CN116626824B - 一种易识别双芯并排隐形蝶缆 - Google Patents
一种易识别双芯并排隐形蝶缆 Download PDFInfo
- Publication number
- CN116626824B CN116626824B CN202310536850.2A CN202310536850A CN116626824B CN 116626824 B CN116626824 B CN 116626824B CN 202310536850 A CN202310536850 A CN 202310536850A CN 116626824 B CN116626824 B CN 116626824B
- Authority
- CN
- China
- Prior art keywords
- invisible
- cable
- butterfly cable
- butterfly
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种易识别双芯并排隐形蝶缆，包括两个蝶缆组件，所述蝶缆组件通过连接件互相连接；所述蝶缆组件包括隐形光缆、加强件和外护套，所述隐形光缆包括光纤和光纤外侧包裹有透明层，加强件设置于所述隐形光缆两侧，所述外护套包裹住隐形光缆和加强件；所述外护套上设有两个凹槽，所述两个蝶缆组件上凹槽的位置不同，一个蝶缆组件上的凹槽在光纤两侧相对设置，另一个蝶缆组件的凹槽分别位于光纤两侧，成不对称设置。本发明的双芯并排隐形蝶缆可以方便实现对两个隐形光缆的快速区分；通过透明层、加强件和外护套三者的结合，提高了隐形蝶缆的力学性能和阻燃性能。本发明的隐形蝶缆成本低，结构简单，整体性能高，使用效果好。
Description
技术领域
本发明属于双芯光缆领域，具体涉及一种易识别双芯并排隐形蝶缆。
背景技术
随着光通信网络的发展，FTTH(隐形光缆到户)网络建设飞速发展，蝶形引入光缆主要应用于FTTH光缆线路的入户引入段，双芯并排蝶形引入光缆布放后可从连接处撕裂分成两根相同独立的蝶形光缆。在使用普通蝶形光缆进行宽带接入时，容易造成家中宽带的数据线杂乱无章，破坏家中装潢的美观。因此通常光缆的护套采用透明的材料，视觉上更加和谐。但由于采用本色透明隐形光缆，所以双芯并排隐形蝶形光缆中分离出的两根隐形光缆外观完全相同，难以辨认，不便于后期维护和管理。同时，隐形蝶缆在楼道内以蝶形光缆的形式铺设，入户后将外护套减掉，只留下隐形进套光纤，在宽带接入时，走线一般较为复杂，存在较多需要弯曲敷设的地方，同时对阻燃性能、力学强度有更高的要求，因此，需要一种新型的易识别双芯并排隐形蝶缆。
发明内容
本发明的目的是提供一种易识别双芯并排隐形蝶缆，可以实现两个隐形光缆的快速区分，并且提高了隐形蝶缆阻燃性和力学强度。
为了实现上述目的，本发明提供了一种易识别双芯并排隐形蝶缆，包括两个蝶缆组件，所述蝶缆组件通过连接件互相连接；所述蝶缆组件包括隐形光缆、加强件和外护套，所述隐形光缆包括光纤和光纤外侧包裹有透明层，加强件设置于所述隐形光缆两侧所述外护套包裹住隐形光缆和加强件；所述外护套上设有两个凹槽，所述两个蝶缆组件上凹槽的位置不同，一个蝶缆组件上的凹槽在与光纤两侧相对设置，另一个蝶缆组件的凹槽分别位于光纤两侧，成不对称设置。
本发明通过将凹槽设置位置的不同，可以轻松区分两个隐形光缆，无需额外设置区分的部件或者标记，降低了制造的成本和工序，更加美观，同时其中一个蝶缆组件的凹槽分别位于光纤两侧，成不对称设置，增加了两个凹槽之间的厚度，可以增加光缆的保护力度，增加了对虫鼠破坏的抵抗性。
优选的，所述透明层的材料的制备方法为：将45~50重量份乙烯-醋酸乙烯共聚物和10~15重量份乙烯-α-烯烃共聚物在双辊开炼机上熔融混合均匀，然后逐次加入20~30重量份阻燃剂、10~20重量份助剂，混炼温度为140~145℃。
优选的，乙烯-醋酸乙烯共聚物具体参数为：醋酸乙烯25wt.%，熔融指数19g/10min(190°C/2.16kg)，购自阿拉丁P101484 24937-78-8；乙烯-α-烯烃共聚物，密度0.861g/cm³，熔流率0.50g/10min，熔融温度<50.0°C，购自三井化学，TAFMER™ DF605。有机物的性质与反应条件共同影响反应的结果，本发明选用的乙烯-醋酸乙烯共聚物和乙烯-α-烯烃共聚物作为基体，与相应的阻燃剂和助剂协同增效，得到的产物的品质更高。
优选的，所述阻燃剂选自表面改性氢氧化铝、氢氧化镁、硼酸锌、TCPP阻燃剂、BDP阻燃剂、十溴二苯乙烷阻燃剂、四溴双酚A阻燃剂中的一种或多种，所述助剂选自抗氧剂1010、抗氧化剂168、PE蜡、硬脂酸锌中的一种或多种。
优选的，所述阻燃剂包括表面改性氢氧化铝、TCPP阻燃剂和十溴二苯乙烷阻燃剂，所述助剂包括抗氧剂1010、抗氧化剂168和硬脂酸锌。
为了提高透明层材料的阻燃性和力学性能，优选的，所述表面改性氢氧化铝、TCPP阻燃剂和十溴二苯乙烷阻燃剂的重量比为1:1：（0.1~0.5），所述抗氧剂1010、抗氧化剂168和硬脂酸锌的重量比为（2~5）:1:1。
优选的，所述透明层的材料的制备方法为：将48重量份乙烯-醋酸乙烯共聚物和12重量份乙烯-α-烯烃共聚物在双辊开炼机上熔融混合均匀，然后逐次加入26重量份阻燃剂、16重量份助剂，混炼温度为142℃。
优选的，所述表面改性氢氧化铝、TCPP阻燃剂和十溴二苯乙烷阻燃剂的重量比为1:1：0.3，所述抗氧剂1010、抗氧化剂168和硬脂酸锌的重量比为3:1:1。
本发明使用自制透明层的材料，通过将基体和阻燃剂、助剂进行合理复配，在阻燃剂使用量低于现有技术的前提下，产物阻燃效果优异，透明度高、隐形效果好，应变拉力高，拉伸力强。本发明通过基材与特定成分和配比的阻燃剂和抗氧剂组合，提高了透明层的整体性能。与现有技术相比，本发明使用的阻燃剂使用量占基材的重量比较低，但是通过三种阻燃剂复配协同产生了优良的抗阻燃效果，有利于降低生产成本。
优选的，一个蝶缆组件上的凹槽在与光纤两侧相对设置，其加强件的材质为磷化钢丝、镀锌钢丝、铜包钢丝、不锈钢丝、涂塑钢丝、光面钢丝中的一种；另一个蝶缆组件的凹槽分别位于光纤两侧，成不对称设置，其加强件的材质为GFRP光缆加强芯、KFRP芳纶纤维增强光缆加强芯、QFRP玻璃纤维光缆加强芯中的一种。
为了提高蝶缆组件的力学性能，优选的，一个蝶缆组件上的凹槽在与光纤两侧相对设置，其加强件的材质为镀锌钢丝；另一个蝶缆组件的凹槽分别位于光纤两侧，成不对称设置，其加强件的材质为KFRP芳纶纤维增强光缆加强芯。
优选的，所述镀锌钢丝的抗拉强度大于等于1350MPa，购自河北振明；所述KFRP芳纶纤维增强光缆加强芯的拉伸强度大于等于1700MPa。
优选的，KFRP芳纶纤维增强光缆加强芯所述外径0.5±0.05mm，密度1.3~1.4 g/cm3，拉伸强度≥1700Mpa，拉伸弹性模量≥50Gpa，断裂伸长率≤3.0%， 最小弯曲直径≤12mm，高温弯曲试验：80℃、24h、Φ30mm，无折断。购自南通赛博通信有限公司。
优选的，所述外护套的材料为高密度聚乙烯。
优选的，所述高密度聚乙烯的密度0.92~0.98g/cm3，21.6kg/190℃熔体流动速率10.5~11.3g/10min，重均分子量大于1×106所占比例大于6%，重均分子量1×104~1×106大于65%。购自伊朗石化，型号HD-1:7000F。高密度聚乙烯实际上是一种混合物，由不同链长的高分子聚合物组成，组成成分不同会带来不同的材料特性，质量分数的分布为所有不同链长分子质量占聚合物总质量的分数，可以反映产品的微观性质。高密度聚乙烯的熔体流动速率影响材料的加工性能，本发明选用的特定的高密度聚乙烯拉伸流变和力学强度高，与透明层和加强件组合协同增效，显著提高了隐形蝶缆的弯曲性能和力学强度。
与现有技术相比，本发明的优点和有益效果为：
1、本发明通过将两个并排的光缆组件中的线缆外套分别设置为不同位置的凹槽，以方便实现对两个隐形光缆的快速区分，以便于后期的管理和维修。
2、本发明两个不同形状的蝶缆组件匹配了相应的金属和非金属的加强件，使两个蝶缆组件的力学性能实现力学性能的均衡，同时金属和非金属加强件的直径不同也可以用于区分两个隐形光缆。
3、本发明的透明层透明度高，更加美观，并且通过阻燃剂和抗氧剂的合理配比，降低了阻燃的用量，显著提高了阻燃性能。
4、本发明通过透明层、加强件和外护套三者的结合，提高了隐形蝶缆的力学性能和阻燃性能。
5、本发明的隐形蝶缆成本低，结构简单，实用型强，整体性能高，使用效果好，易剥离，便于大范围推广和使用。
附图说明
图1为一种易识别双芯并排隐形蝶缆的结构示意图；
其中，1、光纤，2、透明层，3、加强件，4、外护套，5、凹槽，6、连接件。
实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
本实施例提供了一种易识别双芯并排隐形蝶缆，包括两个蝶缆组件，所述蝶缆组件通过连接件6互相连接；所述蝶缆组件包括隐形光缆、加强件3和外护套4，所述隐形光缆包括光纤1和光纤外侧包裹有透明层2，加强件2设置于所述隐形光缆两侧所述外护套4包裹住隐形光缆和加强件3；所述外护套4上设有两个凹槽5，所述两个蝶缆组件上凹槽5的位置不同，一个蝶缆组件上的凹槽5在与光纤1两侧相对设置，其加强件2的材质为镀锌钢丝；另一个蝶缆组件的凹槽5分别位于光纤1两侧，成不对称设置；加强件2的材质为KFRP芳纶纤维增强光缆加强芯。
所述透明层的材料的制备方法为：将48重量份乙烯-醋酸乙烯共聚物和12重量份乙烯-α-烯烃共聚物在双辊开炼机上熔融混合均匀，然后逐次加入26重量份阻燃剂、16重量份助剂，混炼温度为142℃。所述阻燃剂包括重量比为1:1：0.3的表面改性氢氧化铝、TCPP阻燃剂和十溴二苯乙烷阻燃剂，所述助剂包括重量比为3:1:1的抗氧剂1010、抗氧化剂168和硬脂酸锌。所述外护套的材料为高密度聚乙烯。购自伊朗石化，型号HD-1:7000F。所述表面改性氢氧化铝是采用硅烷类，硬脂酸类或钛酸酯类偶联剂经过特殊工艺对氢氧化铝粉体进行有机化改性后的产品，从而使产品阻燃效果好, 容重低，在常温下更稳定，活性氢氧化铝可改善氢氧化铝与树脂的结合性和加工性，使之兼具阻燃和填充双重功能，赋予制品优良的综合性能，购自正恒铝业，F1G01。
本实施例与实施例1的区别在于：本发明所述加强芯均为QFRP玻璃纤维光缆加强芯（购自上海吉锐化工，型号直径0.5±0.05mm），拉伸强度≥1600MPa，高温弯曲性能80℃，24h，无毛刺，无折断，低温弯曲性能-40℃，24h，无毛刺，无折断。
本实施例与实施例1的区别在于，所述外护层的材料为默克427772，重均分子量4000，25 °C密度0.92 g/mL，粘度1.5 poise/25°C。
本实施例与实施例1的区别在于：所述透明层材料为低烟无卤阻 燃聚烯烃材料，购自洛阳威强，WQ-001，密度1.68g/cm3，拉伸强度10MPa，阻燃性A类。
本实施例与实施例1的区别在于：所述助燃剂为重量比1:1表面改性氢氧化铝、TCPP阻燃剂。
本实施例与实施例1的区别在于：所述阻燃剂包括重量比为4:1的表面改性氢氧化铝、TCPP阻燃剂，所述助剂包括重量比为1:2:1的抗氧剂1010、抗氧化剂168和硬脂酸锌。
按照国家标准YD/T1997.1-2022《通信用引入光缆第1部分：蝶形光缆》对 实施例1~6的产品进行了性能检测。结果见表1。
（1）拉伸性能：长期拉伸力300Ｎ下的纤应变A和短期拉伸力300Ｎ下的纤应变B。
（2）冲击性能：残余附加衰减≤0.4。
（3）反复弯曲：残余附加衰减≤0.4。
（4）阻燃性：上支架下缘与炭化部分上起始点之间的距离＞50mm：H1；上支架下缘与炭化部分下起始点之间的距离≤540mm：H2。
表1性能测试结果
通过实施例1~6可知，本发明的隐形蝶缆性能优越，阻燃性高，力学性能强，整体性能高，使用效果好，便于大范围推广和使用，对隐形光缆的发展具有重要意义。
以上所述是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明所述原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (6)
1.一种易识别双芯并排隐形蝶缆，其特征在于，包括两个蝶缆组件，所述蝶缆组件通过连接件互相连接；所述蝶缆组件包括隐形光缆、加强件和外护套，所述隐形光缆包括光纤和光纤外侧包裹有透明层，加强件设置于所述隐形光缆两侧，所述外护套包裹住隐形光缆和加强件；所述外护套上设有两个凹槽，所述两个蝶缆组件上凹槽的位置不同，一个蝶缆组件上的凹槽在光纤两侧相对设置，另一个蝶缆组件的凹槽分别位于光纤两侧，成不对称设置；
所述透明层的材料的制备方法为：将45～50重量份乙烯-醋酸乙烯共聚物和10～15重量份乙烯-α-烯烃共聚物在双辊开炼机上熔融混合均匀，然后逐次加入20～30重量份阻燃剂、10～20重量份助剂，混炼温度为140～145℃；
所述阻燃剂选自表面改性氢氧化铝、氢氧化镁、硼酸锌、TCPP阻燃剂、BDP阻燃剂、十溴二苯乙烷阻燃剂、四溴双酚A阻燃剂中的一种或多种，所述助剂选自抗氧剂1010、抗氧化剂168、PE蜡、硬脂酸锌中的一种或多种；
所述阻燃剂包括表面改性氢氧化铝、TCPP阻燃剂和十溴二苯乙烷阻燃剂，所述助剂包括抗氧剂1010、抗氧化剂168和硬脂酸锌；
所述表面改性氢氧化铝、TCPP阻燃剂和十溴二苯乙烷阻燃剂的重量比为1:1：(0.1～0.5)，所述抗氧剂1010、抗氧化剂168和硬脂酸锌的重量比为(2～5):1:1。
2.根据权利要求1所述的易识别双芯并排隐形蝶缆，其特征在于，一个蝶缆组件上的凹槽在与光纤两侧相对设置，其加强件的材质为磷化钢丝、镀锌钢丝、铜包钢丝、不锈钢丝、涂塑钢丝、光面钢丝中的一种；另一个蝶缆组件的凹槽分别位于光纤两侧，成不对称设置，其加强件的材质为GFRP光缆加强芯、KFRP芳纶纤维增强光缆加强芯、QFRP玻璃纤维光缆加强芯中的一种。
3.根据权利要求2所述的易识别双芯并排隐形蝶缆，其特征在于，一个蝶缆组件上的凹槽在与光纤两侧相对设置，其加强件的材质为镀锌钢丝；另一个蝶缆组件的凹槽分别位于光纤两侧，成不对称设置，其加强件的材质为KFRP芳纶纤维增强光缆加强芯。
4.根据权利要求3所述的易识别双芯并排隐形蝶缆，其特征在于，所述镀锌钢丝抗拉强度大于等于1350MPa；所述KFRP芳纶纤维增强光缆加强芯拉伸强度大于等于1700MPa。
5.根据权利要求1所述的易识别双芯并排隐形蝶缆，其特征在于，其特征在于，所述外护套的材料为高密度聚乙烯。
6.根据权利要求5所述的易识别双芯并排隐形蝶缆，其特征在于，其特征在于，所述高密度聚乙烯的密度0.92～0.98g/cm3，21.6kg/190℃熔体流动速率大于10.5g/10min，重均分子量大于1×106所占比例大于6％，重均分子量1×104～1×106所占比例大于65％。