CN113668013A - 基于巯基苯并噻唑制备双功能电解水催化剂的方法 - Google Patents
基于巯基苯并噻唑制备双功能电解水催化剂的方法 Download PDFInfo
- Publication number
- CN113668013A CN113668013A CN202111021574.3A CN202111021574A CN113668013A CN 113668013 A CN113668013 A CN 113668013A CN 202111021574 A CN202111021574 A CN 202111021574A CN 113668013 A CN113668013 A CN 113668013A
- Authority
- CN
- China
- Prior art keywords
- ldh
- foam
- catalyst
- nifemo
- foamed nickel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (2)