CN113354857A - 一种耐候性能优异的热转印树脂碳带及其制备方法 - Google Patents
一种耐候性能优异的热转印树脂碳带及其制备方法 Download PDFInfo
- Publication number
- CN113354857A CN113354857A CN202110692751.4A CN202110692751A CN113354857A CN 113354857 A CN113354857 A CN 113354857A CN 202110692751 A CN202110692751 A CN 202110692751A CN 113354857 A CN113354857 A CN 113354857A
- Authority
- CN
- China
- Prior art keywords
- thermal transfer
- parts
- transfer printing
- wax
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种耐候性能优异的热转印树脂碳带及其制备方法，热转印树脂碳带包括热转印油墨层、基材和背涂层，所述热转印油墨层和背涂层分别设置在基材的两侧面上，所述热转印油墨层包括氟碳改性丙烯酸树脂。本发明通过采用耐候性能优异氟碳改性的丙烯酸树脂为主体结构，所得树脂碳带可适用范围广，由于含氟碳改性丙烯酸树脂的比表面能低、化学键强度更高，稳定性能好，具有优异打印清晰度且具有更好抗刮、耐油、耐酒精、耐紫外线等优势。通过只设置热转印油墨层和背涂层，极大的缩减了制作工艺并有效降低了成本。
Description
技术领域
本发明涉及热转印相关技术领域，具体涉及一种耐候性能优异的热转印树脂碳带及其制备方法。
背景技术
热转印树脂碳带就是在一定温度下(110-160℃)将热转印油墨层熔融，并在一定压力下将油墨层从基材上剥离下来转印到纸或薄膜的过程，当标签通过打印机的打印头和压轴时，将热转印油墨转印到标签纸和薄膜标签上。
目前户外热转印打印标识在户外严苛环境条件下普遍存在易褪色、掉色等现象，此外常规树脂碳均不耐油和酒精。
越来越多的打印载体出现，传统的碳粉涂层难以保证打印效果以及其使用寿命，为此，不少人对碳粉涂层的配方进行改变，以求碳粉涂层能够适应不同的打印载体，有更好的显示效果。但是，单纯的改变碳粉涂层配方治标不治本，就是目前的碳带打印效果而言，还是容易出现碳粉转印牢度不高，容易掉色的问题。
发明内容
本发明所要解决的技术问题是针对现有技术的不足，提供一种耐候性能优异的热转印树脂碳带及其制备方法。
本发明解决上述技术问题的技术方案如下：一种耐候性能优异的热转印树脂碳带，包括热转印油墨层、基材和背涂层，所述热转印油墨层和背涂层分别设置在基材的两侧面上，所述热转印油墨层包括氟碳改性丙烯酸树脂。
本发明的有益效果是：本发明通过采用耐候性能优异氟碳改性的丙烯酸树脂为主体结构，所得树脂碳带可适用范围广，由于含氟碳改性丙烯酸树脂的比表面能低、化学键强度更高，稳定性能好，具有优异打印清晰度且具有更好抗刮、耐油、耐酒精、耐紫外线等优势。通过只设置热转印油墨层和背涂层，极大的缩减了制作工艺并有效降低了成本。
在上述技术方案的基础上，本发明还可以做如下改进。
进一步，以重量份计，所述热转印油墨层包括，氟碳改性的丙烯酸树脂1-25份，颜料1-20份、蜡1-5份、分散剂1-15份、醋酸丁酸纤维束1-10份。
采用上述进一步方案的有益效果是：热转印油墨层的主体树脂体系为含氟改性丙烯酸，该体系具有优异打印清晰度且具有更好抗刮、耐油、耐酒精、耐紫外线等优势，原因是含氟改性丙烯酸体系的比表面能低、化学键强度更高，化学键不容易稳定性能好。
进一步，以重量份计，所述热转印油墨层包括，氟碳改性的丙烯酸树脂15份，颜料15份、蜡2份、分散剂5份、醋酸丁酸纤维束2份。
采用上述进一步方案的有益效果是：采用该配方的热转印油墨层，具有良好的墨层结合牢固度以及耐磨性能好。
进一步，所述热转印油墨层中还包括耐紫外吸收剂。
采用上述进一步方案的有益效果是：添加耐紫外吸收剂，能够显著提高树脂碳带的耐紫外线性能和使用寿命。
进一步，所述耐紫外吸收剂包括苯井三唑和受阻胺自由基捕捉剂。
进一步，所述蜡包括巴西棕榈蜡、沙索蜡、氟碳蜡、聚乙烯蜡、合成蜡和微晶蜡中的至少一种；所述颜料包括有机颜料和无机颜料中一种。
进一步，以重量份计，所述背涂层包括，硝化纤维素100份、有机硅塑料1-30份、硬脂酸辛树脂1-40份、甲苯二异氰酸酯的芳香族聚异氰酸酯预聚物1-40份。
有机硅塑料耐高低温、耐水性好、高频绝缘性好，耐辐射、耐臭氧性好。
采用硬质酸锌树脂，具有良好的润滑性能
背涂层中在160℃的高温打印条件下，依然有很好润滑性能，使该打印效果能够更好适应恶劣环境下，延长打印头的使用寿命。
进一步，所述基材包括聚脂薄膜。
一种耐候性能优异的热转印树脂碳带的制备方法，包括：取颜料、分散剂加入丙二醇甲醚醋酸酯溶液中，充分搅拌后进行研磨，研磨后溶液中的颗粒粒径D90大小控制5-10μm，得到研磨液；在研磨液中添加2-丁酮、甲苯、蜡、氟碳改性的丙烯酸树脂，充分搅拌后得到热转印油墨涂布液，将热转印油墨涂布液涂布在基材上，并烘干得到热转印油墨层。
本发明的有益效果是：采用本发明的制备方法，制备得到的热转印树脂碳带，热转印油墨层具有良好的耐磨性能，墨层结合牢固性好。
具体实施方式
以下对本发明的原理和特征进行描述，所举实例只用于解释本发明，并非用于限定本发明的范围。
实施例1
本发明实施例的一种耐候性能优异的热转印树脂碳带，包括热转印油墨层、基材和背涂层，所述热转印油墨层和背涂层分别设置在基材的两侧面上，所述热转印油墨层包括氟碳改性丙烯酸树脂。通过采用耐候性能优异氟碳改性的丙烯酸树脂为主体结构，所得树脂碳带可适用范围广，由于含氟碳改性丙烯酸树脂的比表面能低、化学键强度更高，稳定性能好，具有优异打印清晰度且具有更好抗刮、耐油、耐酒精、耐紫外线等优势。通过只设置热转印油墨层和背涂层，极大的缩减了制作工艺并有效降低了成本。
本发明实施例中，以重量份计，所述热转印油墨层包括，氟碳改性的丙烯酸树脂1份，颜料1份、蜡1份、分散剂1份、醋酸丁酸纤维束1份。
所述热转印油墨层中还包括耐紫外吸收剂，能够提高热转印油墨层的使用寿命。所述耐紫外吸收剂包括苯井三唑和受阻胺自由基捕捉剂。
本发明实施例的所述蜡包括巴西棕榈蜡、沙索蜡、氟碳蜡、聚乙烯蜡、合成蜡和微晶蜡中的至少一种；所述颜料包括有机颜料和无机颜料中一种。
本发明实施例中，以重量份计，所述背涂层包括，硝化纤维素100份、有机硅塑料1份、硬脂酸辛树脂1份、甲苯二异氰酸酯的芳香族聚异氰酸酯预聚物40份。
本发明实施例的所述基材包括聚脂薄膜。
一种耐候性能优异的热转印树脂碳带的制备方法，包括：取颜料、分散剂加入丙二醇甲醚醋酸酯溶液中，充分搅拌后进行研磨，研磨后溶液中的颗粒粒径D90大小控制5-10μm，得到研磨液；在研磨液中添加2-丁酮、甲苯、蜡、氟碳改性的丙烯酸树脂，充分搅拌后得到热转印油墨涂布液，将热转印油墨涂布液涂布在基材上，并烘干得到热转印油墨层。采用本发明的制备方法，制备得到的热转印树脂碳带，热转印油墨层具有良好的耐磨性能，墨层结合牢固性好。
实施例2
本发明实施例的一种耐候性能优异的热转印树脂碳带，包括热转印油墨层、基材和背涂层，所述热转印油墨层和背涂层分别设置在基材的两侧面上，所述热转印油墨层包括氟碳改性丙烯酸树脂。通过采用耐候性能优异氟碳改性的丙烯酸树脂为主体结构，所得树脂碳带可适用范围广，由于含氟碳改性丙烯酸树脂的比表面能低、化学键强度更高，稳定性能好，具有优异打印清晰度且具有更好抗刮、耐油、耐酒精、耐紫外线等优势。通过只设置热转印油墨层和背涂层，极大的缩减了制作工艺并有效降低了成本。
本发明实施例，以重量份计，所述热转印油墨层包括，氟碳改性的丙烯酸树脂15份，颜料15份、蜡2份、分散剂5份、醋酸丁酸纤维束2份。
所述热转印油墨层中还包括耐紫外吸收剂，能够提高热转印油墨层的使用寿命。所述耐紫外吸收剂包括苯井三唑和受阻胺自由基捕捉剂。
本发明实施例的所述蜡包括巴西棕榈蜡、沙索蜡、氟碳蜡、聚乙烯蜡、合成蜡和微晶蜡中的至少一种；所述颜料包括有机颜料和无机颜料中一种。
本发明实施例中，以重量份计，所述背涂层包括，硝化纤维素100份、有机硅塑料15份、硬脂酸辛树脂20份、甲苯二异氰酸酯的芳香族聚异氰酸酯预聚物20份。
本发明实施例的所述基材包括聚脂薄膜。
一种耐候性能优异的热转印树脂碳带的制备方法，包括：取颜料、分散剂加入丙二醇甲醚醋酸酯溶液中，充分搅拌后进行研磨，研磨后溶液中的颗粒粒径D90大小控制5-10μm，得到研磨液；在研磨液中添加2-丁酮、甲苯、蜡、氟碳改性的丙烯酸树脂，充分搅拌后得到热转印油墨涂布液，将热转印油墨涂布液涂布在基材上，并烘干得到热转印油墨层。采用本发明的制备方法，制备得到的热转印树脂碳带，热转印油墨层具有良好的耐磨性能，墨层结合牢固性好。
实施例3
本发明实施例的一种耐候性能优异的热转印树脂碳带，包括热转印油墨层、基材和背涂层，所述热转印油墨层和背涂层分别设置在基材的两侧面上，所述热转印油墨层包括氟碳改性丙烯酸树脂。通过采用耐候性能优异氟碳改性的丙烯酸树脂为主体结构，所得树脂碳带可适用范围广，由于含氟碳改性丙烯酸树脂的比表面能低、化学键强度更高，稳定性能好，具有优异打印清晰度且具有更好抗刮、耐油、耐酒精、耐紫外线等优势。通过只设置热转印油墨层和背涂层，极大的缩减了制作工艺并有效降低了成本。
本发明实施例中，以重量份计，所述热转印油墨层包括，氟碳改性的丙烯酸树脂25份，颜料20份、蜡5份、分散剂15份、醋酸丁酸纤维束10份。
所述热转印油墨层中还包括耐紫外吸收剂，能够提高热转印油墨层的使用寿命。所述耐紫外吸收剂包括苯井三唑和受阻胺自由基捕捉剂。
本发明实施例的所述蜡包括巴西棕榈蜡、沙索蜡、氟碳蜡、聚乙烯蜡、合成蜡和微晶蜡中的至少一种；所述颜料包括有机颜料和无机颜料中一种。
本发明实施例中，以重量份计，所述背涂层包括，硝化纤维素100份、有机硅塑料30份、硬脂酸辛树脂40份、甲苯二异氰酸酯的芳香族聚异氰酸酯预聚物1份。
本发明实施例的所述基材包括聚脂薄膜。
一种耐候性能优异的热转印树脂碳带的制备方法，包括：取颜料、分散剂加入丙二醇甲醚醋酸酯溶液中，充分搅拌后进行研磨，研磨后溶液中的颗粒粒径D90大小控制5-10μm，得到研磨液；在研磨液中添加2-丁酮、甲苯、蜡、氟碳改性的丙烯酸树脂，充分搅拌后得到热转印油墨涂布液，将热转印油墨涂布液涂布在基材上，并烘干得到热转印油墨层。采用本发明的制备方法，制备得到的热转印树脂碳带，热转印油墨层具有良好的耐磨性能，墨层结合牢固性好。
对上述实施例的热转印树脂碳带进行墨层结合牢度性能测试、耐磨性能测试以及耐候性能测试。
对上述实施例的热转印树脂碳带打印的标识牌进行墨层结合牢度性能测试，测试标准为凸版装潢印刷品GB/T 7706-2008；实验室内温湿度:23±2℃，50±10％；作为实验样品的标识牌尺寸为300*35mm；标识牌表面光滑平整，色块均匀。测试方法：热转印后标识牌脱落面积均≤0.1，为合格。上述实施例的热转印树脂碳带打印的标识牌脱落面积均≤0.1。
对上述实施例的热转印树脂碳带打印的标识牌进行耐磨性能测试，测试标准为凸版装潢印刷品GB/T 7706-2008；实验室温湿度:23±2℃，50±10％。作为实验样品的标识牌尺寸为240*60mm。要求热转印后标识标牌表面光滑平整，色块均匀。测试方法：样品标识牌测试前后称重，测三组，热转印树脂碳带打印的标识牌的磨损量的平均值均≤2.0mg，为合格。上述每个实施例的热转印树脂碳带打印的标识牌的磨损量的平均值均≤2.0mg。
对上述实施例的热转印树脂碳带打印的标识牌进行耐候性能测试，耐候性能测试标准GB/T 16422.3-2014；实验室温湿度为23±2℃、50±10％。测试条件为紫外光照3600h，光照强度0.76W/cm2；要求热转印后标识标牌表面光滑平整，色块均匀无脱落且与标准品的色差值≤5。上述实施例的热转印树脂碳带打印的标识牌表面光滑平整，色块均匀无脱落且与标准品的色差值≤5。
在本发明中，除非另有明确的规定和限定，术语“安装”、“相连”、“连接”、“设置”等术语应做广义理解，例如，可以是固定连接，也可以是可拆卸连接，或成一体；可以是机械连接，也可以是电连接；可以是直接相连，也可以通过中间媒介间接相连，可以是两个元件内部的连通或两个元件的相互作用关系，除非另有明确的限定。对于本领域的普通技术人员而言，可以根据具体情况理解上述术语在本发明中的具体含义。
在本发明中，除非另有明确的规定和限定，第一特征在第二特征“上”或“下”可以是第一和第二特征直接接触，或第一和第二特征通过中间媒介间接接触。而且，第一特征在第二特征“之上”、“上方”和“上面”可是第一特征在第二特征正上方或斜上方，或仅仅表示第一特征水平高度高于第二特征。第一特征在第二特征“之下”、“下方”和“下面”可以是第一特征在第二特征正下方或斜下方，或仅仅表示第一特征水平高度小于第二特征。
在本说明书的描述中，参考术语“一个实施例”、“一些实施例”、“示例”、“具体示例”、或“一些示例”等的描述意指结合该实施例或示例描述的具体特征、结构、材料或者特点包含于本发明的至少一个实施例或示例中。在本说明书中，对上述术语的示意性表述不必须针对的是相同的实施例或示例。而且，描述的具体特征、结构、材料或者特点可以在任一个或多个实施例或示例中以合适的方式结合。此外，在不相互矛盾的情况下，本领域的技术人员可以将本说明书中描述的不同实施例或示例以及不同实施例或示例的特征进行结合和组合。
尽管上面已经示出和描述了本发明的实施例，可以理解的是，上述实施例是示例性的，不能理解为对本发明的限制，本领域的普通技术人员在本发明的范围内可以对上述实施例进行变化、修改、替换和变型。
Claims (9)
1.一种耐候性能优异的热转印树脂碳带，其特征在于，包括热转印油墨层、基材和背涂层，所述热转印油墨层和背涂层分别设置在基材的两侧面上，所述热转印油墨层包括氟碳改性丙烯酸树脂。
2.根据权利要求1所述一种耐候性能优异的热转印树脂碳带，其特征在于，以重量份计，所述热转印油墨层包括，氟碳改性的丙烯酸树脂1-25份，颜料1-20份、蜡1-5份、分散剂1-15份、醋酸丁酸纤维束1-10份。
3.根据权利要求2所述一种耐候性能优异的热转印树脂碳带，其特征在于，以重量份计，所述热转印油墨层包括，氟碳改性的丙烯酸树脂15份，颜料15份、蜡2份、分散剂5份、醋酸丁酸纤维束2份。
4.根据权利要求1至3任一项所述一种耐候性能优异的热转印树脂碳带，其特征在于，所述热转印油墨层中还包括耐紫外吸收剂。
5.根据权利要求4所述一种耐候性能优异的热转印树脂碳带，其特征在于，所述耐紫外吸收剂包括苯井三唑和受阻胺自由基捕捉剂。
6.根据权利要求2或3所述一种耐候性能优异的热转印树脂碳带，其特征在于，所述蜡包括巴西棕榈蜡、沙索蜡、氟碳蜡、聚乙烯蜡、合成蜡和微晶蜡中的至少一种；所述颜料包括有机颜料和无机颜料中一种。
7.根据权利要求1至3任一项所述一种耐候性能优异的热转印树脂碳带，其特征在于，以重量份计，所述背涂层包括，硝化纤维素100份、有机硅塑料1-30份、硬脂酸辛树脂1-40份、甲苯二异氰酸酯的芳香族聚异氰酸酯预聚物1-40份。
8.根据权利要求1至3任一项所述一种耐候性能优异的热转印树脂碳带，其特征在于，所述基材包括聚脂薄膜。
9.一种权利要求2至8任一项耐候性能优异的热转印树脂碳带的制备方法，其特征在于，包括：取颜料、分散剂加入丙二醇甲醚醋酸酯溶液中，充分搅拌后进行研磨，研磨后溶液中的颗粒粒径D90大小控制5-10μm，得到研磨液；在研磨液中添加2-丁酮、甲苯、蜡、氟碳改性的丙烯酸树脂，充分搅拌后得到热转印油墨涂布液，将热转印油墨涂布液涂布在基材上，并烘干得到热转印油墨层。