CN116924762B - 一种可拆式绿色声学建筑板材 - Google Patents
一种可拆式绿色声学建筑板材 Download PDFInfo
- Publication number
- CN116924762B CN116924762B CN202311204062.XA CN202311204062A CN116924762B CN 116924762 B CN116924762 B CN 116924762B CN 202311204062 A CN202311204062 A CN 202311204062A CN 116924762 B CN116924762 B CN 116924762B
- Authority
- CN
- China
- Prior art keywords
- parts
- building board
- fly ash
- ethyl isopropyl
- green
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及建筑材料技术领域，提出了一种可拆式绿色声学建筑板材，包括以下重量份的原料：硅酸盐水泥60~80份、乙基异丙基砜改性粉煤灰30~50份、石英砂20~30份、纤维5~15份、隔音填料10~20份、粘合剂1~3份、减水剂0.5~1.5份、脱硫石膏1~3份、水25~35份。通过上述技术方案，解决了现有技术中以硅酸盐水泥和粉煤灰为基料的隔音建筑板材抗压强度低、抗折强度低和易吸水的问题。
Description
技术领域
本发明涉及建筑材料技术领域，具体的，涉及一种可拆式绿色声学建筑板材。
背景技术
随着城市化进程的加快和生活水平的提升，人们越来越注重于居住环境的舒适度。近年来，噪声作为污染源影响着居民的工作、生活和健康，对于降低噪音污染，打造安静的工作和生活环境需求日益迫切，因此，吸音建筑物因具有降低噪声的效果，而受到了人们的追捧。
目前，普遍使用的吸音建筑物主要是以硅酸盐水泥和粉煤灰为基料，添加纤维、粘结剂等助剂，固化成型，得到隔音建筑板材。该工艺不仅将对环境产生严重污染的工业固体废弃物粉煤灰进行重复利用，绿色环保，而且得到的建筑板材耐火效果、抗冲击性能好，但抗压强度、抗折强度一般，且粉煤灰具有很强的吸水性，当建筑板材吸水后，会导致隔音性能进一步的下降。
发明内容
本发明提出一种可拆式绿色声学建筑板材，解决了相关技术中以硅酸盐水泥和粉煤灰为基料的隔音建筑板材抗压强度低、抗折强度低和易吸水的问题。
本发明的技术方案如下：
一种可拆式绿色声学建筑板材，包括以下重量份的原料：硅酸盐水泥60~80份、乙基异丙基砜改性粉煤灰30~50份、石英砂20~30份、纤维5~15份、隔音填料10~20份、粘合剂1~3份、减水剂0.5~1.5份、脱硫石膏1~3份、水25~35份。
作为进一步的技术方案，所述乙基异丙基砜改性粉煤灰的制备方法包括以下步骤：将粉煤灰在乙基异丙基砜中浸渍，收集固体，得到乙基异丙基砜改性粉煤灰。
作为进一步的技术方案，所述浸渍为超声浸渍，超声波频率为30~40kHz、功率为120~150W。
作为进一步的技术方案，所述浸渍的温度为40~50℃、时间为50~80min。
作为进一步的技术方案，所述粉煤灰与乙基异丙基砜的质量体积比为1g:10~20mL。
作为进一步的技术方案，所述乙基异丙基砜改性粉煤灰与纤维的质量比为8:1~3。
作为进一步的技术方案，所述乙基异丙基砜改性粉煤灰与纤维的质量比为4:1。
作为进一步的技术方案，所述纤维包括玻璃纤维、麻纤维中的一种或两种。
作为进一步的技术方案，所述隔音填料包括中空玻璃微珠、膨胀珍珠岩中的一种或两种。
作为进一步的技术方案，所述粘合剂包括羟甲基纤维素、羟乙基纤维素、可再分散性乳胶粉中的一种或几种。
作为进一步的技术方案，所述减水剂包括聚羧酸类减水剂、萘系减水剂中的一种或两种。
本发明的工作原理及有益效果为：
本发明利用乙基异丙基砜改性粉煤灰使粉煤灰表面含有非极性基团，对粉煤灰表面的羟基进行分隔和包围，降低了粉煤灰的吸水性。此外，乙基异丙基砜改性后的粉煤灰表面含有砜基可以与纤维表面的羟基形成氢键，附着于纤维表面，并填补在建筑板材的空隙中，从而提高了隔音建筑板材的抗压强度和抗折强度。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都涉及本发明保护的范围。
以下实施例及对比例中粉煤灰为一级粉煤灰、目数为200目；石英砂的目数为60目、二氧化硅含量99.5wt%、密度3.0g/cm3；玻璃纤维和麻纤维的长度均为3mm；中空玻璃微珠的壁厚为1~2μm、粒径5~120μm；聚羧酸减水剂为聚羧酸减水剂540P；萘系减水剂为萘系减水剂FDN-C；膨胀珍珠岩的粒径为1~3mm。
实施例1
S1、将50g粉煤灰在45℃下超声浸渍于750mL乙基异丙基砜中60min，超声波频率为35kHz、功率为130W，过滤，收集固体，得到乙基异丙基砜改性粉煤灰；
S2、将P.O 42.5普通硅酸盐水泥70份、乙基异丙基砜改性粉煤灰40份、石英砂25份、玻璃纤维10份混合均匀后，加入中空玻璃微珠15份、可再分散性乳胶粉2份、聚羧酸减水剂1份、脱硫石膏2份、水30份继续混合，将混合料倒入模具成型，脱模后进行养护，得到可拆式绿色声学建筑板材。
实施例2
S1、将50g粉煤灰在45℃下超声浸渍于750mL乙基异丙基砜中60min，超声波频率为35kHz、功率为130W，过滤，收集固体，得到乙基异丙基砜改性粉煤灰；
S2、将P.O 42.5普通硅酸盐水泥70份、乙基异丙基砜改性粉煤灰40份、石英砂25份、玻璃纤维5份混合均匀后，加入中空玻璃微珠15份、可再分散性乳胶粉2份、聚羧酸减水剂1份、脱硫石膏2份、水30份继续混合，将混合料倒入模具成型，脱模后进行养护，得到可拆式绿色声学建筑板材。
实施例3
S1、将50g粉煤灰在45℃下超声浸渍于750mL乙基异丙基砜中60min，超声波频率为35kHz、功率为130W，过滤，收集固体，得到乙基异丙基砜改性粉煤灰；
S2、将P.O 42.5普通硅酸盐水泥70份、乙基异丙基砜改性粉煤灰40份、石英砂25份、玻璃纤维15份混合均匀后，加入中空玻璃微珠15份、可再分散性乳胶粉2份、聚羧酸减水剂1份、脱硫石膏2份、水30份继续混合，将混合料倒入模具成型，脱模后进行养护，得到可拆式绿色声学建筑板材。
实施例4
S1、将50g粉煤灰在40℃下超声浸渍于500mL乙基异丙基砜中80min，超声波频率为30kHz、功率为150W，过滤，收集固体，得到乙基异丙基砜改性粉煤灰；
S2、将P.O 42.5普通硅酸盐水泥60份、乙基异丙基砜改性粉煤灰30份、石英砂20份、麻纤维5份混合均匀后，加入中空玻璃微珠5份、膨胀珍珠岩5份、羟甲基纤维素1份、萘系减水剂0.5份、脱硫石膏1份、水25份继续混合，将混合料倒入模具成型，脱模后进行养护，得到可拆式绿色声学建筑板材。
实施例5
S1、将50g粉煤灰在50℃下超声浸渍于1000mL乙基异丙基砜中50min，超声波频率为40kHz、功率为120W，过滤，收集固体，得到乙基异丙基砜改性粉煤灰；
S2、将P.O 42.5普通硅酸盐水泥80份、乙基异丙基砜改性粉煤灰50份、石英砂30份、玻璃纤维10份、麻纤维5份混合均匀后，加入中空玻璃微珠20份、羟乙基纤维素1份、可再分散性乳胶粉2份、聚羧酸减水剂1.5份、脱硫石膏3份、水35份继续混合，将混合料倒入模具成型，脱模后进行养护，得到可拆式绿色声学建筑板材。
对比例1
将P.O 42.5普通硅酸盐水泥70份、粉煤灰40份、石英砂25份、玻璃纤维10份混合均匀后，加入中空玻璃微珠15份、可再分散性乳胶粉2份、聚羧酸减水剂1份、脱硫石膏2份、水30份继续混合，将混合料倒入模具成型，脱模后进行养护，得到可拆式绿色声学建筑板材。
将实施例1~5及对比例1得到的可拆式绿色声学建筑板材参考GB/T 17671-2021《水泥胶砂强度检验方法(ISO法)》的方法，进行28d抗折强度、28d抗压强度的测试，参考GB/T 9966.3-2020《天然石材试验方法 第3部分：吸水率、体积密度、真密度、真气孔率试验》的方法，进行吸水率的测试，测试结果记录在表1。
表1 可拆式绿色声学建筑板材的抗折强度、抗压强度和吸水率
由表1可以看出，本发明提供的可拆式绿色声学建筑板材的抗折强度在10.1MPa以上、抗压强度在44.8MPa以上，吸水率在1.5%以下，具有良好的强度和低的吸水性。
实施例1与对比例1相比，实施例1使用乙基异丙基砜改性粉煤灰，对比例1未对粉煤灰改性，实施例1得到的可拆式绿色声学建筑板材的抗折强度、抗压强度高于对比例1，吸水率低于对比例1，说明使用乙基异丙基砜改性粉煤灰可以降低可拆式绿色声学建筑板材的吸水性，同时提高了抗折强度和抗压强度。
以上仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (9)
1.一种可拆式绿色声学建筑板材，其特征在于，包括以下重量份的原料：硅酸盐水泥60~80份、乙基异丙基砜改性粉煤灰30~50份、石英砂20~30份、纤维5~15份、隔音填料10~20份、粘合剂1~3份、减水剂0.5~1.5份、脱硫石膏1~3份、水25~35份；
所述乙基异丙基砜改性粉煤灰与纤维的质量比为8:1~3。
2.根据权利要求1所述的一种可拆式绿色声学建筑板材，其特征在于，所述乙基异丙基砜改性粉煤灰的制备方法包括以下步骤：将粉煤灰在乙基异丙基砜中浸渍，收集固体，得到乙基异丙基砜改性粉煤灰。
3.根据权利要求2所述的一种可拆式绿色声学建筑板材，其特征在于，所述浸渍为超声浸渍，超声波频率为30~40kHz、功率为120~150W。
4.根据权利要求2所述的一种可拆式绿色声学建筑板材，其特征在于，所述浸渍的温度为40~50℃、时间为50~80min。
5.根据权利要求2所述的一种可拆式绿色声学建筑板材，其特征在于，所述粉煤灰与乙基异丙基砜的质量体积比为1g:10~20mL。
6.根据权利要求1所述的一种可拆式绿色声学建筑板材，其特征在于，所述纤维包括玻璃纤维、麻纤维中的一种或两种。
7.根据权利要求1所述的一种可拆式绿色声学建筑板材，其特征在于，所述隔音填料包括中空玻璃微珠、膨胀珍珠岩中的一种或两种。
8.根据权利要求1所述的一种可拆式绿色声学建筑板材，其特征在于，所述粘合剂包括羟甲基纤维素、羟乙基纤维素、可再分散性乳胶粉中的一种或几种。
9.根据权利要求1所述的一种可拆式绿色声学建筑板材，其特征在于，所述减水剂包括聚羧酸类减水剂、萘系减水剂中的一种或两种。