CN112779434A - Method for in-situ self-growing aluminum-based composite material with permanent magnet stirring - Google Patents

Method for in-situ self-growing aluminum-based composite material with permanent magnet stirring Download PDF

Info

Publication number
CN112779434A
CN112779434A CN202011571141.0A CN202011571141A CN112779434A CN 112779434 A CN112779434 A CN 112779434A CN 202011571141 A CN202011571141 A CN 202011571141A CN 112779434 A CN112779434 A CN 112779434A
Authority
CN
China
Prior art keywords
aluminum
pipe
melt
argon
carrier
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202011571141.0A
Other languages
Chinese (zh)
Inventor
王浩伟
王建中
李爱平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Xiangbang Composite Material Co ltd
Anhui Huaibei Ceramic Aluminum New Material Research Institute Shanghai Jiaotong University
Original Assignee
Anhui Xiangbang Composite Material Co ltd
Anhui Huaibei Ceramic Aluminum New Material Research Institute Shanghai Jiaotong University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Xiangbang Composite Material Co ltd, Anhui Huaibei Ceramic Aluminum New Material Research Institute Shanghai Jiaotong University filed Critical Anhui Xiangbang Composite Material Co ltd
Priority to CN202011571141.0A priority Critical patent/CN112779434A/en
Publication of CN112779434A publication Critical patent/CN112779434A/en
Pending legal-status Critical Current

Abstract

The invention discloses a method for preparing an in-situ authigenic aluminum-based composite material with permanent magnetic stirring, which comprises the following steps: providing a vacuum bag comprising a suction port and a dip tube; providing a permanent magnetic stirring device which comprises a track and a carrier, wherein the track and the carrier are arranged below an aluminum smelting furnace, and the carrier can move on the track; the carrier is provided with a permanent magnet device, a motor and a transmission belt; melting pure aluminum or aluminum alloy matrix in an aluminum melting furnace, adding reaction salt and reaction auxiliary agent for reaction, immersing an immersion pipe of a vacuum bag into the aluminum melt, and vacuumizing a vacuum chamber through an extraction opening; lowering the graphite rotor; argon is blown through an argon blowing pipe through the outer pipe; spraying and blowing the powder in the powder conveying bin into the aluminum melt through the inner pipe through the powder conveying pipe; moving the carrier to the position below the aluminum smelting furnace through the track, and starting the permanent magnetic stirring device to stir the aluminum melt.

Description

Method for in-situ self-growing aluminum-based composite material with permanent magnet stirring
Technical Field
The invention relates to an aluminum matrix composite material, in particular to preparation of an in-situ authigenic aluminum matrix composite material.
Background
The in-situ self-generated aluminum-based composite material utilizes chemical reaction among different elements or chemicals under certain conditions to generate one or more ceramic phase particles in an aluminum matrix so as to achieve the purpose of improving the performance of a single metal alloy. The composite material prepared by in-situ self-generation has no pollution on the surface of the reinforcement body and good intermiscibility of the matrix and the reinforcement body. By selecting the reaction type and controlling the reaction parameters, different types and different quantities of in-situ reinforced particles can be obtained.
However, the in-situ autogenous aluminum-based composite material has high requirements on conditions including degassing and impurity removal in the preparation process, otherwise, the prepared composite material is easy to cause uneven particle size and distribution of the reinforcing phase, low mass fraction, or deteriorated structure, poor casting performance and reduced mechanical properties of the material.
In the prior art, the degassing treatment of the aluminum melt is carried out by adopting an inert gas rotary blowing technology. The core part of the technology is a hollow rotating rod with one end provided with a rotating nozzle, namely a rotor, when the technology is used, the rotor is inserted into an aluminum melt, inert gas is blown in through a middle pore passage of the rotating rod and is sprayed out by the rotating nozzle, formed bubbles are scattered into a large number of small bubbles due to high-speed rotation of the nozzle, hydrogen in the aluminum melt is attached to the small bubbles to be separated out into hydrogen, and meanwhile, impurity particles in the aluminum melt are adsorbed to float up to the liquid level, so that the purposes of degassing, removing impurities and purifying are achieved.
At present, most of aluminum melt degassing rotors are made of graphite materials, the graphite materials are excellent in thermal shock resistance and can be machined, aluminum liquid cannot infiltrate graphite, but the graphite materials have the defect that the graphite materials are not resistant to high temperature oxidation, so that the aluminum melt degassing rotors are required to be replaced after the service life is only 14-20 days.
It is therefore a problem addressed by those skilled in the art to effectively try to improve the reaction and preparation conditions to control the size, distribution, and settling segregation of the reinforcing phase and to increase the lifetime of argon-blown graphite rotors.
In addition, how to further improve the uniform distribution degree of the reinforcing phase particles is also a problem that those skilled in the art are aiming to solve.
Meanwhile, how to efficiently and uniformly add alloy powder into the aluminum melt in the treatment process is also a problem to be solved by the technical personnel in the field.
Disclosure of Invention
In order to achieve the above object, the present invention provides in a first aspect an in-situ autogenous aluminum matrix composite system with permanent magnetic stirring, comprising an aluminum melting furnace containing an aluminum melt; the vacuum bag is provided with a dip pipe and an air exhaust port, and the dip pipe is arranged to be immersed into the aluminum melt in the aluminum melting furnace; the graphite rotor is used for argon gas rotary injection, and is provided with a rotating rod and a spray head, wherein the rotating rod is arranged to penetrate through a vacuum chamber of a vacuum bag through a sealing bearing arranged at the top of the vacuum bag, and the spray head is inserted into the bottom of the aluminum melt; the rotating rod comprises an inner pipe and an outer pipe, the outer pipe is connected with the argon injection pipe through a rotary joint, the inner pipe is connected with the powder conveying bin, and the powder conveying bin is connected with the powder conveying air pipe; the permanent magnetic stirring device is arranged below the aluminum smelting furnace.
Further, the permanent magnetic stirring device comprises a rail and a carrier which are arranged at the bottom of the aluminum melting furnace, and the carrier can move on the rail; the carrier is provided with a permanent magnet device, a motor and a transmission belt, the motor can drive the permanent magnet device to rotate through the transmission belt, and the magnetic field of the permanent magnet device and the aluminum melt interact to generate magnetic force to push the aluminum melt to perform stirring motion.
Further, the inner tube is made of a metal material and the outer tube is made of a graphite material.
Furthermore, alloy powder is arranged in the powder conveying bin.
Furthermore, the powder conveying gas pipe and the argon blowing gas pipe share the same argon gas source.
The invention provides a method for preparing an in-situ authigenic aluminum-based composite material with permanent magnetic stirring in a second aspect, which comprises the following steps:
(1) providing a vacuum bag comprising a pumping port and a dip tube, the dip tube being configured to be dipped into an aluminum melt in an aluminum melting furnace; providing a graphite rotor for argon gas rotary injection, wherein the graphite rotor is provided with a rotating rod and a spray head, the rotating rod is arranged to penetrate through a vacuum chamber of a vacuum bag through a sealing bearing arranged at the top of the vacuum bag, and the spray head is inserted into the bottom of an aluminum melt; the rotating rod comprises an inner pipe and an outer pipe, the outer pipe is connected with the argon injection pipe through a rotary joint, the inner pipe is connected with the powder conveying bin, and the powder conveying bin is connected with the powder conveying air pipe; providing a permanent magnetic stirring device, wherein the permanent magnetic stirring device is arranged at the bottom of the aluminum melting furnace and comprises a rail and a carrier, the rail and the carrier are arranged below the aluminum melting furnace, and the carrier can move on the rail; the carrier is provided with a permanent magnet device, a motor and a transmission belt, the motor can drive the permanent magnet device to rotate through the transmission belt, and the magnetic field of the permanent magnet device and the aluminum melt interact to generate magnetic force to push the aluminum melt to stir;
(2) after melting the pure aluminum or aluminum alloy matrix in the aluminum melting furnace, adding reaction salt and reaction auxiliary agent for reaction,
(3) immersing an immersion pipe of a vacuum bag into the aluminum melt, and vacuumizing the vacuum chamber through an air exhaust port;
(4) lowering the graphite rotor to enable the rotating rod to penetrate through a vacuum chamber of the vacuum bag through a sealing bearing arranged at the top of the vacuum bag, and inserting the spray head into the bottom of the aluminum melt;
(5) argon is blown through an argon blowing pipe through the outer pipe; spraying and blowing the powder in the powder conveying bin into the aluminum melt through the inner pipe through the powder conveying pipe;
(6) moving the carrier to the position below the aluminum smelting furnace through the track, and starting the permanent magnetic stirring device to stir the aluminum melt.
Further, the inner tube is made of a metal material and the outer tube is made of a graphite material.
Furthermore, alloy powder is arranged in the powder conveying bin.
Furthermore, the powder conveying gas pipe and the argon blowing gas pipe share the same argon gas source.
Furthermore, the powder conveying and feeding pipe is connected with a nitrogen gas source, and the argon gas blowing gas pipe is connected with an argon gas source.
According to the invention, the vacuum bag and the immersion pipe are used, the aluminum melt is sealed, a vacuum environment is generated by pumping, the oxygen and hydrogen partial pressure is reduced in the vacuum environment, and the degassing condition is enhanced. Meanwhile, the graphite rotating rod enters the aluminum melting furnace through the vacuum chamber, and is not in contact with oxygen in the whole process, so that the oxidation of the graphite rotor is prevented, and the service life of the graphite rotor is greatly prolonged.
According to the invention, a traditional graphite rotor is divided into an inner pipe and an outer pipe which are sleeved, argon is introduced into the outer pipe for rotary blowing, the argon and the nitrogen are used for conveying alloy powder or other raw materials, the alloy powder is sprayed into the bottom of an aluminum melt by high-pressure gas during rotary blowing, and simultaneously the alloy powder is rapidly mixed and reacted with the aluminum melt under the action of argon blowing bubbles, so that the reaction conditions and the distribution uniformity of the alloy powder in the aluminum melt are greatly improved. In addition, the inner pipe and the outer pipe can be made of different materials, the outer pipe is made of graphite materials resistant to high temperature and aluminum melt corrosion, and the inner pipe is made of wear-resistant metal materials such as copper pipes or steel pipes.
According to the invention, through permanent magnetic stirring, the autogenous stirring motion of the aluminum melt is enhanced while argon is injected, so that the distribution of enhanced phase particles is more uniform, and the reaction conditions of degassing and impurity removal are further improved.
According to the invention, a proper amount of metal magnesium is added into the composite material, so that the surface energy is reduced by adsorbing magnesium in aluminum liquid after particles are generated, and then the particles and aluminum form better combination, thus the magnesium is used as a means for reducing the surface energy of the particles and preventing agglomeration, and the phenomenon of particle sedimentation is effectively slowed down. Meanwhile, the viscosity of the aluminum liquid is increased due to the addition of magnesium, and according to a Stocks formula, the viscosity of the composite material is increased, the moving speed of particles is reduced, the particles cannot agglomerate due to mutual contact within a long time, and the particles are easily captured by alpha-Al crystal grains in the solidification process to form a uniform and stable reinforcement.
The TiB2 particles generated in situ are particles with the diameter of about 1 micron, and the particles with the size can not be settled in the aluminum liquid. However, particles are often generated in a local region (at the interface between molten salt and molten aluminum), and are likely to agglomerate due to a high local concentration. And once the agglomeration is generated, the agglomeration is difficult to separate and refine, so that the segregation in the sedimentation and solidification processes occurs. The method is characterized in that a pulse magnetic field and a high-energy ultrasonic field are applied, the protection effect of the reaction molten salt is utilized, the pulse magnetic field strength is controlled to be 2-4T, and the high-energy ultrasonic field strength is controlled to be 200-1800W/m 2. On one hand, the contact chance of molten salt and aluminum liquid can be increased, the reaction is accelerated, and TiB2 particles generated in situ are uniform and fine; on the other hand, the diffusion of the particles from the high concentration region to the low concentration region of the reaction is promoted, so that the TiB2 particles are uniform and dispersed, and the sedimentation phenomenon of the composite material is further relieved to a certain extent.
The conception, the specific structure and the technical effects of the present invention will be further described with reference to the accompanying drawings to fully understand the objects, the features and the effects of the present invention.
Drawings
FIG. 1 is a schematic illustration of a system for melt-controlled in-situ autogenous aluminum matrix composites with a vacuum bag in a preferred embodiment of the invention;
FIG. 2 is a schematic illustration of a system for melt-controlled in-situ autogenous aluminum matrix composites with electromagnetic stirring in a preferred embodiment of the invention;
FIG. 3 is a schematic illustration of a system for melt-controlled in-situ autogenous aluminum matrix composites with continuous processing in a preferred embodiment of the invention;
FIG. 4 is a schematic illustration of a system with powder injection of in situ autogenous aluminum matrix composites in a preferred embodiment of the invention;
FIG. 5 is a schematic view of the graphite rotor of FIG. 4;
FIG. 6 is a schematic illustration of a system for in situ autogenous aluminum matrix composites with permanent magnetic stirring in a preferred embodiment of the invention;
fig. 7 is a schematic view of the graphite rotor of fig. 6.
Detailed Description
The technical contents of the preferred embodiments of the present invention will be more clearly and easily understood by referring to the drawings attached to the specification. The present invention may be embodied in many different forms of embodiments and the scope of the invention is not limited to the embodiments set forth herein.
Example one
As shown in figure 1, melting pure aluminum or aluminum alloy matrix at 700-760 ℃, placing an aluminum melting furnace 1 containing aluminum melt 2 on a hydraulic lifting table 10, and adding reaction salt and reaction auxiliary agent for reaction. The hydraulic lift 10 is raised so that the immersion tube 5 of the vacuum bag 3 disposed above the aluminum melting furnace 1 is immersed into the aluminum melt 2. The vacuum chamber 8 of the vacuum bag 3 is vacuumized through the pumping hole 4, so that the aluminum melt 2 enters the vacuum bag 3 under the action of atmospheric pressure.
And simultaneously carrying out argon rotary blowing on the aluminum melt: graphite rotor falls, graphite rotor's bull stick 6 is through setting up at the sealed bearing 7 at 3 tops of vacuum package, pass real empty room 8, insert shower nozzle 9 to the bottom of aluminium melt 2, the middle pore of argon gas through bull stick 6 blows in, spout by rotatory shower nozzle 9, the bubble of formation is broken up into a large amount of small bubbles because the high-speed rotation of shower nozzle 9, hydrogen in the aluminium melt 2 will depend on and separate out into hydrogen on these small bubbles, adsorb the impurity granule in the aluminium melt simultaneously and come up to the liquid level together, most bubbles get into in real empty room 8, then discharge through extraction opening 4. Through vacuum package 3 and dip tube 5, form sealedly with aluminium melt 2 self, the vacuum environment is produced in the air exhaust, and the vacuum environment reduces oxygen, hydrogen partial pressure, strengthens the degasification condition. Meanwhile, the graphite rotating rod 6 enters the aluminum melting furnace 1 through the vacuum chamber 8, and the whole process is free from oxygen, so that the oxidation of the graphite rotor is prevented, and the service life of the graphite rotor is greatly prolonged.
In a preferred embodiment of the present invention, the argon flow rate of the argon gas injection is set to 7 to 12L/min, and the stirring rotation speed is 270 to 320 r/min.
In a preferred embodiment of the present invention, the reaction salt comprises NaBF in a mass ratio of 1.2:1 to 1.8:14And Na2TiF6
In a preferred embodiment according to the invention, the above reactionThe auxiliary agent comprises Na with the mass ratio of 2.2:1: 1-3.8: 1:13AlF6、LiF3、LiCl3
In a preferred embodiment according to the invention, the above-mentioned reaction auxiliary is added in an amount of 8 to 12 wt% of the reaction salt.
In a preferred embodiment according to the invention, a pulsed magnetic field strength of 2-4T is applied during the reaction.
In a preferred embodiment according to the present invention, 200-1800W/m is applied during the reaction2High-energy ultrasound field strength.
In a preferred embodiment according to the invention, the reaction time is from 10min to 30 min.
Example two
As shown in fig. 2, melting a pure aluminum or aluminum alloy matrix at 700-760 ℃, placing an aluminum melt 2 in an aluminum melting furnace 1, and adding a reaction salt and a reaction auxiliary agent for reaction. The immersion pipe 5 of the vacuum bag 3 disposed above the aluminum melting furnace 1 is immersed into the aluminum melt 2. The vacuum chamber 8 of the vacuum bag 3 is vacuumized through the pumping hole 4, so that the aluminum melt 2 enters the vacuum bag 3 under the action of atmospheric pressure.
And simultaneously carrying out argon rotary blowing on the aluminum melt: graphite rotor falls, graphite rotor's bull stick 6 is through setting up at the sealed bearing 7 at 3 tops of vacuum package, pass real empty room 8, insert shower nozzle 9 to the bottom of aluminium melt 2, the middle pore of argon gas through bull stick 6 blows in, spout by rotatory shower nozzle 9, the bubble of formation is broken up into a large amount of small bubbles because the high-speed rotation of shower nozzle 9, hydrogen in the aluminium melt 2 will depend on and separate out into hydrogen on these small bubbles, adsorb the impurity granule in the aluminium melt simultaneously and come up to the liquid level together, most bubbles get into in real empty room 8, then discharge through extraction opening 4. Through vacuum package 3 and dip tube 5, form sealedly with aluminium melt 2 self, the vacuum environment is produced in the air exhaust, and the vacuum environment reduces oxygen, hydrogen partial pressure, strengthens the degasification condition. Meanwhile, the graphite rotating rod 6 enters the aluminum melting furnace 1 through the vacuum chamber 8, and the whole process is free from oxygen, so that the oxidation of the graphite rotor is prevented, and the service life of the graphite rotor is greatly prolonged.
An electromagnetic stirring device is arranged below the aluminum melting furnace and comprises an inductor 12 and a frequency converter 11, and the electromagnetic stirring device is used for enabling the aluminum melt to generate stirring motion under the action of electromagnetic force.
In a preferred embodiment of the present invention, the argon flow rate of the argon gas injection is set to 7 to 12L/min, and the stirring rotation speed is 270 to 320 r/min.
In a preferred embodiment of the present invention, the reaction salt comprises NaBF in a mass ratio of 1.2:1 to 1.8:14And Na2TiF6
In a preferred embodiment of the present invention, the reaction promoter comprises Na in a mass ratio of 2.2:1:1 to 3.8:1:13AlF6、LiF3、LiCl3
In a preferred embodiment according to the invention, the above-mentioned reaction auxiliary is added in an amount of 8 to 12 wt% of the reaction salt.
In a preferred embodiment according to the invention, a pulsed magnetic field strength of 2-4T is applied during the reaction.
In a preferred embodiment according to the present invention, 200-1800W/m is applied during the reaction2High-energy ultrasound field strength.
In a preferred embodiment according to the invention, the reaction time is from 10min to 30 min.
EXAMPLE III
As shown in fig. 3, melting a pure aluminum or aluminum alloy matrix at 700-760 ℃, placing an aluminum melt 2 in an aluminum melting furnace 1, and adding a reaction salt and a reaction auxiliary agent for reaction. The immersion pipe 5 of the vacuum bag 3 disposed above the aluminum melting furnace 1 is immersed into the aluminum melt 2. The vacuum chamber 8 of the vacuum bag 3 is vacuumized through the pumping hole 4, so that the aluminum melt 2 enters the vacuum bag 3 under the action of atmospheric pressure.
And simultaneously carrying out argon rotary blowing on the aluminum melt: graphite rotor falls, graphite rotor's bull stick 6 is through setting up at the sealed bearing 7 at 3 tops of vacuum package, pass real empty room 8, insert shower nozzle 9 to the bottom of aluminium melt 2, the middle pore of argon gas through bull stick 6 blows in, spout by rotatory shower nozzle 9, the bubble of formation is broken up into a large amount of small bubbles because the high-speed rotation of shower nozzle 9, hydrogen in the aluminium melt 2 will depend on and separate out into hydrogen on these small bubbles, adsorb the impurity granule in the aluminium melt simultaneously and come up to the liquid level together, most bubbles get into in real empty room 8, then discharge through extraction opening 4. Through vacuum package 3 and dip tube 5, form sealedly with aluminium melt 2 self, the vacuum environment is produced in the air exhaust, and the vacuum environment reduces oxygen, hydrogen partial pressure, strengthens the degasification condition. Meanwhile, the graphite rotating rod 6 enters the aluminum melting furnace 1 through the vacuum chamber 8, and the whole process is free from oxygen, so that the oxidation of the graphite rotor is prevented, and the service life of the graphite rotor is greatly prolonged.
An electromagnetic stirring device is arranged below the aluminum melting furnace and comprises an inductor 12 and a frequency converter 11, and the electromagnetic stirring device is used for enabling the aluminum melt to generate stirring motion under the action of electromagnetic force.
An outlet flow passage 13 is arranged on the side wall of the upper part of the aluminum smelting furnace 1, and a flow stopping sliding plate 131 is arranged on the outlet flow passage 13; an inlet flow passage 14 is provided in a bottom side plate of the aluminum melting furnace 1, and a flow stop slide plate 141 is provided in the inlet flow passage 14. After a furnace of aluminum melt is processed, the flow stopping sliding plates 131 and 141 on the aluminum melt outlet runner 13 and the aluminum melt inlet runner 14 are opened, new aluminum melt to be processed is introduced from the aluminum melt inlet runner 14 at the bottom of the melting furnace, the processed aluminum melt in the aluminum melting furnace flows out from the outlet runner 13, after the aluminum melt with set flow rate flows into the aluminum melting furnace 1, the flow stopping sliding plates 131 and 141 are closed, and the operation is carried out again, so that the continuous processing of the aluminum melt under the vacuum condition can be realized, one furnace is not required to be vacuumized once, and the process preparation time and the energy consumption are greatly saved.
In a preferred embodiment of the present invention, the argon flow rate of the argon gas injection is set to 7 to 12L/min, and the stirring rotation speed is 270 to 320 r/min.
In a preferred embodiment of the present invention, the reaction salt comprises NaBF in a mass ratio of 1.2:1 to 1.8:14And Na2TiF6
In a preferred embodiment of the present invention, the reaction promoter comprises Na in a mass ratio of 2.2:1:1 to 3.8:1:13AlF6、LiF3、LiCl3
In a preferred embodiment according to the invention, the above-mentioned reaction auxiliary is added in an amount of 8 to 12 wt% of the reaction salt.
In a preferred embodiment according to the invention, a pulsed magnetic field strength of 2-4T is applied during the reaction.
In a preferred embodiment according to the present invention, 200-1800W/m is applied during the reaction2High-energy ultrasound field strength.
In a preferred embodiment according to the invention, the reaction time is from 10min to 30 min.
Example four
As shown in FIG. 4, a pure aluminum or aluminum alloy substrate is melted at 700-760 ℃, an aluminum melting furnace 1 containing an aluminum melt 2 is placed on a hydraulic lifting table 10, and a reaction salt and a reaction auxiliary agent are added for reaction. The hydraulic lift 10 is raised so that the immersion tube 5 of the vacuum bag 3 disposed above the aluminum melting furnace 1 is immersed into the aluminum melt 2. The vacuum chamber 8 of the vacuum bag 3 is vacuumized through the pumping hole 4, so that the aluminum melt 2 enters the vacuum bag 3 under the action of atmospheric pressure.
And simultaneously carrying out argon rotary blowing on the aluminum melt: graphite rotor falls, graphite rotor's bull stick 6 is through setting up at the sealed bearing 7 at 3 tops of vacuum package, pass real empty room 8, insert shower nozzle 9 to the bottom of aluminium melt 2, the middle pore of argon gas through bull stick 6 blows in, spout by rotatory shower nozzle 9, the bubble of formation is broken up into a large amount of small bubbles because the high-speed rotation of shower nozzle 9, hydrogen in the aluminium melt 2 will depend on and separate out into hydrogen on these small bubbles, adsorb the impurity granule in the aluminium melt simultaneously and come up to the liquid level together, most bubbles get into in real empty room 8, then discharge through extraction opening 4. Through vacuum package 3 and dip tube 5, form sealedly with aluminium melt 2 self, the vacuum environment is produced in the air exhaust, and the vacuum environment reduces oxygen, hydrogen partial pressure, strengthens the degasification condition. Meanwhile, the graphite rotating rod 6 enters the aluminum melting furnace 1 through the vacuum chamber 8, and the whole process is free from oxygen, so that the oxidation of the graphite rotor is prevented, and the service life of the graphite rotor is greatly prolonged.
As shown in fig. 5, the graphite rotating rod 6 includes an inner tube 65 and an outer tube 63, and an argon blowing pipe 64 is provided in the inner tube 65 and the outer tube 63. The outer pipe 63 is connected with an argon gas injection pipe 631 through a rotary joint 62, the inner pipe 65 is connected with a powder conveying bin 61, the powder conveying bin 61 is connected with a powder conveying pipe 611, and a powder conveying pipeline 66 is arranged in the inner pipe 65.
Argon gas is blown through the outer tube 63 by an argon gas blowing tube 631; the alloy powder 9 in the powder conveying bin 61 is blown into the aluminum melt 2 through the inner pipe 65 by the powder conveying pipe 611.
Preferably, the inner tube 63 is made of a metal material such as copper or steel, and the outer tube 63 is made of a graphite material. This is to improve the wear resistance of the inner tube 63 against the erosion of the high-pressure gas and the powder.
Preferably, powder delivery tube 611 and argon purge gas tube 631 share the same argon gas source.
In a preferred embodiment of the present invention, the argon flow rate of the argon gas injection is set to 7 to 12L/min, and the stirring rotation speed is 270 to 320 r/min.
In a preferred embodiment of the present invention, the reaction salt comprises NaBF in a mass ratio of 1.2:1 to 1.8:14And Na2TiF6
In a preferred embodiment of the present invention, the reaction promoter comprises Na in a mass ratio of 2.2:1:1 to 3.8:1:13AlF6、LiF3、LiCl3
In a preferred embodiment according to the invention, the above-mentioned reaction auxiliary is added in an amount of 8 to 12 wt% of the reaction salt.
In a preferred embodiment according to the invention, a pulsed magnetic field strength of 2-4T is applied during the reaction.
In a preferred embodiment according to the present invention, 200-1800W/m is applied during the reaction2High-energy ultrasound field strength.
In a preferred embodiment according to the invention, the reaction time is from 10min to 30 min.
EXAMPLE five
As shown in fig. 6, melting a pure aluminum or aluminum alloy matrix at 700-760 ℃, placing an aluminum melt 2 in an aluminum melting furnace 1, and adding a reaction salt and a reaction auxiliary agent for reaction. The immersion pipe 5 of the vacuum bag 3 disposed above the aluminum melting furnace 1 is immersed into the aluminum melt 2. The vacuum chamber 8 of the vacuum bag 3 is vacuumized through the pumping hole 4, so that the aluminum melt 2 enters the vacuum bag 3 under the action of atmospheric pressure.
And simultaneously carrying out argon rotary blowing on the aluminum melt: graphite rotor falls, graphite rotor's bull stick 6 is through setting up at the sealed bearing 7 at 3 tops of vacuum package, pass real empty room 8, insert shower nozzle 9 to the bottom of aluminium melt 2, the middle pore of argon gas through bull stick 6 blows in, spout by rotatory shower nozzle 9, the bubble of formation is broken up into a large amount of small bubbles because the high-speed rotation of shower nozzle 9, hydrogen in the aluminium melt 2 will depend on and separate out into hydrogen on these small bubbles, adsorb the impurity granule in the aluminium melt simultaneously and come up to the liquid level together, most bubbles get into in real empty room 8, then discharge through extraction opening 4. Through vacuum package 3 and dip tube 5, form sealedly with aluminium melt 2 self, the vacuum environment is produced in the air exhaust, and the vacuum environment reduces oxygen, hydrogen partial pressure, strengthens the degasification condition. Meanwhile, the graphite rotating rod 6 enters the aluminum melting furnace 1 through the vacuum chamber 8, and the whole process is free from oxygen, so that the oxidation of the graphite rotor is prevented, and the service life of the graphite rotor is greatly prolonged.
As shown in fig. 7, the graphite rotating rod 6 includes an inner tube 65 and an outer tube 63, and an argon blowing pipe 64 is provided in the inner tube 65 and the outer tube 63. The outer pipe 63 is connected with an argon gas injection pipe 631 through a rotary joint 62, the inner pipe 65 is connected with a powder conveying bin 61, the powder conveying bin 61 is connected with a powder conveying pipe 611, and a powder conveying pipeline 66 is arranged in the inner pipe 65.
Argon gas is blown through the outer tube 63 by an argon gas blowing tube 631; the alloy powder 9 in the powder conveying bin 61 is blown into the aluminum melt 2 through the inner pipe 65 by the powder conveying pipe 611.
Preferably, the inner tube 63 is made of a metal material such as copper or steel, and the outer tube 63 is made of a graphite material. This is to improve the wear resistance of the inner tube 63 against the erosion of the high-pressure gas and the powder.
Preferably, powder delivery tube 611 and argon purge gas tube 631 share the same argon gas source.
As shown in fig. 6, a track 17 of the permanent magnetic stirring device is disposed below the aluminum melting furnace 1, a carrier 16 capable of moving on the track 17 is disposed on the track 17, and a motor 18, a transmission belt 19 and a permanent magnet device 15 are disposed on the track 17, when the permanent magnetic stirring device operates, the carrier 16 moves below the aluminum melting furnace 1, the motor 18 drives the permanent magnet device 15 to rotate through the transmission belt, and a magnetic force is generated by interaction between a magnetic field of the permanent magnet device 15 and the aluminum melt 2 to push the aluminum melt 2 to perform stirring movement.
In a preferred embodiment of the present invention, the argon flow rate of the argon gas injection is set to 7 to 12L/min, and the stirring rotation speed is 270 to 320 r/min.
In a preferred embodiment of the present invention, the reaction salt comprises NaBF in a mass ratio of 1.2:1 to 1.8:14And Na2TiF6
In a preferred embodiment of the present invention, the reaction promoter comprises Na in a mass ratio of 2.2:1:1 to 3.8:1:13AlF6、LiF3、LiCl3
In a preferred embodiment according to the invention, the above-mentioned reaction auxiliary is added in an amount of 8 to 12 wt% of the reaction salt.
In a preferred embodiment according to the invention, a pulsed magnetic field strength of 2-4T is applied during the reaction.
In a preferred embodiment according to the present invention, 200-1800W/m is applied during the reaction2High-energy ultrasound field strength.
In a preferred embodiment according to the invention, the reaction time is from 10min to 30 min.
In other embodiments, the aluminum melting furnace can be arranged on the lifting platform, a rotating platform is rotatably arranged on the lifting platform, the rotating platform can rotate relative to the lifting platform under the driving of a motor, the aluminum melting furnace is fixedly arranged on the rotating platform, and when argon gas injection is carried out on aluminum liquid in the aluminum melting furnace, the aluminum melting furnace rotates along with the rotating platform and simultaneously drives the aluminum liquid therein, particularly the aluminum liquid on the furnace wall side of the aluminum melting furnace to move, so that the defect that the part of the aluminum liquid is weaker in argon gas rotary injection action is overcome
The foregoing detailed description of the preferred embodiments of the invention has been presented. It should be understood that numerous modifications and variations could be devised by those skilled in the art in light of the present teachings without departing from the inventive concepts. Therefore, the technical solutions available to those skilled in the art through logic analysis, reasoning and limited experiments based on the prior art according to the concept of the present invention should be within the scope of protection defined by the claims.

Claims (5)

1. The method for preparing the in-situ authigenic aluminum-based composite material with the permanent magnet stirring function is characterized by comprising the following steps of:
(1) providing a vacuum bag comprising a pumping port and a dip tube, the dip tube being configured to be immersible into an aluminum melt in an aluminum melting furnace; providing a graphite rotor for argon gas rotary blowing, wherein the graphite rotor is provided with a rotating rod and a nozzle, the rotating rod is arranged to penetrate through a vacuum chamber of the vacuum bag through a sealing bearing arranged at the top of the vacuum bag, and the nozzle is inserted into the bottom of the aluminum melt; the rotating rod comprises an inner pipe and an outer pipe, the outer pipe is connected with an argon injection pipe through a rotary joint, the inner pipe is connected with a powder conveying bin, and the powder conveying bin is connected with a powder conveying air pipe; providing a permanent magnetic stirring device, wherein the permanent magnetic stirring device is arranged at the bottom of the aluminum melting furnace and comprises a track and a carrier, the track and the carrier are arranged below the aluminum melting furnace, and the carrier can move on the track; the carrier is provided with a permanent magnet device, a motor and a transmission belt, the motor can drive the permanent magnet device to rotate through the transmission belt, and the magnetic field of the permanent magnet device interacts with the aluminum melt to generate magnetic force to push the aluminum melt to stir;
(2) after melting the pure aluminum or aluminum alloy matrix in the aluminum melting furnace, adding reaction salt and reaction auxiliary agent for reaction,
(3) immersing a dip pipe of the vacuum bag into the aluminum melt, and vacuumizing the vacuum chamber through the air exhaust port;
(4) lowering the graphite rotor so that the rotating rod passes through a vacuum chamber of the vacuum bag through a sealing bearing arranged at the top of the vacuum bag, and inserting the spray head into the bottom of the aluminum melt;
(5) argon is blown through the outer pipe through the argon blowing pipe; the powder in the powder conveying bin is blown into the aluminum melt by the powder conveying pipe through the inner pipe;
(6) and moving the carrier to the position below the aluminum melting furnace through the rail, and starting the permanent magnetic stirring device to stir the aluminum melt.
2. The method for in situ autogenous aluminum matrix composite with permanent magnet agitation of claim 1, wherein the inner tube is made of a metallic material and the outer tube is made of a graphite material.
3. The method for permanent magnetic stirring of in situ autogenous aluminum matrix composites as claimed in claim 2, wherein the powder delivery silo contains alloy powder.
4. The method for in situ autogenous aluminum matrix composites with permanent magnet agitation of claim 3, wherein the powder feed gas line and the argon blowing gas line share the same argon source.
5. The method for in situ autogenous aluminum matrix composites with permanent magnet agitation of claim 4, wherein the powder feed line is connected to a source of nitrogen gas and the argon gas injection line is connected to a source of argon gas.
CN202011571141.0A 2020-12-27 2020-12-27 Method for in-situ self-growing aluminum-based composite material with permanent magnet stirring Pending CN112779434A (en)