CN114940838A - 一种建筑用负离子除醛无机涂料及其制备方法 - Google Patents
一种建筑用负离子除醛无机涂料及其制备方法 Download PDFInfo
- Publication number
- CN114940838A CN114940838A CN202210696587.9A CN202210696587A CN114940838A CN 114940838 A CN114940838 A CN 114940838A CN 202210696587 A CN202210696587 A CN 202210696587A CN 114940838 A CN114940838 A CN 114940838A
- Authority
- CN
- China
- Prior art keywords
- aldehyde
- removing inorganic
- building
- nano
- titanate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种建筑用负离子除醛无机涂料及其制备方法，具体涉及除醛无机涂料领域，该负离子除醛无机涂料由以下质量份的各物质组成：碱金属硅酸盐：20‑26；乳液：3‑10；纳米TiO2：15‑25；纳米钛酸盐：5‑10；CaCO3：10‑15；HEC：0.3‑0.5；云母粉：2‑5；生物基除醛剂：1.5‑3.5；稳定剂：0.1‑0.3；消泡剂：0.2‑0.5；分散剂：0.3‑0.5；阻聚剂：0.3‑0.5；水：15‑25，本发明利用硅酸钾的特性，将其进行酸改性，向硅酸钾中加入无机酸或有机酸对硅酸钾/硅溶胶改性，减少游离的NaOH的含量。将合成树脂乳液作为辅助成膜物质与硅酸盐等无机基料复合使用，使有机树脂填充在—Si—O—Si—网状结构的间隙中，从而减少涂膜对水的敏感程度，还能延缓涂膜在冷热交替时的伸缩，防止开裂。
Description
技术领域
本发明属于建筑涂装领域，尤其涉及一种建筑用负离子除醛无机涂料及其制备方法。
背景技术
建筑物内外涂装是美化建筑物、改善居住环境和改进建筑物原有性能的一个重要方面，尽管现代建筑主体结构是用不燃材料建造的,但是表面涂装材料基本以有机成膜物为主，不具有阻燃性，因此，负离子除醛无机涂料对建筑涂装意义重大。
室内空气污染对人体危害较大，我们从普通室内空气中检出了500多种有机物，其中最常见的、大家普遍关注的室内污染物主要有甲醛、苯、甲苯、二甲苯、氨和总挥发性有机物，这些污染物对人体的危害主要有：致癌作用、抑制酶活性导致机体的损害和致突变作用导致遗传性突变。
目前，室内空气主要污染物就是甲醛，主要来自制作家具及室内装修的人造板，生产人造板的胶粘剂是脲醛树脂，这种材料会持续缓慢释放甲醛，严重污染室内环境，影响人体健康。国际癌症研究所将甲醛列为可疑致癌物质。
负离子除醛无机涂料料只是建筑涂料中的一种，负离子除醛无机涂料有别于其他建筑涂料，其一：除醛耐火涂料是以碱金属硅酸盐为主要成膜物制备的的一种装饰型材料，普遍用作室内外装修时表面涂装，是建筑装饰不可或缺的一种主要材料，其二：负离子除醛无机涂料形成的涂膜耐光、净化空气性能优良，防火性好，硬度较高，耐污染性好，耐老化优异等诸多优点而越来越受到人们的关注与青睐；因此，提供一种能除醛、释放负离子、阻燃的建筑涂料，对建筑持久安全及居家健康起到有力的保障。
发明内容
为了克服现有技术的上述缺陷，本发明的实施例提供一种建筑用负离子除醛无机涂料及其制备方法，通过利用硅酸钾的特性，将其进行酸改性，向硅酸钾中加入无机酸或有机酸对硅酸钾进行改性，在硅酸钾中生产新的盐或复盐，减少游离的NaOH的含量，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种建筑用负离子除醛无机涂料，由以下质量份的各物质组成：
碱金属硅酸盐：20-26；
建筑乳液：3-10；
HEC：0.3-0.5；
纳米TiO2：15-25；
纳米钛酸盐：5-10
云母粉：2-5；
CaCO3：10-15
生物基除醛剂：1.5-3.5
稳定剂：0.1-0.3；
阻聚剂：0.3-0.5；
pH调节剂：0.1-0.3；
分散剂：0.3-0.5；
消泡剂：0.2-0.5；
水：15-25。
在一个优选地实施方式中，所述碱金属硅酸盐为硅酸钾、硅酸钠、硅酸锂等溶液中的一种或多种。
在一个优选地实施方式中，所述建筑乳液为丙烯酸脂聚合乳液。
在一个优选地实施方式中，所述纳米TiO2为金红石型纳米TiO2。
在一个优选地实施方式中，所述纳米钛酸盐为钛酸钡、钛酸锶、钛酸钠、钛酸钙中的一种或多种。
在一个优选地实施方式中，所述稳定剂为磷酸三钠、三聚磷酸钠、碱金属偏磷酸盐或聚偏磷酸盐、多聚磷酸钠中的一种或多种。
在一个优选地实施方式中，所述阻聚剂为三氯化钛、硫酸钠、硫氰酸铵中的一种或多种。
在一个优选地实施方式中，所述分散剂为聚羧酸钠盐、聚丙烯酸铵盐中的一种或两种。
在一个优选地实施方式中，所述消泡剂为有机硅类、矿物油类、金属皂中的一种或多种。
在一个优选地实施方式中，所述建筑用负离子除醛无机涂料，由以下质量份的各物质组成：
碱金属硅酸盐：26；
pH调节剂：0.2；
铵分散剂：0.45；
消泡剂：0.4；
HEC：0.4；
纳米TiO2：22；
纳米钛酸盐：10；
云母粉：2；
CaCO3：10；
生物基除醛剂：2；
乳液：6；
稳定剂：0.1；
阻聚剂：0.4；
水：20。
一种建筑用负离子除醛无机涂料的制备方法，包括以下步骤：
S1：向搅拌罐中投入碱金属硅酸盐,加入pH调节剂搅拌均匀。
S2：按配方量向搅拌罐中投入分散剂、消泡剂搅拌均匀。
S3：缓慢投入HEC充分搅拌均匀，至HEC完全溶解。
S4：投入重质碳酸钙、云母粉、纳米TiO2、纳米钛酸盐和生物基除醛剂剂搅拌均匀。
S5：将上述混合料通过砂磨机或者其他磨细设备研磨至细度小于60μm。再将磨细后的混合料转移至搅拌罐中。
S6：向搅拌罐中投入乳液搅拌均匀。
S7：在搅拌罐中的物料处于搅拌状态下，投入稳定剂、阻聚剂、水搅拌均匀，即得到成品。
根据上述的一种负离子除醛无机涂料的制备方法，所述S1：中碱金属硅酸盐为硅酸钾，所述S4：中纳米钛酸盐为钛酸钡，且各组分按以下质量比依次加入：
硅酸钾：26；
pH调节剂：0.2；
铵分散剂：0.45；
消泡剂：0.4；
HEC：0.4；
纳米TiO2：22；
纳米钛酸钡：10；
云母粉：2；
CaCO3：10；
生物基除醛剂：2；
乳液：6；
稳定剂：0.1；
阻聚剂：0.4；
水：20。
本发明的技术效果和优点：
1、本发明利用硅酸钾的特性，将其进行酸改性，向硅酸钾中加入无机酸或有机酸对硅酸钾进行改性，在硅酸钾中生产新的盐或复盐，减少游离的NaOH 的含量。将合成树脂乳液作为辅助成膜物质与硅酸盐等无机基料复合使用，使有机树脂填充在—Si—O—Si—网状结构的间隙中，屏蔽残存的羟基，从而减少涂膜对水的敏感程度，还能延缓涂膜在冷热交替时的伸缩，防止开裂；
2、本发明采用钛酸钡为“永久电极”，无需外部能源可持续产生电流，与空气中水蒸气和氧气发生电离反应，持续产生O2 -和H3O2 -负离子。当负氧离子遇到室内的甲醛、甲苯有毒有害气体时会产生反应结合后，使结构产生改变或能量的转移，从而去除或转化为无毒无害物质；
3、本发明采用生物基除醛剂对空气中甲醛吸附并进行化学反应，生成稳定的高分子无毒物质，不会产生二次污染，不像活性炭等材料只吸附不消灭；
4、本发明一种建筑用负离子除醛无机涂料的制备方法简单易行，得到的负离子除醛无机涂料溶于水，易处理，无环境危害，与无机类基材有牢固的黏结力，膜层的硬度高，不容易受到机械损伤，具有难燃性、无烟性，在发生火灾时能延缓火势的持续扩大，同时能有效净化甲醛，为居家环境提供有力保障，具有很大的应用前景。
附图说明
图1为本发明的制备材料配比范围示意图。
图2为本发明的制备材料配比示意图。
图3为本发明的实施例一材料配比示意图。
图4为本发明的实施例二材料配比示意图。
图5为本发明的实施例三材料配比示意图。
图6为本发明的实施例实验对比示意图。
图7为本发明的制备方法流程示意图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
参照说明书附图1-7，本发明一实施例的一种建筑用负离子除醛无机涂料，由以下质量份的各物质组成：
碱金属硅酸盐：20-26；
建筑乳液：3-10；
HEC：0.3-0.5；
纳米TiO2：15-25；
纳米钛酸盐：5-10
云母粉：2-5；
CaCO3：10-15
生物基除醛剂：1.5-3.5
稳定剂：0.1-0.3；
阻聚剂：0.3-0.5；
pH调节剂：0.1-0.3；
分散剂：0.3-0.5；
消泡剂：0.2-0.5；
水15-25。
同时，碱金属硅酸盐为硅酸钾、硅酸钠、硅酸锂等溶液中的一种或多种。
同时，建筑乳液为丙烯酸脂聚合乳液。
同时，纳米TiO2为金红石型纳米TiO2。
同时，纳米钛酸盐为钛酸钡、钛酸锶、钛酸钠、钛酸钙中的一种或多种。
同时，稳定剂为磷酸三钠、三聚磷酸钠、碱金属偏磷酸盐或聚偏磷酸盐、多聚磷酸钠中的一种或多种。
同时，阻聚剂为三氯化钛、硫酸钠、硫氰酸铵中的一种或多种。
同时，分散剂为聚羧酸钠盐、聚丙烯酸铵盐中的一种或两种。
同时，消泡剂为有机硅类、矿物油类、金属皂中的一种或多种。
同时，建筑用负离子除醛无机涂料，由以下质量份的各物质组成。
一种建筑用负离子除醛无机涂料的制备方法，包括以下步骤：
S1：向搅拌罐中投入碱金属硅酸盐,加入pH调节剂搅拌均匀。
S2：按配方量向搅拌罐中投入分散剂、消泡剂搅拌均匀。
S3：缓慢投入HEC充分搅拌均匀，至HEC完全溶解。
S4：投入重质碳酸钙、云母粉、纳米TiO2、纳米钛酸盐和生物基除醛剂剂搅拌均匀。
S5：将上述混合料通过砂磨机或者其他磨细设备研磨至细度小于60μm。再将磨细后的混合料转移至搅拌罐中。
S6：向搅拌罐中投入乳液搅拌均匀。
S7：在搅拌罐中的物料处于搅拌状态下，投入稳定剂、阻聚剂、水搅拌均匀，即得到成品。
根据上述的一种负离子除醛无机涂料的制备方法，所述S1：中碱金属硅酸盐为硅酸钾，所述S4：中纳米钛酸盐为钛酸钡，且各组分按以下质量比依次加入：
硅酸钾：26；
pH调节剂：0.2；
铵分散剂：0.45；
消泡剂：0.4；
HEC：0.4；
纳米TiO2：22；
纳米钛酸钡：10；
云母粉：2；
CaCO3：10；
生物基除醛剂：2；
乳液：6；
稳定剂：0.1；
阻聚剂：0.4；
水：20。
实例1：建筑用负离子除醛无机涂料，由以下质量份的各物质组成：
硅酸钾：23；
pH调节剂：0.2；
铵分散剂：0.45；
消泡剂：0.4；
HEC：0.4；
纳米TiO2：22；
纳米钛酸钡：8；
云母粉：2；
CaCO3：12；
生物基除醛剂：2；
乳液：6；
稳定剂：0.1；
阻聚剂：0.4；
水：23。
本发明的建筑用负离子除醛无机涂的制备方法如下：
S1：向搅拌罐中投入硅酸钾,加入pH调节剂搅拌均匀。
S2：按配方量向搅拌罐中投入分散剂、消泡剂搅拌均匀。
S3：缓慢投入HEC充分搅拌均匀，至HEC完全溶解。
S4：投入重质碳酸钙、云母粉、纳米TiO2、纳米钛酸钡和生物基除醛剂剂搅拌均匀。
S5：将上述混合料通过砂磨机或者其他磨细设备研磨至细度小于60μm。再将磨细后的混合料转移至搅拌罐中。
S6：向搅拌罐中投入乳液搅拌均匀。
S7：在搅拌罐中的物料处于搅拌状态下，投入稳定剂、阻聚剂、水搅拌均匀，即得到成品。
实例2：建筑用负离子除醛无机涂料，由以下质量份的各物质组成：
硅酸钾：24；
pH调节剂：0.2；
铵分散剂：0.45；
消泡剂：0.4；
HEC：0.4；
纳米TiO2：22；
纳米钛酸钡：9；
云母粉：2；
CaCO3：11；
生物基除醛剂：2；
乳液：6；
稳定剂：0.1；
阻聚剂：0.4；
水：22。
本发明的建筑用负离子除醛无机涂料的制备方法如下：
S1：向搅拌罐中投入硅酸钾,加入pH调节剂搅拌均匀。
S2：按配方量向搅拌罐中投入分散剂、消泡剂搅拌均匀。
S3：缓慢投入HEC充分搅拌均匀，至HEC完全溶解。
S4：投入重质碳酸钙、云母粉、纳米TiO2、纳米钛酸钡和生物基除醛剂剂搅拌均匀。
S5：将上述混合料通过砂磨机或者其他磨细设备研磨至细度小于60μm。再将磨细后的混合料转移至搅拌罐中。
S6：向搅拌罐中投入乳液搅拌均匀。
S7：在搅拌罐中的物料处于搅拌状态下，投入稳定剂、阻聚剂、水搅拌均匀，即得到成品。
实例3：建筑用负离子除醛无机涂料，由以下质量份的各物质组成：
硅酸钾：26；
pH调节剂：0.2；
铵分散剂：0.45；
消泡剂：0.4；
HEC：0.4；
纳米TiO2：22；
纳米钛酸钡：10；
云母粉：2；
CaCO3：10；
生物基除醛剂：2；
乳液：6；
稳定剂：0.1；
阻聚剂：0.4；
水：20。
本发明的建筑用负离子除醛无机涂料的制备方法如下：
S1：向搅拌罐中投入硅酸钾,加入pH调节剂搅拌均匀。
S2：按配方量向搅拌罐中投入分散剂、消泡剂搅拌均匀。
S3：缓慢投入HEC充分搅拌均匀，至HEC完全溶解。
S4：投入重质碳酸钙、云母粉、纳米TiO2、纳米钛酸钡和生物基除醛剂剂搅拌均匀。
S5：将上述混合料通过砂磨机或者其他磨细设备研磨至细度小于60μm。再将磨细后的混合料转移至搅拌罐中。
S6：向搅拌罐中投入乳液搅拌均匀。
S7：在搅拌罐中的物料处于搅拌状态下，投入稳定剂、阻聚剂、水搅拌均匀，即得到成品。
将实施例1-3和对比产品(市售无机涂料)做对比试验，检测其耐洗刷性、耐沾污性、燃烧时间、耐碱性、负离子浓度、除醛性，结果如下：
通过以上检测结果可知，本发明的建筑用负离子除醛无机涂料耐洗刷性优异、耐沾污性好，除醛性能优异，且难燃系数大大优于市场同类产品，本发明一种建筑用负离子除醛无机涂料的制备方法简单易行，具有很大的应用前景。
其次：本发明公开实施例附图中，只涉及到与本公开实施例涉及到的结构，其他结构可参考通常设计，在不冲突情况下，本发明同一实施例及不同实施例可以相互组合；
最后：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种建筑用负离子除醛无机涂料，由以下质量份的各物质组成：
碱金属硅酸盐：20-26；
建筑乳液：3-10；
HEC：0.3-0.5；
纳米TiO2：15-25；
纳米钛酸盐：5-10
云母粉：2-5；
CaCO3：10-15
生物基除醛剂：1.5-3.5
稳定剂：0.1-0.3；
阻聚剂：0.3-0.5；
pH调节剂：0.1-0.3；
分散剂：0.3-0.5；
消泡剂：0.2-0.5；
水15-25。
2.根据权利要求1所述的一种建筑用负离子除醛无机涂料，其特征在于，所述碱金属硅酸盐为硅酸钾、硅酸钠、硅酸锂等溶液中的一种或多种。
3.根据权利要求1所述的一种建筑用负离子除醛无机涂料，其特征在于：所述建筑乳液为丙烯酸脂聚合乳液。
4.根据权利要求1所述的一种建筑用负离子除醛无机涂料，其特征在于，所述纳米TiO2为金红石型纳米TiO2。
5.根据权利要求1所述的一种建筑用负离子除醛无机涂料，其特征在于，所述纳米钛酸盐为钛酸钡、钛酸锶、钛酸钠、钛酸钙中的一种或多种。
6.根据权利要求1所述的一种建筑用负离子除醛无机涂料，其特征在于，所述稳定剂为磷酸三钠、三聚磷酸钠、碱金属偏磷酸盐或聚偏磷酸盐、多聚磷酸钠中的一种或多种。
7.根据权利要求1所述的一种建筑用负离子除醛无机涂料，其特征在于，所述阻聚剂为三氯化钛、硫酸钠、硫氰酸铵中的一种或多种。
8.根据权利要求1所述的一种建筑用负离子除醛无机涂料，其特征在于，所述分散剂为聚羧酸钠盐、聚丙烯酸铵盐中的一种或两种。
9.根据权利要求1所述的一种建筑用负离子除醛无机涂料，其特征在于，所述消泡剂为有机硅类、矿物油类、金属皂中的一种或多种。
10.根据权利要求1至9所述的一种建筑用负离子除醛无机涂料，其特征在于，所述建筑用负离子除醛无机涂料，由以下质量份的各物质组成：
碱金属硅酸盐：26；
pH调节剂：0.2；
铵分散剂：0.45；
消泡剂：0.4；
HEC：0.4；
纳米TiO2：22；
纳米钛酸盐：10；
云母粉：2；
CaCO3：10；
生物基除醛剂：2；
乳液：6；
稳定剂：0.1；
阻聚剂：0.4；
水：20。
一种建筑用负离子除醛无机涂料的制备方法，其特征在于，包括以下步骤：
S1：向搅拌罐中投入碱金属硅酸盐,加入pH调节剂搅拌均匀。
S2：按配方量向搅拌罐中投入分散剂、消泡剂搅拌均匀。
S3：缓慢投入HEC充分搅拌均匀，至HEC完全溶解。
S4：投入重质碳酸钙、云母粉、纳米TiO2、纳米钛酸盐和生物基除醛剂剂搅拌均匀。
S5：将上述混合料通过砂磨机或者其他磨细设备研磨至细度小于60μm。再将磨细后的混合料转移至搅拌罐中。
S6：向搅拌罐中投入乳液搅拌均匀。
S7：在搅拌罐中的物料处于搅拌状态下，投入稳定剂、阻聚剂、水搅拌均匀，即得到成品。
根据上述的一种负离子除醛无机涂料的制备方法，其特征在于，所述S1：中碱金属硅酸盐为硅酸钾，所述S4：中纳米钛酸盐为钛酸钡，且各组分按以下质量比依次加入：
硅酸钾：26；
pH调节剂：0.2；
铵分散剂：0.45；
消泡剂：0.4；
HEC：0.4；
纳米TiO2：22；
纳米钛酸钡：10；
云母粉：2；
CaCO3：10；
生物基除醛剂：2；
乳液：6；
稳定剂：0.1；
阻聚剂：0.4；
水：20。