CN112844334A - Slag recovery circulating water purification adsorbent and preparation method thereof - Google Patents
Slag recovery circulating water purification adsorbent and preparation method thereof Download PDFInfo
- Publication number
- CN112844334A CN112844334A CN202011594542.8A CN202011594542A CN112844334A CN 112844334 A CN112844334 A CN 112844334A CN 202011594542 A CN202011594542 A CN 202011594542A CN 112844334 A CN112844334 A CN 112844334A
- Authority
- CN
- China
- Prior art keywords
- parts
- circulating water
- water purification
- emulsion
- slag recovery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a slag recovery circulating water purification adsorbent, which comprises the following components in parts by weight: 45-60 parts of polyacrylic resin, 30-60 parts of emulsion, 15-25 parts of nano particles, 0.5-1.5 parts of carbon black, 2-6 parts of thickening agent and 20-40 parts of deionized water. The invention has the beneficial effects that: the slag recovery circulating water purification adsorbent can effectively adsorb metal or mineral particles remained in slag recovery circulating water; prepared into strips, and can avoid the diffusion of the adsorbent after being wrapped by a wire mesh, thereby being beneficial to the recovery.
Description
Technical Field
The invention relates to purification of mineral wastewater, in particular to a slag recovery circulating water purification adsorbent and a preparation method thereof.
Background
A large amount of water is needed in the recovery process of valuable metals in the gold ore smelting waste slag, and although zero emission is realized to a great extent at present, the circulating water still needs to be replaced regularly. The replaced circulating water contains a certain amount of metal or mineral particles, but the content is low, and the metal or mineral particles are not enough to be recovered by large-scale mechanical equipment.
Disclosure of Invention
The invention provides a slag recovery circulating water purification adsorbent and a preparation method thereof, aiming at the problem of low purification efficiency of smelting circulating water by adopting mechanical equipment.
The technical scheme for solving the technical problems is as follows: the slag recovery circulating water purification adsorbent comprises the following components in parts by weight: 45-60 parts of polyacrylic resin, 30-60 parts of emulsion, 15-25 parts of nano particles, 0.5-1.5 parts of carbon black, 2-6 parts of thickening agent and 20-40 parts of deionized water.
Specifically, the emulsion is one or a combination of more of styrene-acrylate emulsion, acrylic emulsion or aqueous polyurethane emulsion; the nano particles are selected from one or more of nano magnesium oxide, nano magnesium hydroxide, nano zinc oxide or nano aluminum oxide; the thickening agent is one or more of starch, gelatin or CMC.
The invention also discloses a preparation method of the slag recycling circulating water purification adsorbent, which comprises the following steps: weighing the components according to the weight percentage, grinding and filtering the polyacrylic resin, mixing the ground polyacrylic resin with the nano particles, adding the mixture into emulsion, adding deionized water while stirring, adding carbon black and a thickening agent after continuously stirring uniformly, pouring the mixed solution into a strip-shaped mold after uniformly stirring, drying, demolding, and wrapping a blank mold with a metal wire mesh to obtain the coating.
The invention has the beneficial effects that: the slag recovery circulating water purification adsorbent can effectively adsorb metal or mineral particles remained in slag recovery circulating water; prepared into strips, and can avoid the diffusion of the adsorbent after being wrapped by a wire mesh, thereby being beneficial to the recovery.
Detailed Description
The present invention is described below with reference to examples, which are provided for illustration only and are not intended to limit the scope of the present invention.
Example 1
The slag recovery circulating water purification adsorbent comprises the following components in parts by weight: 45 parts of polyacrylic resin, 60 parts of styrene-acrylate emulsion, 25 parts of nano magnesium oxide, 0.5 part of carbon black, 6 parts of starch and 20 parts of deionized water.
Example 2
The slag recovery circulating water purification adsorbent comprises the following components in parts by weight: 50 parts of polyacrylic resin, 45 parts of acrylic emulsion, 20 parts of nano zinc oxide, 1 part of carbon black, 4 parts of CMC and 30 parts of deionized water.
Example 3
The slag recovery circulating water purification adsorbent comprises the following components in parts by weight: 60 parts of polyacrylic resin, 30 parts of waterborne polyurethane emulsion, 15 parts of nano-alumina, 0.5 part of carbon black, 2 parts of gelatin and 40 parts of deionized water.
The above description is only for the purpose of illustrating the preferred embodiments of the present invention and is not to be construed as limiting the invention, and any modifications, equivalents, improvements and the like that fall within the spirit and principle of the present invention are intended to be included therein.
Claims (5)
1. The slag recovery circulating water purification adsorbent is characterized by comprising the following components in parts by weight: 45-60 parts of polyacrylic resin, 30-60 parts of emulsion, 15-25 parts of nano particles, 0.5-1.5 parts of carbon black, 2-6 parts of thickening agent and 20-40 parts of deionized water.
2. The slag recovery circulating water purification adsorbent of claim 1, wherein the emulsion is a combination of one or more of a styrene-acrylate emulsion, an acrylic acid emulsion, or an aqueous polyurethane emulsion.
3. The slag recovery circulating water purification adsorbent of claim 1, wherein the nanoparticles are selected from one or more of nano magnesium oxide, nano magnesium hydroxide, nano zinc oxide or nano aluminum oxide in combination.
4. The slag recovery circulating water purification adsorbent of claim 1, wherein the thickener is a combination of one or more of starch, gelatin, or CMC.
5. A method for preparing an adsorbent for slag-recycling circulating water purification according to any one of claims 1 to 4, comprising the steps of: weighing the components according to the weight percentage, grinding and filtering the polyacrylic resin, mixing the ground polyacrylic resin with the nano particles, adding the mixture into emulsion, adding deionized water while stirring, adding carbon black and a thickening agent after continuously stirring uniformly, pouring the mixed solution into a strip-shaped mold after uniformly stirring, drying, demolding, and wrapping a blank mold with a metal wire mesh to obtain the coating.