CN1156612C - Non-crack nm-class Ti-based anode and its preparing process - Google Patents

Non-crack nm-class Ti-based anode and its preparing process Download PDF

Info

Publication number
CN1156612C
CN1156612C CNB001256149A CN00125614A CN1156612C CN 1156612 C CN1156612 C CN 1156612C CN B001256149 A CNB001256149 A CN B001256149A CN 00125614 A CN00125614 A CN 00125614A CN 1156612 C CN1156612 C CN 1156612C
Authority
CN
China
Prior art keywords
titanium
internal layer
titanium matrix
grams
iridium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB001256149A
Other languages
Chinese (zh)
Other versions
CN1293263A (en
Inventor
陈康宁
林纪筠
张萌萌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
East China Normal University
Donghua University
Original Assignee
East China Normal University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by East China Normal University filed Critical East China Normal University
Priority to CNB001256149A priority Critical patent/CN1156612C/en
Publication of CN1293263A publication Critical patent/CN1293263A/en
Application granted granted Critical
Publication of CN1156612C publication Critical patent/CN1156612C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

The present invention relates to a crackless nanometer titanium base anode and the preparation thereof, and belongs to the technical field of electrochemistry. The prepared titanium base anode is composed of a titanium matrix 1 and an outer layer 2, wherein an inner layer 3 can be arranged between the titanium matrix 1 and the outer layer 2, the titanium matrix 1 is a pure titanium plate, and the outer layer 2 is prepared from one to two kinds of iridium dioxide and ruthenium dioxide and one kind of titanium oxide and tantalum oxide. The inner layer 3 is prepared from the iridium dioxide, the surface of the outer layer 2 has no cracks, and the average diameter of oxide grains deposited on the surface of the outer layer 2 is less than 20 nanometers. The crackless nanometer titanium base anode has the advantages of long service life and high current efficiency, and is suitable for titanium base anodes for producing chlorate and hypochlorite which can carry out oxygen evolution reactions and have strong oxidizing properties.

Description

Non-crack nm-class Ti-based anode and preparation thereof
The present invention relates to a kind of non-crack nm-class Ti-based anode and preparation thereof, belong to technical field of electrochemistry.
Background technology is introduced.1. publication number is that the Chinese invention patent prospectus of CN1036413A is addressed a kind of titanium anode for electrochemical industry.This titanium anode is a matrix with the titanium, scribbles iridium, cobalt/cobalt oxide coating and ruthenium, tin, titanium oxide coating on it successively as its middle layer and skin, is prepared from pyrolysis technique.This titanium substrate anode is used for the hypochlorite generator, and current efficiency and reinforcing life were respectively 58.1% and 31 hour.2.Electrochemica Acta44 (1998) P.1509~1513, delivers iridium tantalum titanium substrate anode for becoming block crannied coating, crystal grain diameter is 30~100 nanometers, uses in production sodium chlorate electricity groove, and current efficiency is 90%, and reinforcing life is 60 hours.These titanium substrate anodes have following shortcoming: the oxide film structure inequality of coating, and the thick one-tenth piece of crystal grain, coating has the crack, causes the index of above-mentioned current efficiency and reinforcing life to be difficult to improve.
An object of the present invention is to release a kind of coating leakless, coated grains diameter less than the long non-crack nm-class Ti-based anode of 20 nanometers, current efficiency height and reinforcing life.
Another object of the present invention provides the preparation method that above-mentioned purpose is addressed titanium substrate anode.
Description of drawings.Fig. 1 is the structural representation of titanium substrate anode of the present invention, and 1 is the titanium matrix among the figure, the 2nd, and outer.Fig. 2 is the structural representation that contains the titanium substrate anode of internal layer 3 of the present invention, and 3 is internal layers among the figure.
Now by reference to the accompanying drawings, technology contents of the present invention is described. Above-mentioned purpose is by being achieved by the following technical solutions: make matrix processing, baking temperature, oxidizing temperature, heat time heating time and be coated with between the formula of liquid reasonably to be cooperated.
A kind of non-crack nm-class Ti-based anode, formed by titanium matrix 1 and outer 2, between the titanium matrix 1 and outer 2 internal layer 3 can be arranged, it is characterized in that, titanium matrix 1 is pure titanium plate, outer 2 are comprised of metal oxide containing precious metals and non-noble metal oxide, metal oxide containing precious metals is following two kinds of oxides: in iridium dioxide and the ruthenic oxide one to two kind, non-noble metal oxide is following two kinds of oxides: a kind of in titanium oxide and the tantalum oxide, the mol ratio of outer 2 interior noble metals and base metal is 1: 3~5: 1, outer 2 interior bullion contents are relevant with the area of titanium matrix 1, and this content is 4~40 grams/rice2, internal layer 3 is iridium dioxide, outer 2 surperficial frees from flaw are deposited on the oxide grain average diameter on outer 2 surfaces less than 20 nanometers.
The preparation method of above-mentioned titanium substrate anode is characterized in that, operation steps:
The 1st step was cleaned titanium matrix 1, with 5% soda ash solution digestion titanium matrix 1 one hours, washing was immersed 10% oxalic acid solution again and was boiled two hours, washing, wash down with deionized water, dry back is stand-by, as no internal layer 3 between titanium matrix 1 and outer 2, skipped for the 2nd step, entered for the 3rd step,, enter down the step as between titanium matrix 1 and outer 2 internal layer 3 being arranged;
The 2nd step deposition internal layer 3, the titanium matrix 1 that the last step was cleaned immerses masking liquid, take out after the dip-coating, put into the heated drying stove dry 10 minutes, drying temperature is 40~100 ℃, moves into warm air oxidized still oxidation 10 minutes then, and oxidizing temperature is 350~550 ℃, immerse masking liquid after the cooling again, dry again, oxidation, cooling repeats said process, and multiplicity is 3~5 times, the masking liquid that this step adopts is with the chloro-iridic acid that contains iridium 25~36 grams, 55~200 milliliters of hydrochloric acid, 250~750 milliliters of propyl carbinols, 250~750 milliliters of sol solutionses that are made into of Virahol, so far, internal layer 3 is deposited on the surface of titanium matrix 1;
The 3rd step deposition outer 2, make finished product, the work in-process that the last step was obtained immerse masking liquid, below operation is that 15~30 times and last oxidization time are one hour except multiplicity, all the other all go on foot together with the 2nd, the masking liquid that adopts of this step mixes and is made into containing iridium concentration and containing sol solutions that tantalum concentration is respectively the iridium salt of 6.3~10.5 grams per liters and 4~6 grams per liters and tantalum salt, or with chloro-iridic acid 160~220 gram, ruthenium trichloride 180~250 grams, tetrabutyl titanate 2400~3200 grams, 7000~10000 milliliters of sol solutionses that are made into of propyl carbinol, so far, outer 2 are deposited on the surface of titanium matrix 1 or internal layer 3, obtain finished product, titanium substrate anode.
The preparation of the titanium substrate anode of embodiment 1. no internal layers 3 is characterized in that operation steps:
No internal layer 3 between the 1st step titanium matrix 1 and outer 2 directly entered for the 3rd step, and all the other are identical with the preparation method's of above-mentioned titanium substrate anode the 1st step corresponding part;
The 3rd step drying temperature, oxidizing temperature and multiplicity are respectively 50 ± 5 ℃, 480 ± 5 ℃ and 25 times, the masking liquid that adopts of this step mixes and is made into containing iridium concentration and containing sol solutions that tantalum concentration is respectively the iridium salt of 8.4 grams per liters and 5 grams per liters and tantalum salt, and to go on foot corresponding part identical with the 3rd of above-mentioned titanium substrate anode preparation method for all the other.
The reinforcing life test of finished product is at 40%H 2SO 4In the solution and current density be 2A/cm 2Condition under carry out; The test that finished product is used for production of sodium chlorate is to carry out at the no divide power slot that 30%NaCl solution is housed.The results are shown in Table 1,, enumerated the corresponding data of background technology in the table 1 for ease of comparing.
Table 1
Type of electrodes The coatingsurface pattern Coated grains diameter (nm) Reinforcing life (h) Current efficiency (%)
Iridium, tantalum (the present invention) Leakless 9.8 300 94.00
Iridium, tantalum (background technology-2) The crack is arranged 30~100 60 90.00
Embodiment 2 contains the preparation of the titanium substrate anode of internal layer 3, it is characterized in that operation steps:
Between the 1st step titanium matrix 1 and outer 2 internal layer 3 is arranged, enter down the step, all the other are identical with the preparation method's of above-mentioned titanium substrate anode the 1st step corresponding part;
The 2nd step drying temperature, oxidizing temperature and multiplicity are respectively 50 ± 5 ℃, 450 ± 5 ℃ and 3 times, the masking liquid that this step adopts is with 600 milliliters of 160 milliliters of chloro-iridic acid, hydrochloric acid, propyl carbinols and 600 milliliters of sol solutionses that are made into of Virahol of containing iridium 64.5 grams, and all the other are identical with the preparation method's of above-mentioned titanium substrate anode the 2nd step corresponding part;
The 3rd step drying temperature, oxidizing temperature and multiplicity are respectively 50 ± 5 ℃, 450 ± 5 ℃ and 20 times, the masking liquid that this step adopts is with chloro-iridic acid 195 grams, ruthenium trichloride 230 grams, tetrabutyl titanate 2700 grams, 8600 milliliters of sol solutionses that are made into of propyl carbinol, and all the other are identical with the preparation method's of above-mentioned titanium substrate anode the 3rd step corresponding part.
The current efficiency of finished product is tested: finished product is packed into per hour to produce among 10 kilograms of hypochlorite generators test, the results are shown in Table 2.For ease of comparing, enumerate the corresponding data of background technology in the table 2.
Table 2
Type of electrodes The coatingsurface pattern Coated grains diameter (nm) Reinforcing life (h) Current efficiency (%)
Iridium, (internal layer) iridium, ruthenium, titanium (skin) (the present invention) Leakless 6.4 8 70
Iridium, cobalt (internal layer) iridium, ruthenium, tin, titanium (skin) (background technology-1) Bulk has the crack <10 4.04 58.1
Preparation method of the present invention makes matrix processing, drying temperature, oxidizing temperature, heat-up time and is coated with between the liquid formula and reasonably cooperated, the nucleation rate that makes crystal grain is greater than the speed of growth, cause finished product, titanium substrate anode has that coatingsurface pattern and coated grains diameter are respectively leakless and less than the feature of 20 nanometers.The internal layer 3 of this titanium substrate anode and outer 2 is multilayered structure, forms with identical technology.The small performance to this titanium substrate anode of leakless and crystal grain diameter: solidity to corrosion, work-ing life and current efficiency have direct influence.Skin 2 and internal layer 3 leakless show, this titanium substrate anode is used for that the oxymuriate of oxygen evolution reaction and strong oxidizing property is arranged, the production of hypochlorite, oxygen is difficult to infiltration with medium and contacts with titanium matrix 1, can delay electrode passivation, the work-ing life that helps improving the solidity to corrosion of electrode and prolong electrode.Crystal grain diameter in skin 2 and the internal layer 3 is small, and for nano level shows, crystal grain quantity is many, the dispersity of coating is even, the summation that grain surface amasss is huge, and the real work area of this titanium substrate anode increases greatly, helps improving the electrocatalysis characteristic and the current efficiency of electrode.
Compare with background technology, the present invention has following advantage:
1. outer 2 and internal layer 3 surperficial frees from flaw, corrosion resistance is remarkable, long service life.
2. the coated grains diameter of skin 2 and internal layer 3 is small, is nanoscale, and the electrocatalysis characteristic of electrode is good, and the current efficiency of electrode is high.
To sum up, preparation method of the present invention is particularly suitable for producing the chlorate of oxygen evolution reaction and strong oxidizing property, the titanium substrate anode of hypochlorite.

Claims (4)

1. non-crack nm-class Ti-based anode, form by titanium matrix (1) and outer (2), between titanium matrix (1) and outer (2) internal layer (3) can be arranged, it is characterized in that, titanium matrix (1) is pure titanium plate, outer (2) are made up of metal oxide containing precious metals and non-noble metal oxide, metal oxide containing precious metals is following two kinds of oxide compounds: in iridium dioxide and the ruthenium dioxide one to two kind, non-noble metal oxide is following two kinds of oxide compounds: a kind of in titanium oxide and the tantalum oxide, the mol ratio of outer (2) interior precious metal and base metal is 1: 3~5: 1, outer (2) interior bullion content is relevant with the area of titanium matrix (1), this content is 4~40 gram/rice 2, internal layer (3) is an iridium dioxide, outer (2) surperficial leakless, and the oxide grain mean diameter that is deposited on skin (2) surface is less than 20 nanometers.
2. the preparation method of the described titanium substrate anode of claim 1 is characterized in that, operation steps:
The 1st step was cleaned titanium matrix (1), with 5% soda ash solution digestion titanium matrix (1) a hour, washing was immersed 10% oxalic acid solution again and was boiled two hours, washing, wash down with deionized water, dry back is stand-by, as not having internal layer (3) between titanium matrix (1) and outer (2), skipped for the 2nd step, entered for the 3rd step,, enter down the step as between titanium matrix (1) and outer (2) internal layer (3) being arranged;
The 2nd step deposition internal layer (3), the titanium matrix (1) that the last step was cleaned immerses masking liquid, take out after the dip-coating, put into the heated drying stove dry 10 minutes, drying temperature is 40~100 ℃, moves into warm air oxidized still oxidation 10 minutes then, and oxidizing temperature is 350~550 ℃, immerse masking liquid after the cooling again, dry again, oxidation, cooling repeats said process, and multiplicity is 3~5 times, the masking liquid that this step adopts is with the chloro-iridic acid that contains iridium 25~36 grams, 55~200 milliliters of hydrochloric acid, 250~750 milliliters of propyl carbinols, 250~750 milliliters of sol solutionses that are made into of Virahol, so far, internal layer (3) is deposited on the surface of titanium matrix (1);
The 3rd step deposition outer (2), make the work in-process immersion masking liquid that finished product obtained the last step, below operation is that 15~30 times and last oxidization time are one hour except multiplicity, all the other all go on foot together with the 2nd, the masking liquid that adopts of this step mixes and is made into containing iridium concentration and containing sol solutions that tantalum concentration is respectively the iridium salt of 6.3~10.5 grams per liters and 4~6 grams per liters and tantalum salt, or with chloro-iridic acid 160~220 gram, ruthenium trichloride 180~250 grams, tetrabutyl titanate 2400~3200 grams, 7000~10000 milliliters of sol solutionses that are made into of propyl carbinol, so far, outer (2) are deposited on the surface of titanium matrix (1) or internal layer (3), obtain finished product, titanium substrate anode.
3. according to the preparation method of the described titanium substrate anode of claim 2, it is characterized in that operation steps:
Do not have internal layer (3) between the 1st step titanium matrix (1) and outer (2), directly entered for the 3rd step, all the other are identical with the 1st step corresponding part of claim 2;
The 3rd step drying temperature, oxidizing temperature and multiplicity are respectively 50 ± 5 ℃, 480 ± 5 ℃ and 25 times, the masking liquid that adopts of this step mixes and is made into containing iridium concentration and containing sol solutions that tantalum concentration is respectively the iridium salt of 8.4 grams per liters and 5 grams per liters and tantalum salt, and to go on foot corresponding part identical with the 3rd of claim 2 for all the other.
4. according to the preparation method of the described titanium substrate anode of claim 2, it is characterized in that operation steps:
Between the 1st step titanium matrix (1) and outer (2) internal layer (3) is arranged, enter down the step, all the other are identical with the 1st step corresponding part of claim 2;
The 2nd step drying temperature, oxidizing temperature and multiplicity are respectively 50 ± 5 ℃, 450 ± ℃ and 3 times, the masking liquid that this step adopts is with 600 milliliters of 160 milliliters of chloro-iridic acid, hydrochloric acid, propyl carbinols and 600 milliliters of sol solutionses that are made into of Virahol of containing iridium 64.5 grams, and all the other are identical with the 2nd step corresponding part of claim 2;
The 3rd step drying temperature, oxidizing temperature and multiplicity are respectively 50 ± 5 ℃, 450 ± 5 ℃ and 20 times, the masking liquid that this step adopts is with chloro-iridic acid 195 grams, ruthenium trichloride 230 grams, tetrabutyl titanate 2700 grams, 8600 milliliters of sol solutionses that are made into of propyl carbinol, and all the other are identical with the 3rd step corresponding part of claim 2.
CNB001256149A 2000-09-30 2000-09-30 Non-crack nm-class Ti-based anode and its preparing process Expired - Fee Related CN1156612C (en)