CN114248511A - 一种高效热防护铝箔玻纤复合织物 - Google Patents
一种高效热防护铝箔玻纤复合织物 Download PDFInfo
- Publication number
- CN114248511A CN114248511A CN202111584415.4A CN202111584415A CN114248511A CN 114248511 A CN114248511 A CN 114248511A CN 202111584415 A CN202111584415 A CN 202111584415A CN 114248511 A CN114248511 A CN 114248511A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- aluminum foil
- adhesive
- silicon dioxide
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高效热防护铝箔玻纤复合织物，涉及防护织物领域。本发明包括：S01、纳米二氧化硅表面改性：将纳米二氧化硅与去离子水进行混合并超声，放入硅烷偶联剂KH550，高速搅拌以对纳米二氧化硅进行表面改性，分离烘干备用；S02、向有机硅树脂中添加有改性纳米二氧化硅，充分搅拌混合后制得纳米二氧化硅/有机硅树脂复合粘合剂；S03、取纳米二氧化硅/有机硅树脂复合粘合剂，均匀涂覆在玻璃纤维织物上，再将铝箔平整的贴于玻璃纤维织物表面，轧辊挤压多余的粘合剂就取出并放入至烘箱内，加热烘干升温。本发明制成的高效热防护铝箔玻纤复合织物具有更加优异的热防护性能以及更加优异的玻璃性能，适于广泛应用并推广。
Description
技术领域
本发明属于防护织物领域，特别是涉及一种高效热防护铝箔玻纤复合织物。
背景技术
在各种火灾中，热源温度高达1500摄氏度，通过热传导、热对流以及热辐射的方式传递热量，严重危害消防员的生命安全。在消防领域，利用铝箔/玻璃纤维织物复合面料制备的热防护服应用广泛。
铝箔/玻璃纤维织物复合织物是以玻璃纤维织物为基布，表面复合铝箔制备而成，具有优良的热防护性能，外层铝箔可以对90％以上的反射辐射热进行反射，大大减少进入织物内的热量，从而有效保护人体不受危害，内层的玻纤织物主要起到支撑作用。然而，粘结剂仅仅具有粘合铝箔和玻纤织物的作用，不能起到热防护作用，复合织物的热防护性能还有待进一步提升。
针对这一问题，本发明拟采用纳米二氧化硅添加技术，制备一种高效热防护铝箔玻纤复合织物，对于提高消防员的个体防护能力具有重要的意义。
发明内容
本发明提供了一种高效热防护铝箔玻纤复合织物，解决了以上问题。
为解决上述技术问题，本发明是通过以下技术方案实现的：
本发明的一种高效热防护铝箔玻纤复合织物，采用如下步骤制备而成：
S01、纳米二氧化硅表面改性：将纳米二氧化硅与去离子水以质量份数1:20进行混合并超声一定时间，接着放入纳米二氧化硅质量份数0.5-1.5％的硅烷偶联剂KH550，高速搅拌以对纳米二氧化硅进行表面改性，持续一定时间后通过过滤的方法将纳米二氧化硅和去离子水分离，烘干备用；
S02、向有机硅树脂中添加有机硅胶树脂质量份数为2-6％的改性纳米二氧化硅，充分搅拌混合后制得纳米二氧化硅/有机硅树脂复合粘合剂；
S03、取15ml纳米二氧化硅/有机硅树脂复合粘合剂，均匀涂覆在玻璃纤维织物上，再将铝箔平整的贴于玻璃纤维织物表面，送入轧辊，挤压多余的粘合剂就取出并放入至烘箱内，80℃加热40min后保温5min，继续升温至120℃并保温5min，再加热至160℃并保温5min。
进一步地，所述有机硅树脂采用端基或侧基带有-OH、NH2、-CONH2、-COOR、-COOH、-COR基团的聚硅氧烷的其中一种或多种混合物。
进一步地，所述纳米二氧化硅为疏水性气相二氧化硅，粒径为75-125nm。
进一步地，所述铝箔的厚度为0.02mm。
本发明相对于现有技术包括有以下有益效果：
本发明制成的高效热防护铝箔玻纤复合织物具有更加优异的热防护性能以及更加优异的玻璃性能，适于广泛应用并推广。
当然，实施本发明的任一产品并不一定需要同时达到以上所述的所有优点。
附图说明
为了更清楚地说明本发明实施例的技术方案，下面将对实施例描述所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1为本发明一种高效热防护铝箔玻纤复合织物制成后的结构示意图；
图2为本发明制备方法的流程步骤图；
图3为发明具体实施例添加不同比例二氧化硅的铝箔玻纤复合织物热防护性能折线图；
图4为本发明具体实施例添加不同比例二氧化硅的铝箔玻纤复合织物热剥离性能折线图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
具体实施例1：
请参阅图1-2所示，本实施例的一种高效热防护铝箔玻纤复合织物，采用如下步骤制备而成：
S01、纳米二氧化硅表面改性：将纳米二氧化硅与去离子水以质量份数1:20进行混合并超声45min，接着放入纳米二氧化硅质量份数1％的硅烷偶联剂KH550，高速搅拌以对纳米二氧化硅进行表面改性，持续30min后通过过滤的方法将纳米二氧化硅和去离子水分离，烘干备用；
S02、向有机硅树脂中添加有机硅胶树脂质量份数为2％的改性纳米二氧化硅，充分搅拌混合后制得纳米二氧化硅/有机硅树脂复合粘合剂；
S03、取15ml纳米二氧化硅/有机硅树脂复合粘合剂，均匀涂覆在玻璃纤维织物上，再将铝箔平整的贴于玻璃纤维织物表面，送入轧辊，挤压多余的粘合剂就取出并放入至烘箱内，80℃加热40min后保温5min，继续升温至120℃并保温5min，再加热至160℃并保温5min。
其中，有机硅树脂采用端基或侧基带有-OH、NH2、-CONH2、-COOR、-COOH、-COR基团的聚硅氧烷的其中一种或多种混合物，本具体实施例中采用带-OH基团的聚硅氧烷。
其中，纳米二氧化硅为疏水性气相二氧化硅，粒径为75-125nm。
其中，铝箔的厚度为0.02mm。
具体实施例2：
本具体实施例相对于具体实施例1的区别在于：S02步骤中添加有机硅胶树脂质量份数为4％的改性纳米二氧化硅；有机硅树脂采用端基带NH2基团的聚硅氧烷。
具体实施例3：
本具体实施例相对于具体实施例1的区别在于：S02步骤中添加有机硅胶树脂质量份数为6％的改性纳米二氧化硅；有机硅树脂采用侧基带-CONH2基团的聚硅氧烷。
按照上述三个具体实施例进行添加对应比例的二氧化硅并制备形成对应的铝箔玻纤复合织物，并测试其热防护性能，获得如图3所示的折线图；由此图可知，随着二氧化硅添加比例的逐渐增长，该铝箔玻纤复合织物材料的热防护性能逐渐增加。
对应的，采用上述三个具体实施例进行添加对应比例的二氧化硅并制备形成对应的铝箔玻纤复合织物，并测试其对剥离能力，获得如图4所示的折线图，由图可知，随着二氧化硅添加比例的逐渐增长，该铝箔玻纤复合织物材料的剥离能力即对应的剥离强力逐渐下降。
有益效果：
本发明制成的高效热防护铝箔玻纤复合织物具有更加优异的热防护性能以及更加优异的玻璃性能，适于广泛应用并推广。
以上公开的本发明优选实施例只是用于帮助阐述本发明。优选实施例并没有详尽叙述所有的细节，也不限制该发明仅为所述的具体实施方式。显然，根据本说明书的内容，可作很多的修改和变化。本说明书选取并具体描述这些实施例，是为了更好地解释本发明的原理和实际应用，从而使所属技术领域技术人员能很好地理解和利用本发明。本发明仅受权利要求书及其全部范围和等效物的限制。
Claims (4)
1.一种高效热防护铝箔玻纤复合织物，其特征在于，采用如下步骤制备而成：
S01、纳米二氧化硅表面改性：将纳米二氧化硅与去离子水以质量份数1:20进行混合并超声一定时间，接着放入纳米二氧化硅质量份数0.5-1.5％的硅烷偶联剂KH550，高速搅拌以对纳米二氧化硅进行表面改性，持续一定时间后通过过滤的方法将纳米二氧化硅和去离子水分离，烘干备用；
S02、向有机硅树脂中添加有机硅胶树脂质量份数为2-6％的改性纳米二氧化硅，充分搅拌混合后制得纳米二氧化硅/有机硅树脂复合粘合剂；
S03、取15ml纳米二氧化硅/有机硅树脂复合粘合剂，均匀涂覆在玻璃纤维织物上，再将铝箔平整的贴于玻璃纤维织物表面，送入轧辊，挤压多余的粘合剂就取出并放入至烘箱内，80℃加热40min后保温5min，继续升温至120℃并保温5min，再加热至160℃并保温5min。
2.根据权利要求1所述的一种高效热防护铝箔玻纤复合织物，其特征在于，所述有机硅树脂采用端基或侧基带有-OH、NH2、-CONH2、-COOR、-COOH、-COR基团的聚硅氧烷的其中一种或多种混合物。
3.根据权利要求1所述的一种高效热防护铝箔玻纤复合织物，其特征在于，所述纳米二氧化硅为疏水性气相二氧化硅，粒径为75-125nm。
4.根据权利要求1所述的一种高效热防护铝箔玻纤复合织物，其特征在于，所述铝箔的厚度为0.02mm。