CN113817349B - Acrylic acid modified polysiloxane coating and preparation method thereof - Google Patents
Acrylic acid modified polysiloxane coating and preparation method thereof Download PDFInfo
- Publication number
- CN113817349B CN113817349B CN202111286040.3A CN202111286040A CN113817349B CN 113817349 B CN113817349 B CN 113817349B CN 202111286040 A CN202111286040 A CN 202111286040A CN 113817349 B CN113817349 B CN 113817349B
- Authority
- CN
- China
- Prior art keywords
- ingredient
- acrylic
- functional groups
- following components
- modified polysiloxane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to the technical field of heavy-duty anticorrosive coatings, in particular to an acrylic acid modified polysiloxane coating and a preparation method thereof. The material comprises a first material and a second material, wherein the first material comprises the following components in parts by weight: 20-30% of acrylic resin containing active hydrogen functional groups, 10-20% of polysiloxane intermediate containing phenyl/methyl functional groups, 20-30% of pigment and filler, 0.1-0.5% of rheological additive, 5-20% of composite environment-friendly solvent, 0.2-1% of flatting agent, 10-15% of methyl methacrylate and 3-7% of butyl acrylate. The ingredient II comprises the following components in parts by weight: 20-30% of organic silicon resin containing active hydroxyl groups, 5-10% of organic siloxane containing reactive glycidoxy and methoxy groups and 0.1-0.5% of catalyst. The invention can effectively keep color and luster for a long time by adding the polysiloxane resin, and can be used as a part of a high-performance anti-corrosion coating system; the invention provides a plurality of functional groups for the system, and the functional groups are mutually catalyzed and reacted, so that the crosslinking density is high. The product has the characteristics of long adaptation period, quick drying, good chemical resistance and the like.
Description
Technical Field
The invention relates to the technical field of heavy-duty anticorrosive coatings, in particular to an acrylic acid modified polysiloxane coating and a preparation method thereof.
Background
The polysiloxane coating is divided into acrylic polysiloxane and epoxy polysiloxane. The gloss and color durability of acrylic modified polysiloxane coatings was significantly better than typical polyurethane finishes and retention of gloss and color was better than that of the first generation epoxy modified polysiloxane finishes. In addition, compared with the traditional epoxy resin technology, the acrylic modified polysiloxane coating has the same corrosion resistance and slightly superior mechanical properties. There are currently two main classes of acrylic polysiloxanes: one is the addition and hydrolytic condensation between acrylic resin containing double bonds and siloxane, and the other is the hydrolytic crosslinking reaction between acrylic resin polysiloxane intermediate and alkylamino. The former can be thickly coated, but the reaction is complex, the influence by the environment is large, and the influence on the later-period resistance of the coating is large; the latter is generally suggested as a thin coating, and is greatly affected by air humidity, and is inferior in gloss stability, so that acrylic polysiloxane is limited in practical application and popularization.
Disclosure of Invention
The invention aims to provide an acrylic acid modified polysiloxane coating and a preparation method thereof, which are used for solving the problems in the process.
In order to achieve the purpose, the invention provides the following technical scheme: an acrylic modified polysiloxane coating comprises a first ingredient and a second ingredient, wherein the first ingredient comprises the following components in parts by weight: 20-30% of acrylic resin containing active hydrogen functional groups, 10-20% of polysiloxane intermediate containing phenyl/methyl functional groups, 20-30% of pigment and filler, 0.1-0.5% of rheological additive, 5-20% of composite environment-friendly solvent, 0.2-1% of flatting agent, 10-15% of methyl methacrylate and 3-7% of butyl acrylate;
the ingredient II comprises the following components in parts by weight: 20-30% of organic silicon resin containing active hydroxyl groups, 5-10% of organic siloxane containing reactive glycidoxy and methoxy groups and 0.1-0.5% of catalyst.
Preferably, the leveling agent is a polyether modified polymethyl alkyl siloxane solution.
Preferably, the catalyst is an organic titanium compound.
Preferably, the ingredient I comprises the following components in parts by weight: 20% of acrylic resin containing active hydrogen functional groups, 10% of polysiloxane intermediate containing phenyl/methyl functional groups, 20% of pigment and filler, 0.3% of rheological additive, 10% of composite environment-friendly solvent, 0.2% of flatting agent, 10% of methyl methacrylate and 3% of butyl acrylate.
Preferably, the ingredient two comprises the following components in parts by weight: 20 percent of organic silicon resin containing active hydroxyl groups, 6.1 percent of organic siloxane containing reactive epoxy propoxy and methoxy groups and 0.4 percent of catalyst.
A method for using an acrylic modified polysiloxane coating comprises the following operation steps:
the method comprises the following steps: preparing a first ingredient; adding acrylic resin into a kettle, adding pigment and filler at the rotating speed of 500 plus one year 1000r/min, increasing the rotating speed to 1000 plus one year 1500r/min, dispersing at a high speed, grinding until the fineness is less than 25 mu m, adding polysiloxane resin, rheological additive, composite environment-friendly solvent and flatting agent while dispersing at 500 plus one year 1000r/min, and continuously rotating for fifteen minutes;
step two: perfecting a first ingredient; filtering the solution obtained on the basis of the step one for the first time, continuously stirring the solution, adding 10-15 parts of methyl methacrylate and butyl acrylate in the stirring process, continuously stirring for ten minutes, and then filtering again to obtain a material I;
step three: and preparing a second ingredient, namely mixing and stirring the organic silicon resin containing the active hydroxyl group and the organic siloxane containing the reactive glycidoxy group and the methoxy group in a kettle, and continuously adding the catalyst in the stirring process. At the moment, the second ingredient can be prepared;
step four: mixing materials; mixing the ingredient I in the step II with the ingredient II in the step III, and after the ingredient I and the ingredient II are uniformly mixed, filtering the mixture by a 100-200-mesh filter screen and directly spraying the mixture on a base material coated with the primer.
Compared with the prior art, the invention has the beneficial effects that:
1. the invention can effectively keep color and luster for a long time by adding the polysiloxane resin, and can be used as a part of a high-performance anti-corrosion coating system;
2. the invention provides a plurality of functional groups for the system, and the functional groups are mutually catalyzed and reacted, so that the crosslinking density is high. The product has the characteristics of long adaptation period, quick drying, good chemical resistance and the like;
3. according to the invention, through the addition of the butyl acrylate monomer and the high-solid low-viscosity resin, the solid content of the coating can be improved, the VOC emission is reduced, the one-time coating rate is high, the film forming is uniform, and the gloss stability is good.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The invention provides a technical scheme that:
example one
An acrylic modified polysiloxane coating comprises a first ingredient and a second ingredient, wherein the first ingredient comprises the following components in parts by weight: 20-30% of acrylic resin containing active hydrogen functional groups, 10-20% of polysiloxane intermediate containing phenyl/methyl functional groups, 20-30% of pigment and filler, 0.1-0.5% of rheological additive, 5-20% of composite environment-friendly solvent, 0.2-1% of flatting agent, 10-15% of methyl methacrylate and 3-7% of butyl acrylate;
the ingredient II comprises the following components in parts by weight: 20-30% of organic silicon resin containing active hydroxyl groups, 5-10% of organic siloxane containing reactive glycidoxy and methoxy groups and 0.1-0.5% of catalyst.
Preferably, the leveling agent is a polyether modified polymethyl alkyl siloxane solution.
Preferably, the catalyst is an organic titanium compound.
Preferably, the ingredient I comprises the following components in parts by weight: 20% of acrylic resin containing active hydrogen functional groups, 10% of polysiloxane intermediate containing phenyl/methyl functional groups, 20% of pigment and filler, 0.3% of rheological additive, 10% of composite environment-friendly solvent, 0.2% of flatting agent, 10% of methyl methacrylate and 3% of butyl acrylate.
Preferably, the ingredient two comprises the following components in parts by weight: 20 percent of organic silicon resin containing active hydroxyl groups, 6.1 percent of organic siloxane containing reactive epoxy propoxy and methoxy groups and 0.4 percent of catalyst.
A method for using an acrylic modified polysiloxane coating comprises the following operation steps:
the method comprises the following steps: preparing a first ingredient; adding acrylic resin into a kettle, adding pigment and filler at the rotating speed of 500 plus one year 1000r/min, increasing the rotating speed to 1000 plus one year 1500r/min, dispersing at a high speed, grinding until the fineness is less than 25 mu m, adding polysiloxane resin, rheological additive, composite environment-friendly solvent and flatting agent while dispersing at 500 plus one year 1000r/min, and continuously rotating for fifteen minutes;
step two: perfecting a first ingredient; filtering the solution obtained on the basis of the step one for the first time, continuously stirring the solution, adding 10-15 parts of methyl methacrylate and butyl acrylate in the stirring process, continuously stirring for ten minutes, and then filtering again to obtain a material I;
step three: and preparing a second ingredient, namely mixing and stirring the organic silicon resin containing the active hydroxyl group and the organic siloxane containing the reactive glycidoxy group and the methoxy group in a kettle, and continuously adding the catalyst in the stirring process. At the moment, the second ingredient can be prepared;
step four: mixing materials; mixing the ingredient I in the step II with the ingredient II in the step III, and after the ingredient I and the ingredient II are uniformly mixed, filtering the mixture by a 100-200-mesh filter screen and directly spraying the mixture on a base material coated with the primer.
Example two
An acrylic modified polysiloxane coating comprises a first ingredient and a second ingredient, wherein the first ingredient comprises the following components in parts by weight: 20-30% of acrylic resin containing active hydrogen functional groups, 10-20% of polysiloxane intermediate containing phenyl/methyl functional groups, 20-30% of pigment and filler, 0.1-0.5% of rheological additive, 5-20% of composite environment-friendly solvent, 0.2-1% of flatting agent, 10-15% of methyl methacrylate and 3-7% of butyl acrylate;
the ingredient II comprises the following components in parts by weight: 20-30% of organic silicon resin containing active hydroxyl groups, 5-10% of organic siloxane containing reactive glycidoxy and methoxy groups and 0.1-0.5% of catalyst.
Preferably, the leveling agent is a polyether modified polymethyl alkyl siloxane solution.
Preferably, the catalyst is an organic titanium compound.
Preferably, the ingredient I comprises the following components in parts by weight: 21% of acrylic resin containing active hydrogen functional groups, 10% of polysiloxane intermediate containing phenyl/methyl functional groups, 20% of pigment and filler, 0.3% of rheological additive, 10% of composite environment-friendly solvent, 0.2% of flatting agent, 10% of methyl methacrylate and 3% of butyl acrylate.
Preferably, the ingredient two comprises the following components in parts by weight: 22 percent of organic silicon resin containing active hydroxyl groups, 3.1 percent of organic siloxane containing reactive epoxy propoxy and methoxy groups and 0.4 percent of catalyst.
A method for using an acrylic modified polysiloxane coating comprises the following operation steps:
the method comprises the following steps: preparing a first ingredient; adding acrylic resin into a kettle, adding pigment and filler at the rotating speed of 500 plus one year 1000r/min, increasing the rotating speed to 1000 plus one year 1500r/min, dispersing at a high speed, grinding until the fineness is less than 25 mu m, adding polysiloxane resin, rheological additive, composite environment-friendly solvent and flatting agent while dispersing at 500 plus one year 1000r/min, and continuously rotating for fifteen minutes;
step two: perfecting a first ingredient; filtering the solution obtained on the basis of the step one for the first time, continuously stirring the solution, adding 10-15 parts of methyl methacrylate and butyl acrylate in the stirring process, continuously stirring for ten minutes, and then filtering again to obtain a material I;
step three: and preparing a second ingredient, namely mixing and stirring the organic silicon resin containing the active hydroxyl group and the organic siloxane containing the reactive glycidoxy group and the methoxy group in a kettle, and continuously adding the catalyst in the stirring process. At the moment, the second ingredient can be prepared;
step four: mixing materials; mixing the ingredient I in the step II with the ingredient II in the step III, and after the ingredient I and the ingredient II are uniformly mixed, filtering the mixture by a 100-200-mesh filter screen and directly spraying the mixture on a base material coated with the primer.
EXAMPLE III
An acrylic modified polysiloxane coating comprises a first ingredient and a second ingredient, wherein the first ingredient comprises the following components in parts by weight: 20-30% of acrylic resin containing active hydrogen functional groups, 10-20% of polysiloxane intermediate containing phenyl/methyl functional groups, 20-30% of pigment and filler, 0.1-0.5% of rheological additive, 5-20% of composite environment-friendly solvent, 0.2-1% of flatting agent, 10-15% of methyl methacrylate and 3-7% of butyl acrylate;
the ingredient II comprises the following components in parts by weight: 20-30% of organic silicon resin containing active hydroxyl groups, 5-10% of organic siloxane containing reactive glycidoxy and methoxy groups and 0.1-0.5% of catalyst.
Preferably, the leveling agent is a polyether modified polymethyl alkyl siloxane solution.
Preferably, the catalyst is an organic titanium compound.
Preferably, the ingredient I comprises the following components in parts by weight: 25% of acrylic resin containing active hydrogen functional groups, 10% of polysiloxane intermediate containing phenyl/methyl functional groups, 22% of pigment and filler, 0.3% of rheological additive, 5% of composite environment-friendly solvent, 0.2% of flatting agent, 10% of methyl methacrylate and 3% of butyl acrylate.
Preferably, the ingredient two comprises the following components in parts by weight: 20 percent of organic silicon resin containing active hydroxyl groups, 4.1 percent of organic siloxane containing reactive epoxy propoxy and methoxy groups and 0.4 percent of catalyst.
A method for using an acrylic modified polysiloxane coating comprises the following operation steps:
the method comprises the following steps: preparing a first ingredient; adding acrylic resin into a kettle, adding pigment and filler at the rotating speed of 500 plus one year 1000r/min, increasing the rotating speed to 1000 plus one year 1500r/min, dispersing at a high speed, grinding until the fineness is less than 25 mu m, adding polysiloxane resin, rheological additive, composite environment-friendly solvent and flatting agent while dispersing at 500 plus one year 1000r/min, and continuously rotating for fifteen minutes;
step two: perfecting a first ingredient; filtering the solution obtained on the basis of the step one for the first time, continuously stirring the solution, adding 10-15 parts of methyl methacrylate and butyl acrylate in the stirring process, continuously stirring for ten minutes, and then filtering again to obtain a material I;
step three: and preparing a second ingredient, namely mixing and stirring the organic silicon resin containing the active hydroxyl group and the organic siloxane containing the reactive glycidoxy group and the methoxy group in a kettle, and continuously adding the catalyst in the stirring process. At the moment, the second ingredient can be prepared;
step four: mixing materials; mixing the ingredient I in the step II with the ingredient II in the step III, and after the ingredient I and the ingredient II are uniformly mixed, filtering the mixture by a 100-200-mesh filter screen and directly spraying the mixture on a base material coated with the primer.
Example four
An acrylic modified polysiloxane coating comprises a first ingredient and a second ingredient, wherein the first ingredient comprises the following components in parts by weight: 20-30% of acrylic resin containing active hydrogen functional groups, 10-20% of polysiloxane intermediate containing phenyl/methyl functional groups, 20-30% of pigment and filler, 0.1-0.5% of rheological additive, 5-20% of composite environment-friendly solvent, 0.2-1% of flatting agent, 10-15% of methyl methacrylate and 3-7% of butyl acrylate;
the ingredient II comprises the following components in parts by weight: 20-30% of organic silicon resin containing active hydroxyl groups, 5-10% of organic siloxane containing reactive glycidoxy and methoxy groups and 0.1-0.5% of catalyst.
Preferably, the leveling agent is a polyether modified polymethyl alkyl siloxane solution.
Preferably, the catalyst is an organic titanium compound.
Preferably, the first ingredient comprises the following components in parts by weight: 23% of acrylic resin containing active hydrogen functional groups, 10% of polysiloxane intermediate containing phenyl/methyl functional groups, 23% of pigment and filler, 0.3% of rheological additive, 5% of composite environment-friendly solvent, 0.2% of flatting agent, 10% of methyl methacrylate and 3% of butyl acrylate.
Preferably, the ingredient two comprises the following components in parts by weight: 20 percent of organic silicon resin containing active hydroxyl groups, 5.1 percent of organic siloxane containing reactive epoxy propoxy and methoxy groups and 0.4 percent of catalyst.
A method for using an acrylic modified polysiloxane coating comprises the following operation steps:
the method comprises the following steps: preparing a first ingredient; adding acrylic resin into a kettle, adding a pigment and filler at the rotating speed of 500-1000r/min, increasing the rotating speed to 1000-1500r/min for high-speed dispersion, grinding until the fineness is less than 25um, adding polysiloxane resin, rheological additive, composite environment-friendly solvent and flatting agent while dispersing at 500-1000r/min, and continuously rotating for fifteen minutes;
step two: perfecting a first ingredient; filtering the solution obtained on the basis of the step one for the first time, continuously stirring the solution, adding 10-15 parts of methyl methacrylate and butyl acrylate in the stirring process, continuously stirring for ten minutes, and then filtering again to obtain a material I;
step three: and preparing a second ingredient, namely mixing and stirring the organic silicon resin containing the active hydroxyl group and the organic siloxane containing the reactive glycidoxy group and the methoxy group in a kettle, and continuously adding the catalyst in the stirring process. At the moment, the second ingredient can be prepared;
step four: mixing materials; mixing the ingredient I in the step II with the ingredient II in the step III, and after the ingredient I and the ingredient II are uniformly mixed, filtering the mixture by a 100-200-mesh filter screen and directly spraying the mixture on a base material coated with the primer.
To summarize: experiments show that: the acrylic silicone coating obtained in the embodiments 1-4 of the invention has the advantages of high dryness, good gloss stability, good weather resistance and good corrosion resistance.
The acrylic silicone coating obtained in example 1 was compared with a commercially available product to obtain data as shown in Table 1.
TABLE 1
From the data in table 1: all the performances of the acrylic acid modified polysiloxane prepared by the preparation method of the combination of the components in the embodiment 1 are obviously higher than technical indexes, especially the performances of gloss stability, acid resistance, alkali resistance, salt spray resistance, artificial aging resistance and the like.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that various changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (6)
1. An acrylic modified polysiloxane coating is characterized in that: the material comprises a first material and a second material, wherein the first material comprises the following components in percentage by weight: 20-30% of acrylic resin containing active hydrogen functional groups, 10-20% of polysiloxane intermediate containing phenyl/methyl functional groups, 20-30% of pigment and filler, 0.1-0.5% of rheological additive, 5-20% of composite environment-friendly solvent, 0.2-1% of flatting agent, 10-15% of methyl methacrylate and 3-7% of butyl acrylate; the ingredient II comprises the following components in percentage by weight: 20-30% of organic silicon resin containing active hydroxyl groups, 5-10% of organic siloxane containing reactive glycidoxy and methoxy groups and 0.1-0.5% of catalyst.
2. The acrylic-modified polysiloxane coating according to claim 1, wherein: the leveling agent is polyether modified polymethyl alkyl siloxane solution.
3. The acrylic-modified polysiloxane coating according to claim 1, wherein: the catalyst is an organic titanium compound.
4. The acrylic-modified polysiloxane coating according to claim 1, wherein: the ingredient I comprises the following components in percentage by weight: 20% of acrylic resin containing active hydrogen functional groups, 10% of polysiloxane intermediate containing phenyl/methyl functional groups, 20% of pigment and filler, 0.3% of rheological additive, 10% of composite environment-friendly solvent, 0.2% of flatting agent, 10% of methyl methacrylate and 3% of butyl acrylate.
5. The acrylic-modified polysiloxane coating according to claim 2, wherein: the ingredient II comprises the following components in percentage by weight: 20 percent of organic silicon resin containing active hydroxyl groups, 6.1 percent of organic siloxane containing reactive epoxy propoxy and methoxy groups and 0.4 percent of catalyst.
6. A method for preparing an acrylic modified polysiloxane coating material according to any one of claims 1 to 5, comprising the following steps: the method comprises the following steps: preparing a first ingredient; adding acrylic resin into a kettle, adding pigment and filler at the rotating speed of 500-1000r/min, increasing the rotating speed to 1000-1500r/min, dispersing at a high speed, grinding until the fineness is less than 25 mu m, adding a polysiloxane intermediate containing phenyl/methyl functional groups, a rheological aid, a composite environment-friendly solvent and a flatting agent while dispersing at the speed of 500-1000r/min, and continuously rotating for fifteen minutes; step two: perfecting a first ingredient; filtering the solution obtained on the basis of the step one for the first time, continuously stirring the solution, adding methyl methacrylate and butyl acrylate in the stirring process, continuously stirring for ten minutes, and then filtering again to obtain a first ingredient; step three: preparing a second ingredient, namely mixing and stirring the organic silicon resin containing the active hydroxyl group and the organic siloxane containing the reactive glycidoxy group and the methoxy group in a kettle, and continuously adding a catalyst in the stirring process, thus preparing the second ingredient; step four: mixing materials; mixing the ingredient I in the step II with the ingredient II in the step III, and after the ingredient I and the ingredient II are uniformly mixed, filtering the mixture by a 100-sand 200-mesh filter screen, and directly spraying the mixture on a base material coated with the primer.