方法，属于粉末冶金领域。
背景技术：中等电流和大电流开关电器的分断触头，通常是通过粉末冶金方法制造的复合材料制成的。触头是在冲击和局部电弧作用等多次循环动态载荷的严酷条件下工作，这种条件对其机械稳定性和耐电弧烧蚀提出了较高要求。其中表征电接触元件质量的重要指标之一是在严酷条件下的工作持久性，就是粉末触头的残余孔隙率应当很低，或者说，其相对密度应当很高。众所周知，残余孔隙率的含量即使低到1-1.5％的量级，也会降低触头，乃至电器的使用寿命。孔隙率还会同时降低材料的导电率和机械强度，也就使其使用性能恶化。目前，利用粉末组元制备低压电器用电触头时，最广泛应用的生产方法是包含下述基本工艺环节：混合粉末制备，触头坯件冷压成型和烧结，致密化，退火。致密化环节的目的在于降低残余孔隙率(烧结后的坯件孔隙率一般为15-20％)，原则上是通过复压对烧结之后的锄触头坯件进行冷变形处理，复压压强一般为800-1000MPa，但这一环节并不能保证残余孔隙率达到所要求的水平，这一点对铜基电触头尢为明显。也有些方法建议，为降低触头烧结时的孔隙率，可以在混合粉末中引入具有活化烧结作用的添加剂，但这种条件下成品件的强度不足。目前，利用复压和中间热处理工艺，使触头坯件多次变形以达到致密化的方法已经是一种成熟的工艺方法，但这种方法的缺点在于，采用两次复压，甚至三次复压，孔隙率仍然不会降低到1-1.5％以下的水平。
发明内容：本发明的目的在于提供一种无孔隙的铜基粉末电触头的制备方法，它包含以下的制备过程：混合粉末制备、触头坯件冷压成型、烧结、致密化、退火，致密化过程为多次深度压力变形过程：首先是热挤压，将大坯件挤成板材或棒材，温度为700～750℃，挤压比为20～30；然后通过板材轧制或丝材拉拔进行多道次的冷变形强化，冷变形强化总变形量为70～90％，板材轧制时单次压下量不超过10％，变形量达到30％左右进行一次中间退火，中间退火温度为500～550℃；最终通过冲压或冷镦变形制成触头件。利用本发明的方法制造出近乎无孔隙的电触头，从而使电触头的质量得到提高，本发明的方法提高了开关电器的可靠性和持久性，它使触头元件的工作寿命得到提高，同时使其它一些使用性能得到改善，如机械强度、电导率以及对称触头副之间的接触电阻。通过本发明的致密化过程，可以保证电触头高效密实至理论密度，获得高质量触头，此外在高效塑性变形过程中，还会发生晶粒和组成相的细化，从而提高了电触头的质量。
具体实施方式：本实施方式包含以下的制备过程：混合粉末制备、触头坯件冷压成型、烧结、致密化、退火，混合粉末的化学成分(重量比)为：1.2％的镉、2.0％的铌、0.5％的金刚石，其余为铜。具体步骤为：首先将铜基粉末混合，在压强为300MPa的封闭模具中冷压成坯件，成型后坯件在保护气氛烧结炉中在900℃条件下保温1～2小时烧结，烧结后的坯件通过多次深度压力变形过程达到致密化，致密化过程为：(1)热挤压，将大坯件挤成板材，温度为700～750℃，挤压比为20；(2)板材轧制变形，轧制总变形量为70％，单次压下量不超过10％，变形量达到30％左右进行一次中间退火，中间退火温度为500～550℃；(3)轧制到接近产品厚度尺寸的板带最终通过冲压加工制成触头件。最后，成品触头在500℃的条件下保温0.5小时进行退火，即得铜基粉末电触头。
为了便于对比试验，利用现行传统典型工艺(两次复压，压制压强为1100MPa，中间退火温度为500℃)和本方法制备了铜基复合材料触头元件。整体工艺环节为：混合粉末制备，坯件成型(压制压强为300MPa)，坯件烧结(烧结温度为900℃，保温时间1h)，成品触头退火(退火温度500℃，保温时间0.5h)。两种方法上述工艺参数相同。
  方法   相对密度，d/dm％ ρ，μΩ·cm  HB，MPa   RK，mΩ    G，μg/次
现行方法     98.70     2.84     680     14.9     115
本方法     99.96     2.78     770     11.8     81
由表中可见，本方法制备触头的相对密度和硬度值相对较高，电阻率和对称触头副之间的接触电阻相对较低，而且耐烧蚀性能提高。这些都源于残余孔隙率的降低和组织的优化。与现行方法相比，本方法可以提高电器开关触头件的可靠性和持久性。

Claims (2)

1.一种铜基粉末电触头的制备方法，它包含以下的制备过程：混合粉末制备、触头坯件冷压成型、烧结、致密化、退火，其特征在于致密化过程为多次深度压力变形过程：首先是热挤压，将大坯件挤成板材或棒材，温度为700～750℃，挤压比为20～30；然后通过板材轧制或丝材拉拔进行多道次的冷变形强化，冷变形强化总变形量为70～90％，板材轧制时单次压下量不超过10％，变形量达到30％左右进行一次中间退火，中间退火温度为500～550℃；最终通过冲压或冷镦变形制成触头件。
2.根据权利要求1所述的铜基粉末电触头的制备方法，其特征在于它的制备过程为：首先将铜基粉末混合，在压强为300MPa的封闭模具中冷压成坯件，成型坯件在保护气氛烧结炉中在900℃条件下保温1～2小时烧结，烧结后的坯件通过多次深度压力变形过程达到致密化，最后，成品触头在500℃的条件下保温0.5小时进行退火，即得铜基粉末电触头。
CN 03132535 2003-07-29 2003-07-29 铜基粉末电触头的制备方法 Expired - Fee Related CN1209778C (zh)