CN111978800A - Preparation method of sand-containing art rock paint - Google Patents
Preparation method of sand-containing art rock paint Download PDFInfo
- Publication number
- CN111978800A CN111978800A CN202010791706.XA CN202010791706A CN111978800A CN 111978800 A CN111978800 A CN 111978800A CN 202010791706 A CN202010791706 A CN 202010791706A CN 111978800 A CN111978800 A CN 111978800A
- Authority
- CN
- China
- Prior art keywords
- sand
- parts
- stirring
- following
- preparing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of sand-containing art rock paint, which comprises the following steps: s1, preparing a sand-containing rock paint raw material: the sand-containing art rock paint comprises the following raw materials in parts by weight: 20% binder 590-610 parts, sand 295-305 parts and thin rock slices 95-105 parts; s2, preparing 20% of base stock; s3, sieving the sand and the thin rock slices by a 75-85 mesh sieve, and then sieving by a 10-15 mesh sieve; s4, mixing the 20% base material obtained in the S1 with the sand and the thin rock slices sieved in the S2, and uniformly stirring to obtain the sand-containing art rock paint; when the white sand is added, the white sand is subjected to double-screening, so that the granular feeling of the white sand is high in hardness and transparent, the flaky texture effect of the marble can be well shown, and the texture effect of the natural stone can be very vividly and perfectly shown.
Description
Technical Field
The invention relates to the technical field of home decoration materials, in particular to a preparation method of sand-containing art rock paint.
Background
The stone paint is a chemical raw material, and the finished product raw material is characterized in that the finished product raw material can generate the light reflection effect of inlaying diamonds under illumination after being used, and is classified into real stone paint (stone-like paint), granite paint, cave stone paint, artistic stone paint and the like;
the building decorated by the stone paint has natural and real natural color, gives people elegant, harmonious and solemn aesthetic feeling, and is suitable for indoor and outdoor decoration of various buildings. Especially, the decoration on the curved surface building is vivid and lifelike, and has an effect of returning to nature. The stone paint has the advantages of fire prevention, water prevention, acid and alkali resistance and pollution resistance. No toxicity, no smell, strong bonding force, no fading and the like, can effectively prevent the corrosion of the external severe environment to the building, and prolongs the service life of the building.
However, the prior art rock paint has a plurality of problems in production;
in the preparation process of the existing art rock paint, because sand grains in the raw materials are too coarse and easily fall off in spraying, the construction dosage and the cost are influenced, the grain size is too fine and the flaky texture effect of marble cannot be well developed, the use restriction cannot perfectly show the texture effect of natural stone vividly, and meanwhile, the shearing force in the existing materials is low, solid grains and emulsion cannot be stably, effectively and homogeneously lifted and suspended, and the preparation of the stone paint is not facilitated; therefore, a preparation method of the sand-containing art rock paint is provided.
Disclosure of Invention
The invention aims to provide a preparation method of a sand-containing artistic rock paint, which aims to solve the problems in the background technology.
In order to achieve the purpose, the invention provides the following technical scheme: a preparation method of sand-containing artistic rock paint comprises the following steps:
s1, preparing a sand-containing rock paint raw material: the sand-containing art rock paint comprises the following raw materials in parts by weight: 20% binder 590-610 parts, sand 295-305 parts and thin rock slices 95-105 parts;
s2, preparing 20% of base stock;
s3, sieving the sand and the thin rock slices by a 75-85 mesh sieve, and then sieving by a 10-15 mesh sieve;
s4, mixing the 20% base material obtained in the S1 with the sand and the thin rock slices sieved in the S2, and uniformly stirring to obtain the sand-containing art rock paint.
As further preferable in the present technical solution: the 20% base material is prepared from the following raw materials in parts by weight:
336 parts of silicone-acrylic emulsion, 16-18 parts of film-forming additive, 626 parts of water 620, 1.4-1.6 parts of mildew preventive, 9-11 parts of ethylene glycol, 8-10 parts of thickener, 3.4-3.6 parts of neutralizer and 0.8-1.0 part of aluminum magnesium silicate thixotropic lubricant.
As further preferable in the present technical solution: at S2, at 20% base production, the following steps were included:
s21, adding water into a stirring pot, adding the silicone-acrylic emulsion, wherein the rotation speed of the stirring pot is 20-25 r/m, and the stirring time is 8-10 minutes;
s22, adding the film-forming assistant, the mildew preventive and the ethylene glycol into the stirring pot, adjusting the rotating speed of the stirring pot to 35-45 rpm, and stirring for 25-30 minutes;
s23, adding the thickening agent and the neutralizing agent into the stirring pot, and stirring for 8-10 minutes;
s24, adding a thixotropic lubricant of aluminum magnesium silicate into the stirring pot, adjusting the rotating speed of the stirring pot to be 55-60 r/m, and stirring for 20-25 minutes to be sticky to obtain a 20% base material.
As further preferable in the present technical solution: in S3, the sand is preferably a transparent white yarn having a good granular hardness, and the overall appearance of the sand is measured.
As further preferable in the present technical solution: the thin rock slices are colorful thin rock slices.
As further preferable in the present technical solution: in S4, when 20% of base material is mixed with the sand and the thin rock slices, the sand is added into the 20% of base material, the rotating speed of the stirring pot is adjusted to 80-85 r/m, the stirring is carried out for 35-40 minutes, and the mixture is uniformly mixed.
As further preferable in the present technical solution: and (3) after uniformly mixing 20% of base material and sand, adding the thin rock slices, adjusting the rotating speed of a stirring pot to 90-95 revolutions per minute, stirring for 40-50 minutes, and uniformly mixing to obtain paste-like rock paint containing the sand art.
As further preferable in the present technical solution: in S23, when the thickener and the neutralizer are added, the thickener is added first, and is diluted with water in an amount of four times the amount of the thickener, and slowly added.
As further preferable in the present technical solution: after the thickener was added, the neutralizer was added, and diluted with twice the amount of water as the neutralizer and slowly added.
Compared with the prior art, the invention has the beneficial effects that:
the magnesium aluminum silicate thixotropic lubricant is added to enable the interior of the stone paint to present an association network structure, so that stable, effective and homogeneous lifting and suspension can be generated for solid particles, emulsion and gas in a system, the solid particles, the emulsion and the gas are prevented from sinking due to the action of gravity, and the stone paint has excellent anti-sinking performance;
when the white sand is added, the white sand is subjected to double-screening, so that the granular feeling of the white sand is good in hardness and transparent, the flaky texture effect of the marble can be well shown, and the texture effect of the natural stone is very vividly and perfectly shown;
and thirdly, when the thickening agent and the neutralizing agent are added, diluting the thickening agent by using water in an amount which is four times that of the thickening agent, and slowly adding the water, so that the sand-containing rock paint is ensured to have good water resistance.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to data in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Example one
The invention provides a technical scheme that: a preparation method of sand-containing artistic rock paint comprises the following steps:
s1, preparing a sand-containing rock paint raw material: the sand-containing art rock paint comprises the following raw materials in parts by weight: 590 parts of 20% base stock, 305 parts of sand and 105 parts of thin rock slices;
s2, preparing 20% of base stock;
s3, sieving the sand and the thin rock slices with a 75-mesh sieve, and then sieving with a 10-mesh sieve;
s4, mixing the 20% base material obtained in the S1 with the sand and the thin rock slices sieved in the S2, and uniformly stirring to obtain the sand-containing art rock paint.
In this embodiment, specifically: the 20% base material is prepared from the following raw materials in parts by weight:
330 parts of silicone-acrylic emulsion, 16 parts of film-forming assistant, 620 parts of water, 1.4 parts of mildew preventive, 9-11 parts of ethylene glycol, 8 parts of thickener, 3.6 parts of neutralizer and 0.8 part of aluminum magnesium silicate thixotropic lubricant.
In this embodiment, specifically: at S2, at 20% base production, the following steps were included:
s21, adding water into a stirring pot, adding the silicone-acrylic emulsion, wherein the rotation speed of the stirring pot is 20 revolutions per minute, and the stirring time is 8 minutes;
s22, adding the film-forming assistant, the mildew preventive and the ethylene glycol into the stirring pot, adjusting the rotating speed of the stirring pot to 35 revolutions per minute, and stirring for 25 minutes;
s23, adding the thickening agent and the neutralizing agent into the stirring pot, and stirring for 8 minutes;
s24, adding a thixotropic lubricant of aluminum magnesium silicate into the stirring pot, adjusting the rotating speed of the stirring pot to be 55 revolutions per minute, and stirring for 20 minutes to form a sticky state to obtain a 20% base material.
In this embodiment, specifically: in S3, the sand is preferably a transparent white yarn having a good granular hardness, and the overall appearance of the sand is measured.
In this embodiment, specifically: the thin rock slices are colorful thin rock slices.
In this embodiment, specifically: in S4, when 20% of base material is mixed with the sand and the thin rock slices, the sand is added into the 20% of base material, the rotating speed of the stirring pot is adjusted to 80 r/m, the stirring is carried out for 35 minutes, and the mixture is uniformly mixed.
In this embodiment, specifically: and (3) after uniformly mixing 20% of base material and sand, adding the thin rock slices, adjusting the rotating speed of a stirring pot to 90 revolutions per minute, stirring for 40 minutes, and uniformly mixing to obtain paste-like rock paint containing the sand art.
In this embodiment, specifically: in S23, when the thickener and the neutralizer are added, the thickener is added first, and is diluted with water in an amount of four times the amount of the thickener, and slowly added.
In this embodiment, specifically: after the thickener was added, the neutralizer was added, and diluted with twice the amount of water as the neutralizer and slowly added.
Example two
The invention provides a technical scheme that: a preparation method of sand-containing artistic rock paint comprises the following steps:
s1, preparing a sand-containing rock paint raw material: the sand-containing art rock paint comprises the following raw materials in parts by weight: 600 parts of 20% base material, 300 parts of sand and 100 parts of thin rock slices;
s2, preparing 20% of base stock;
s3, sieving the sand and the thin rock slices with a 80-mesh sieve, and then sieving with a 15-mesh sieve;
s4, mixing the 20% base material obtained in the S1 with the sand and the thin rock slices sieved in the S2, and uniformly stirring to obtain the sand-containing art rock paint.
In this embodiment, specifically: the 20% base material is prepared from the following raw materials in parts by weight:
333 parts of silicone-acrylic emulsion, 17 parts of film-forming assistant, 623 parts of water, 1.5 parts of mildew inhibitor, 10 parts of ethylene glycol, 9 parts of thickener, 3.5 parts of neutralizer and 0.9 part of magnesium aluminum silicate thixotropic lubricant.
In this embodiment, specifically: at S2, at 20% base production, the following steps were included:
s21, adding water into a stirring pot, adding the silicone-acrylic emulsion, wherein the rotation speed of the stirring pot is 23 revolutions per minute, and the stirring time is 9 minutes;
s22, adding the film-forming assistant, the mildew preventive and the ethylene glycol into the stirring pot, adjusting the rotating speed of the stirring pot to 40 revolutions per minute, and stirring for 28 minutes;
s23, adding the thickening agent and the neutralizing agent into the stirring pot, and stirring for 9 minutes;
s24, adding a thixotropic lubricant of aluminum magnesium silicate into the stirring pot, adjusting the rotating speed of the stirring pot to be 58 r/min, and stirring for 23 minutes to form a sticky state to obtain a 20% base material.
In this embodiment, specifically: in S3, the sand is preferably a transparent white yarn having a good granular hardness, and the overall appearance of the sand is measured.
In this embodiment, specifically: the thin rock slices are colorful thin rock slices.
In this embodiment, specifically: in S4, when 20% of base material is mixed with the sand and the thin rock slices, the sand is added into the 20% of base material, the rotating speed of the stirring pot is adjusted to 82 r/m, stirring is carried out for 38 minutes, and the mixture is uniformly mixed.
In this embodiment, specifically: and (3) uniformly mixing 20% of base material and sand, adding the thin rock slices, adjusting the rotating speed of a stirring pot to 93 revolutions per minute, stirring for 45 minutes, and uniformly mixing to obtain paste-like rock paint containing the sand art.
EXAMPLE III
The invention provides a technical scheme that: a preparation method of sand-containing artistic rock paint comprises the following steps:
s1, preparing a sand-containing rock paint raw material: the sand-containing art rock paint comprises the following raw materials in parts by weight: 610 parts of 20% base material, 295 parts of sand and 95 parts of thin rock slices;
s2, preparing 20% of base stock;
s3, sieving the sand and the thin rock slices with a 85-mesh sieve, and then sieving with a 15-mesh sieve;
s4, mixing the 20% base material obtained in the S1 with the sand and the thin rock slices sieved in the S2, and uniformly stirring to obtain the sand-containing art rock paint.
In this embodiment, specifically: the 20% base material is prepared from the following raw materials in parts by weight:
336 parts of silicone-acrylic emulsion, 16 parts of film-forming assistant, 620 parts of water, 1.6 parts of mildew preventive, 11 parts of ethylene glycol, 10 parts of thickening agent, 3.4 parts of neutralizer and 0.8 part of aluminum magnesium silicate thixotropic lubricant.
In this embodiment, specifically: at S2, at 20% base production, the following steps were included:
s21, adding water into a stirring pot, adding the silicone-acrylic emulsion, wherein the rotation speed of the stirring pot is 25 revolutions per minute, and the stirring time is 10 minutes;
s22, adding the film-forming assistant, the mildew preventive and the ethylene glycol into the stirring pot, adjusting the rotating speed of the stirring pot to 45 revolutions per minute, and stirring for 30 minutes;
s23, adding the thickening agent and the neutralizing agent into the stirring pot, and stirring for 10 minutes;
s24, adding a thixotropic lubricant of aluminum magnesium silicate into the stirring pot, adjusting the rotating speed of the stirring pot to 60 revolutions per minute, and stirring for 25 minutes to form a viscous state to obtain a 20% base material.
In this embodiment, specifically: in S3, the sand is preferably a transparent white yarn having a good granular hardness, and the overall appearance of the sand is measured.
In this embodiment, specifically: the thin rock slices are colorful thin rock slices.
In this embodiment, specifically: in S4, when 20% of base material is mixed with the sand and the thin rock slices, the sand is added into the 20% of base material, the rotating speed of the stirring pot is adjusted to 85 r/m, the stirring is carried out for 40 minutes, and the mixture is uniformly mixed.
In this embodiment, specifically: and (3) uniformly mixing 20% of base material and sand, adding the thin rock slices, adjusting the rotating speed of a stirring pot to 95 revolutions per minute, stirring for 50 minutes, and uniformly mixing to obtain paste-like rock paint containing the sand art.
Examples of the experiments
The invention also provides a sand-containing artistic rock paint prepared by the method, which comprises the following steps:
when producing a certain art rock paint, preparing 333KG silicone-acrylate emulsion, 17KG film forming additive, 623KG water, 1.5KG mildew preventive, 10KG ethylene glycol, 9KG thickener, 3.5KG neutralizer, 1KG magnesium aluminum silicate thixotropic lubricant, 600KG sand and 100KG thin rock slices;
sieving 600KG white sand with a 80-mesh sieve, remaining 595KG after sieving with the 80-mesh sieve, preparing 10KG white sand, sieving with the 80-mesh sieve, adding the rest 9KG into the 595KG white sand, sieving with the 10-mesh sieve, removing powder, remaining 601KG, taking out 1KG white sand, and remaining 600KG white sand;
sieving 100KG thin rock slices with a 80-mesh sieve, sieving with the 80-mesh sieve to obtain 97KG, preparing 5KG thin rock slices, sieving with the 80-mesh sieve to obtain 4KG, adding the 5KG thin rock slices into the 97KG thin rock slices, sieving with a 10-mesh sieve, and removing powder to obtain 100 KG;
adding water into a stirring pot, adding the silicone-acrylic emulsion, wherein the rotating speed of the stirring pot is 23 revolutions per minute, and the stirring time is 9 minutes;
adding a film forming auxiliary agent, a mildew preventive and glycol, adjusting the rotating speed of a stirring pot to 40 revolutions per minute, and stirring for 28 minutes;
adding thickener and neutralizer, stirring for 9 min, detecting viscosity to be 139KU, and continuing stirring for 1min until viscosity is 140KU to reach standard viscosity;
adding a magnesium aluminum silicate thixotropic lubricant, adjusting the rotating speed of a stirring pot to be 58 r/min, and stirring for 23 minutes to form a viscous state;
adding white sand, adjusting the rotating speed of a stirring pot to 82 revolutions per minute, stirring for 38 minutes, and uniformly mixing;
adding the thin rock slices, adjusting the rotating speed of a stirring pot to 93 revolutions per minute, stirring for 45 minutes, and uniformly mixing to obtain paste-like rock paint containing sand;
the working principle is as follows: during the preparation process, the aluminum magnesium silicate thixotropic lubricant is added to make the interior of the stone paint present an associated network structure, can generate stable, effective and homogeneous lifting and suspension for solid particles, emulsion and gas in a system, prevent the solid particles, the emulsion and the gas from sinking due to the action of gravity, has excellent anti-sinking performance, in addition, the aluminum magnesium silicate plays a thixotropic role in the stone paint, the shearing force is large enough, the system viscosity is greatly reduced, the fluidity is good, and simultaneously when white sand is added, the double-sieving sieve for the white sand ensures that the white sand has good granular hardness and transparency, can well show the flaky texture effect of the marble and vividly and perfectly show the texture effect of the natural stone, meanwhile, when the thickening agent and the neutralizing agent are added, the thickening agent is diluted by water in four times of the thickening agent, and the water is slowly added, so that the sand-containing rock paint is ensured to have good water resistance.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (9)
1. A preparation method of sand-containing art rock paint is characterized by comprising the following steps: the method comprises the following steps:
s1, preparing a sand-containing rock paint raw material: the sand-containing art rock paint comprises the following raw materials in parts by weight: 20% binder 590-610 parts, sand 295-305 parts and thin rock slices 95-105 parts;
s2, preparing 20% of base stock;
s3, sieving the sand and the thin rock slices by a 75-85 mesh sieve, and then sieving by a 10-15 mesh sieve;
s4, mixing the 20% base material obtained in the S1 with the sand and the thin rock slices sieved in the S2, and uniformly stirring to obtain the sand-containing art rock paint.
2. The method for preparing a sandstone paint containing sand as claimed in claim 1, wherein the method comprises the following steps: the 20% base material is prepared from the following raw materials in parts by weight:
336 parts of silicone-acrylic emulsion, 16-18 parts of film-forming additive, 626 parts of water 620, 1.4-1.6 parts of mildew preventive, 9-11 parts of ethylene glycol, 8-10 parts of thickener, 3.4-3.6 parts of neutralizer and 0.8-1.0 part of aluminum magnesium silicate thixotropic lubricant.
3. The method for preparing a sandstone paint containing sand as claimed in claim 1, wherein the method comprises the following steps: at S2, at 20% base production, the following steps were included:
s21, adding water into a stirring pot, adding the silicone-acrylic emulsion, wherein the rotation speed of the stirring pot is 20-25 r/m, and the stirring time is 8-10 minutes;
s22, adding the film-forming assistant, the mildew preventive and the ethylene glycol into the stirring pot, adjusting the rotating speed of the stirring pot to 35-45 rpm, and stirring for 25-30 minutes;
s23, adding the thickening agent and the neutralizing agent into the stirring pot, and stirring for 8-10 minutes;
s24, adding a thixotropic lubricant of aluminum magnesium silicate into the stirring pot, adjusting the rotating speed of the stirring pot to be 55-60 r/m, and stirring for 20-25 minutes to be sticky to obtain a 20% base material.
4. The method for preparing a sandstone paint containing sand as claimed in claim 1, wherein the method comprises the following steps: in S3, the sand is preferably a transparent white yarn having a good granular hardness, and the overall appearance of the sand is measured.
5. The method for preparing a sandstone paint containing sand as claimed in claim 4, wherein the method comprises the following steps: the thin rock slices are colorful thin rock slices.
6. The method for preparing a sandstone paint containing sand as claimed in claim 1, wherein the method comprises the following steps: in S4, when 20% of base material is mixed with the sand and the thin rock slices, the sand is added into the 20% of base material, the rotating speed of the stirring pot is adjusted to 80-85 r/m, the stirring is carried out for 35-40 minutes, and the mixture is uniformly mixed.
7. The method for preparing a sandstone paint containing sand as claimed in claim 6, wherein the method comprises the following steps: and (3) after uniformly mixing 20% of base material and sand, adding the thin rock slices, adjusting the rotating speed of a stirring pot to 90-95 revolutions per minute, stirring for 40-50 minutes, and uniformly mixing to obtain paste-like rock paint containing the sand art.
8. The method for preparing a sandstone paint containing sand as claimed in claim 3, wherein the method comprises the following steps: in S23, when the thickener and the neutralizer are added, the thickener is added first, and is diluted with water in an amount of four times the amount of the thickener, and slowly added.
9. The method for preparing a sandstone paint containing sand as claimed in claim 4, wherein the method comprises the following steps: after the thickener was added, the neutralizer was added, and diluted with twice the amount of water as the neutralizer and slowly added.