CN112522011A - 一种环保型空气压缩机油及其制备方法 - Google Patents
一种环保型空气压缩机油及其制备方法 Download PDFInfo
- Publication number
- CN112522011A CN112522011A CN202011223816.2A CN202011223816A CN112522011A CN 112522011 A CN112522011 A CN 112522011A CN 202011223816 A CN202011223816 A CN 202011223816A CN 112522011 A CN112522011 A CN 112522011A
- Authority
- CN
- China
- Prior art keywords
- parts
- air compressor
- oil
- compressor oil
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种环保型空气压缩机油及其制备方法,所述的环保型空气压缩机油包括以下重量份组分:季戊四醇油酸酯和三羟甲基丙烷油酸酯复合而成的合成酯类油46~66份,烷基磷酸酯6~10份,硫化油脂8~13.5份,硼酸盐5~10份,烷基硫代磷酸盐7.95~10份,磷酸三甲酚酯7~10份,消泡剂0.05~0.5份。与现有技术相比,本发明具有易生物降解、保护环境、长寿命、节能、抗高温、抗高压等优点。
Description
技术领域
本发明涉及空气压缩机油领域,具体涉及一种环保型空气压缩机油及其制备方法。
背景技术
空气压缩机是一种应用广泛的通用机械,几乎涉及国民经济工业各个领域,其用量和生产量相当大,要保证空气压缩机安全可靠的工作,润滑是重要环节之一。空气压缩机油,是指用于空气压缩机在运转中汽缸运动部件及排气阀的润滑,以有效保护螺杆、轴承、齿轮等部件,并通过油循环起到对零部件冷却、防锈和清净作用,同时用于对螺杆和壳体的起密封作用的一类油品。由于空气压缩机一直处于高压、高温及有冷凝水存在的环境中,因此空气压缩机油应具有优良的抗高温氧化性能、低积炭倾向性、优异的粘温性能、良好的油水分离性和防锈性能。目前空气压缩机油主要分为矿物型和合成型两大类,前者作为传统空气压缩机油,存在着高温氧化安定性能不佳,产品使用寿命不长(一般2000h左右)、具有高的积炭倾向性,这样导致使用时换油频繁,能耗大,不利于节能、环保、可持续发展的新型经济发展观念。后者可以有效提高油品使用寿命问题(一般6000h左右),也可以解决压缩机在运行中的积炭问题,但是,由于采用合成酯和聚α烯烃作为原料导致产品在使用中的成本过高,大大增加了使用空气压缩机油的成本,使得产品在使用中的性价比不高,市场采用的比率始终不高。
发明专利CN1088977263A公开了一种环保型合成酯空气压缩机油,包括改性植物油、合成酯、高温抗氧化剂、防锈剂、抗磨剂、降凝剂和抗泡剂,改性植物油在空气压缩机油中的质量百分比为45%~50%,合成酯在空气压缩机油中的质量百分比为45%~50%,高温抗氧剂在空气压缩机油中的质量百分比为1%~2%,防锈剂在空气压缩机油中的质量百分比为1%~2%,抗磨剂在空气压缩机油中的质量百分比为1%~2%,降凝剂在空气压缩机油中的质量百分比为1~2%,抗泡剂在空气压缩机油中的质量百分比为50~100ppm。该环保型合成酯空气压缩机油开口闪点可到300~350℃,倾点-45℃以下,在85~95℃的使用时间可达10000h以上,旋转氧弹法测得的氧化安定性可达3000h以上。但是该空气压缩机油价格昂贵,原料不易得到。
发明专利公开了一种无灰螺杆式空气压缩机油,按质量份计算,包括原料:聚α烯烃20~30份,己二酸二异辛酯10~15份,季戊四醇油酸酯3~5份,三羟甲基丙烷油酸酯2~3份,烷基化二苯胺0.1~1.4份,2,6-二叔丁基混合酚0.8~1份,甲基苯三唑衍生物0.05~0.3份,苯三唑脂肪酸胺盐0.05~0.3份,磷酸三丁酯10~12份,烷基硫代磷酸酯1.2~1.2份,甲基硅氧烷混合物或液态酯共聚物0.005~0.05份,二烷基萘磺酸金属盐3~7份,脂肪硫化异丁烯17~19份。该无灰螺杆式空气压缩机油具有优良的抗氧化安定性、抗乳化性、抗腐防锈性、极好的消泡性和优异的粘温性能等优点,使其性能指标达到46号压缩机油标准,用于空气压缩系统机械设备等。但是,该空气压缩机油含硫量过高,易降解成分减少,造成其生物降解性低。
发明内容
本发明的目的就是为了克服上述现有技术存在的缺陷而提供一种环保型空气压缩机油及其制备方法,具有绿色环保、易生物降解、长寿命、节能、抗高温高压等优点。
本发明的目的可以通过以下技术方案来实现:一种环保型空气压缩机油,包括以下重量份组分:季戊四醇油酸酯和三羟甲基丙烷油酸酯复合而成的合成酯类油46~66份,烷基磷酸酯6~10份,硫化油脂8~13.5份,硼酸盐5~10份,烷基硫代磷酸盐7.95~10份,磷酸三甲酚酯7~10份,消泡剂0.05~0.5份。
进一步地,所述的合成酯类油中,季戊四醇油酸酯和三羟甲基丙烷油酸酯的重量比为1:1~1.3。
所述的季戊四醇油酸酯包括PETO-A、PETO-B或PETO-C,作为环保型合成基础油。季戊四醇油酸酯PETO具有优异的润滑性能,粘度指数高、抗燃性好,生物降解率达90%以上。
所述的三羟甲基丙烷油酸酯包括TMPTO-A、TMPTO-B或TMPTO-C,作为环保型合成基础油。三羟甲基丙烷油酸酯TMPTO具有优异的润滑性能,粘度指数高、抗燃性好,生物降解率达90%以上。
所述的烷基磷酸酯包括二甲基磷酸酯等二烷基磷酸酯类化合物。烷基磷酸酯包括T308,是一种极压抗磨剂,为磷氮型多效添加剂,具有抗摩擦、抑制腐蚀及防锈等多种功能,油溶性、配伍性好,可减少腐蚀抑制剂及其它添加剂的用量,是一种绿色环保型添加剂。
所述的硫化油脂包括硫化猪油、硫化烯烃棉籽油或硫化脂肪油。所述的硫化烯烃棉籽油包括T405,具有良好的油溶性、极压抗磨和降低摩擦等性能,是一种绿色环保型油性减摩剂。
所述的硼酸盐包括三硼酸钾或偏硼酸钠。硼酸盐或偏硼酸钠为T361,是一类绿色环保的极压抗磨剂。
所述的烷基硫代磷酸盐包括T203,作为抗氧抗腐剂以及极压添加剂使用;同时兼具抗氧剂功能,所述的磷酸三甲酚酯包括T306,为透明油状液体,具有良好的极压抗磨性能、阻燃性能、耐霉菌性能,挥发性低,抗磨性能好可作为极压抗磨剂,是一种绿色环保型添加剂。
所述的消泡剂包括T911,为一种丙烯酸酯与醚共聚的非硅消泡剂,适用于高黏度润滑油。
本发明硼酸盐中的硼酸基团在使用摩擦过程中生成硼无机反应膜,硫和磷酸酯都是在高速高温摩擦过程中生成耐极压的反应膜S和P,B、S、P反应膜共同作用使该油品有优异的抗磨减摩性能,具有长寿命。
一种上述环保型空气压缩机油的制备方法,包括以下步骤:
(1)按重量份称取各组分;
(2)在常温下将季戊四醇油酸酯和三羟甲基丙烷油酸酯复合而成的合成酯类油加入到调合釜中;
(3)加热至50~70℃,在300~380r/min搅拌条件下,投入烷基磷酸酯、硫化油脂、硼酸盐、烷基硫代磷酸盐、磷酸三甲酚酯和消泡剂;
(4)保持55~65℃继续搅拌1~2h;
(5)静置沉降0.8~1.2h,即得环保型空气压缩机油。
与现有技术相比,本发明具有以下优点:
1.绿色环保,易生物降解:本发明采用环保型易生物降解的季戊四醇油酸酯和三羟甲基丙烷油酸酯复合而成的合成酯基础油,同时添加绿色润滑添加剂如烷基磷酸酯、硫化油脂、硼酸盐、磷酸三甲酚酯等,VOC含量低,产品生物降解性达95%以上,绿色环保;
2.抗高温高压,寿命长,节能:本发明产品的氧化安定性可达5000h以上,比46号标准压缩机油高2/3,最大无卡咬负荷达1000N以上,延长了空气压缩机油的更换周期,且降低了设备摩擦,更加节能,与不添加空气压缩机油时相比,节能3%以上;
3.本发明所使用的原料易得,制备方法简单,成本较低。
具体实施方式
下面对本发明的实施例作详细说明,以下实施例在以本发明技术方案为前提下进行实施,给出了详细的实施方式和具体的操作过程,但本发明的保护范围不限于下述的实施例。
以下实施例所用的各种原料的规格及生产厂家信息如下表所示:
实施例1
一种环保型空气压缩机油,包括如下质量份数的原料:二甲基磷酸酯6份,硫化猪油8份,三硼酸钾5份,烷基硫代磷酸盐7.95份,磷酸三甲酚酯7份,季戊四醇油酸酯32份和三羟甲基丙烷油酸酯34份,消泡剂0.05份。
其制备方法为:按质量份数计算,在常温下将季戊四醇油酸酯32份和三羟甲基丙烷油酸酯34份加入到调合釜中,加热至62℃,在300转/分搅拌条件下,依次投入二甲基磷酸酯6份,硫化猪油8份,三硼酸钾5份,烷基硫代磷酸盐7.95份,磷酸三甲酚酯7份,然后加入0.05份消泡剂,搅拌均匀,保持60℃继续搅拌1.5h,静置沉降1h,即得环保型空气压缩机油。
实施例2
一种环保型空气压缩机油,包括如下质量份数的原料:二烷基磷酸酯10份,硫化脂肪油13.5份,偏硼酸钠10份,烷基硫代磷酸盐10份,磷酸三甲酚酯10份,季戊四醇油酸酯20份和三羟甲基丙烷油酸酯26份,消泡剂0.5份。
其制备方法为:按质量份数计算,在常温下将季戊四醇油酸酯20份和三羟甲基丙烷油酸酯26份到调合釜中,加热至62℃,在380转/分搅拌条件下,依次投入二烷基磷酸酯10份,硫化脂肪油13.5份,烷基硫代磷酸盐10份,磷酸三甲酚酯10份,搅拌均匀后,再投入偏硼酸钠10份,然后加入0.5份消泡剂,搅拌均匀,保持60℃继续搅拌1.5h,静置沉降1h,即得环保型空气压缩机油
实施例3
一种环保型空气压缩机油,包括如下质量份数的原料:二烷基磷酸酯8份,硫化脂肪油11份,硼酸钾8份,烷基硫代磷酸盐9份,磷酸三甲酚酯8份,季戊四醇油酸酯28份和三羟甲基丙烷油酸酯28份,消泡剂0.1份。
其制备方法为:按质量份数计算,在常温下将季戊四醇油酸酯28份和三羟甲基丙烷油酸酯28份到调合釜中,加热至62℃,在350转/分搅拌条件下,依次投入二烷基磷酸酯8份,硫化脂肪油11份,烷基硫代磷酸盐9份,磷酸三甲酚酯8份,搅拌均匀后,再投入硼酸钾8份,然后加入0.1份消泡剂,搅拌均匀,保持60℃继续搅拌1.5h,静置沉降1h,即得环保型空气压缩机油。
实施例1~3所得环保型空气压缩机油与对比例市售长城迅能DAH喷油回转式空气压缩机油的性能参数对比如下表所示:
从上表可以看出:本发明环保型空气压缩机油与市售长城迅能DAH喷油回转式空气压缩机油相比,各项性能指标都优于长城迅能DAH,具有优异的综合性能。
实施例4
一种环保型空气压缩机油,包括以下重量份组分:季戊四醇油酸酯和三羟甲基丙烷油酸酯复合而成的合成酯类油50份,其中,季戊四醇油酸酯25份,三羟甲基丙烷油酸酯25份,烷基磷酸酯8份,硫化油脂10份,硼酸盐6份,烷基硫代磷酸盐9份,磷酸三甲酚酯8份,消泡剂0.05份。
其具体制备方法为:
(1)按重量份称取各组分;
(2)在常温下将季戊四醇油酸酯和三羟甲基丙烷油酸酯复合而成的合成酯类油加入到调合釜中;
(3)加热至50℃,在380r/min搅拌条件下,投入烷基磷酸酯、硫化油脂、硼酸盐、烷基硫代磷酸盐、磷酸三甲酚酯和消泡剂;
(4)保持55℃继续搅拌2h;
(5)静置沉降1.2h,即得环保型空气压缩机油。
按CEC L-33-T-93测试方法,测试得该油品生物降解率为95.1%。
实施例5
一种环保型空气压缩机油,包括以下重量份组分:季戊四醇油酸酯和三羟甲基丙烷油酸酯复合而成的合成酯类油50份,其中,季戊四醇油酸酯25份,三羟甲基丙烷油酸酯25份,烷基磷酸酯8份,硫化油脂10份,硼酸盐6份,烷基硫代磷酸盐9份,磷酸三甲酚酯8份,消泡剂0.5份。
其具体制备方法为:
(1)按重量份称取各组分;
(2)在常温下将季戊四醇油酸酯和三羟甲基丙烷油酸酯复合而成的合成酯类油加入到调合釜中;
(3)加热至70℃,在300r/min搅拌条件下,投入烷基磷酸酯、硫化油脂、硼酸盐、烷基硫代磷酸盐、磷酸三甲酚酯和消泡剂;
(4)保持65℃继续搅拌1h;
(5)静置沉降0.8h,即得环保型空气压缩机油。
按CEC L-33-T-93测试方法,测试得该油品生物降解率为95.4%。
上述的对实施例的描述是为便于该技术领域的普通技术人员能理解和使用发明。熟悉本领域技术的人员显然可以容易地对这些实施例做出各种修改,并把在此说明的一般原理应用到其他实施例中而不必经过创造性的劳动。因此,本发明不限于上述实施例,本领域技术人员根据本发明的揭示,不脱离本发明范畴所做出的改进和修改都应该在本发明的保护范围之内。
Claims (10)
1.一种环保型空气压缩机油,其特征在于,包括以下重量份组分:季戊四醇油酸酯和三羟甲基丙烷油酸酯复合而成的合成酯类油46~66份,烷基磷酸酯6~10份,硫化油脂8~13.5份,硼酸盐5~10份,烷基硫代磷酸盐7.95~10份,磷酸三甲酚酯7~10份,消泡剂0.05~0.5份。
2.根据权利要求1所述的环保型空气压缩机油,其特征在于,所述的合成酯类油中,季戊四醇油酸酯和三羟甲基丙烷油酸酯的重量比为1:1~1.3。
3.根据权利要求1所述的环保型空气压缩机油,其特征在于,所述的季戊四醇油酸酯包括PETO-A、PETO-B或PETO-C。
4.根据权利要求1所述的环保型空气压缩机油,其特征在于,所述的三羟甲基丙烷油酸酯包括TMPTO-A、TMPTO-B或TMPTO-C。
5.根据权利要求1所述的环保型空气压缩机油,其特征在于,所述的烷基磷酸酯包括二甲基磷酸酯。
6.根据权利要求1所述的环保型空气压缩机油,其特征在于,所述的硫化油脂包括硫化猪油、硫化烯烃棉籽油或硫化脂肪油。
7.根据权利要求1所述的环保型空气压缩机油,其特征在于,所述的硼酸盐包括三硼酸钾或偏硼酸钠。
8.根据权利要求1所述的环保型空气压缩机油,其特征在于,所述的烷基硫代磷酸盐包括T203;所述的磷酸三甲酚酯包括T306。
9.根据权利要求1所述的环保型空气压缩机油,其特征在于,所述的消泡剂包括T911。
10.一种如权利要求1~9任一项所述的环保型空气压缩机油的制备方法,其特征在于,包括以下步骤:
(1)按重量份称取各组分;
(2)在常温下将季戊四醇油酸酯和三羟甲基丙烷油酸酯复合而成的合成酯类油加入到调合釜中;
(3)加热至50~70℃,在300~380r/min搅拌条件下,投入烷基磷酸酯、硫化油脂、硼酸盐、烷基硫代磷酸盐、磷酸三甲酚酯和消泡剂;
(4)保持55~65℃继续搅拌1~2h;
(5)静置沉降0.8~1.2h,即得环保型空气压缩机油。