CN112172274A - 一种抗菌防辐射保健型面料制造工艺 - Google Patents
一种抗菌防辐射保健型面料制造工艺 Download PDFInfo
- Publication number
- CN112172274A CN112172274A CN202010902539.1A CN202010902539A CN112172274A CN 112172274 A CN112172274 A CN 112172274A CN 202010902539 A CN202010902539 A CN 202010902539A CN 112172274 A CN112172274 A CN 112172274A
- Authority
- CN
- China
- Prior art keywords
- strip
- protective layer
- fabric
- cloth
- width
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及面料制造技术领域，且公开了一种抗菌防辐射保健型面料制造工艺，包括以下步骤，将银纤维面料裁剪为宽度为四厘米的长条状布料，为银纤维布条，将棉布裁剪为宽度为两厘米的长条状布料，为棉布条，将银纤维布条和棉布条上下交错固定在一起，得到第一防护层。该抗菌防辐射保健型面料制造工艺，通过将第一防护层、第二防护层和第三防护层的边角修齐，缝制收边，得到抗菌防辐射保健型面料，三层防护层包括银纤维面料、金属纤维面料和金属涂层面料，其整体抗辐射能力强，通过设置棉布条、纱布条和涤纶布条，面料的柔软性较好，整体弯折不受影响，金属材料不会弯折损坏，贴身面料可以贴合人体，体验更加舒适。
Description
技术领域
本发明涉及面料制造技术领域，具体为一种抗菌防辐射保健型面料制造工艺。
背景技术
面料就是用来制作服装的材料，作为服装三要素之一，面料不仅可以诠释服装的风格和特性，而且直接左右着服装的色彩和造型的表现效果，在服装大世界里，服装的面料五花八门，日新月异，但是从总体上来讲，优质且高档的面料，大都具有穿著舒适、吸汗透气、悬垂挺括、视觉高贵和触觉柔美等几个方面的特点。
中国专利CN109355919A提出了一种防辐射面料的制备方法，该发明经线由硅酸铝纤维、棉纤维、四氟乙烯-六氟丙烯共聚纤维和镍纤维混纺编织而成，纬线由碳纤维、醋酸纤维、竹纤维和钴合金纤维混纺编织而成，将防辐射纤维与透气轻薄面料纤维混纺编织成防辐射面料层，不但具有防辐射的功能，同时使面料穿着舒适，但是该申请的防辐射效果一般，在追求舒适的同时丧失了其最重要的防辐射效果，故而提出一种抗菌防辐射保健型面料制造工艺。
发明内容
(一)解决的技术问题
针对现有技术的不足，本发明提供了一种抗菌防辐射保健型面料制造工艺，具备穿着舒适且抗辐射效果好等优点，解决了传统防辐射面料在追求舒适的同时丧失了其最重要的防辐射效果的问题。
(二)技术方案
为实现上述穿着舒适且抗辐射效果好的目的，本发明提供如下技术方案：一种抗菌防辐射保健型面料制造工艺，包括以下步骤：
1)将银纤维面料裁剪为宽度为四厘米的长条状布料，为银纤维布条，将棉布裁剪为宽度为两厘米的长条状布料，为棉布条，将银纤维布条和棉布条上下交错固定在一起，得到第一防护层；
2)将金属纤维面料裁剪为宽度为四厘米的长条状布料，为金属纤维布条，将纱布裁剪为宽度为两厘米的长条状布料，为纱布条，将金属纤维布条和纱布条上下交错固定在一起，得到第二防护层；
3)将金属涂层面料裁剪为宽度为四厘米的长条状布料，为金属涂层布条，将涤纶布裁剪为宽度为两厘米的长条状布料，为涤纶布条，将金属涂层布条和涤纶布条上下交错固定在一起，得到第三防护层；
4)将第一防护层、第二防护层和第三防护层从下到上一次叠放在一起，第一防护层上的棉布条与第二防护层上的纱布条相对应，第二防护层上的纱布条与第三防护层上的涤纶布条相对应，将第二防护层移动，使得第二防护层上的纱布条对应在第一防护层上银纤维布条的正中，第二防护层上的纱布条对应在第三防护层上金属涂层布条的正中，将第一防护层、第二防护层和第三防护层的边角修齐，缝制收边，得到抗菌防辐射保健型面料。
优选的，步骤1所述将银纤维面料裁剪为宽度为四厘米的长条状布料，为银纤维布条，将棉布裁剪为宽度为两厘米的长条状布料，为棉布条，将银纤维布条和棉布条上下交错固定在一起，得到第一防护层，其中，银纤维布条和棉布条之间交叠一厘米宽度，交叠部分的外部添加棉布然后一起缝制对接。
优选的，步骤2所述将金属纤维面料裁剪为宽度为四厘米的长条状布料，为金属纤维布条，将纱布裁剪为宽度为两厘米的长条状布料，为纱布条，将金属纤维布条和纱布条上下交错固定在一起，得到第二防护层，金属纤维布条和纱布条之间交叠一厘米宽度，交叠部分的外部添加棉布然后一起缝制对接。
优选的，步骤3所述将金属涂层面料裁剪为宽度为四厘米的长条状布料，为金属涂层布条，将涤纶布裁剪为宽度为两厘米的长条状布料，为涤纶布条，将金属涂层布条和涤纶布条上下交错固定在一起，得到第三防护层，金属涂层布条和涤纶布条之间交叠一厘米宽度，交叠部分的外部添加棉布然后一起缝制对接。
优选的，步骤4所述将第一防护层、第二防护层和第三防护层从下到上一次叠放在一起，第一防护层上的棉布条与第二防护层上的纱布条相对应，第二防护层上的纱布条与第三防护层上的涤纶布条相对应，将第二防护层移动，使得第二防护层上的纱布条对应在第一防护层上银纤维布条的正中，第二防护层上的纱布条对应在第三防护层上金属涂层布条的正中，将第一防护层、第二防护层和第三防护层的边角修齐，缝制收边，将第一防护层、第二防护层和第三防护层的边角修齐后，在其外边缘包覆皮革，将皮革与第一防护层、第二防护层和第三防护层缝制在一起。
(三)有益效果
与现有技术相比，本发明提供了一种抗菌防辐射保健型面料制造工艺，具备以下有益效果：
该抗菌防辐射保健型面料制造工艺，通过将第一防护层、第二防护层和第三防护层从下到上一次叠放在一起，第一防护层上的棉布条与第二防护层上的纱布条相对应，第二防护层上的纱布条与第三防护层上的涤纶布条相对应，将第二防护层移动，使得第二防护层上的纱布条对应在第一防护层上银纤维布条的正中，第二防护层上的纱布条对应在第三防护层上金属涂层布条的正中，将第一防护层、第二防护层和第三防护层的边角修齐，缝制收边，得到抗菌防辐射保健型面料，三层防护层包括银纤维面料、金属纤维面料和金属涂层面料，其整体抗辐射能力强，通过设置棉布条、纱布条和涤纶布条，面料的柔软性较好，整体弯折不受影响，金属材料不会弯折损坏，贴身面料可以贴合人体，体验更加舒适。
具体实施方式
下面将结合本发明的实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一：一种抗菌防辐射保健型面料制造工艺，包括以下步骤：
1)将银纤维面料裁剪为宽度为四厘米的长条状布料，为银纤维布条，将棉布裁剪为宽度为两厘米的长条状布料，为棉布条，将银纤维布条和棉布条上下交错固定在一起，得到第一防护层；
2)将金属纤维面料裁剪为宽度为四厘米的长条状布料，为金属纤维布条，将纱布裁剪为宽度为两厘米的长条状布料，为纱布条，将金属纤维布条和纱布条上下交错固定在一起，得到第二防护层；
3)将金属涂层面料裁剪为宽度为四厘米的长条状布料，为金属涂层布条，将涤纶布裁剪为宽度为两厘米的长条状布料，为涤纶布条，将金属涂层布条和涤纶布条上下交错固定在一起，得到第三防护层；
4)将第一防护层、第二防护层和第三防护层从下到上一次叠放在一起，第一防护层上的棉布条与第二防护层上的纱布条相对应，第二防护层上的纱布条与第三防护层上的涤纶布条相对应，将第二防护层移动，使得第二防护层上的纱布条对应在第一防护层上银纤维布条的正中，第二防护层上的纱布条对应在第三防护层上金属涂层布条的正中，将第一防护层、第二防护层和第三防护层的边角修齐，缝制收边，得到抗菌防辐射保健型面料。
将银纤维面料裁剪为宽度为四厘米的长条状布料，为银纤维布条，将棉布裁剪为宽度为两厘米的长条状布料，为棉布条，将银纤维布条和棉布条上下交错固定在一起，得到第一防护层，其中，银纤维布条和棉布条之间交叠一厘米宽度，交叠部分的外部添加棉布然后一起缝制对接。
将金属纤维面料裁剪为宽度为四厘米的长条状布料，为金属纤维布条，将纱布裁剪为宽度为两厘米的长条状布料，为纱布条，将金属纤维布条和纱布条上下交错固定在一起，得到第二防护层，金属纤维布条和纱布条之间交叠一厘米宽度，交叠部分的外部添加棉布然后一起缝制对接。
将金属涂层面料裁剪为宽度为四厘米的长条状布料，为金属涂层布条，将涤纶布裁剪为宽度为两厘米的长条状布料，为涤纶布条，将金属涂层布条和涤纶布条上下交错固定在一起，得到第三防护层，金属涂层布条和涤纶布条之间交叠一厘米宽度，交叠部分的外部添加棉布然后一起缝制对接。
将第一防护层、第二防护层和第三防护层从下到上一次叠放在一起，第一防护层上的棉布条与第二防护层上的纱布条相对应，第二防护层上的纱布条与第三防护层上的涤纶布条相对应，将第二防护层移动，使得第二防护层上的纱布条对应在第一防护层上银纤维布条的正中，第二防护层上的纱布条对应在第三防护层上金属涂层布条的正中，将第一防护层、第二防护层和第三防护层的边角修齐，缝制收边，将第一防护层、第二防护层和第三防护层的边角修齐后，在其外边缘包覆皮革，将皮革与第一防护层、第二防护层和第三防护层缝制在一起。
本发明的有益效果是：该抗菌防辐射保健型面料制造工艺，通过将第一防护层、第二防护层和第三防护层从下到上一次叠放在一起，第一防护层上的棉布条与第二防护层上的纱布条相对应，第二防护层上的纱布条与第三防护层上的涤纶布条相对应，将第二防护层移动，使得第二防护层上的纱布条对应在第一防护层上银纤维布条的正中，第二防护层上的纱布条对应在第三防护层上金属涂层布条的正中，将第一防护层、第二防护层和第三防护层的边角修齐，缝制收边，得到抗菌防辐射保健型面料，三层防护层包括银纤维面料、金属纤维面料和金属涂层面料，其整体抗辐射能力强，通过设置棉布条、纱布条和涤纶布条，面料的柔软性较好，整体弯折不受影响，金属材料不会弯折损坏，贴身面料可以贴合人体，体验更加舒适，解决了传统防辐射面料在追求舒适的同时丧失了其最重要的防辐射效果的问题。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (5)
1.一种抗菌防辐射保健型面料制造工艺，其特征在于，包括以下步骤：
1)将银纤维面料裁剪为宽度为四厘米的长条状布料，为银纤维布条，将棉布裁剪为宽度为两厘米的长条状布料，为棉布条，将银纤维布条和棉布条上下交错固定在一起，得到第一防护层；
2)将金属纤维面料裁剪为宽度为四厘米的长条状布料，为金属纤维布条，将纱布裁剪为宽度为两厘米的长条状布料，为纱布条，将金属纤维布条和纱布条上下交错固定在一起，得到第二防护层；
3)将金属涂层面料裁剪为宽度为四厘米的长条状布料，为金属涂层布条，将涤纶布裁剪为宽度为两厘米的长条状布料，为涤纶布条，将金属涂层布条和涤纶布条上下交错固定在一起，得到第三防护层；
4)将第一防护层、第二防护层和第三防护层从下到上一次叠放在一起，第一防护层上的棉布条与第二防护层上的纱布条相对应，第二防护层上的纱布条与第三防护层上的涤纶布条相对应，将第二防护层移动，使得第二防护层上的纱布条对应在第一防护层上银纤维布条的正中，第二防护层上的纱布条对应在第三防护层上金属涂层布条的正中，将第一防护层、第二防护层和第三防护层的边角修齐，缝制收边，得到抗菌防辐射保健型面料。
2.根据权利要求1所述的一种抗菌防辐射保健型面料制造工艺，其特征在于：步骤1所述将银纤维面料裁剪为宽度为四厘米的长条状布料，为银纤维布条，将棉布裁剪为宽度为两厘米的长条状布料，为棉布条，将银纤维布条和棉布条上下交错固定在一起，得到第一防护层，其中，银纤维布条和棉布条之间交叠一厘米宽度，交叠部分的外部添加棉布然后一起缝制对接。
3.根据权利要求1所述的一种抗菌防辐射保健型面料制造工艺，其特征在于：步骤2所述将金属纤维面料裁剪为宽度为四厘米的长条状布料，为金属纤维布条，将纱布裁剪为宽度为两厘米的长条状布料，为纱布条，将金属纤维布条和纱布条上下交错固定在一起，得到第二防护层，金属纤维布条和纱布条之间交叠一厘米宽度，交叠部分的外部添加棉布然后一起缝制对接。
4.根据权利要求1所述的一种抗菌防辐射保健型面料制造工艺，其特征在于：步骤3所述将金属涂层面料裁剪为宽度为四厘米的长条状布料，为金属涂层布条，将涤纶布裁剪为宽度为两厘米的长条状布料，为涤纶布条，将金属涂层布条和涤纶布条上下交错固定在一起，得到第三防护层，金属涂层布条和涤纶布条之间交叠一厘米宽度，交叠部分的外部添加棉布然后一起缝制对接。
5.根据权利要求1所述的一种抗菌防辐射保健型面料制造工艺，其特征在于：步骤4所述将第一防护层、第二防护层和第三防护层从下到上一次叠放在一起，第一防护层上的棉布条与第二防护层上的纱布条相对应，第二防护层上的纱布条与第三防护层上的涤纶布条相对应，将第二防护层移动，使得第二防护层上的纱布条对应在第一防护层上银纤维布条的正中，第二防护层上的纱布条对应在第三防护层上金属涂层布条的正中，将第一防护层、第二防护层和第三防护层的边角修齐，缝制收边，将第一防护层、第二防护层和第三防护层的边角修齐后，在其外边缘包覆皮革，将皮革与第一防护层、第二防护层和第三防护层缝制在一起。