CN1140424C - Production process of stainless steel wheel for motor vehicle - Google Patents
Production process of stainless steel wheel for motor vehicle Download PDFInfo
- Publication number
- CN1140424C CN1140424C CNB001109383A CN00110938A CN1140424C CN 1140424 C CN1140424 C CN 1140424C CN B001109383 A CNB001109383 A CN B001109383A CN 00110938 A CN00110938 A CN 00110938A CN 1140424 C CN1140424 C CN 1140424C
- Authority
- CN
- China
- Prior art keywords
- wheel
- forming
- wheel rim
- spoke
- technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a production technology of a stainless steel wheel for a motor vehicle, which relates to machining processes of a wheel rim and a wheel spoke and a press fitting process of the wheel rim and the wheel spoke. The technical process of the wheel rim orderly comprises: blanking, edge rolling, butt weld, slag scrape, flaring, first roll shape, second roll shape, expansion, air valve hole punching, polish and surface treatment to a press fitting line; the technical process of the wheel spoke can be divided into a punching technology and a spinning technology, wherein the punching technology comprises: blanking, first to third forming, combination punching, screw hole squeeze, ventilating hole punching, ventilating hole squeeze, machine work and surface treatment to a press fitting line, and the spinning technology comprises: a spinning forming process replaces the first to third forming of the punching technology, and the other processes are in the same with the punching technology; the wheel rim and the wheel spoke is welded to form a wheel set at the press fitting lines. The technology is used for producing a stainless steel wheel, the equipment investment of the stainless steel wheel is approximately in the same with that of an ordinary steel wheel, and the wheel displays the special performance, the appearance and the luxurious brightness of stainless steel.
Description
Technical field:
The utility model relates to a kind of vehicle wheels production technology.
Background technology:
Existing wheel can be divided into steel wheel, aluminum-alloy wheel and steel aluminium built-up wheel by its manufactured materials.Steel wheel rim adopts rolling technology, and spoke adopts Sheet Metal Forming Technology, form by press-fiting the final application of welding, and low price, simple, the small investment of technology, shortcoming is that product specification is low, aesthetic measure is poor.Aluminum-alloy wheel is to form by molten refining, casting, heat treatment, machinework and surface treatment, has luxurious attractive in appearance, in light weight, the product precision advantages of higher of external form, and shortcoming is that equipment has high input, reject rate height, product price height.Steel aluminium built-up wheel adopts ordinary steel ratch rim and aluminum alloy spoke assembling seam, the characteristics of aluminum alloy spoke and steel wheel rim have been taken into account, price is between two kinds of wheels, shortcoming is that rim surface need be electroplated, easily cause industrial pollution, the aluminum alloy spoke equally needs huge investment with aluminum-alloy wheel in addition.
Summary of the invention:
It is the vehicle wheels production technology of material with the corrosion-resistant steel that the purpose of this utility model provides a kind of, utilizes this explained hereafter corrosion-resistant steel wheel, and equipment investment is few, roughly suitable with the steel wheel investment, and makes wheel body reveal the distinctive performance of corrosion-resistant steel.
The purpose of this utility model realizes as follows: this production technology relates to the process that press-fits of the course of processing of wheel rim and spoke and the two, and the course of processing of wheel rim is: blanking → volume circle → butt welding → scrape slag → enlarging → one time roll-forming → secondary roll-forming → expanding → valve hole → polishing → surface treatment → to pressing assembly; The spoke course of processing can adopt Sheet Metal Forming Technology or spinning process, and the Sheet Metal Forming Technology of spoke is: blanking → one-shot forming → post forming → three time moulding → connection dashes → squeezes screw → towards breather port → squeeze breather port → machinework → surface treatment → to pressing assembly; The spinning process of spoke is: blanking → spin forming → connection dashes → squeezes screw → towards breather port → squeeze breather port → machinework → surface treatment → to pressing assembly; At pressing assembly wheel rim and spoke are welded as wheel set; Wherein, in the course of processing of wheel rim, the furling plate round machine roller surface sand-blast finish of wheel rim volume sired results preface, wheel rim enlarging operation adopts the enlarging of expanding formula, and expanding mold design modulus of resilience 0.15% reduces shaping expanding amount as far as possible, and the expanding amount is controlled at about 5mm; The running roller of wheel rim roll-forming operation need adopt Cr12 alloy die steel and laser hardening, laser transformation hardening, and the surface of running roller needs ground finish; Forming force in roll-in, punching press, spin forming process needs bigger by 20% than general steel; Duration of light is 5-6 second in welding process, and the welding machine upset force increases by 15% than ordinary steel; Glossing or other shotblasting and electrochemical treatment technology are adopted in surface treatment.
Adopt this production technology, can produce stainless steel wheel for motor vehicle, corrosion-resistant steel is greatly improved the strength at repeated alternation of wheel with the high and unique mechanical characteristics of its intensity, has greatly improved travel safety and the reliability of wheel under the high-speed cruising state; Unique elegance that corrosion-resistant steel has after with its good anti-oxidant, resistant to corrosion ability and polishing and electrochemical treatment is firmly got user's favor.Needn't carry out pickling to material in the corrosion-resistant steel wheel production process, reduce aerial contamination and water and polluted.
The specific embodiment:
Production process of stainless steel wheel for motor vehicle comprises the process that press-fits of the course of processing of wheel rim and spoke and the two.The course of processing of wheel rim is: blanking → volume circle → butt welding → scrape slag → enlarging → one time roll-forming → secondary roll-forming → expanding → valve hole → polishing → surface treatment → to pressing assembly; The spoke course of processing can adopt Sheet Metal Forming Technology or spinning process, and the Sheet Metal Forming Technology of spoke is: blanking → one-shot forming → post forming → three time moulding → connection dashes → squeezes screw → towards breather port → squeeze breather port → machinework → surface treatment → to pressing assembly; The spinning process of spoke is: blanking → spin forming → connection dashes → squeezes screw → towards breather port → squeeze breather port → machinework → surface treatment → to pressing assembly; At pressing assembly wheel rim and spoke are welded as wheel set.Because corrosion-resistant steel is lower than carbon structural steel superficial hardness, in the course of processing and transport process, cause easily and scratch and collide with, this brings difficulty can for the polishing of final workpiece, influence surface quality of products, thereby require the per pass operation all to take appropriate measures to guarantee the surface quality of workpiece, the scuffing of stopping to collide with, take following measure: the roller at wheel rim volume sired results ordered pair furling plate round machine carries out the surface sand-blasting processing for this reason, make volume circle roller surface finer and smoother, promptly guarantee the required friction force of volume circle, guaranteed the surface quality of workpiece again; Wheel rim enlarging operation is the easiest operation that causes scuffing, existing enlarging process mould adopts two cones, there are Frictional Slipping in cone and workpiece during enlarging, produce very big friction force, directly affect product design, even it is also of no avail with the change roughness to improve die surface hardness, after engineer testing adopts the enlarging of expanding formula, problem is satisfactorily resolved; Wheel rim roll-forming operation also is to be easy to generate the operation that workpiece scratches, the way that solves is to adopt the Cr12 alloy die steel through laser hardening, laser transformation hardening, the pair roller wheel surface carries out ground finish in addition, improve the hardness on running roller surface and reduced roughness of surface, adopt the external hydraulic-driven roller pressing forming machine of introducing in addition, roller pressing forming machine two main shafts are adjusted automatically, guaranteed two running roller linear velocity unanimities, avoid the friction of roll-forming process middle roll and workpiece that workpiece is formed scuffing; Other operation and spoke stamping, spinning operation to wheel rim are also taked corresponding measure, accomplish that the work piece production process does not roll off the production line, and transform the raceway and the transhipment working position apparatus of manufacturing line.Corrosion-resistant steel has higher mechanical strength than common material, and resistance of deformation is bigger by 20% than common material in the process of roll-forming, punch forming, spin forming, and corresponding forming force also strengthens 20%; Corrosion-resistant steel has bigger springback capacity man-hour adding, and takes corresponding measure reducing and compensate resilience on mold design and technological parameter are determined, modulus of resilience presses 0.15% during the design of expanding mould.Corrosion-resistant steel has higher work hardening characteristic, inter process in repeatedly moulding very easily produces work hardening, when serious even cause be full of cracks, whether rationally be key of success, should rationally arrange technology and definite technological parameter if handling in the technological design, reduce to process number of times as far as possible, control rational work hardening capacity, reduce shaping expanding amount as far as possible during design wheel rim technology and avoid the expanding cracking, generally be controlled at about 5mm, avoid roll compacting excessively in the roll-forming process; Corrosion-resistant steel compares permeability of heat with carbon structural steel and electric conductivity is relatively poor, fusion temperature is low, heat is slower to the periphery diffusion in the welding process, require the secondary non-load voltage of welding machine to want high when therefore welding, require flash of light stable violent in the welding process, the time is 5~6 seconds, requires welding machine to have bigger upset force, increase 15% than ordinary steel, to produce enough plastic deformation at weld zone.Be to reduce the oxidation of high-temperature metal in the weld bond, begin, finish the flash of light process with maximum flashing speed with the flashing speed of minimum.Because the stainless steel hot conductance is little, the line expansion factor is big, under patterned heat and cooling condition, welded joint may form bigger tensile stress in cooling process, corrosion-resistant steel easily forms the very strong column crystal seam organization of directivity simultaneously, has impelled the segregation of impurity such as S, P, form the interdendritic liquid interlayer, therefore cause thermal crack easily, select low power welding conditions and welding speed faster when adopting submerged arc-welding, on solder flux is selected, select of the generation of SJ601 sintered flux for use with the minimizing thermal crack.The corrosion-resistant steel wheel has been cancelled the pickling and the painting process of material in the steel car wheel production process, no acid solution, waste water and discharge of harmful gases.The appearance of corrosion-resistant steel wheel depends on polishing process and surface treatment, adopts glossing or other surface polishing and electrochemical treatment technology, makes wheel surface reach pure and fresh bright and clean, luxurious beautiful impression.
Claims (1)
- A kind of production process of stainless steel wheel for motor vehicle, relate to the process that press-fits of the course of processing of wheel rim and spoke and the two, the course of processing of wheel rim is: blanking → volume circle → butt welding → scrape slag → enlarging → one time roll-forming → secondary roll-forming → expanding → valve hole → polishing → surface treatment → to pressing assembly; The spoke course of processing can adopt Sheet Metal Forming Technology or spinning process, and the Sheet Metal Forming Technology of spoke is: blanking → one-shot forming → post forming → three time moulding → connection dashes → squeezes screw → towards breather port → squeeze breather port → machinework → surface treatment → to pressing assembly; The spinning process of spoke is: blanking → spin forming → connection dashes → squeezes screw → towards breather port → squeeze breather port → machinework → surface treatment → to pressing assembly; At pressing assembly wheel rim and spoke are welded as wheel set; Wherein, in the course of processing of wheel rim, the furling plate round machine roller surface sand-blast finish of wheel rim volume sired results preface, wheel rim enlarging operation adopts the enlarging of expanding formula, expanding mold design modulus of resilience 0.15%, the expanding amount is controlled at about 5mm; The running roller of wheel rim roll-forming operation need adopt Cr12 alloy die steel and laser hardening, laser transformation hardening, and the surface of running roller needs ground finish; Forming force in roll-in, punching press, spin forming process needs bigger by 20% than general steel; Duration of light is 5-6 second in welding process, and the welding machine upset force increases by 15% than ordinary steel; Glossing or other shotblasting and electrochemical treatment technology are adopted in surface treatment.