CN1132798A - 用作电阻加热元件的含铝铁基合金 - Google Patents
用作电阻加热元件的含铝铁基合金 Download PDFInfo
- Publication number
- CN1132798A CN1132798A CN95121729A CN95121729A CN1132798A CN 1132798 A CN1132798 A CN 1132798A CN 95121729 A CN95121729 A CN 95121729A CN 95121729 A CN95121729 A CN 95121729A CN 1132798 A CN1132798 A CN 1132798A
- Authority
- CN
- China
- Prior art keywords
- alloy
- ferrous
- room temperature
- ferrous alloy
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
组成(重量百分比) | ||||||||||||||
合金编号Fe | Al | Si | Ti | Mo | Zr | C | Ni | Y | B | Nb | Ta | Cr | Ce | |
1 | 91.5 | 8.5 | ||||||||||||
2 | 91.5 | 6.5 | 2.0 | |||||||||||
3 | 90.5 | 8.5 | 1.0 | |||||||||||
4 | 90.27 | 8.5 | 1.0 | 0.2 | 0.03 | |||||||||
5 | 90.17 | 8.5 | 0.1 | 1.0 | 0.2 | 0.03 | ||||||||
6 | 89.27 | 8.5 | 1.0 | 1.0 | 0.2 | 0.03 | ||||||||
7 | 89.17 | 8.5 | 0.1 | 1.0 | 1.0 | 0.2 | 0.03 | |||||||
8 | 93 | 6.5 | 0.5 | |||||||||||
9 | 94.5 | 5.0 | 0.5 | |||||||||||
10 | 92.5 | 6.5 | 1.0 | |||||||||||
11 | 75.0 | 5.0 | 20.0 | |||||||||||
12 | 71.5 | 8.5 | 20.0 | |||||||||||
13 | 72.25 | 5.0 | 0.5 | 1.0 | 1.0 | 0.2 | 0.03 | 20.0 | 0.02 | |||||
14 | 76.19 | 6.0 | 0.5 | 1.0 | 1.0 | 0.2 | 0.03 | 15.0 | 0.08 | |||||
15 | 81.19 | 6.0 | 0.5 | 1.0 | 1.0 | 0.2 | 0.03 | 10.0 | 0.08 | |||||
16 | 86.23 | 8.5 | 1.0 | 4.0 | 0.2 | 0.03 | 0.04 | |||||||
17 | 88.77 | 8.5 | 1.0 | 1.0 | 0.6 | 0.09 | 0.04 | |||||||
18 | 85.77 | 8.5 | 1.0 | 1.0 | 0.6 | 0.09 | 3.0 | 0.04 | ||||||
19 | 83.77 | 8.5 | 1.0 | 1.0 | 0.6 | 0.09 | 5.0 | 0.04 | ||||||
20 | 88.13 | 8.5 | 1.0 | 1.0 | 0.2 | 0.03 | 0.04 | 0.5 | 0.5 | |||||
21 | 61.48 | 8.5 | 30.0 | 0.02 | ||||||||||
22 | 88.90 | 8.5 | 0.1 | 1.0 | 1.0 | 0.2 | 0.3 | |||||||
23 | 87.60 | 8.5 | 0.1 | 2.0 | 1.0 | 0.2 | 0.6 | |||||||
24 | 余量 | 8.19 | 2.13 | |||||||||||
25 | 余量 | 8.30 | 4.60 | |||||||||||
26 | 余量 | 8.28 | 6.93 | |||||||||||
27 | 余量 | 8.22 | 9.57 | |||||||||||
28 | 余量 | 7.64 | 7.46 | |||||||||||
29 | 余量 | 7.47 | 0.32 | 7.53 | ||||||||||
30 | 84.75 | 8.0 | 6.0 | 0.8 | 0.1 | 0.25 | 0.1 | |||||||
31 | 85.10 | 8.0 | 6.0 | 0.8 | 0.1 | |||||||||
32 | 86.00 | 8.0 | 6.0 |
合金编号 | 热处理 | 试验温度(℃) | 屈服强度(ksi) | 抗拉强度(ksi) | 延伸率(%) | 面收缩率(%) |
1111 | ABAB | 2323800800 | 60.6055.193.191.94 | 73.7968.533.991.94 | 25.5023.56108.76122.20 | 41.4631.3972.4457.98 |
22 | AA | 23800 | 94.166.40 | 94.167.33 | 0.90107.56 | 1.5571.87 |
33 | AA | 23800 | 69.637.19 | 86.707.25 | 22.6494.00 | 28.0274.89 |
4444 | ABAB | 2323800800 | 70.1565.215.225.35 | 89.8585.017.495.40 | 29.8830.94144.70105.96 | 41.9735.6881.0575.42 |
55 | AB | 23800 | 73.629.20 | 92.689.86 | 27.32198.96 | 40.8389.19 |
66 | AA | 23800 | 74.509.97 | 93.8011.54 | 30.36153.00 | 40.8185.56 |
7777 | ABAB | 2323800800 | 79.2975.1010.367.60 | 99.1197.0910.369.28 | 19.6013.20193.30167.00 | 21.0716.0084.4682.53 |
88 | AA | 23800 | 51.104.61 | 66.535.14 | 35.80155.80 | 27.9655.47 |
99 | AA | 23800 | 37.775.56 | 59.676.09 | 34.20113.50 | 18.8848.82 |
1010 | AA | 23800 | 64.515.99 | 74.466.24 | 14.90107.86 | 1.4571.00 |
合金编号 | 热处理 | 试验温度(℃) | 屈服强度(ksi) | 抗拉强度(ksi) | 延伸率(%) | 面收缩率(%) |
13131313 | ACAC | 2323800800 | 151.90163.279.4925.61 | 185.88183.9617.5529.90 | 10.087.14210.9062.00 | 15.9821.5489.0157.66 |
1616 | AA | 23800 | 86.4814.50 | 107.4414.89 | 6.4694.64 | 7.0976.94 |
17171717 | ABAB | 2323800800 | 76.6669.689.3712.05 | 96.4491.1011.6814.17 | 27.4029.04111.10108.64 | 45.6739.7185.6975.67 |
20202020 | ABAB | 2323800800 | 88.6377.797.2213.58 | 107.0299.7011.1014.14 | 17.9424.06127.32183.40 | 28.6037.2080.3788.76 |
21212121 | DCDC | 2323800800 | 207.2985.6145.0348.58 | 229.76159.9855.5657.81 | 4.7038.0037.408.40 | 14.2532.6535.088.34 |
2222 | CC | 23800 | 67.8010.93 | 91.1311.38 | 26.00108.96 | 42.3079.98 |
2424 | EF | 2323 | 71.3069.30 | 84.3084.60 | 2322 | 3340 |
2525 | EF | 2323 | 73.3071.80 | 85.2086.90 | 3427 | 6860 |
2626 | EF | 2323 | 61.2061.20 | 83.2584.20 | 1521 | 1527 |
2727 | EF | 2323 | 59.60- | 86.9088.80 | 1318 | 1519 |
2828 | EE | 2323 | 60.4059.60 | 77.7079.80 | 3526 | 7458 |
合金编号 | 热处理 | 试验温度(℃) | 屈服强度(ksi) | 抗拉强度(ksi) | 延伸率(%) | 面收缩率(%) |
2929 | FF | 2323 | 62.2061.70 | 76.6086.80 | 1712 | 1712 |
3030 | 23650 | 97.6026.90 | 116.6028.00 | 438 | 586 | |
3131 | 23650 | 79.4038.50 | 104.3047.00 | 727 | 780 | |
3232 | 23650 | 76.8029.90 | 94.8032.70 | 735 | 586 |
样品支撑端 | 样品厚度(mil) | 加热时间(h) | 弯曲量 | ||
合金17 | 合金20 | 合金22 | |||
Onea | 30 | 16 | 1/8 | - | - |
Oneb | 30 | 21 | - | 3/8 | 1/8 |
两端 | 30 | 185 | - | 0 | 0 |
两端 | 10 | 68 | - | - | 1/8 |
样品 | 试验温度 | 蠕变断裂强度 (ksi) | |||
°F | ℃ | 10h | 100h | 1000h | |
1 | 1400 | 760 | 2.90 | 2.05 | 1.40 |
1500 | 816 | 1.95 | 1.35 | 0.95 | |
1600 | 871 | 1.20 | 0.90 | - | |
1700 | 925 | 0.90 | - | - | |
4 | 1400 | 760 | 3.50 | 2.50 | 1.80 |
1500 | 816 | 2.40 | 1.80 | 1.20 | |
1600 | 871 | 1.65 | 1.15 | - | |
1700 | 925 | 1.15 | - | - | |
5 | 1400 | 760 | 3.60 | 2.50 | 1.85 |
1500 | 816 | 2.40 | 1.80 | 1.20 | |
1600 | 871 | 1.65 | 1.15 | - | |
1700 | 925 | 1.15 | - | - | |
6 | 1400 | 760 | 3.50 | 2.60 | 1.95 |
1500 | 816 | 2.50 | 1.90 | 1.40 | |
1600 | 871 | 1.80 | 1.30 | - | |
1700 | 925 | 1.30 | - | - | |
7 | 1400 | 760 | 3.90 | 2.90 | 2.15 |
1500 | 816 | 2.80 | 2.00 | 1.65 | |
1600 | 871 | 2.00 | 1.50 | - | |
1700 | 925 | 1.50 | - | - | |
17 | 1400 | 760 | 3.95 | 3.0 | 2.3 |
1500 | 816 | 2.95 | 2.20 | 1.75 | |
1600 | 871 | 2.05 | 1.65 | 1.25 | |
1700 | 925 | 1.65 | 1.20 | - | |
20 | 1400 | 760 | 4.90 | 3.25 | 2.05 |
1500 | 816 | 3.20 | 2.20 | 1.65 | |
1600 | 871 | 2.10 | 1.55 | 1.0 | |
1700 | 925 | 1.56 | 0.95 | - |
样品 | 试验温度 | 蠕变断裂强度 (ksi) | |||
°F | ℃ | 10h | 100h | 1000h | |
22 | 1400 | 760 | 4.70 | 3.60 | 2.65 |
1500 | 816 | 3.55 | 2.60 | 1.35 | |
1600 | 871 | 2.50 | 1.80 | 1.25 | |
1700 | 925 | 1.80 | 1.20 | 1.0 |
Claims (26)